JP2007234233A - リチウム二次電池用活物質及びその製造方法、並びにそれを用いたリチウム二次電池 - Google Patents
リチウム二次電池用活物質及びその製造方法、並びにそれを用いたリチウム二次電池 Download PDFInfo
- Publication number
- JP2007234233A JP2007234233A JP2006050651A JP2006050651A JP2007234233A JP 2007234233 A JP2007234233 A JP 2007234233A JP 2006050651 A JP2006050651 A JP 2006050651A JP 2006050651 A JP2006050651 A JP 2006050651A JP 2007234233 A JP2007234233 A JP 2007234233A
- Authority
- JP
- Japan
- Prior art keywords
- lithium
- active material
- lithium secondary
- secondary battery
- titanium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】一般式A2Ti3O7で表される複合チタン酸化物を主成分とし、結晶構造が単斜晶系のNa2Ti3O7型の層状構造であることを特徴とするリチウム二次電池用活物質。概複合酸化物は、ナトリウム化合物と酸化チタンから生成されたナトリウムチタン酸化物を出発原料とし、イオン交換反応工程によって合成される。(式中、Aは、Na、Li、Hから選択された1種又は2種以上を示す)
【選択図】図1
Description
なお図1において、八面体はTiO6八面体を表し、その中央にチタンが占有している。また図1において、球はナトリウム、リチウム、或いは水素が占有している位置を表している。
(1)式A2Ti3O7で表される複合チタン酸化物を主成分とし、結晶構造が単斜晶系のNa2Ti3O7型の層状構造であることを特徴とするリチウム二次電池用活物質。(式中、Aは、Na、Li、Hから選択された1種又は2種以上を示す)
(2)単斜晶系の格子定数がA元素の種類と量比によって決定され、a軸長は、9.0〜9.4Å、b軸長が3.7〜4.1Å、c軸長が7.5〜8.5Å、β角が97〜102°の範囲であるリチウム二次電池用活物質。
(3)ナトリウム化合物と酸化チタンから生成されたナトリウムチタン酸化物を出発原料として、イオン交換する工程によって合成されることを特徴とした(1)に記載のリチウム二次電池用活物質の製造方法。
(4)上記イオン交換の方法として、リチウム溶融塩を用いるリチウムイオン交換、或いは酸性溶液を用いるプロトン交換反応を適用することを特徴とする(4)に記載のリチウム二次電池用活物質の製造方法。
(5)リチウム溶融塩を用いるリチウムイオン交換における熱処理温度が30℃から300℃の範囲内にある(4)に記載のリチウム二次電池用活物質の製造方法。
(6)正極及び負極として使用する2つの電極と、電解質からなるリチウム二次電池において、(1)に記載の活物質を含有する電極を構成部材として用いたリチウム二次電池。
また上記層状複合チタン酸化物A2Ti3O7の格子定数等は、A元素を構成するNa、Li、Hから選択された1種又は2種以上の種類と量比によって決定されることになるが、それぞれa軸長は、9.0〜9.4Å、b軸長は、3.7〜4.1Å、c軸長は、7.5〜8.5Å、β角は、97〜102°の範囲である。
本発明のうち、層状複合チタン酸化物活物質の製造方法は、ナトリウム化合物と酸化チタンから生成されたナトリウムチタン酸化物を出発原料として、イオン交換する工程によって合成されることを特徴とする方法である。
また、本発明の層状複合チタン酸化物活物質を含有する電極を構成部材として用いたリチウム二次電池は、スムーズなリチウム挿入・脱離反応が可能で、長期にわたる充放電サイクルに対応可能であり、また300mAh/gの高容量が期待できる電池である。
(層状ナトリウムチタン酸化物活物質の製造)
本発明のうち、Na2Ti3O7活物質は、原料として、ナトリウム化合物の少なくとも1種、及びチタン化合物の少なくとも1種を、Na2Ti3O7の化学組成となるように秤量・混合し、空気中などの酸素ガスが存在する雰囲気中で加熱することによって、製造することができる。
次いで、上記により得られたNa2Ti3O7を出発原料として、酸性溶液を用いてプロトン交換反応を適用することにより、ナトリウムの一部又は全部がプロトンと交換したプロトン交換体活物質が得られる。
一方、上記により得られたNa2Ti3O7、又はそれをさらにプロトン交換した(Na、H)2Ti3O7、或いは完全にプロトン交換されたH2Ti3O7を出発原料として、リチウム化合物を含む溶融塩中でリチウムイオン交換反応を適用することにより、ナトリウム、又はプロトンの一部又は全部がリチウムと交換したリチウムイオン交換体活物質(Na、Li、H)2Ti3O7が得られる。
本発明のリチウム二次電池は、前記層状複合チタン酸化物A2Ti3O7(Aは、Na、Li、Hから選択された1種又は2種以上)活物質を含有する電極を構成部材として用いるものである。すなわち、電極材料のひとつに本発明の層状複合チタン酸化物活物質を用いる以外は、公知のリチウム二次電池(コイン型、ボタン型、円筒型、全固体型等)の電池要素をそのまま採用することができる。
図2は、本発明のリチウム二次電池を、コイン型電池に適用した1例を示す模式図である。このコイン型電池1は、負極端子2、負極3、(セパレータ+電解液)4、絶縁パッキング5、正極6、正極缶7により構成される。
純度99%以上の炭酸ナトリウム(NaCO3)粉末と純度99.99%以上の二酸化チタン(TiO2)粉末をモル比でNa:Ti=2:3となるように秤量した。これらを乳鉢中で混合したのち、JIS規格白金製るつぼに充填し、電気炉を用いて、空気中、高温条件下で加熱した。焼成温度は、800℃で、焼成時間は20時間とした。その後、電気炉中で自然放冷した後、再度、乳鉢中で粉砕・混合を行い、800℃で20時間再焼成を行い、層状ナトリウムチタン酸化物活物質を得た。
a=9.073Å(誤差:0.002Å以内)
b=3.787Å(誤差:0.001Å以内)
c=8.445Å(誤差:0.007Å以内)
β=101.32°(誤差:0.05°以内)
このようにして得られた層状ナトリウムチタン酸化物Na2Ti3O7活物質に、導電剤としてアセチレンブラック、結着剤としてテトラフルオロエチレンを、重量比で80:15:5となるように配合し電極を作製し、対極にリチウム金属を用いて、6フッ化リン酸リチウムをエチレンカーボネート(EC)とジエチルカーボネート(DEC)との混合溶媒(体積比1:1)に溶解させた1M溶液を電解液とする、図2に示す構造のリチウム二次電池(コイン型セル)を作製し、その電気化学的リチウム挿入・脱離挙動を測定した。電池の作製は、公知のセルの構成・組み立て方法に従って行った。
実施例1で合成された層状ナトリウムチタン酸化物Na2Ti3O7の粉砕物を出発原料として、0.5Nの塩酸溶液に浸漬し、室温条件下で5日間保持して、プロトン交換処理を行った。交換処理速度を速めるために、12時間毎に溶液を交換して行った。その後、水洗し、真空中120℃で24時間乾燥を行い、プロトン交換体活物質を得た。
a=9.139Å(誤差:0.005Å以内)
b=4.081Å(誤差:0.003Å以内)
c=7.93Å(誤差:0.01Å以内)
β=101.9°(誤差:0.1°以内)
このようにして得られた層状ナトリウムチタン酸化物プロトン交換体H2Ti3O7活物質について、実施例1と同様にして電極を作製し、実施例1と同様のリチウム二次電池を作製した。このリチウム二次電池について、実施例1と同条件で電気化学的リチウム挿入・脱離試験を行ったところ、リチウム挿入・脱離反応に伴って、2.5Vから1.0Vまでなだらかに電圧が変化し、かつ、可逆的なリチウム挿入・脱離が可能であることが判明した。リチウム挿入量は、H2Ti3O7の化学式当たり1.64に相当し、活物質重量当たりの容量は174mAh/gであった。リチウム挿入・脱離反応に伴う電圧変化を、図5に示す。このことから、本発明による層状複合チタン酸化物活物質は、既存活物質であるスピネル型リチウムチタン酸化物(最大容量:170mAh/g)を越える高容量を可能とする材料であることが明白であり、リチウム二次電池の更なる高性能化が可能である。
実施例1で合成された層状ナトリウムチタン酸化物Na2Ti3O7の粉砕乾燥物を、あらかじめ280℃で溶融させた硝酸リチウムと塩化リチウムの混合溶融塩(モル比88:12)中に投入し、空気中260℃で10時間保持することによって、リチウムイオン交換処理を行った。その後、エタノールでよく洗浄し、自然乾燥することによって、リチウム交換体活物質を得た。
a=9.298Å(誤差:0.002Å以内)
b=3.746Å(誤差:0.001Å以内)
c=7.541Å(誤差:0.001Å以内)
β=97.69°(誤差:0.03°以内)
このようにして得られた層状ナトリウムチタン酸化物リチウム交換体(Li、Na)2Ti3O7活物質について、実施例1と同様にして電極を作製し、実施例1と同様のリチウム二次電池を作製した。このリチウム二次電池について、実施例1と同条件で電気化学的リチウム挿入・脱離試験を行ったところ、リチウム挿入・脱離反応に伴って、1.6V付近に電圧平坦部を有し、可逆的なリチウム挿入・脱離が可能であることが判明した。リチウム挿入量は、(Li、Na)2Ti3O7の化学式当たり1.48に相当し、活物質重量当たりの容量は147mAh/gであった。リチウム挿入・脱離反応に伴う電圧変化を、図6に示す。このことから、より残留するナトリウム量を少なく抑えることにより、高容量が期待でき、本発明による層状複合チタン酸化物活物質の使用により、リチウム二次電池の更なる高性能化が可能である。
2 負極端子
3 負極
4 セパレータ+電解液
5 絶縁パッキング
6 正極
7 正極缶
Claims (6)
- 式A2Ti3O7で表される複合チタン酸化物を主成分とし、結晶構造が単斜晶系のNa2Ti3O7型の層状構造であることを特徴とするリチウム二次電池用活物質。(式中、Aは、Na、Li、Hから選択された1種又は2種以上を示す)
- 単斜晶系の格子定数がA元素の種類と量比によって決定され、a軸長は、9.0〜9.4Å、b軸長が3.7〜4.1Å、c軸長が7.5〜8.5Å、β角が97〜102°の範囲である請求項1に記載のリチウム二次電池用活物質。
- ナトリウム化合物と酸化チタンから生成されたナトリウムチタン酸化物を出発原料として、イオン交換する工程によって合成されることを特徴とする請求項1に記載のリチウム二次電池用活物質の製造方法。
- 上記イオン交換の方法として、リチウム溶融塩を用いるリチウムイオン交換、或いは酸性溶液を用いるプロトン交換反応を適用することを特徴とする請求項3に記載のリチウム二次電池用活物質の製造方法。
- リチウム溶融塩を用いるリチウムイオン交換における熱処理温度が30℃から300℃の範囲内にある請求項3に記載のリチウム二次電池用活物質の製造方法。
- 正極及び負極として使用する2つの電極と、電解質からなるリチウム二次電池において、請求項1に記載のリチウム二次電池用活物質を含有する電極を構成部材として用いたリチウム二次電池。