KR100963860B1 - 생분해성 수지 조성물 및 생분해성 수지 조성물용 충전재및 성형체 - Google Patents

생분해성 수지 조성물 및 생분해성 수지 조성물용 충전재및 성형체 Download PDF

Info

Publication number
KR100963860B1
KR100963860B1 KR1020030053034A KR20030053034A KR100963860B1 KR 100963860 B1 KR100963860 B1 KR 100963860B1 KR 1020030053034 A KR1020030053034 A KR 1020030053034A KR 20030053034 A KR20030053034 A KR 20030053034A KR 100963860 B1 KR100963860 B1 KR 100963860B1
Authority
KR
South Korea
Prior art keywords
biodegradable resin
resin composition
filler
biodegradable
delete delete
Prior art date
Application number
KR1020030053034A
Other languages
English (en)
Other versions
KR20040015677A (ko
Inventor
고지노자키
다카히사나미키
Original Assignee
후지쯔 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 후지쯔 가부시끼가이샤 filed Critical 후지쯔 가부시끼가이샤
Publication of KR20040015677A publication Critical patent/KR20040015677A/ko
Application granted granted Critical
Publication of KR100963860B1 publication Critical patent/KR100963860B1/ko

Abstract

본 발명은 강도, 내수성, 성형 가공성, 내열성 등의 성능이 우수하며, 또한 폐기시에는 자연계에 일반적으로 존재하는 미생물에 의해서 조속히 분해 가능하고, 각종 분야에서의 성형체에 적합한 생분해성 수지 조성물 등을 제공하는 것을 목적으로 한다.
본 발명의 생분해성 수지 조성물은 생분해성 수지와 이 생분해성 수지로 표면이 코팅된 충전재를 함유한다. 충전재가 운모, 탈크 및 몬모릴로나이트로부터 선택되는 적어도 1종인 형태, 충전재의 함유량이 5.0∼50.0 질량%인 형태, 충전재의 평균 입자 지름이 0.01∼200 μm인 형태, 생분해성 수지가 지방족 폴리에스테르 수지인 형태, 지방족 폴리에스테르 수지가 폴리젖산인 형태, 실리콘계 화합물, 금속염, 금 속수산화염 및 인계 화합물로부터 선택되는 적어도 1종의 난연 성분을 함유하는 형태 등을 들 수 있다.

Description

생분해성 수지 조성물 및 생분해성 수지 조성물용 충전재 및 성형체{BIODEGRADABLE RESIN COMPOSITION, FILLER THEREFOR AND MOLDED ARTICLE THEREOF}
본 발명은 기존의 플라스틱과 동등한 성능을 지니고, 또한 폐기시에는 자연계에 일반적으로 존재하는 미생물에 의해서 조속히 분해 가능하며, 각종 분야에서의 성형체에 적합한 생분해성 수지 조성물 및 이 생분해성 수지 생물에 적합하게 사용할 수 있으며, 분산성이 우수한 생분해성 수지 조성물용 충전재, 및 각종 전기 제품 등의 광체 등으로서 적합하게 이용되어, 환경 문제를 발생하는 일없이 용이하게 폐기 처분이 가능한 성형체에 관한 것이다.
종래부터, 수지 조성물은 광체 등으로서 각종 전기 제품에 사용되고 있다. 그러나, 수지 조성물은 폐기 처분시에 연소하면 고열로 인해 연소로를 파손시키며, 또한, 다이옥신 등의 유독 가스를 발생하여 흙 속에 매립하더라도 분해되지 않기 때문에 폐기 처분이 용이하지 않고 환경 문제를 야기할 가능성이 있다고 하는 문제가 있다.
2001년 4월부터 「사용 완료 전기 제품 리사이클법」이 시행되어, 현재, TV( 텔레비젼) 등의 대형 전기 제품의 회수가 시작되고 있지만, 회수된 대형 전기 제품의 대부분은 리사이클되는 일이 없고, 법적 규제도 없기 때문에 불연 쓰레기로서 폐기 처분되고 있다. 한편, 소형 전기 제품의 경우, 일반적으로 대형 전기 제품에 비하여 판매수가 많기 때문에, 전체적으로 다량의 불연 먼지가 발생한다. 따라서, 대형·소형에 관계없이 전기 제품의 폐기 처분은 현재 심각한 사회 문제가 되고 있다.
최근, 이 사회 문제를 해결하는 대책으로서 생분해성 수지가 주목받고 있다. 상기 생분해성 수지란, 사용후에는 자연계에서 미생물이 관여하여 저분자 화합물로, 최종적으로는 물과 이산화탄소로 분해되는 플라스틱이다(생분해성 플라스틱 연구회, ISO/TC-207/SC3). 상기 생분해성 수지로는 분자 골격에 지방족계 폴리에스테르 수지를 갖는 것, 폴리비닐알코올을 갖는 것, 다당류를 갖는 것의 3종으로 크게 구별된다. 생분해성 수지는 지금까지 농림 수산용 자재(필름, 식재 포트, 낚시 실, 어망), 토목 공사 자재(보수 시트, 식물 네트 등), 포장·용기 분야(흙, 식품 등이 부착되어 리사이클이 어려운 물건) 등 주로 일회용 용품에 대하여 실용화가 진행되어 오고 있다.
따라서, 생분해성 수지를 수지 조성물에 사용하면 흙 속으로의 폐기 처분 등이 가능해져 환경에의 부하를 대폭 저하시킬 수 있다.
그러나, 상기 생분해성 수지를 전기 제품에 관한 성형체, 예컨대 광체, 구조재 등으로서 사용하는 경우에는 강도, 내열성, 난연성 등이 우수한 물질을 갖는 것이 요구되기 때문에, 단순히 생분해성 수지를 사용한 것만으로는 상기 물질을 원하 는 범위로 할 수 없다. 예컨대, 상기 생분해성 수지의 하나인 지방족 폴리에스테르 수지는 유리 전이 온도(Tg: 저장 탄성율이 상온시의 약1/10∼약1/100으로 저하하는 온도)가 60℃ 부근이며, 60℃ 이상에서는 저장 탄성율이 상온시의 약 1×109 Pa에서 약 1×107 Pa로 급격히 저하되어, 기계적 변형이 발생하기 쉬워지기 때문에 전기 제품 등의 광체 등의 용도에는 그대로 사용할 수 없다.
따라서, 사용 중에는 기존의 플라스틱과 동등한 성능, 예컨대 강도, 내수성, 성형 가공성, 내열성 등을 지니고, 또한 폐기 처분시에는 자연계에 일반적으로 존재하는 미생물에 의해 조속히 분해 가능하며, 각종 전기 제품 등의 성형체에 적합한 수지 조성물은 아직 개발되어 있지 않은 것이 현재의 상황을 고려해서, 이러한 수지 조성물의 개발이 요구되고 있다.
본 발명은 강도, 내수성, 성형 가공성, 내열성 등의 성능이 우수하며, 또한 폐기시에는 자연계에 일반적으로 존재하는 미생물에 의해서 조속히 분해 가능하고, 각종 분야에서의 성형체에 적합한 생분해성 수지 조성물 및 이 생분해성 수지 생물에 적합하게 사용할 수 있으며, 분산성이 우수한 생분해성 수지 조성물용 충전재, 및 각종 전기 제품 등의 광체 등으로서 적합하게 이용되어 환경 문제를 생기는 일없이 용이하게 폐기 처분이 가능한 성형체를 제공하는 것을 목적으로 한다.
본 발명의 생분해성 수지 조성물은 생분해성 수지와 이 생분해성 수지로 표 면이 코팅된 충전재를 함유하는 것을 특징으로 한다.
본 발명의 생분해성 수지 조성물용 충전재는 충전재의 표면이 생분해성 수지로 코팅되어 되는 것을 특징으로 한다.
본 발명의 성형체는 상기 생분해성 수지 조성물로 형성된 것을 특징으로 한다.
(생분해성 수지 조성물 및 생분해성 수지 조성물용 충전재)
본 발명의 생분해성 수지 조성물은 생분해성 수지와 이 생분해성 수지로 표면이 코팅된 충전재를 함유하여 이루어지며, 더욱 필요에 따라서 적절하게 선택한 그 밖의 성분 등을 함유하여 이루어진다.
본 발명의 생분해성 수지 조성물용 충전재는 상기 생분해성 수지로 표면이 코팅된 충전재이며, 상기 생분해성 수지 조성물의 설명 중에서 더불어 설명한다.
-생분해성 수지-
상기 생분해성 수지로서 특별히 제한하는 것은 없고, 공지된 것 중에서 적절하게 선택할 수 있으며, 천연물 유래의 것, 화학 합성된 것, 그 밖의 것 등을 들 수 있다. 이들은 1종 단독으로 사용하더라도 좋고, 2종 이상을 병용하더라도 좋다.
상기 천연물 유래의 것으로는 예컨대, 키틴·키토산, 알긴산, 글루텐, 콜라겐, 폴리아미노산, 박테리아 셀룰로오스, 풀루란, 카드런, 다당류계 부산물 등을 들 수 있다.
상기 화학 합성된 것으로는, 예컨대, 지방족 폴리에스테르, 지방족·방향족 폴리에스테르, 폴리비닐알코올(PVA), 폴리우레탄(PU), 천연물 유래의 생분해성 수지와 합성 생분해성 수지와의 블렌드 등을 들 수 있다.
상기 지방족 폴리에스테르로는 예컨대, 폴리히드록시부틸레이트(PHB)(-OCH2CH2CH2CO-)n, 폴리카프로락톤(PCL)[C6H10O2 ]n, 폴리부틸렌숙시네이트(PBS)(-COCH2CH2COO(CH2)4O-)n, 폴리부틸렌숙시네이트/아디페이트(PBSA)(-O(CH2)4OCO(CH2)aCO-)n 단 a=2,4, 폴리에틸렌숙시네이트(PES)(-O(CH2 )4OCO(CH2)2CO-)n, 폴리글리콜산(PGA), 폴리젖산(PLA)[C3H4O2]n, 및, 이들의 유도체, 이들의 모노머의 공중합체 등을 들 수 있다.
천연물 유래의 생분해성 수지와 합성 생분해성 수지와의 블렌드로는 전분을 기재로 하는 것 등을 들 수 있다.
상기 그 밖의 것으로는 예컨대, 지방족 폴리에스테르의 카보네이트 공중합체, 지방족 폴리에스테르와 폴리아미드와의 공중합체 등을 들 수 있다.
상기 생분해성 수지 중에서도 화학 합성된 것이 바람직하며, 그 중에서도 성형성·내열성·내충격성 등이 우수하다는 점에서 지방족 폴리에스테르 수지가 보다 바람직하고, 히드록시카르복실산을 모노머 단위로서 포함하는 폴리에스테르가 특히 바람직하다.
상기 히드록시카르복실산을 모노머 단위로서 포함하는 폴리에스테르로는 예컨대, 젖산, 사과산, 글루코스산 등의 옥시산의 중합체, 이들의 공중합체 등을 들 수 있다. 이들 중에서도 젖산을 모노머 단위로서 포함하는 수지가 특히 바람직하며, 폴리젖산이 가장 바람직하다.
상기 히드록시카르복실산을 모노머 단위로 포함하는 폴리에스테르의 제조 방 법으로는 특별히 제한은 없고, 목적에 따라서 적절하게 선택할 수 있지만, 예컨대, 환상 디에스테르인 락티드 및 대응하는 락톤류의 개환 중합에 의한 락티드법, 젖산 직접 탈수 축합법 등을 들 수 있다. 또한, 제조시에 사용하는 촉매로는 주석, 안티몬, 아연, 티탄, 철, 알루미늄 화합물 등을 들 수 있다. 이들은 1종 단독으로 사용하더라도 좋고, 2종 이상을 병용하더라도 좋다. 이들 중에서도 주석, 알루미늄 화합물 등이 바람직하며, 옥틸산주석, 알루미늄아세틸아세토네이트가 보다 바람직하다.
본 발명에 있어서는 상기 생분해성 수지를 2종 이상의 생분해성 수지의 조합으로 하는 경우, 폴리 젖산과, 폴리카프로락톤, 폴리히드록시부틸레이트 및 폴리부틸렌숙시네이트로부터 선택되는 적어도 1종과의 조합이 바람직하다.
-충전재-
상기 충전재로서는 특별히 제한은 없고, 공지의 것으로부터 목적에 따라서 적절하게 선택할 수 있는데, 예컨대, 수산화알루미늄, 알루미늄, 탄산석회, 규산석회, 카올린, 운모, 이황화몰리브덴, 탈크, 몬모릴로나이트, 그라피트, 카본블랙, 또한, 산화마그네슘, 산화티탄, 실리카 등의 금속 산화물 등을 들 수 있다.
이들은 1종 단독으로 사용하더라도 좋고, 2종 이상을 병용하더라도 좋다. 이들 중에서도 가격, 범용성, 강도 등의 점에서 운모, 탈크 및 몬모릴로나이트로부터 선택되는 것이 바람직하다.
상기 충전재의 상기 생분해성 수지 조성물에 있어서의 함유량으로는 5.0∼50.0 질량%인 것이 바람직하며, 5∼30 질량%인 것이 보다 바람직하며, 10∼20 질량%인 것이 특히 바람직하다.
상기 충전재의 함유량이 5.0 질량% 이상인 것은 상기 생분해성 수지 조성물의 기계적 강도의 관점에서 바람직하며, 한편, 50.0 질량% 이하인 것은 생분해성의 관점에서 바람직하다.
상기 충전재의 평균 입자 지름으로는 0.01∼200 μm이 바람직하며, 1∼50 μm이 보다 바람직하다.
또, 상기 충전재는 보다 미립자이며 입도 분포가 같은 것이 균일 분산성을 향상시키는 점에서 바람직하다.
본 발명에 있어서, 상기 충전재는 상기 생분해성 수지에 의해서 표면이 코팅되어 있고, 이 생분해성 수지로 표면이 코팅된 상기 충전재가 상기 생분해성 수지 중에 첨가되어 상기 생분해성 수지 조성물이 조제된다.
상기 생분해성 수지로 표면이 코팅된 상기 충전재가 본 발명의 생분해성 수지 조성물용 충전재이다.
본 발명의 생분해성 수지 조성물용 충전재에 있어서의 상기 생분해성 수지의 상기 충전재 표면에의 코팅량, 면적 등에 관해서는 특별히 제한은 없고, 목적에 따라서 적절하게 선택할 수 있다.
또, 본 발명의 생분해성 수지 조성물용 충전재를 생분해성 수지 조성물 중에 첨가하여 사용하는 경우에는, 이 생분해성 수지 조성물용 충전재에 있어서의 상기 생분해성 수지와 상기 생분해성 수지 조성물에 포함되는 상기 생분해성 수지 조성물과의 종류가 같은 계통인 것이면, 이 생분해성 수지 조성물용 충전재의 상술한 생분해성 수지 중에서의 분산성이 우수하여 결과적으로 굽힘 탄성률 등의 성능을 향상시킬 수 있는 점에서 바람직하며, 동일한 것이 그 효과가 현저하다는 점에서 특히 바람직하다.
본 발명의 생분해성 수지 조성물용 충전재는 본 발명의 생분해성 수지 조성물에 특히 적합하게 사용할 수 있다.
-난연 성분-
본 발명의 생분해성 수지 조성물은 난연 성분을 포함하고 있더라도 좋다.
상기 난연 성분으로는 특별히 제한하는 것은 없고, 목적에 따라서 적절하게 선택할 수 있어, 예컨대, 실리콘계 화합물, 금속염, 금속수산화염, 인계 화합물 등을 들 수 있다. 이들은 1종 단독으로 사용하더라도 좋고, 2종 이상을 병용하더라도 좋다.
상기 난연 성분의 상기 생분해성 수지 조성물에 있어서의 함유량으로는 특별히 제한하는 것은 없고, 상기 생분해성 수지, 상기 충전재 등의 종류·함유량 등에 따라서 적절하게 결정할 수 있다.
-섬유 성분-
본 발명의 생분해성 수지 조성물은 섬유 성분을 포함하고 있더라도 좋다.
상기 섬유 성분으로는 특별히 제한하는 것은 없고, 목적에 따라서 적절하게 선택할 수 있어, 예컨대, 마 섬유, 키틴·키토산, 야자곡 섬유, 및 이들로부터 유도된 단섬유 내지 분체, 석면, 카본 섬유, 유리 섬유, 셀룰로오스, α-셀룰로오스, 면, 나일론, 올론, 레이온 등을 들 수 있다.
이들은 1종 단독으로 사용하더라도 좋고, 2종 이상을 병용하더라도 좋다. 이들 중에서도 생물 유래로 생분해성을 나타내는 점에서 마 섬유, 키틴·키토산, 야자곡 섬유, 및 이들로부터 유도된 단섬유 내지 분체가 바람직하며, 또한, 굽힘 탄성률 향상의 관점에서는 유리 섬유, 카본 섬유가 바람직하다.
상기 섬유 성분의 상기 생분해성 수지 조성물에 있어서의 함유량으로서 특별히 제한하는 것은 없고, 상기 생분해성 수지, 상기 충전재 등의 종류·함유량 등에 따라서 적절하게 결정할 수 있다.
-첨가제-
본 발명의 생분해성 수지 조성물은 목적에 따라서 적절하게 선택한 첨가제를 함유할 수 있다.
상기 첨가제로는 예컨대, 상기 생분해성 수지의 가수분해를 억제시킬 수 있는 물질로서, 폴리에스테르 수지의 말단 관능기인 카르복실산, 및 카르보디이미드 화합물, 이소시아네이트 화합물, 옥시졸린계 화합물 등의 수산기와의 반응성을 갖는 화합물, 또한 내후성 개량제, 산화방지제, 열안정제, 자외선 흡수제, 가소제, 결정핵제, 윤활제, 이형제, 착색제, 상용화제 등을 들 수 있다.
본 발명의 생분해성 수지 조성물은 각종 분야에서 적합하게 사용할 수 있어, 각종 성형체, 예컨대 전기 제품의 광체 등에 특히 적합하게 사용할 수 있다.
(성형체)
본 발명의 성형체는 본 발명의 생분해성 수지 조성물을 이용하여 형성된 것 이외에는 특별히 제한은 없고, 그 형상, 구조, 크기, 용도 등에 관해서는 목적에 따라서 적절하게 선택할 수 있다.
상기 성형체의 성형 방법으로는 특별히 제한하는 것은 없고, 공지의 방법으로부터 적절하게 선택되지만, 폴리젖산의 결정화도를 올려 강도를 향상시키는 점에서 사출 성형이 바람직하다. 상기 사출 성형의 조건으로는 금형의 온도를 90∼100℃로 30초∼5분 정도 유지하는 것이 바람직하다.
본 발명의 성형체는 각종 분야에서 적합하게 사용할 수 있어, 예컨대, 전기 제품의 광체 등에 특히 적합하게 사용할 수 있다.
이하, 본 발명의 실시예를 구체적으로 설명하지만, 본 발명은 이들 실시예에 하등 한정되는 것이 아니다.
[실시예]
실시예 1
-생분해성 수지 조성물의 조제-
본 발명의 생분해성 수지 조성물 E∼G 및 L∼N, 및, 비교예의 조성물 A∼D 및 H∼K를 조제하여, 각 굽힘 탄성률을 평가했다. 결과를 표 1에 나타냈다.
또, 생분해성 수지로는 폴리젖산(미츠이 가가쿠 제조, 레이시아 H-100 J)을 이용했다. 또한, 충전재의 조성물 전체에 있어서의 함유량은 각 조성물에서 같아지도록 했다. 표 중의 「%」는 「질량%」을 의미하고, 「A」 등의 알파벳은 생분해성 수지 조성물 A 등을 의미하고, 「폴리부틸렌숙시네이트」는 쇼와고분자 제조(비오놀레)이다. 또한, E∼G 및 L∼N에서의 각 충전재는 표면이 폴리젖산으로 코팅된 것이다.
수지 충전재 굽힘 탄성률
(GPa)
A 폴리젖산 없음 3.7
B 폴리젖산 운모(30% 첨가, 야마구찌운모 고교 제조 A-21) 8.0
C 폴리젖산 탈크(30% 첨가, 하야시카세이 제조) 6.7
D 폴리젖산 몬모릴로나이트(30% 첨가) 5.3
E 폴리젖산 운모(40% 첨가, 폴리젖산코팅) 10.0
F 폴리젖산 탈크(40% 첨가, 폴리젖산코팅) 8.1
G 폴리젖산 몬모릴로나이트(40% 첨가, 폴리젖산코팅) 6.3
H 폴리젖산+
폴리부틸렌숙시네이트(1:1)
없음 1.96
I 폴리젖산+
폴리부틸렌숙시네이트(1:1)
운모(30% 첨가, 야마구찌운모 고교 제조 A-21) 5.6
J 폴리젖산+
폴리부틸렌숙시네이트(1:1)
탈크(30% 첨가, 하야시카세이 제조) 4.3
K 폴리젖산+
폴리부틸렌숙시네이트(1:1)
몬모릴로나이트(30% 첨가) 3.3
L 폴리젖산+
폴리부틸렌숙시네이트(1:1)
운모(40% 첨가, 폴리젖산코팅) 7.2
M 폴리젖산+
폴리부틸렌숙시네이트(1:1)
탈크(40% 첨가, 폴리젖산코팅) 5.7
L 폴리젖산+
폴리부틸렌숙시네이트(1:1)
몬모릴로나이트(40% 첨가, 폴리젖산코팅) 4.0
이상과 같이, 생분해성 수지로 코팅한 운모, 탈크 또는 몬모릴로나이트, 즉 본 발명의 생분해성 수지용 충전재를 함유하는 본 발명의 생분해성 수지 조성물은 표면이 생분해성 수지로 코팅되어 있지 않은 운모, 탈크, 몬모릴로나이트 등의 종래의 충전재에 비하여 생분해성 수지 조성물 중에서의 분산성이 매우 양호하며, 이 생분해성 수지 조성물의 굽힘 탄성률을 크게 향상시킬 수 있다는 것을 알았다.
실시예 2
실시예 1에 있어서, 양호한 굽힘 탄성률이 얻어진 본 발명의 생분해성 수지 조성물 E∼G와, 비교예의 수지 조성물 A에 관해서, 유리 섬유(닛토 방적 제조, CS-3PE941) 또는 카본 섬유(미츠비시 레이온 제조, TR-06U)를 첨가하여, 각 굽힘 탄성률을 평가했다. 결과를 표 2에 나타냈다. 또, 표 2 중의 「%」는 「질량%」을 의미한다.
섬유 성분(20%) 굽힘 탄성률(GPa)
A 유리섬유 6.8
E 유리섬유 12.8
F 유리섬유 10.1
G 유리섬유 8.9
A 카본섬유 14.7
E 카본섬유 18.8
F 카본섬유 16.3
G 카본섬유 15.0

이상과 같이, 본 발명의 생분해성 수지 조성물에 유리 섬유 또는 카본 섬유를 첨가하면 굽힘 탄성률을 현저히 향상시킬 수 있다는 것이 알았다.
실시예 3
실시예 1에 있어서, 양호한 굽힘 탄성률이 얻어진 본 발명의 생분해성 수지 조성물 E∼G와, 비교예의 수지 조성물 A에 관해서, 난연제로서 실리콘계 화합물 DC4-7081(다우 코닝 토레이 실리콘 제조), 수산화마그네슘 또는 붉은인을 첨가하여 불꽃 분리 후의 상황, 거즈에의 착화 상황에 기초하여 난연성을 평가했다. 시험편은 성형기에 의해 12.7 ×12.7 ×3.1(mm)의 사이즈로 작성했다. 또, 표 3 중의 「%」는 「질량%」을 의미한다.
상기 불꽃 분리 후의 상황은 이하와 같이 하여 평가했다.
계속 탄다···불꽃이 있거나 또는 불꽃이 없는 연소인 상태
꺼진다···완전히 실화되어 있는 상태
상기 거즈에의 착화 상황은 이하와 같이 하여 평가했다.
착화한다···불꽃이 있는 연소하는 상태
착화하지 않는다···연소하지 않는 상태
난연제 불꽃 분리후의
상황
거즈로의 착화 상황
A 없음 계속해서 탄타 착화한다
A 실리콘계 화합물(5%) 계속해서 탄다 착화한다
E 실리콘계 화합물(5%) 꺼진다 착화하지않는다
E 수산화마그네슘(30%) 꺼진다 착화하지않는다
E 붉은인(10%) 꺼진다 착화하지않는다
F 실리콘계 화합물(5%) 꺼진다 착화하지않는다
F 수산화마그네슘(30%) 꺼진다 착화하지않는다
F 붉은인(10%) 꺼진다 착화하지않는다
G 실리콘계 화합물(5%) 꺼진다 착화하지않는다
G 수산화마그네슘(30%) 꺼진다 착화하지않는다
G 붉은인(10%) 꺼진다 착화하지않는다

이상과 같이, 본 발명의 생분해성 수지 조성물에 난연제를 첨가하면 다른 특성을 열화시키지 않고서 난연성을 향상시킬 수 있다는 것을 알았다.
본 발명에 의하면, 종래에 있어서의 문제를 해결할 수 있어, 강도, 내수성, 성형 가공성, 내열성 등의 성능이 우수하며, 또한 폐기시에는 자연계에 일반적으로 존재하는 미생물에 의해서 조속히 분해 가능하고, 각종 분야에서의 성형체에 적합한 생분해성 수지 조성물 및 이 생분해성 수지 생물에 적합하게 사용할 수 있으므로, 분산성이 우수한 생분해성 수지 조성물용 충전재, 및 각종 전기 제품 등의 광 체 등으로서 적합하게 이용되어, 환경 문제를 생기는 일없이 용이하게 폐기 처분이 가능한 성형체를 제공할 수 있다.

Claims (20)

  1. 생분해성 수지와 이 생분해성 수지로 표면이 코팅된 충전재를 함유하는 것을 특징으로 하는 생분해성 수지 조성물.
  2. 제1항에 있어서, 충전재가 운모, 탈크 및 몬모릴로나이트로부터 선택되는 적어도 1종인 생분해성 수지 조성물.
  3. 제1항 또는 제2항에 있어서, 충전재의 함유량이 5.0∼50.0 질량%인 생분해성 수지 조성물.
  4. 제1항 또는 제2항에 있어서, 충전재의 평균 입자 지름이 0.01∼200 μm인 생분해성 수지 조성물.
  5. 제1항 또는 제2항에 있어서, 생분해성 수지가 지방족 폴리에스테르 수지인 생분해성 수지 조성물.
  6. 제5항에 있어서, 지방족 폴리에스테르 수지가 폴리젖산인 생분해성 수지 조성물.
  7. 제1항 또는 제2항에 있어서, 실리콘계 화합물, 금속염, 금속수산화염 및 인계 화합물로부터 선택되는 적어도 1종의 난연 성분을 함유하는 생분해성 수지 조성물.
  8. 제1항 또는 제2항에 있어서, 유리 섬유, 카본 섬유의 적어도 1종의 섬유 성분을 함유하는 생분해성 수지 조성물.
  9. 충전재의 표면이 생분해성 수지로 코팅되어 이루어지는 것을 특징으로 하는 생분해성 수지 조성물용 충전재.
  10. 제1항에 기재한 생분해성 수지 조성물로 형성된 것을 특징으로 하는 성형체.
  11. 삭제
  12. 삭제
  13. 삭제
  14. 삭제
  15. 삭제
  16. 삭제
  17. 삭제
  18. 삭제
  19. 삭제
  20. 삭제
KR1020030053034A 2002-08-13 2003-07-31 생분해성 수지 조성물 및 생분해성 수지 조성물용 충전재및 성형체 KR100963860B1 (ko)