CN100538930C - 具有优异端面绝缘的铁心和处理铁心端面以得到绝缘涂层的方法 - Google Patents
具有优异端面绝缘的铁心和处理铁心端面以得到绝缘涂层的方法 Download PDFInfo
- Publication number
- CN100538930C CN100538930C CNB2005100855867A CN200510085586A CN100538930C CN 100538930 C CN100538930 C CN 100538930C CN B2005100855867 A CNB2005100855867 A CN B2005100855867A CN 200510085586 A CN200510085586 A CN 200510085586A CN 100538930 C CN100538930 C CN 100538930C
- Authority
- CN
- China
- Prior art keywords
- coating
- organosilicon polymer
- iron core
- solution
- wrapping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (13)