RU2005122604A - Способ получения водных дисперсий - Google Patents
Способ получения водных дисперсий Download PDFInfo
- Publication number
- RU2005122604A RU2005122604A RU2005122604/04A RU2005122604A RU2005122604A RU 2005122604 A RU2005122604 A RU 2005122604A RU 2005122604/04 A RU2005122604/04 A RU 2005122604/04A RU 2005122604 A RU2005122604 A RU 2005122604A RU 2005122604 A RU2005122604 A RU 2005122604A
- Authority
- RU
- Russia
- Prior art keywords
- parts
- weight
- mass
- alkyl
- carbon atoms
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F2/00—Processes of polymerisation
- C08F2/12—Polymerisation in non-solvents
- C08F2/16—Aqueous medium
- C08F2/22—Emulsion polymerisation
- C08F2/24—Emulsion polymerisation with the aid of emulsifying agents
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
- C08L51/003—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F285/00—Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L33/04—Homopolymers or copolymers of esters
- C08L33/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
- C08L33/10—Homopolymers or copolymers of methacrylic acid esters
- C08L33/12—Homopolymers or copolymers of methyl methacrylate
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
- C09D133/04—Homopolymers or copolymers of esters
- C09D133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
- C09D133/10—Homopolymers or copolymers of methacrylic acid esters
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L33/04—Homopolymers or copolymers of esters
- C08L33/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
- C08L33/10—Homopolymers or copolymers of methacrylic acid esters
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L33/18—Homopolymers or copolymers of nitriles
- C08L33/20—Homopolymers or copolymers of acrylonitrile
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L35/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least one other carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
- C08L35/06—Copolymers with vinyl aromatic monomers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L55/00—Compositions of homopolymers or copolymers, obtained by polymerisation reactions only involving carbon-to-carbon unsaturated bonds, not provided for in groups C08L23/00 - C08L53/00
- C08L55/005—Homopolymers or copolymers obtained by polymerisation of macromolecular compounds terminated by a carbon-to-carbon double bond
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
- Y10T428/2991—Coated
- Y10T428/2998—Coated including synthetic resin or polymer
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Graft Or Block Polymers (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Polymerisation Methods In General (AREA)
Claims (17)
1. Способ получения водной дисперсии, в соответствии с которым
а) берут воду и эмульгатор,
б) прибавляют от 25,0 до 45,0 частей массы первого состава, содержащего
А) от 50,0 до 99,9 частей массы алкилметакрилатов с числом атомов углерода в алкильном остатке от одного до двадцати,
Б) от 0,0 до 40 частей массы алкилакрилатов с числом атомов углерода в алкильном остатке от одного до двадцати,
В) от 0,1 до 10,0 частей массы мономеров, образующих межмолекулярные связи,и
Г) от 0,0 до 8,0 частей массы стирольных мономеров общей формулы (I)
причем остатки от R1 до R5 в каждом отдельном случае независимо друг от друга означают атом водорода, галогена, алкильную группу с числом атомов углерода от одного до шести или алкенильную группу с числом атомов углерода от двух до шести и остаток R6 означает атом водорода или алкильную группу с числом атомов углерода от одного до шести,
и полимеризуют до степени превращения не менее 85,0 мас.% из расчета на общую массу компонент А), Б), В) и Г),
в) прибавляют от 35,0 до 55,0 частей массы второго состава, содержащего
Д) от 80,0 до 100,0 частей массы (мет)акрилатов,
Е) от 0,05 до 10,0 частей массы мономеров, образующих межмолекулярные связи, и
Ж) от 0,0 до 20,0 частей массы стирольных мономеров общей формулы (I),
и полимеризуют до степени превращения не менее 85,0 мас.% из расчета на общую массу компонент Д), Е) и Ж),
г) прибавляют от 10,0 до 30,0 частей массы третьего состава, содержащего
3) от 50,0 до 100,0 частей массы алкилметакрилатов с числом атомов углерода в алкильном остатке от одного до двадцати,
И) от 0,0 до 40,0 частей массы алкилакрилатов с числом атомов углерода в алкильном остатке от одного до двадцати и
К) от 0,0 до 10,0 частей массы стирольных мономеров общей формулы (I),
и полимеризуют до степени превращения не менее 85,0 мас.% из расчета на общую массу компонент З), И) и К),
причем указанные части массы составов б), в) и г) в сумме составляют 100,0 частей массы,
отличающийся тем, что
д) каждую полимеризацию проводят в интервале температур от более 60°С до менее 90°С и
е) относительное содержание всех веществ выбирают так, чтобы общая масса компонент от А) до К) из расчета на общую массу водной дисперсии была более 50,0 мас.%.
2. Способ по п.1, отличающийся тем, что получают водную дисперсию, содержащую менее 5,0 мас.% коагулята из расчета на ее общую массу.
3. Способ по п.1, отличающийся тем, что в качестве исходной смеси загружают от 90,00 до 99,99 частей массы воды и от 0,01 до 10,00 частей массы эмульгатора, причем указанные части массы в сумме составляют 100 частей массы.
4. Способ по п.1, отличающийся тем, что используют анионные или неионогенные эмульгаторы.
5. Способ по п.1, отличающийся тем, что исходная водная эмульсия содержит затравочный латекс.
6. Способ по п.5, отличающийся тем, что загружаемый затравочный латекс имеет радиус частиц, измеренный по способу Коултера, в пределах от 5,0 до 20,0 нм.
7. Способ по п.1, отличающийся тем, что исходная водная эмульсия содержит алкиловый спирт с числом атомов углерода в алкильном остатке от двенадцати до двадцати.
8. Способ по п.1, отличающийся тем, что полимеризацию на стадиях от б) до г) инициируют с использованием пероксодисульфата, в предпочтительном случае с использованием пероксодисульфата аммония и/или щелочного металла.
9. Способ по п.1, отличающийся тем, что относительное содержание всех веществ выбирают так, чтобы получались ядерно-оболочечные частицы с общим радиусом, измеренным по способу Коултера, в пределах от 150,0 до менее 250,0 нм.
10. Способ по одному из пп.1-9, отличающийся тем, что вторую и третью смесь мономеров прибавляют по мере их расходования.
11. Ядерно-оболочечные частицы, получаемые способом по не менее чем одному из приведенных выше пунктов, в частности, способом по п.6.
12. Формовочная масса, содержащая в каждом отдельном случае из расчета на ее общую массу
A) от 1,0 до 50,0 мас.% по крайней мере одних ядерно-оболочечных частиц по п.11;
Б) от 1,0 до 99,0 мас.% по крайней мере одного (мет)акрильного полимера;
B) от 0,0 до 45,0 мас.% стирол-акрилонитрильных сополимеров и
Г) от 0,0 до 10,0 мас.% других добавок,
при этом проценты массы в сумме составляют 100,0 мас.%.
13. Формовочная масса по п.12, отличающаяся тем, что (мет)акрильный полимер включает, в каждом отдельном случае из расчета на его общую массу,
а) от 50,0 до 100,0 мас.% алкилметакрилатных повторяющихся структурных единиц с числом атомов углерода в алкильном остатке от одного до двадцати,
б) от 0,0 до 40,0 мас.% алкилакрилатных повторяющихся структурных единиц с числом атомов углерода в алкильном остатке от одного до двадцати и
в) от 0,0 до 8,0 мас.% стирольных повторяющихся структурных единиц общей формулы (I),
при этом проценты массы в сумме составляют 100,0 мас.%.
14. Формовочная масса по п.12, отличающаяся тем, что формовочная масса содержит стирол-акрилонитрильные сополимеры, причем стирол-акрилонитрильные сополимеры получают в результате полимеризации смеси, состоящей из
от 70 до 92 мас.% стирола, от 8 до 30 мас.% акрилонитрила и
от 0 до 22 мас.% других сомономеров, в каждом отдельном случае из расчета на общую массу полимеризующихся мономеров.
15. Формовочная масса по одному из пп.12-14, отличающаяся тем, что из расчета на ее общую массу она содержит от 0,1 до 10,0 мас.% еще одного продукта полимеризации, среднечисловая молекулярная масса которого по сравнению с (мет)акрильным полимером б) выше не менее чем на 10%.
16. Формованное изделие, получаемое из формовочной массы по одному из пп.12-15.
17. Формованное изделие по п.16, отличающееся тем, что формованное изделие характеризуется Викат-температурой размягчения по ISO 306 (В 50) не менее 85, в более предпочтительном случае не менее 90 и в наиболее предпочтительном случае не менее 93°С, ударной вязкостью на образце с надрезом (Charpy 179/1eA) по ISO 179 не ниже 6,0 кДж/м2 при 23°С и не ниже 2,5 кДж/м2 при -10°С, модулем упругости по ISO 527-2 на менее 1500 МПа, белесоватостью по ASTM D 1003 (1997) не более 2,5%, пропусканием (D 65/10°) по DIN 5033/5036 не менее 88,5%.