CN106694009B - 合金催化剂用于碳水化合物催化制备低碳二元醇的方法 - Google Patents
合金催化剂用于碳水化合物催化制备低碳二元醇的方法 Download PDFInfo
- Publication number
- CN106694009B CN106694009B CN201510770769.6A CN201510770769A CN106694009B CN 106694009 B CN106694009 B CN 106694009B CN 201510770769 A CN201510770769 A CN 201510770769A CN 106694009 B CN106694009 B CN 106694009B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- reaction
- tin
- metallic
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种合金催化剂用于碳水化合物催化制备低碳二元醇的方法。该方法以碳水化合物为反应原料，以水作溶剂，以锡与过渡金属铁、钴、镍、钌、铑、钯、铱、铂、铜中的一种或两种以上二者构成的合金为催化剂，在120‑300℃，氢气压力1‑13MPa的水热条件下经过一步催化转化过程，实现碳水化合物高效、高选择性、高收率制备乙二醇等低碳二元醇。与现有的石油基乙二醇合成路线相比较，本发明所提供的反应具有原料为可再生资源、原子经济性高、环境友好的优点。此外，与其他的以生物质为原料制多元醇的技术相比较，本过程具有催化剂稳定流失量极低、循环性好、易于回收等优点。
Description
技术领域
本发明涉及一种合金催化剂用于催化转化碳水化合物到低碳二元醇的方法，具体地说是碳水化合物在水热条件下经催化制备乙二醇的过程。
背景技术
乙二醇等低碳二元醇是重要的能源液体燃料，也是非常重要的聚酯合成原料。乙二醇主要用于合成聚对苯二甲酸乙二酯(PET)和聚萘二甲酸乙二醇酯(PEN)，还可以用作防冻剂、润滑剂、增塑剂、表面活性剂，是用途广泛的有机化工原料。
目前，乙二醇的工业生产主要是采用石油原料路线，即乙烯环氧化后得到环氧乙烷，然后水合得到乙二醇【文献1：崔小明，国内外乙二醇生产发展概况，化学工业，2007，25，(4),15-21.文献2：Process for preparing ethanediol by catalyzing epoxyethanehydration，Patent No.CN1463960-A；CN1204103-C】。乙二醇的合成方法依赖于不可再生的石油资源，而且生产过程中包括选择氧化或环氧化步骤，技术难度大，效率低，副产物多，能耗高且污染严重。
利用具有可再生性的生物质制备乙二醇，可以减少人类对化石能源物质的依赖，有利于实现环境友好和经济可持续发展。纤维素等碳水化合物是地球上产量最大的可再生资源，来源非常丰富，利用成本非常低廉。利用纤维素等碳水化合物制乙二醇不仅可以开辟新的合成路径，实现由廉价的碳水化合物得到高经济价值的产品。而且，由于纤维素等部分碳水化合物不能被人类食用，因而不会对人类的粮食安全造成影响。
目前，通过水热条件下催化加氢转化纤维素制备乙二醇【文献1：Directcatalytic conversion of cellulose into ethylene glycol using nickel-promotedtungsten carbide catalysts，Angew.Chem.Int.Ed.2008,47,8510-8513；文献2：Transition metal-tungsten bimetallic catalysts for the conversion ofcellulose into ethylene glycol，ChemSusChem 2010,3,63-66；文献3：CN 102190562 A，一种多羟基化合物制乙二醇的方法】。该方法以钨基催化剂和加氢催化剂组成的复合催化剂对纤维素进行催化转化，从而获得60-75％的乙二醇。
类似地，通过玉米芯水解获得木糖，进而通过催化加氢裂解同样可以得到乙二醇、丙二醇和甘油的混合物【文献4:CN 101704710 A一种玉米芯催化转化制乙二醇、丙二醇、丙三醇的方法】。该方法可以获得30％的乙二醇和丙二醇的选择性。
本发明所提供的方法以碳水化合物为原料，以水为反应介质，在合金催化剂作用下，通过一步反应过程，即可以实现碳水化合物高效转化为低碳二元醇。此方法不仅操作简单，成本低廉，而且催化剂稳定流失量极低，循环性好、易于回收。
发明内容
本发明的目的在于提供一种快速、高效催化转化碳水化合物到低碳二元醇的方法，所述低碳二元醇为乙二醇、1,2-丙二醇。较常规过程此方法操作简单，成本低廉，催化剂稳定流失量极低，循环性好、易于回收等特点。
为实现上述目的，本发明采取的技术方案为：
以碳水化合物为反应原料，在高压反应釜内，于水中进行催化加氢反应，
所采用的合金催化剂由至少两种以上的金属前驱体制备得到；
合金催化剂中含有金属锡，其余金属元素为过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的一种或二种以上，合金催化剂中金属锡与其余金属的重量比在0.01-100范围之间；
或，催化剂使用前由复合前体构成，其中一种前驱体为锡的单质或化合物中的一种或二种以上，其余的金属前驱体为过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上，反应过程中形成合金，合金催化剂中金属锡与其余金属的重量比在0.01-100范围之间；
或催化剂为金属锡与金属镍合金构成的骨架金属催化剂；
反应于密闭间歇式、连续式或半连续式高压反应釜中搅拌进行；反应前反应釜中充填氢气，反应温度≥120℃，反应时间不少于5分钟，或液体反应空速不大于20h-1。
在使用过程中，合金催化剂的重量浓度为反应物与反应溶剂质量总合的0.1％-50％。
反应前反应釜中充填氢气，室温时氢气的初始压力为1-12MPa；反应温度≥120℃，温度上限以反应产物不发生热分解为准。
反应温度为200-280℃，室温下反应釜中氢气压力3-7MPa，对于密闭间歇式反应釜的反应时间为0.5-5h，对于半连续或连续式高压反应釜，反应空速GWSV为0.1-50h-1，GWSV代表流动状态下反应物每小时进入反应器的干基重量与反应器中催化剂重量的比值。半连续高压反应釜工作方式：在反应温度和压力条件下，物料采用连续注入的方式进入到反应釜中，物料加入完毕后，停止物料加入并待反应结束后，一次性取出反应产物。
所述合金催化剂为非负载型催化剂，即以合金金属作为催化剂骨架的骨架金属催化剂，骨架金属催化剂中金属锡与其余金属的重量比在0.1-10范围之间，反应釜中合金骨架催化剂的重量浓度为1％-30％。
所述骨架金属催化剂中金属锡与其余金属的重量比在0.5-2范围之间，反应体系中合金催化剂的重量浓度在2％-20％。
所述合金催化剂为负载型催化剂，将金属锡组分与金属组分铁、钴、钌、铑、钯、铱、铂、铜中的一种或两种以上共同负载在同一载体上，所述载体为活性炭、氧化铝、氧化硅、碳化硅、氧化锆、氧化锌、二氧化钛一种载体或二种以上的复合载体，合金于催化剂上的含量在0.01-50wt％，金属锡与其余金属的重量比在0.1-10范围之间。合金于催化剂上的优选含量在1-35wt％，金属锡与其余金属的重量比优选在0.5-2范围之间。
将锡的单质或化合物中的一种或二种以上作为载体，将过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上担载在作为载体的锡的单质或化合物上，过渡金属于催化剂上的含量在0.01-50wt％；
或，将过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上作为载体，将锡的单质或化合物中的一种或二种以上担载在作为载体的过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合上，锡于催化剂上的含量在0.01-50wt％。
反应原料与水的用量以反应条件下反应物料部分或完全为液态即可；所述碳水化合物为纤维素、淀粉、半纤维素、菊芋、蔗糖、葡萄糖、甘露糖、果糖、果聚糖、木糖、阿拉伯糖、可溶性低聚木糖、赤藓糖、壳聚糖、中的一种或二种以上；
锡的单质或化合物为金属锡、氟化亚锡、氯化亚锡、溴化亚锡、碘化亚锡、氟化锡、氯化锡、溴化锡、碘化锡、氢氧化锡、氢氧化亚锡、氧化亚锡、二氧化锡、硫酸亚锡、醋酸锡、草酸亚锡、锡酸钠、锡酸钾、锡酸钙、磷化锡、焦磷酸锡中的一种或二种以上；
过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物为金属铁、金属钴、金属钌、金属铑、金属钯、金属铱、金属铂、金属铜、兰尼铁、兰尼钴、兰尼铜、硝酸铁、硝酸钴、硝酸钌、硝酸铑、硝酸钯、硝酸铱、硝酸铂、硝酸铜、氯化铁、氯化钴、氯化钌、氯化铑、氯化钯、氯化铱、氯化铂、氯化铜、三氧化二铁、四氧化三铁、氧化亚铁、硫酸铁、氧化亚钴、三氧化二钴、四氧化三钴、硫酸钴、硫酸镍、氧化铜、硫酸铜中的一种或二种以上。
本发明有如下优点：
1.以自然界生物质中产量的最大的纤维素等类碳水化合物为原料，其来源广泛，成本低廉。而且，相对于现有的乙二醇工业合成路线中使用乙烯为原料，本发明所提供的反应过程不消耗化石资源，具有原料资源可再生的优点，符合可持续发展的要求，对废物利用、农民增收具有重要的意义。
2.此合金催化剂结构稳定，金属流失量极低。
3.在催化剂稳定使用状态下，催化剂呈中性或弱碱性，因而长期使用对反应装置腐蚀性小，可大大节省设备投入，工业应用前景好。
4.作为多相催化剂，此合金催化剂易于从反应液中分离，循环性能好。
下面通过具体实施例对本发明进行详细说明，但这些实施例并不对本发明的内容构成限制。
附图说明
图1为水热法制备的骨架型镍锡合金催化剂的XRD图谱。
具体实施方式
实施例1
负载型合金催化剂制备：将活性炭、氧化铝、氧化硅、碳化硅、氧化锆、氧化锌、二氧化钛一种或二种以上作为载体，将锡的金属盐水溶液和过渡金属铁、钴、镍、钌、铑、钯、铱、铂的金属盐水溶液通过等体积浸渍法共同负载到载体上，在120℃下干燥过夜。用氢气在300℃下还原2h，在1％O2/N2(V/V)气氛下钝化4h。
实施例2
二氧化锡负载镍催化剂制备：称取1.5g SnO2，1.8g Ni(NO3)2·6H2O，将氯化钌溶于20ml水中，再将SnO2加入到溶解完全的氯化钌溶液中，在25℃水浴条件下，搅拌12h至溶液蒸发完全。在120℃烘箱中干燥8h，在N2气氛，300℃下焙烧2h，然后在H2气氛，300℃下还原2h。
实施例3
三氧化二铁负载锡催化剂制备：称取1.5g Fe2O3，0.9g SnCl4·5H2O，将四氯化锡溶于20ml水中，再将Fe2O3加入到溶解完全的四氯化锡溶液中，在25℃水浴条件下，搅拌12h至溶液蒸发完全。在120℃烘箱中干燥8h，在N2气氛，300℃下焙烧2h，然后在H2气氛，300℃下还原2h。
实施例4
金属加氢催化剂制备：将活性炭、氧化铝、氧化硅、碳化硅、氧化锆、氧化锌、二氧化钛一种或二种以上作为载体，将氯铂酸、氯化钯、氯化钌、氯化铑、氯化铱、硝酸镍、硝酸铁、硝酸钴、硝酸铜的水溶液通过等体积浸渍法分别负载到载体上，在120℃下干燥过夜。
以上负载钌、铑、钯、铱、铂等贵金属的催化剂在使用前，需用氢气在250℃下还原2h，在1％O2/N2(V/V)气氛下钝化4h；负载镍、铁、钴、铜等非贵金属的催化剂在使用前，需用氢气在450℃下还原2h，在1％O2/N2(V/V)气氛下钝化4h。
实施例5
合金催化剂原位制备：将锡的单质或化合物中的一种或二种以上与金属加氢催化剂或骨架型金属催化剂共同加入到反应釜中，按照实施例7的反应条件加入反应物和溶剂水，充入氢气，升至反应温度开始反应，在反应中原位生成合金催化剂。
实施例6
骨架型合金催化剂制备：采用水热制备方法。将含有0.6g金属锡与1.0g骨架型金属催化剂兰尼镍共同加入到水热合成釜中，加入10-100mL的水作溶剂，充入7MPa压力的氢气，在250℃下水热处理3h，将过滤得到催化剂在120℃下干燥过夜。由图1可以看出制备得到的合金催化剂，经XRD表征确认形成了镍锡合金。
实施例7
催化转化实验：将0.25g碳水化合物，一定质量的复合催化剂和25ml水加入到75ml反应釜中，然后通入氢气置换六次气体后，充氢气至5MPa，升温到一定温度，反应30-240min。反应结束后，降至室温，取离心后的上清液体，在高效液相色谱上分析检测。产物收率中仅对目标产物乙二醇、丙二醇以及六元醇(包括山梨醇、甘露醇)进行计算。
实施例8
负载型合金催化剂下微晶纤维素的催化转化结果对比。合金催化剂中，一种金属组分为锡，负载量为3％，另一种金属组分为不同过渡金属，负载量为5％，反应条件同实施例7。
表一负载型合金催化剂下纤维素催化转化的结果(负载型合金催化剂质量为0.1g；反应温度为245℃，反应时间为95min)
如表一所示，负载型合金催化剂对乙二醇的生成具有促进作用，对比合金催化剂和单过渡金属加氢催化剂上乙二醇和六元醇的收率，可以看到合金的形成促使乙二醇的收率明显提高，六元醇收率明显降低。
实施例9
非负载型合金催化剂下微晶纤维素的催化转化结果对比。非负载型合金催化剂中，一种金属组分为锡，另一种金属组分为不同过渡金属，反应条件同实施例7。
表二非负载型合金催化剂下纤维素催化转化的结果(非负载型合金催化剂质量为0.05g，催化剂中锡与镍、铜、钴的质量比分别为1:3,1:5,1:2.5；反应温度为245℃，反应时间为95min)
如表二所示，非负载型合金催化剂对乙二醇的生成也具有促进作用，对比合金催化剂和兰尼单金属催化剂上乙二醇和六元醇收率，可以看到合金的形成促使乙二醇的收率明显提高，六元醇收率明显降低。
实施例10
合金催化剂为负载型合金催化剂RuSn/AC，Sn与Ru的质量比为1:3.5，Ru在催化剂上的负载量为5％。反应条件同实施例7，催化剂在不同碳水化合物上的催化转化结果(表三)。
表三合金催化剂在不同碳水化合物上的催化转化结果(RuSn/AC质量为0.1g；反应温度为245℃，反应时间为95min)
如表三所示，RuSn合金催化剂在碳水化合物转化过程中对乙二醇和丙二醇的总选择性要高于山梨醇，说明此合金催化剂对含有不饱和化学键的糖类碳水化合物具有很好的断裂碳碳键的作用。以纤维素作原料得到的乙二醇的收率高于其他碳水化合物。反应中，乙二醇、丙二醇的相对选择性与原料的种类由一定的关系，当原料中含有果糖或者可以被异构为果糖时，丙二醇的收率提高。另一方面，该合金催化剂对山梨醇催化活性极低，不能选择性断裂山梨醇中的碳碳键生成乙二醇和丙二醇，类似地对木糖醇、甘油的转化效果也很差。
实施例11
反应时间的影响。合金催化剂为负载型合金催化剂PtSn/AC(0.5％Sn，5％Pt)不同反应时间下纤维素催化转化结果(表四)。除反应时间不同外，反应条件同实施例7。
表四不同反应时间下合金催化剂上纤维素催化转化结果(PtSn/AC质量为0.1g；反应温度为245℃)
如表四所示，在一定时间范围内，此合金催化体系均有较好的乙二醇收率。较佳时间为1h-2.5h。
实施例12
反应温度的影响。合金催化剂为负载型合金催化剂5％Ir3.5％Sn/AC，不同反应温度下纤维素催化转化结果(表五)，反应条件同实施例7。
表五不同反应温度下合金催化剂上纤维素催化转化结果(IrSn/AC质量为0.2g；反应时间为95min)
如表五所示，在一定温度范围内，此合金催化体系均有较好的乙二醇收率。较佳温度为230-260℃。
实施例13
合金催化剂上锡铱质量比例的影响。合金催化剂为负载型合金催化剂IrSn/AC，不同Sn/Ir质量比例下纤维素催化转化结果(表六)，反应条件同实施例7。
表六合金催化剂中不同锡铱质量比例下纤维素催化转化结果(IrSn/AC质量为0.1g；反应温度为245℃，反应时间为95min)
如表六所示，在一定锡铱质量比例范围内，此合金催化体系均有较好的乙二醇收率。合金催化剂中锡铱较佳质量比例为0.6-1.8。
实施例14
连续式反应中液体反应空速影响。合金催化剂为负载型合金催化剂5％Ir4％Sn/AC，考查不同液体空速的影响(表七)反应条件同实施例7。
表七不同液体反应空速下木糖转化的结果(IrSn/AC质量为5g，木糖反应液浓度20wt％,反应温度为245℃)
如表七所示，在一定的液体空速范围内，此合金催化体系均有较好的乙二醇和丙二醇的总收率。连续式反应中较佳液体反应空速为0.8h-1。
实施例15
合金催化剂循环性的考查与对比。合金催化剂为非负载型兰尼镍锡催化剂(镍锡质量比为3:1)以及活性炭负载的5％Ni3％Sn/AC，5％Ir3％Sn/AC催化剂，考查此催化剂的循环性(表八)，反应条件同实施例7。
表八纤维素催化转化反应中，兰尼镍锡循环使用考查结果(兰尼镍锡催化剂质量为0.08g，NiSn/AC催化剂质量为0.1g，反应温度为245℃，反应时间为95min)
| 催化剂 | 循环次数 | 乙二醇收率％ | 丙二醇收率％ | 六元醇收率％ |
| 兰尼镍锡 | 第一次 | 60.4 | 13.2 | 4.6. |
| 兰尼镍锡 | 第二次 | 59.8 | 10.9 | 4.2 |
| 兰尼镍锡 | 第三次 | 54.9 | 11.1 | 5.8 |
| 兰尼镍锡 | 第四次 | 53.7 | 13.6 | 2.9 |
| NiSn/AC | 第一次 | 38.7 | 9.5 | 6.1 |
| NiSn/AC | 第二次 | 28.5 | 8.2 | 5.4 |
| NiSn/AC | 第三次 | 20.3 | 6.5 | 4.5 |
| NiSn/AC | 第四次 | 14.4 | 4.2 | 3.1 |
| IrSn/AC | 第一次 | 54.4 | 13.2 | 4.6 |
| IrSn/AC | 第二次 | 52.3 | 13.0 | 4.0 |
| IrSn/AC | 第四次 | 50.1 | 12.0 | 4.7 |
如表八所示，骨架型合金催化剂兰尼镍锡前四次循环均能得到较高的乙二醇收率。反应后溶液中的离子分析检测结果显示，使用兰尼镍锡催化剂每次循环得到的反应溶液中，镍、锡离子的浓度小于1ppm，催化剂活性组分流失量极低。贵金属Ir与锡的合金催化剂同样表现出了非常好的选择性以及稳定性。与此不同，活性炭负载型镍锡催化剂NiSn/AC的乙二醇的收率以及稳定性均明显差于骨架型催化剂。骨架型镍锡催化剂具有相对更为优异的催化效果。
本发明中的合金催化体系可以实现碳水化合物高效转化为乙二醇、丙二醇。此方法不仅操作简单，成本低廉，而且催化剂稳定流失量极低、循环性好、易于回收等优点。
Claims (10)
1.合金催化剂用于碳水化合物催化制备低碳二元醇的方法，其特征在于：其以碳水化合物为反应原料，在高压反应釜内，于水中进行催化加氢反应；
所采用的合金催化剂由至少两种以上的金属组成；
合金催化剂中含有金属锡和其余金属元素，其余金属元素为过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的一种或二种以上，合金催化剂中金属锡与其余金属的重量比在0.01-100范围之间；
或，催化剂使用前由金属锡前驱体和其余金属元素前驱体构成，其中金属锡前驱体为锡的单质或化合物中的一种或二种以上，其余金属元素前驱体为过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上，反应过程中金属锡和其余金属元素形成合金，合金催化剂中金属锡与其余金属的重量比在0.01-100范围之间；
反应于密闭间歇式、连续式或半连续式高压反应釜中搅拌进行；反应前反应釜中充填氢气，反应温度≥120 ℃，反应时间不少于5分钟，液体反应空速不大于20h-1；
在使用过程中，合金催化剂的重量浓度为反应物与反应溶剂质量总和的0. 1%-50%；
所述低碳二元醇为乙二醇或1,2-丙二醇中的一种或二种；
所述碳水化合物为纤维素、淀粉、半纤维素、菊芋、蔗糖、葡萄糖、甘露糖、果糖、果聚糖、木糖、阿拉伯糖、可溶性低聚木糖、赤藓糖、壳聚糖中的一种或二种以上。
2.按照权利要求1所述的方法，其特征在于：反应前反应釜中充填氢气，室温时氢气的初始压力为1-12MPa；反应温度≥120℃，温度上限以反应产物不发生热分解为准。
3.按照权利要求1所述的方法，其特征在于：反应温度为200-280 ℃，室温下反应釜中氢气压力3-7 MPa，对于密闭间歇式反应釜的反应时间为0.5 -5 h，对于半连续或连续式高压反应釜，反应空速GWSV为0.1-50 h-1，GWSV代表流动状态下反应物每小时进入反应器的干基重量与反应器中催化剂重量的比值。
4.按照权利要求1所述的方法，其特征在于：所述合金催化剂为非负载型催化剂，其以合金金属作为催化剂骨架的骨架金属催化剂；优选催化剂为锡镍合金构成的骨架金属催化剂；骨架金属催化剂中金属锡与其余金属元素的重量比在0.1-10范围之间，反应釜中合金骨架催化剂的重量浓度为反应物与反应溶剂质量总和的1%-30%。
5.按照权利要求4所述的方法，其特征在于：所述骨架金属催化剂中金属锡与其余金属元素的重量比在0.5-2范围之间，反应体系中合金催化剂的重量浓度在2%-20%。
6.按照权利要求1所述的方法，其特征在于：所述合金催化剂为负载型催化剂，将金属锡组分与金属组分铁、钴、钌、铑、钯、铱、铂、铜中的一种或两种以上共同负载在同一载体上，所述载体为活性炭、氧化铝、氧化硅、碳化硅、氧化锆、氧化锌、二氧化钛一种载体或二种以上的复合载体，合金于催化剂上的含量在0.01-50 wt%，金属锡与其余金属的重量比在0.1-10范围之间。
7.按照权利要求6所述的方法，其特征在于：合金于催化剂上的含量在1-35 wt%，金属锡与其余金属的重量比在0.5-2范围之间。
8.按照权利要求1所述的方法，其特征在于：将锡的单质或化合物中的一种或二种以上作为载体，将过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上担载在作为载体的锡的单质或化合物上，过渡金属于催化剂上的含量在0.01-50 wt%；
或，将过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物中一种或二种以上作为载体，将锡的单质或化合物中的一种或二种以上担载在作为载体的过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合上，锡于催化剂上的含量在0.01-50 wt%。
9.按照权利要求1所述的方法，其特征在于：反应原料与水的用量以反应条件下反应物料部分或完全为液态即可。
10.按照权利要求1所述的方法，其特征在于：
锡的单质或化合物为金属锡、氟化亚锡、氯化亚锡、溴化亚锡、碘化亚锡、氟化锡、氯化锡、溴化锡、碘化锡、氢氧化锡、氢氧化亚锡、氧化亚锡、二氧化锡、硫酸亚锡、醋酸锡、草酸亚锡、锡酸钠、锡酸钾、锡酸钙、磷化锡、焦磷酸锡中的一种或二种以上；
过渡金属铁、钴、钌、铑、钯、铱、铂、铜中的单质或化合物为金属铁、金属钴、金属钌、金属铑、金属钯、金属铱、金属铂、金属铜、兰尼铁、兰尼钴、兰尼铜、硝酸铁、硝酸钴、硝酸钌、硝酸铑、硝酸钯、硝酸铱、硝酸铂、硝酸铜、氯化铁、氯化钴、氯化钌、氯化铑、氯化钯、氯化铱、氯化铂、氯化铜、三氧化二铁、四氧化三铁、氧化亚铁、硫酸铁、氧化亚钴、三氧化二钴、四氧化三钴、硫酸钴、氧化铜、硫酸铜中的一种或二种以上。