Prior art keywords
microinchs
basic component
copper
thickness
ultrasonic transducers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201480013826.XA
Other languages
English (en)
Other versions
CN105074050B (zh
Inventor
K·泰勒
P·钱德勒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Recor Medical Inc
Original Assignee
Recor Medical Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Recor Medical Inc filed Critical Recor Medical Inc
Publication of CN105074050A publication Critical patent/CN105074050A/zh
Application granted granted Critical
Publication of CN105074050B publication Critical patent/CN105074050B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10N—ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10N30/00—Piezoelectric or electrostrictive devices
    • H10N30/01—Manufacture or treatment
    • H10N30/06—Forming electrodes or interconnections, e.g. leads or terminals
    • H10N30/067—Forming single-layered electrodes of multilayered piezoelectric or electrostrictive parts
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61B—DIAGNOSIS; SURGERY; IDENTIFICATION
    • A61B8/00—Diagnosis using ultrasonic, sonic or infrasonic waves
    • A61B8/44—Constructional features of the ultrasonic, sonic or infrasonic diagnostic device
    • A61B8/4483—Constructional features of the ultrasonic, sonic or infrasonic diagnostic device characterised by features of the ultrasound transducer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B06—GENERATING OR TRANSMITTING MECHANICAL VIBRATIONS IN GENERAL
    • B06B—METHODS OR APPARATUS FOR GENERATING OR TRANSMITTING MECHANICAL VIBRATIONS OF INFRASONIC, SONIC, OR ULTRASONIC FREQUENCY, e.g. FOR PERFORMING MECHANICAL WORK IN GENERAL
    • B06B1/00—Methods or apparatus for generating mechanical vibrations of infrasonic, sonic, or ultrasonic frequency
    • B06B1/02—Methods or apparatus for generating mechanical vibrations of infrasonic, sonic, or ultrasonic frequency making use of electrical energy
    • B06B1/06—Methods or apparatus for generating mechanical vibrations of infrasonic, sonic, or ultrasonic frequency making use of electrical energy operating with piezoelectric effect or with electrostriction
    • B06B1/0644—Methods or apparatus for generating mechanical vibrations of infrasonic, sonic, or ultrasonic frequency making use of electrical energy operating with piezoelectric effect or with electrostriction using a single piezoelectric element
    • B06B1/0662—Methods or apparatus for generating mechanical vibrations of infrasonic, sonic, or ultrasonic frequency making use of electrical energy operating with piezoelectric effect or with electrostriction using a single piezoelectric element with an electrode on the sensitive surface
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1646—Characteristics of the product obtained
    • C23C18/165—Multilayered product
    • C23C18/1651—Two or more layers only obtained by electroless plating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1675—Process conditions
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/18—Pretreatment of the material to be coated
    • C23C18/1851—Pretreatment of the material to be coated of surfaces of non-metallic or semiconducting in organic material
    • C23C18/1872—Pretreatment of the material to be coated of surfaces of non-metallic or semiconducting in organic material by chemical pretreatment
    • C23C18/1886—Multistep pretreatment
    • C23C18/1893—Multistep pretreatment with use of organic or inorganic compounds other than metals, first
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/54—Contact plating, i.e. electroless electrochemical plating
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10N—ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10N30/00—Piezoelectric or electrostrictive devices
    • H10N30/01—Manufacture or treatment
    • H10N30/06—Forming electrodes or interconnections, e.g. leads or terminals
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/31—Coating with metals
    • C23C18/32—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron
    • C23C18/34—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents
    • C23C18/36—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents using hypophosphites
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/31—Coating with metals
    • C23C18/38—Coating with copper

Abstract

根据一些实施例，将至少一个电极沉积于超声换能器的基础构件上的方法包括，使用第一腐蚀剂至少部分地腐蚀所述基础构件的表面，使用第一催化剂催化所述基础构件的表面，使用化学电镀法在所述基础构件的表面上电镀铜，检查电镀于所述基础构件表面上的铜，使用第二腐蚀剂至少部分地腐蚀所述镀有铜的表面，使用第二催化剂催化所述镀有铜的表面，使用化学电镀法在所述镀有铜的表面上电镀镍，以及在所述镀有镍的表面上沉积至少一个金层。

Description

电镀或涂覆超声换能器的方法
背景
技术领域
本申请一般地涉及超声换能器，并且更具体地，涉及电镀或以其方式涂覆陶瓷管或其他管以生产换能器的电极的方法。
背景技术
超声换能器可包含具有内电极和/或外电极的陶瓷基材料，对所述电极通电以产生声能。因此，本文公开了将电极布置于超声换能器表面上的方法。
发明内容
根据一些实施例，将至少一个电极放置于超声换能器的基础构件上的方法(例如，制造换能器)包括，使用第一腐蚀剂至少部分地腐蚀所述基础构件的表面，使用第一催化剂催化所述基础构件的所述表面，在所述基础构件的所述表面上镀铜，使用第二腐蚀剂至少部分地腐蚀所述镀有铜的表面，使用第二催化剂催化所述镀有铜的表面，以及使用化学电镀方法在所述镀有铜的表面上镀镍。在一些实施例中，所述基础构件包含不导电的材料。在一个实施例中，所述基础构件包含陶瓷材料或其他不导电的材料。在一些实施例中，所述方法还包括在所镀有镍的表面上沉积至少一层金。
根据一些实施例，所述方法还包括在使用第一腐蚀剂至少部分地腐蚀所述基础构件的表面之前使用清洁剂清洁基础构件。在一个实施例中，所述清洁剂包括脱脂剂和醇中的至少一种。在一些实施例中，所述第一腐蚀剂和所述第二腐蚀剂中的至少一种包含酸。在一些实施例中，所述第一催化剂和所述第二催化剂中的至少一种包含钯。在一个实施例中，在所述基础构件的所述表面上镀铜包括将所述基础构件放置于铜浴中。
根据一些实施例，所述方法还包括检查在所述基础构件的所述表面上所镀的铜。在一个实施例中，检查在所述基础构件的所述表面上所镀的铜包括确认在所述基础构件上所镀的铜的厚度以及确认沿所述基础构件的镀层的均匀性中的至少一种。在一些实施例中，如果所述基础构件不满足所述检查的至少一个阈值要求，则所述方法还包括使用化学电镀法来在所述基础构件的所述表面上重新镀铜。
根据一些实施例，在所述基础构件的所述表面上镀铜包括使用化学电镀法和/或另一电镀法。在一个实施例中，在所述基础构件的所述表面上镀镍包括使用化学电镀法和/或另一电镀法。
根据一些实施例，所述第二催化剂包括硫酸根阴离子基溶液。在一个实施例中，在所述镀有铜的表面上镀锌包括将超声换能器放置于包含高-磷镍的浴液中。在一些实施例中，在所述镀有镍的表面上沉积至少一层金包括沿所述镀有镍的表面浸渍单层的金。在一些实施例中，沿涂有镍的表面的金的厚度介于0.1至10微英寸之间(例如，0.1至0.2微英寸、0.2至0.3微英寸、0.3至0.4微英寸、0.4至0.5微英寸、0.5至0.6微英寸、0.6至0.7微英寸、0.7至0.8微英寸、0.8至0.9微英寸、0.9至1微英寸、1至2微英寸、2至3微英寸、3至4微英寸、4至5微英寸、5至6微英寸、6至7微英寸、7至8微英寸、8至9微英寸、9至10微英寸，前述范围之间的厚度，等)。在一些实施例中，沿涂有镍的表面的金的厚度小于0.1微英寸或大于10微英寸(例如，10至15微英寸、15至20微英寸、20至30微英寸，大于30微英寸，等)。在一个实施例中，沿涂有镍的表面的金的厚度为约5微英寸。在一些实施例中，沿所述基础构件的所述表面的铜的厚度介于10至25微英寸之间(例如，10至12、12至14微英寸、14至16微英寸、16至18微英寸、18至20微英寸，前述范围之间的厚度，等)。在一个实施例中，沿所述基础构件的所述表面的铜的厚度为约15微英寸。在另一些实施例中，沿所述基础构件的所述表面的铜的厚度小于10微英寸(例如，0至1微英寸、1至2微英寸、2至3微英寸、3至4微英寸、5至6微英寸、6至7微英寸、7至8微英寸、8至9微英寸、9至10微英寸，前述范围之间的厚度，等)或大于25微英寸(例如，25至30微英寸、30至35微英寸、35至40微英寸、40至50微英寸、50至60微英寸、60至70微英寸、70至80微英寸、80至90微英寸、909至100微英寸，大于100微英寸，等)。在一些实施例中，沿所述涂有铜的表面的镍的厚度介于100至200微英寸之间(例如，100至110微英寸、110至120微英寸、120至130微英寸、130至140微英寸、140至150微英寸、150至160微英寸、160至170微英寸、170至180微英寸、180至190微英寸、190至200微英寸，前述范围之间的厚度，等)。
在一个实施例中，沿所述涂有铜的表面的镍的厚度为约150微英寸。在另一些实施例中，沿所述涂有铜的表面的镍的厚度小于100微英寸(例如，0至10微英寸、10至20微英寸、20至30微英寸、30至40微英寸、40至50微英寸、50至60微英寸、60至70微英寸、70至80微英寸、80至90微英寸、90至100微英寸，前述范围之间的厚度，等)或大于200微英寸(例如，200至210微英寸、210至220微英寸、220至230微英寸、230至240微英寸、240至250微英寸、250至300微英寸、300至400微英寸、400至500微英寸，前述范围之间的厚度，大于500微英寸，等)。
根据一些实施例，沿所述基础构件的外表面和内表面都沉积铜、镍和金。在一些实施例中，所述基础构件包含压电陶瓷材料。在一个实施例中，使用批方法在多个基础构件上沉积至少一个电极。在一些实施例中，将所述基础构件布置于线支架上。在一些实施例中，将所述基础构件布置于桶系统中。根据一些实施例，从较大的块构件切取所述基础构件。
根据一些实施例，使用本文描述的方法制造的超声换能器包括圆柱形换能器。在另一些实施例中，所述超声换能器具有非圆柱形状(例如，所述换能器具有平的、凹的、凸的、弯曲的、波浪的、不规则的、正弦曲线的和/或任何其他形状)。
根据一些实施例，超声换能器包括基础构件、沿所述基础构件的表面布置的至少一个铜层、沿所述至少一个铜层布置的至少一个镍层，其中将所述至少一个铜层布置于所述基础构件与所述至少一个镍层之间，以及沿所述至少一个镍层布置的至少一个金层。
根据一些实施例，将所述至少一个铜层镀于所述基础构件的所述表面上。在一些实施例中，使用化学电镀法将所述至少一个铜层镀于所述基础构件的所述表面上。在一些实施例中，沿所述至少一个铜层电镀所述至少一个镍层。在一个实施例中，使用化学电镀法沿所述至少一个铜层电镀所述至少一个镍层。在一些实施例中，所述基础构件包含不导电的材料。在一些实施例中，所述基础构件包含陶瓷。
在一些实施例中，沿所述涂有镍的表面的金的厚度介于0.1至10微英寸之间(例如，0.1至0.2微英寸、0.2至0.3微英寸、0.3至0.4微英寸、0.4至0.5微英寸、0.5至0.6微英寸、0.6至0.7微英寸、0.7至0.8微英寸、0.8至0.9微英寸、0.9至1微英寸、1至2微英寸、2至3微英寸、3至4微英寸、4至5微英寸、5至6微英寸、6至7微英寸、7至8微英寸、8至9微英寸、9至10微英寸，前述范围之间的厚度，等)。在一些实施例中，沿所述涂有镍的表面的金的厚度小于0.1微英寸或大于10微英寸(例如，10至15微英寸、15至20微英寸、20至30微英寸，大于30微英寸，等)。在一个实施例中，沿涂有镍的表面的金的厚度为约5微英寸。在一些实施例中，沿所述基础构件的所述表面的铜的厚度介于10至25微英寸之间(例如，10至12微英寸、12至14微英寸、14至16微英寸、16至18微英寸、18至20微英寸，前述范围之间的厚度，等)。在一个实施例中，沿所述基础构件的所述表面的铜的厚度为约15微英寸。在另一些实施例中，沿所述基础构件的所述表面的铜的厚度小于10微英寸(例如，0至1微英寸、1至2微英寸、2至3微英寸、3至4微英寸、5至6微英寸、6至7微英寸、7至8微英寸、8至9微英寸、9至10微英寸，前述范围之间的厚度，等)或大于25微英寸(例如，25至30微英寸、30至35微英寸、35至40微英寸、40至50微英寸、50至60微英寸、60至70微英寸、70至80微英寸、80至90微英寸、909至100微英寸，大于100微英寸，等)。在一些实施例中，沿所述涂有铜的表面的镍的厚度介于100至200微英寸之间(例如，100至110微英寸、110至120微英寸、120至130微英寸、130至140微英寸、140至150微英寸、150至160微英寸、160至170微英寸、170至180微英寸、180至190微英寸、190至200微英寸，前述范围之间的厚度，等)。在一个实施例中，沿所述涂有铜的表面的镍的厚度为约150微英寸。在另一些实施例中，沿所述涂有铜的表面的镍的厚度小于100微英寸(例如，0至10、10至20微英寸、20至30微英寸、30至40微英寸、40至50微英寸、50至60微英寸、60至70微英寸、70至80微英寸、80至90微英寸、90至100微英寸，前述范围之间的厚度，等)或大于200微英寸(例如，200至210微英寸、210至220微英寸、220至230微英寸、230至240微英寸、240至250微英寸、250至300微英寸、300至400微英寸、400至500微英寸，前述范围之间的厚度，大于500微英寸，等)。
根据一些实施例，所述至少一个铜层的厚度介于10至25微英寸之间，所述至少一个镍层的厚度介于100至200微英寸之间，并且所述至少一个金层的厚度介于0.1至10微英寸之间。
根据一些实施例，所述基础构件包含压电陶瓷材料。在一个实施例中，所述换能器包括圆柱形换能器。在一些实施例中，所述超声换能器具有非圆柱形状(例如，所述换能器具有平的、凹的、凸的、弯曲的、波浪的、不规则的、正弦曲线的和/或任何其他形状)。根据一个实施例，所述换能器的内表面和外表面均包括铜层、镍层和金层。
根据一些实施例，在超声换能器的基础构件上放置至少一个电极的方法包括，用清洁剂清洁基础构件，其中所述基础构件包含陶瓷材料。所述方法还包含，使用第一腐蚀剂(例如，酸)至少部分地腐蚀所述基础构件的表面，使用第一催化剂(例如，包含钯的溶液)催化所述基础构件的所述表面，使用化学电镀法在所述基础构件的所述表面上镀铜，检查所述基础构件的所述表面上所镀的铜，使用第二腐蚀剂(例如，酸)至少部分地腐蚀所述镀有铜的表面，使用第二催化剂(例如，包含钯的溶液)催化所述镀有铜的表面，使用化学电镀法在所述镀有铜的表面上镀镍，以及在所述镀有镍的表面上沉积至少一个金层。
根据一些实施例，所述清洁剂包括脱脂剂、醇和/或诸如此类。在一些实施例中，所述第一腐蚀剂和所述第二腐蚀剂包含酸(例如，Citranox、H2SO4等)。在一些实施例中，在所述基础构件的所述表面上镀铜包括将所述基础构件放置于铜浴中。在一些实施例中，检查在所述基础构件的所述表面上所镀的铜包括确认在所述基础构件上所镀的铜的厚度，确认沿所述基础构件的镀层的均匀性和/或铜镀层的品质和范围的任何其他方面。根据一些实施例，如果所述基础构件不满足所述检查的至少一个阈值要求，则所述方法还包括使用化学电镀法来在所述基础构件的所述表面上重新镀铜。
根据一些实施例，所述第二催化剂包括硫酸根阴离子基溶液。在一些实施例中，在所述镀有铜的表面上镀锌包括将所述超声换能器放置于包含高-磷镍的浴液中。在一些实施例中，在所述镀有镍的表面上沉积至少一个金层包括沿所述镀有镍的表面浸渍单层的金。
根据一些实施例，沿所述基础构件的所述表面的铜的厚度为约10至20微英寸(例如，15微英寸、10至12微英寸、12至14微英寸、14至16微英寸、16至18微英寸、18至20微英寸，等)。在一些实施例中，沿所述涂有铜的表面的镍的厚度为约100至200微英寸(例如，150微英寸，100至120微英寸、120至140微英寸、140至160微英寸、160至180微英寸、180至200微英寸，等)。在一些实施例中，沿所述涂有镍的表面的金的厚度为约0.1至10微英寸(例如，5微英寸，0至1微英寸、1至2微英寸、2至3微英寸、4至5微英寸，等)。
根据一些实施例，所述基础构件具有圆柱形状。在一些实施例中，沿所述基础构件的外表面和内表面沉积有铜、镍和金。在一个实施例中，所述基础构件包含压电陶瓷材料(例如，PZT)。在一些实施例中，使用批方法(例如，使用线支架、桶系统等)在多个基础构件上沉积至少一个电极。在一些实施例中，从较大的块构件(例如，长的陶瓷筒)切取所述基础构件。
上文概述的以及下文更详细记载的方法描述了某些由实施者(例如，制造者)采取的行为；但是，应理解，它们还可包括由另一方对这些行为的指导。因此，例如“沉积至少一个层”等动作包括“指导沉积至少一个层”。
附图说明
图1以图示的方式描述了根据一个实施例在超声换能器的基础构件上沉积电极的流程图。
具体实施方式
在一些实施例中，超声换能器具有包含基础材料的圆柱形状。这样的基础材料可包括陶瓷，例如，锆钛酸铅(PZT)、其他压电陶瓷材料和/或诸如此类。在一些实施例中，将长圆柱形的陶瓷基础材料切割和/或以其他方式加工成较小的部段，以制造具有期望长度的单个换能器。在产生基础管部分后，可使用一种或多种金属电镀方法来选择性地在其上沉积一个或多个电极。如本文所述，所述电极可包含一种或多种金属、合金和/或其他导电材料。图1的流程图中以图示的方式示出了电镀换能器的方法10的一个实施例。在本文公开的任何实施例中，可制备多个圆柱管，并同时对其进行涂覆，例如，在批系统中涂覆。例如，在一些实施例中，将多个换能器管放置于支架系统(例如，线支架)、桶系统和/或诸如此类中。因此，在制备、电镀和/或其他制造步骤期间，可同时将多个管浸没或至少部分地浸没于一种或多种浴液或溶液中。
在一些实施例中，本文公开的多种涂覆方法和技术可用于不是圆柱形的表面，例如，平表面、波浪表面、凸面、凹面或其他圆表面、不规则形状的表面、其他非圆柱形表面和/或诸如此类。因此，本文公开的多种涂覆方法可用于制造不是圆柱形的超声换能器和/或不具有圆柱形状的换能器的电极，所述换能器例如，平换能器、凹或凸换能器、不规则形状的换能器等。
清洁与初始准备
在一些实施例中，使用机械加工油、其他油、润滑脂、天然涂层或层和/或其他材料来生产单个的管长度。因此，在开始涂覆方法之前，可期望或要求清洁和以其他方式准备20所述管。例如，在一些实施例中，所述方法包括使用超声脱脂器、醇基清洁剂和/或任何其他清洁产品或试剂来对管进行脱脂。如上文所述，可将管浸没或以其他方式放置于浴液(例如，脱脂溶液)内。在暴露于脱脂剂或其他清洁剂特定时间(例如，～1分钟)后，可移出该管并将其放置于去离子水溶液或浴液中(例如，保持～1分钟)，以去除余量的脱脂剂和/或其他清洁溶液。在另一些实施例中，对将超声电极布置于其上的表面的初始清洁或脱脂可通过使用任何其他方法或设备来完成，包括但不限于，化学清洁、机械清洁(例如，沙化、再表面化等)和/或诸如此类。此外，初始脱脂或其他初始清洁阶段的时间可为小于1分钟(例如，0至20秒、20至30秒、30至40秒、40至50秒、50至60秒，前述范围之间的时间，等)或大于1分钟(例如，1至1.5分钟、1.5至2分钟、2至3分钟、3至4分钟、4至5分钟、5至10分钟，大于10分钟，等)。
然后，在一个实施例中，可使用酸清洁剂和/或其他腐蚀材料进一步清洁该管的表面。例如，可将该管放置于溶液或其他相对弱的酸溶液中，保持约1分钟。在另一些实施例中，所述酸清洁或腐蚀步骤或类似的准备步骤的时间可为小于1分钟(例如，0至20秒、20至30秒、30至40秒、40至50秒、50至60秒，前述范围之间的时间，等)或大于1分钟(例如，1至1.5分钟、1.5至2分钟、2至3分钟、3至4分钟、4至5分钟、5至10分钟，大于10分钟，等)。这可帮助将额外的不想要的层、涂层或材料从该管的暴露在外的表面(例如，内表面和外表面)去除。在一些实施例中，酸清洁步骤(例如，使用相对弱的酸)至少部分地腐蚀或再表面化该管的外表面。在一些实施例中，可使用水冲洗(例如，使用去离子水)或另一种流体冲洗以将余量的酸清洁剂从该管去除。
铜电镀的准备
在一些实施例中，首先对管或其他换能器基础构件进行镀铜。在一些实施例中，可在电镀铜方法前采取一个或多个准备性步骤24。例如，可将该管放置于强酸溶液中，例如，10％的HBF4(例如，四氟硼酸、其他氟硼酸等)和乙酸盐溶液中。可使用一种或多种其他酸，例如，盐酸、硫酸、硝酸、任何其他酸等，其可在HBF4和乙酸盐之外或替代HBF4和乙酸盐来使用。在一个实施例中，将该管暴露于这种溶液中，保持约90秒(例如，60至120秒、60至70秒、70至80秒、80至90秒、90至100秒、100至110秒、110至120秒，前述范围之间的时间等)。但是，在另一些实施例中，如特定方法(例如，基于所要求的腐蚀的量、所使用的酸的类型和强度等)所期望或要求的，在该步骤的暴露时间可少于或多于90秒(例如，60至90秒、90至120秒、30至60秒、小于30秒、多于120秒等)。无论确切方案是什么，这样的暴露的结果是，可至少部分地腐蚀该管的外表面。这可帮助去除铅和/或其他不期望的物质，这些物质可能干扰后续电镀铜的步骤。在一些实施例中，在腐蚀步骤期间必须要注意防止损坏该管的几何结构。换言之，如果进行了过量腐蚀，则改变管的圆柱形状，从而不利地影响该换能器的声能特性。例如，如果该管不是在特定的容许程度中的圆柱形，则由该换能器发射的声能在径向上会不均匀的传递(例如，产生热点、较低能量强度点等)。
一旦对该该管已经充分地腐蚀了，即可对其进行冲洗以去除任何余量的腐蚀溶液或材料。例如，在一个实施例中，该管可经历一次、两次或更多次去离子水冲洗和/或其他液体基冲洗。例如，在一些实施例中，该管经历了两个分离的去离子水冲洗循环，每个循环可持续约30秒。但是，在另一些实施例中，冲洗时间可少于或多于30秒(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。
在一些实施例中，使该换能器随后经历清洁的铜试镀(copperdummy)负载溶液，例如，10％的HBF4溶液(和/或具有不同酸、不同强度和/或其他性质的另一溶液)，保持约1分钟。但是，在另一些实施例中，该步骤可少于或多于1分钟(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。这样的步骤可帮助该管的外表面和内表面对后续的铜电镀步骤更具反应性。在一些实施例中，将包含铜的一种或多种片或其他构件布置于该管所放置的浴液或溶液中。例如，在一些实施例中，在开始实际的镀铜方法之前，将包含铜的一个或多个组件(例如，板、其他构件等)的约1/2平方英尺的表面积放置于浴液中，保持约1至5分钟。
在将其暴露于铜试镀负载溶液中后，可在水冲洗阶段对该换能器管进行冲洗。在一些实施例中，例如可使用去离子水冲洗该管约30秒。但是，在另一些实施例中，冲洗时间可少于或多于30秒(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。
电镀铜
继续参照图1，在一些实施例中，在电镀铜准备步骤后，该换能器管或其他换能器基构件(例如，板)可进行电镀铜工艺28。在一个实施例中，可为一种或多种电镀用催化剂的后续应用来处理该管的表面。例如，可将该管或其他构件暴露于敏化剂(例如，Enthone432)，保持约1分钟。在一些布置中，使Enthone或其他准备性溶液进行一个或多个冲洗步骤。例如，该管可经历两次使用去离子水冲洗的步骤，每个步骤可持续约20秒。但是，在另一些实施例中，暴露于敏化剂或任何后续冲洗步骤的时间可比上文所述的时间更短或更长。例如，可将该管或其他基础构件暴露于敏化剂，保持少于或多于1分钟(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。同样地，随后的冲洗可采用单一步骤或多步骤(例如，2、3、4、多于4个步骤等)，并且可持续少于或多于20秒(例如，0至5秒、5至10秒、10至15秒、15至20秒、20至25秒、25至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。
然后，在一些实施例中，可用钯至少部分地催化换能器管或其他换能器基础构件的表面。例如，可将该管或其他构件放置于催化剂溶液(例如，Enthone440)浴中，保持约3分钟。在一些实施例中，可将该管或其他基础构件与催化剂溶液接触放置少于或多于3分钟(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟、5至6分钟、6至7分钟、7至8分钟、8至9分钟、9至10分钟，前述范围之间的时间，多于10分钟，等)。在一些实施例中，所述钯是辅助在管表面上进行后续电镀铜的催化剂。可使用一种或多种其他催化剂替代钯，或除钯以外还使用一种或多种其他催化剂。然后，可使用速蘸法和/或任何其他方法或步骤来去除过量的包含钯的溶液和/或其他催化剂。
一旦准备好了换能器管或其他换能器基础构件的表面，即可将该管或其他基础构件放置于浴液中(例如，Enthone406、其他包含铜的溶液等中)，以能够将铜电镀至该管或其他基础构件上。例如，在一些实施例中，将该管在这样的浴液中保持约10分钟。在一些实施例中，这样的电镀方法可在该管上形成约10至20微英寸(例如，10微英寸、11微英寸、12微英寸、13微英寸、14微英寸、15微英寸、16微英寸、17微英寸、18微英寸、19微英寸、20微英寸，前述范围之间的厚度，等)的铜涂层。但是，在一些实施例中，可将该管或其他基础构件放置于浴液中来进行该步骤，保持少于或多于10分钟(例如，0至10秒、10至20秒、20至30秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟、5至6分钟、6至7分钟、7至8分钟、8至9分钟、9至10分钟、11至12分钟、12至13分钟、13至14分钟、14至15分钟、15至20分钟，前述范围之间的时间，多于20分钟，等)。此外，按期望或要求，所得的铜涂层可小于10微英寸(例如，0至1微英寸、1至2微英寸、2至3微英寸、3至4微英寸、5至6微英寸、6至7微英寸、7至8微英寸、8至9微英寸、9至10微英寸，等)或大于20微英寸(例如，20至25微英寸、25至30微英寸、30至40微英寸、40至50微英寸，前述范围之间的尺寸，大于50微英寸，等)。
铜镀层检查
在一些实施例中，在检测阶段32后，如果确定铜的镀层不足(例如，镀层厚度不足、镀层不均匀等)，可将该管经历一个或多个电镀铜循环28。因此，如由图1中的步骤36所示，不需要由头(例如，图1中的步骤20或24)开始电镀方法。步骤10中的这种短循环步骤36可缩短制造时间，简化制造方案并提供一种或多种益处和优点。在一些实施例中，在弃掉换能管前，可重复短循环步骤36不超过约4次。
镍电镀的准备
在一些实施例中，如果电镀铜令人满意，则随后可使该管或其他基础构件经历一个或多个电镀镍步骤。在一些实施例中，在电镀铜步骤28和检查步骤32后，该管可进行电镀镍准备工艺40。例如，可在进行腐蚀步骤之前，用去离子水和/或其他溶液冲洗该管约20秒。在一些实施例中，可在10％H2SO4溶液和/或任何其他酸溶液中至少部分地腐蚀镀有铜的管，保持约30秒。在一些实施例中，所述冲洗步骤和/或腐蚀步骤可与上文所述不同。例如，可冲洗该管或其他基础构件少于或多于20秒(例如，0至5秒、5至10秒、10至15秒、15至20秒、20至25秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。此外，所述腐蚀步骤可按期望或要求持续少于或多于30秒(例如，0至5秒、5至10秒、10至15秒、15至20秒、20至25秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。在一些实施例中，H2SO4和/或其他酸性溶液的使用可提供先前电镀铜步骤中使用的硫酸根阴离子的更佳匹配，从而促进电镀镍工艺。
在一些实施例中，一旦已经腐蚀了镀有铜的管，即可使其经历钯催化剂溶液(例如，TechniCatalystAT4000)和/或另一催化剂溶液或混合物。例如，可将该管放置于钯催化剂溶液中，保持约2分钟。在一些实施例中，可按期望或要求将该管于催化剂中保持少于或多于2分钟(例如，0至5秒、5至10秒、10至15秒、15至20秒、20至25秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。在一些实施例中，所述钯催化剂溶液包含硫酸根离子活化剂。在一些实施例中，所述钯催化剂溶液不包含氯离子活化剂。在暴露于所述钯催化剂后，可终止铜试镀负载，并冲洗该管以去除任何过量的钯催化剂溶液(例如，通过使用去离子水速蘸法)。
电镀镍
在一些实施例中，该换能器管随后可进行镀镍方法44。例如，可将该管或其他基础构件放置于镍溶液中，保持约15分钟。在一些实施例中，可按要求将该管或其他基础构件放置于镍溶液中，保持少于或多于15分钟(例如，0至5分钟、5至10分钟、10至15分钟、15至20分钟、20至25分钟、30至40分钟、40至50分钟、50至60分钟、1至2小时、2至3小时、3至4分钟、4至5小时，前述范围之间的时间，多于5小时，等)。在一些实施例中，所述镍溶液包括高-磷镍溶液(例如，NICHEM5100)。在一些实施例中，由于暴露于这样的镍溶液，可将约100至200微英寸(例如，150微英寸)的镍电镀于该换能器管或其他基础构件的外表面上(例如，处于电镀的铜层上面)。在已经充分地将镍电镀于该换能器管的外表面上后，可用去离子水冲洗该管或其他构件(例如，保持约20秒)来去除过量的镍溶液。在另一些实施例中，如所期望或要求的，该冲洗步骤可或其他基础构件可持续少于或多于20秒(例如，0至5秒、5至10秒、10至15秒、15至20秒、20至25秒、30至40秒、40至50秒、50至60秒、1至2分钟、2至3分钟、3至4分钟、4至5分钟，前述范围之间的时间，多于5分钟，等)。
金浸渍
在一些实施例中，可沿着换能器管上已经镀有的铜层和镍层的外侧来布置48金层(和/或另一金属或合金涂层)。例如，可在该管外侧上将金浸渍为单层。在另一些实施例中，按期望或要求使用多于一个(例如，2个、3个、多于3个，等)金层。在一些实施例中，使该管经历金(例如，OMGFidelity9027+钾金)的浸渍，保持约2分钟。这种浸渍层的使用可消除或降低因在圆筒的表面上，尤其是在相对较小的圆筒的内表面内进行电镀金而导致的复杂化(complications)的可能性。因此，在一些实施例中，在不使用电解法的情况下，将所述金放置于换能器管上。在一些实施例中，沉积于该管上(例如，沿铜和镍层外侧)的金单层的厚度为约2至10微英寸(例如，5微英寸)。在金浸渍工艺后，可使用去离子水冲洗(例如，保持约20秒)从管外去除任何过量的金。
干燥和结束
根据一些实施例，在沿着换能器管外侧已经布置期望的铜层、镍层、金层和/或任何其他材料层后，该管可经历一个或多个饰面(finishing)步骤52。例如，可使用醇冲洗(包含例如，异丙醇)来去除任何过量的水，以及促进该管外表面的干燥。最后，在一些实施例中，可将该管放置于烘箱或其他热环境中，以去除醇并干燥该管。
根据本文公开的多个实施例的电镀和/或以其他方式涂覆的换能器管可包含三种金属，例如，铜基层、镍中间层和金外层。在一些实施例中，布置于该管上的多种金属的厚度可为约150至200微英寸。例如，在一个实施例中，换能器可包括分别具有约15微英寸的铜基层、150微英寸的镍中间层和5微英寸的金外层。在另一些实施例中，一个或多个层的厚度可按期望或要求而变化。
在以下文献中提供了与可能的超声换能器设计和实施例有关的额外细节(例如，在结构上的和操作上的)：2001年7月13日提交的美国专利申请11/267,123，并于2002年6月6日公开，公开号为2002/0068885；2001年7月13日提交的美国专利申请09/905,227，并于2003年10月21日授权为美国专利6,635,054；2001年7月13日提交的美国专利申请09/904,620，并且于2004年7月20日授权为美国专利6,763,722；2004年2月20日提交的美国专利申请10/783,310，并于2010年11月23日授权为美国专利7,837,676；2010年2月3日提交的美国专利申请12/227,508，并于2010年5月27日公开，公开号为2010/0130892；2003年6月30日提交的美国专利申请10/611,838，并于2004年4月29日公开，公开号为2004/0082859；以及2011年2月18日提交的PCT申请PCT/US2011/025543，并于2012年8月23日公开，公开号为WO2012/112165。所有前述申请的整体都通过引用并入本文，并形成本申请的一部分。
为了辅助描述所公开的实施例，上文使用以下词语来描述不同的实施例和/或附图：向上、上、底、向下、下、后、正、垂直、水平、上游、下游。但是，应领会，无论是否进行了描述，不同的实施例可位于和朝向多种期望的位置。
虽然本文公开了一些实施例和实施例，但是本申请可超过具体公开的实施例延伸至其他的替代实施例，和/或本发明的用途以及它们的变型和等同物。还理解的是，可对这些实施例的具体特征和方面进行组合或亚组合，并仍然落在本发明的范围内。因此，应理解，可将所公开的实施例的多个特征和方面进行彼此组合或替代，以形成本发明的多样的模式。因此，本文公开的本发明的范围不应被上文具体公开的实施例所限制，而应当仅由通过直接阅读后面的权利要求书来确定。
虽然本发明允许有各种变型和替代形式，但其具体实施例已经在附图中示出并在本文中进行了详细描述。但是，应理解，本发明不限制于所公开的特定形式，恰好相反，本发明意在覆盖落入所描述的多种实施例和所附的权利要求书的精神与范围内的所有变型、等同物以及替代方案。本文公开的任何方法不必以所列举的顺序来进行。本文公开的方法包括由实施者采取的某些行为；但是它们还可包括任何第三方对这些行为的指导，无论是以明示的方式还是以暗示的方式。例如，例如“沉积至少一个层”等动作包括“指导沉积至少一个层”。本文公开的范围还涵盖任何和所有重叠区、子范围及其组合。例如“不超过”、“至少”、“大于”、“小于”、“之间”等用语包括所列举的数字。前面加有术语“约”的数字包括所列举的数字。例如，“约10mm”包括“10mm”。前面加有术语例如“基本”的术语或短语包括所列举的术语或短语。例如，“基本平行”包括“平行”。

Claims (52)

1.一种将至少一个电极沉积于超声换能器的基础构件上的方法，所述方法包括：
使用第一腐蚀剂至少部分地腐蚀所述基础构件的表面；
使用第一催化剂催化所述基础构件的表面；
在所述基础构件的表面上电镀铜；
使用第二腐蚀剂至少部分地腐蚀镀有铜的表面；
使用第二催化剂催化所述镀有铜的表面；以及
使用化学电镀法在所述镀有铜的表面上电镀镍。
2.如权利要求1所述的方法，其中所述基础构件包含不导电的材料。
3.如权利要求1所述的方法，其中所述基础构件包含陶瓷。
4.如权利要求1所述的方法，还包括在所述镀有镍的表面上沉积至少一个金层。
5.如权利要求1所述的方法，还包括在使用第一腐蚀剂至少部分地腐蚀所述基础构件的表面之前使用清洁剂清洁基础构件。
6.如权利要求5所述的方法，其中所述清洁剂包括脱脂剂和醇中的至少一种。
7.如权利要求1所述的方法，其中所述第一腐蚀剂和所述第二腐蚀剂中的至少一种包含酸。
8.如权利要求1所述的方法，其中所述第一催化剂和所述第二催化剂中的至少一种包含钯。
9.如前述权利要求中任一项所述的方法，其中在所述基础构件的表面上电镀铜包括将所述基础构件放置于铜浴中。
10.如权利要求1至8中任一项所述的方法，还包括检查在所述基础构件的表面上电镀的铜。
11.如权利要求10所述的方法，其中检查在所述基础构件的表面上电镀的铜包括确认在所述基础构件上电镀的铜的厚度以及确认沿所述基础构件的镀层的均匀性中的至少一种。
12.如权利要求11所述的方法，其中，如果所述基础构件不满足所述检查的至少一个阈值要求，则所述方法还包括使用化学电镀法在所述基础构件的表面上重新镀铜。
13.如权利要求1至8中任一项所述的方法，其中在所述基础构件的表面上电镀铜包括使用化学电镀法。
14.如权利要求1至8中任一项所述的方法，其中在所述基础构件的表面上电镀镍包括使用化学电镀法。
15.如权利要求1至8中任一项所述的方法，其中所述第二催化剂包括硫酸根阴离子基溶液。
16.如权利要求1至8中任一项所述的方法，其中在镀有铜的表面上电镀锌包括将所述超声换能器放置于包含高-磷镍的浴液中。
17.如权利要求4所述的方法，其中在镀有镍的表面上沉积至少一个金层包括沿所述镀有镍的表面浸渍金的单层。
18.如权利要求4所述的方法，其中沿涂覆有镍的表面的金的厚度介于0.1至10微英寸之间。
19.如权利要求4所述的方法，其中沿涂覆有镍的表面的厚度为约5微英寸。
20.如权利要求1至8中任一项所述的方法，其中沿所述基础构件的表面的铜的厚度介于10至25微英寸之间。
21.如权利要求1至8中任一项所述的方法，其中沿所述基础构件的表面的铜的厚度为约15微英寸。
22.如权利要求1至8中任一项所述的方法，其中沿镀有铜的表面的镍的厚度介于100至200微英寸之间。
23.如权利要求1至8中任一项所述的方法，其中沿镀有铜的表面的镍的厚度为约150微英寸。
24.如权利要求4所述的方法，其中沿所述基础构件的外表面和内表面沉积所述铜、镍和金。
25.如权利要求1至8中任一项所述的方法，其中所述基础构件包含压电陶瓷材料。
26.如权利要求1至8中任一项所述的方法，其中使用批方法在多个基础构件上沉积至少一个电极。
27.如权利要求27所述的方法，其中将所述基础构件布置于线支架上。
28.如权利要求27所述的方法，其中将所述基础构件布置于桶系统中。
29.如权利要求1至8中任一项所述的方法，其中从较大的块构件切取所述基础构件。
30.一种超声换能器，其包括使用权利要求1至29中任一项所述的方法沉积于所述换能器的基础构件上的电极。
31.如权利要求30所述的换能器，其中所述换能器包括圆柱形换能器。
32.如权利要求30所述的超声换能器，其中所述超声换能器具有非圆柱形状。
33.如权利要求32所述的超声换能器，其中所述超声换能器具有平的、凹的或凸的形状。
34.一种超声换能器，其包括：
基础构件；
沿所述基础构件的表面布置的至少一个铜层；
沿所述至少一个铜层布置的至少一个镍层，其中将所述至少一个铜层布置于所述基础构件与所述至少一个镍层之间，以及
沿所述至少一个镍层布置的至少一个金层。
35.如权利要求34所述的超声换能器，其中所述至少一个铜层是电镀于所述基础构件的表面上。
36.如权利要求35所述的超声换能器，其中使用化学电镀法将所述至少一个铜层电镀于所述基础构件的表面上。
37.如权利要求34所述的超声换能器，其中所述至少一个镍层的沿所述至少一个铜层电镀的。
38.如权利要求37所述的超声换能器，其中使用化学电镀法沿所述至少一个铜层电镀所述至少一个镍层。
39.如权利要求34所述的超声换能器，其中所述基础构件包含不导电的材料。
40.如权利要求34所述的超声换能器，其中所述基础构件包含陶瓷。
41.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个铜层的厚度介于10和25微英寸之间。
42.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个铜层的厚度为约15微英寸。
43.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个镍层的厚度介于100和200微英寸之间。
44.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个镍层的厚度为约150微英寸。
45.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个金层的厚度介于0.1和10微英寸之间。
46.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个金层的厚度为约5微英寸。
47.如权利要求34至40中任一项所述的超声换能器，其中所述至少一个铜层的厚度介于10至25微英寸之间，所述至少一个镍层的厚度介于100至200微英寸之间，并且所述至少一个金层的厚度介于0.1至10微英寸之间。
48.如权利要求34至40中任一项所述的超声换能器，其中所述基础构件包含压电陶瓷材料。
49.如权利要求34至40中任一项所述的超声换能器，其中所述换能器包括圆柱形换能器。
50.如权利要求34至40中任一项所述的超声换能器，其中所述超声换能器具有非圆柱形状。
51.如权利要求50所述的超声换能器，其中所述超声换能器具有平的、凹的或凸的形状。
52.如权利要求34至40中任一项所述的超声换能器，其中所述换能器的内表面和外表面均包含铜层、镍层和金层。
CN201480013826.XA 2013-03-14 2014-03-10 电镀或涂覆超声换能器的方法 Active CN105074050B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201361784164P 2013-03-14 2013-03-14
US61/784,164 2013-03-14
PCT/US2014/022796 WO2014159273A1 (en) 2013-03-14 2014-03-10 Methods of plating or coating ultrasound transducers

Publications (2)

Publication Number Publication Date
CN105074050A true CN105074050A (zh) 2015-11-18
CN105074050B CN105074050B (zh) 2019-02-15

Family

ID=50630977

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201480013826.XA Active CN105074050B (zh) 2013-03-14 2014-03-10 电镀或涂覆超声换能器的方法

Country Status (5)

Country Link
US (1) US10230041B2 (zh)
EP (1) EP2971232A1 (zh)
JP (1) JP6337080B2 (zh)
CN (1) CN105074050B (zh)
WO (1) WO2014159273A1 (zh)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8241274B2 (en) 2000-01-19 2012-08-14 Medtronic, Inc. Method for guiding a medical device
US8150519B2 (en) 2002-04-08 2012-04-03 Ardian, Inc. Methods and apparatus for bilateral renal neuromodulation
US7617005B2 (en) 2002-04-08 2009-11-10 Ardian, Inc. Methods and apparatus for thermally-induced renal neuromodulation
US20040082859A1 (en) 2002-07-01 2004-04-29 Alan Schaer Method and apparatus employing ultrasound energy to treat body sphincters
US10499937B2 (en) 2006-05-19 2019-12-10 Recor Medical, Inc. Ablation device with optimized input power profile and method of using the same
US20080039746A1 (en) 2006-05-25 2008-02-14 Medtronic, Inc. Methods of using high intensity focused ultrasound to form an ablated tissue area containing a plurality of lesions
US20160059044A1 (en) 2009-10-12 2016-03-03 Kona Medical, Inc. Energy delivery to intraparenchymal regions of the kidney to treat hypertension
CN102596320B (zh) 2009-10-30 2016-09-07 瑞蔻医药有限公司 通过经皮超声波去肾神经治疗高血压的方法和装置
EP3799931A1 (en) 2013-03-14 2021-04-07 ReCor Medical, Inc. Ultrasound-based neuromodulation system
WO2014159273A1 (en) 2013-03-14 2014-10-02 Recor Medical, Inc. Methods of plating or coating ultrasound transducers
US11047979B2 (en) * 2016-07-27 2021-06-29 Sound Technology Inc. Ultrasound transducer array
EP4108197A1 (en) 2021-06-24 2022-12-28 Gradient Denervation Technologies Systems for treating tissue
US20240058028A1 (en) 2022-08-16 2024-02-22 Otsuka Medical Devices Co., Ltd. Air-backed transducers for ultrasound denervation and methods and systems that use air-backed transducers

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0838980A2 (en) * 1996-10-25 1998-04-29 Canon Kabushiki Kaisha Glass circuit substrate and fabrication method thereof
JP2000054153A (ja) * 1998-08-07 2000-02-22 Murata Mfg Co Ltd 電子部品の電極形成方法
CN1428458A (zh) * 2001-12-18 2003-07-09 株式会社村田制作所 电子部件的制造方法及该电子部件，无电敷镀方法
CN1763245A (zh) * 2004-10-21 2006-04-26 阿尔卑斯电气株式会社 镀覆衬底、非电解镀方法及使用了该方法的电路形成方法
WO2009149315A2 (en) * 2008-06-06 2009-12-10 Boston Scientific Scimed, Inc. Transducers, devices and systems containing the transducers, and methods of manufacture

Family Cites Families (256)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3938502A (en) * 1972-02-22 1976-02-17 Nicolaas Bom Apparatus with a catheter for examining hollow organs or bodies with the ultrasonic waves
US4841977A (en) 1987-05-26 1989-06-27 Inter Therapy, Inc. Ultra-thin acoustic transducer and balloon catheter using same in imaging array subassembly
US5108369A (en) 1990-03-15 1992-04-28 Diagnostic Devices Group, Limited Dual-diameter multifunction catheter
US5324255A (en) 1991-01-11 1994-06-28 Baxter International Inc. Angioplasty and ablative devices having onboard ultrasound components and devices and methods for utilizing ultrasound to treat or prevent vasopasm
US5769812A (en) 1991-07-16 1998-06-23 Heartport, Inc. System for cardiac procedures
GB2258364A (en) * 1991-07-30 1993-02-03 Intravascular Res Ltd Ultrasonic tranducer
JPH0568684A (ja) 1991-09-13 1993-03-23 Olympus Optical Co Ltd 超音波治療装置
US5327885A (en) 1991-10-08 1994-07-12 Griffith James M Combination catheter for invasive probe delivery and balloon dilation
US5295992A (en) 1992-03-16 1994-03-22 Othy, Inc. Patella cutting system
CH683718A5 (de) * 1992-05-15 1994-04-29 Kk Holding Ag Kombinierter Kraft-, Dehnungs- und Schallemissionsaufnehmer.
US5295995A (en) 1992-08-27 1994-03-22 Kleiman Jay H Perfusion dilatation catheter
US5620479A (en) 1992-11-13 1997-04-15 The Regents Of The University Of California Method and apparatus for thermal therapy of tumors
US5400267A (en) 1992-12-08 1995-03-21 Hemostatix Corporation Local in-device memory feature for electrically powered medical equipment
US5423220A (en) * 1993-01-29 1995-06-13 Parallel Design Ultrasonic transducer array and manufacturing method thereof
ATE178218T1 (de) 1993-02-05 1999-04-15 Joe W And Dorothy Dorsett Brow Ultraschallballonkatheter für angioplastik
US5308356A (en) 1993-02-25 1994-05-03 Blackshear Jr Perry L Passive perfusion angioplasty catheter
US5630837A (en) 1993-07-01 1997-05-20 Boston Scientific Corporation Acoustic ablation
US5354200A (en) 1993-09-27 1994-10-11 Michael Klein Temperature gauge for dental drills and method employing same
WO1996000043A1 (en) 1994-06-27 1996-01-04 Ep Technologies, Inc. Tissue heating and ablation system
JPH0826437A (ja) * 1994-07-11 1996-01-30 Fuji Photo Film Co Ltd ワーク移送方法及び移送装置
NL9401184A (nl) 1994-07-19 1996-03-01 Cordis Europ Zuigcatheter.
US6142994A (en) 1994-10-07 2000-11-07 Ep Technologies, Inc. Surgical method and apparatus for positioning a diagnostic a therapeutic element within the body
DE4438799A1 (de) * 1994-10-18 1996-04-25 Atotech Deutschland Gmbh Verfahren zum Beschichten elektrisch nichtleitender Oberflächen mit Metallstrukturen
JPH08264371A (ja) * 1995-03-17 1996-10-11 Taiyo Yuden Co Ltd 無電解メッキ膜付電子部品の製造方法
US5938645A (en) 1995-05-24 1999-08-17 Boston Scientific Corporation Northwest Technology Center Inc. Percutaneous aspiration catheter system
US5803083A (en) 1995-11-09 1998-09-08 Cordis Corporation Guiding catheter with ultrasound imaging capability
US5775338A (en) 1997-01-10 1998-07-07 Scimed Life Systems, Inc. Heated perfusion balloon for reduction of restenosis
CN1230120C (zh) 1997-05-23 2005-12-07 普罗里森姆股份有限公司 由mri引导的治疗装置
US6869431B2 (en) 1997-07-08 2005-03-22 Atrionix, Inc. Medical device with sensor cooperating with expandable member
US6117101A (en) 1997-07-08 2000-09-12 The Regents Of The University Of California Circumferential ablation device assembly
JP4000243B2 (ja) 1997-07-08 2007-10-31 ザ リージェンツ オブ ザ ユニヴァーシティ オブ カリフォルニア 周辺部切除装置組立体および方法
JP2001514921A (ja) 1997-08-13 2001-09-18 サークス， インコーポレイテッド 組織収縮のための非侵襲性デバイス、方法、およびシステム
US6517534B1 (en) 1998-02-11 2003-02-11 Cosman Company, Inc. Peri-urethral ablation
US6299583B1 (en) 1998-03-17 2001-10-09 Cardiox Corporation Monitoring total circulating blood volume and cardiac output
US6905494B2 (en) 1998-03-31 2005-06-14 Innercool Therapies, Inc. Method and device for performing cooling- or cryo-therapies for, e.g., angioplasty with reduced restenosis or pulmonary vein cell necrosis to inhibit atrial fibrillation employing tissue protection
US7198635B2 (en) 2000-10-17 2007-04-03 Asthmatx, Inc. Modification of airways by application of energy
US6162178A (en) 1998-07-31 2000-12-19 Scimed Life Systems, Inc. Ultrasonic transducer off-aperture connection
US6355030B1 (en) 1998-09-25 2002-03-12 Cardiothoracic Systems, Inc. Instruments and methods employing thermal energy for the repair and replacement of cardiac valves
JP3316748B2 (ja) * 1998-10-20 2002-08-19 株式会社村田製作所 無電解めっき用ホルダおよび無電解めっき方法
US6149596A (en) 1998-11-05 2000-11-21 Bancroft; Michael R. Ultrasonic catheter apparatus and method
US6277077B1 (en) 1998-11-16 2001-08-21 Cardiac Pathways Corporation Catheter including ultrasound transducer with emissions attenuation
US6102863A (en) 1998-11-20 2000-08-15 Atl Ultrasound Ultrasonic diagnostic imaging system with thin cable ultrasonic probes
US6607502B1 (en) 1998-11-25 2003-08-19 Atrionix, Inc. Apparatus and method incorporating an ultrasound transducer onto a delivery member
WO2000041881A1 (en) 1999-01-15 2000-07-20 Bic Corporation Correction tape having dye migration blocking properties
US6097985A (en) 1999-02-09 2000-08-01 Kai Technologies, Inc. Microwave systems for medical hyperthermia, thermotherapy and diagnosis
US6492762B1 (en) 1999-03-22 2002-12-10 Transurgical, Inc. Ultrasonic transducer, transducer array, and fabrication method
US6190377B1 (en) 1999-05-05 2001-02-20 James A. Kuzdrall Method and apparatus for predictive beam energy control in laser surgery
US6712836B1 (en) 1999-05-13 2004-03-30 St. Jude Medical Atg, Inc. Apparatus and methods for closing septal defects and occluding blood flow
US20010007940A1 (en) 1999-06-21 2001-07-12 Hosheng Tu Medical device having ultrasound imaging and therapeutic means
EP1207788A4 (en) 1999-07-19 2009-12-09 St Jude Medical Atrial Fibrill FABRIC ABLATION TECHNIQUES AND CORRESPONDING DEVICE
AU7362400A (en) 1999-09-10 2001-04-10 Transurgical, Inc. Occlusion of tubular anatomical structures by energy application
JP2001111126A (ja) * 1999-10-13 2001-04-20 Sumitomo Metal Electronics Devices Inc 圧電素子
US20040215235A1 (en) 1999-11-16 2004-10-28 Barrx, Inc. Methods and systems for determining physiologic characteristics for treatment of the esophagus
US8221402B2 (en) 2000-01-19 2012-07-17 Medtronic, Inc. Method for guiding a medical device
US20020165771A1 (en) 2001-05-07 2002-11-07 Walker Jay S. Method and apparatus for establishing prices for a plurality of products
US6913581B2 (en) 2000-03-20 2005-07-05 Paul D. Corl High output therapeutic ultrasound transducer
CA2399570C (en) 2000-03-24 2009-02-10 Transurgical, Inc. Apparatus and method for intrabody thermal treatment
US6547946B2 (en) * 2000-04-10 2003-04-15 The Regents Of The University Of California Processing a printed wiring board by single bath electrodeposition
AU6321301A (en) 2000-05-16 2001-11-26 Atrionix Inc Apparatus and method incorporating an ultrasound transducer onto a delivery member
DE60134739D1 (de) 2000-05-16 2008-08-21 Atrionix Inc Katheter mit lenkbarer spitze und spurausrichtungsmechanismus eines führungsdrahts
JP3579326B2 (ja) 2000-05-25 2004-10-20 オリンパス株式会社 超音波診断装置および超音波診断装置の制御方法
EP1647305B1 (en) 2000-06-20 2010-12-29 Boston Scientific Corporation System for heating a body organ
AU7346801A (en) 2000-07-13 2002-01-30 Transurgical Inc Energy application with inflatable annular lens
CN1241658C (zh) 2000-07-13 2006-02-15 普罗里森姆股份有限公司 一种在存活对象的体内施加能量的装置
US8251986B2 (en) 2000-08-17 2012-08-28 Angiodynamics, Inc. Method of destroying tissue cells by eletroporation
US7422586B2 (en) 2001-02-28 2008-09-09 Angiodynamics, Inc. Tissue surface treatment apparatus and method
US20040253450A1 (en) * 2001-05-24 2004-12-16 Shipley Company, L.L.C. Formaldehyde-free electroless copper plating process and solution for use in the process
US20030032898A1 (en) 2001-05-29 2003-02-13 Inder Raj. S. Makin Method for aiming ultrasound for medical treatment
US20020193781A1 (en) 2001-06-14 2002-12-19 Loeb Marvin P. Devices for interstitial delivery of thermal energy into tissue and methods of use thereof
US6763722B2 (en) 2001-07-13 2004-07-20 Transurgical, Inc. Ultrasonic transducers
US20060116736A1 (en) 2001-07-23 2006-06-01 Dilorenzo Daniel J Method, apparatus, and surgical technique for autonomic neuromodulation for the treatment of obesity
US6953469B2 (en) 2001-08-30 2005-10-11 Ethicon, Inc, Device and method for treating intraluminal tissue
US20030060813A1 (en) 2001-09-22 2003-03-27 Loeb Marvin P. Devices and methods for safely shrinking tissues surrounding a duct, hollow organ or body cavity
US6475146B1 (en) 2001-09-24 2002-11-05 Siemens Medical Solutions Usa, Inc. Method and system for using personal digital assistants with diagnostic medical ultrasound systems
US7285116B2 (en) 2004-05-15 2007-10-23 Irvine Biomedical Inc. Non-contact tissue ablation device and methods thereof
US8974446B2 (en) 2001-10-11 2015-03-10 St. Jude Medical, Inc. Ultrasound ablation apparatus with discrete staggered ablation zones
US20030161805A1 (en) 2001-11-16 2003-08-28 Kobo Products, Inc. Organosilicon treated cosmetic powders, their production and use
US7347852B2 (en) 2001-11-20 2008-03-25 Angiodynamics, Inc. Catheter retention
AU2003209287A1 (en) 2002-01-15 2003-07-30 The Regents Of The University Of California System and method providing directional ultrasound therapy to skeletal joints
US7819826B2 (en) 2002-01-23 2010-10-26 The Regents Of The University Of California Implantable thermal treatment method and apparatus
US6736835B2 (en) 2002-03-21 2004-05-18 Depuy Acromed, Inc. Early intervention spinal treatment methods and devices for use therein
US7160434B2 (en) 2002-03-22 2007-01-09 Robert E. Moroney, Llc Therapeutic electrolysis device
US7853333B2 (en) 2002-04-08 2010-12-14 Ardian, Inc. Methods and apparatus for multi-vessel renal neuromodulation
US8347891B2 (en) 2002-04-08 2013-01-08 Medtronic Ardian Luxembourg S.A.R.L. Methods and apparatus for performing a non-continuous circumferential treatment of a body lumen
US20070135875A1 (en) 2002-04-08 2007-06-14 Ardian, Inc. Methods and apparatus for thermally-induced renal neuromodulation
US7756583B2 (en) 2002-04-08 2010-07-13 Ardian, Inc. Methods and apparatus for intravascularly-induced neuromodulation
US8131371B2 (en) 2002-04-08 2012-03-06 Ardian, Inc. Methods and apparatus for monopolar renal neuromodulation
US8774913B2 (en) 2002-04-08 2014-07-08 Medtronic Ardian Luxembourg S.A.R.L. Methods and apparatus for intravasculary-induced neuromodulation
US8150520B2 (en) 2002-04-08 2012-04-03 Ardian, Inc. Methods for catheter-based renal denervation
US8145316B2 (en) 2002-04-08 2012-03-27 Ardian, Inc. Methods and apparatus for renal neuromodulation
US8150519B2 (en) 2002-04-08 2012-04-03 Ardian, Inc. Methods and apparatus for bilateral renal neuromodulation
US20070129761A1 (en) 2002-04-08 2007-06-07 Ardian, Inc. Methods for treating heart arrhythmia
US8145317B2 (en) 2002-04-08 2012-03-27 Ardian, Inc. Methods for renal neuromodulation
US7620451B2 (en) 2005-12-29 2009-11-17 Ardian, Inc. Methods and apparatus for pulsed electric field neuromodulation via an intra-to-extravascular approach
US7162303B2 (en) 2002-04-08 2007-01-09 Ardian, Inc. Renal nerve stimulation method and apparatus for treatment of patients
US7653438B2 (en) 2002-04-08 2010-01-26 Ardian, Inc. Methods and apparatus for renal neuromodulation
US7617005B2 (en) 2002-04-08 2009-11-10 Ardian, Inc. Methods and apparatus for thermally-induced renal neuromodulation
US6978174B2 (en) 2002-04-08 2005-12-20 Ardian, Inc. Methods and devices for renal nerve blocking
US7503904B2 (en) 2002-04-25 2009-03-17 Cardiac Pacemakers, Inc. Dual balloon telescoping guiding catheter
NZ537256A (en) 2002-05-23 2007-09-28 Gendel Ltd Ablation device using electric field to sensitise the target tissue and ultrasound to treat the tissue
US6793635B2 (en) 2002-06-28 2004-09-21 Ethicon, Inc. Devices having deployable ultrasound transducers and method of use of same
US20130197555A1 (en) 2002-07-01 2013-08-01 Recor Medical, Inc. Intraluminal devices and methods for denervation
US20040082859A1 (en) 2002-07-01 2004-04-29 Alan Schaer Method and apparatus employing ultrasound energy to treat body sphincters
WO2004004572A1 (en) 2002-07-08 2004-01-15 Prorhythm, Inc. Cardiac ablation using microbubbles
US6866662B2 (en) 2002-07-23 2005-03-15 Biosense Webster, Inc. Ablation catheter having stabilizing array
US6712767B2 (en) 2002-08-29 2004-03-30 Volcano Therapeutics, Inc. Ultrasonic imaging devices and methods of fabrication
WO2004073505A2 (en) 2003-02-20 2004-09-02 Prorhythm, Inc. Cardiac ablation devices
US20040163655A1 (en) 2003-02-24 2004-08-26 Plc Systems Inc. Method and catheter system applicable to acute renal failure
EP1619925B1 (en) * 2003-04-01 2017-11-01 Olympus Corporation Ultrasonic vibrator and its manufacturing method
US20040230116A1 (en) 2003-05-12 2004-11-18 Pharmasonics, Inc. Method and apparatus for detection of ultrasound transducer failure in catheter systems
JP2004363304A (ja) 2003-06-04 2004-12-24 Toshiba Corp 半導体装置の検査方法及び検査装置
US7678104B2 (en) 2003-07-17 2010-03-16 Biosense Webster, Inc. Ultrasound ablation catheter and method for its use
US7670335B2 (en) 2003-07-21 2010-03-02 Biosense Webster, Inc. Ablation device with spiral array ultrasound transducer
US6911935B2 (en) 2003-08-15 2005-06-28 Siemens Milltronics Process Instruments Inc. Field interchangeable level measurement system
AU2004285412A1 (en) 2003-09-12 2005-05-12 Minnow Medical, Llc Selectable eccentric remodeling and/or ablation of atherosclerotic material
US7396336B2 (en) 2003-10-30 2008-07-08 Sherwood Services Ag Switched resonant ultrasonic power amplifier system
US20050156362A1 (en) * 2003-11-29 2005-07-21 Joe Arnold Piezoelectric device and method of manufacturing same
US8425417B2 (en) 2003-12-05 2013-04-23 Dexcom, Inc. Integrated device for continuous in vivo analyte detection and simultaneous control of an infusion device
US7854733B2 (en) 2004-03-24 2010-12-21 Biosense Webster, Inc. Phased-array for tissue treatment
US9713730B2 (en) 2004-09-10 2017-07-25 Boston Scientific Scimed, Inc. Apparatus and method for treatment of in-stent restenosis
US9277955B2 (en) 2010-04-09 2016-03-08 Vessix Vascular, Inc. Power generating and control apparatus for the treatment of tissue
JP5220412B2 (ja) 2004-09-13 2013-06-26 バイオセンス・ウエブスター・インコーポレーテツド フェーズド・アレイ超音波トランスデューサを伴うアブレーション装置
EP1795132B1 (en) * 2004-09-21 2011-07-06 Olympus Corporation Ultrasonic transducer
US8521295B2 (en) 2004-09-23 2013-08-27 Michael D. Laufer Location and deactivation of muscles
EP1808130A4 (en) * 2004-09-24 2018-02-14 Olympus Corporation Ultrasonic transducer, ultrasonic array and ultrasonic endoscope system
US10123903B2 (en) 2004-10-14 2018-11-13 Koninklijke Philips N.V. Ablation devices and methods with ultrasonic imaging
US7937143B2 (en) 2004-11-02 2011-05-03 Ardian, Inc. Methods and apparatus for inducing controlled renal neuromodulation
JP2006161116A (ja) * 2004-12-08 2006-06-22 Konica Minolta Holdings Inc 無電解めっきによる電極形成方法及びインクジェットヘッドの製造方法
US8162858B2 (en) 2004-12-13 2012-04-24 Us Hifu, Llc Ultrasonic medical treatment device with variable focal zone
US20060155269A1 (en) 2005-01-12 2006-07-13 Prorhythm, Inc. Epicardial ablation using focused ultrasound
US20100033940A1 (en) 2005-03-01 2010-02-11 Matsushita Electric Industrial Co., Ltd. Inter-board coupling connector and circuit board device using inter-board coupling connector
US20060241523A1 (en) 2005-04-12 2006-10-26 Prorhythm, Inc. Ultrasound generating method, apparatus and probe
US20060270976A1 (en) 2005-05-31 2006-11-30 Prorhythm, Inc. Steerable catheter
WO2006134651A1 (ja) 2005-06-15 2006-12-21 Nissan Chemical Industries, Ltd. 農薬顆粒状水和剤及びその製造方法
EP2662044B1 (en) 2005-07-21 2018-10-31 Covidien LP Systems for treating a hollow anatomical structure
US20070021803A1 (en) 2005-07-22 2007-01-25 The Foundry Inc. Systems and methods for neuromodulation for treatment of pain and other disorders associated with nerve conduction
US8140170B2 (en) 2005-09-12 2012-03-20 The Cleveland Clinic Foundation Method and apparatus for renal neuromodulation
US8734438B2 (en) 2005-10-21 2014-05-27 Covidien Ag Circuit and method for reducing stored energy in an electrosurgical generator
US20070124458A1 (en) 2005-11-30 2007-05-31 Cisco Technology, Inc. Method and system for event notification on network nodes
US20070203547A1 (en) 2005-12-15 2007-08-30 Costello Benedict J Medical device identification
CA2574934C (en) 2006-01-24 2015-12-29 Sherwood Services Ag System and method for closed loop monitoring of monopolar electrosurgical apparatus
US20070175359A1 (en) * 2006-02-01 2007-08-02 Kilnam Hwang Electroless gold plating solution and method
US8790281B2 (en) 2006-04-20 2014-07-29 The Regents Of The University Of California Method of thermal treatment of myolysis and destruction of benign uterine tumors
US20100198065A1 (en) 2009-01-30 2010-08-05 VyntronUS, Inc. System and method for ultrasonically sensing and ablating tissue
EP2540246B8 (en) 2006-05-12 2020-10-07 Vytronus, Inc. Device for ablating body tissue
US10499937B2 (en) 2006-05-19 2019-12-10 Recor Medical, Inc. Ablation device with optimized input power profile and method of using the same
WO2007135875A1 (en) 2006-05-19 2007-11-29 Daikin Industries, Ltd. Silicone-containing thermoplastic fluororesin composition, article molded therefrom, and process for preparing silicone-containing thermoplastic fluororesin composition
EP2092957B2 (en) 2006-06-28 2019-11-20 Medtronic Ardian Luxembourg S.à.r.l. Systems for thermally-induced renal neuromodulation
US7652411B2 (en) 2006-09-18 2010-01-26 Medicis Technologies Corporation Transducer with shield
CA2666661C (en) 2006-10-18 2015-01-20 Minnow Medical, Inc. Tuned rf energy and electrical tissue characterization for selective treatment of target tissues
US8192363B2 (en) 2006-10-27 2012-06-05 Ekos Corporation Catheter with multiple ultrasound radiating members
JP4513802B2 (ja) 2006-12-20 2010-07-28 セイコーエプソン株式会社 印刷装置
JP2008214669A (ja) * 2007-03-01 2008-09-18 Matsushita Electric Ind Co Ltd 電子部品のめっき装置およびめっき方法
US7581296B2 (en) * 2007-04-11 2009-09-01 Ge Inspection Technologies, Lp Acoustic stack for ultrasonic transducers and method for manufacturing same
US10183183B2 (en) 2007-04-13 2019-01-22 Acoustic Medsystems, Inc. Acoustic applicators for controlled thermal modification of tissue
WO2008151001A2 (en) 2007-05-30 2008-12-11 The Cleveland Clinic Foundation Method for treating a renal disease or disorder
US10021789B2 (en) * 2007-07-02 2018-07-10 Ebara-Udylite Co., Ltd. Metal-laminated polyimide substrate, and method for production thereof
JP5676255B2 (ja) * 2007-07-03 2015-02-25 コーニンクレッカ フィリップス エヌ ヴェ 存在検出のための薄膜検出器
JP4892102B2 (ja) 2007-07-11 2012-03-07 コーニンクレッカ フィリップス エレクトロニクス エヌ ヴィ 調整可能な流体レンズを備える超音波アセンブリ
US8734483B2 (en) 2007-08-27 2014-05-27 Cook Medical Technologies Llc Spider PFO closure device
DE102007046951B3 (de) 2007-10-01 2009-02-26 B. Braun Melsungen Ag Vorrichtung zum Einführen eines Medikaments in einen Infusionsbehälter
US8439907B2 (en) 2007-11-07 2013-05-14 Mirabilis Medica Inc. Hemostatic tissue tunnel generator for inserting treatment apparatus into tissue of a patient
US8115367B2 (en) * 2007-11-26 2012-02-14 Sii Nanotechnology Inc. Piezoelectric actuator provided with a displacement meter, piezoelectric element, and positioning device
US9107690B2 (en) 2007-12-03 2015-08-18 Covidien Ag Battery-powered hand-held ultrasonic surgical cautery cutting device
US10492854B2 (en) 2007-12-05 2019-12-03 Biosense Webster, Inc. Catheter-based acoustic radiation force impulse system
WO2009077939A1 (en) 2007-12-14 2009-06-25 Koninklijke Philips Electronics N.V. Adjustable lens system for real-time applications
US8562600B2 (en) 2007-12-27 2013-10-22 St. Jude Medical, Atrial Fibrillation Division, Inc. Integration of control software with a medical device and system
US20090248011A1 (en) 2008-02-28 2009-10-01 Hlavka Edwin J Chronic venous insufficiency treatment
US20090228003A1 (en) 2008-03-04 2009-09-10 Prorhythm, Inc. Tissue ablation device using radiofrequency and high intensity focused ultrasound
US9138213B2 (en) 2008-03-07 2015-09-22 W.L. Gore & Associates, Inc. Heart occlusion devices
US8133222B2 (en) 2008-05-28 2012-03-13 Medwaves, Inc. Tissue ablation apparatus and method using ultrasonic imaging
US9155588B2 (en) 2008-06-13 2015-10-13 Vytronus, Inc. System and method for positioning an elongate member with respect to an anatomical structure
US20090312693A1 (en) 2008-06-13 2009-12-17 Vytronus, Inc. System and method for delivering energy to tissue
US20100152582A1 (en) 2008-06-13 2010-06-17 Vytronus, Inc. Handheld system and method for delivering energy to tissue
US20090312673A1 (en) 2008-06-14 2009-12-17 Vytronus, Inc. System and method for delivering energy to tissue
US20100049099A1 (en) 2008-07-18 2010-02-25 Vytronus, Inc. Method and system for positioning an energy source
US10363057B2 (en) 2008-07-18 2019-07-30 Vytronus, Inc. System and method for delivering energy to tissue
JP5622729B2 (ja) 2008-09-22 2014-11-12 べシックス・バスキュラー・インコーポレイテッド 身体組織に対して温度効果を誘発するシステム
US9192789B2 (en) 2008-10-30 2015-11-24 Vytronus, Inc. System and method for anatomical mapping of tissue and planning ablation paths therein
US8414508B2 (en) 2008-10-30 2013-04-09 Vytronus, Inc. System and method for delivery of energy to tissue while compensating for collateral tissue
US9033885B2 (en) 2008-10-30 2015-05-19 Vytronus, Inc. System and method for energy delivery to tissue while monitoring position, lesion depth, and wall motion
US8475379B2 (en) 2008-11-17 2013-07-02 Vytronus, Inc. Systems and methods for ablating body tissue
CN102307618B (zh) 2008-12-09 2014-03-12 内费拉有限公司 泌尿系统的刺激
US8923970B2 (en) 2008-12-09 2014-12-30 Nephera Ltd. Stimulation of the urinary system
US8882672B2 (en) 2008-12-29 2014-11-11 Perseus-Biomed Inc. Method and system for tissue imaging and analysis
US8864669B2 (en) 2008-12-29 2014-10-21 Perseus-Biomed Inc. Method and system for tissue imaging and analysis
US8870772B2 (en) 2008-12-29 2014-10-28 Perseus-Biomed Inc. Method and system for tissue recognition
US8712550B2 (en) 2008-12-30 2014-04-29 Biosense Webster, Inc. Catheter with multiple electrode assemblies for use at or near tubular regions of the heart
US8808345B2 (en) 2008-12-31 2014-08-19 Medtronic Ardian Luxembourg S.A.R.L. Handle assemblies for intravascular treatment devices and associated systems and methods
US20100168739A1 (en) 2008-12-31 2010-07-01 Ardian, Inc. Apparatus, systems, and methods for achieving intravascular, thermally-induced renal neuromodulation
US8652129B2 (en) 2008-12-31 2014-02-18 Medtronic Ardian Luxembourg S.A.R.L. Apparatus, systems, and methods for achieving intravascular, thermally-induced renal neuromodulation
WO2010080886A1 (en) 2009-01-09 2010-07-15 Recor Medical, Inc. Methods and apparatus for treatment of mitral valve in insufficiency
NZ619320A (en) 2009-04-22 2015-08-28 Mercator Medsystems Inc Use of guanethidine for treating hypertension by local vascular delivery
US8287472B2 (en) 2009-04-30 2012-10-16 Boston Scientific Scimed, Inc. Ultrasound heater-agitator for thermal tissue treatment
KR101619380B1 (ko) * 2009-05-14 2016-05-11 삼성디스플레이 주식회사 식각액 조성물 및 이를 이용한 어레이 기판의 제조방법
US20110054515A1 (en) 2009-08-25 2011-03-03 John Bridgeman Device and method for occluding the left atrial appendage
US20110092880A1 (en) 2009-10-12 2011-04-21 Michael Gertner Energetic modulation of nerves
US8295912B2 (en) 2009-10-12 2012-10-23 Kona Medical, Inc. Method and system to inhibit a function of a nerve traveling with an artery
AU2010307029B2 (en) 2009-10-12 2014-07-31 Otsuka Medical Devices Co., Ltd. Energetic modulation of nerves
US9119951B2 (en) 2009-10-12 2015-09-01 Kona Medical, Inc. Energetic modulation of nerves
US8469904B2 (en) 2009-10-12 2013-06-25 Kona Medical, Inc. Energetic modulation of nerves
US8517962B2 (en) 2009-10-12 2013-08-27 Kona Medical, Inc. Energetic modulation of nerves
US9174065B2 (en) 2009-10-12 2015-11-03 Kona Medical, Inc. Energetic modulation of nerves
US20110257563A1 (en) 2009-10-26 2011-10-20 Vytronus, Inc. Methods and systems for ablating tissue
CN102596320B (zh) 2009-10-30 2016-09-07 瑞蔻医药有限公司 通过经皮超声波去肾神经治疗高血压的方法和装置
US20110112400A1 (en) 2009-11-06 2011-05-12 Ardian, Inc. High intensity focused ultrasound catheter apparatuses, systems, and methods for renal neuromodulation
US20110263921A1 (en) 2009-12-31 2011-10-27 Anthony Vrba Patterned Denervation Therapy for Innervated Renal Vasculature
US9072894B2 (en) 2010-01-18 2015-07-07 The Board Of Trustees Of The Leland Stanford Junior University Method and apparatus for radioablation of regular targets such as sympathetic nerves
EP2525715A4 (en) 2010-01-19 2014-06-04 Medtronic Ardian Luxembourg S R L METHODS AND APPARATUS FOR RENAL NEUROMODULATION BY STEREOTACTIC RADIOTHERAPY
CA2787062C (en) 2010-01-26 2017-07-11 Michael A. Evans Methods, devices, and agents for denervation
US9743980B2 (en) 2010-02-24 2017-08-29 Safepass Vascular Ltd Method and system for assisting a wire guide to cross occluded ducts
US20110257562A1 (en) 2010-04-01 2011-10-20 Alan Schaer Method and apparatus employing ultrasound energy to remodulate vascular nerves
JP5649322B2 (ja) * 2010-04-12 2015-01-07 三菱電機株式会社 半導体装置および半導体装置の製造方法
US9192790B2 (en) 2010-04-14 2015-11-24 Boston Scientific Scimed, Inc. Focused ultrasonic renal denervation
CA2796865A1 (en) 2010-04-26 2011-11-10 Medtronic Ardian Luxembourg S.A.R.L. Catheter apparatuses, systems, and methods for renal neuromodulation
US20120065554A1 (en) 2010-09-09 2012-03-15 Michael Pikus Dual Balloon Ablation Catheter with Vessel Deformation Arrangement for Renal Nerve Ablation
WO2012052926A2 (en) 2010-10-18 2012-04-26 CardioSonic Ltd. Tissue treatment
US20120215106A1 (en) 2010-10-18 2012-08-23 CardioSonic Ltd. Tissue treatment
US9566456B2 (en) 2010-10-18 2017-02-14 CardioSonic Ltd. Ultrasound transceiver and cooling thereof
US20130218054A1 (en) 2010-10-18 2013-08-22 CardioSonic Ltd. Separation device for ultrasound element
US8585601B2 (en) 2010-10-18 2013-11-19 CardioSonic Ltd. Ultrasound transducer
EP3449856B1 (en) 2010-10-25 2023-06-28 Medtronic Ardian Luxembourg S.à.r.l. Device for evaluation and feedback of neuromodulation treatment
US9668811B2 (en) 2010-11-16 2017-06-06 Boston Scientific Scimed, Inc. Minimally invasive access for renal nerve ablation
US9326751B2 (en) 2010-11-17 2016-05-03 Boston Scientific Scimed, Inc. Catheter guidance of external energy for renal denervation
JP6046631B2 (ja) 2010-11-19 2016-12-21 ボストン サイエンティフィック サイムド，インコーポレイテッドＢｏｓｔｏｎ Ｓｃｉｅｎｔｉｆｉｃ Ｓｃｉｍｅｄ，Ｉｎｃ． 腎神経の検出切除装置
US10016233B2 (en) 2010-12-06 2018-07-10 Biosense Webster (Israel) Ltd. Treatment of atrial fibrillation using high-frequency pacing and ablation of renal nerves
US9308041B2 (en) 2010-12-22 2016-04-12 Biosense Webster (Israel) Ltd. Lasso catheter with rotating ultrasound transducer
US20140163540A1 (en) 2011-02-18 2014-06-12 Recor Medical, Inc. Apparatus for effecting renal denervation using ultrasound
EP2521593B1 (en) 2011-03-15 2015-12-09 Kona Medical, Inc. Energetic modulation of nerves
CN103747756B (zh) 2011-04-13 2016-12-07 维特罗纳斯有限公司 集成式消融与标测系统
WO2012170482A1 (en) 2011-06-06 2012-12-13 St. Jude Medical, Inc. Renal denervation system and method
US20140200489A1 (en) 2011-09-01 2014-07-17 Perseus-Biomed Inc Method and system for tissue modulation
US20130090650A1 (en) 2011-10-11 2013-04-11 Boston Scientific Scimed, Inc. Renal nerve ablation cooling device and technique
WO2013096913A2 (en) 2011-12-23 2013-06-27 Vessix Vascular, Inc. Methods and apparatuses for remodeling tissue of or adjacent to a body passage
EP2809399B1 (en) 2012-01-30 2023-04-19 Auris Health, Inc. Tissue necrosis apparatus
US9439722B2 (en) 2012-05-09 2016-09-13 Biosense Webster (Israel) Ltd. Ablation targeting nerves in or near the inferior vena cava and/or abdominal aorta for treatment of hypertension
US11357447B2 (en) 2012-05-31 2022-06-14 Sonivie Ltd. Method and/or apparatus for measuring renal denervation effectiveness
WO2014012053A1 (en) 2012-07-13 2014-01-16 Boston Scientific Scimed, Inc. Off -wall electrode devices for nerve modulation
US20140025069A1 (en) 2012-07-17 2014-01-23 Boston Scientific Scimed, Inc. Renal nerve modulation catheter design
US20140067029A1 (en) 2012-08-28 2014-03-06 Boston Scientific Scimed, Inc. Renal nerve modulation and ablation catheter electrode design
CN104768487A (zh) 2012-09-13 2015-07-08 波士顿科学西美德公司 肾脏神经调节球囊及其制造和使用方法
WO2014102756A2 (en) 2012-12-31 2014-07-03 Perseus-Biomed Inc. Cath lab system for aiming ultrasound energy
US20140249524A1 (en) 2013-03-01 2014-09-04 Boston Scientific Scimed, Inc. System and method for performing renal nerve modulation
USD708810S1 (en) 2013-03-04 2014-07-08 Medtronic Ardian Luxembourg S.A.R.L. Generator cart
USD712833S1 (en) 2013-03-04 2014-09-09 Medtronic Ardian Luxembourg S.A.R.L. Generator system
USD712352S1 (en) 2013-03-04 2014-09-02 Medtronic Ardian Luxembourg S.A.R.L. Generator
USD697036S1 (en) 2013-03-04 2014-01-07 Medtronic Ardian Luxembourg S.A.R.L. Remote control
USD712353S1 (en) 2013-03-04 2014-09-02 Medtronic Ardian Luxembourg S.A.R.L. Generator system
EP2968931B1 (en) 2013-03-12 2022-03-16 Boston Scientific Scimed, Inc. Medical systems and methods for modulating nerves
US8876813B2 (en) 2013-03-14 2014-11-04 St. Jude Medical, Inc. Methods, systems, and apparatus for neural signal detection
WO2014159273A1 (en) 2013-03-14 2014-10-02 Recor Medical, Inc. Methods of plating or coating ultrasound transducers
EP3799931A1 (en) 2013-03-14 2021-04-07 ReCor Medical, Inc. Ultrasound-based neuromodulation system
US10265122B2 (en) 2013-03-15 2019-04-23 Boston Scientific Scimed, Inc. Nerve ablation devices and related methods of use
US9179973B2 (en) 2013-03-15 2015-11-10 St. Jude Medical, Cardiology Division, Inc. Feedback systems and methods for renal denervation utilizing balloon catheter
JP6220044B2 (ja) 2013-03-15 2017-10-25 ボストン サイエンティフィック サイムド，インコーポレイテッドＢｏｓｔｏｎ Ｓｃｉｅｎｔｉｆｉｃ Ｓｃｉｍｅｄ，Ｉｎｃ． 腎神経アブレーションのための医療用デバイス
EP2907464A1 (en) 2014-02-12 2015-08-19 Perseus-Biomed Inc. Methods and systems for treating nerve structures

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0838980A2 (en) * 1996-10-25 1998-04-29 Canon Kabushiki Kaisha Glass circuit substrate and fabrication method thereof
JP2000054153A (ja) * 1998-08-07 2000-02-22 Murata Mfg Co Ltd 電子部品の電極形成方法
CN1428458A (zh) * 2001-12-18 2003-07-09 株式会社村田制作所 电子部件的制造方法及该电子部件，无电敷镀方法
CN1763245A (zh) * 2004-10-21 2006-04-26 阿尔卑斯电气株式会社 镀覆衬底、非电解镀方法及使用了该方法的电路形成方法
WO2009149315A2 (en) * 2008-06-06 2009-12-10 Boston Scientific Scimed, Inc. Transducers, devices and systems containing the transducers, and methods of manufacture

Also Published As

Publication number Publication date
JP2016514438A (ja) 2016-05-19
WO2014159273A1 (en) 2014-10-02
US10230041B2 (en) 2019-03-12
EP2971232A1 (en) 2016-01-20
US20140272110A1 (en) 2014-09-18
JP6337080B2 (ja) 2018-06-06
CN105074050B (zh) 2019-02-15

Similar Documents

Publication Publication Date Title
CN105074050A (zh) 电镀或涂覆超声换能器的方法
JP2006188761A (ja) 伝導性金属めっきポリイミド基板及びその製造方法
KR0184889B1 (ko) 산성 팔라듐 스트라이크욕
JP2011246739A (ja) ステンレス鋼材へのめっき方法及びそのめっき材
JP7096422B2 (ja) 金属表面にグラフェンコーティング層を製造する方法
CN101986422A (zh) 制造半导体器件的方法及设备
CN106852007A (zh) 应用于pcb表面处理的双层镍金工艺
US6913791B2 (en) Method of surface treating titanium-containing metals followed by plating in the same electrolyte bath and parts made in accordance therewith
ATE447701T1 (de) Verfahren zur herstellung eines temperaturmessfühlers
CN100505159C (zh) 非平面表面金属微细图形化的方法
CN112030202B (zh) 一种跑道零件表面镀层的加工方法及其电镀挂具
US20040173466A1 (en) Titanium-containing metals with adherent coatings and methods for producing same
JP2006219724A (ja) 無電解めっき方法
CN108570700A (zh) 铝管电镀前的预处理方法
CN101624716A (zh) 铝管电镀前的预处理方法
CN110144609A (zh) 一种多次沉锌的电镀加工方法
JP4975344B2 (ja) めっき方法
KR101789110B1 (ko) 미세 파이프 제조방법 및 이에 의해 제조된 미세 파이프
CN1250772C (zh) 电镀预处理溶液和电镀预处理方法
JP4616490B2 (ja) Ｃｖｔ用プーリーへのめっき方法
JP2003041392A (ja) ガラス成形用金型のメッキ方法
JP4785081B2 (ja) 錫めっき処理材の被膜剥離方法
CN110049813A (zh) 改善液态金属对固体基底的表面的润湿的方法
KR20180053217A (ko) 미세 파이프 제조방법 및 이에 의해 제조된 미세 파이프
JP5552695B2 (ja) めっき方法及びその方法に用いられるめっき前処理液。

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant