JP6328125B2 - 低弾性率層および残留強度を有する物品 - Google Patents
低弾性率層および残留強度を有する物品 Download PDFInfo
- Publication number
- JP6328125B2 JP6328125B2 JP2015536984A JP2015536984A JP6328125B2 JP 6328125 B2 JP6328125 B2 JP 6328125B2 JP 2015536984 A JP2015536984 A JP 2015536984A JP 2015536984 A JP2015536984 A JP 2015536984A JP 6328125 B2 JP6328125 B2 JP 6328125B2
- Authority
- JP
- Japan
- Prior art keywords
- glass substrate
- film
- crack
- layer
- mitigating layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
図1を参照すると、物品100は、対向する主面122、124を有するガラス基板120(ここに記載したように、強化されていても強力であってもよい)、少なくとも1つの対向する主面(122または124)に配置された膜110および膜110とガラス基板120との間に配置された亀裂軽減層130を備えている。1つ以上の代わりの実施の形態において、亀裂軽減層130および膜110は、少なくとも1つの主面(122または124)上に配置されることに加え、またはその代わりに、ガラス基板の副面(minor surface)に配置されていてもよい。ここに用いたように、ガラス基板120は実質的に平らな板であってよいが、他の実施の形態は、湾曲したもしくは別なふうに形成または造形されたガラス基板を利用してもよい。ガラス基板120は、実質的に透き通り、透明であり、光を拡散しないことがある。このガラス基板は、約1.45から約1.55の範囲の屈折率を有することがある。1つ以上の実施の形態において、ガラス基板120は、ここにさらに詳しく記載するように、強化されていても、強力であると特徴付けられてもよい。ガラス基板120は、そのような強化前に、比較的無垢であり、傷を含まないことがある(例えば、表面傷の数が少ない、または平均表面傷サイズが約1マイクロメートル未満である)。強化されたまたは強力なガラス基板120が使用される場合、そのような基板は、そのような基板の1つ以上の対向する主面において、高い平均曲げ強度(強化されていないまたは強力ではないガラス基板と比べて)または高い表面破壊歪み(強化されていないまたは強力ではないガラス基板と比べて)を有すると特徴付けられるであろう。
物品100は、ガラス基板120の表面上に配置された膜110を備えている。膜110は、ガラス基板120の一方または両方の主面122、124上に配置されてもよい。1つ以上の実施の形態において、膜110は、一方または両方の主面122、124上に配置されることに加えて、またはその代わりに、ガラス基板120の1つ以上の副面(図示せず)上に配置されていてもよい。1つ以上の実施の形態において、膜110は、目に容易に見える巨視的引っ掻き傷または欠陥を含まない。
(1)光学干渉効果を最小にするために、ガラス基板120、亀裂軽減層130および/または他の膜または層のいずれかの屈折率と同様の屈折率、
(2)反射防止干渉効果を達成するために調整された屈折率(実および/または虚成分)、および/または
(3)UVまたはIR遮断または反射を達成するため、または着色/色付け効果を達成するためなどの、波長選択的反射効果または波長選択的吸収効果を達成するために調整された屈折率(実および/または虚成分)、
のいずれかを有する材料を膜110に含むことが都合よいであろう。1つ以上の実施の形態において、膜110は、ガラス基板120の屈折率より高いおよび/または亀裂軽減層130の屈折率より高い屈折率を有することがある。1つ以上の実施の形態において、その膜は、約1.7から約2.2の範囲、または約1.4から約1.6の範囲、または約1.6から約1.9の範囲の屈折率を有することがある。
1つ以上の実施の形態による亀裂軽減層130は、膜110の臨界歪みエネルギー解放率より大きい臨界歪みエネルギー解放率(GIC=KIC 2/E)を有することがある。1つ以上の実施の形態において、膜110は、約0.1kJ/m2以下の臨界歪みエネルギー解放率を有することがあり、亀裂軽減層130は、約0.1kJ/m2超の臨界歪みエネルギー解放率を有することがある。亀裂軽減層130は、約1.0kJ/m2以上の臨界歪みエネルギー解放率を有することがある。特定の実施の形態において、亀裂軽減層130は、約0.05kJ/m2から約100kJ/m2の範囲の臨界歪みエネルギー解放率を有することがあるのに対し、膜110は、約0.05kJ/m2未満の臨界歪みエネルギー解放率を有することがある。亀裂軽減層130は、約0.05kJ/m2から約90kJ/m2、約0.5kJ/m2から約80kJ/m2、約0.5kJ/m2から約70kJ/m2、約0.5kJ/m2から約60kJ/m2、約0.5kJ/m2から約50kJ/m2、約0.5kJ/m2から約40kJ/m2、約0.5kJ/m2から約30kJ/m2、約0.5kJ/m2から約20kJ/m2、約0.5kJ/m2から約10kJ/m2、約0.5kJ/m2から約5kJ/m2、約1kJ/m2から約100kJ/m2、約5kJ/m2から約100kJ/m2、約10kJ/m2から約100kJ/m2、約20kJ/m2から約100kJ/m2、約30kJ/m2から約100kJ/m2、約40kJ/m2から約100kJ/m2、約50kJ/m2から約100kJ/m2、約60kJ/m2から約100kJ/m2、約70kJ/m2から約100kJ/m2、約80kJ/m2から約100kJ/m2、約90kJ/m2から約100kJ/m2、約0.05kJ/m2から約1kJ/m2、約1kJ/m2から約5kJ/m2、約5kJ/m2から約10kJ/m2、約10kJ/m2から約20kJ/m2、約20kJ/m2から約30kJ/m2、約30kJ/m2から約40kJ/m2、約40kJ/m2から約50kJ/m2、約50kJ/m2から約60kJ/m2、約60kJ/m2から約70kJ/m2、約70kJ/m2から約80kJ/m2、および約80kJ/m2から約90kJ/m2の範囲の臨界歪みエネルギー解放率を有することがある。
実施例1A〜1Jは、本開示の1つ以上の実施の形態または従来技術のガラス基板による物品を含む。実施例1A〜1Jの各々では、61モル%≦SiO2≦75モル%;7モル%≦Al2O3≦15モル%;0モル%≦B2O3≦12モル%;9モル%≦Na2O≦21モル%;0モル%≦K2O≦4モル%;0モル%≦MgO≦7モル%;0モル%≦CaO≦3モル%;および0モル%≦SnO2≦1モル%の組成を有するガラス基板を使用した。それらのガラス基板の厚さは0.7mmであった。実施例1A〜1Eにおいて、ガラス基板をイオン交換により強化して、約690MPaの表面圧縮応力(CS)および約23μmの圧縮層の深さ(DOL)を提供した。実施例1Fのガラス基板はイオン交換により強化しなかった。実施例1G〜1Jにおいて、強化したガラス板は、イオン交換により強化して、約740MPaの表面圧縮応力および約44μmの圧縮層の深さを提供した。ポリイミドからなる亀裂軽減層および/またはインジウムスズ酸化物からなる膜を、表1において下記に与えられるように、強化ガラス基板および(非強化)ガラス基板上に配置した。実施例1A、1E、1F、1Gおよび1Hは、亀裂軽減層を備えていなかったので、比較として示されている。
実施例2A〜2Dの各々では、61モル%≦SiO2≦75モル%;7モル%≦Al2O3≦15モル%;0モル%≦B2O3≦12モル%;9モル%≦Na2O≦21モル%;0モル%≦K2O≦4モル%;0モル%≦MgO≦7モル%;0モル%≦CaO≦3モル%;および0モル%≦SnO2≦1モル%の組成を有するガラス基板を使用した。それらのガラス基板は、0.7mmの厚さを有し、イオン交換により強化し、実施例1A〜1Jに関して記載したのと同じプロセスを使用して、亀裂軽減層および/または膜との組合せのために調製した。実施例2A〜2Dの強化ガラス基板は、約776MPaの表面圧縮応力(CS)および約41.4μmの圧縮層の深さ(DOL)を有した。ポリイミドからなる亀裂軽減層およびインジウムスズ酸化物からなる膜を、実施例1A〜1Jに関して記載した方法を使用して、表2において下記に与えられるように、強化ガラス基板上に配置して、実施例2A〜2Dの物品を提供した。接着促進剤は、実施例1B〜1D、1Iおよび1Jと同じ様式で利用した。実施例2Aは、250nmのポリイミド厚を有し、溶媒希釈剤で30:70の比に希釈されたポリイミド溶液を使用して調製し、最初に、3秒間に亘り500rpmで回転させ、その後、60秒間に亘り4000rpmで回転させた。実施例2Bは、90nmのポリイミド厚を有し、溶媒希釈剤で20:80の比に希釈されたポリイミド溶液を使用して調製し、最初に、3秒間に亘り500rpmで回転させ、その後、60秒間に亘り4000rpmで回転させた。実施例2Aおよび2Bについて、高分子溶液は、その溶液をガラス基板上に施し、スピンコーティングする前に、少なくとも1時間に亘り室温(約25℃)で平衡させた。これらのポリイミド被覆サンプルの乾燥、焼成および硬化は、実施例1B〜1D、1Iおよび1Jと同じ様式で行った。実施例2Cおよび2Dは、亀裂軽減層を備えていなかったので、比較例として示した。
実施例3A〜3Cは、図7〜9に示された予言的な実施例であり、関連するモデル化光反射率データが図10〜12に示されている。実施例3Aおよび3Bは、それぞれ、以下に記載されている実施例4Cおよび4Eに相関する。実施例3A〜3Cは、各々が、ガラス基板302、312、322、ガラス基板302、312、322上に配置されたポリイミドを含む亀裂軽減層304、314、324、および亀裂軽減層がガラス基板と膜との間にあるように、ガラス基板302、312、322上に配置されたインジウムスズ酸化物を含む膜306、316、326を備えた、物品300、310、320を含む。実施例3A〜3Cの各々において、ガラス基板は、約0.2mmから約2.0mmの範囲の厚さを有する。実施例3Aは、74nmの厚さを有する亀裂軽減層304および115nmの厚さを有する膜306を備えている。実施例3Bは、85nmの厚さを有する亀裂軽減層314および23nmの厚さを有する膜316を備えている。実施例3Cは、64nmの厚さを有する亀裂軽減層324および115nmの厚さを有する膜326を備えている。実施例3Cは、亀裂軽減層324と膜326との間に配置された、保護層として機能する、SiOxNyを含む追加の膜328を備えている。この追加の膜328の厚さは10nmである。実施例3A〜3Cにおいて、ガラス基板302、312、322は、約1.45〜1.55の範囲の屈折率を有し、亀裂軽減層304、314、324は、約1.6〜1.75の範囲の屈折率を有し、膜306、316、326は、約1.8〜2.2の範囲の屈折率を有する。実施例3Cにおいて、SiOxNyを含む追加の膜328は、亀裂軽減層324の屈折率と同様の屈折率を有する。実施例3A〜3Cの各々は、接着剤を含むことがある第2の追加の膜(図10、11および12に示されている)を含むことがありり、これは、モデル化実施例4においてより十分に記載される。
実施例4Cおよび4E、並びに比較実施例4A、4B、4Dおよび4Fは、表3における以下の情報を使用して、光学的にモデル化した。実施例4Cおよび4Eは、実施例3Aおよび3Bに相関する。
実施例5A〜5Gは、0.7mm厚のイオン交換により強化したアルミノケイ酸塩ガラス基板を提供することによって作製した。このガラス基板は、61モル%≦SiO2≦75モル%;7モル%≦Al2O3≦15モル%;0モル%≦B2O3≦12モル%;9モル%≦Na2O≦21モル%;0モル%≦K2O≦4モル%;0モル%≦MgO≦7モル%;0モル%≦CaO≦3モル%;および0モル%≦SnO2≦1モル%の組成を含んだ。このガラス基板を、3〜8時間に亘り約350〜450℃の温度を有するKNO3溶融塩浴中でイオン交換した。このイオン交換ガラス基板は、約687MPaの表面圧縮応力および約24マイクロメートルのイオン交換層の深さを有した。次いで、ガラス基板を、40〜110kHzで超音波撹拌しながら、約50〜70℃の温度を有するKOH清浄液(1〜4%のSemiclean KG)中で洗浄し、同じ周波数範囲で超音波処理しながら、脱イオン水で濯ぎ、乾燥させた。
実施例6A〜6Fは、1.0mm厚のイオン交換により強化したアルミノケイ酸塩ガラス基板を提供することによって作製した。このガラス基板は、61モル%≦SiO2≦75モル%;7モル%≦Al2O3≦15モル%;0モル%≦B2O3≦12モル%;9モル%≦Na2O≦21モル%;0モル%≦K2O≦4モル%;0モル%≦MgO≦7モル%;0モル%≦CaO≦3モル%;および0モル%≦SnO2≦1モル%の組成を有した。このガラス基板を、3〜8時間に亘り約350〜450℃の温度を有するKNO3溶融塩浴中でイオン交換して、強化ガラス基板を提供した。この強化ガラス基板は、約885MPaの圧縮応力および約42マイクロメートルのイオン交換層の深さを有した。次いで、強化ガラス基板を、40〜110kHzで超音波撹拌しながら、約50〜70℃の温度を有するKOH清浄液(1〜4%のSemiclean KG)中で洗浄し、同じ周波数範囲で超音波処理しながら、脱イオン水で濯ぎ、乾燥させた。
実施例7A〜7Bは、1.0mm厚のイオン交換により強化したアルミノケイ酸塩ガラス基板を提供することによって作製した。このガラス基板は、61モル%≦SiO2≦75モル%;7モル%≦Al2O3≦15モル%;0モル%≦B2O3≦12モル%;9モル%≦Na2O≦21モル%;0モル%≦K2O≦4モル%;0モル%≦MgO≦7モル%;0モル%≦CaO≦3モル%;および0モル%≦SnO2≦1モル%の組成を有した。このガラス基板を、3〜8時間に亘り約350〜450℃の温度を有するKNO3溶融塩浴中でイオン交換して、強化ガラス基板を提供した。この強化ガラス基板は、約885MPaの圧縮応力および約42マイクロメートルのイオン交換層の深さを有した。次いで、ガラス基板を、40〜110kHzで超音波撹拌しながら、約50〜70℃の温度を有するKOH清浄液(1〜4%のSemiclean KG)中で洗浄し、同じ周波数範囲で超音波処理しながら、脱イオン水で濯ぎ、乾燥させた。
11 貫通亀裂
12,110 膜
13 片側の逸れ
14 両側の逸れ
16 停止亀裂
18 キンク
100 物品
130 亀裂軽減層
Claims (10)
- 物品において、
対向する主面を有し、第1の平均破壊歪みを有するガラス基板、
前記ガラス基板の第1の主面上に配置された、第1の弾性率を有する亀裂軽減層、および
前記亀裂軽減層上に配置された膜であって、前記第1の平均破壊歪みより小さい第2の平均破壊歪みおよび前記第1の弾性率より大きい第2の弾性率を有する膜、
を備え、
前記亀裂軽減層が、前記膜から始まる亀裂が、該亀裂軽減層および前記ガラス基板の1つ以上に橋渡しするときに、該亀裂の応力拡大係数を減少させる、物品。 - 前記亀裂軽減層が、前記応力拡大係数を少なくとも10%減少させるか、または前記亀裂が前記ガラス基板に橋渡しするのに要する荷重を少なくとも10%増加させる、請求項1記載の物品。
- 前記第1の弾性率が50GPa以下である、請求項1または2記載の物品。
- 前記亀裂軽減層が、10体積%から50体積%の範囲の気孔率を有する多孔質材料から構成される、請求項1から3いずれか1項記載の物品。
- 前記ガラス基板が、化学強化されており、500MPa超の圧縮応力および15μm超の圧縮応力層の深さを有する、請求項1から4いずれか1項記載の物品。
- 物品において、
対向する主面を有するガラス基板であって、0.5%超の第1の平均破壊歪みを有するガラス基板、
前記ガラス基板の第1の主面上に配置された、多孔質材料から構成された亀裂軽減層、および
前記亀裂軽減層上に配置された膜、
を備え、
前記亀裂軽減層が、前記膜および前記ガラス基板の一方で始まり、該亀裂軽減層に入る亀裂を、該亀裂軽減層内に留まらせる、物品。 - 前記亀裂軽減層が、1MPa・m1/2以下の破壊靭性を示す、請求項6記載の物品。
- 前記ガラス基板と前記亀裂軽減層が第1の界面を形成し、前記膜と前記亀裂軽減層が第2の界面を形成し、前記亀裂軽減層が、前記膜および前記ガラス基板の一方から始まる前記亀裂を前記第1の界面および前記第2の界面の一方または両方に実質的に平行な方向に該亀裂軽減層内に伝搬させるか、または前記膜および前記ガラス基板の一方から始まる前記亀裂を前記第1の界面または前記第2の界面のいずれかに実質的に沿って伝搬させる、請求項6または7記載の物品。
- 前記亀裂軽減層が、SiO、SiOx、SiO2、Al2O3、AlN、AlOxNy、Si3N4、SiOxNy、SiAlxOyNz、TiO2、Nb2O5、Ta2O5、ZrO2、GeO2、SiCxNy、SiCxOyNz、SiC、Si、Ge、インジウムスズ酸化物、酸化スズ、フッ素化酸化スズ、アルミニウム亜鉛酸化物、および酸化亜鉛の1つ以上から構成される、請求項6から8いずれか1項記載の物品。
- 物品において、
対向する主面を有するガラス基板であって、第1の平均破壊歪みを有するガラス基板、
前記ガラス基板の第1の主面上に配置されて、第1の界面を形成する亀裂軽減層、および
前記亀裂軽減層上に配置されて、第2の界面を形成する膜であって、前記第1の平均破壊歪みより小さい第2の平均破壊歪みを有する膜、
を備え、
前記膜から始まる亀裂が前記第2の界面を横切って橋渡しするのに必要な荷重が、該亀裂が前記第1の界面を横切って橋渡しするのに必要な荷重より大きい、物品。