JP2005154791A - 軟磁性粉末材料の製造方法 - Google Patents
軟磁性粉末材料の製造方法 Download PDFInfo
- Publication number
- JP2005154791A JP2005154791A JP2003391318A JP2003391318A JP2005154791A JP 2005154791 A JP2005154791 A JP 2005154791A JP 2003391318 A JP2003391318 A JP 2003391318A JP 2003391318 A JP2003391318 A JP 2003391318A JP 2005154791 A JP2005154791 A JP 2005154791A
- Authority
- JP
- Japan
- Prior art keywords
- soft magnetic
- oxidation
- oxide film
- magnetic powder
- gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 鉄を主成分とし、Si等の鉄よりも酸化反応性の高い第2の元素を含有する軟磁性合金粉末を用いる。この軟磁性合金粉末を、不活性ガスに水蒸気等の弱酸化性ガスを混入した弱酸化性雰囲気中において加熱し、鉄の酸化を抑制しつつ粉末表層部の第2の元素を選択的に酸化反応させて高電気抵抗の薄い酸化膜を形成する。
【選択図】 図1
Description
(1)磁気特性を向上させるには、SiやAl等が少ない方がよい。
(2)金属間化合物を形成しない固溶限界内とする。
(3)酸化膜の膜厚は、目標電気抵抗値を確保できる膜厚以上とする。
を考慮して決定される。例えば、(1)の磁気特性の向上のためには、これら元素の組成比を2%以下、好ましくは1%以下とするのがよく、この範囲で十分な酸化膜を形成できる最小限の組成比を選択するとよい。なお、上記軟磁性合金粉末を二種以上混合して使用してもよい。
酸素(O2 )による酸化の場合
2Fe+O2 →2FeO ・・・(式1)
Si+O2 →SiO2 ・・・(式2)
水蒸気(H2 O)による酸化の場合
Fe+H2 O →FeO+H2 ・・・(式3)
Si+2H2 O→SiO2 +H2 ・・・(式4)
ホールペッチの法則:σy =σ0 +k・d-1/2
ここで、σy は降伏応力、kは定数、dは軟磁性粉末の粒径である。
その上、製造工程が簡素で、生産性にも優れている。このようにして得られた軟磁性材料の焼結体は、内燃機関のソレノイドバルブやトランスのコア材といった各種軟磁性部品として有用である。
Claims (8)
- 表面を酸化膜で被覆した軟磁性粉末材料を製造する方法において、鉄を主成分とし鉄よりも酸化反応性の高い第2の元素を含有する軟磁性合金粉末を、不活性ガスに弱酸化性ガスを混入した弱酸化性雰囲気中で加熱し、粉末表層部の前記第2の元素を主に酸化反応させて、前記酸化膜を形成することを特徴とする軟磁性粉末材料の製造方法。
- 表面を酸化膜で被覆した軟磁性粉末材料を製造する方法において、鉄を主成分とし鉄よりも酸化反応性の高い第2の元素を含有する軟磁性合金粉末を、不活性ガスに弱酸化性ガスを混入した弱酸化性雰囲気中において加熱する酸化処理工程と、還元性雰囲気中において加熱する還元処理工程とを交互に行い、粉末表層部の前記第2の元素を主に酸化反応させて、前記酸化膜を形成することを特徴とする軟磁性粉末材料の製造方法。
- 前記第2の元素がSi、Ti、Al、Crから選択される少なくとも一種であることを特徴とする請求項1または2に記載の軟磁性粉末材料の製造方法。
- 前記弱酸化性ガスが水蒸気または一酸化二窒素ガスであることを特徴とする請求項1ないし3のいずれかに記載の軟磁性粉末材料の製造方法。
- 前記弱酸化性ガスを水蒸気とし、常温での相対湿度が50%より高くなるように前記不活性ガスに混入することを特徴とする請求項1ないし4のいずれかに記載の軟磁性粉末材料の製造方法。
- 前記弱酸化性ガスを水蒸気とし、常温での相対湿度が70%〜100%となるように前記不活性ガスに混入することを特徴とする請求項1ないし5のいずれかに記載の軟磁性粉末材料の製造方法。
- 前記酸化反応を、400〜900℃の温度条件下で行なうことを特徴とする請求項1ないし6のいずれかに記載の軟磁性粉末材料の製造方法。
- 前記軟磁性合金粉末は、平均粒径が0.01〜500μmのアトマイズ合金粉末であることを特徴とする請求項1ないし7のいずれかに記載の軟磁性粉末材料の製造方法。