WO2011020109A2 - Abrasive articles including abrasive particles bonded to an elongated body, and methods of forming thereof - Google Patents
Abrasive articles including abrasive particles bonded to an elongated body, and methods of forming thereof Download PDFInfo
- Publication number
- WO2011020109A2 WO2011020109A2 PCT/US2010/045647 US2010045647W WO2011020109A2 WO 2011020109 A2 WO2011020109 A2 WO 2011020109A2 US 2010045647 W US2010045647 W US 2010045647W WO 2011020109 A2 WO2011020109 A2 WO 2011020109A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- abrasive article
- abrasive
- bonding layer
- average
- coating layer
- Prior art date
Abstract
Description
Claims