JP4663812B2 - 消臭材 - Google Patents
消臭材 Download PDFInfo
- Publication number
- JP4663812B2 JP4663812B2 JP2009553452A JP2009553452A JP4663812B2 JP 4663812 B2 JP4663812 B2 JP 4663812B2 JP 2009553452 A JP2009553452 A JP 2009553452A JP 2009553452 A JP2009553452 A JP 2009553452A JP 4663812 B2 JP4663812 B2 JP 4663812B2
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane
- fiber
- deodorizing
- diol
- carboxyl group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、木綿繊維等のセルロース系繊維にメタクリル酸をグラフト共重合させて得られる改質セルロース系繊維は、アンモニアや屎尿臭等の悪臭に対する消臭性に優れたものとして知られている(例えば、特許文献1参照)。さらに、消臭性については、高齢化社会の進行により、特に加齢臭の消臭機能が求められている。一般に、加齢臭とは、アンモニア、酢酸、イソ吉草酸及びノネナールの各臭気成分よりなるものと考えられており、社団法人繊維評価技術協議会(JTETC)公表の「消臭加工繊維製品認証基準」の評価基準によれば、加齢臭の消臭には、アンモニア、酢酸、イソ吉草酸及びノネナールの全ての成分を減少させる機能が必須とされている。
しかしながら、出願人の知る限り、ノネナールや加齢臭に対する優れた消臭性を備えた消臭材については、未だ報告されていないのが現状である。
[1] ノネナールを消臭するポリウレタン系樹脂を含有することを特徴とする消臭材。
[2] ポリウレタン系樹脂が、アンモニア、酢酸、およびイソ吉草酸からなる群より選択される少なくとも1種をさらに消臭する[1]記載の消臭材。
[3] ポリウレタン系樹脂のガラス転移点(Tg)が−100〜0℃である[1]または[2]に記載の消臭材。
[4] ポリウレタン系樹脂が、ポリウレタンウレア系繊維である[1]〜[3]のいずれかに記載の消臭材。
[5] さらに、カルボキシル基を含有する繊維を含有する[1]〜[4]のいずれかに記載の消臭材。
[6] カルボキシル基を含有する繊維が、カルボキシル基濃度30〜3000meq/kgのカルボキシル基を含有する[5]記載の消臭材。
[7] カルボキシル基を含有する繊維が、親水性ビニル系モノマーが2〜30重量%グラフト重合されたセルロース系繊維である[5]記載の消臭材。
[8] ノネナールを消臭する消臭材を製造するためのポリウレタン系樹脂の使用。
また、本発明の消臭材で使用されるポリウレタン系樹脂の好ましい実施態様は以下に記載した通りのストレッチ布帛である。
[1’] (A)カルボキシル基を含有するセルロース系繊維を紡績糸に対して100〜5重量%およびポリエステル繊維を紡績糸に対して0〜95重量%含む紡績糸、および(B)ポリウレタン系弾性繊維を含有し、(A)紡績糸を布帛に対して99〜70重量%、および(B)ポリウレタン系弾性繊維を1〜30重量%含有する布帛であって、抗菌剤が吸尽もしくは担持されているストレッチ布帛。
[2’] カルボキシル基を含有するセルロース系繊維がセルロース系繊維にメタクリル酸をグラフト共重合反応させて得られる改質セルロース系繊維である[1’]記載のストレッチ布帛。
[3’] 紡績糸が、リング・トラベラー法、オープンエンド法、結束法および精紡交撚法のいずれか1種以上の製造方法により得られたものである[1’]または[2’]に記載のストレッチ布帛。
[4’] ポリエステル繊維の1g当たりの繊維表面積が約0.1m2以上またはポリエステル繊維の単繊維繊度が約3デニール以下である[1’]〜[3’]のいずれかに記載のストレッチ布帛。
[5’] ポリウレタン系弾性繊維を構成するポリウレタンのウレタン基濃度が約0.2mol/kg以上3.5mol/kg以下である[1’]〜[4’]のいずれかに記載のストレッチ布帛。
[6’] ポリウレタン系弾性繊維が、下記の構造単位(a)を5〜25モル%及び構造単位(b)を95〜75モル%含む数平均分子量が250〜10000であるポリアルキレンエーテルジオールと、ジイソシアネート化合物と、ジアミノ化合物とを重合させて得られるポリウレタンウレアからなる[1’]〜[5’]のいずれかに記載のストレッチ布帛。
[7’] ポリウレタン系弾性繊維を構成するポリウレタンの有効末端アミン濃度が15〜50meq/kgである[1’]〜[6’]のいずれかに記載のストレッチ布帛。
[8’] 抗菌剤が有機窒素硫黄系化合物、第4級アンモニウム系化合物、リン酸エステル系化合物および金属イオンを含有する無機系化合物のいずれか1種以上から選択されている[1’]〜[7’]のいずれかに記載のストレッチ布帛。
[9’] 目付が100〜1000g/m2であり、タテ方向および/またはヨコ方向の伸長率が5%以上である[1’]〜[8’]のいずれかに記載のストレッチ布帛。
[10’] 紡績糸が6〜60英式綿番手である[1’]〜[9’]のいずれかに記載のストレッチ布帛。
[11’] 抗菌剤による吸尽もしくは担持処理に際し、抗菌剤を含む処理液のpHが5.0以上6.0以下の範囲である[1’]〜[10’]のいずれかにに記載のストレッチ布帛。
まず、本発明のポリウレタン系樹脂を説明する。
ポリウレタン系樹脂を構成する構造単位のポリマージオールとしては、ポリエーテル系グリコール、ポリエステル系グリコール、ポリカーボネートジオール等が好ましい。そして、特に消臭性、柔軟性、繊維とした際に高い伸度を付与する観点からポリエーテル系グリコールが使用されることが好ましい。
また、これらのポリマージオールは単独で使用してもよいし、2種以上混合もしくは共重合して使用してもよい。
アミン系触媒としては、例えば、N,N−ジメチルシクロヘキシルアミン、N,N−ジメチルベンジルアミン、トリエチルアミン、N−メチルモルホリン、N−エチルモルホリン、N,N,N’,N’−テトラメチルエチレンジアミン、N,N,N’,N’−テトラメチル−1,3−プロパンジアミン、N,N,N’,N’−テトラメチルヘキサンジアミン、ビス−2−ジメチルアミノエチルエーテル、N,N,N’,N’,N’−ペンタメチルジエチレントリアミン、テトラメチルグアニジン、トリエチレンジアミン、N,N’−ジメチルピペラジン、N−メチル−N’−ジメチルアミノエチル−ピペラジン、N−(2−ジメチルアミノエチル)モルホリン、1−メチルイミダゾール、1,2−ジメチルイミダゾール、N,N−ジメチルアミノエタノール、N,N,N’−トリメチルアミノエチルエタノールアミン、N−メチル−N’−(2−ヒドロキシエチル)ピペラジン、2,4,6−トリス(ジメチルアミノメチル)フェノール、N,N−ジメチルアミノヘキサノール、トリエタノールアミン等が挙げられる。
また、有機金属触媒としては、オクタン酸スズ、二ラウリン酸ジブチルスズ、オクタン酸鉛ジブチル等が挙げられる。
溶液重合法の場合、かかるポリウレタンは、例えば、N,N−ジメチルアセトアミド(以下、DMAcと略す)、ジメチルホルムアミド(以下、DMFと略す)、ジメチルスルホキシド、N−メチルピロリドンなどやこれらを主成分とする溶剤の中で、上記の原料を用い合成することにより得られる。例えば、こうした溶剤中に、各上記原料を投入、溶解させ、適度な温度に加熱し反応させてポリウレタンとする、いわゆるワンショット法、また、ポリマージオールとジイソシアネートを、まず溶融反応させ、しかる後に、反応物を溶剤に溶解し、前述の鎖伸長剤と反応させてポリウレタンとする方法などが、特に好適な方法として採用され得る。この場合、得られるポリウレタン溶液の濃度は、通常、30重量%以上80重量%以下の範囲が好ましい。
減少率(%)=(2時間後の空試験濃度−2時間後の試料試験濃度)/(2時間後の空試験濃度)×100
有効末端アミン濃度(meq/kg)=(a)−(b)
また、ポリマージオールと反応させるジイソシアネート化合物としては通常のものが用いられ、例えば、MDIが用いられる。
以下に説明する。
上記セルロース系繊維とは、綿、麻などのセルロース系天然繊維やレーヨンなどのセルロース系再生繊維、半合成セルロース系繊維、いわゆる指定外繊維(リヨセル、キュプラ)等が挙げられる。特にリヨセルは、その柔らかな風合いや吸湿性の良さから、衣服素材として本発明の消臭材を製造する際に好ましく用いられる。
前記親水性ビニル系モノマーがグラフト重合されたセルロース系繊維は、グラフト前の重量と比較して2〜30重量%分の重量が増加している(グラフト率2〜30重量%)ことが好ましく、さらにグラフト率5〜15重量%が好ましい。
上記ポリエステル繊維は、特に限定されないが、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリテトラメチレングリコールテレフタレートあるいは、これらの構成単位を主体とし、他の共重合成分を共重合したポリエステル系樹脂から得られたポリエステル繊維であり、特に好ましいのは、ポリエチレンテレフタレート系繊維、即ち、主たるポリマーがポリエチレンテレフタレートや共重合ポリエチレンテレフタレートである繊維である。
また、吸水速乾性ポリエステル繊維糸が好ましく用いられる。吸水速乾性の合成繊維としては、中空繊維の壁面に更に小さな孔が多数設けられている繊維や、繊維表面などに多くの溝や孔などが設けられて、吸水性はこれら繊維自体の微小な孔、繊維表面の溝、繊維間、糸間の空隙に水分が吸収されるようにした異形断面形状の繊維などで、合成繊維メーカーにより、吸水速乾性繊維として各種市販されているものを用いることができる 。例えば、吸水速乾性ポリエステル繊維としては、インビスタ社製“クールマックス”、東レ株式会社製“セオα”、帝人ファイバー株式会社製“ウエルキイ”、東洋紡績株式会社製“ドライファスト” 、旭化成せんい株式会社製“テクノファイン”などが挙げられる。
なお、(A)紡績糸は、カルボキシル基を含有するセルロース系繊維が100〜5重量%およびポリエステル繊維が0〜95重量%からなり、さらにポリエステル繊維以外の複数種の合成繊維、羊毛、絹等の天然繊維が、50重量%未満の割合で組み合わされたものであっても良い。
尚、6番手より太い糸を使用すると基布が厚くなりすぎてソフト性に欠けるので好ましくなく、60番手より細い糸を使用すると薄くなりすぎ、傷みやすくなるため好ましくない。
本発明の好ましい実施の態様であるストレッチ布帛は、上記抗菌剤による吸尽もしくは担持処理に際し、処理液のpHが5.0以上6.0以下の範囲で吸尽もしくは担持処理されたものであることが好ましい。
すなわち、上記(A)紡績糸を99〜70重量%、および(B)ポリウレタン系弾性繊維を1〜30重量%を含有するストレッチ布帛への抗菌剤による吸尽もしくは担持処理は、通常、常法により行われ、抗菌剤を必要により溶媒に溶解した処理液に布帛などをディッピングして行われるが、その場合の処理液のpHは好ましくは5.0以上6.0以下の範囲であり、抗菌剤が均一に規定量だけストレッチ布帛にしみこみ、吸尽される。処理時間は1〜120分、処理温度は40℃以上200℃以下が好ましい。
織物の組織は、平織、斜文織、朱子織等の三原組織、変化平織、変化斜文織、変化朱子織等の変化組織、蜂の巣織、模紗織、梨地織等の特別組織、たて二重織、よこ二重織等の片二重組織、風通織、袋織、二重ビロード等の二重織組織、ベルト織等の多層組織、たてビロード、タオル、シール、ベロア等のたてパイル織、別珍、よこビロード、ベルベット、コール天等のよこパイル織、絽、紗、紋紗等のからみ組織等が好ましい。
製織は有杼織機(フライシャットル織機等)または無杼織機(レピア織機、グリッパー織機、ウォータージェット織機、エアージェット織機等)等によって行われるのが好ましい。
製編は、丸編機、横編機、コットン式編機のような平型編機、トリコット編機、ラッシェル編機、ミラニーズ編機等によって行われるのが好ましい。
さらに、本発明の布帛はタイツ、ストッキング、パンティストッキング、ソックス等の靴下類や下着類に対して、特に好適である。
本発明の好ましい実施の態様であるストレッチ布帛は、上記紡績糸を99〜70重量%、およびポリウレタン系弾性繊維を1〜30重量%含有する布帛であり、好ましくは紡績糸95〜80重量%、およびポリウレタン系弾性繊維を5〜20重量%含有するものである。
また、本発明の好ましい実施の態様であるストレッチ布帛は、目付が100〜1000g/m2であり、伸長率がタテ方向および/またはヨコ方向とも5%以上であることが好ましく、目付は150〜280g/m2であることが特に好ましい。
ポリウレタン系樹脂をノネナール消臭材の製造に用いることも好ましい。
臭気成分として、加齢臭の原因とされている2−ノネナール(C9H16O、分子量140.2、CAS番号:463−53−8 以下、単にノネナールという)を用いて消臭試験を行い、下記の方法により消臭性能を評価した。
機器分析試験はガスクロマトグラフィー法により行った。ノネナールは減少率75%以上を合格(表示○)とした。
脱水されたテトラヒドロフラン87.5モルと脱水された3メチル−テトラヒドロフラン12.5モルとを撹拌機付き反応器に仕込み、窒素シール下、温度10℃で、触媒(過塩素酸70重量%及び無水酢酸30重量%の混合物)の存在下で8時間重合反応を行ない、反応終了液に水酸化ナトリウム水溶液で中和する共重合方法により得られた、数平均分子量2500の共重合テトラメチレンエーテルジオール(3−メチル−テトラヒドロフラン由来の構造単位(a)を12.5モル%含む)を、ポリアルキレンエーテルジオールとして用いた。
この共重合テトラメチレンエーテルジオール1モルに対し4,4’−MDIを1.97モルになるように容器に仕込み、90℃で反応せしめ、得られた反応生成物をN,N−ジメチルアセトアミド(DMAc)に十分に撹拌し、溶解させて溶液を得た。次に、鎖伸長剤として60モル%のエチレンジアミン(EDA)と40モル%の1,2−プロパンジアミン(1,2−PDA)を含むDMAc溶液を、前記反応物を溶解させた溶液に添加し、さらに末端封鎖剤としてジエチルアミンを含むDMAc溶液を添加して、ポリマー固体分が25重量%であるポリウレタンウレア溶液を調製した。得られた溶液は40℃で約2400ポイズの粘度を有していた。重合体はDMAc中で0.5g/100mlの溶液濃度で25℃で測定すると、0.95の極限粘度であった。
ノネナール消臭試験による減少率は80%であった。
実施例1の共重合テトラメチレンエーテルジオール1モルに対し4,4’−MDIを6.4モルになるように容器に仕込み、90℃で反応せしめ、得られた反応生成物をDMAcに十分に撹拌し、溶解させた。次に、鎖伸長剤として60モル%のEDAと40モル%の1,2−PDAを含むDMAc溶液を、前記反応物が溶解した溶液に添加し、さらに末端封鎖剤としてジシクロヘキシルアミンを含むDMAc溶液を添加してポリマー固体分が25重量%であるポリウレタンウレア溶液を調製した。得られた溶液は40℃で約5400ポイズの粘度を有していた。重合体はDMAc中で0.5g/100mlの溶液濃度で25℃で測定すると、1.25の極限粘度であった。
ノネナール消臭試験による減少率は76%であった。
3mm厚のカイノール活性炭繊維不織布(日本カイノール社製)を使用し、ノネナール消臭試験を実施した。その結果を表2に示した。
ノネナール消臭試験による減少率は60%であった。
ウーリーナイロン糸(N)(44dtex、34fil)のみを使用し、320針、釜径3.5インチ(29ゲージ)の1口筒編み機に供給して編成し、120℃にて1分間のスチームセットを行い幅約5cmの筒編み地(55g/m2)を得た。これを開反しないままサンプルとし(55g/m2の編地2枚重ねに相当する)、ノネナール消臭試験を実施した。その結果を表2に示した。
ノネナール消臭試験による減少率は22%であった。
ポリエチレンテレフタレート糸(E)(44dtex、36fil)のみを使用し、320針、釜径3.5インチ(29ゲージ)の1口筒編み機に供給して編成し、120℃にて1分間のスチームセットを行い幅約5cmの筒編み地(55g/m2)を得た。これを開反しないままサンプルとし(55g/m2の編地2枚重ねに相当する)、ノネナール消臭試験を実施した。その結果を表2に示した。
ノネナール消臭試験による減少率は0%であった。
ポリアルキレンエーテルジオールとして数平均分子量1400のポリテトラメチレンエーテルジオール(PTMG)を用い、PTMG1モルに対し4,4’−MDIを12.5モルになるように容器に仕込み、80℃で反応せしめ、得られた反応生成物をDMAcに十分に撹拌し、溶解させた。次に、鎖伸長剤としてエチレングリコールを含むDMAc溶液を、前記反応物が溶解した溶液に添加して、ポリマー中の固体分が25重量%であるポリウレタン溶液を調製した。得られた溶液は40℃で約3000ポイズの粘度を有していた。重合体はDMAc中で0.5g/100mlの溶液濃度で25℃で測定すると、1.60の極限粘度であった。
このポリウレタン溶液を、紡糸口金から水中に4フィラメントで吐出し、熱風ガス(120℃)中を通過させることにより乾燥し、110m/分のスピードで巻き取り、4フィラメント合着で44dtexのポリウレタン系繊維(B−c)を製造した。(B−c)のガラス転移点(Tg)は12℃であった。なお、このポリウレタン系繊維(B−c)を構成するポリウレタンのウレタン基濃度は0.51mol/kgであった。
ノネナール消臭試験による減少率は32%であった。
臭気成分としてノネナール、アンモニア、酢酸及びイソ吉草酸の4成分を用いて消臭試験を行い、下記の方法により消臭性能を評価した。
消臭性能評価
JTETCが定める消臭加工繊維製品認証基準に従い、上記4成分について機器分析試験を行い、さらにノネナールについては別途官能試験を行った。なお、洗濯はJIS L 0217 103法(1995)に従い、その後タンブル乾燥を行った。
機器分析試験:容器に臭気成分とサンプルを入れ、2時間放置後の臭気成分の残留濃度(2時間後の試料試験濃度)を測定した。臭気成分のみを入れた容器の残留濃度を空試験濃度として、下式より臭気成分の減少率を計算した。アンモニアと酢酸は検知管法により、イソ吉草酸とノネナールはガスクロマトグラフィー法により測定した。
減少率(%)=(2時間後の空試験濃度−2時間後の試料試験濃度)/(2時間後の空試験濃度)×100
ノネナールの減少率75%以上、イソ吉草酸の減少率85%以上、アンモニアの減少率70%以上、酢酸の減少率80%以上の条件全てを満足する場合を合格(表示○)と判定した。
官能試験:判定者6名のうち、5名以上が下記基準により臭気を弱と判断した場合を合格とした。
臭気強:判定臭ガスより強い場合
臭気弱:判定臭ガスと比較して同等もしくはより弱い場合
ガラス転移点(Tg)が0℃以下のポリウレタン系繊維として実施例1で製造したポリウレタンウレア系繊維(B−a)を使用し、下記の方法によりカルボキシル基を含有する繊維(X)及び(Y)を得た。
常法により乾式紡糸した酢化度55%のジアセテート繊維(88dtex、24フイラメント、三菱レイヨン株式会社製)をメタクリル酸20.0g/l、硫酸第1鉄アンモニウム0.6g/l、過酸化水素0.3g/lの水溶液で浴比1:40、80℃×60分でオーバーマイヤー加工機を用いて、グラフト重合処理した。この後、水洗、湯洗を繰り返した。この時のグラフト率は約10%、カルボキシル基濃度は320meq/kgであった。これを(X)とし、同様にジアセテート繊維として150dtex、48フィラメントを用いた以外は上記と同様の方法でカルボキシル基含有ジアセテート繊維(Y)を得た。(Y)のグラフト率とカルボキシル基濃度は(X)と同じであった。
・グラフト率の測定:反応前の絶乾重量(W0)から、グラフト重合し洗浄した後の絶乾重量(W1)への重量増加率から計算した。
グラフト率=(W1−W0)×100/W0
まず、実施例1で得られたポリウレタンウレア系繊維(B−a)を2本引き揃えてマルチエンド糸(88dtex)を作製した。ヨコ糸用として、上記マルチエンド糸を(X)にてカバーリング(カバーリング加工条件:ヨリ数=400T/M、ドラフト=3.0)したカバードヤーンを作製した。タテ糸用として、上記マルチエンド糸を(Y)にてカバーリング(カバーリング加工条件:ヨリ数=600T/M、ドラフト=3.5)したカバードヤーンを作製した。これらのタテ糸及びヨコ糸を用いてレピア織機にて2/1綾組織で製織(タテ糸:90本/インチ、ヨコ糸:106本/インチ)し、常法に従い180℃でプレセットして、織物(ポリウレタンウレア系繊維11%、カルボキシル基を含有する繊維89%)を得た。この織物を加齢臭消臭試験用の織物とした。
実施例3においてポリウレタンウレア系繊維(B−a)の代わりに比較例4で製造したポリウレタン系繊維(B−c)を使用した以外は、実施例3と同様の方法で織物を製作し、加齢臭消臭試験を実施した。その結果を表3に示した。
加齢臭消臭試験の結果、ノネナールの減少率35%、アンモニアの減少率72%、酢酸の減少率93%、イソ吉草酸の減少率60%であり、比較例5のポリウレタン系繊維は消臭性基準に未達であり、加齢臭消臭性能を有さないポリウレタン系繊維構造物であった。
温湯循環式室内暖房装置(日立ファンコンベクターFU30FEA−T、日立製作所製)のエアーフィルター(ポリプロピレン不織布)を取り外し、フィルター素材を剥がし、代わりに後述の実施例4、5及び比較例6で得たフェルトを貼付した後、再び暖房装置内に装填し、本発明の消臭フィルター材循環式室内暖房装置とした。
さらに、上記の実施例及び比較例で得られた、ポリウレタンウレア系繊維(B−a)、(B−b)、及びポリウレタン系繊維(B−c)を用いてフェルトを作製し、消臭フィルター材試験に供した。
ここで、試験用のフェルトは、以下の手順により得た。
まず、実施例1,2及び比較例4のいずれかで得られた、ポリウレタンウレア系繊維(B−a)、(B−b)、及びポリウレタン系繊維(B−c)を裁断して、原毛を作成し、ニードルにより嵩を形成し、100℃の熱プレスにより、ポリウレタンウレア系繊維またはポリウレタン系繊維のみで構成される1mm厚の通気度が100cc/cm2/secのフェルトを得る。通気度はニードルパンチによる嵩で調整し、これを消臭フィルター材とした。試験の結果、表3から明らかなように、(B−a)、(B−b)をそれぞれ使用した本発明の空気清浄用フィルター(実施例4、5)は、いずれも不快臭がなく、有効期間も10日以上と長く顕著に優れている。
Claims (12)
- ポリマージオールと、ジイソシアネート化合物と、鎖伸長剤としてジアミノ化合物および/または低分子量ジオールとを重合してなり、かつガラス転移点(Tg)が−100〜0℃であるポリウレタンを主構成成分とし、ノネナールを消臭し得るポリウレタン系樹脂を含有することを特徴とする消臭材。
- ポリウレタン系樹脂が、アンモニア、酢酸、およびイソ吉草酸からなる群より選択される少なくとも1種をさらに消臭する請求項1記載の消臭材。
- ポリウレタン系樹脂が、ポリウレタン系繊維である請求項1または2に記載の消臭材。
- さらに、カルボキシル基を含有する繊維を含有する請求項1〜3のいずれかに記載の消臭材。
- カルボキシル基を含有する繊維が、カルボキシル基濃度30〜3000meq/kgのカルボキシル基を含有する請求項4記載の消臭材。
- カルボキシル基を含有する繊維が、親水性ビニル系モノマーが2〜30重量%グラフトされたセルロース系繊維である請求項4記載の消臭材。
- 構造単位(a)が5〜25モル%であり、構造単位(b)が95〜75モル%であり、かつ数平均分子量が250〜10000であることを特徴とする請求項8記載の消臭材。
- ポリウレタンが、鎖伸長剤として、エチレンジアミン、1,2−プロパンジアミン、1,3−プロパンジアミン、ヘキサメチレンジアミン、p−フェニレンジアミン、p−キシリレンジアミン、m−キシリレンジアミン、p,p’−メチレンジアミン、1,3−シクロヘキシルジアミン、ヘキサヒドロメタフェニレンジアミン、2−メチルペンタメチレンジアミンおよびビス(4−アミノフェニル)フォスフィンオキサイドからなる群から選ばれる1以上のジアミノ化合物を重合してなるポリウレタンウレアであることを特徴とする請求項1〜9のいずれかに記載の消臭材。
- ポリウレタンが、鎖伸長剤として、エチレングリコール、1,3−プロパンジオール、1,4−ブタンジオール、ビスヒドロキシエトキシベンゼン、ビスヒドロキシエチレンテレフタレートおよび1−メチル−1,2−エタンジオールからなる群から選ばれる1以上の低分子量ジオールを重合してなるポリウレタンであることを特徴とする請求項1〜9のいずれかに記載の消臭材。
- ノネナールを消臭する消臭材を製造するための、ポリマージオールと、ジイソシアネート化合物と、鎖伸長剤としてジアミノ化合物および/または低分子量ジオールとを重合してなり、かつガラス転移点(Tg)が−100〜0℃であるポリウレタンを主構成成分とするポリウレタン系樹脂の使用。