US20130209724A1 - Pile layer with carbon-fiber encompassing bundles - Google Patents

Pile layer with carbon-fiber encompassing bundles Download PDF

Info

Publication number
US20130209724A1
US20130209724A1 US13/704,121 US201113704121A US2013209724A1 US 20130209724 A1 US20130209724 A1 US 20130209724A1 US 201113704121 A US201113704121 A US 201113704121A US 2013209724 A1 US2013209724 A1 US 2013209724A1
Authority
US
United States
Prior art keywords
fibers
pile layer
pile
bundles
carbon fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/704,121
Other languages
English (en)
Inventor
Birgit Reiter
Martin Danzer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SGL Automotive Carbon Fibers GmbH and Co KG
Original Assignee
SGL Carbon SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SGL Carbon SE filed Critical SGL Carbon SE
Assigned to SGL CARBON SE reassignment SGL CARBON SE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: DANZER, MARTIN, REITER, BIRGIT
Publication of US20130209724A1 publication Critical patent/US20130209724A1/en
Assigned to SGL AUTOMOTIVE CARBON FIBERS GMBH & CO. KG reassignment SGL AUTOMOTIVE CARBON FIBERS GMBH & CO. KG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SGL CARBON SE
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H11/00—Non-woven pile fabrics
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/04—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts comprising reinforcements only, e.g. self-reinforcing plastics
    • B29C70/06—Fibrous reinforcements only
    • B29C70/08—Fibrous reinforcements only comprising combinations of different forms of fibrous reinforcements incorporated in matrix material, forming one or more layers, and with or without non-reinforced layers
    • B29C70/081—Combinations of fibres of continuous or substantial length and short fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/022—Non-woven fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/028—Net structure, e.g. spaced apart filaments bonded at the crossing points
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/06—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer characterised by a fibrous or filamentary layer mechanically connected, e.g. by needling to another layer, e.g. of fibres, of paper
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/22—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed
    • B32B5/24—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer
    • B32B5/26—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by the presence of two or more layers which are next to each other and are fibrous, filamentary, formed of particles or foamed one layer being a fibrous or filamentary layer another layer next to it also being fibrous or filamentary
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
    • B32B7/04—Interconnection of layers
    • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01G—PRELIMINARY TREATMENT OF FIBRES, e.g. FOR SPINNING
    • D01G1/00—Severing continuous filaments or long fibres, e.g. stapling
    • D01G1/02—Severing continuous filaments or long fibres, e.g. stapling to form staple fibres not delivered in strand form
    • D01G1/04—Severing continuous filaments or long fibres, e.g. stapling to form staple fibres not delivered in strand form by cutting
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01G—PRELIMINARY TREATMENT OF FIBRES, e.g. FOR SPINNING
    • D01G13/00—Mixing, e.g. blending, fibres; Mixing non-fibrous materials with fibres
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01G—PRELIMINARY TREATMENT OF FIBRES, e.g. FOR SPINNING
    • D01G15/00—Carding machines or accessories; Card clothing; Burr-crushing or removing arrangements associated with carding or other preliminary-treatment machines
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01G—PRELIMINARY TREATMENT OF FIBRES, e.g. FOR SPINNING
    • D01G7/00—Breaking or opening fibre bales
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/04—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres having existing or potential cohesive properties, e.g. natural fibres, prestretched or fibrillated artificial fibres
    • D04H1/06—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres having existing or potential cohesive properties, e.g. natural fibres, prestretched or fibrillated artificial fibres by treatment to produce shrinking, swelling, crimping or curling of fibres
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/4209—Inorganic fibres
    • D04H1/4242—Carbon fibres
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/4274—Rags; Fabric scraps
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
    • D04H1/4374—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece using different kinds of webs, e.g. by layering webs
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/44—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling
    • D04H1/46—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling by needling or like operations to cause entanglement of fibres
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
    • D04H1/44—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling
    • D04H1/46—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling by needling or like operations to cause entanglement of fibres
    • D04H1/498—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties the fleeces or layers being consolidated by mechanical means, e.g. by rolling by needling or like operations to cause entanglement of fibres entanglement of layered webs
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
    • D04H1/70—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres characterised by the method of forming fleeces or layers, e.g. reorientation of fibres
    • D04H1/74—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres characterised by the method of forming fleeces or layers, e.g. reorientation of fibres the fibres being orientated, e.g. in parallel (anisotropic fleeces)
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/02—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments
    • D04H3/04—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments in rectilinear paths, e.g. crossing at right angles
    • D04H3/045—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of forming fleeces or layers, e.g. reorientation of yarns or filaments in rectilinear paths, e.g. crossing at right angles for net manufacturing
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H5/00—Non woven fabrics formed of mixtures of relatively short fibres and yarns or like filamentary material of substantial length
    • D04H5/02—Non woven fabrics formed of mixtures of relatively short fibres and yarns or like filamentary material of substantial length strengthened or consolidated by mechanical methods, e.g. needling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
    • B29B11/00—Making preforms
    • B29B11/14—Making preforms characterised by structure or composition
    • B29B11/16—Making preforms characterised by structure or composition comprising fillers or reinforcement
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/20—All layers being fibrous or filamentary
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0276—Polyester fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/10—Inorganic fibres
    • B32B2262/101—Glass fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/10—Inorganic fibres
    • B32B2262/106—Carbon fibres, e.g. graphite fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2605/00—Vehicles
    • B32B2605/08—Cars
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/23929—Edge feature or configured or discontinuous surface
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/23957—Particular shape or structure of pile
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/23957—Particular shape or structure of pile
    • Y10T428/23964—U-, V-, or W-shaped or continuous strand, filamentary material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/23979—Particular backing structure or composition
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/23993—Composition of pile or adhesive

Definitions

  • the present invention relates to a pile layer, which exhibits a plurality of bundles partially broken up into single fibers and encompassing carbon fibers, as well as foreign materials according to the preamble of claim 1 , as well as to a method for manufacturing such a pile layer according to the preamble of claim 14 .
  • the invention further relates to a nonwoven or nonwoven material, which encompass such pile layers.
  • Pile layers encompassing carbon fibers are especially well suited as an initial structure for manufacturing nonwovens or nonwoven materials, which are used in numerous applications in the automobile industry. They are used above all for manufacturing automobile components.
  • the nonwovens and nonwoven materials in question are advantageously processed into light, yet mechanically very resilient fiber composite structures, which are increasingly being viewed as a preferred and pioneering material.
  • Pile formation typically involves supplying single fibers having a predetermined length distribution to a pile forming machine via suitable feeding devices.
  • a pile forming machine can be designed as a carding machine.
  • air-operated, pneumatic or eluent-assisted pile forming machines are known alternatives.
  • Suitable functional components in the respective pile forming machines intertwine the single fibers, so that a flat structure is formed, to which the intertwined fibers impart enough intrinsic stability to withstand the outer mechanical stresses that arise during continued processing.
  • the pile layers removed from pile forming machines can be processed into nonwoven materials in additional steps.
  • the pile layers can be doubled, i.e., the pile layers can be laid one on top of the other, so as to create a nonwoven with a desired thickness and suitable overall fiber content, which even once solidified, e.g., via needling, can be relayed to another processing step as a nonwoven material.
  • Nonwoven materials generally differ from conventional nonwovens in that they have undergone a chemical, mechanical or thermal solidification.
  • a pile layer and a nonwoven. All of these structures are obtained in a process aimed at intertwining the fibers into a mechanically relatively stable flat structure.
  • the nonwoven material is distinguished from the nonwoven or pile layer by the subsequent additional step of solidification, as described further above.
  • the problem with respect to the described procedures is that the single fibers fed to the pile forming machines must typically be subjected to complex mechanical preparation. Used for this purpose are opening and/or mixing units, which break up and prepare the fibers, for example at classic spinning mills.
  • the manufacture of pile layers using carbon fibers also requires a complicated preparation of carbon fibers.
  • the carbon fibers can be removed from carbon fiber strands. To this end, the latter must first be removed from a spool and fed to a cutting device. After cut o a suitable length, the bundles of carbon fibers must be broken up by separating the carbon fibers in the bundle sections. Before fed into the pile forming machine, the fibers must also be suitably accumulated and metered into the pile forming process. Only thereafter are the isolated, i.e., completely broken up fibers, fed to the pile forming machine, in which the fibers can be processed into a pile.
  • the object of the present invention is to propose a pile layer along with a method for manufacturing such a pile layer that enables the simple return of materials obtained from recycling processes, in particular of carbon fibers, to textile structures suitable for technical applications.
  • the object of the present invention is to propose a pile layer that also permits the use of recycled carbon fibers, while not diminishing the suitability of the pile layer for technical application.
  • the object of the present invention is to suggest a nonwoven or nonwoven material that encompasses these types of pile layers.
  • the object further to be achieved with the manufacturing process lies in providing a less cost-intensive method for fabricating a pile layer by comparison with the method known from prior art.
  • this object is achieved with a pile layer according to claim 1 , as well as with a manufacturing method according to claim 14 .
  • the object of the invention is achieved with a nonwoven or nonwoven material according to claim 13 .
  • the object underlying the invention is achieved by a pile layer comprising a plurality of bundles that are partially broken up into single fibers and encompass carbon fibers, as well as foreign materials, wherein the carbon fibers comprise at least 70% by weight of the overall weight of the pile layer, and the foreign materials comprise no more than 30%, but not less than 2%, and wherein the foreign materials are derived from a recycling process.
  • the solution according to the invention further involves a method for manufacturing a pile layer, which encompasses the following steps: Cutting a flat structure that exhibits bundles encompassing carbon fibers, and is at least partially fixed by means of foreign materials, in particular knitting or sowing threads, or a binder; processing the cut flat structure to partially break open the bundle into single fibers in an opening unit, in particular in a tearing machine; introducing the batch partially broken up as the result of being processed in this way into a pile forming machine, in particular into a carding machine; operating the pile forming machine in such a way as not to completely isolate the bundles into single fibers, but rather to intertwine carbon fibers in the bundles with additional fibers; removing the pile layer from the pile forming machine.
  • the pile layer according to the invention is advantageously distinguished by the fact that it exhibits a percentage of foreign material measuring at most 30%, while the carbon fibers exhibit a percentage by weight of at least 70%.
  • the percentage of carbon fibers here determines first and foremost the strength as well as the quality of the pile layer, wherein the percentage of foreign material contributes to the basis weight of the textile as a whole, but without also significantly influencing the strength and quality.
  • the quality and strength relates in particular to the quality and strength that the pile layer can provide to a composite material into which it is integrated.
  • the process for manufacturing the pile layer according to the invention with a pile forming machine can be adjusted in such a way that the introduced bundles need not be resolved into single fibers in the pile forming machine.
  • this does not mean that single fibers will not be introduced into the pile forming machine aside from bundles.
  • the bundles can be present in a random arrangement of fibers that has not been solidified or further processed, in which in part isolated fibers protrude from a bundle, and are intertwined with other fibers, wherein other fibers can also be present in the bundle.
  • the bundle can consist completely of carbon fibers, or just a percentage thereof.
  • the fibers sent to the pile forming machine can here also consist in part of original fibers that were not taken from a recycling process.
  • a bundle must be understood as an accumulation of fibers that at least partially progress in an essentially parallel direction, wherein the fiber density in the bundle is at least partially elevated by comparison to the fiber density of the environment.
  • Bundles can in this respect also be visually identified very well, since they stand out visually in a readily discernible manner from their environment, and can be easily visually identified as a bundle.
  • a bundle can also exhibit a cohesion of single fibers, which safeguards the bundle against falling apart into single fibers when exposed to a mechanical stress.
  • the advantage to the pile layer according to the invention is that, while the bundles are also encompassed by the pile layer, the fibers are not resolved into single fibers. This imparts a special strength to the pile layer, in particular as relates to a mechanical stress, which acts on the bundles in a longitudinal direction of the fibers. By comparison to isolated fibers that are not further aligned relative to each other, this allows bundles to absorb external forces that act on the fiber composite material to be fabricated later in the direction of their fiber progression to a significantly better degree without failing.
  • One especially advantageous embodiment of the pile layer according to the invention is distinguished by the fact that the bundles encompassing carbon fibers are at least partially also obtained from recycling process.
  • the bundles it is also conceivable in this embodiment for the bundles to have been obtained at least partially from a recycling process, along with the fibers encompassed by the pile layer. This enables an especially cost-effective fabrication of the pile layer, since fewer manufacturing steps are to be expected.
  • the materials used in the pile layer are sometimes already tailored to each other.
  • the pile layer to be manufactured can also be mixed with original, i.e., as yet unused carbon fibers, so as to offset any potential losses in quality owing to the reused carbon fibers.
  • original carbon fiber bundles can be incorporated in the pile forming process.
  • the embodiment can also provide that the foreign materials at least partially exhibit foreign fibers, which are not carbon fibers.
  • such foreign fibers are glass fibers and synthetic fibers, e.g., chemical textile fibers made of polyethylene, polyamide, polyester, polypropylene, etc. These fibers are also integrated into the pile layer during the pile forming process. These fibers here preferably become intertwined with the carbon fibers or other fibers encompassed by the pile layer.
  • the foreign fibers only contribute negligibly to the strength of the pile layer, since the strength essentially stems from the carbon fibers. This relates in particular to the strength which the pile layer imparts to a fiber composite work piece encompassing it. But since the pile layer according to the embodiment exhibits enough carbon fibers, the required minimum strength can continue to be ensured.
  • One especially preferred further embodiment of the invention can also provide that the carbon fibers exhibit a predetermined first arrangement relative to each other, which determines a first pattern, and the foreign fibers exhibit a second arrangement relative to each other, which determines a second pattern, wherein the first pattern differs from the second pattern.
  • a pattern is to be understood as a distribution of material density over the surface area to be considered, wherein variations in material density are at least partially present. In particular, these variations in material density are visually discernible, and can be systematically compared.
  • the differentiation between the two patterns can be ascertained by means of a flat autocorrelation function.
  • a surface section of the pile layer according to the embodiment for example a surface section measuring 15 cm by 15 cm, is here selected and divided into smaller surface subunits—e.g., 1.5 mm by 1.5 mm—having the same surface area.
  • a value is assigned to the individual surface subunits from a prescribed scale, for example a scale ranging from ⁇ 5 to +5. Standardization takes place in relation to the overall fiber content in the surface section under examination.
  • a two dimensional integral or two dimensional sum is then calculated over all adjacent surface subunits for each surface subunit, wherein the integral or sum is calculated over a product of the value for the predetermined surface subunit and the values for the adjacent surface subunits. Therefore, the calculation involves a correlation of fiber surface density for the surface subunits themselves, i.e., an autocorrelation of fiber surface density. The value determined in this way is assigned to the respectively predetermined surface subunit, wherein the calculation must be performed accordingly for all other surface subunits.
  • a two-dimensional weight function can also be taken into account, for example which limits the integration or sum to an integration or sum encompassing the next 10 neighbors.
  • the number selected cannot be so small as to prevent the integration or sum from extending to possibly repeating patterns for the carbon fiber density, for example caused by the corresponding arrangement of bundles in the pile layer.
  • the results obtained from the individual calculations are then standardized once again, so that they can be made comparable relative to each other for all surface subunits. Standardization also makes it possible to correspondingly take edge effects into account too, which can arise given surface subunits lying close to the edge of the selected and examined surface section measuring about 15 cm by 15 cm.
  • the values for the autocorrelation function will deviate from zero or another baseline value, which indicates that no repeating regularities arise, i.e., the distribution of values is purely random.
  • the autocorrelation function is able to account for regularities in a pattern.
  • these regularities must differ from a strictly static sequence of values. If the patterns are purely random, i.e., these patterns come about only as the result of a purely statistically random distribution of the individual values, the autocorrelation function will yield a baseline value or zero for all surface subunits.
  • the baseline value depends on the scale values selected in advance, i.e., the baseline value denoting that a purely random distribution is present also depends among other things on the initially chosen scale.
  • the two patterns can also be compared using a simplified examination approach. As will be explained in detail in the figures section, this is preferred in particular when the foreign material density or foreign fiber density is so low that only a percentage of the surface subunits for the foreign material density or foreign fiber density exhibits an overlap with the surface subunits, while other surface subunits can have no overlap. Additional explanations regarding this simplified, and in most instances preferred, method of comparison may be gleaned from the figures section.
  • the diversity of patterns reveals a varied distribution of single fibers in a selected surface section. If the foreign materials or foreign fibers that behave differently from the carbon fibers or the bundles encompassing carbon fibers in the pile manufacturing process are typically stochastically distributed, the bundles that encompass carbon fibers are typically increasingly distributed uniformly over the entire surface area of the pile layer, in part spaced apart at regular intervals. This circumstance also stems from the fact that the bundles exhibit an elevated tendency to be uniformly distributed over the entire surface area during the pile forming process in the pile forming machine when exposed to a mechanical stress. By contrast, the foreign fibers that are sometimes encountered in far fewer numbers in the pile layer can also be randomly distributed over the surface area of the pile layer, but are at times present in vastly lower concentrations.
  • the order is here determined based on the mathematical aspects to be applied in conjunction with patterns and complex arrangements. Determining the order within the meaning of a complex order here enables a generalization of the aspects described above for calculating an autocorrelation. Logical procedures for calculating the order are known to the expert, and can be applied accordingly to the case at hand.
  • a further embodiment of the present invention can also provide that at least 10% of the foreign fibers have a tensile strength that is 1.5 times, in particular 2 times, lower by comparison to the carbon fibers.
  • the lower strength of the foreign fibers only diminishes the strength of the pile layer or the fiber composite material fabricated therewith to a slight extent, if at all, since the carbon fibers are present in sufficient amounts. In particular for applications in automotive engineering, the very small, yet possible losses in strength are insignificant.
  • Another embodiment can also provide that at least a portion of the foreign fibers are sewing or knitting threads. Accordingly, sewing or knitting threads originally provided to fix a textile to be reused, i.e., recycled, can be relayed to the pile forming process along with the carbon fibers encompassed by this textile, without having to be separated out of the carbon fibers or carbon fiber bundles. This reduces the manufacturing outlay on the one hand, and also ensures the production of a relatively more cost-effective pile layer.
  • the foreign fibers exhibit a different color by comparison to the carbon fibers.
  • this makes it easy to identify locations where accumulations of foreign fibers arise, which could potentially detract from the quality, while on the other hand, the foreign fibers can also be removed from the pile layer after the fact as needed in a targeted manner, should this become necessary.
  • consideration can be given to removing the foreign fibers from the pile layer composite.
  • An embodiment can also provide that at least a portion of the foreign fibers exhibits a crimp. Fibers with a crimp are better anchored with the surrounding carbon fibers, so that an additional local solidification can be achieved for the pile layer. The latter is especially advantageous when, after it has been manufactured, the pile layer is exposed to a mechanical stress during further processing that might at times cause damage to the pile layer as the result of handling.
  • Another embodiment can also provide that at least a portion of the foreign fibers be approx. 50%, preferably even 100%, longer on average than the carbon fibers in the bundle.
  • solidifying threads derived from the recycling process can still be present in the pile layer.
  • Solidifying threads include in particular knitting threads or sewing threads that can be used to solidify carbon fiber textiles, but were not additionally isolated during the recycling process. Since these threads are typically also significantly less brittle than carbon fibers, these threads are not shortened to as great an extent as carbon fibers, even when processed in a mill, in particular a hammer mill. In addition, these threads typically already have a greater length when present in the textile object to be reused.
  • the foreign fibers are glass fibers and/or polyester fibers.
  • the latter are preferred auxiliary fibers, which are readily used especially in textile structures intended for preliminary solidification.
  • polyester fibers are preferably used for sewing or knitting individual textile layers.
  • Other fibers are also possible, including polyamide fibers, polyethylene fibers, polypropylene fibers or the like.
  • Another embodiment of the invention can also provide that the foreign substances at least partially exhibit a chemical binder, in particular a resin. Therefore, the embodiment does not require that a binder be removed from the fiber surface or completely removed before relaying the fibers to a pile forming process. Rather, percentages of this binder can be integrated into the pile layer, but without having to diminish the strength requirements placed on the fiber composite material to be subsequently manufactured.
  • the binder can instead even help to pre-solidify the fibers in the pile layer, so that the pile layer can exhibit an improved cohesion of fibers, for example. As a consequence, this type of pile layer is easier to handle, and can be exposed to a stronger mechanical stress, for example when subsequently processed.
  • the binder can be identical with the resin used to later treat the pile layer, so as to fabricate a fiber composite material.
  • the binder can also be chemically compatible with another resin, which serves to subsequently manufacture a fiber composite material by means of the pile layer.
  • a preferred embodiment can also provide that the bundles encompass at least 200, preferably at least 500, and especially preferably at least 1000 carbon fibers.
  • This makes it possible to increase the strength given to the pile layer by a possible alignment of the bundles, as a result of which an improved, directionally dependent strength is also imparted to the fiber composite material to be subsequently manufactured, for example.
  • this makes it possible to reuse carbon fiber textiles from a recycling process, which typically exhibit strands comprising more than 1000 fibers per strand.
  • the latter are prepared in a carbon fiber textile to be reused in such a way as to break open the strands to a minimum number of fibers.
  • a pile layer exhibit a mass per unit area (weight per unit area) of at most 50 g/m 2 , and no less than 10 g/m 2 , preferably between 35 g/m 2 and 25 g/m 2 .
  • Such pile layers are especially desired in particular in the automobile industry, since they exhibit a sufficient strength in the fiber composite material to be subsequently manufactured, while allowing a very large reduction in the weight of the component.
  • the masses per unit area according to the embodiment enable an efficient use of the valuable raw material, carbon fibers, while at the same time ensuring compliance with the minimal requirements placed on strength. Therefore, the ratio between required strength and the present weight is especially advantageous.
  • Another preferred embodiment of the nonwoven material can also provide that it exhibit a pile layer according to the embodiments described previously, which is needled for solidification purposes. Needling causes the fibers encompassed by the pile layer to become further intertwined, in particular intertwined on a local level, thereby producing a local solidification. If the pile layer is needled with a sufficient number of sufficiently dense stitches, a distinctly improved strength can be imparted to the entire pile layer structure.
  • Another embodiment of a nonwoven or nonwoven material can also provide that the orientation of the curved bundles in a pile layer deviate from the orientation of the curved bundles in another pile layer by at least 5°, in particular differing by an angle of 15°, 30°, 45°, 60°, 75° or 90°.
  • this makes it easy to generate preferred directions within the nonwoven or nonwoven material with a defined angular deviation. This proves very advantageous within the framework of processing in automotive vehicle construction, since the preferred directions can be suitably tailored relative to the applications.
  • each subunit exhibits the number of needling punctures according to the embodiment.
  • the needling punctures provide a sufficient number of openings in the pile layer or pile layers to enable a more efficient impregnation with a liquid resin or a polymer. This is because the openings make it possible to efficiently relay the resin or polymer over the entire needling thickness, and hence, as stipulated in the embodiment, over the entire thickness of the pile layer(s). This reduces the impregnation time for one, and hence also the manufacturing time for components that encompass the pile layer(s).
  • a further aspect of the solution to the object of the invention can also provide that a resin-impregnated component exhibit a pile layer described above, or a nonwoven described above, or a nonwoven material described above, wherein the component is designed in particular as a vehicle component.
  • Such components can exhibit the described pile layers, nonwovens or nonwoven materials separately or in conjunction with other textile structures.
  • the described pile layers, nonwovens or nonwoven materials can be encompassed by the component in conjunction with a structure and/or a fabric, wherein the structure and/or fabric is furnished primarily to absorb stresses.
  • the components of a vehicle exhibiting the described pile layers, nonwovens or nonwoven materials not to be provided to ensure the passive safety of a vehicle.
  • these components are preferably designed as parts of the outer skin of a vehicle.
  • the component can be impregnated with resin, wherein a complete impregnation or even just a partial impregnation can be achieved.
  • the resin-impregnated component can be hardened.
  • the resin impregnation according to the embodiment must also include a suitable polymer impregnation.
  • An especially preferred embodiment of the method according to the invention can also provide that the method not encompass the step of separating the foreign materials, or not encompass the step of partially separating the foreign materials.
  • FIG. 1 a is a first embodiment of a pile layer according to the invention, top view
  • FIG. 1 b is the percentage of carbon fiber in the pile layer according to FIG. 1 a , isolated view;
  • FIG. 1 c is the percentage of foreign fiber in the pile layer according to FIG. 1 a , isolated view
  • FIG. 2 is a schematic view of the percentage of foreign fibers according to FIG. 1 c in conjunction with a flat distribution for characterizing the pattern or order of the pattern of foreign fibers;
  • FIG. 4 is a flowchart for illustrating the sequence of individual steps, which are encompassed by an embodiment of the manufacturing method according to the invention.
  • FIG. 1 presents a first embodiment of a pile layer 1 according to the invention with a plurality of bundles 2 that encompass carbon fibers 10 . While the bundles here exhibit a preferred curved progression, they can also have any other technically possible progression. The curvature of the present bundles is the result of being processed with a carding machine. The bundles 2 are intertwined with other fibers encompassed by the pile layer 1 , which can also be carbon fibers 10 , thereby making it possible to prepare a pile layer 1 that is strong enough, for example, that it can be removed from the pile forming machine as a complete structure, or undergo further mechanical processing.
  • the pile layer 1 according to FIG. 1 a also encompasses a number of foreign materials 20 , in particular in the form of foreign fibers 20 , which are shown in bold. These foreign materials 20 or foreign fibers 20 are again depicted in an isolated view on FIG. 1 c .
  • the foreign materials 20 or foreign fibers 20 are here each randomly arranged. In particular, the progression of the foreign material 20 or foreign fiber progression exhibits no regularity. In addition, the individual foreign materials 20 or foreign fibers 20 also have a purely random arrangement relative to each other.
  • the bundles exhibit a relatively similar, curved progression.
  • the latter is characterized by a vertex area, which has the largest curvature in the progression of a bundle.
  • the vertex area is situated between the bundle ends, wherein the bundle end areas exhibit only a relatively slight curvature by comparison to the vertex area.
  • the bundle end areas are sometimes not even curved at all.
  • the bundles 2 Due to the curved progression, the bundles 2 also exhibit a preferred direction not just roughly in the direction of fiber progression at the bundle end areas, but also roughly in the direction tangential to the vertex area. Therefore, the curved progression ensures that the bundles 2 exhibit a preferred direction not just with respect to force absorption, but also another preferred direction that deviates from it, in particular running perpendicular to the first preferred direction.
  • the curvature of a bundle 2 is determined from the averaged directional progression of all fibers in the bundle 2 .
  • the fibers in a bundle are acquired in terms of their individual spatial position, wherein the average position is calculated from comparable sections of individual fibers in the bundle 2 .
  • the average progression essentially corresponds with that of the fiber located in the middle of the bundle 2 in relation to the cross section.
  • the fibers are fanned out, as will sooner typically be the case at the bundle ends, it will be possible to calculate the average progression of the bundle 2 by averaging the layers of all comparable sections of the individual fibers. Based upon established deliberations, the expert can calculate the average so as to determine the average progression.
  • the bundles 2 exhibit a comparable orientation. In the present case, this means that the vertex areas of the bundles 2 are oriented to one side of the pile layer 1 , while the individual bundle ends of the respective bundles 2 point to the opposite side of the pile layer 1 .
  • the distances between the individual bundles 2 and the respective immediately adjacent bundles 2 only vary to a negligible extent for all bundles 2 . This relates both to the distances between the respectively adjacent bundles 2 laterally as shown on FIG. 1 b , as well as to the distances from the next bundles 2 above or below a bundle 2 in the respective illustration.
  • the examined surface section of the pile layer 1 for example a surface section measuring 20 cm by 20 cm, can very easily be divided into respectively identical surface subsections.
  • FIG. 2 the depicted surface section was divided into a checkerboard pattern of 32 by 32 surface subsections.
  • a value can now be assigned to the respective surface subsections.
  • the foreign material density and foreign fiber density must here be standardized to the overall [material] density or overall fiber density. In the simplest case, a value of 1 could be assigned if percentages of foreign materials or foreign fibers were present in the surface subsection.
  • both patterns were now to be identical, subtraction would yield a value of zero for each surface subunit.
  • the more varied the patterns the more different the individual values yielded by subtracting the surface subunits. This results in a gauge for the disparity between the patterns to be compared. From a practical standpoint, it could be determined that the two patterns differ if the subtracted values for all respective comparable surface subunits exceed an average limit. For example, the patterns could differ if the sum of all subtracted values for all surface subunits standardized to the overall number of surface subunits exceeds a predetermined value. This value must be determined in a reasonable manner in accordance with the scale graduation selected above. For example, it could measure 0.1 in a scale ranging from ⁇ 5 to +5.
  • determining the differences between the patterns for both examined surface sections is relatively easy, since the distribution of carbon fibers 10 clearly differs from the distribution of foreign materials 20 or foreign fibers 20 . In each instance, this difference can already be discerned with the naked eye. This holds true in particular because the distribution of foreign materials 20 or foreign fibers 20 does not even cover numerous surface subunits of the examined surface section. However, if most or even all surface subunits are covered, a simple comparison of patterns by subtracting the values for the respective comparable surface subsections can at times produce a false picture. In addition, certain patterns may not be immediately obvious, since the patterns are scarcely perceptible in the amount of existing carbon fibers 10 or foreign materials 20 . In this respect, it may be appropriate to use a more refined method of pattern comparison. For example, as already described above, the flat autocorrelation for all surface subunits can be calculated, which is sometimes better able to have existing pattern regularities included in the calculation.
  • Both introduced methods are each equivalent in terms of comparing patterns within the framework of the present invention, wherein the simpler method is preferably to be used given a foreign material distribution if at least 5% of the identified surface subsections of a surface section chosen for purposes of pattern comparison are unable to show any foreign materials in the overlap.
  • FIG. 3 shows a first embodiment of a nonwoven or nonwoven material according to the invention, which consists of two plies of a pile layer 1 fabricated through doubling. If a nonwoven fabric is present, the latter can have been solidified by needling the two plies of the pile layers 2 .
  • the two pile layers 2 are arranged relative to each other in such a way that their respective preferred directions are turned by a specific angle in relation to one another. In this way, the strength-enhancing properties that may be derived from the preferred directions of the individual pile layers 2 can be adjusted in a directionally specific manner.
  • a relative arrangement of the two pile layers 1 to each other can preferably involve turning by an angle of 15°, 30°, 45°, 60°, 75° and 90°. In the present case, the relative arrangement of the two pile layers 1 has them turned by about 45° relative to each other.
  • FIG. 4 relates to a flowchart for illustrating the progression of individual steps, which are encompassed by an embodiment of the method according to the invention for manufacturing a pile layer.
  • a flat structure which exhibits bundles 2 encompassing carbon fibers 10 , and is fixed at least partially by foreign materials 20 , in particular by knitting threads.
  • Cutting can here be understood in its most general form, and also encompasses a blanking step, for example.
  • the cut flat structure be processed, in particular in a hammer mill, so as to partially break up the bundles 2 into single fibers; also encompassed is a step of introducing the batch partially broken up during this processing step into a pile forming machine, in particular into a carding machine.
  • the pile forming machine is subsequently operated so as to not completely isolate the bundles 2 into single fibers, while still intertwining carbon fibers 10 in the bundles 2 with other fibers.
  • the pile layer fabricated in this way is then removed from the pile forming machine.
  • the method does not also encompass the step of separating the foreign materials 20 or foreign fibers 20 .
  • the pile layers can subsequently also be processed into nonwovens or nonwoven materials. Needling, stitching or knitting can also be considered for solidifying several pile layers 1 laid on top of each other.
  • the curved bundles 2 encompassed by the pile layers 1 must here only be partially damaged, if at all.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Composite Materials (AREA)
  • Nonwoven Fabrics (AREA)
  • Laminated Bodies (AREA)
  • Reinforced Plastic Materials (AREA)
  • Woven Fabrics (AREA)
  • Manufacturing Of Multi-Layer Textile Fabrics (AREA)
US13/704,121 2010-11-03 2011-11-03 Pile layer with carbon-fiber encompassing bundles Abandoned US20130209724A1 (en)

Applications Claiming Priority (21)

Application Number Priority Date Filing Date Title
DE102010043347.0 2010-11-03
DE102010043349.7 2010-11-03
DE102010043346.2 2010-11-03
DE102010043300 2010-11-03
DE102010043346 2010-11-03
DE102010043349 2010-11-03
DE102010043347 2010-11-03
DE102010043345.4 2010-11-03
DE102010043345 2010-11-03
DE102010043300.4 2010-11-03
DE102011077880 2011-06-21
DE102011077879.9 2011-06-21
DE102011077881 2011-06-21
DE102011077879 2011-06-21
DE102011077881.0 2011-06-21
DE102011077880.2 2011-06-21
DE102011078741 2011-07-06
DE102011078741.0 2011-07-06
DE102011078739.9 2011-07-06
DE102011078739 2011-07-06
PCT/EP2011/069316 WO2012059540A1 (de) 2010-11-03 2011-11-03 Florschicht mit carbonfasern umfassenden bündeln

Publications (1)

Publication Number Publication Date
US20130209724A1 true US20130209724A1 (en) 2013-08-15

Family

ID=44947070

Family Applications (3)

Application Number Title Priority Date Filing Date
US13/704,114 Active 2033-06-29 US9551098B2 (en) 2010-11-03 2011-11-03 Nonwoven batt with curved carbon fiber bundles
US13/704,121 Abandoned US20130209724A1 (en) 2010-11-03 2011-11-03 Pile layer with carbon-fiber encompassing bundles
US13/704,104 Abandoned US20130209725A1 (en) 2010-11-03 2011-11-03 Reinforced nonwoven fabric

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US13/704,114 Active 2033-06-29 US9551098B2 (en) 2010-11-03 2011-11-03 Nonwoven batt with curved carbon fiber bundles

Family Applications After (1)

Application Number Title Priority Date Filing Date
US13/704,104 Abandoned US20130209725A1 (en) 2010-11-03 2011-11-03 Reinforced nonwoven fabric

Country Status (13)

Country Link
US (3) US9551098B2 (es)
EP (3) EP2635733A1 (es)
JP (3) JP5718462B2 (es)
KR (3) KR101577861B1 (es)
CN (3) CN103025940B (es)
BR (1) BR112012031770A8 (es)
CA (3) CA2802301C (es)
ES (2) ES2544991T3 (es)
HK (1) HK1181433A1 (es)
MX (3) MX2012014612A (es)
PL (2) PL2635417T3 (es)
PT (1) PT2635417E (es)
WO (3) WO2012059538A1 (es)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130209725A1 (en) * 2010-11-03 2013-08-15 Sgl Carbon Se Reinforced nonwoven fabric
WO2020212087A1 (en) 2019-04-18 2020-10-22 Teijin Carbon Europe Gmbh Wedge filler preform
US20220333280A1 (en) * 2019-09-06 2022-10-20 Green Petition Dis Ticaret Anonim Sirketi Textile products made of recycled fibers

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10066084B2 (en) * 2013-02-21 2018-09-04 Toray Industries, Inc. Stampable sheet
WO2014145457A1 (en) * 2013-03-15 2014-09-18 Federal-Mogul Powertrain, Inc. Moldable nonwoven having high strength to weight ratio for structural components and method of construction thereof
CN103352316B (zh) * 2013-07-04 2016-01-20 浙江和中非织造股份有限公司 用于墙体加固的无纺布及其生产工艺
CN104708860A (zh) * 2015-04-08 2015-06-17 常州众杰复合材料有限公司 一种网格夹芯缝编复合织物及其应用
DE202016104070U1 (de) * 2016-07-26 2017-10-27 Autefa Solutions Germany Gmbh Florprodukt mit unidirektional erhöhter Festigkeit zur Herstellung von CFK-Bauteilen
KR102402639B1 (ko) 2017-11-24 2022-05-26 삼성전자주식회사 전자 장치 및 그의 통신 방법
US20210062373A1 (en) * 2017-12-28 2021-03-04 Uchino Co., Ltd. Pile fabric
DE102018113587B8 (de) 2018-06-07 2024-02-29 Reinhard Koch Faserprofile zum Einsatz als Bewehrung in Betonbauten für hohe brandschutztechnische Anforderungen und Verfahren zu ihrer Herstellung
CN113461143B (zh) * 2021-07-14 2023-04-07 深圳华鹂环境技术有限公司 一种生态膜的制备方法

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5609707A (en) * 1991-09-04 1997-03-11 The B. F. Goodrich Company Carbon fiber reinforced carbon/carbon composite and method of its manufacture
DE102009023529A1 (de) * 2009-05-30 2010-12-02 Bayerische Motoren Werke Aktiengesellschaft Recyclingverfahren
DE102011079525A1 (de) * 2011-07-21 2013-01-24 Bayerische Motoren Werke Aktiengesellschaft Verfahren zur Herstellung eines faserverstärkten Kunstststoffhalbzeugs
US20130192189A1 (en) * 2010-02-05 2013-08-01 University Of Leeds Carbon fibre yarn and method for the production thereof
US20130196154A1 (en) * 2010-02-17 2013-08-01 Sgl Automotive Carbon Fibers Gmbh & Co. Kg Method for producing pellets from fiber composite materials and carbon fiber containing pellet
US20130192434A1 (en) * 2010-12-24 2013-08-01 Toray Industries, Inc Method for producing carbon fiber aggregate, and method for producing carbon fiber-reinforced plastic
US20130210298A1 (en) * 2010-02-17 2013-08-15 Sgl Automotive Carbon Fibers Gmbh & Co. Kg Method for producing a flat semi-finished product from a fiber composite material and flat semi-finished product
WO2013144844A1 (en) * 2012-03-26 2013-10-03 Agenzia Nazionale Per Le Nuove Tecnologie, L'energia E Lo Sviluppo Economico Sostenibile (Enea) Method and apparatus for manufacturing of non-woven fabric from recycled carbon fibers and the non-woven fabric so formed
WO2014037724A1 (en) * 2012-09-05 2014-03-13 University Of Ulster Carbon fibre composites
US20140245577A1 (en) * 2011-10-04 2014-09-04 Agenzia Nazionale Per Le Nuove Tecnologie, L/Energ E Lo Sviluppo Economico Sostenibile (Enea) Method for the manufacturing of yarns from recycled carbon fibers
US20150044438A1 (en) * 2012-03-09 2015-02-12 Quadrant Plastic Composites Ag Planar composite material

Family Cites Families (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63307915A (ja) 1987-06-10 1988-12-15 Dainippon Ink & Chem Inc 繊維強化樹脂複合成形品の製造方法
JP2570312B2 (ja) * 1987-08-07 1997-01-08 大日本インキ化学工業株式会社 炭素繊維樹脂成形品
JP2543981Y2 (ja) * 1988-05-02 1997-08-13 大阪瓦斯株式会社 補強された繊維状活性炭フィルター材
JP2639504B2 (ja) * 1988-07-28 1997-08-13 株式会社高分子加工研究所 立体的網状構造体
US5536486A (en) * 1989-03-15 1996-07-16 Petoca Ltd. Carbon fibers and non-woven fabrics
JPH05156595A (ja) * 1991-12-10 1993-06-22 Nikkiso Co Ltd ネット付き炭素繊維シートおよびその製造方法
DE9207367U1 (de) 1992-05-30 1992-09-10 Johns Manville International, Inc., Denver, Col. Schichtstoff aus Vlies und Gelege
JPH08144153A (ja) * 1994-11-21 1996-06-04 Toray Ind Inc 炭素繊維パイル布帛
US5804007A (en) * 1995-07-21 1998-09-08 Sunchemical Co., Ltd. Methods of manufacturing composite fiber sheet
JP3535619B2 (ja) * 1995-05-01 2004-06-07 サンケミカル株式会社 複合繊維シートの製造方法
JPH0912730A (ja) * 1995-06-30 1997-01-14 Kobe Steel Ltd 異形状繊維強化プラスチック
JPH0978396A (ja) * 1995-09-04 1997-03-25 Toray Ind Inc 炭素繊維パイル布帛
JP3737849B2 (ja) 1996-03-31 2006-01-25 大阪瓦斯株式会社 炭素繊維３次元構造体の製造方法
JPH1018146A (ja) * 1996-06-28 1998-01-20 Nitto Boseki Co Ltd 経一層三軸組布
DE19743545A1 (de) * 1996-10-02 1998-04-30 Fraunhofer Ges Forschung Verfahren zur Verarbeitung von Prepreg-Verschnittresten
DE19642714A1 (de) * 1996-10-16 1998-04-23 Asglawo Gmbh Stoffe Zum Daemme Material für die schall- und wärmedämmende Auskleidung des Motorraumes eines Kraftfahrzeuges
KR19990012382A (ko) * 1997-07-29 1999-02-25 유승빈 도전성 제전시트 및 그를 이용한 복식품
US6183835B1 (en) * 1997-08-27 2001-02-06 Moon Soo Cho Manufacturing method of reinforced fiber sheet useful for repairing/reinforced concrete structure
JP2000054252A (ja) * 1998-08-07 2000-02-22 Osaka Gas Co Ltd 炭素繊維フィルター
JP2001158017A (ja) * 1999-12-03 2001-06-12 Nikkiso Co Ltd 繊維強化樹脂プリプレグ廃材の破砕装置及び破砕回収方法
WO2001085439A1 (en) * 2000-05-11 2001-11-15 Fortafil Fibers, Inc. Method for the manufacture of a sheet of reinforcing fibers and the product obtained thereby
WO2001092002A2 (en) * 2000-06-02 2001-12-06 Ihc Rehabilitation Products Method for consolidation for random carbon fiber orientation and for forming a carbon fiber preform
CN2433277Y (zh) * 2000-08-15 2001-06-06 曹玉明 单向无纺碳纤维布
ITPD20040084A1 (it) 2004-03-30 2004-06-30 Orv Spa Prodotto stratiforme rinforzato a base di tessuto non tessuto particolarmente per bitumazione e suo procedimento di produzione
JP2005336407A (ja) * 2004-05-28 2005-12-08 Toho Tenax Co Ltd 表面平滑性に優れた複合材料
US7713893B2 (en) * 2004-12-08 2010-05-11 Albany Engineered Composites, Inc. Three-dimensional woven integrally stiffened panel
JP4675656B2 (ja) * 2005-03-23 2011-04-27 三乗工業株式会社 自動車用内装材のリサイクル方法
JP4353926B2 (ja) * 2005-07-20 2009-10-28 株式会社ユウホウ 導電性不織布の製法
CN100510211C (zh) * 2005-12-26 2009-07-08 上海杰事杰新材料股份有限公司 一种梳理机的喂入和梳理系统
EP2020282B1 (en) * 2006-05-25 2014-08-13 Mitsubishi Engineering-Plastics Corporation Moldings of fiber-reinforced thermoplastic resin
US8367569B2 (en) * 2006-05-26 2013-02-05 Fortress Stabilization Systems Carbon reinforced concrete
JP4895370B2 (ja) * 2006-09-27 2012-03-14 高安株式会社 炭素繊維不織布及びその製造方法
DE102006060241A1 (de) 2006-12-20 2008-06-26 Johns Manville Europe Gmbh Trägereinlage, Verfahren zu deren Herstellung und deren Verwendung
DE102008004005A1 (de) 2008-01-11 2009-07-16 CeTech Co., Ltd., Tanzih Leitfähiger Bogen aus Kohlefasern und Verfahren zu seiner Herstellung
CN103524769B (zh) 2008-07-31 2017-05-10 东丽株式会社 预浸料坯、预成型体、成型品及预浸料坯的制造方法
CN101392433B (zh) * 2008-10-30 2010-06-23 王常义 一种非织造网格增强复合无纺布制造方法
KR101406869B1 (ko) * 2009-05-13 2014-06-16 주식회사 데크 니들펀칭 공법을 이용한 탄소프리폼 제조 방법
JP3152748U (ja) * 2009-05-31 2009-08-13 エアテクス株式会社 カーボン不織布
WO2012059538A1 (de) * 2010-11-03 2012-05-10 Sgl Carbon Se Verstärkter vliesstoff
JP6051529B2 (ja) * 2011-02-18 2016-12-27 東レ株式会社 炭素繊維基材および炭素繊維複合材料ならびにそれらの製造方法
JP2012188779A (ja) * 2011-03-10 2012-10-04 Toray Ind Inc 炭素繊維不織布の製造方法
JP2012193466A (ja) * 2011-03-16 2012-10-11 Doshisha 不織布、この不織布の製造方法及びこの不織布を用いたサンドイッチ材
KR102041989B1 (ko) * 2011-11-16 2019-11-07 도레이 카부시키가이샤 섬유 강화 복합 재료 및 섬유 강화 복합 재료의 제조 방법

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5609707A (en) * 1991-09-04 1997-03-11 The B. F. Goodrich Company Carbon fiber reinforced carbon/carbon composite and method of its manufacture
US5869411A (en) * 1991-09-04 1999-02-09 The B. F. Goodrich Company Carbon fiber reinforced carbon/carbon composite and method of its manufacture
DE102009023529A1 (de) * 2009-05-30 2010-12-02 Bayerische Motoren Werke Aktiengesellschaft Recyclingverfahren
US20130192189A1 (en) * 2010-02-05 2013-08-01 University Of Leeds Carbon fibre yarn and method for the production thereof
US20130196154A1 (en) * 2010-02-17 2013-08-01 Sgl Automotive Carbon Fibers Gmbh & Co. Kg Method for producing pellets from fiber composite materials and carbon fiber containing pellet
US20130210298A1 (en) * 2010-02-17 2013-08-15 Sgl Automotive Carbon Fibers Gmbh & Co. Kg Method for producing a flat semi-finished product from a fiber composite material and flat semi-finished product
US20130192434A1 (en) * 2010-12-24 2013-08-01 Toray Industries, Inc Method for producing carbon fiber aggregate, and method for producing carbon fiber-reinforced plastic
DE102011079525A1 (de) * 2011-07-21 2013-01-24 Bayerische Motoren Werke Aktiengesellschaft Verfahren zur Herstellung eines faserverstärkten Kunstststoffhalbzeugs
US20140245577A1 (en) * 2011-10-04 2014-09-04 Agenzia Nazionale Per Le Nuove Tecnologie, L/Energ E Lo Sviluppo Economico Sostenibile (Enea) Method for the manufacturing of yarns from recycled carbon fibers
US20150044438A1 (en) * 2012-03-09 2015-02-12 Quadrant Plastic Composites Ag Planar composite material
WO2013144844A1 (en) * 2012-03-26 2013-10-03 Agenzia Nazionale Per Le Nuove Tecnologie, L'energia E Lo Sviluppo Economico Sostenibile (Enea) Method and apparatus for manufacturing of non-woven fabric from recycled carbon fibers and the non-woven fabric so formed
WO2014037724A1 (en) * 2012-09-05 2014-03-13 University Of Ulster Carbon fibre composites

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
definition of "pile", Dictionary of Fiber and Textile Technology, Hoechst Celanese, 1989, page 112. *
English translation of DE 102009023529 A1, 12/2010. *
Google Search definition of "pile", 01/24/2016. *
merriam-webster.com definition of "pile", 01/24/2016 *
Partial Google translation of DE 102009023529 A1, sections [0012] and [0013]. 12/2010. *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130209725A1 (en) * 2010-11-03 2013-08-15 Sgl Carbon Se Reinforced nonwoven fabric
WO2020212087A1 (en) 2019-04-18 2020-10-22 Teijin Carbon Europe Gmbh Wedge filler preform
US20220333280A1 (en) * 2019-09-06 2022-10-20 Green Petition Dis Ticaret Anonim Sirketi Textile products made of recycled fibers
US12031247B2 (en) * 2019-09-06 2024-07-09 Green Petition Dis Ticaret Anonim Sirketi Textile products made of recycled fibers

Also Published As

Publication number Publication date
BR112012031770A8 (pt) 2018-01-02
HK1181433A1 (zh) 2013-11-08
KR101497788B1 (ko) 2015-03-02
JP5745052B2 (ja) 2015-07-08
CN103025940A (zh) 2013-04-03
JP2013540902A (ja) 2013-11-07
KR20130042504A (ko) 2013-04-26
JP5718462B2 (ja) 2015-05-13
KR101494507B1 (ko) 2015-02-17
KR20130042506A (ko) 2013-04-26
CA2802301A1 (en) 2012-05-10
US9551098B2 (en) 2017-01-24
PL2635417T3 (pl) 2016-04-29
CA2802315C (en) 2015-01-06
CA2802296C (en) 2015-03-24
JP2013534278A (ja) 2013-09-02
WO2012059540A1 (de) 2012-05-10
BR112012031770A2 (pt) 2017-02-21
CN103025942B (zh) 2016-10-05
PL2635732T3 (pl) 2015-10-30
EP2635732A1 (de) 2013-09-11
KR101577861B1 (ko) 2015-12-15
ES2544991T3 (es) 2015-09-07
MX336749B (es) 2016-01-29
EP2635417B1 (de) 2015-09-02
CN103025940B (zh) 2016-03-09
WO2012059538A1 (de) 2012-05-10
CA2802315A1 (en) 2012-05-10
JP2013535588A (ja) 2013-09-12
US20130287991A1 (en) 2013-10-31
CN103025942A (zh) 2013-04-03
CA2802296A1 (en) 2012-05-10
MX2012014598A (es) 2013-02-07
WO2012059539A1 (de) 2012-05-10
ES2554928T3 (es) 2015-12-28
CA2802301C (en) 2016-04-26
JP5728577B2 (ja) 2015-06-03
MX2012014614A (es) 2013-02-07
EP2635417A1 (de) 2013-09-11
KR20130054968A (ko) 2013-05-27
US20130209725A1 (en) 2013-08-15
CN103025494A (zh) 2013-04-03
PT2635417E (pt) 2015-12-22
MX2012014612A (es) 2013-02-07
EP2635733A1 (de) 2013-09-11
EP2635732B1 (de) 2015-05-13

Similar Documents

Publication Publication Date Title
CA2802315C (en) Pile layer with carbon-fiber encompassing bundles
KR102253933B1 (ko) 부분 분섬 섬유 다발과 그의 제조 방법, 및 부분 분섬 섬유 다발을 사용한 섬유 강화 수지 성형 재료와 그의 제조 방법
TWI529273B (zh) 縫合的多軸防皺布
DE60107223T2 (de) Herstellung von fasermatte aus gehackten strängen
EP2759387B1 (en) Reinforced fiber / resin fiber composite, and method for manufacturing same
DE112009001838T5 (de) Verfahren zur Verbesserung der Anpassungsfähigkeit eines ungekräuselten Geleges und mit derartigen Verfahren hergestellte konturierte Verbundwerkstoffkomponenten
JP6944658B2 (ja) 繊維強化樹脂成形品およびその圧縮成形方法
KR20190016977A (ko) 부분 분섬 섬유 다발과 그의 제조 방법, 및 부분 분섬 섬유 다발을 사용한 섬유 강화 수지 성형 재료와 그의 제조 방법
HUE035531T2 (en) Steel Stranded Reinforced Composites
KR102253276B1 (ko) 부분 분섬 섬유 다발과 그의 제조 방법, 및 부분 분섬 섬유 다발을 사용한 섬유 강화 수지 성형 재료와 그의 제조 방법
RU2365687C1 (ru) Нетканый иглопробивной материал и способ его изготовления
KR102253926B1 (ko) 부분 분섬 섬유 다발의 제조 방법과 부분 분섬 섬유 다발, 및 부분 분섬 섬유 다발을 사용한 섬유 강화 수지 성형 재료와 그의 제조 방법
CN106739196B (zh) 复合土工布及其制备方法和制造设备
TWI696733B (zh) 混纖絲線的製造方法、混纖絲線及織物或編物的製造方法
EP1111110A2 (en) Reinforced panel structure
DE19907350A1 (de) Textile Matte, Verfahren und Vorrichtung zu deren Herstellung
WO2014128149A1 (de) Faserbasierte trägerstruktur für flüssigkeiten und feststoffpartikel
EP3022087B1 (de) Unterkonstruktion für eine fussmatte
CN113795620A (zh) 具有不连续中间层的多轴织物
DE102005049784A1 (de) Verfahren zur Herstellung eines in seinen Festigkeitseigenschaften variabel definierbaren Spinnvliesstoffes

Legal Events

Date Code Title Description
AS Assignment

Owner name: SGL CARBON SE, GERMANY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:REITER, BIRGIT;DANZER, MARTIN;REEL/FRAME:029606/0419

Effective date: 20121212

AS Assignment

Owner name: SGL AUTOMOTIVE CARBON FIBERS GMBH & CO. KG, GERMAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SGL CARBON SE;REEL/FRAME:039124/0316

Effective date: 20130809

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION