CN1214095C - 用于金属材料塑性加工的水性润滑剂以及润滑薄膜的处理方法 - Google Patents

用于金属材料塑性加工的水性润滑剂以及润滑薄膜的处理方法 Download PDF

Info

Publication number
CN1214095C
CN1214095C CNB018169635A CN01816963A CN1214095C CN 1214095 C CN1214095 C CN 1214095C CN B018169635 A CNB018169635 A CN B018169635A CN 01816963 A CN01816963 A CN 01816963A CN 1214095 C CN1214095 C CN 1214095C
Authority
CN
China
Prior art keywords
water
lubricant
metallic substance
paraffin
based lubricant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CNB018169635A
Other languages
English (en)
Other versions
CN1468294A (zh
Inventor
今井康夫
永田秀二
吉田昌之
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nihon Parkerizing Co Ltd
Original Assignee
Nihon Parkerizing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nihon Parkerizing Co Ltd filed Critical Nihon Parkerizing Co Ltd
Publication of CN1468294A publication Critical patent/CN1468294A/zh
Application granted granted Critical
Publication of CN1214095C publication Critical patent/CN1214095C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

一种用于金属材料塑性加工的水性润滑剂，它包括：(A)水溶性无机盐，(B)选自二硫化钼和石墨的润滑剂，和(C)石蜡，其中这些成分是溶解或分散在水中的，(B)/(A)的浓度比(重量比)为1.0～5.0，(C)/(A)为0.1～1.0。一种金属材料上的润滑薄膜的处理方法，特征在于，通过在清洁的金属材料上涂覆干重为0.5～40g/m2的水性润滑剂形成润滑薄膜。水溶性无机盐(A)优选选自由硫酸盐、硅酸盐、硼酸盐、钼酸盐和钨酸盐组成的组中。石蜡(C)优选为可分散到水中、熔点为70～150℃的天然石蜡或合成石蜡。该水性润滑剂可容易地用于为上面未形成化学薄膜的金属表面提供优良的润滑性。

Description

用于金属材料塑性加工的水性润 滑剂以及润滑薄膜的处理方法
                          技术领域
本发明涉及一种用于诸如钢铁、不锈钢、钛、铝以及其它材料的金属材料塑性加工的水性润滑剂，其中的金属材料表面未经任何化学转化处理。另外，本发明还涉及该润滑剂的使用方法。
更具体而言，本发明涉及一种用于产生润滑薄膜的水性润滑油，所述润滑薄膜适合在诸如钢铁、不锈钢、钛、铝以及其他材料的金属材料的表面上进行塑性变形加工，所述塑性变形加工例如锻造、拉丝、管材拉拔和其他加工，其中金属材料表面未经任何化学转化处理。
                          技术背景
在对诸如钢铁、不锈钢和其他材料的金属材料实施冷塑性加工时，为了防止因金属材料与工具间的金属接触而产生的燃烧缺陷和磨损缺陷，通常要在金属材料表面上设置润滑薄膜。
考虑到要在金属表面上设置润滑薄膜，存在着使润滑剂以物理方式粘附到金属表面上的润滑薄膜，以及通过提前对金属材料进行化学转化处理、然后将润滑剂涂敷到化学转化层上从而在金属表面上形成化学转化层的其它润滑薄膜。
以物理方式粘附到金属表面上的润滑剂通常用于微减量的冷加工，这是因为它们的粘附力要弱于涂敷到化学转化层上的润滑剂的粘附力。
在利用化学转化薄膜过程中，要在金属表面上设置磷酸盐薄膜或草酸盐薄膜，这些薄膜扮演着作为其上涂敷的润滑剂的载体的角色。该类型的润滑薄膜由2层构成：载体层和润滑剂层，该润滑薄膜表现出非常优良的耐受金属材料燃烧缺陷的性能。其广泛用于诸如拉丝、管材拉拔、锻造以及其他加工的冷加工。除了用于高减量的冷加工领域之外，它还广泛用于提供磷酸盐薄膜或草酸盐薄膜，然后在这些薄膜上涂覆润滑剂。
根据用途可将化学转化层上涂覆的润滑剂分为两类。第一类包括以机械方式粘附到化学转化层上的润滑剂，第二类包括与化学转化层起反应的润滑剂。
第一类润滑剂包括：利用矿物油、植物油或合成油作为基础油而制备的那些润滑剂，所述基础油中含有极压添加剂；还包括通过将诸如石墨和二硫化钼之类的固体润滑剂与粘合剂成分一起溶解到水中而制得的另一种润滑剂。这些润滑剂要经过粘附并干燥。
由于第一类润滑剂能通过喷涂或浸涂方式方便地使用，因此对于溶液处理而言这些润滑剂具有方便使用的优点。但是，由于它们仅具有较低的润滑性，所以倾向于将它们用于需要金属材料形变量小的情况。
另一方面，在第二类润滑剂中，是将例如硬脂酸钠之类的活性皂用于需要高润滑性的冷加工。活性皂与化学转化层反应，形成高润滑性的层。
但是，因为活性皂引起了化学反应，因此处理过程中溶液的成分控制、化学反应的温度控制、以及通过从溶液中排出废物而对品质退化溶液进行的再生控制等变得非常重要。
近来，为了全球的环境保护，减少工业废弃物成为一个大问题。所以，现在非常渴望不会排出废物的新型润滑剂和新型润滑处理方法。另外，还渴望一些新处理方法来简化对上述第二类中的处理方法和溶液的复杂控制。
为了解决上述问题，JP52-20967A中已经公开了一种润滑剂组合物，它包括：作为基本成分的水溶性聚合物或其水乳液，固体润滑剂和成膜剂。但是，还没得到象利用了化学转化层的传统方法中那样具有相同程度的较好效果的组合物。
为了解决上述问题，已经披露了另一项现有技术JP10-8085A。该现有技术涉及用于金属材料塑性加工的水性润滑剂，其中(A)水溶性无机盐、(B)固体润滑剂、(C)选自矿物油、动物油、植物油和合成油的组中的至少一种油、(D)表面活性剂、以及E)水都得到很好分散并均匀乳化。但是，由于必须让油性成分保持乳化状态，而它又表现出不稳定的性质，因此依照该现有技术的润滑剂太不稳定，以致不能在工业领域使用。
引用发明JP2000-63880A作为另一项现有技术。该现有技术涉及用于金属材料塑性加工的润滑剂，该润滑剂包括(A)合成树脂、(B)水溶性无机盐和水，其中，固体状态下(B)/(A)的重量比范围为0.25/1到9/1，合成树脂在组合物中保持溶化或分散状态。但是，由于该组合物的主要成分是合成树脂，因此在缩小量大的冷加工过程中，该组合物在展现高润滑性方面还不稳定。
所以本发明的目的是提供一种用于金属材料塑性加工的水性润滑剂以及润滑薄膜的处理方法，其中，金属材料未经任何化学转化处理，其解决了传统方法中存在的问题，改善了全球环境保护方面的问题，可将它们用到多种金属材料上。
                         发明内容
本发明研究了解决上述问题的方法，并发现：利用含特定比例的水溶性无机盐、选自二硫化钼和石墨的润滑剂和石蜡的水溶液能获得优良的润滑性能。还找到了一种在金属表面上形成润滑薄膜的处理方法，该方法可以节约处理能源和处理空间。
即，本发明是一种用于金属材料加工的水性润滑剂，它包括(A)水溶性无机盐、(B)选自二硫化钼和石墨的润滑剂、以及(C)石蜡，这些成分都溶解或分散于水中，固体状态下(B)/(A)的重量比范围为1.0-5.0，固体状态下(C)/(A)的重量比范围为0.1-1.0。
优选的是，上面的(A)是选自硫酸盐、硅酸盐、硼酸盐、钼酸盐以及钨酸盐的组中的一种或多种水溶性无机盐，并且优选的是，上面的石蜡是熔点介于70-150℃之间的水分散型天然石蜡或合成石蜡。
另外，本发明是一种在金属材料表面上形成粘附重量为0.5～40g/m2的润滑薄膜的方法，其中可将上述水性润滑剂涂覆到金属材料的洁净表面上，然后干燥。优选的是让金属材料表面预先经受选自喷丸处理、喷砂处理、碱洗脱脂的组中的一项或多项过程的清洁处理，另外优选的是，在金属材料加热到60-100℃以后，再将水性润滑剂涂覆到金属材料表面上。
                         附图说明
图1：后方冲压(rear punching)试验的示意图。
图2：成钉(spike)试验的示意图。
                     具体实施方式
现在将进一步详细解释本发明。为了赋予涂膜一定的硬度和强度，纳入了本发明的水性润滑剂中使用的水溶性无机盐(A)。为了该目的，要求该水溶性无机盐具备能均匀溶解到水溶液中、干燥后形成牢固润滑薄膜的性能。
作为具备该性能的无机盐，优选的是利用至少一种选自由硫酸盐、硅酸盐、硼酸盐、钼酸盐和钨酸盐组成的组中的盐。作为上述无机盐的例子，可给出硫酸钠、硫酸钾、硅酸钾、硼砂(四硼酸钠)、硼酸钾(四硼酸钾)、硼酸铵(四硼酸铵)、钼酸铵、钼酸钠和钨酸钠。这些盐中的任何一种都可以单独使用，也可以将2种或多种盐结合使用。
本发明中，为了增强润滑性能，可以使用选自二硫化钼和石墨中的一种或多种的润滑剂(B)。将它们以分散形式纳入进来，需要时可以使用公知的表面活性剂。
(B)/(A)、即水溶性无机盐(A)和润滑剂(B)的固态重量比范围优选为1.0-5.0，更优选为2.0-4.0。当该比例小于1.0时，润滑膜的滑动性会降低，这是不理想的。但是，当比例大于5.0时，水性润滑剂变得不稳定，这是不理想的。
对于石蜡(C)，尽管对它们的化学结构和类型没有特别限制，但优选使用天然石蜡或合成石蜡。石蜡可能因金属材料的塑性形变过程中产生的热量而熔融，由此改善了涂层的润滑性能。基于该原因，优选使用熔点介于70～150℃且在水性润滑剂中保持稳定的那些石蜡，以及使用不会降低润滑薄膜的强度以便从塑性加工的初期阶段就能展现优良润滑性的石蜡。
这些石蜡的实际例子包括：硬石蜡，微晶石蜡，矿脂蜡，fisher·tropsch石蜡，聚乙烯石蜡，聚丙烯石蜡，棕榈蜡，山地蜡等。这些石蜡优选结合其它组分使用，它们以水分散体或水乳液的形式被包含到本发明的水性润滑剂中。
(C)/(A)、即水溶性无机盐(A)与石蜡(C)的固态重量比优选在0.1～1.0的范围内，更优选在0.2～0.8的范围内。当该比例低于0.1时，润滑薄膜的滑动性不足，而当比例高于1.0时，涂层的粘附性就会不足。
在形变量大的冷加工过程中，还可以向本发明的水性润滑剂中加入另一种油或另一种固态润滑物质。
当为了将润滑物质和石蜡分散到水性润滑剂中而需要表面活性剂时，可以使用非离子、阴离子、两性和阳离子型中的任何表面活性剂。尽管不作限制，但非离子表面活性剂可包括：聚氧乙烯烷基醚，聚氧化烯(乙烯或丙烯)烷基苯基醚，含聚乙烯醇(或环氧乙烯)和高级脂肪酸(例如C12～C18)的聚氧化乙烯烷基酯，含山梨糖醇酐、聚乙烯醇以及高级脂肪酸(例如C12～C18)的聚氧化乙烯山梨糖醇酐烷基酯。
尽管没有任何限制，但阴离子表面活性剂包括：脂肪酸盐，硫酸酯盐，磺酸盐，磷酸酯盐，以及二硫代磷酸酯盐。尽管不作限制，但两性表面活性剂可包括：氨基酸结构或内铵盐结构的羧酸盐，硫酸酯盐，磺酸盐，磷酸酯盐。
尽管没有任何限制，但阳离子表面活性剂包括脂肪酸的胺盐、季铵盐等。
这些表面活性剂中的每一种都可以单独使用，或者两种或两种以上结合使用。
在用公知的磷酸盐层(磷酸锌，磷酸镁，磷酸铁，磷酸锡等)、草酸盐(草酸铁等)、氟铝酸钠和铝酸钙层的形成方法涂覆了钢铁、不锈钢、铜或铜合金、铝或铝合金、钛或钛合金之类的金属材料时，还可将本发明的水性润滑剂用作冷加工(拉丝、管材拉拔、锻造等)的润滑剂。
对金属材料的形状不作特别限制，不仅可以使用棒材和铸锭，而且还可以使用通过热锻造制得的成形产品(齿轮、轴等)。
依照本发明的润滑薄膜形成方法，可让净化过的金属材料表面与前述水性润滑剂接触，然后干燥，于是在金属材料表面上形成0.5～40g/m2的润滑薄膜。因此本发明的润滑薄膜处理工艺是不反应型的。可根据塑性冷加工的形变程度调整要在金属表面上形成的润滑薄膜量。其范围更优选为2～20g/m2。
当该量值低于0.5g/m2时，润滑性变得不足。当其大于40g/m2时，尽管在润滑性方面不会出现特殊问题，但在加工过程中会出现渣滓，产生的渣滓会填满工具表面上设置的凹腔。可根据金属材料的表面积和处理前后的重量差来计算润滑薄膜的量。
可以调整各成分的重量浓度来调整上述润滑薄膜的量。许多情况下，可通过用水稀释浓缩的水性润滑剂来获得处理溶液。对用于该稀释目的的水没有限制，但是去离子水或蒸馏水是优选的。
在本发明的润滑薄膜处理过程中，金属材料的表面清洁优选通过选自以下处理中的一个或多个清洁步骤进行，所述处理包括喷丸处理，喷砂处理，碱洗脱脂处理。这些处理的主要目的是清除退火过程中产生的氧化皮或清除油或其它污染物。
近来，从环境观点出发希望减少废水的处理量。在本发明中，例如通过喷丸处理来清洁表面同时利用本发明的水性润滑剂来形成润滑薄膜可将废水减少到零。
对于将本发明的水性润滑剂涂覆到金属材料表面上的方法没有特别限制。可以采用浸渍法、流动涂覆法、喷涂法和其它方法。当表面被水性润滑剂充分覆盖时，涂覆就足够了，在涂覆时间方面没有任何限制。
涂覆之后，必须让水性润滑剂干燥。可通过将其保持在常温下进行干燥，将其保持在60～150℃下达10～60分钟也是优选的。
为了提高干燥效率，优选的是在将金属材料加热到60～100℃以后再涂覆水性润滑剂。此外，在将水性润滑剂加热到50～90℃以后再涂覆该润滑剂也是优选的。
这样就能大大提高干燥效率，并能大幅降低热能损耗。
举例
通过展示实施例和比较例来更实际地解释本发明的有益效果。
(后方冲压试验的试样)
从市场上购买JIS S45C的一系列钢棒试样，对它们进行球化(spherodizing)退火处理，如图(A)所示，其直径为30mm，系列高度为18～40mm，每根棒材的高度彼此相差2mm。
(成钉试验的试样)
从市场上购买JIS S45C的钢棒试样，对它们进行球化退火处理，其直径为25mm，高度为30mm。
(处理过程)
·过程A
(1)脱脂：使用市场上出售的脱脂剂(由Nihon Parkerizing有限公司生产的FINE CLEANERR 4360)，浓度：20g/L，温度：60℃，浸渍时间：10分钟。
(2)清洗：用自来水，60℃，浸渍30秒。
(3)润滑处理：在60℃度下与润滑剂接触，浸渍10秒钟。
(4)干燥：在80℃干燥3分钟。
·过程B
(1)喷丸处理：颗粒直径：0.5mm，处理5分钟。
(2)清洗：用自来水在90℃浸渍90秒。
(3)润滑处理：使其在70℃与润滑剂接触，浸渍5秒钟。
(4)干燥：室温下(吹风)3分钟。
(后方冲压试验)————图1
利用图1(B)的200吨曲轴压力机对图1(A)中的一系列钢棒试样进行冷加工，制造出图1(C)所示的一系列杯形制品。每次冲压时都留下10mm的底部，横截面积的减量为50％。检查杯子的内表面上的缺陷，将未观察到缺陷的杯子的最大深度(Zmm)作为冲压深度(mm)示于表1中。该试验中，模具材料是JIS SKDI I，冲压材料为JISHAP40，冲压直径为21.21mm，每分钟冲压30次。
(成钉试验)————图2
按照与JP5-7969A中所示方式相同的方式进行成钉试验。
模具(1)的内表面为类似漏斗的形状。将棒材试样(2)置于图2(A)所示的模具(1)的顶部，然后施压，如图2(B)所示，使试样(2)底部被压迫进入模具(1)的漏斗孔。通过该过程就制出了形状与漏斗相应的长钉。将所得长钉的高度作为长钉高度示于表1中。当长钉具有很大的长钉高度时，润滑效果优良。
(实施例1)
在上述处理过程A中使用下面的水性润滑剂1(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂1
水溶性无机盐：四硼酸钠，
润滑剂：二硫化钼
石蜡：聚乙烯石蜡
比例(B/A)：3.0
比例(C/A)：0.4
形成的薄膜量，g/m2：15
(实施例2)
在上述处理过程B中使用下面的水性润滑剂2(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂2
水溶性无机盐：四硼酸钠
润滑剂：石墨
石蜡：聚乙烯石蜡
比例(B/A)：2.0
比例(C/A)：0.8
形成的薄膜量，g/m2：15
(实施例3)
在上述的处理过程A中使用下面的水性润滑剂3(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂3
水溶性无机盐：硅酸钠，
润滑剂：石墨
石蜡：聚乙烯石蜡
比例(B/A)：1.0
比例(C/A)：1.0
形成的薄膜量，g/m2：15
(实施例4)
在上述的处理过程A中使用下面的水性润滑剂4(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂4
水溶性无机盐：钨酸钠
润滑剂：二硫化钼
石蜡：固体石蜡
比例(B/A)：4.0
比例(C/A)：0.1
形成的薄膜量，g/m2：15
(实施例5)
在上述的处理过程B中使用下面的水性润滑剂5(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂5
水溶性无机盐：硫酸钾
润滑剂：二硫化钼
石蜡：硬石蜡
比例(B/A)：3.0
比例(C/A)：0.5
形成的薄膜量，g/m2：15
(比较例1)
在上述的处理过程A中使用下面的水性润滑剂6(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂6
水溶性无机盐：硫酸钠，
石蜡：硬石蜡
比例(C/A)：0.1
形成的薄膜量，g/m2：10
(比较例2)
在上述的处理过程B中使用下面的水性润滑剂7(为了分散而含有1wt％的非离子表面活性剂)。
水性润滑剂7
水溶性无机盐：硫酸钠，
润滑剂：二硫化钼
比例(B/A)：0.5
形成的薄膜量，g/m2：15
(比较例3)
按照下面的处理过程C进行处理。
·过程C
(1)脱脂：利用市场上出售的脱脂剂(由Nihon Parkerizing有限公司生产的FINE CLEANERR 4360)，浓度：20g/L，温度：60℃，浸渍时间：10分钟。
(2)清洗：用自来水，室温，浸渍30秒。
(3)化学转化处理：使用从市场上购买的含有磷酸锌的化学转化试剂(由Nihon Parkerizing有限公司生产的PALBONDR 181X)，浓度：90g/L，温度：80℃，浸渍时间：10分钟。
(4)清洗：用自来水，室温，浸渍30秒钟。
(5)皂洗处理：市场上出售的活性皂润滑剂(由NihonParkerizing有限公司生产的PALUBER 235)，浓度：70g/L，温度80℃，浸渍时间：5分钟。
(6)干燥：80℃，3分钟。
(比较例4)
在处理过程A中使用下面的水性润滑剂8。
水性润滑剂8
水溶性无机盐：硼砂：10％
润滑剂：硬脂酸钙：10％
油组分：棕榈油；0.5％
表面活性剂：聚氧乙烯烷基醇；1％
其它：水
形成的薄膜量，g/m2：10
(比较例5)
在过程A中使用下面的水性润滑剂9(为分散而含有1wt％的非离子表面活性剂)。
水性润滑剂9
水溶性无机盐：四硼酸钠
合成树脂：尿烷树脂
脂肪酸的金属盐：硬脂酸钙
固态(水溶性无机盐/合成树脂)的比例＝2/2
固态(硬脂酸钙/合成树脂)的比例＝3/1
形成的薄膜量，g/m2：10
试验结果示于表1中。从表1中可以清楚看到，使用了依照本发明的金属材料加工用水性润滑剂的实施例1～5展现出极好的润滑性以及简单易行的处理工艺。
不含润滑剂的比较例1和不含石蜡的比较例2在润滑性能方面要差一些。在比较例3中利用了磷酸盐和反应皂的化学转化层的传统工艺进行处理，其润滑性与本发明中的一样优良。但是，会由化学转化反应产生大量废物，处理这些废水和控制水性润滑剂时必需要有专用的复杂设备，保护环境的负担加重。
另外还证明，在与JP10-8085A所示内容相同的比较例4的成钉试验中润滑性较差，在与JP2000-63880A所示内容相同、以合成树脂为主要成分的比较例5中润滑性也较差。
发明优点
由上面的描述显而易见的是，利用本发明的水性润滑剂和本发明的润滑薄膜处理方法，经过简单易行的处理就能形成高润滑性的薄膜。另外，还降低了废物产生量，使较好的环境保护成为可能。因此，本发明具有很大的工业实用性。
                           表1
  处理过程中的步骤数   处理   冲压深度(mm)     长钉高度(mm)
实施例1   4   涂覆型   60     13.2
实施例2   4   涂覆型   60     13.2
实施例3   4   涂覆型   60     13.2
实施例4   4   涂覆型   60     13.1
实施例5   4   涂覆型   60     13.1
比较例1   4   涂覆型   40     11.6
比较例2   4   涂覆型   40     11.7
比较例3   4   反应型/废物多   56     13.0
比较例4   4   涂覆型   56     12.5
比较例5   4   涂覆型   56     12.6

Claims (4)

1.一种用于金属材料塑性加工的水性润滑剂，该金属材料在应用前不经受酸洗，
其包括：
(A)水溶性无机盐；
(B)选自二硫化钼和石墨中的一种或一种以上的润滑剂；以及
(C)石蜡，这些成分溶解或分散在水中，(B)/(A)的固态重量比范围为1.0～5.0，(C)/(A)的固态重量比范围为0.1～1.0。
2.根据权利要求1所述的用于金属材料塑性加工的水性润滑剂，其中水溶性无机酸是选自硫酸盐、硅酸盐、硼酸盐、钼酸盐和钨酸盐的组中的一种或一种以上的水溶性无机盐。
3.根据权利要求1～2中任一项所述的用于金属材料塑性加工的水性润滑剂，其中石蜡是熔点为70～150℃的水分散型天然石蜡或合成石蜡。
4.根据权利要求1所述的用于金属材料塑性加工的水性润滑剂，其中，在应用前不经受酸洗的所述金属材料是经下述处理方法清洁且在其应用前不经受酸洗的金属材料，所述处理方法包括喷丸处理、喷砂处理、碱洗处理至少之一。
CNB018169635A 2000-08-07 2001-04-26 用于金属材料塑性加工的水性润滑剂以及润滑薄膜的处理方法 Expired - Lifetime CN1214095C (zh)