WO2003007416A1 - Electrolyte non aqueux et cellule secondaire faisant appel a cet electrolyte - Google Patents
Electrolyte non aqueux et cellule secondaire faisant appel a cet electrolyte Download PDFInfo
- Publication number
- WO2003007416A1 WO2003007416A1 PCT/JP2002/006906 JP0206906W WO03007416A1 WO 2003007416 A1 WO2003007416 A1 WO 2003007416A1 JP 0206906 W JP0206906 W JP 0206906W WO 03007416 A1 WO03007416 A1 WO 03007416A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- electrolyte
- compound
- carbonate
- lithium
- Prior art date
Description
Claims