US20180051397A1 - Method for producing carbon fibers - Google Patents

Method for producing carbon fibers Download PDF

Info

Publication number
US20180051397A1
US20180051397A1 US15/557,506 US201615557506A US2018051397A1 US 20180051397 A1 US20180051397 A1 US 20180051397A1 US 201615557506 A US201615557506 A US 201615557506A US 2018051397 A1 US2018051397 A1 US 2018051397A1
Authority
US
United States
Prior art keywords
temperature
spinning
heat treatment
coal
ash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/557,506
Other languages
English (en)
Inventor
Maki Hamaguchi
Shohei Wada
Toshinori Inoue
Seongho Yoon
Jin Miyawaki
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kyushu University NUC
Kobe Steel Ltd
Original Assignee
Kyushu University NUC
Kobe Steel Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyushu University NUC, Kobe Steel Ltd filed Critical Kyushu University NUC
Assigned to KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.), KYUSHU UNIVERSITY, NATIONAL UNIVERSITY CORPORATION reassignment KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MIYAWAKI, JIN, HAMAGUCHI, MAKI, INOUE, TOSHINORI, WADA, SHOHEI, YOON, SEONGHO
Publication of US20180051397A1 publication Critical patent/US20180051397A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
    • D01F9/145—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from pitch or distillation residues
    • D01F9/15—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from pitch or distillation residues from coal pitch
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
    • C10G1/00—Production of liquid hydrocarbon mixtures from oil-shale, oil-sand, or non-melting solid carbonaceous or similar materials, e.g. wood, coal
    • C10G1/04—Production of liquid hydrocarbon mixtures from oil-shale, oil-sand, or non-melting solid carbonaceous or similar materials, e.g. wood, coal by extraction
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D10/00—Physical treatment of artificial filaments or the like during manufacture, i.e. during a continuous production process before the filaments have been collected
    • D01D10/02—Heat treatment
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/08—Melt spinning methods

Definitions

  • the present invention relates to a method for producing carbon fibers.
  • Carbon fibers are in extensive use as a reinforcing material for structural materials such as, for example, resins, concrete and ceramic. Carbon fibers are used also as, for example, a heat insulator, raw material for activated carbon, electrically conductive material, and heat transfer material.
  • Carbon fibers are produced by forming a synthetic resin, e.g., polyacrylonitrile, or a pitch obtained from petroleum or coal into fibers by spinning and then subjecting the fibers to infusibilization (air oxidation) and carbonization.
  • Coal derived pitch is a viscous black substance and is a residue that remains after volatile components including naphthalene are taken out by distillation from coal tar, which is a liquid substance yielded as a by-product when producing a coke by dry distillation of coal.
  • Such coal derived pitch is a mixture of a large number of compounds including a large proportion of aromatic compounds each having many benzenes in the skeleton.
  • coal derived pitch Upon heating about from 100° C. to 200° C., coal derived pitch melts to become a viscous liquid. By extruding this from a nozzle, the coal derived pitch can hence be spun.
  • coal derived pitch is a by-product of coke production and is recovered as a residue as stated above, it contains various components, e.g., metallic impurities and solid carbon matter, which inhibit the spinning and subsequent infusibilization and carbonization. It is therefore difficult to stably and efficiently produce carbon fibers.
  • these impurities can be causative of defects of the carbon fibers to be produced.
  • the pitch to be used for producing carbon fibers should have a high carbon content and contain neither metallic impurities nor solid carbon matter.
  • the pitch to be used for producing carbon fibers should evenly melt at a certain temperature when subjected to spinning.
  • the softening point of the pitch is preferably 150° C. or higher in order that the infusibilization treatment for fixing the shape of fibers obtained by spinning the pitch can be performed at an elevated temperature to heighten the efficiency, and is preferably 300° C. or lower in order that the spinning can be conducted at temperatures which do not result in a pyrolysis reaction during the spinning.
  • coal derived pitch modification treatments result in an increase in the cost of carbon fiber production.
  • an object of the present invention is to provide a method capable of producing carbon fibers at low cost.
  • the invention which has been achieved in order to solve the problem described above, is a method for producing a carbon fiber, including a step of separating an ash-free coal obtained from a bituminous coal or a sub-bituminous coal, into a soluble component(s) and an insoluble component(s) by a solvent extraction treatment, a step of heat-treating the soluble component(s), a step of melt-spinning the soluble component(s) subjected to the heat treatment, a step of infusibilizing a filament body obtained by the melt spinning, and a step of carbonizing the filament body subjected to the infusibilization.
  • an ash-free coal having a low content of impurities, e.g., ash matter, which inhibit spinning is subjected to a solvent extraction treatment to thereby extract therefrom soluble components including organic substances having relatively low molecular weights as main components, and from the soluble components are further removed volatile components and low-temperature pyrolizable components, which inhibit spinning, by a heat treatment, thereby obtaining a pitch.
  • This pitch is low in the content of impurities and components having relatively high molecular weights and has a softening temperature which is suitable for melt spinning and capable of performing infusibilization at a relatively high temperature. Because of this, carbon fibers can be efficiently produced by this method for carbon fiber production. Furthermore, since the pitch can be obtained by merely performing a solvent extraction treatment and a heat treatment, carbon fibers of high quality can be produced at relatively low cost.
  • a solvent extraction temperature should be lower than 300° C.
  • the pitch obtained does not contain components having relatively high molecular weights and has a softening temperature at which the melt-spinning can be performed relatively easily. The efficiency of spinning is thus heightened, and the cost of carbon fiber production can be further reduced thereby.
  • a heat treatment temperature should be 150° C. or higher.
  • volatile components which inhibit spinning can be more reliably removed from the pitch, and the efficiency of melt spinning can hence be improved.
  • components which soften at low temperatures are removed from the pitch to narrow the range of softening temperature, thereby enabling the infusibilization treatment at a higher temperature. The efficiency of melt spinning and infusibilization can be thus heightened, thereby further reducing the cost of carbon fiber production.
  • the heat treatment temperature in the heat treatment step should be higher than the solvent extraction temperature in the separation step.
  • the heat treatment temperature in the heat treatment step should be higher than a spinning temperature in the melt spinning step.
  • bituminous coal and “sub-bituminous coal” herein mean coals each having the coal properties as provided for in JIS-M1002 (1978).
  • ash-free coal means a modified coal which was obtained by modifying a coal and has an ash matter content of 5% or less, preferably 3% or less, more preferably 1% or less.
  • ash matter means a value determined in accordance with JIS-M8812 (2004).
  • FIG. 1 is a flowchart which illustrates the procedure of a method for carbon fiber production as an embodiment of the present invention.
  • the method for carbon fiber production includes a step of subjecting bituminous coal or sub-bituminous coal to pyrolysis and a solvent extraction treatment to thereby form an ash-free coal (ash-free coal formation step: step S 1 ), a step of separating the ash-free coal obtained from bituminous coal or sub-bituminous coal into soluble components and insoluble components by a low-temperature solvent extraction treatment (separation step: step S 2 ), a step of heat-treating the soluble components obtained (heat treatment step: step S 3 ), a step of melt-spinning the soluble components subjected to the heat treatment (melt spinning step: step S 4 ), a step of infusibilizing a filament body obtained by the melt spinning (infusibilization step: step S 5 ), and a step of carbonizing the shaped mixture (carbonization step: step S 6 ).
  • ash-free coal formation step: step S 1 a step of separating the ash-free coal obtained from bitumin
  • bituminous coal and sub-bituminous coal are superior in yield and pitch property compared to other kinds of coals. For example, brown coal and lignite have a high oxygen content and a low carbon content, and there are 1.5 cases where these properties are problematic as a raw material for carbon fibers.
  • Ones having a high degree of coalification, such as anthracite, are unfavorable because the yield of ash-free coal is low.
  • the solvent is not particularly limited so long as it has a property of dissolving bituminous coal or sub-bituminous coal.
  • use can be made of monocyclic aromatic compounds such as benzene, toluene and xylene and bicyclic aromatic compounds such as naphthalene, methylnaphthalene, dimethylnaphthalene, and trimethylnaphthalene.
  • the bicyclic aromatic compounds include naphthalenes having an aliphatic chain and biphenyls having a long aliphatic chain.
  • Preferred of those solvents are bicyclic aromatic compounds which are coal derivatives obtained by purifying products of dry coal distillation.
  • the bicyclic aromatic compounds which are coal derivatives are stable even in a heated state and have an excellent affinity for coals. Because of this, by using such bicyclic aromatic compounds as the solvent, not only the proportion of coal components to be extracted with the solvent can be heightened but also the solvent can be easily recovered by a method such as distillation and circulated and used.
  • a lower limit of the slurry heating temperature is preferably 300° C., more preferably 350° C., even more preferably 380° C.
  • an upper limit of the slurry heating temperature is preferably 470° C., more preferably 450° C.
  • the bonds between the molecules constituting the coal cannot be sufficiently weakened and, hence, in the case of using, for example, a low-rank coal as the raw material coal, there is a possibility that the ash-free coal obtained by the extraction cannot have a heightened re-solidification temperature or there is a possibility that the yield might be low, making it uneconomical.
  • the extraction rate from the bituminous coal or sub-bituminous coal (yield of ash-free coal) in the ash-free coal formation step is, for example, 40% by mass or more and 60% by mass or less, although it depends on the quality of the bituminous coal or sub-bituminous coal used as a raw material coal.
  • the separation step as step S 2 the ash-free coal obtained in the ash-free coal formation step as step S 1 is subjected to a low-temperature solvent extraction treatment, thereby separating into relatively low-molecular-weight soluble components, which are solvent-extractable at low temperatures, and relatively high-molecular-weight insoluble components, which are not solvent-extractable.
  • relatively low-molecular-weight soluble components which are solvent-extractable at low temperatures
  • relatively high-molecular-weight insoluble components which are not solvent-extractable.
  • the ash-free coal which has been pulverized is dispersed in a solvent to prepare a slurry.
  • This slurry is held for a certain time period at a given temperature range, followed by separating a solid matter, i.e., insoluble components of the slurry, and liquid matter, i.e., the solvent in which soluble components have dissolved.
  • a lower limit of the average particle diameter of the ash-free coal to be dispersed in the solvent is preferably 50 ⁇ m, more preferably 100 ⁇ m.
  • an upper limit of the average particle diameter of the ash-free coal to be dispersed in the solvent is preferably 3 mm, more preferably 1 mm.
  • the average particle diameter of the ash-free coal to be dispersed in the solvent is less than the lower limit, there is a possibility that it might be difficult to separate the liquid containing extracted soluble components and the solid matter that is insoluble components.
  • the average particle diameter of the ash-free coal to be dispersed in the solvent exceeds the upper limit, there is a possibility that the efficiency of extraction of soluble components might decrease.
  • the term “average particle diameter” means the volume-based 50% cumulative particle diameter in a particle size distribution measured by the laser diffraction scattering method.
  • a lower limit of the mixing proportion of the ash-free coal to the solvent in the slurry is preferably 3% by mass, more preferably 5% by mass.
  • an upper limit of the mixing proportion of the ash-free coal to the solvent is preferably 40% by mass, more preferably 30% by mass.
  • the mixing proportion of the ash-free coal to the solvent is less than the lower limit, there is a possibility that the production efficiency might be low, making it uneconomical.
  • the mixing proportion of the ash-free coal to the solvent exceeds the upper limit, there is a possibility that it might be difficult to handle the slurry or separate the insoluble components.
  • Methods for separating the solvent in which soluble components are dissolved and the insoluble components are not particularly limited. Use can be made of any of known separation methods including a filtration method, centrifugal method and gravitational settling method, or a combination of two methods of these. Preferred of these is a combination of a centrifugal separation method and a filtration method, in which a continuous processing of fluids is possible, which is low in cost and suitable for large-quantity treatments, and which is capable of reliably removing the insoluble components.
  • the solvent is then removed from the liquid (supernatant) obtained by separating the insoluble components, thereby separating and recovering the soluble components of the ash-free coal. Meanwhile, the solvent is removed from the high-solid-content liquid, thereby separating and recovering the insoluble components of the ash-free coal.
  • Methods for removing the solvent from the supernatant and from the high-solid-content liquid are not particularly limited, and use can be made of a general distillation method, a vaporization method or the like. Especially for removing the solvent from the insoluble components, use of distillation is preferred for recovering and reutilizing the solvent.
  • the solvent to be used in the separation step may be any one as long as it can dissolve low-molecular-weight components of the ash-free coal. Use can be made of the one similar to the solvent used in the ash-free coal formation step.
  • the solvent for use in the separation step preferred is a solvent with which a sufficiently high extraction rate is obtained at low temperatures, preferably ordinary temperature. Examples of such preferred solvent include pyridine, methylnaphthalene and tetrahydrofuran.
  • the solvent extraction treatment temperature in the separation step varies in optimal temperature depending on the kind of the solvent.
  • the solvent extraction treatment temperature is preferably lower than 300° C., more preferably 200° C. or lower, even more preferably 150° C. or lower.
  • there is no particular lower limit on the solvent extraction treatment temperature but it is preferably ordinary temperature, e.g., 20° C.
  • the solvent extraction treatment temperature exceeds the upper limit, there is a possibility that the molecular weights of the soluble components to be extracted might increase, resulting in too high a softening temperature and a decrease in spinning efficiency in step S 4 .
  • the solvent extraction treatment temperature is below the lower limit, there is a possibility that cooling might be necessary, resulting in an unnecessary increase in cost.
  • a lower limit of the extraction period in the separation step is preferably 10 minutes, more preferably 15 minutes.
  • an upper limit of the extraction period is preferably 120 minutes, more preferably 90 minutes.
  • the extraction period is shorter than the lower limit, there is a possibility that low-molecular-weight components of the ash-free coal cannot be sufficiently dissolved away.
  • the extraction period exceeds the upper limit, there is a possibility that the production cost might increase unnecessarily.
  • a lower limit of the extraction rate of soluble components from the ash-free coal in the separation step is preferably 10% by mass, more preferably 20% by mass, even more preferably 30% by mass.
  • an upper limit of the extraction rate of soluble components from the ash-free coal is preferably 90% by mass, more preferably 70% by mass, even more preferably 50% by mass.
  • the extraction rate of soluble components from the ash-free coal in the separation step is less than the lower limit, there is a possibility that the yield might be low, resulting in an increase in production cost.
  • the extraction rate of soluble components from the ash-free coal in the separation step exceeds the upper limit, there is a possibility that the soluble components might have a higher softening temperature, resulting in a decrease in spinning efficiency.
  • the soluble components obtained in the separation step as step S 2 are heated to volatilize low-molecular-weight components and to decompose and remove, in advance, components which are pyrolizable at low temperatures, thereby obtaining a pitch to be used in the melt spinning step as step S 4 .
  • the beat treatment should be conducted by heating in a non-oxidizing gas atmosphere.
  • a non-oxidizing gas atmosphere By thus conducting the heating in a non-oxidizing gas atmosphere to prevent oxidative crosslinking, troubles such as an increase in softening temperature can be avoided.
  • the non-oxidizing gas is not particularly limited so long as the pitch can be inhibited from oxidizing therein. However, nitrogen gas is more preferred from the standpoint of profitability.
  • the heat treatment should be conducted under reduced pressure. By thus conducting the heat treatment under reduced pressure, the vapor of volatile components and the gas of pyrolysis products can be efficiently removed from the pitch.
  • a lower limit of the heat treatment temperature in the heat treatment step is preferably 150° C., more preferably 170° C.
  • an upper limit of the heat treatment temperature is preferably 320° C., more preferably 280° C.
  • the beat treatment temperature is below the lower limit, there is a possibility that volatile components in the insoluble components cannot be sufficiently removed, resulting in a pitch which has insufficient stringiness to reduce the spinning efficiency.
  • the heat treatment temperature exceeds the upper limit, there are possibilities that the energy cost might increase unnecessarily, that useful components might be pyrolyzed to reduce the production efficiency, and that carbonization might proceed further to reduce the spinnability.
  • the heat treatment temperature in the heat treatment step should be higher than the solvent extraction treatment temperature in the separation step as step S 2 .
  • the heat treatment temperature in the heat treatment step should be higher than the solvent extraction treatment temperature in the separation step as step S 2 .
  • the heat treatment temperature in the heat treatment step should be higher than the melt spinning temperature in the melt spinning step as step S 4 , which will be described later.
  • the heat treatment temperature in the heat treatment step should be higher than the melt spinning temperature in the melt spinning step as step S 4 , which will be described later.
  • a lower limit of the heat treatment period (period for holding at the heat treatment temperature) in the heat treatment step is preferably 10 minutes, more preferably 15 minutes.
  • an upper limit of the heat treatment period in the heat treatment step is preferably 120 minutes, more preferably 90 minutes.
  • the heat treatment period in the heat treatment step is shorter than the lower limit, there is a possibility that low-molecular-weight components cannot be sufficiently removed.
  • the heat treatment period in the heat treatment step exceeds the upper limit, there is a possibility that the treatment cost might increase unnecessarily.
  • a lower limit of the softening temperature of the pitch obtained by heat-treating the soluble components is preferably 150° C., more preferably 170° C.
  • an upper limit of the softening temperature of the pitch is preferably 280° C., more preferably 250° C.
  • the softening temperature of the pitch is below the lower limit, there is a possibility that the infusibilization treatment temperature in the infusibilization step as step S 5 cannot be heightened, making the infusibilization treatment inefficient.
  • the softening temperature of the pitch exceeds the upper limit, it is necessary to heighten the spinning temperature in the melt spinning step as step S 4 and there are possibilities that the spinning becomes unstable and that the cost increases.
  • the “softening temperature” is a value measured by a ring-and-ball method according to ASTM-D36.
  • a lower limit of the yield of the pitch from the soluble components obtained in the separation step is preferably 80% by mass, more preferably 85% by mass.
  • an upper limit of the yield of the pitch from the soluble components in the heat treatment step is preferably 98% by mass, more preferably 96% by mass.
  • the pitch obtained in the heat treatment step as step S 3 is melt-spun by using a known spinning device. Namely, the pitch in a molten state is passed through a nozzle (die) and thereby formed into filament shape, and the shape of the pitch is fixed to the filament shape by cooling.
  • nozzle used for this melt spinning a known one may be used. For example, one having a diameter of 0.1 mm or more and 0.5 mm or less and a length of 0.2 mm or more and 1 mm or less can be used.
  • the filament body formed by melt-spinning the pitch is wound, for example, by a drum having a diameter of about 100 mm or more and 300 mm or less.
  • a lower limit of the melt spinning temperature is preferably 180° C., more preferably 200° C.
  • an upper limit of the melt spinning temperature is preferably 350° C., more preferably 300° C.
  • the melt spinning temperature is below the lower limit, there is a possibility that the melting of the pitch might be insufficient, making stable spinning impossible.
  • the melt spinning temperature exceeds the upper limit, there is a possibility that a component of the pitch might be pyrolyzed to break the filament body formed by the spinning.
  • the linear velocity in the melt spinning there is no particular lower limit on the linear velocity in the melt spinning. However, it is preferably 100 m/min, more preferably 150 m/min. Meanwhile, an upper limit of the linear velocity in the melt spinning is preferably 500 m/min, more preferably 400 m/min. In the case where the linear velocity in the melt spinning is below the lower limit, there is a possibility that the production efficiency might be low, resulting in an increase in the price of carbon fibers. Conversely, in the case where the linear velocity in the melt spinning exceeds the upper limit, there is a possibility that the spinning might be unstable to rather reduce the production efficiency, resulting also in an increase in the price of carbon fibers.
  • a lower limit of the average diameter of the pitch fibers obtained by spinning in the melt spinning is preferably 7 ⁇ m, more preferably 10 ⁇ m.
  • an upper limit of the average diameter of the pitch fibers obtained by spinning in the melt spinning is preferably 20 ⁇ m, more preferably 15 ⁇ m.
  • the average diameter of the pitch fibers is less than the lower limit, there is a possibility that stable spinning might be impossible.
  • the average diameter of the pitch fibers exceeds the upper limit, there is a possibility that the pitch fibers might have insufficient flexibility.
  • the filament body obtained in the melt spinning step as step S 4 is heated in an oxygen-containing atmosphere to thereby perform crosslinking and infusibilization.
  • Air is generally used as the oxygen-containing atmosphere.
  • a lower limit of the infusibilization treatment temperature is preferably 150° C., more preferably 200° C.
  • an upper limit of the infusibilization treatment temperature is preferably 300° C., more preferably 280° C.
  • the infusibilization treatment temperature is below the lower limit, there is a possibility that the infusibilization might be insufficient or that a prolonged infusibilization treatment period might be necessary, making the treatment inefficient.
  • the infusibilization treatment temperature exceeds the upper limit, there is a possibility that the filament body might melt without undergoing crosslinking by oxygen.
  • a lower limit of the infusibilization treatment period is preferably 10 minutes, more preferably 20 minutes.
  • an upper limit of the infusibilization treatment period is preferably 120 minutes, more preferably 90 minutes. In the case where the infusibilization treatment period is shorter than the lower limit, there is a possibility that the infusibilization might be insufficient. Conversely, in the case where the infusibilization treatment period exceeds the upper limit, there is a possibility that the cost of carbon fiber production might increase unnecessarily.
  • the filament body infusibilized in the infusibilization step as step S 5 is heated and carbonized, thereby obtaining carbon fibers.
  • the filament body is introduced into any desired heating device, e.g., an electric furnace, and the inside thereof is replaced with a non-oxidizing gas, followed by heating while supplying a non-oxidizing gas into this heating device.
  • any desired heating device e.g., an electric furnace
  • the inside thereof is replaced with a non-oxidizing gas, followed by heating while supplying a non-oxidizing gas into this heating device.
  • a lower limit of the heat treatment temperature in the carbonization step is preferably 800° C., more preferably 1,000° C.
  • an upper limit of the heat treatment temperature is preferably 3,000° C., more preferably 2,800° C.
  • the heat treatment temperature is below the lower limit, there is a possibility that the carbonization might be insufficient.
  • the heat treatment temperature exceeds the upper limit, there is a possibility that the production cost might increase from the standpoints of improving the heat resistance of the equipment, and the fuel consumption.
  • a heating period in the carbonization step may also be suitably set in accordance with the properties required of the carbon material, without particular limitations.
  • the heating period is preferably 15 minutes or more and 10 hours or less. In the case where the heating period is shorter than the lower limit, there is a possibility that the carbonization might be insufficient. Conversely, in the case where the heating period exceeds the upper limit, there is a possibility that the efficiency of carbon material production might decrease.
  • the non-oxidizing gas is not particularly limited so long as it is capable of inhibiting the carbon material from oxidizing.
  • nitrogen gas is preferred from the standpoint of profitability.
  • carbon fibers obtained through the melt spinning, infusibilization and carbonization of a pitch, the carbon fibers using a pitch obtained by heat-treating soluble components obtained by a solvent extraction treatment of an ash-free coal obtained from bituminous coal or sub-bituminous coal, are produced.
  • an ash-free coal having a low content of impurities, e.g., ash matter, which inhibit spinning is subjected to a solvent extraction treatment to thereby extract therefrom soluble components including organic substances having relatively low molecular weights as main components, and from the soluble components are further removed volatile components and low-temperature pyrolizable components, which inhibit spinning, by a heat treatment.
  • a pitch which is low in the content of impurities that inhibit spinning and which has a softening temperature which is suitable for melt spinning and capable of performing infusibilization at a relatively high temperature is obtained. Because of this, this method for producing carbon fibers is high in the efficiency of carbon fiber production and is capable of producing carbon fibers of high quality at relatively low cost.
  • the method of the present invention for producing carbon fibers does not require, for itself, producing an ash-free coal from bituminous coal or sub-bituminous coal. Namely, in the method of the present invention for carbon material production, an ash-free coal produced by a third party may be used as a starting material.
  • This method for producing carbon fibers may include, after the carbonization step, a step of further graphitizing the carbon fibers by heating in a non-oxidizing atmosphere to a temperature higher than in the carbonization step.
  • Carbon fibers of Examples 1 to 4 were produced experimentally through the ash-free coal formation step, separation step, heat treatment step, melt spinning step, infusibilization step, and carbonization step which are explained below.
  • Carbon fibers of Comparative Example 1 were produced experimentally by omitting the heat treatment step from Example 1.
  • carbon fibers of Comparative Example 2 were produced experimentally by melt-spinning the ash-free coal.
  • Example 2 Example 3
  • Example 4 Example 1
  • Solvent extraction 115 320 100 65 115 — temperature (° C.) Yield (% by mass) 42 93 38 36 42 — Heat treatment temperature 250 250 250 — — (° C.) Yield (% by mass) 92 96 97 98 — — Softening temperature (° C.) 205 259 194 188 195 245 Spinnability A
  • A A
  • Average fiber diameter ( ⁇ m) 12.4 13.1 11.0 11.7 — —
  • the ash-free coal to be used as a raw material in Examples 1 to 4 and the Comparative Examples was produced by using bituminous coal for general use as a fuel for boilers.
  • the yield of the ash-free coal based on the raw material coal was 48% by mass.
  • the ash-free coal was pulverized to an average particle diameter of 0.5 mm or less. Soluble components were extracted from 100 g of this ash-free coal by using 1 L of a solvent.
  • a solvent In Example 1 and Comparative Example 1, pyridine was used as the solvent, and the solvent extraction temperature and the extraction period were set at 115° C. and 60 minutes, respectively.
  • methylnaphthalene was used as the solvent, and the solvent extraction temperature and the extraction period were set at 320° C. and 60 minutes, respectively.
  • Example 3 methylnaphthalene was used as the solvent, and the solvent extraction temperature and the extraction period were set at 100° C. and 60 minutes, respectively.
  • Example 4 tetrahydrofuran was used as the solvent, and the solvent extraction temperature and the extraction period were set at 65° C. and 60 minutes, respectively.
  • the specific separation method was as follows. The ash-free coal was dispersed in the solvent, followed by holding at the solvent extraction temperature for the extraction period, thereby obtaining a slurry. The insoluble components were separated from this slurry by vacuum filtration, and the solvent was further removed by vacuum distillation to thereby take out soluble components.
  • the extraction rate i.e., yield (% by mass), of the soluble components, from the ash-free coal, which were obtained by the separation step was measured.
  • the yields of the soluble components were found to be 42% by mass in Example 1 and Comparative Example 1, 93% by mass in Example 2, 38% by mass in Example 3, and 36% by mass in Example 4.
  • the soluble components obtained in the separation step were heat-treated in a nitrogen atmosphere to thereby obtain pitches of each of the Examples.
  • the heat treatment conditions included a heat treatment temperature of 250° C. and a heat treatment period (holding period) of 1 hour.
  • the yield of each pitch in this heat treatment step i.e., the ratio of the mass of each pitch after the heat treatment to the mass of the soluble components before the heat treatment, was measured.
  • the yields through the heat treatment were found to be 92% by mass in Example 1, 96% by mass in Example 2, 97% by mass in Example 3, and 98% by mass in Example 4.
  • the pitches of Examples 1 to 4, which had been obtained through the heat treatment, the pitch of Comparative Example 1 (the soluble components which had undergone no heat treatment), and the ash-free coal of Comparative Example 2 were examined for softening temperature.
  • the softening temperature of each pitch was measured by the ring-and-ball method according to ASTM-D36, and the softening temperature of the ash-free coal was measured by a Gieseler method according to JIS-M8801 (2004).
  • the softening temperatures of the pitches were found to be 205° C. in Example 1, 259° C. in Example 2, 194° C. in Example 3, 188° C. in Example 4, and 195° C. in Comparative Example 1, and the softening temperature of the ash-free coal of Comparative Example 2 was found to be 245° C.
  • the pitches of Examples 1 to 4 and Comparative Example 1 and the ash-free coal of Comparative Example 2 were melt-spun and formed into filament shape.
  • the melt spinning conditions included: use of a nozzle having a diameter of 0.2 mm and a length of 0.4 mm; a spinning temperature of 250° C.; and a spinning speed of 188 m/min.
  • the spinning stability in the melt spinning step was evaluated.
  • the cases where spinning could be performed continuously are indicated by “A”
  • the case where breakage of the filament rarely occurred is indicated by “B”
  • the cases where breakage of the filament frequently occurred are indicated by “C”.
  • Example 1 and Examples 3 and 4 showed exceedingly satisfactory spinnability.
  • Example 2 was slightly poor in stringiness and rarely suffered breakage of the filament (clogging in nozzle).
  • Comparative Example 1 the formed filament frequently suffered breakage due to the generation of a gas.
  • Comparative Example 2 showed considerably poor stringiness and frequently suffered breakage of the filament (clogging in nozzle).
  • the filament bodies formed in the melt spinning step were heat-treated in air and infusibilized thereby.
  • the infusibilization treatment conditions included a treatment temperature of 250° C. and a treatment period of 1 hour.
  • the filaments which had been infusibilized in the infusibilization step were carbonized in a nitrogen atmosphere.
  • the carbonization treatment conditions included a carbonization treatment temperature of 800° C. and a holding period of 30 minutes.
  • the tensile strengths of the carbon fibers were found to be 600 MPa in Example 1, 750 MPa in Example 2, 800 MPa in Example 3, and 850 MPa in Example 4. Meanwhile, in Comparative Example 1 and Comparative Example 2, carbon fibers were unable to be obtained because it was difficult to perform melt-spinning continuously and stably at a constant fiber diameter. The tensile strength measurement was hence not performed in Comparative Example 1 and Comparative Example 2.
  • the method for carbon fiber production of the present invention is especially suitably applied to a production of carbon fibers required to have dimensional accuracy.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Textile Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Mechanical Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Inorganic Fibers (AREA)
  • Solid Fuels And Fuel-Associated Substances (AREA)
US15/557,506 2015-03-17 2016-02-08 Method for producing carbon fibers Abandoned US20180051397A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2015053477A JP6437355B2 (ja) 2015-03-17 2015-03-17 炭素繊維の製造方法
JP2015-053477 2015-03-17
PCT/JP2016/053664 WO2016147743A1 (ja) 2015-03-17 2016-02-08 炭素繊維の製造方法

Publications (1)

Publication Number Publication Date
US20180051397A1 true US20180051397A1 (en) 2018-02-22

Family

ID=56918771

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/557,506 Abandoned US20180051397A1 (en) 2015-03-17 2016-02-08 Method for producing carbon fibers

Country Status (6)

Country Link
US (1) US20180051397A1 (zh)
JP (1) JP6437355B2 (zh)
KR (1) KR101943784B1 (zh)
CN (1) CN107407012B (zh)
DE (1) DE112016001254T5 (zh)
WO (1) WO2016147743A1 (zh)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019044313A (ja) * 2017-09-06 2019-03-22 株式会社神戸製鋼所 炭素繊維の製造方法
WO2020186011A1 (en) * 2019-03-12 2020-09-17 University Of Wyoming Thermo-chemical processing of coal via solvent extraction
US20200332197A1 (en) * 2017-09-13 2020-10-22 University Of Wyoming Systems and methods for refining coal into high value products

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6571043B2 (ja) * 2016-05-19 2019-09-04 株式会社神戸製鋼所 炭素繊維の製造方法、炭素繊維及び電気二重層キャパシタ用電極
JP2018016920A (ja) * 2016-07-29 2018-02-01 株式会社神戸製鋼所 炭素繊維の製造方法
JP2018140883A (ja) * 2017-02-24 2018-09-13 株式会社神戸製鋼所 多孔質炭素粒子の製造方法及び多孔質炭素粒子
JP2018178284A (ja) * 2017-04-07 2018-11-15 株式会社神戸製鋼所 多孔質炭素繊維シートの製造方法及び多孔質炭素電極の製造方法
JP6767918B2 (ja) * 2017-04-19 2020-10-14 株式会社神戸製鋼所 電界紡糸用組成物及び多孔質炭素繊維の製造方法
US11046584B2 (en) 2017-12-22 2021-06-29 Carbon Holdings Intellectual Properties, Llc Methods for producing advanced carbon materials from coal
CN108560082B (zh) * 2018-05-10 2021-06-22 湖南大学 一种高强度煤系各向同性沥青基碳纤维的制备方法
KR102227071B1 (ko) * 2019-05-20 2021-03-15 한국에너지기술연구원 저등급 석탄 및 애쉬프리콜로부터의 방사성 피치 제조방법 및 저비용 고강도의 등방성 탄소섬유로의 응용방법

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4756818A (en) * 1986-03-27 1988-07-12 Rutgerswerke Aktiengesellschaft A method for the production of a carbon fiber precursor
US20170096340A1 (en) * 2014-05-19 2017-04-06 Kabushiki Kaisha Kobe Seiko Sho ( Kobe Steel, Ltd.) Method for producing carbon material, and carbon material

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS56140019A (en) * 1980-03-29 1981-11-02 Mitsui Cokes Kogyo Kk Manufacture of activated carbon fiber
JPS59155494A (ja) * 1983-02-22 1984-09-04 Kawasaki Steel Corp 炭素繊維の原料用ピツチの製造法
US4578177A (en) * 1984-08-28 1986-03-25 Kawasaki Steel Corporation Method for producing a precursor pitch for carbon fiber
JPH0216190A (ja) * 1988-07-05 1990-01-19 Kawasaki Steel Corp 炭素繊維用プリカーサーピッチの製造方法
JPH0715099A (ja) 1993-06-22 1995-01-17 Mitsubishi Shindoh Co Ltd 回路基板およびその製造方法
JP5128351B2 (ja) * 2007-10-23 2013-01-23 株式会社神戸製鋼所 炭素材料の製造方法
JP2012184125A (ja) * 2011-03-03 2012-09-27 Kobe Steel Ltd 炭素材料の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4756818A (en) * 1986-03-27 1988-07-12 Rutgerswerke Aktiengesellschaft A method for the production of a carbon fiber precursor
US20170096340A1 (en) * 2014-05-19 2017-04-06 Kabushiki Kaisha Kobe Seiko Sho ( Kobe Steel, Ltd.) Method for producing carbon material, and carbon material

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019044313A (ja) * 2017-09-06 2019-03-22 株式会社神戸製鋼所 炭素繊維の製造方法
US20200332197A1 (en) * 2017-09-13 2020-10-22 University Of Wyoming Systems and methods for refining coal into high value products
WO2020186011A1 (en) * 2019-03-12 2020-09-17 University Of Wyoming Thermo-chemical processing of coal via solvent extraction
US12006219B2 (en) 2019-03-12 2024-06-11 University Of Wyoming Thermo-chemical processing of coal via solvent extraction

Also Published As

Publication number Publication date
KR101943784B1 (ko) 2019-01-29
CN107407012A (zh) 2017-11-28
JP6437355B2 (ja) 2018-12-12
JP2016172940A (ja) 2016-09-29
WO2016147743A1 (ja) 2016-09-22
KR20170117177A (ko) 2017-10-20
DE112016001254T5 (de) 2017-12-07
CN107407012B (zh) 2019-08-23

Similar Documents

Publication Publication Date Title
US20180051397A1 (en) Method for producing carbon fibers
US20170096340A1 (en) Method for producing carbon material, and carbon material
CN107532086B (zh) 碳纤维制造用原料沥青
JPH0150272B2 (zh)
JP6424152B2 (ja) 炭素繊維製造用原料ピッチの製造方法
WO2018021386A1 (ja) 炭素繊維の製造方法
JPS60170694A (ja) 炭素繊維プリカ−サ−ピツチの製造方法
JPH0149316B2 (zh)
JPH0532494B2 (zh)
JP2018016921A (ja) 炭素繊維の製造方法
JP2780231B2 (ja) 炭素繊維の製造方法
JPH023496A (ja) 高性能炭素繊維用原料の製造方法
JPH0150271B2 (zh)
JP2691231B2 (ja) ピッチの製造方法
JPS6247969B2 (zh)
US9751764B2 (en) Carbon material production method and carbon material
JPH10204441A (ja) 含浸用ピッチの製造方法およびその製造装置
JPS58126317A (ja) 炭素繊維製造用原料組成物および炭素繊維製造法
JPH0367123B2 (zh)
JPS6018573A (ja) 炭素繊維用プリカ−サ−ピツチの製造方法
JPH054434B2 (zh)
JPS6320387A (ja) メソフエ−ズピツチの製造方法およびその製造装置
JPH0461089B2 (zh)
JPH0635584B2 (ja) 炭素繊維用粗原料ピツチの貯蔵方法
JPS60110924A (ja) 炭素繊維製造法

Legal Events

Date Code Title Description
AS Assignment

Owner name: KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.)

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HAMAGUCHI, MAKI;WADA, SHOHEI;INOUE, TOSHINORI;AND OTHERS;SIGNING DATES FROM 20170615 TO 20170620;REEL/FRAME:043552/0410

Owner name: KYUSHU UNIVERSITY, NATIONAL UNIVERSITY CORPORATION

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HAMAGUCHI, MAKI;WADA, SHOHEI;INOUE, TOSHINORI;AND OTHERS;SIGNING DATES FROM 20170615 TO 20170620;REEL/FRAME:043552/0410

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION