Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05D5/00—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures
  • B05D5/06—Processes for applying liquids or other fluent materials to surfaces to obtain special surface effects, finishes or structures to obtain multicolour or other optical effects
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D11/00—Producing optical elements, e.g. lenses or prisms
  • B29D11/00009—Production of simple or compound lenses
  • B29D11/00038—Production of contact lenses
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D11/00—Producing optical elements, e.g. lenses or prisms
  • B29D11/00009—Production of simple or compound lenses
  • B29D11/00038—Production of contact lenses
  • B29D11/00125—Auxiliary operations, e.g. removing oxygen from the mould, conveying moulds from a storage to the production line in an inert atmosphere
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D11/00—Producing optical elements, e.g. lenses or prisms
  • B29D11/00634—Production of filters
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
  • B29D11/00—Producing optical elements, e.g. lenses or prisms
  • B29D11/00865—Applying coatings; tinting; colouring
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/04—Optical elements characterised by the material of which they are made; Optical coatings for optical elements made of organic materials, e.g. plastics
  • G02B1/041—Lenses
  • G02B1/043—Contact lenses

Definitions

• This invention is related to a method for making ophthalmic lenses (including contact lenses and intraocular lenses) capable of blocking ultra-violet ("UV”) radiation and thereby protecting eyes to some extent from damages caused by UV radiation.
• This invention also provides UV-absorbing ophthalmic lenses made according to a method of the invention.
• UV-absorbing ophthalmic lenses in particular UV-absorbing contact lenses are typically produced in mass by a so-called cast-molding process, which involves thermo- or UV- induced free-radical polymerization of a lens-forming composition including a polymerizable UV-absorber and at least one vinylic monomer, macromer and or prepolymer in molds.
• Copolymerizable benzotriazole, benzophenone and triazine UV absorbers which include an ethylenically unsaturated group covalently linked to their UV- absorbing moieties, are known and have been used previously. Those UV-absorbers can be incorporated into the polymer matrix of ophthalmic lenses.
• UV-induced polymerization process which has a processing cycle shorter than that of the thermo-induced polymerization process
• the efficiency of incorporation of the UV-absorber in lenses may not be certain.
• a UV-absorber present in a lens forming composition can reduce the amount of UV radiation available to initiate polymerization and may even lower the efficiency of covalent incorporation of the UV absorber into resultant lenses.
• Unreacted UV absorbers generally must be removed from the lenses in one or more extraction processes.
• a UV-absorber may result in ineffective or uneven photo-polymerization of the lens forming composition.
• the invention provides a method for making UV-absorbing ophthalmic lenses, the method comprising the steps of: obtaining an ophthalmic lens, preferably a contact lens; dipping the ophthalmic lens in a coating solution comprising a first organic solvent and a UV-absorbing polymer for a period of time sufficient to form a UV-absorbing coating on the ophthalmic lens; wherein the UV-absorbing polymer comprises UV-absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units; and optionally but preferably covalently attaching a hydrophilic polymer or polymeric material having reactive functional groups onto the UV-absorbing coating to form a hydrogel coating, wherein the hydrogel coating is covalently attached onto the UV-absorbing coating through linkages each formed between one carboxylic group of the UV-absorbing coating and one reactive functional group of the hydrophilic polymer or polymeric material.
• the invention provides an ophthalmic lenses, the lens comprising a polymeric lens body; a layer of UV-absorbing polymer on the lens body; and a hydrogel coating covalently attached onto the layer of the UV-absorbing polymer, wherein the UV- absorbing polymer comprises UV-absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units, wherein the hydrogel coating is obtained by covalently attaching a hydrophilic polymer or polymeric material having reactive functional groups onto the layer of the UV-absorbing polymer through linkages each formed between one carboxylic group of the UV-absorbing coating and one reactive functional group of the hydrophilic polymer or polymeric material.
• Figure 1 shows the UV-Vis transmission spectra of silicone hydrogel contact lenses with coatings thereon obtained by dipping in a fluorescein-modified PAA solution for different time periods.
• Figure 2 shows the UV-Vis absorbance at 490 nm of silicone hydrogel contact lenses with coatings thereon as function of dipping time for obtaining the coatings.
• Figure 3 shows the UV-Vis transmission spectrum of a silicone hydrogel contact lens with a UV-absorbing coating thereon.
• Figure 4 shows the UV-Vis transmission spectra of silicone hydrogel contact lenses with different coatings thereon. 1 : with PAA-L20 coating (dipping in PAA-L20 solution for about 20 minutes); with PAA-N20 and PAA-L20 coating (dipping in the PAA-N20 solution and then in the PAA-L20 solution respectively for about 20 minutes).
• an “ophthalmic lens” refers to a contact lens and/or an intraocular lens.
• a “contact Lens” refers to a structure that can be placed on or within a wearer's eye. A contact lens can correct, improve, or alter a user's eyesight, but that need not be the case.
• a “silicone hydrogel contact lens” refers to a contact lens comprising a silicone hydrogel material.
• hydrogel or “hydrogel material” refers to a crosslinked polymeric material which is not water-soluble and can contains at least 10% by weight of water within its polymer matrix when fully hydrated.
• soluble in reference to a compound or material in a solvent, means that the compound or material can be dissolved in the solvent to give a solution with a concentration of at least 0.5% by weight at room temperature (i.e., at a temperature of about 20°C to about 30°C).
• insoluble in reference to a compound or material in a solvent, means that the compound or material can be dissolved in the solvent to give a solution with a concentration of less than 0.005% by weight at room temperature.
• a “silicone hydrogel” refers to a hydrogel containing silicone.
• a silicone hydrogel typically is obtained by copolymerization of a polymerizable composition comprising at least one silicone-containing vinylic monomer or at least one silicone-containing vinylic macromer or at least one silicone-containing prepolymer having ethylenically unsaturated groups.
• a "vinylic monomer” refers to a compound that is soluble in a solvent and has one sole ethylenically-unsaturated group.
• exemplary ethylenically unsaturated groups include without
• (meth)acrylamide refers to methacrylamide and/or acrylamide.
• (meth)acrylate refers to methacrylate and/or acrylate.
• hydrophilic vinylic monomer refers to a vinylic monomer which can be polymerized to form a homopolymer that is water-soluble or can absorb at least 10 percent by weight of water.
• hydrophobic vinylic monomer refers to a vinylic monomer which can be polymerized to form a homopolymer that is insoluble in water and can absorb less than 10 percent by weight of water.
• the term "macromer” or “prepolymer” refers to a medium and high molecular weight compound or polymer that is soluble in a solvent and contains two or more ethylenically unsaturated groups.
• Medium and high molecular weight typically means average molecular weights greater than 700 Daltons.
• crosslinker refers to a compound having at least two ethylenically unsaturated groups.
• a “crosslinking agent” refers to a crosslinker having a molecular weight of about 700 Daltons or less.
• polymer means a material formed by polymerizing/crosslinking one or more monomers or macromers or prepolymers.
• molecular weight of a polymeric material refers to the weight-average molecular weight unless otherwise specifically noted or unless testing conditions indicate otherwise.
• amino group refers to a primary or secondary amino group of formula -NHR', where R' is hydrogen or a C C 2 o unsubstituted or substituted, linear or branched alkyl group, unless otherwise specifically noted.
• epichlorohydrin-functionalized polyamine or "epichlorohydrin-functionalized polyamidoamine” refers to a polymer obtained by reacting a polyamine or polyamidoamine with epichlorohydrin to convert all or a substantial percentage of amine groups of the polyamine or polyamidoamine into azetidinium groups.
• azetidinium group refers to a positively charged group of ⁇ .
• phosphorylcholine refers to a zwitterionic
• n is an integer of 1 to 5 and R-i , R 2 and R 3 independently of each other are C C 8 alkyl or C C 8 hydroxyalkyl.
• water contact angle refers to an average water contact angle (i.e., contact angles measured by Sessile Drop method), which is obtained by averaging measurements of contact angles.
• crosslinked coating or “hydrogel coating” interchangeably is used to describe a crosslinked polymeric material having a three- dimensional network that can contain water when fully hydrated.
• the three-dimensional network of a crosslinked polymeric material can be formed by crosslinking of two or more linear or branched polymers through crosslinkages.
• Polymer means a material formed by crosslinking or polymerizing one or more monomers.
• the invention is generally directed to a cost-effective and time-efficient method for making UV-absorbing ophthalmic lenses, in particular, contact lenses.
• a method of the invention involves a simple dipping process to apply a UV-absorbing coating onto an ophthalmic lens posterior to molding.
• the invention is partly based on the discovery that a layer (or coating) of a UV-absorbing polymer with carboxyl groups can be easily applied onto a cast-molded ophthalmic lens just by dipping the ophthalmic lens in a solution of the UV-absorbing polymer.
• the thickness and durability of the UV-absorbing coating can be controlled by using an organic solvent as the solvent or one of the solvent mixture in the UV-absorbing polymer solution and then rinsing with water or a mixture of water and at least one organic solvent. It is believed that when a solvent system containing at least one organic solvent is used for preparing a coating solution, it can swell an ophthalmic lens so that a portion of the UV-absorbing polymer may penetrate into the ophthalmic lens and increase the thickness of the UV-absorbing coating. The subsequent water-rinsing step can shrink the ophthalmic lens and embed partially the UV-absorbing polymer and increase the durability of the UV-absorbing coating.
• the present invention can provide the following advantages.
• Second, the whole process is based on wet chemistry (dipping ophthalmic lenses in a solution for a period of time). Such process can be easily implemented in a fully-automated, mass- production environment.
• Third, the process for incorporating UV-absorbers can be an integral part of a coating process for applying a hydrogel coating onto a contact lens.
• the invention provides a method for making UV-absorbing ophthalmic lenses, the method comprising the steps of: obtaining an ophthalmic lens, preferably a contact lens; dipping the ophthalmic lens in a coating solution comprising a first organic solvent and a UV-absorbing polymer for a period of time sufficient to form a UV-absorbing coating on the ophthalmic lens; wherein the UV-absorbing polymer comprises UV-absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units; and optionally but preferably covalently attaching a hydrophilic polymer or polymeric material having reactive functional groups onto the UV-absorbing coating to form a hydrogel coating, wherein the hydrogel coating is covalently attached onto the UV-absorbing coating through linkages each formed between one carboxylic group of the UV-absorbing coating and one reactive functional group of the hydrophilic polymer or polymeric material.
• a contact lens can be any contact lens, including soft and hard contact lens.
• a preferred soft contact lens is a silicone hydrogel contact lens.
• contact lenses can be produced in a conventional "spin-casting mold," as described for example in U.S. Patent No. 3,408,429, or by the full cast-molding process in a static form, as described in U.S. Patent Nos. 4,347,198; 5,508,317; 5,789,464; and 5,849,810, or by lathe cutting of silicone hydrogel buttons as used in making customized contact lenses.
• a lens formulation typically is dispensed into molds and cured (i.e., polymerized and/or crosslinked) in molds for making contact lenses.
• a lens formulation for cast-molding of contact lenses generally comprises at least one components selected from the group consisting of a silicone-containing vinylic monomer, a silicone-containing vinylic macromer, a hydrophilic vinylic monomer, a hydrophilic vinylic macromer, a hydrophobic vinylic monomer, and combination thereof.
• a lens-forming composition can also comprise various components, such as, for example, a crosslinking agent, a visibility tinting agent (e.g., dyes, pigments, or mixtures thereof), antimicrobial agents (e.g., preferably silver nanoparticles), a bioactive agent, leachable lubricants, leachable tear-stabilizing agents, and mixtures thereof, as known to a person skilled in the art.
• Resultant silicone hydrogel contact lenses then can be subjected to extraction with an extraction solvent to remove unpolymerized components from the resultant lenses and to hydration process, as known by a person skilled in the art.
• a contact lens can be a colored contact lens (i.e., a contact lens having at least one colored patterns printed thereon as well known to a person skilled in the art).
• a silicone hydrogel lens formulation for making commercial silicone hydrogel contact lenses such as, lotrafilcon A, lotrafilcon B, balafilcon A, galyfilcon A, senofilcon A, narafilcon A, narafilcon B, comfilcon A, enfilcon A, asmofilcon A, filcon II 3, can also be used in making silicone hydrogel contact lenses which then can be used to make UV-absorbing contact lenses according to a method of the invention.
• a mold for cast molding
• a mold generally comprises at least two mold sections (or portions) or mold halves, i.e. first and second mold halves.
• the first mold half defines a first molding (or optical) surface and the second mold half defines a second molding (or optical) surface.
• the first and second mold halves are configured to receive each other such that a lens forming cavity is formed between the first molding surface and the second molding surface.
• the molding surface of a mold half is the cavity-forming surface of the mold and in direct contact with lens-forming material.
• Methods of manufacturing mold sections for cast-molding a contact lens are generally well known to those of ordinary skill in the art.
• the process of the present invention is not limited to any particular method of forming a mold. In fact, any method of forming a mold can be used in the present invention.
• the first and second mold halves can be formed through various techniques, such as injection molding or lathing. Examples of suitable processes for forming the mold halves are disclosed in U.S. Patent Nos. 4,444,71 1 to Schad; 4,460,534 to Boehm et al.; 5,843,346 to Morrill; and 5,894,002 to Boneberqer et aL, which are also incorporated herein by reference.
• Virtually all materials known in the art for making molds can be used to make molds for making contact lenses.
• polymeric materials such as polyethylene, polypropylene, polystyrene, PMMA, Topas ® COC grade 8007-S10 (clear amorphous copolymer of ethylene and norbornene, from Ticona GmbH of Frankfurt, Germany and Summit, New Jersey), or the like can be used.
• Other materials that allow UV light transmission could be used, such as quartz glass and sapphire.
• a UV-absorbing polymer comprises UV-absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units; each UV-absorbing monomeric unit comprises a UV-absorbing moiety which can be benzotriazole-moiety, benzophenone- moiety or triazine moiety, with benzotriazole-moiety or benzophenone-moiety as preferred UV-absorbing moiety, with benzotriazole-moiety as most preferred UV-absorbing moiety.
• the term "monomeric units" refers to repeating units of a polymer, which are derived from a vinylic monomer in a polymerization and optionally can be modified by a compound after polymerization.
• a UV-absorbing polymer of the invention can be obtained by copolymerizing a polymerizable mixture comprising at least one carboxyl-containing vinylic monomer and at least one UV-absorbing vinylic monomer in the presence or absence of a vinylic monomer, provided that the carboxyl-containing vinylic monomer is present in an amount of at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90% by mole in the polymerizable composition.
• UV-absorbing vinylic monomers can be used in the preparation of a UV- absorbing polymer of the invention.
• preferred UV-absorbing vinylic monomers include without limitation benzotriazole-containing vinylic monomers (e.g., 2-(2-hydroxy-5- vinylphenyl)-2H-benzotriazole, 2-(2-hydroxy-5-acrylyloxyphenyl)-2H-benzotriazole, 2-(2- hydroxy-3-methacrylamido methyl-5-tert octylphenyl) benzotriazole, 2-(2'-hydroxy-5'- methacrylamidophenyl)-5-chlorobenzotriazole, 2-(2'-hydroxy-5'-methacrylamidophenyl)-5- methoxybenzotriazole, 2-(2'-hydroxy-5'-methacryloxypropyl-3'-t-butyl-phenyl)-5- chlorobenzotriazo le, 2-(2'-hydroxy-5'-methacryloxyethylphenyl)
• benzophenone-containing vinyl monomers e.g., 2-hydroxy-4-acryloxy alkoxy
• Benzotriazole-containing vinyl monomers can be prepared according to procedures described in US patent Nos. 3,299, 173, 4,612,358, 4,716,234, 4,528,31 1 (herein incorporated by reference in their entireties) or can be obtained from commercial suppliers.
• Benzophenone-containing vinyl monomers can be prepared according to procedures described in US patent Nos 3, 162,676 (herein incorporated by reference in its entirety) or can be obtained from commercial suppliers.
• carboxyl-containing vinylic monomers can be used in the preparation of a UV-absorbing polymer of the invention.
• suitable carboxyl-containing vinylic monomers include without limitation acrylic acid, C1-C12 alkylacrylic acid (e.g., methacrylic acid, ethylacrylic acid, propylacrylic acid, butylacrylic acid, pentylacrylic acid, etc.), ⁇ , ⁇ -2-acrylamidoglycolic acid, beta-methyl-acrylic acid (crotonic acid), alpha-phenyl acrylic acid, beta-acryloxy propionic acid, sorbic acid, angelic acid, cinnamic acid, 1- carobxy-4-phenyl butadiene-1 ,3, itaconic acid, citraconic acid, mesaconic acid, glutaconic acid, aconitic acid, maleic acid, fumaric acid, tricarboxy ethylene, and combinations thereof.
• a UV-absorbing polymer is prepared from at least one carboxy
• a UV-absorbing polymer of the invention can be obtained by reacting a UV-absorbing compound with (i.e., covalently attaching UV-absorbing moieties to) a precursor polymer having at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units in a coupling reaction known to a person skilled in the art.
• a “coupling reaction” is intended to describe any reaction between a pair of matching functional groups in the presence or absence of a coupling agent to form covalent bonds or linkages under various reaction conditions well known to a person skilled in the art, such as, for example, oxidation-reduction conditions, dehydration condensation conditions, addition conditions, substitution (or displacement) conditions, Diels-Alder reaction conditions, cationic crosslinking conditions, ring-opening conditions, epoxy hardening conditions, and combinations thereof.
• Non-limiting examples of coupling reactions under various reaction conditions between a pair of matching co-reactive functional groups selected from the group preferably consisting of amino group (-NHR' as defined above), hydroxyl group, carboxylic acid group, acid halide groups (—COX, X CI, Br, or I), acid anhydrate group, aldehyde group, azlactone group, isocyanate group, epoxy group, aziridine group, thiol group, and amide groups (— CONH2), are given below for illustrative purposes.
• a carboxylic acid group reacts with an amino group -NHR' in the presence of a coupling agent - carbodiimide (e.g., 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC), ⁇ , ⁇ '-dicyclohexylcarbodiimide (DCC), 1-cylcohexyl-3-(2- morpholinoethyl)carbodiimide, diisopropyl carbodiimide, or mixtures thereof) to form an amide linkage;
• a carboxylic acid group reacts with an isocyanate group under heating to form an amide linkage;
• a carboxyl group reacts with an epoxy or aziridine group to form an ester bond;
• a carboxyl group reacts with a halide group (-CI, -Br or -I) to form an ester bond; an amino group reacts with aldehyde group to form a Schiff base which may further
• coupling agents with two reactive functional groups may be used in the coupling reactions.
• a diisocyanate, di-acid halide, di-carboxylic acid, di-azlactone, or di-epoxy compound can be used in the coupling of two hydroxyl, two amino groups, two carboxyl groups, two epoxy groups, or combination thereof;
• a diamine or dihydroxyl compound can be used in the coupling of two isocyanate, two epoxy, two aziridine, two carboxyl, two acid halide, or two azlactone groups, or combinations thereof.
• Any polymer comprising at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units can be used as precursor polymer in the preparation of a UV-absorbing polymer.
• a precursor polymer is: a homopolymer of a carboxyl-containing vinylic monomer (acrylic acid or C Ci 2 alkylacrylic acid); a copolymer of acrylic acid and C Ci 2 alkylacrylic acid; a copolymer of a carboxyl-containing vinylic monomer (acrylic acid or C 1 -C 12 alkylacrylic acid) and an amino- containing vinylic monomer (e.g., amino-C 2 -C 6 alkyl (meth)acrylate, C C 6 alkylamino-C 2 - C 6 alkyl (meth)acrylate, allylamine, vinylamine, amino-C 2 -C 6 alkyl (meth)acrylamide, C C 6 alkylamino-C 2 -C 6 alkyl (meth)acrylamide); a copolymer of a carboxyl-containing vinylic monomer (acrylic acid or C C, 2 alkylacrylic acid) and one or more hydrophilic vinylic monomers
• polymethacrylic acid poly(C 2 -Ci 2 alkylacrylic acid), poly(acrylic acid-co-methacrylic acid), poly[C 2 -Ci 2 alkylacrylic acid-co-(meth)acrylic acid], poly(N,N-2-acrylamidoglycolic acid), poly[(meth)acrylic acid-co-acrylamide], poly[(meth)acrylic acid-co-vinylpyrrolidone], poly[C 2 - Ci2 alkylacrylic acid-co-acrylamide], poly[C 2 -Ci 2 alkylacrylic acid-co-vinylpyrrolidone], hydrolyzed poly[(meth)acrylic acid-co-vinylacetate], hydrolyzed poly[C 2 -Ci 2 alkylacrylic acid-co-vinylacetate], or combinations thereof.
• UV-absorbing compounds which comprises UV-absorbing moieties and a reactive functional group selected from the group consisting of amino group, azlactone group, epoxy group, isocyanate group, aziridine group, and combination thereof, can be used in the invention.
• a preferred UV-absorbing compound having a benzotriazole-moiety, which can be used in the invention, is represented by formula I, II, or III
• R 1 and R 2 independently of each other are hydrogen, a C1-C12 linear or branched alkyl group, a halogen (CI or Br), a C 6 to C24 aryl group, a C 7 to C24 alkylaryl group, a C 7 to C 2 4 arylalkyl, or a C1-C12 linear or branched alkoxy group;
• L 1 is a covalent bond or a divalent radical of -X a -E 1 -X b -E 2 -Xc- in which X a is a o
• n is from 1 to 10,— c— o— , or— c— N— in which R" is H or Ci-C 8 alkyl, E 1 and E 2 independently of each other are a covalent bond, a divalent radical of -(R a O) n - in which R a and n are defined above, or
• R" is H or C C 8 alkyl, a Ci to C12 linear or branched alkylene divalent radical, a cycloalkyi divalent radical with up to 40 carbon atoms, an alkylcycloalkyi divalent radical with up to 40 carbon atoms, an alkylaryl divalent radical with up to 40 carbon atoms, an arylalkylene divalent radical with up to 40 carbon atoms, or a dicarbonyl group having the formula -C(0)L 2 C(0)- in which L 2 is a Ci to C12 linear or branched alkylene divalent radical or -(R e1 -0) w i-(R e2 -0) w2 -(R e3 -0) w3 - wherein R e1 , R e2 , and R e3 independently of one another are a linear or branched CrC 4 -alkylene and w1 , w2 and w3
• X b and X c independently of each other are a covalent bond, carbonyl,— c— , -0-,
• Y is an azlactone group, an epoxy group, an isocyanate group, an aziridine group, or an amino group of -NHR' in which R' is hydrogen or a C1-C12 unsubstituted or substituted, linear or branched alkyl group.
• amino-containing UV-absorbing compounds of formula I , I I or I I I include without limitation 2-(2'-hydroxy-3'-aminomethyl-5'-methylphenyl)-2H-benzotriazole, 2-(2'-hydroxy-5'-aminophenyl)-2H-benzotriazole, 2-(2'-hydroxy-4'-(3- aminopropoxy)phenyl)-2H-benzotriazole, 2-(2'-hydroxy-4'-ethylaminophenyl)-5-chloro- benzotriazole.
• amino-containing UV-absorbing compounds of formula I , I I , or I I I can be prepared from a benzotriazole-containing vinyl monomer (any one of those described above) by reacting its ethylenically-unsaturated group with an aminomercaptan (e.g., 2-aminoethanethiol) according to Michael Addition or thiol-ene reaction well known to a person skilled in the art.
• an aminomercaptan e.g., 2-aminoethanethiol
• UV-absorbing compounds of formula I, II or III in which Y is an azlactone group, an epoxy group, or an isocyanate group can be prepared from a bezotriazole compound having one hydroxyalkoxy group or an amino group by reacting it with an excess molar equivalent amount of a di-azlactone compound, a di-epoxy compound, or a di-isocyanate compound under customary coupling reaction condition well known to a person skilled in the art.
• di-epoxy compounds are neopentyl glycol diglycidyl ether, 1 ,6- hexanediol diglycidyl ether, ethylene glycol diglycidyl ether, diethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, and dipropylene glycol diglycidyl ether.
• di-epoxy compounds are available commercially (e.g..those DENACOL series di-epoxy compounds from Nagase ChemteX Corporation).
• Examples of Ci 0 -C 2 4 di-azlactone compounds include those described in U.S. Patent No.
• C4-C24 diisocyanates examples include without limitation isophorone diisocyanate, hexamethyl-1 ,6-diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, toluene diisocyanate, 4,4'-diphenyl diisocyanate, 4,4'-diphenylmethane diisocyanate, p-phenylene diisocyanate, 1 ,4-phenylene 4, 4'-diphenyl diisocyanate, 1 ,3-bis- (4,4'-isocyanto methyl) cyclohexane, cyclohexane diisocyanate, and combinations thereof.
• Y preferably is an amino group of -NHR' in which R' is hydrogen or a C1-C12 unsubstituted or substituted, linear or branched alkyl group.
• a preferred UV-absorbing compound having a benzophenone-moiety which can be used in the invention, is represented by formula IV
• R 3 is hydrogen, a C Ci 2 linear or branched alkyl group, a halogen, a C 6 to C 2 4 aryl group, a C 7 to C24 alkylaryl group, a C 7 to C24 arylalkyl, or a C1-C12 linear or branched alkoxy group;
• L 3 is a covalent bond or a divalent radical of -X a -E 1 -X b -E 2 -Xc- in which X a is a o
• n is from 1 to 10,— c— o— , or— c— N— in which R" is H or Ci-C 8 alkyl, E 1 and E 2 independently of each other are a covalent bond, a divalent -N N— seemingly radical of -(R a O) n - in which R a and n are defined above, V— / ,— c— o— , or
• R" is H or C-i-Ce alkyl, a Ci to C 12 linear or branched alkylene divalent radical, a cycloalkyl divalent radical with up to 40 carbon atoms, an alkylcycloalkyl divalent radical with up to 40 carbon atoms, an alkylaryl divalent radical with up to 40 carbon atoms, an arylalkylene divalent radical with up to 40 carbon atoms, or a dicarbonyl group having the formula -C(0)L 2 C(0)- in which L 2 is a Ci to C 12 linear or branched alkylene divalent radical or -(R e1 -0) w i-(R e2 -0) w2 -(R e3 -0) w3 - wherein R e1 , R e2 , and R e3 independently of one another are a linear or branched CrC 4 -alkylene and w1 , w2 and
• X b and X c independently of each other are a covalent bond, carbonyl,— c— , -0-,
• Y 1 is an azlactone group, an epoxy group, an isocyanate group, an aziridine group, or an amino group of -NHR in which R is hydrogen or a C 1 -C 12 unsubstituted or substituted, linear or branched alkyl group.
• Y 1 preferably is an amino group of -NHR in which R is hydrogen or a C 1 -C 20 unsubstituted or substituted, linear or branched alkyl group.
• Amino-containing UV-absorbing compounds of formula IV can be prepared from a benzophenone-containing vinyl monomer by reacting its ethylenically-unsaturated group with an aminomercaptan (e.g., 2-aminoethanethiol) according to Michael Addition or thiol- ene reaction well known to a person skilled in the art.
• an aminomercaptan e.g., 2-aminoethanethiol
• Resultants amino-containing UV- absorbing compounds of formula IV then can be used directly in the invention or in preparing UV-absorbing compounds of formula IV in which Y 1 is an azlactone group, an epoxy group, or an isocyanate group, by reacting an amino-containing UV-absorbing compounds of formula IV with an excess molar equivalent amount of a di-azlactone compound, a di-epoxy compound, or a di-isocyanate compound under customary coupling reaction condition well known to a person skilled in the art.
• the UV-absorbing compound comprises one or more compounds of formula I, II, III or IV, preferably of formula I, II or III, in which Y and Y 1 is an amino group of -NHR' in which R' is hydrogen or a C 1 -C 12 unsubstituted or substituted, linear or branched alkyl group, R 1 and R 2 independent of each other is hydrogen, halogen, Ci-C 6 linear or branched alkoxy, C 1 -C 12 linear or branched alkyl (preferably t-butyl), or C 6 - Ci5 aryl, L is a covalent bond or a divalent radical of -X a -E 1 -X b -E 2 -Xc- in which X a is a
• R" is H or d-C 8 alkyl
• E 1 and E 2 independently of each other are a covalent bond, a divalent radical of -(R a O) n - in which R a is a linear or branched CrCi 2 -alkylene and n is from 1 to 10, a Ci to Ci 2 linear or branched alkylene divalent radical, a cycloalkyl divalent radical with up to 12 carbon atoms, an alkylcycloalkyl divalent radical with up to 20 carbon atoms, an alkylphenyl divalent radical with up to 20 carbon atoms, or an phenylalkylene divalent radical with up to 20 carbon o atoms, X b and X c independently of each other are a covalent bond, carbonyl,— c— , -0-,
• Y is an amino group of -NHR in which R is hydrogen or a C C 6 unsubstituted or substituted, linear or branched alkyl group.
• a solution of a UV-absorbing polymer for forming a UV-absorbing layer (coating) on contact lenses can be prepared by dissolving one or more UV-absorbing polymers in water, a mixture of water and one or more organic solvents miscible with water, an organic solvent, or a mixture of one or more organic solvent.
• Example of preferred organic solvents includes without limitation, tetrahydrofuran, tripropylene glycol methyl ether, dipropylene glycol methyl ether, ethylene glycol n-butyl ether, ketones (e.g., acetone, methyl ethyl ketone, etc.), diethylene glycol n-butyl ether, diethylene glycol methyl ether, ethylene glycol phenyl ether, propylene glycol methyl ether, propylene glycol methyl ether acetate, dipropylene glycol methyl ether acetate, propylene glycol n-propyl ether, dipropylene glycol n-propyl ether, tripropylene glycol n-butyl ether, propylene glycol n-butyl ether, dipropylene glycol n-butyl ether, tripropylene glycol n-butyl ether, propylene glycol n-butyl ether, diprop
• the UV-absorbing polymers are dissolved in a mixture of water and one or more organic solvents, an organic solvent, or a mixture of one or more organic solvent. It is believed that a solvent system containing at least one organic solvent can swell a contact lens so that a portion of the UV-absorbing polymer may penetrate into the contact lens and increase the thickness and durability of the UV-absorbing coating. Any organic solvents described above can be used in preparation of a solution of the UV-absorbing polymer, so long as it can dissolve the UV-absorbing polymer.
• Contacting of a contact lens with a solution of a UV-absorbing polymer can be carried in any manner known to a person skilled in the art.
• a preferred contact method is dipping a contact lens in the solution or spraying the contact with the solution, with the former being preferred. It is understood that, before contacting with a solution of a UV- absorbing polymer, a contact lens can be subjected to extraction with an extraction solvent to remove unpolymerized components from the molded lens, as known by a person skilled in the art. Alternatively, extraction step can be carried out after a coating (layer) of the UV- absorbing polymer is applied onto the contact lens.
• the first organic solvent is present in an amount of at least about 60%, preferably at least about 70%, more preferably at least about 80%, even more preferably at least about 90%, most preferably at least about 95% by weight in the coating solution, and the method of the invention further comprises a step of rinsing the ophthalmic lens having the UV-absorbing coating thereon with a mixture of water and at most about 50%, preferably at most about 40%, more preferably at most about 30%, even more preferably at most about 20%, most preferably at most about 10% by weight of a second organic solvent (which can be identical to or different from the first organic solvent).
• a second organic solvent which can be identical to or different from the first organic solvent.
• a method of the invention comprises a step of covalently attaching a hydrophilic polymer or polymeric material having reactive functional groups onto the UV-absorbing coating to form a hydrogel coating, wherein the hydrogel coating is covalently attached onto the UV-absorbing coating through linkages each formed between one carboxylic group of the UV-absorbing coating and one reactive functional group of the hydrophilic polymer or polymeric material.
• Any hydrophilic polymer and any hydrophilic polymeric material, which comprises reactive functional groups can be used in the invention, so long as the hydrophilic polymer or the hydrophilic polymeric material can be dissolved in any solvent or solvent system, preferably in water.
• a water-soluble and crosslinkable hydrophilic polymeric material used for forming the hydrogel coating is a partially-crosslinked polymeric material that comprises a three-dimensional network and reactive functional groups selected from the group consisting of azetidinium groups, epoxy groups, isocyanate groups, aziridine groups, azlactone groups, amino groups, carboxyl groups, and combinations thereof, with azetidinium groups as most preferred embodiment, within the network.
• a hydrophilic polymer or hydrophilic polymeric material for forming the hydrogel coating comprises UV-absorbing moieties.
• the UV-absorbing moieties can be introduced by coupling a UV-absorbing compound of formula (I), (II), (III) or (IV) above to a hydrophilic polymer or hydrophilic polymeric material (as described above), so long as not all of the reactive functional groups of the hydrophilic polymer or polymeric material is consumed.
• the hydrophobic UV-absorbing moieties can be buried below a hydrogel surface and would not affect the hydrophilicity and wettability of the contact lenses.
• hydrophilic polymers comprising reactive functional groups selected from the group consisting of azetidinium groups, epoxy groups, isocyanate groups, aziridine groups, azlactone groups, amino groups, carboxyl groups, and combinations thereof can be used in the formation of hydrogel coating (hydrogel coatings) according to any coupling reactions known to a person skilled in the art.
• the mole percentage of monomeric units containing a reactive functional group is about 40% or less, preferably about 35% or less, more preferably about 30% or less, even more preferably about 25% or less, most preferably about 20% or less.
• crosslinked coating can have a relatively low crosslinkage density and thereby a low softness (elastic modulus) and lubricity for comfort.
• preferred hydrophilic polymers for forming hydrogel coatings on contact lenses include without limitation copolymers comprising at least about 60% by mole of at least one non-reactive vinylic monomer and at most about 40% by mole of at least one reactive vinylic monomers, wherein the reactive vinylic monomer is selected from the group consisting of a carboxyl- containing vinylic monomer, an amino-containing vinylic monomer, an epoxy-containing vinylic monomer, an aziridine-containing vinylic monomer, an azlactone-containing vinylic monomer, an isocyanate-containing vinylic monomer, combinations thereof, wherein the non-reactive hydrophilic vinylic monomer is selected from the group consisting of acrylamide (AAm), ⁇ , ⁇ -dimethylacrylamide (DMA), N-vinylpyrrolidone (NVP), N-vinyl-N- methyl
• amino-containing vinylic monomers include without limitation amino- Ci-C 6 alkyl (meth)acrylate, C C 6 alkylamino- C C 6 alkyl (meth)acrylate, allylamine, vinylamine, amino-Ci-C 6 alkyl (meth)acrylamide, C C 6 alkylamino-Ci-C 6 alkyl
• (meth)acrylamide di-amino- d-Ce alkyl (meth)acrylamide, di-d-Ce alkylamino-d-Ce alkyl (meth)acrylamide, or combinations thereof.
• Examples of azlactone-containing vinylic monomers include without limitation 2- vinyl-4,4-dimethyl-1 ,3-oxazolin-5-one, 2-isopropenyl-4,4-dimethyl-1 ,3-oxazolin-5-one, 2- vinyl-4-methyl-4-ethyl-1 ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-butyl-1 ,3-oxazolin-5- one, 2-vinyl-4,4-dibutyl-1 ,3-oxazolin-5-one, 2-isopropenyl-4-methyl-4-dodecyl-1 ,3-oxazolin- 5-one, 2-isopropenyl-4,4-diphenyl-1 ,3-oxazolin-5-one, 2-isopropenyl-4,4-pentamethylene- 1 ,3-oxazolin-5-one, 2-isopropenyl-4,4-tetram
• epoxy-containing vinylic monomers includes without limitation glycidyl (meth)acrylate, ally glycidyl ether, methylallyl glycidyl ether, glycidyl (meth)acrylamide, C1- C6 hydroxyalkyi (meth)acrylate dlycidyl ether (e.g., 4-hydroxypropyl (meth)acrylate glycidyl ether, hydroxypropyl (meth)acrylate glycidyl ether, hydroxylethyl (meth)acrylate glycidyl ether), glycidyl (meth)acrylamide, di-glycidyl (meth)acrylamide, glycidyl ethacrylate, glycidyl itaconate, methylglycidyl (meth)acrylate, 3,4-epoxy-1-vinylcyclohexane, and those disclosed in US 5,677,398 (herein incorporated by reference in its
• isocyanate-containing vinylic monomers include without limitation isocyanato-C C 6 alkyl (meth)acrylate.
• aziridine-containing vinylic monomers include without limitation aziridinyl C1-C12 alkyl (meth)acrylate (e.g., 2-(1 -aziridinyl) ethyl (meth)acrylate, 3-(1- aziridinyl) propyl (meth)acrylate, 4-(1 -aziridinyl) butyl (meth)acrylate, 6-(1 -aziridinyl) hexyl (meth)acrylate, or 8-(1 -aziridinyl) octyl (meth)acrylate), and those aziridinyl vinyl monomers disclosed in US 3,974,131 (herein incorporated by reference in its entirety) (e.g., diethylen glycol mono-(meth)acrylate mono-2-aziridinyl propionate).
• aziridinyl C1-C12 alkyl (meth)acrylate e.g., 2-(1 -aziridinyl
• the water-soluble and crosslinkable hydrophilic polymeric material for forming the hydrogel coating (or crosslinked coating) comprises (i) from about 20% to about 95% by weight of first polymer chains derived from an epichlorohydrin-functionalized polyamine or polyamidoamine, (ii) from about 5% to about 80% by weight of hydrophilic moieties or second polymer chains derived from at least one hydrophilicity-enhancing agent having at least one reactive functional group selected from the group consisting of amino group, carboxyl group, thiol group, and combination thereof, wherein the hydrophilic moieties or second polymer chains are covalently attached to the first polymer chains through one or more covalent linkages each formed between one azetitdinium group of the epichlorohydrin-functionalized polyamine or polyamidoamine and one amino, carboxyl or thiol group of the hydrophilicity-enhancing agent, and (iii) azetidinium groups which are parts of the first polymer chains or
• the hydrogel coating (or crosslinked coating) can be formed by simply heating a contact lens having the UV-absorbing coating thereon in an aqueous solution in the presence of the hydrophilic polymeric material to and at a temperature from about 40°C to about 140°C for a period of time sufficient to covalently attach the hydrophilic polymeric material onto the surface of the contact lens through covalent linkages each formed between one azetidinium group of the hydrophilic polymeric material and one of the carboxyl groups of the UV-absorbing coating on the contact lens, thereby forming a crosslinked hydrophilic coating on the contact lens.
• any water-soluble and crosslinkable hydrophilic polymeric material containing reactive functional groups e.g., those described above
• a water-soluble and thermally-crosslinkable hydrophilic polymeric material containing azetidinium groups comprises (i.e., has a composition including) from about 20% to about 95%, preferably from about 35% to about 90%, more preferably from about 50% to about 85%, by weight of first polymer chains derived from an epichlorohydrin- functionalized polyamine or polyamidoamine and from about 5% to about 80%, preferably from about 10% to about 65%, even more preferably from about 15% to about 50%, by weight of hydrophilic moieties or second polymer chains derived from at least one hydrophilicity-enhancing agent having at least one reactive functional group selected from the group consisting of amino group, carboxyl group, thiol group, and combination thereof.
• the composition of the hydrophilic polymeric material is determined by the composition (based on the total weight of the reactants) of a reactants mixture used for preparing the thermally-crosslinkable hydrophilic polymeric material according to the crosslinking reactions shown in Scheme I above. For example, if a reactant mixture comprises about 75% by weight of an epichlorohydrin-functionalized polyamine or polyamidoamine and about 25% by weight of at least one hydrophilicity-enhancing agent based on the total weight of the reactants, then the resultant hydrophilic polymeric material comprise about 75% by weight of first polymer chains derived from the epichlorohydrin-functionalized polyamine or polyamidoamine and about 25% by weight of hydrophilic moieties or second polymer chains derived from said at least one hydrophilicity-enhancing agent.
• the azetidinium groups of the thermally-crosslinkable hydrophilic polymeric material are those azetidinium groups (of the epichlorohydrin-functionalized polyamine or polyamidoamine) which do not participate in crosslinking reactions for preparing the thermally-crosslinkable hydrophilic polymeric material.
• An epichlorohydrin-functionalized polyamine or polyamidoamine can be obtained by reacting epichlorohydrin with a polyamine polymer or a polymer containing primary or secondary amino groups.
• a poly(alkylene imines) or a poly(amidoamine) which is a polycondensate derived from a polyamine and a dicarboxylic acid (e.g., adipic acid-diethylenetriamine copolymers) can react with epichlorohydrin to form an
• epichlorohydrin-functionalized polymer Similarly, a homopolymer or copolymer of aminoalkyl(meth)acrylate, mono-alkylaminoalkyl (meth)acrylate,
• aminoalkyl(meth)acrylamide, or mono-alkylaminoalkyl (meth)acrylamide can also react with epichlorohydrin to form an epichlorohydrin-functionalized polyamine.
• the reaction conditions for epichlorohydrin-functionalization of a polyamine or polyamidoamine polymer are taught in EP1465931 (herein incorporated by reference in its entirety).
• a preferred epichlorohydrin-functionalized polymer is polyaminoamide-epichlorohydrin (PAE) (or polyamide-polyamine-epichlorohydrin or polyamide-epichlorohydrin), such as, for example, Kymene® or Polycup ® resins (epichlorohydrin-functionalized adipic acid-diethylenetriamine copolymers) from Hercules or Polycup ® or Servamine ® resins from Servo/Delden.
• PAE polyaminoamide-epichlorohydrin
• PAE polyamide-polyamine-epichlorohydrin or polyamide-epichlorohydrin
• Kymene® or Polycup ® resins epichlorohydrin-functionalized adipic acid-diethylenetriamine copolymers
• hydrophilicity-enhancing agents can be used in the invention so long as they contain at least one amino group, at least one carboxyl group, and/or at least one thiol group.
• hydrophilicity-enhancing agents include without limitation: amino-, carboxyl- or thiol-containing monosaccharides (e.g., 3-amino-1 ,2-propanediol, 1- thiolglycerol, 5-keto-D-gluconic acid, galactosamine, glucosamine, galacturonic acid, gluconic acid, glucosaminic acid, mannosamine, saccharic acid 1 ,4-lactone, saccharide acid, Ketodeoxynonulosonic acid, N-methyl-D-glucamine, 1-amino-1-deoxy-3-D-galactose, 1-amino-1-deoxysorbitol, 1-methylamino-1-deoxysorbitol, N-aminoethyl gluconamide); amino-, carboxyl- or thiol-containing disaccharides (e.g., chondroitin disaccharide sodium salt, di(3-D-xylopy
• hydrophilicity-enhancing agents is hydrophilic polymers having one or more amino, carboxyl and/or thiol groups. More preferably, the content of monomeric units having an amino (-NHR' with R' as defined above), carboxyl (-COOH) and/or thiol (-SH) group in a hydrophilic polymer as a hydrophilicity-enhancing agent is less than about 40%, preferably less than about 30%, more preferably less than about 20%, even more preferably less than about 10%, by weight based on the total weight of the hydrophilic polymer.
• hydrophilic polymers as hydrophilicity-enhancing agents are amino- or carboxyl-containing polysaccharides, for example, such as,
• carboxymethylcellulose having a carboxyl content of about 40% or less, which is estimated based on the composition of repeating units,— [C6Hio- m 0 5 (CH 2 CC>2H) m ]— in which m is 1 to 3
• carboxyethylcellulose having a carboxyl content of about 36% or less, which is estimated based on the composition of repeating units, in which m is 1 to 3
• carboxypropylcellulose having a carboxyl content of about 32% or less, which is estimated based on the composition of repeating units,— [C 6 H 10 - m 0 5 (C3H 6 CC>2H) m ]— , in which m is 1 to 3
• hyaluronic acid having a carboxyl content of about 1 1 %, which is estimated based on the composition of repeating units, — (C13H20O9NCO2H)— ), chondroitin sulfate (having a carboxymethylcellulose (
• hydrophilic polymers as hydrophilicity-enhancing agents include without limitation: poly(ethylene glycol) (PEG) with mono-amino, carboxyl or thiol group (e.g., PEG-NH 2 , PEG-SH, PEG-COOH); H 2 N-PEG-NH 2 ; HOOC-PEG-COOH; HS- PEG-SH; H2N-PEG-COOH; HOOC-PEG-SH; H 2 N-PEG-SH; multi-arm PEG with one or more amino, carboxyl or thiol groups; PEG dendrimers with one or more amino, carboxyl or thiol groups; a diamino- or dicarboxyl-terminated homo- or co-polymer of a non-reactive hydrophilic vinylic monomer; a monoamino- or monocarboxyl-terminated homo- or copolymer of a non-reactive hydrophilic vinylic monomer; a copolymer which
• polymerization product of a composition comprising (1 ) about 60% by weight or less, preferably from about 0.1 % to about 30%, more preferably from about 0.5% to about 20%, even more preferably from about 1 % to about 15%, by weight of one or more reactive vinylic monomers and (2) at least one non-reactive hydrophilic vinylic monomer and/or at least one phosphorylcholine-containing vinylic monomer; and combinations thereof.
• Reactive vinylic monomer(s) and non-reactive hydrophilic vinylic monomer(s) are those described previously.
• a hydrophilic polymer as a hydrophilicity-enhancing agent is PEG- NH 2 ; PEG-SH; PEG-COOH; H 2 N-PEG-NH 2 ; HOOC-PEG-COOH; HS-PEG-SH; H 2 N-PEG- COOH; HOOC-PEG-SH; H 2 N-PEG-SH; multi-arm PEG with one or more amino, carboxyl or thiol groups; PEG dendrimers with one or more amino, carboxyl or thiol groups; a monoamino-, monocarboxyl-, diamino- or dicarboxyl-terminated homo- or copolymer of a non-reactive hydrophilic vinylic monomer selected from the group consisting of acrylamide (AAm), ⁇ , ⁇ -dimethylacrylamide (DMA), N-vinylpyrrolidone (NVP), N-vinyl-N-methyl acetamide, glycerol (meth)
• (meth)acrylamide CrC 4 -alkoxy polyethylene glycol (meth)acrylate having a weight average molecular weight of up to 400 Daltons, vinyl alcohol, N-methyl-3-methylene-2- pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, N,N- dimethylaminoethyl (meth)acrylate, ⁇ , ⁇ -dimethylaminopropyl (metha)crylamide,
• (meth)acryloyloxyethyl phosphorylcholine and combinations thereof; a copolymer which is a polymerization product of a composition comprising (1 ) from about 0.1 % to about 30%, preferably from about 0.5% to about 20%, more preferably from about 1 % to about 15%, by weight of (meth)acrylic acid, C 2 -Ci 2 alkylacrylic acid, vinylamine, allylamine, and/or amino- C 2 -C 4 alkyl (meth)acrylate, and (2) (meth)acryloyloxyethyl phosphorylcholine and/or at least one non-reactive hydrophilic vinylic monomer selected from the group consisting of acrylamide, ⁇ , ⁇ -dimethylacrylamide, N-vinylpyrrolidone, N-vinyl-N-methyl acetamide, glycerol (meth)acrylate, hydroxyethyl (meth)acrylate, N-hydroxyethyl (meth)acrylamide,
• the hydrophilicity-enhancing agent as a hydrophilicity-enhancing agent is PEG-NH 2 ; PEG-SH; PEG-COOH; monoamino-, monocarboxyl-, diamino- or dicarboxyl-terminated polyvinylpyrrolidone; monoamino-, monocarboxyl-, diamino- or dicarboxyl-terminated polyacrylamide; monoamino-, monocarboxyl-, diamino- or dicarboxyl- terminated poly(DMA); monoamino- or monocarboxyl-, diamino- or dicarboxyl-terminated poly(DMA-co-NVP); monoamino-, monocarboxyl-, diamino- or dicarboxyl-terminated poly(NVP-co-N,N-dimethylaminoethyl (meth)acrylate)); monoamino-, monocarboxyl-, diamino- or dicarboxyl
• (meth)acryloyloxyethyl phosphorylcholine and (2) from about 0.1 % to about 30%, preferably from about 0.5% to about 20%, more preferably from about 1 % to about 15%, by weight of a carboxylic acid containing vinylic monomer and/or an amino-containing vinylic monomer, and combination thereof.
• PEGs with functional groups and multi-arm PEGs with functional groups can be obtained from various commercial suppliers, e.g., Polyscience, and Shearwater Polymers, inc., etc.
• phosphorylcholine-containing vinylic monomer can be prepared according to procedures described in U.S. Patent No. 6,218,508, herein incorporated by reference in its entirety.
• a chain transfer agent with an amino or carboxyl group e.g., 2-aminoethanethiol, 2-mercaptopropinic acid, thioglycolic acid, thiolactic acid, or other hydroxymercaptanes, aminomercaptans, or carboxyl-containing mercaptanes
• optionally other vinylic monomer are copolymerized (thermally or actinically) with a reactive vinylic monomer (having an amino or carboxyl group), in the presence of an free-radical initiator.
• the molar ratio of chain transfer agent to that of all of vinylic monomers other than the reactive vinylic monomer is from about 1 :5 to about 1 : 100, whereas the molar ratio of chain transfer agent to the reactive vinylic monomer is 1 :1.
• the chain transfer agent with amino or carboxyl group is used to control the molecular weight of the resultant hydrophilic polymer and forms a terminal end of the resultant hydrophilic polymer so as to provide the resultant hydrophilic polymer with one terminal amino or carboxyl group, while the reactive vinylic monomer provides the other terminal carboxyl or amino group to the resultant hydrophilic polymer.
• a monoamino- or monocarboxyl-terminated homo- or copolymer of a non-reactive hydrophilic vinylic monomer the non-reactive vinylic monomer, a chain transfer agent with an amino or carboxyl group (e.g., 2-aminoethanethiol, 2- mercaptopropinic acid, thioglycolic acid, thiolactic acid, or other hydroxymercaptanes, aminomercaptans, or carboxyl-containing mercaptanes) and optionally other vinylic monomers are copolymerized (thermally or actinically) in the absence of any reactive vinylic monomer.
• a chain transfer agent with an amino or carboxyl group e.g., 2-aminoethanethiol, 2- mercaptopropinic acid, thioglycolic acid, thiolactic acid, or other hydroxymercaptanes, aminomercaptans, or carboxyl-containing mercaptanes
• Copolymers comprising a non-reactive hydrophilic vinylic monomer and a reactive vinylic monomer (e.g., a carboxyl-containing vinylic monomer) can be prepared according to any well-known radical polymerization methods or obtained from commercial suppliers. Copolymers containing methacryloyloxyethyl phosphorylcholine and carboxyl-containing vinylic monomer can be obtained from NOP Corporation (e.g., LIPIDURE® -A and -AF).
• NOP Corporation e.g., LIPIDURE® -A and -AF
• the weight average molecular weight M w of the hydrophilic polymer having at least one amino, carboxyl or thiol group is preferably from about 500 to about 1 ,000,000, more preferably from about 1 ,000 to about 500,000.
• the reaction between a hydrophilicity-enhancing agent and an epichlorohydrin-functionalized polyamine or polyamidoamine is carried out at a temperature of from about 40°C to about 100°C for a period of time sufficient (from about 0.3 hour to about 24 hours, preferably from about 1 hour to about 12 hours, even more preferably from about 2 hours to about 8 hours) to form a water-soluble and thermally- crosslinkable hydrophilic polymeric material containing azetidinium groups.
• the concentration of a hydrophilicity-enhancing agent relative to an epichlorohydrin-functionalized polyamine or polyamidoamine must be selected not to render a resultant hydrophilic polymeric material water-insoluble (i.e., a solubility of less than 0.005 g per 100 ml of water at room temperature) and not to consume more than about 99%, preferably about 98%, more preferably about 97%, even more preferably about 96% of the azetidinium groups of the epichlorohydrin-functionalized polyamine or polyamidoamine.
• heating is performed preferably by autoclaving a contact lens with the UV-absorbing coating thereon in a packaging solution (i.e., a buffered aqueous solution) including a water-soluble thermally crosslinkable hydrophilic polymeric material in a sealed lens package at a temperature of from about 1 18°C to about 125°C for approximately 20-90 minutes.
• a packaging solution i.e., a buffered aqueous solution
• the packaging solution is a buffered aqueous solution which is ophthalmically safe after autoclave.
• a contact lens which comprises a UV-absorbing coating and a layer of a water-soluble thermally crosslinkabe hydrophilic polymeric material on top of the base coating, immersed in a packaging solution (i.e., a buffered aqueous solution) in a sealed lens package at a temperature of from about 1 18°C to about 125°C for approximately 20-90 minutes.
• a packaging solution i.e., a buffered aqueous solution
• Lens packages are well known to a person skilled in the art for autoclaving and storing a soft contact lens. Any lens packages can be used in the invention.
• a lens package is a blister package which comprises a base and a cover, wherein the cover is detachably sealed to the base, wherein the base includes a cavity for receiving a sterile packaging solution and the contact lens.
• Lenses are packaged in individual packages, sealed, and sterilized (e.g., by autoclave at about 120°C or higher for at least 30 minutes) prior to dispensing to users.
• autoclave at about 120°C or higher for at least 30 minutes
• a person skilled in the art will understand well how to seal and sterilize lens packages.
• a packaging solution contains at least one buffering agent to maintain a pH of the packaging solution in a physiologically acceptable range of about 6 to about 8.5, one or more other tonicity agents to provide a tonicity of from about 200 to about 450 milliosmol (mOsm), preferably from about 250 to about 350 mOsm, and other ingredients known to a person skilled in the art.
• examples of other ingredients include without limitation, surfactants/ lubricants, antibacterial agents, preservatives, and/or water-soluble viscosity builders (e.g., cellulose derivatives, polyvinyl alcohol,
• physiologically compatible buffering agents are boric acid, borates, e.g. sodium borate, citric acid, citrates, e.g. potassium citrate, bicarbonates, e.g. sodium bicarbonate, TRIS (2-amino-2-hydroxymethyl-1 ,3-propanediol), Bis-Tris (Bis-(2- hydroxyethyl)-imino-tris-(hydroxymethyl)-methane), bis-aminopolyols, triethanolamine, ACES (N-(2-hydroxyethyl)-2-aminoethanesulfonic acid), BES (N,N-Bis(2-hydroxyethyl)-2- aminoethanesulfonic acid), HEPES (4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid), MES (2-(N-morpholino)ethanesulfonic acid), MOPS (3-[N-morpholino]-propanesulfonic acid), PIP
• each buffer agent in a packaging solution is preferably from 0.001 % to 2%, preferably from 0.01 % to 1 %; most preferably from about 0.05% to about 0.30% by weight.
• Suitable ocularly acceptable tonicity agents include, but are not limited to sodium chloride, potassium chloride, glycerol, propylene glycol, polyols, mannitols, sorbitol, xylitol and mixtures thereof.
• a packaging solution of the invention has a viscosity of from about 1 centipoise to about 20 centipoises, preferably from about 1.2 centipoises to about 10 centipoises, more preferably from about 1.5 centipoises to about 5 centipoises, at 25°C.
• the packaging solution comprises preferably from about 0.01 % to about 2%, more preferably from about 0.05% to about 1.5%, even more preferably from about 0.1 % to about 1 %, most preferably from about 0.2% to about 0.5%, by weight of a water-soluble and thermally-crosslinkable hydrophilic polymeric material of the invention.
• the packaging solution preferably comprises an a-oxo-multi-acid or salt thereof in an amount sufficient to have a reduced susceptibility to oxidation degradation of the polyethylene glycol segments.
• a commonly- owned co-pending patent application discloses that oxo-multi-acid or salt thereof can reduce the susceptibility to oxidative degradation of a PEG-containing polymeric material.
• Exemplary a-oxo-multi-acids or biocompatible salts thereof include without limitation citric acid, 2-ketoglutaric acid, or malic acid or biocompatible (preferably ophthalmically compatible) salts thereof. More preferably, a a-oxo-multi-acid is citric or malic acid or biocompatible (preferably ophthalmically compatible) salts thereof (e.g., sodium, potassium, or the like).
• the packaging solution can further comprises mucin-like materials, ophthalmically beneficial materials, and/or surfactants.
• mucin-like materials described above, exemplary ophthalmically beneficial materials described above, exemplary surfactants described above can be used in this embodiment.
• a method of the invention further comprises a step of dipping the contact lens in a solution of blue light-absorbing polymer having blue light- absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units.
• blue light-absorbing monomeric units refers to repeating units of a polymer each of which comprises a blue light-absorbing moiety.
• a "blue light-absorbing moiety” refers to an organic group which can render a compound containing such group to absorb light in the region of from about 400 nm to about 480 nm.
• One preferred blue light-absorbing moiety is
• a blue light absorbing polymer can be prepared according to procedures similar to those described above for UV-absorbing polymers.
• a blue light-absorbing polymer can be prepared by polymerizing a polymerizable mixture comprising at least one carboxyl-containing vinylic monomer (any one of those described above) and at least one blue light-absorbing vinylic monomer, or alternatively by reacting a blue light-absorbing compound having a reactive functional group (e.g., amino group, azlactone group, epoxy group, isocyanate group, aziridine group, and combination thereof, with amino groups as most preferred reactive functional groups) with a precursor polymer (any one of those described above for preparing UV-absorbing polymers) containing carboxyl and optional amino groups.
• a reactive functional group e.g., amino group, azlactone group, epoxy group, isocyanate group, aziridine group, and combination thereof
• a contact lens preferably a silicone hydrogel contact lens obtained according to a method of the invention has a surface wettability characterized by having an averaged water contact angle of about 90 degrees or less, preferably about 80 degrees or less, more preferably about 70 degrees or less, even more preferably about 60 degrees or less, most preferably about 50 degrees or less.
• the invention provides an ophthalmic lenses, the lens comprising a polymeric lens body; a layer of UV-absorbing polymer on the lens body; and a hydrogel coating covalently attached onto the layer of the UV-absorbing polymer, wherein the UV- absorbing polymer comprises UV-absorbing monomeric units and at least about 50%, preferably at least about 60%, more preferably at least about 70%, even more preferably at least about 80%, most preferably at least about 90%, by mole of carboxyl-containing monomeric units, wherein the hydrogel coating is obtained by covalently attaching a hydrophilic polymer or polymeric material having reactive functional groups onto the layer of the UV-absorbing polymer through linkages each formed between one carboxylic group of the UV-absorbing coating and one reactive functional group of the hydrophilic polymer or polymeric material.
• Norbloc i.e., 2-[3-(2H-Benzotriazol-2-yl)-4-hydroxyphenyl] ethyl methacrylate
• Aldrich Cat# 413437-100G
• Cysteamine hydrochloride is received from Fluka (Cat # 30078).
• 0.1 N iodine aqueous solution is received from Acros (Cat #
• reaction mixture is cooled to room temperature and transferred to 4 liter separatory funnel. 400 mL of THF is added to the funnel. Reaction mixture is extracted with 1 L of brine for 2 times. Aqueous phase is discarded and organic phase is dried over magnesium sulfate. Solution is filtered and solvent is removed on a rotary evaporator. Resulting product is a clear, viscous, fluorescent-yellow liquid. Yield of the reaction is about 54.0 grams (90%). Characterization
• Amino-functionalized Norbloc (the product) is characterized by 1 H-NMR;
• a repeat synthesis is conducted to display reproducibility of the synthesis along with a slight scale-up.
• the repeat product is confirmed as identical to the previously synthesized product.
• a 4-L beaker 24.13 g of Na 2 C0 3 , 80 g of NaCI and 1.52 kg of deionized water are mixed to dissolve.
• a separate 4-L beaker 700 g of bis-3-aminopropyl- polydimethylsiloxane (Shin-Etsu, MW ca. 1 1500) are dissolved in 1000 g of hexane.
• a 4-L reactor is equipped with overhead stirring with turbine agitator and a 250-mL addition funnel with micro-flow controller. The two solutions are then charged to the reactor, and mixed for 15 minutes with heavy agitation to produce an emulsion.
• a 4-L beaker 61.73 g of Na 2 C0 3 , 80 g of NaCI and 1.52 kg of deionized water are mixed to dissolve.
• a separate 4-L beaker 700 g of bis-3-aminopropyl- polydimethylsiloaxane (Shin-Etsu, MW ca. 4500) are dissolved in 1000 g of hexane.
• a 4-L reactor is equipped with overhead stirring with turbine agitator and a 250-mL addition funnel with micro-flow controller. The two solutions are then charged to the reactor, and mixed for 15 minutes with heavy agitation to produce an emulsion.
• a 2-L jacketed reactor is equipped with a heating/chilling loop, reflux condenser, N 2 - inlet/vacuum adapter, feeding tube adapter and overhead mechanical stirring.
• a solution is generated by dissolving 90.00 g of PDMS crosslinker I prepared above and 30.00 g of PDMS crosslinker II prepared above in 480 g of 1-propanol. This solution is charged to the reactor and cooled to 8°C. The solution is degassed by evacuating to less than 15 mBar, holding at vacuum for 15 minutes, and then re-pressurizing with dry nitrogen. This degas procedure is repeated for a total of 3 times. The reactor is held under a blanket of dry nitrogen.
• a monomer solution is prepared by mixing 1.50 g of cysteamine hydrochloride, 0.3 g of AIBN (2-2-Azoiso bisbutyronitrile), 55.275 g of DMA (N,N- dimethylacrylamide), 18.43 g of HEA (hydroxyethyl acrylate) and 364.5 g of 1-propanol.
• This solution is filtered with a Waterman 540 filter paper, and then added to the reactor through a degas unit and HPLC pump with a flow rate of 3.0 ml_ /minute. The reaction temperature is then elevated to 68°C with a heating ramp about one hour.
• a feeding solution is prepared by mixing 4.5 g of cysteamine hydrochloride and 395.5 g of 1-propanol and then filtering with Waterman 540 filter paper. When the reactor temperature reaches 68°C, this solution is slowly dosed into the reactor through the degasser/HPLC pump over 3 hours. The reaction is then continued at 68°C for an additional 3 hours, on which heating has discontinued and the reactor is allowed to cool to room temperature.
• reaction mixture is transferred to a flask and stripped solvent at 40°C under vacuum on a rotary evaporator until 1000 g of sample remained.
• the solution is then slowly mixed with 2000 g of deionized water with rapid agitation. Additional solvent is further removed until about 2000 g of sample remain. During this stripping process, the solution gradually becomes an emulsion.
• the resulting material is purified by ultrafiltration over a 10 kD molecular weight cut-off membrane until the permeate conductance is below 2.5 ⁇ / ⁇
• This emulsion is then charged to a 2-L reactor equipped with overhead stirring, refrigeration loop, thermometer, and the pH meter and dispensing tip of a Metrohm Model 718 STAT Titrino.
• the reaction mixture is then cooled to 1 °C. 7.99 g of NaHC0 3 are charged to the emulsion and stirred to dissolve.
• the Titrino is set to maintain pH at 9.5 by intermittent addition of 15% sodium hydroxide solution. 1 1.59 ml_ of acryloyl chloride are then added over one hour using a syringe pump.
• the emulsion is stirred for another hour, then the Titrino is set to neutralize the reaction mixture by addition of a 15% solution of HCI.
• the product is purified by ultrafiltration again with 10 kD molecular weight cut-off membrane until the permeate conductance is below 2.5 ⁇ / ⁇ .
• the final macromonomer is isolated by lypophilization.
• This example illustrates a method of the invention by using a fluorescein-modified polya 0.
• PAA-F50 has a molecular weight of about 50 kD and comprises about 0.6% by mole of monomeric units having one fluorescin moiety. It is prepared as follows.
• w [g/L] is the concentration of PAA-F50 in the solution
• M A (72 g/mol) and M F (419 g/mol) are the molar masses of the repeating monomeric units, acrylic acid and fluorescein-modified acrylic acid (i.e., 6-acryloylamido-fluorescein), in the copolymer PAA- F50, respectively.
• PAA-F50 dissolved in 1-propanol, pH adjusted with HCOOH to about 2.0; 0.36 g/l PAA-F50, labelling degree: 0.59 Mol-%)
• PAA-F50 continuously diffuses into the lens.
• This diffusion of PAA-F50 into the lens is reflected by a colorization of the lenses, whereas the intensity of the lens colour increases with increasing treatment time (see Figure 1 ).
• the diffusion and increasing colorization can also be monitored by UV- VIS spectroscopy.
• PAA-F50 coating on the lens is demonstrated by first dipping a contact lens in the PAA-F50 solution (prepared above) for about one hour and then transferring and storing the PAA-F50 coated lens in an aqueous phosphate buffered saline (PBS) solution.
• PBS aqueous phosphate buffered saline
• This example illustrates how to prepare a contact lens with a UV-absorbing coating thereon according to a preferred embodiment of the invention.
• a UV-absorbing polymer of formula (2) (in which m:n ⁇ 80:20), designated as PAA- N20, has a molecular weight of about 36 kD and comprises about 8.1 % by mole of UV- absorbing monomeric units (Norbloc, [3-(2-H-Benzotriazol-2-yl)-4-hydroxyphenyl]ethyl methacrylate). It is prepared according to the procedures described below.
• X Norbioc [ Mol-%] 100 x [3 x A aroma tic (7x Ai - 4 x A aroma t ic )] in which A 1 is the integral of the area of the protons between 1.02 - 3,15 ppm and A aroma t ic is the integral of the area of the aromatic signals between 6.5 - 8.15 ppm.
• a contact lens prepared in Example 2 is dipped in a solution of PAA-N20 (0.36 g/L PAA-N20 dissolved in 1-propanol, pH adjusted with HCOOH to about 2.0) for about 30 minutes and then rinsed with and stored in an aqueous phosphate buffered saline (PBS) solution.
• PBS aqueous phosphate buffered saline
• a blue light-absorbing polymer of formula (3) designated as PAA-L20, has a molecular weight of about XX kD and comprises about 12.3% by mole of blue-light- absorbing monomeric units ((S)-2-methacryloyloxymethyl-1-(4-nitrophenyl)pyrrolidine). It is prepared according to the procedures described below.
• X Blue [Mol-%] 100 x [3 x A 2 / (2 x A 1 - 6 x A 2 )] in which A 1 is the integral of the area of the protons between 1 .0 - 2.8 ppm and A 2 is the integral of the area of the aromatic signals between 7.7 - 8.4 ppm.
• IPDI isophorone diisocyanate
• dibutyltindilaurate DBTDL
• the reaction is kept for 4.5 h at 40° C, forming IPDI-PDMS- IPDI.
• the reactor is held for 4.5 h at 40° C, forming HO-PDMS-IPDI-PDMS-IPDI-PDMS- OH.
• MEK is then removed under reduced pressure.
• the terminal hydroxyl- groups are capped with methacryloyloxyethyl groups in a third step by addition of 7.77 g of isocyanatoethylmethacrylate (IEM) and an additional 0.063 g of DBTDL, forming IEM- PDMS-IPDI-PDMS-IPDI-PDMS-IEM.
• IEM isocyanatoethylmethacrylate
• CE-PDMS can be prepared as follows. 240.43 g of KF-6001 is added into a 1 -L reactor equipped with stirring, thermometer, cryostat, dropping funnel, and nitrogen/vacuum inlet adapter, and then dried by application of high vacuum (2x10 "2 mBar). Then, under an atmosphere of dry nitrogen, 320 g of distilled MEK is then added into the reactor and the mixture is stirred thoroughly. 0.235 g of DBTDL are added to the reactor. After the reactor is warmed to 45°C, 45.86 g of IPDI are added through an addition funnel over 10 minutes to the reactor under moderate stirring. The reaction is kept for 2 hours at 60°C.
• a lens formulation is prepared by dissolving components in 1 -propanol to have the following composition: about 32% by weight of CE-PDMS macromer prepared above, about 21 % by weight of TRIS-Am, about 23% by weight of DMA, about 0.6% by weight of L-PEG (N-(carbonyl-methoxypolyethylene glycol-2000)-1 ,2-disteaoyl-sn-glycero-3- phosphoethanolamin, sodium salt), about 1 % by weight of Darocur 1 173, about 0.1 % by weight of visitint (5% copper phthalocyanine blue pigment dispersion in TRIS), about 0.8% by weight of DMPC (1 ,2-dimyristoyl-sn-glycero-3-phosphocholine), about 200 ppm H- tempo (4-hydroxy-2,2,6,6-tetramethyl-1 -piperidinyloxy), and about 22% by weight of 1 - propanol.
• L-PEG N-(carbonyl-me
• Lenses are prepared by cast-molding from the lens formulation prepared above in a reusable mold (quartz female mold half and glass male mold half), similar to the mold shown in Figs. 1 -6 in U.S. patent Nos.7,384,590 and 7,387,759 (Figs. 1 -6).
• the lens formulation in the molds is irradiated with UV irradiation (13.0 mW/cm 2 ) for about 24 seconds. Molded lenses are extracted with MEK.
• a contact lens prepared above is dipped in a bath containing a PAA-N20 solution (3,6 g/L of PAA-N20 dissolved in 1 -propanol, adjusted to pH ⁇ 2.0 with HCOOH) for about 20 minutes, rinsed with 1 -propanol and subsequently dipped in a bath with a PAA-L20 solution (3,6 g/L PAA-L20, adjusted to pH ⁇ 2.0 with HCOOH).
• Figure 4 shows that the obtained contact lens absorbs the UV light not only in the range between 280 - 380 nm, but also in the range between 380 - 480 nm, i.e. beside the criteria for a lens with UV absorber class 1 properties. It also fulfills the properties of a blue-light absorbing lens.

Landscapes

• Engineering & Computer Science (AREA)
• Ophthalmology & Optometry (AREA)
• Health & Medical Sciences (AREA)
• Manufacturing & Machinery (AREA)
• Mechanical Engineering (AREA)
• Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• General Physics & Mathematics (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Materials For Medical Uses (AREA)
• Eyeglasses (AREA)
• Optical Filters (AREA)
• Coating Of Shaped Articles Made Of Macromolecular Substances (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=47116399

Family Applications (1)

Country Status (9)

Cited By (32)

Families Citing this family (13)

Citations (23)

Family Cites Families (495)

• 2012
  • 2012-10-10 SG SG11201400228WA patent/SG11201400228WA/en unknown
  • 2012-10-10 CN CN201280050162.5A patent/CN103917899B/zh active Active
  • 2012-10-10 MY MYPI2014000495A patent/MY164605A/en unknown
  • 2012-10-10 EP EP12780968.9A patent/EP2766750B1/en active Active
  • 2012-10-10 JP JP2014535808A patent/JP6017572B2/ja active Active
  • 2012-10-10 US US13/648,522 patent/US9005700B2/en active Active
  • 2012-10-10 CA CA2851668A patent/CA2851668C/en active Active
  • 2012-10-10 HU HUE12780968A patent/HUE029018T2/en unknown
  • 2012-10-10 WO PCT/US2012/059479 patent/WO2013055746A1/en not_active Ceased