JP6950778B2 - 複合体及びその製造方法 - Google Patents
複合体及びその製造方法 Download PDFInfo
- Publication number
- JP6950778B2 JP6950778B2 JP2020066351A JP2020066351A JP6950778B2 JP 6950778 B2 JP6950778 B2 JP 6950778B2 JP 2020066351 A JP2020066351 A JP 2020066351A JP 2020066351 A JP2020066351 A JP 2020066351A JP 6950778 B2 JP6950778 B2 JP 6950778B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- sheet
- coating
- coating layer
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明はまた、高強度で透明性の高い複合体、また、微細セルロース繊維を主成分とするシート(シート層)と、硬化性樹脂層又はフィルム層との密着性の高い複合体、微細セルロース繊維を主成分とするシート(シート層)と、被覆層との密着性の高い張り合わせ用シートを提供することを解決すべき課題とした。
詳細には、本発明者らは上記の課題を解決するために鋭意検討した。その結果、1)平均繊維幅2〜1000nmの微細繊維を主成分とするシート(以下、「シート層」という。)の片面又は両面に硬化性樹脂層又はフィルム層が積層された複合体は高強度で高透明であることを見出した。また、2)平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に被覆層を介して硬化性樹脂層又はフィルム層が積層された複合体、3)平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に被覆層が積層された張り合わせ用シートは、各層間の密着性が高く、高強度で高透明であることを見出し、本発明を完成するに至った。
(1)平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に、硬化性樹脂層又はフィルム層を有する複合体。
(2)微細繊維の平均繊維幅が2〜100nmである、(1)に記載の複合体。
(3)シート層の密度が0.90g/cm3以上である、(1)又は(2)に記載の複合体。
(4)シート層が不織布である(1)から(3)の何れか1項に記載の複合体。
(5)微細繊維が、セルロース繊維を含む繊維である、(1)から(4)の何れか1項に記載の複合体。
(6)シート層の片面又は両面に設けられた被覆層を介して、硬化性樹脂層又はフィルム層が積層された、(1)から(5)の何れか1項に記載の複合体。
(7)シート層の厚さが2〜150μmであり、被覆層の厚さが0.1〜30μmであり、硬化性樹脂層又はフィルム層の厚さが0.2〜100μmである、(6)に記載の複合体。
(8)シート層と、硬化性樹脂層又はフィルム層の密着性が、JIS規格K5400に準拠したクロスカット試験において100マス中のはく離数が10以下である、(6)又は(7)に記載の複合体。
(9)全光線透過率が85%以上であり、ヘーズが10%以下である、(6)から(8)の何れか1項に記載の複合体。
(10)被覆層が、有機成分と無機成分のハイブリッド材である、(6)から(9)の何れか1項に記載の複合体。
(11)有機成分と無機成分のハイブリッド材が、ケイ素骨格を有する有機成分と無機成分から構成される、(10)に記載の複合体。
(12)有機成分がメチル基、メルカプト基、メタクリル基、アクリロイル基、ビニル基、及びアミノ基から選ばれる少なくとも1種を含む成分である、(10)又は(11)に記載の複合体。
(13)有機成分と無機成分のハイブリッド材が、シルセスキオキサンである、(10)から(12)の何れか1項に記載の複合体。
(14)被覆層が、熱硬化性樹脂、熱可塑性樹脂、及び光硬化性樹脂の中から選ばれる少なくとも1種である、(6)から(9)の何れか1項に記載の複合体。
(15)被覆層が粘着剤である、(6)から(9)の何れか1項に記載の複合体。
(16)平均繊維幅2〜1000nmのセルロース微細繊維を主成分とするシート層の片面又は両面に、被覆層を有する貼り合わせ用シート。
(17)被覆層が、有機成分と無機成分のハイブリッド材である(16)に記載のシート。
(18)有機成分がメチル基、メルカプト基、メタクリル基、アクリロイル基、ビニル基、及びアミノ基から選ばれる少なくとも1種を含む成分である、(17)に記載のシート。
(19)有機成分と無機成分のハイブリッド材が、シルセスキオキサンである、(17)又は(18)に記載のシート。
(20)(16)〜(19)のシートに、硬化性樹脂層又はフィルム層を積層した複合体。
(21)平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に、被覆層を設ける工程;及び前記被覆層の、シート層とは反対側の表面上に、硬化性樹脂層又はフィルム層を設ける工程、を含む、複合体の製造方法。
(22)シート層と被覆層が、塗工、又は貼り合わせにより積層された、(21)に記載の複合体の製造方法。
(23)被覆層と、硬化性樹脂層又はフィルム層が、塗工、又は貼り合わせにより積層された、(21)に記載の複合体の製造方法。
(24)(1)から(20)の何れか1項に記載の複合体を含む、照明装置、投影装置、看板又は画像表示装置、タッチパネル又は太陽電池。
[2]微細繊維の平均繊維幅が2〜100nmである、[1]に記載の不織布樹脂複合体。
[3]不織布層の密度が0.90g/cm3以上である、[1]又は[2]に記載の不織布樹脂複合体。
[4]不織布層の厚さが2〜150μmであり、易接着性層の厚さが0.1〜30μmであり、樹脂層の厚さが0.2〜50μmである、[1]から[3]の何れかに記載の不織布樹脂複合体。
[5]樹脂層の密着性が、JIS規格K5400に準拠したクロスカット試験において100マス中のはく離数が10以下である、[1]から[4]の何れかに記載の不織布樹脂複合体。
[6]全光線透過率が85%以上であり、ヘーズが10%以下である[1]から[5]の何れかに記載の不織布樹脂複合体。
[7]易接着性層が、樹脂からなる、[1]から[6]の何れかに記載の不織布樹脂複合体。
[8]易接着性層が、ポリエステル樹脂又はシルセスキオキサン系樹脂からなる、[1]から[7]の何れかに記載の不織布樹脂複合体。
[9]樹脂層が、硬化性樹脂前駆体を紫外線処理又は熱処理によって硬化することにより得た樹脂層である、[1]から[8]の何れかに記載の不織布樹脂複合体。
[10]微細繊維が、セルロース繊維を含む繊維である、[1]から[9]の何れかに記載の不織布樹脂複合体。
[11]繊維原料を化学的処理及び解繊処理することにより得た平均繊維幅2〜1000nmの微細繊維を含有する不織布層の片面又は両面に、易接着性層を設ける工程;及び
前記易接着性層の、不織布層とは反対側の表面上に、樹脂層を設ける工程、
を含む、[1]から[10]の何れかに記載の不織布樹脂複合体の製造方法。
[12][1]から[10]の何れかに記載の不織布樹脂複合体を含む、照明装置、投影装置、看板又は画像表示装置、タッチパネル又は太陽電池。
2 被覆層
3 硬化性樹脂層又はフィルム層
本発明におけるシート層は、平均繊維幅2〜1000nmの微細繊維を主成分とする。微細繊維は、平均繊維幅が2〜1000nmの微細繊維であればその種類は特に限定されず、微細セルロース繊維でもよいし、微細セルロース繊維以外の微細繊維でもよく、微細セルロース繊維と、微細セルロース繊維以外の微細繊維との混合物でもよい。好ましくは、微細繊維はセルロース繊維である。
本発明においては、微細繊維として、セルロース原料を化学的処理及び解繊処理することによって得られる微細セルロース繊維を使用してもよい。
セルロース原料としては、製紙用パルプ、コットンリンターやコットンリントなどの綿系パルプ、麻、麦わら、パガスなどの非木材系パルプ、ホヤや海草などから単離されるセルロースなどが挙げられるが、特に限定されない。これらの中でも、入手のしやすさという点で、製紙用パルプが好ましいが、特に限定されない。製紙用パルプとしては、化学パルプ、半化学パルプ、機械パルプ、非木材パルプ、及び脱墨パルプが挙げられるが、特に限定されない。化学パルプとしては、広葉樹クラフトパルプ、針葉樹クラフトパルプ、サルファイトパルプ(SP)、ソーダパルプ(AP)等を挙げることができる。ここで広葉樹クラフトパルプとしては、晒クラフトパルプ(LBKP)、未晒クラフトパルプ(LUKP)、酸素漂白クラフトパルプ(LOKP)などが挙げられる。また針葉樹クラフトパルプとしては、晒クラフトパルプ(NBKP)、未晒クラフトパルプ(NUKP)、酸素漂白クラフトパルプ(NOKP)などが挙げられる。半化学パルプとしては、セミケミカルパルプ(SCP)、ケミグラウンドウッドパルプ(CGP)等が挙げられる。機械パルプとしては、砕木パルプ(GP)、サーモメカニカルパルプ(TMP、BCTMP)等を挙げられる。非木材パルプとしては、楮、三椏、麻、ケナフ等を原料とする非木材パルプが挙げられる。脱墨パルプとしては、古紙を原料とする脱墨パルプが挙げられる。これらの中でも、より入手しやすいことから、クラフトパルプ、脱墨パルプ、サルファイトパルプが好ましいが、特に限定されない。セルロース原料は1種を単独で用いてもよいし、2種以上混合して用いてもよい。
(2)同じ画像内で該直線と垂直に交差する直線Yを引き、該直線Yに対し、20本以上の繊維が交差する。
セルロース原料又はその他の繊維原料(無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維など)の化学的処理の方法は、微細繊維を得ることができる方法である限り特に限定されない。処理の方法は、例えば、オゾン処理、TEMPO酸化処理、酵素処理、又はセルロース又は繊維原料中の官能基と共有結合を形成し得る化合物による処理などが挙げられるがこれらに限定されない。
(1)特開2011−162608に記載されている四級アンモニウム基を有する化合物による処理;
(2)特開2013−136859(特開2013−136859の内容は全て本明細書中に引用される)に記載されているカルボン酸系化合物を使用する方法;並びに
(3)国際公開WO2013/73652(WO2013/73652の内容は全て本明細書中に引用される)に記載されている「構造中にリン原子を含有するオキソ酸、ポリオキソ酸又はそれらの塩から選ばれる少なくとも1種の化合物」を使用する方法:
セルロース原料又はその他の繊維原料(無機繊維、有機繊維、合成繊維等、半合成繊維、再生繊維など)は解繊処理に供することにより微細化して、数平均繊維幅が2〜1000nmである微細繊維を得ることができる。解繊処理工程では、解繊処理装置を用いて、前記の化学的処理で得られた原料を解繊処理して、微細繊維分散液を得ることができる。
本発明におけるシート層の密度は、特に限定されないが、好ましくは0.90g/cm3以上であり、より好ましくは1.00g/cm3以上であり、さらに好ましくは1.10g/cm3以上である。シート層の密度の上限は、特に限定されないが、一般的には、1.60g/cm3以下である。
なお、シート層は、目的に応じて複数のシート層を積層したものでもよい。複数のシート層を使用する場合は、複数のシート層の合計の厚み並びに合計の密度が、上記した範囲内であることが好ましい。
シート層の形成に際して、微細繊維を含む懸濁液を調製する。この懸濁液には、親水性高分子を添加してもよい。親水性高分子としては、例えば、ポリエチレングリコール、セルロース誘導体(ヒドロキシエチルセルロース,カルボキシエチルセルロース,カルボキシメチルセルロース等)、カゼイン、デキストリン、澱粉、変性澱粉、ポリビニルアルコール、変性ポリビニルアルコール(アセトアセチル化ポリビニルアルコール等)、ポリエチレンオキサイド、ポリビニルピロリドン、ポリビニルメチルエーテル、ポリアクリル酸塩類、ポリアクリルアミド、アクリル酸アルキルエステル共重合体、ウレタン系共重合体などを挙げることができるが、特に限定されない。
被覆層を構成する成分は、特に限定されず、無機成分と有機成分のハイブリッド材、熱硬化性樹脂、光硬化性樹脂、熱可塑性樹脂などを用いることができる。前記樹脂としては、ポリエステル系樹脂、ウレタン系樹脂、アクリル系樹脂、オレフィン系樹脂、フッ素系樹脂、塩化ビニル系樹脂、スチレン系樹脂、エポキシ系樹脂、シリコーン系樹脂、等が挙げられる。被覆層を構成する成分は、無機成分と有機成分のハイブリッド材を用いることが好ましい。前記、無機成分と有機成分のハイブリッド材、又は樹脂は、1種を単独で使用してもよいし、2種以上を併用してもよい。無機成分と有機成分のハイブリッド材と樹脂を併用することもできる。また、被覆層として、粘着剤、粘着シートなどを用いることもできる。
被覆層は、2層以上とすることもできる。複数の被覆層とする場合は、複数の被覆層の合計の厚みが、上記の範囲内であることが好ましい。
硬化性樹脂層又はフィルム層を構成する成分としては、特に限定されないが、熱可塑性樹脂、熱硬化性樹脂、光硬化性樹脂などを用いることができる。硬化性樹脂層又はフィルム層を構成する成分は、湿度、水、熱、ガスなどに対してバリア能を有する成分を用いることが望ましい。硬化性樹脂層又はフィルム層は、少なくとも2層以上積層することもできる。
なお、上記の熱可塑性樹脂、熱硬化性樹脂及び光硬化性樹脂のうち、光硬化性樹脂が
最も好ましい。
また、塗布により被覆層を介してシート層に硬化性樹脂層又はフィルム層を接着させる場合、シート層に被覆層を塗工した後、被覆層に上記と同様の方法により硬化性樹脂層又はフィルム層を形成させることができる。
被覆層として、粘着剤、粘着剤と剥離シートから構成される粘着剤(使用時に粘着剤をカバーしている剥離シートを剥がし粘着剤を使用する。(例)商品名:ノンキャリアテープ)、粘着シートなどを用いてシート層と硬化性樹脂層又はフィルム層を貼合わせることもできる。
硬化性樹脂層又はフィルム層は、目的に応じて複数の硬化性樹脂層又はフィルム層を積層したものでもよい。複数の硬化性樹脂層又はフィルム層を使用する場合は、複数の硬化性樹脂層又はフィルム層の合計の厚みが、上記の範囲内であることが好ましい。
本発明の複合体は、1)シート層に硬化性樹脂層又はフィルム層が積層された複合体(2層)、2)シート層と、硬化性樹脂層又はフィルム層が、被覆層を介して積層された複合体(3層)、3)シート層に被覆層が積層された張り合わせ用シート(2層)である。
1)シート層に硬化性樹脂層又はフィルム層が積層された複合体(2層)は、高強度で高透明であるという特徴を有する。2)シート層と、硬化性樹脂層又はフィルム層が、被覆層を介して積層された複合体(3層)は、高強度で高透明であり、シート層と、硬化性樹脂層又はフィルム層の密着性が高いという特徴を有する。3)シート層に被覆層が積層された張り合わせ用シート(2層)は、高強度で高透明であり、シート層と被覆層の密着性が高いという特徴を有する。
前記複合体、及び張り合わせ用シートの各層間の密着性は、以下の実験例に記載したJIS規格K5400に準拠したクロスカット試験において100マス中のはく離数が10以下であることが好ましく、より好ましくは5以下であり、さらに好ましくは3以下である。
また、本発明の複合体、及び張り合わせ用シートは透明性が高いことを特徴とする。本発明の複合体の全光線透過率は、好ましくは70%以上であり、より好ましくは80%以上であり、さらに好ましくは85%以上であり、さらに好ましくは90%以上である。全光線透過率の上限は特に限定されず、100%でもよいし、99%以下でもよい。本発明の複合体のヘーズは、好ましくは10%以下であり、より好ましくは5%以下であり、さらに好ましくは3%以下である。
本発明の複合体、及び張り合わせ用シートは、液晶ディスプレイ、プラズマディスプレイ、有機ELディスプレイ、フィールドエミッションディスプレイ、リアプロジェクションテレビ等の画像表示装置等に用いることができる。さらに本発明の複合体は、照明装置、投影装置に用いることもできる。さらに本発明の複合体、及び張り合わせ用シートは、タッチパネルや太陽電池(シリコン系太陽電池、色素増感太陽電池など)の配線基板や前面板、カラーフィルター基板等に用いることができる。基板としての用途において、バリア膜、ITO、TFT等と積層してもよい。
(1)シート層(A)(不織布層(A)ということもある。)の成膜
シートとして不織布を用いて下記の方法でシート層(不織布層)を作製した。
リン酸二水素ナトリウム二水和物265g、及びリン酸水素二ナトリウム197gを538gの水に溶解させ、リン酸系化合物の水溶液(以下、「リン酸化試薬」という。)を得た。
ポリエステル系樹脂であるUVコートアンカー剤(荒川化学工業社製アラコートAP2510、固形分30質量%)76重量部、硬化剤(荒川化学工業社製アラコートCL2502、固形分20質量%)10重量部及びメチルエチルケトン14重量部を混合し、易接着性塗工液を得た。次いで、不織布層(A)の片面に易接着性塗工液をメイヤーバーを用いて塗工した。その後、100℃で3分間乾燥して易接着性塗工液を硬化し、厚さ1μmの被覆層(B)を成膜した。以上の手順により、不織布層(A)と被覆層(B)から構成される複合体を得た。
アクリル樹脂組成物(荒川化学工業社製「ビームセット381」)80重量部、及びメチルエチルケトン20重量部を混合して、硬化性樹脂前駆体溶液を得た。不織布層(A)・被覆層(B)複合体の被覆層(B)の上に上記の硬化性樹脂前駆体溶液をメイヤーバーを用いて塗工した。次いでUVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、硬化性樹脂前駆体溶液を硬化し、厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の片面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
(1)被覆層(B)の成膜
実験例1の(2)において、不織布層(A)の片面に被覆層(B)を成膜した後、反対側の面にも同様の手順で厚さ1.0μmの被覆層(B)を成膜し、不織布層(A)と被覆層(B)から構成される複合体を得た。
不織布層(A)と被覆層(B)から構成される複合体の片面に実験例1の(3)と同様の手順で2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
ウレタンアクリレート樹脂組成物(荒川化学工業社製「ビームセット575CB」)50重量部、及びメチルエチルケトン50重量部を混合して、硬化性樹脂前駆体溶液を得た。 実験例2の(1)において得た不織布層(A)と被覆層(B)から構成される複合体の片面に、上記の硬化性樹脂前駆体溶液をメイヤーバーを用いて塗工した。次いで80℃で3分間乾燥した後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、硬化性樹脂前駆体溶液を硬化し、厚さ2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
アクリル樹脂組成物(アデカ社製「アデカオプトマー HC500−60」)40重量部、及びメチルエチルケトン60重量部を混合して、硬化性樹脂前駆体溶液を得た。実施例2の(1)において得た不織布層(A)と被覆層(B)から構成される複合体の片面に、上記の硬化性樹脂前駆体溶液をメイヤーバーを用いて塗工した。次いで100℃で2分間乾燥した後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、硬化性樹脂前駆体溶液を硬化し、厚さ2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例4において、不織布層(A)の厚さを50μm(密度1.47g/cm3)とした。上記以外は実験例4と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例4において、不織布層(A)の厚さを75μm(密度1.46g/cm3)とした。上記以外は実験例4と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例6において、不織布層(A)と被覆層(B)から構成される複合体の両面に成膜する樹脂層(C)の厚さを10μmとした。上記以外は実験例6と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例6において、不織布層(A)と被覆層(B)から構成される複合体の両面に成膜する樹脂層(C)の厚さを20μmとした。上記以外は実験例6と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
(1)被覆層(B)の成膜
シルセスキオキサン(荒川化学工業社製「コンポセランSQ107」)26重量部、硬化剤(荒川化学工業社製「HBSQ201」)14重量部、イソプロピルアルコール60重量部を混合し、接着性塗工液を得た。次いで、実験例1の(1)で得られた不織布層(A)の片面に接着性塗工液をメイヤーバーを用いて塗工した。その後、100℃で3分間乾燥した後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、接着性塗工液を硬化し、厚さ2.5μmの被覆層(B)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの被覆層を成膜した。以上の手順により、不織布層(A)と被覆層(B)から構成される複合体を得た。
アクリル樹脂組成物(アデカ社製「アデカオプトマー HC500−60」)40重量部、及びメチルエチルケトン60重量部を混合して、硬化性樹脂前駆体溶液を得た。不織布層(A)と被覆層(B)から構成される複合体の片面に、上記の硬化性樹脂前駆体溶液をメイヤーバーを用いて塗工した。次いで100℃で2分間乾燥した後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、硬化性樹脂前駆体溶液を硬化し、厚さ2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例9において、不織布層(A)の両面に成膜する被覆層(B)の厚さを5.0μmとし、また不織布層(A)と被覆層(B)から構成される複合体の両面に成膜する樹脂層(C)の厚さを10μmとした。上記以外は実験例9と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例10において、不織布層(A)の厚さを130μm(密度1.42g/cm3)とした。上記以外は実験例10と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例11において、不織布層(A)と被覆層(B)から構成される複合体の両面に成膜する樹脂層(C)の厚さを40μmとした。なお、樹脂層(C)の成膜においては、硬化性樹脂前駆体溶液の塗工量を増やし、所定の膜厚とするため、フィルムアプリケーターを用いて塗工を行った。上記以外は実験例11と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例12において、不織布層(A)の両面に成膜する被覆層(B)の厚さ25μmとした。なお、被覆層(B)、及び樹脂層(C)の成膜においては、易接着性塗工液、及び硬化性樹脂前駆体溶液の塗工量を増やし、所定の膜厚とするため、フィルムアプリケーターを用いて塗工を行った。上記以外は実験例12と同様の手順で、不織布層(A)の両面に被覆層(B)を介して樹脂層(C)が積層された複合体を得た。
実験例1の(1)で得られた不織布層(A)の片面に、実験例1の(3)と同様の手順で2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に樹脂層(C)が直接積層された複合体を得た。
実験例1の(1)で得られた不織布層(A)の片面に、アクリル樹脂組成物(アデカ社製「アデカオプトマー HC500−60」)40重量部、及びメチルエチルケトン60重量部を混合して得た硬化性樹脂前駆体溶液をメイヤーバーを用いて塗工した。次いで100℃で2分間乾燥した後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いて300mJ/cm2の紫外線を照射して、硬化性樹脂前駆体溶液を硬化し、厚さ2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に樹脂層(C)が直接積層された複合体を得た。
実験例1の(1)において、ポリエチレングリコール(和光純薬社製:分子量4000000)を微細繊維状セルロース100質量部に対し、150質量部になるように添加した以外は実験例1の(1)と同様にして不織布層(A)を得た(不織布層に含まれる微細繊維状セルロースの含有量は、40質量%)。次いで、実験例1の(3)と同様の手順で2.5μmの樹脂層(C)を成膜した。さらに、反対側の面にも同様の手順で厚さ2.5μmの樹脂層(C)を成膜した。以上の手順により、不織布層(A)の両面に樹脂層(C)が直接積層された複合体を得た。
前記の実験例で作製した複合体について以下の評価方法に従って評価した。上記の評価結果を表1に示す。
JIS規格K5400に準拠し、複合体の面に1mm2のクロスカットを100個入れ、セロハンテープ(ニチバン社製)をその上に貼り付け、1.5kg/cm2の荷重で押し付けた後、90°方向にはく離した。はく離したマス数により、不織布層(A)と樹脂層(C)の密着性を評価した。
(2)複合体の全光線透過率
JIS規格K7105に準拠し、ヘーズメータ(スガ試験機社製「HM−150」)を用いてC光による全光線透過率を測定した。
(3)複合体のヘーズ
JIS規格K7136に準拠し、ヘーズメータ(スガ試験機社製「HM−150」)を用いてC光によるヘーズ値を測定した。
(4)引張弾性率
JIS規格P8113に準拠し、引張試験機(L&W社製「フラクチャータフネステスターSE−064」)を用いて引張弾性率を測定した。
実験例1において、不織布層(A)に被覆層(B)を成膜し、樹脂層(C)を成膜しない複合体を作製した。すなわち、不織布層(A)と被覆層(B)の2層から構成される張り合わせ用シート(複合体)を作製した。不織布層(A)と被覆層(B)の密着性について評価した。それ以外は全て実験例1と同様の方法で試験した。結果を表2に示す。
実験例17において、不織布層の片面に被覆層を成膜した後、不織布層の反対側の面にも同様の手順で厚さ1.0μmの被覆層を成膜した以外は全て実験例17と同様の方法で試験した。結果を表2に示す。
実験例1で作製した複合体の割れ易さについて下記の方法で評価した(以下、「割れ性の評価」という。)。結果を表3に示す。
複合体(縦10cm x 横10cm)を手で折り曲げ、不織布複合体に亀裂が生じるかかどうかを目視で下記の基準で評価した。
○:亀裂が生じなかった。
×:亀裂が生じた
実験例2で作製した複合体の割れ易さについて実験例19と同様の方法で評価した。結果を表3に示す。
実験例1において、被覆層としてポリエステル系樹脂の代わりにシルセスキオキサン(荒川化学工業社製「コンポセランSQ107」)を用いた以外は全て実験例1と同様の方法で試験した。作製した複合体の割れ易さについて実験例19と同様の方法で評価した。結果を表3に示す。
実験例2において、被覆層としてポリエステル系樹脂の代わりにシルセスキオキサン(荒川化学工業社製「コンポセランSQ107」)を用いた以外は全て実験例2と同様の方法で試験した。作製した複合体の割れ易さについて実験例19と同様の方法で評価した。結果を表3に示す。
実験例1で得られた不織布層(A)に対し、被覆層(B)としてアフターUV型粘着剤(新タック化成製「DC011」、厚さ25μm)を貼合した。さらに、被覆層(B)の上面にフィルム層(C)としてPETフィルム(東レ製「ルミラーS10」、厚さ25μm)を貼合した。その後、UVコンベア装置(アイグラフィックス社製「ECS−4011GX」)を用いてフィルム層(C)側から250mJ/cm2の紫外線を6回照射して、被覆層(B)を硬化させた。以上の手順により、不織布層(A)の片面に被覆層(B)を介してフィルム層(C)が積層された複合体を得た。結果を表4に示す。
実験例23において、シート層(A)の片面に被覆層(B)、及びフィルム層(C)を積層した後、反対側の面にも同様の手順で被覆層(B)、及びフィルム層(C)を積層した。以上の手順により、シート層(A)の両面に被覆層(B)を介してフィルム層(C)が積層された複合体を得た。結果を表4に示す。
Claims (23)
- 平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に、硬化性樹脂層又はフィルム層を有する複合体であって、シート層が親水性高分子または親水性低分子化合物を含み、シート層の密度が0.90g/cm3以上1.60g/cm 3 以下である、複合体。
- 微細繊維の平均繊維幅が2〜100nmである、請求項1に記載の複合体。
- シート層が不織布である、請求項1又は2に記載の複合体。
- 微細繊維が、セルロース繊維を含む繊維である、請求項1から3の何れか1項に記載の複合体。
- シート層の片面又は両面に設けられた被覆層を介して、硬化性樹脂層又はフィルム層が積層された、請求項1から4の何れか1項に記載の複合体。
- シート層の厚さが2〜150μmであり、被覆層の一層当たりの厚さが0.1〜30μmであり、硬化性樹脂層又はフィルム層の一層当たりの厚さが0.2〜100μmである、請求項5に記載の複合体。
- シート層と、硬化性樹脂層又はフィルム層の密着性が、JIS規格K5400に準拠したクロスカット試験において100マス中のはく離数が10以下である、請求項5又は6に記載の複合体。
- 全光線透過率が85%以上であり、ヘーズが10%以下である、請求項5から7の何れか1項に記載の複合体。
- 被覆層が、有機成分と無機成分のハイブリッド材である、請求項5から8の何れか1項に記載の複合体。
- 有機成分と無機成分のハイブリッド材が、ケイ素骨格を有する有機成分と無機成分から構成される、請求項9に記載の複合体。
- 有機成分がメチル基、メルカプト基、メタクリル基、アクリロイル基、ビニル基、及びアミノ基から選ばれる少なくとも1種類を含む成分である、請求項9又は10に記載の複合体。
- 有機成分と無機成分のハイブリッド材が、シルセスキオキサンである、請求項9から11の何れか1項に記載の複合体。
- 被覆層が、熱硬化性樹脂、熱可塑性樹脂、及び光硬化性樹脂から選ばれる少なくとも1種である、請求項5から8の何れか1項に記載の複合体。
- 被覆層が粘着剤である、請求項5から8の何れか1項に記載の複合体。
- 平均繊維幅2〜1000nmのセルロース微細繊維を主成分とするシート層の片面又は両面に、被覆層を有する貼り合わせ用シートであって、シート層が親水性高分子または親水性低分子化合物を含み、シート層の密度が0.90g/cm3以上1.60g/cm 3 以下である、貼り合わせ用シート。
- 被覆層が、有機成分と無機成分のハイブリッド材である、請求項15に記載のシート。
- 有機成分が、メチル基、メルカプト基、メタクリル基、アクリロイル基、ビニル基、及びアミノ基から選ばれる少なくとも1種を含む成分である、請求項16に記載のシート。
- 有機成分と無機成分のハイブリッド材が、シルセスキオキサンである、請求項16又は17に記載のシート。
- 請求項15〜18のシートに、硬化性樹脂層又はフィルム層を積層した複合体。
- 平均繊維幅2〜1000nmの微細繊維を主成分とするシート層の片面又は両面に、被覆層を設ける工程;及び
前記被覆層の、シート層とは反対側の表面上に、硬化性樹脂層又はフィルム層を設ける工程
を含む、シート層が親水性高分子または親水性低分子化合物を含み、シート層の密度が0.90g/cm3以上1.60g/cm 3 以下である、複合体の製造方法。 - シート層と被覆層が、塗工、又は貼り合わせにより積層された、請求項20に記載の複合体の製造方法。
- 被覆層と、硬化性樹脂層又はフィルム層が、塗工、又は貼り合わせにより積層された、請求項20に記載の複合体の製造方法。
- 請求項1から14および19の何れか1項に記載の複合体を含む、照明装置、投影装置、看板又は画像表示装置、タッチパネル、又は太陽電池。