WO2009113422A1 - 積層フィルム - Google Patents
積層フィルム Download PDFInfo
- Publication number
- WO2009113422A1 WO2009113422A1 PCT/JP2009/053908 JP2009053908W WO2009113422A1 WO 2009113422 A1 WO2009113422 A1 WO 2009113422A1 JP 2009053908 W JP2009053908 W JP 2009053908W WO 2009113422 A1 WO2009113422 A1 WO 2009113422A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- resin
- layer
- cross
- width direction
- Prior art date
Abstract
Description
2: 樹脂B
3: 樹脂流入部
4: マニホールド部
5: 第1スリット部
6: ノズル部
7: 第2マニホールド部
8: 合流部
9: 第2スリット部
10: ダイ
11: ノズル
12: 合流部
13: ダイ
14: 貫通孔
21: ダイ
22: 導入口
23: 導入口
24: 流路
25: マニホールド
26: 多孔板
27: 孔
28: 流路
29: マニホールド
30: 合流部
31: リップ
本発明の積層フィルムにおいては、フィルム幅方向-厚み方向断面において、図2に例示したごとく、B層が樹脂(例えば、樹脂A)で覆われていることも好ましい。B層が樹脂で覆われているとは、フィルム端部でB層を露出させる処理を行った場合の該露出部分を除いてB層側面が露出していない状態をいう。樹脂で覆われたB層は、B層の全数に対して過半数あることが好ましい。このような構造であると、異なる樹脂界面での層間剥離が生じにくくなるために、製造、使用時での曲げや引張、衝撃によっても光拡散性・集光性といった光学特性を保持でき、耐久性にすぐれたフィルムとなる。より好ましくは全てのB層が樹脂で覆われていることであり、製造、使用時での曲げや引張、衝撃による光学特性の変化をほぼ抑制することができるようになる。
(物性値の評価法)
(1)B層の断面幅、平均断面幅、層数、形状
まず、研磨機により観察するフィルム幅方向-厚み方向断面の平滑化処理を行った。カッターナイフを用いてフィルム断面を切り出し、このフィルムの両表面を厚さ2mmのアクリル板ではさみ、治具に固定した。次に、研磨機(NAP-240 日新化成社製)を用い、研磨板に#6000番手の研磨フィルム(砥粒 酸化アルミニウム)を貼り付け、研磨液に純水を用い、研磨板の回転数240rpmで10分間研磨することにより平滑な断面とした。この処理をフィルム全幅について、順次行った。次に、非接触三次元測定機(NEXIV VMR-H3030TZ Nikon社製)を用いて、B層の断面幅、層数、形状を計測した。
(2)透過率むら
日本電色工業株式会社製 濁度計 NDH5000を用いて、JIS K7736-1(1996)に基づいて、全光線透過率を測定した。なお、フィルム全幅について等間隔で10点の全光線透過率をそれぞれ計測し、その10点の全光線透過率の最大値と最小値の差を、透過率むらとした。
25℃、65%RHの環境下で、JIS C6823(1999)カットバック法(IEC60793-C1A)に準じて行った。サンプルは、試験長10cm、9cm、8cm、7cmと準備し、各サンプルの挿入損失を測定した。光源には、波長850nmのLED(アンリツ製0901A)を用い、モードスクランブラを介してサンプルに光入力を行った。光ファイバーは、入力側φ50μmのマルチモードファイバ型GI(NA0.21)、検出側コア径0.2mmのSIタイプ(NA0.22)を用いた。なお、光の入出力には、調芯器を用いて光軸合わせを行った。また、検出器には、光パワーセンサ(アンリツ社製MA9421A)を用いた。伝搬損失は、長さに対する挿入損失をプロットし、最小二乗法により決定した。すなわち、得られた一次式の傾きを損失とした。また、最小二乗の際、寄与率R2が0.99以上のときのみ伝播損失として採用した。0.99以下の場合は、再調芯、再サンプル調整などの再測定を繰り返すことによって、0.99以上の値を得た。なお、フィルム全幅について等間隔で10点の損失をそれぞれ計測し、その平均値を平均損失とした。また、10点の損失の最大値と最小値の差を、損失むらとした。
高分子計器株式会社製 アスカーA型ゴム硬度計にて、JIS K7215(1986)に準拠し、巻長さ500mのフィルムロール表層について、幅方向に10点巻き硬度を測定した。その最大値と最小値の差を巻き硬度むらとした。
以下の樹脂A、樹脂Bを用意した。
住友化学製 ポリプロピレン ノーブレンWF836DG
樹脂B:ポリカーボネート(PC)
出光興産製 ポリカーボネート LC1700
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて280℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、図3~5に示すような幅700mmのダイに樹脂Aと樹脂Bを流入させた。ダイには長方形型のノズルが600個あり、樹脂Bがノズル内を流れた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、80℃の温度に保持されたドラムにてニップキャストした。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られた積層フィルム厚みは1000μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.05mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅800μm±8μmの樹脂Bが600個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、低損失で光を伝送することが可能であり、光導波路やライトガイド、照明装置として好適であった。一方、フィルム表面に対し垂直に入射した光は弱いもののフィルム表面に対し斜め方向に出射する性能を有していたものの、このフィルムは、集光フィルムや異方拡散フィルムとしても使用可能なものであった。
幅が1900mmであり、ノズルの個数が1800個のダイを用い、吐出量を調整した以外は、実施例1とほぼ同様の条件にて製膜した。得られたフィルム厚みは1000μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.09mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅800μm±9μmの樹脂Bが1800個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、低損失で光を伝送することが可能であり、光導波路やライトガイド、照明装置として好適であった。
以下の樹脂A、樹脂Bを用意した。
出光興産製 ポリカーボネート LC1700
樹脂B:ポリカーボネート(PC)+カーボンブラック(CB) 2wt%
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて290℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、図3~5に示すような幅700mmのダイに樹脂Aと樹脂Bを流入させた。ダイには、実施例1に比べ厚み方向の長さが長い長方形型のノズルが3000個あり、樹脂Bがノズル内を流れた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、80℃の温度に保持されたドラムにてニップキャストした。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られたフィルム厚みは500μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には200μm±10μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状はほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅100μm±2μmで樹脂Bが3000個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、フィルム表面に対し垂直な方向の光はほぼ透過するが、フィルム表面に対し幅方向に15°以上傾いた角度では光はほとんど透過しなくなった。このフィルムは、視野角制御フィルムとして好適なものであった。
以下の樹脂A、樹脂Bを用意した。
invista製 P100
樹脂B:共重合ポリエステル(PCT/I)
イーストマン製 Z6006
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて290℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、図3~5に示すような幅700mmのダイに樹脂Aと樹脂Bを流入させた。ダイには、第2スリット表面に対し45°傾いた長方形型のノズルが3000個あり、樹脂Bがノズル内を流れた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、40℃の温度に保持されたドラムに、ワイヤー状の電極に高電圧を印加して密着させた。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られたフィルム厚みは500μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には200μm±15μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状はほぼ平行四辺形であり、高さ(厚み方向の長さ)が約450μm、断面幅100μm±2μmの樹脂Bが3000個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、フィルム表面に対し垂直に入射した光を、フィルム表面に対し斜め方向に出射する性能を有していた。このフィルムは、集光フィルムや異方拡散フィルムとして好適なものであった。
以下の樹脂A、樹脂Bを用意した。
出光興産製 ポリカーボネート LC1700
樹脂B:ポリカーボネート(PC)+ポリメチルペンテン(PMP) 25wt%
三井化学製 DX820
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて280℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、図3~5に示すような幅700mmのダイに樹脂Aと樹脂Bを流入させた。ダイには、実施例1に比べ厚み方向の長さが長い長方形型のノズルが3000個あり、樹脂Bがノズル内を流れた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、80℃の温度に保持されたドラムにてニップキャストした。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られたフィルム厚みは500μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には200μm±10μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状はほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅100μm±2μmの樹脂Bが3000個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、フィルム表面に対し垂直な方向に入射した光を、長手方向にのみ光を強く拡散した。このフィルムは、異方拡散フィルムとして好適なものであった。
以下の樹脂A、樹脂Bを用意した。
住友化学製 MGSS
樹脂B:ポリスチレン(PS)
日本ポリスチレン製 G120K
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて230℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、図3~5に示すような幅700mmのダイに樹脂Aと樹脂Bを流入させた。ダイには長方形型のノズルが600個あり、樹脂Bがノズル内を流れた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、80℃の温度に保持されたドラムにてニップキャストした。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られた積層フィルム厚みは1000μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.10間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅800μm±8μmの樹脂Bが600個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、低損失で光を伝送することが可能であり、光導波路やライトガイド、照明装置として好適であった。
スリッターで、ナーリング加工と保護フィルムを貼りあわせせずに、フィルムロールを得た以外は、実施例1とほぼ同様に積層フィルムを得た。得られた積層フィルム厚みは1000μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.2mmの間隔で配置されており、幅方向中心の隣り合うB層の間隔の0.90倍以上1.10倍以下であるB層は最大でも0.05mmしか存在しなかった。また、その樹脂Bを樹脂Aで被覆した構造となっており、樹脂Bの断面形状は、ほぼ円形状であり、断面幅800μm±8μmの樹脂Bが600個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、平面性が若干悪いものであったが、低損失で光を伝送することが可能であり、光導波路やライトガイド、照明装置として好適であった。
(実施例8)
ダイ幅やノズル個数などのダイ形状と、吐出量を変更した以外は、実施例1とほぼ同様の条件にて製膜した。得られた積層フィルムの厚みは1650μm(保護フィルムを除く)であり、フィルム幅は600mmであった。樹脂Bは長手方向には連続であり、幅方向には1.8mm±0.1mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅1600μm±9μmの樹脂Bが500個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、低損失で光を伝送することが可能であり、光導波路やライトガイド、照明装置として好適であった。
(実施例9)
樹脂の吐出量の比率を変えた以外は実施例3とほぼ同様の条件にて製膜した。
ダイを図6~8に示すような流路Cを有するものにした以外は実施例1とほぼ同様の条件で製膜した。ここで、流路Cには樹脂Aが供給され、貫通孔14から供給される樹脂Aと流路Cから供給される樹脂Aの総流量は、実施例1と変わらないように供給する流量を調整した。得られた積層フィルム厚みは1000μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.03mm間隔で均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅800μm±3μmの樹脂Bが600個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、実施例1に示すフィルムと比較してより真円状に近い形状を有し、低損失で光を伝送することが可能であり、特に実施例1に示すフィルムよりも光導波路やライトガイド、照明装置として用いるときの接続が容易で好適なものであった。
実施例1に比べ厚み方向の長さが長い長方形型のノズルを用いた以外は実施例8と同様の条件で製膜した。得られた積層フィルムの厚みは500μm(保護フィルムを除く)であり、フィルム幅は600mmであった。樹脂Bは長手方向には連続であり、幅方向には1.8mm±0.1mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅1600μm±9μmの樹脂Bが500個存在していた。表1に、得られた積層フィルムの構造と性能を示す。さらに得られたフィルムに、ピッチ100μm、深さ100μmの溝が幅方向に彫られたエンボスロールを用いてエンボス処理を行い、表面に凹凸処理を行った。得られたフィルムは、一部樹脂Aの被覆のない場所ができており、フィルム端面から光を入射したときにエンボス加工により作製した凹凸面から光を発光し、面状照明として好適なものであった。
ダイの幅が1000mmであるダイを用いた以外は、実施例14と同様の条件で製膜、エンボス加工を行った。得られた積層フィルムの厚みは500μm(保護フィルムを除く)であり、フィルム幅は900mmであった。樹脂Bは長手方向には連続であり、幅方向には2.8mm±0.1mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅2700μm±14μmの樹脂Bが500個存在しており、平均断面幅±10μmを満たすB層は70%程度であった。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、一部樹脂Aの被覆のない場所ができており、フィルム端面から光を入射したときにエンボス加工により作製した凹凸面から光を発光し、面状照明として好適なものであったが、実施例14と比較すると輝度は若干弱いものであった。
周期的にB層の断面幅と隣り合うB層の間隔が25mm周期で変動するように設けられたノズルを含むダイを用いる以外は、実施例5と同様の条件で製膜した。得られたフィルム厚みは500μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には150~250μmの間で間隔が25mm周期で変動しており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状はほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅が75~125μmの間で25mm周期をもって変動している樹脂Bが3000個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、フィルム表面に対し垂直な方向に入射した光を、長手方向にのみ光を強く拡散するものであり、特に25mm間隔でランプが配置された表示装置に実装したところ、ランプの輝度ムラを効果的に抑制できるものであった。
樹脂として以下の樹脂を用い、樹脂の吐出量の比率を変更した以外は、実施例9と同様の条件にて製膜した。
出光興産製 ポリカーボネート LC1700
樹脂B:ポリカーボネート(PC)+ポリメチルペンテン(PMP) 25wt%
三井化学製 DX820
得られたフィルム厚みは500μm(保護フィルムを除く)であり、フィルム幅は600mmであった。樹脂Bは長手方向には連続であり、幅方向には200μm±18μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状はほぼ長方形であり、高さ(厚み方向の長さ)が約450μm、断面幅20μm±1μmの樹脂Bが3000個存在していた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、フィルム表面に対し垂直な方向に入射した光を、長手方向にのみ光を強く拡散したが、若干の光学ムラが確認された。このフィルムは、異方拡散フィルムとして好適なものであった。
実施例1と樹脂の吐出量の割合とキャスティングドラムの速度を変更した以外は、実施例1と同様の条件で製膜した。得られた積層フィルム厚みは200μm(保護フィルムを除く)であった。樹脂Bは長手方向には連続であり、幅方向には1mm±0.05mm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ円形状であり、断面幅100μm±12μmの樹脂Bが600個存在していた。しかし、若干場所により断面積のばらつきが顕著であった。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、低損失で光を伝送することが可能であり、特に通信用途に好適であった。
以下の樹脂A、樹脂Bを用意した。
+ポリメチルペンテン(PMP) 1wt%
樹脂B:ポリエチレンテレフタレート(PET)
+ポリメチルペンテン(PMP) 40wt%
上記PET樹脂は、以下に記す方法にて重合されたものである。まず、ジメチルテレフタレート100重量部とエチレングリコール60重量部の混合物に、エステル交換反応触媒として酢酸カルシウムを添加し、加熱昇温してメタノールを留出させてエステル交換反応を行った。次いで、該エステル交換反応生成物に、重合触媒として三酸化アンチモン、熱安定剤としてリン酸を加え重縮合反応槽に移行した。次いで、加熱昇温しながら反応系を徐々に減圧し、290℃減圧下で内部を攪拌しメタノールを留出させながら重合し、PET樹脂を得た。
樹脂として以下の樹脂を用いた以外は、実施例16と同様の条件にて製膜した。
+ポリメチルペンテン(PMP) 1wt
樹脂B:ポリエチレンテレフタレート(PET)
+酸化チタン粒子(Ti) 4wt%
得られた積層フィルム厚みは1500μmであった。樹脂Bは長手方向には連続であり、幅方向には25000μm±1000μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aで被覆した構造となっていた。また、樹脂Bの断面形状は、ほぼ半円形状であり、断面幅10000μm±500μm、厚み500μm±20μmの樹脂Bが13個存在していた。樹脂A中に分散しているPMPの粒子径は10μm、樹脂B中に分散しているTi粒子の粒子径は0.25μmであった。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、樹脂Bからなる層(B層)において光を強く拡散できるものであり、ランプ間隔25mmのバックライトに対してB層がランプ上部となるように配置することによりランプの輝度ムラをより効果的に抑制できるものであった。
以下の樹脂A、樹脂Bを用意した。
+ポリメチルペンテン(PMP) 1wt%
樹脂B:共重合ポリエステル(PCT/I)
+ポリメチルペンテン(PMP) 40wt%
また、ダイとして、半円状の孔が1200含むダイを用いた。これらの樹脂、ダイを用いた以外は、実施例16と同様の条件にて製膜した。得られたフィルムの厚みは250μmであった。樹脂Bは長手方向に連続であり、幅方向には300μm±10μm間隔でほぼ均等に配置されており、その樹脂Bを樹脂Aが被覆した構造となっていた。また、樹脂Bの断面形状は擬半円形状であり、断面幅200μm±7μm、厚み120μm±2μmの樹脂Bが1200個存在していた。樹脂A中ならびに樹脂B中に分散しているPMPの粒子径は10μmであった。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、強い異方拡散性があり、バックライトのランプの輝度ムラを抑制できるものであった。
以下の樹脂A、樹脂Bを用意した。
住友化学製 ポリプロピレン ノーブレンWF836DG
樹脂B:ポリカーボネート(PC)
出光興産製 ポリカーボネート LC1700
次に、押出機1に樹脂Aを、押出機2に樹脂Bを供給し、それぞれの押出機にて2800℃の溶融状態とし、ギヤポンプおよびフィルタを介した後、公知のスクエアーミキサーにて樹脂Aと樹脂Bが交互に幅方向に計1200層積層し、幅700mmのダイからシート状にして吐出させた。ダイから吐出されたシートは、エッジガイドにて端部を拘束されながら、80℃の温度に保持されたドラムにてニップキャストした。その後、ワインダーにてオシレーションせずに、両側端部45mmを切り落とし、巻きとった。次に、スリッターで、ナーリング加工しながら、保護フィルム(パナック製 耐熱保護フィルム HP25)を片面に貼り合わせながら巻き取り、フィルムロールを得た。得られた積層フィルム厚みは1000μm(保護フィルムを除く)であった。しかしながら、樹脂Bは長手方向には連続であるものの、幅方向には一定の間隔でならんでおらず、また層の形状も非常に乱れてほぼ全ての層は隣接する層と結合した形状となっていた。このため、断面幅が0.1μm以上10000μm以下であるB層の数は、300個以下となっていた。表1に、得られた積層フィルムの構造と性能を示す。得られたフィルムは、光をほとんど伝送できなかった。
Claims (24)
- 樹脂Aからなる層(A層)と樹脂Bからなる層(B層)を交互に幅方向に積層した構造を少なくとも有するフィルムであって、フィルムの幅が400mm以上であり、かつ断面幅が0.1μm以上10000μm以下であるB層の数が10以上であることを特徴とする積層フィルム。
- 隣り合うB層間の間隔Pがフィルム幅方向中央において隣り合うB層間の間隔Pcに対して0.90倍以上1.10倍以下となるB層が幅方向に連続して300mm以上存在することを特徴とする請求項1に記載の積層フィルム。
- 隣り合うB層間の間隔が周期性をもって変化することを特徴とする請求項1に記載の積層フィルム。
- 断面積Aがフィルム幅方向中央に位置するB層の断面積Acに対して0.90倍以上1.10倍以下であるB層が幅方向に連続して300mm以上存在することを特徴とする請求項1~3のいずれかに記載の積層フィルム。
- フィルム厚み方向-幅方向断面において、B層の形状が厚み方向の中心軸に対して非対称であることを特徴とする請求項1~4のいずれかに記載の積層フィルム。
- 厚み方向の中心軸で2分されるB層の断面積S1、S2(S1<S2)について、S1がS2の0.8倍以下であることを特徴とする請求項1に記載の積層フィルム。
- 樹脂Bが熱可塑性樹脂であり、過半数のB層が樹脂で被覆されていることを特徴とする請求項1~6のいずれかに記載の積層フィルム。
- 樹脂Aまたは樹脂Bどちらか一方が溶解可能な溶媒に対し、もう一方の樹脂は不溶性であることを特徴とする請求項1~7のいずれかに記載の積層フィルム。
- フィルムの末端の一部が、分岐していることを特徴とする請求項1~8のいずれかに記載の積層フィルム。
- 過半量のB層の断面幅が、平均断面幅±10μmであることを特徴とする請求項1~9のいずれかに記載の積層フィルム。
- 請求項1~10のいずれかに記載の積層フィルムからなることを特徴とするフィルムロール。
- ロール幅方向の巻き硬度むらが0.0001以上6以下であることを特徴とする請求項11に記載のフィルムロール。
- 請求項1~12のいずれかに記載のフィルムを用いた光モジュール。
- 請求項1~12のいずれかに記載のフィルムを用いた照明装置。
- 請求項1~12のいずれかに記載のフィルムを用いた通信装置。
- 請求項1~12のいずれかに記載のフィルムを用いた表示装置。
- 請求項1~12のいずれかに記載のフィルムを用いたライトガイド。
- 請求項1~12のいずれかに記載のフィルムを用いた拡散フィルム。
- 請求項1~12のいずれかに記載のフィルムを用いた集光フィルム。
- 請求項1~12のいずれかに記載のフィルムを用いた視野角制御フィルム。
- 請求項1~12のいずれかに記載のフィルムを用いた光導波路フィルム。
- 少なくとも2種類以上の樹脂を幅方向に積層させるためのダイであって、幅方向に配列してなるノズルを少なくとも10以上有し、かつ前記ノズルの各々の周囲を取り囲むように配置してなる貫通孔14を10以上有し、かつ配列した前記ノズルおよび前記貫通孔14と連通する合流部を有してなり、前記ノズルおよび前記貫通孔14とは異なる経路で合流部に連通する流路を少なくとも一つ有してなることを特徴とするダイ。
- 前記貫通孔14および/またはノズルが、厚み方向の中心軸に対して非対称であることを特徴とする請求項22に記載のダイ。
- 少なくとも2種類以上の樹脂を幅方向に積層させるためのダイであって、幅方向に配列してなる孔を10以上有し、かつ配列した孔と連通した合流部を有し、かつ前記孔とは異なる経路で合流部と連通する流路を少なくとも一つ有してなり、かつ、前記細孔が、細孔の厚み方向の中心軸に対して非対称であることを特徴とするダイ。