Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
  • H01M4/1315—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx containing halogen atoms, e.g. LiCoOxFy
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
  • C01G51/00—Compounds of cobalt
  • C01G51/006—Compounds containing, besides cobalt, two or more other elements, with the exception of oxygen or hydrogen
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
  • C01G51/00—Compounds of cobalt
  • C01G51/40—Cobaltates
  • C01G51/42—Cobaltates containing alkali metals, e.g. LiCoO2
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
  • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/04—Processes of manufacture in general
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
  • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
  • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/50—Solid solutions
  • C01P2002/52—Solid solutions containing elements as dopants
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
  • C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
  • C01P2002/74—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by peak-intensities or a ratio thereof only
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/01—Particle morphology depicted by an image
  • C01P2004/03—Particle morphology depicted by an image obtained by SEM
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/30—Particle morphology extending in three dimensions
  • C01P2004/32—Spheres
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/30—Particle morphology extending in three dimensions
  • C01P2004/45—Aggregated particles or particles with an intergrown morphology
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/51—Particles with a specific particle size distribution
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/54—Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/11—Powder tap density
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/12—Surface area
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/40—Electric properties
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
  • H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
  • H01M10/0565—Polymeric materials, e.g. gel-type or solid-type
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M2004/021—Physical characteristics, e.g. porosity, surface area
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
  • H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/36—Selection of substances as active materials, active masses, active liquids
  • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
  • H01M4/485—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries

Definitions

• the present invention relates to a positive electrode active material for a lithium secondary battery, which has a large volume capacity density and high safety and is excellent in the charge and discharge cyclic durability, a positive electrode for a lithium secondary battery employing it, and a lithium secondary battery.
• a non-aqueous electrolyte secondary battery such as a lithium secondary battery which is small in size and light in weight and has a high energy density
• a positive electrode active material for the non-aqueous electrolyte secondary battery a composite oxide of lithium and a transition metal such as LiCoO 2 , LiNiO 2 , LiNi 0.8 Co 0.2 O 2 , LiMn 2 O 4 or LiMnO 2 , has been known.
• a lithium secondary battery using a lithium-cobalt composite oxide (LiCoO 2 ) as a positive electrode active material and using a lithium alloy or carbon such as graphite or carbon fiber as a negative electrode can obtain a high voltage at a level of 4V, whereby it has been widely used as a battery having a high energy density.
• LiCoO 2 lithium-cobalt composite oxide
• the average particle size of LiCoO 2 as a positive electrode active material be from 3 to 9 ⁇ m
• the volume occupied by a group of particles having a particle size of from 3 to 15 ⁇ m be at least 75% of the total volume
• the positive electrode active material is preferably one which does not substantially have such a particle size distribution that the particle size of LiCoO 2 is 1 ⁇ m or smaller or 25 ⁇ m or larger.
• the coating properties and the cyclic properties have been improved, but, the safety, the volume capacity density and the weight capacity density, have not yet been fully satisfactory.
• JP-A-2000-82466 proposes a positive electrode active material wherein the average particle size of lithium-cobalt composite oxide particles is from 0.1 to 50 ⁇ m, and at least two peaks are present in the particle size distribution. Further, it has been proposed to mix two types of positive electrode active materials having different average particle sizes to prepare a positive electrode active material wherein at least two peaks are present in the particle size distribution.
• JP-A-3-201368 proposes to replace 5 to 35% of Co atoms with W, Mn, Ta, Ti or Nb to improve the cyclic properties.
• JP-A-10-312805 proposes to use hexagonal LiCoO 2 as a positive electrode active material to improve the cyclic properties, wherein the c axis length of the lattice constant is at most 14.051 ⁇ , and the crystal lattice size of (110) direction of the crystal lattice is from 45 to 100 nm.
• JP-A-10-72219 proposes that a lithium-cobalt composite oxide of the formula Li x Ni 1-y N y O 2 (wherein 0 ⁇ x ⁇ 1.1, 0 ⁇ y ⁇ 1), of which the primary particles are plate-like or columnar, the ratio of (volume basis cumulative 95% size-volume basis cumulative 5% size)/(volume basis cumulative 5% size) is at most 3, and further, the average particle size is from 1 to 50 ⁇ m, has a high initial discharge capacity per weight and further is excellent in the charge and discharge cyclic durability.
• the present invention is essentially directed to the following.
• M is a transition metal element other than Co or an alkaline earth metal element, 0.9 ⁇ p ⁇ 1.1, 0.9
• M is at least one member selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Mn, Mg, Ca, Sr, Ba and Al.
• the positive electrode active material according to the above (1) or (2), wherein the average particle size D50 is from 5 to 15 ⁇ m, the specific surface area is from 0.3 to 0.7 m 2 /g, the half value width of the diffraction peak on (110) plane at 2 ⁇ 66.5 ⁇ 1° is from 0.07 to 0.14° as measured by X-ray diffraction using CuK ⁇ as a radiation source, and the press density is from 3.1 to 3.4 g/cm 3 .
• a process for producing the positive electrode active material for a lithium secondary battery as defined in any one of the above (1) to (3) which comprises firing, as a cobalt source, a mixture of substantially spherical large particle size cobalt hydroxide or tricobalt tetraoxide having such a sharp particle size distribution that the average particle size D50 is from 7 to 20 ⁇ m, the average particle size D10 is at least 50% of the average particle size D50, and the average particle size D90 is at most 150% of the average particle size D50, and small particle size cobalt hydroxide or tricobalt tetraoxide having an average particle size D50 of from 10 to 30% of the average particle size D50 of the large particles, in a proportion of from 9:1 to 1:2 as the cobalt atomic ratio, at a temperature of from 700° C. to 1050° C. in an oxygen-containing atmosphere.
• each of the large particle size cobalt hydroxide or tricobalt tetraoxide and the small particle size cobalt hydroxide or tricobalt tetraoxide has a specific surface area of from 2 to 20 m 2 /g.
• a positive electrode for a lithium secondary battery which contains the positive electrode active material as defined in any one of the above (1) to (4).
• a positive electrode for a lithium secondary battery which contains a positive electrode active material produced by the production process as defined in any one of the above (5) to (15).
• a lithium secondary battery employing the positive electrode active material as defined in the above (16) or (17).
• the lithium-cobalt composite oxide for a positive electrode of a lithium secondary battery produced in the present invention is represented by the formula Li p Co x M y O z F a .
• M, p, x, y, z and a are as defined above.
• a is larger than 0, it is a composite oxide having some of its oxygen atoms substituted by fluorine atoms. In such a case, the safety of the obtained positive electrode active material will be improved.
• M is a transition metal element other than Co, or an alkaline earth metal.
• the transition metal element represents a transition metal of Group 4, Group 5, Group 6, Group 7, Group 8, Group 9, Group 10 or Group 11 of the Periodic Table.
• M is preferably at least one element selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Mg, Ca, Sr, Ba and Al.
• Ti, Zr, Hf, Mg or Al is preferred from the viewpoint of the volume development properties, the safety, the cyclic durability, etc.
• each of the element M and F is preferably present on the surface of the lithium cobalt oxide particles. If it is present in the interior of the particles, not only the effect of improving the battery characteristics tends to be small, but also the battery characteristics may decrease in some cases.
• the important battery characteristics such as the safety or the charge and discharge cyclic properties can be improved by an addition of a small amount without bringing about the reduction of the battery performance.
• the presence of these elements on the surface can be judged by carrying out a spectroscopic analysis such as a XPS analysis with respect to the positive electrode particles.
• the positive electrode for a lithium secondary battery of the present invention is a lithium-cobalt composite oxide having the above composition, comprising a mixture of substantially spherical first particles of lithium-cobalt composite oxide having such a sharp particle size distribution that the volume basis cumulative size D10 is at least 50% of the average particle size D50 and the volume basis cumulative size D90 is at most 150% of the average particle size D50, and second particles of lithium-cobalt composite oxide filling the space among the above lithium-cobalt composite oxide particles.
• the first particles are required to have a narrow particle size distribution so as to achieve a large volume capacity density.
• D10 is preferably at least 50%, particularly preferably at least 65% of the above D50, and D90 is preferably at most 150%, particularly preferably at most 135% of the above D50. Further, the surface of the first particles is preferably as smooth as possible.
• the average particle sizes D10, D50 and D90 are volume basis particle sizes with respect to the particle size of secondary particles formed by agglomeration and sintering of primary particles, and respectively mean the volume basis cumulative 10% size (D10), 50% size (D50) and 90% size (D90) as particle sizes at points 10%, 50% and 90% in a cumulative curve prepared by obtaining the particle size distribution on the basis of the volume and bringing the total volume to 100%.
• the particle size distribution can be obtained by a frequency distribution and cumulative volume distribution curve measured by a laser scattering particle size distribution measuring apparatus.
• the particles are sufficiently dispersed in an aqueous medium by e.g.
• the first particles being substantially spherical mean that the major axis/minor axis of the particles, i.e. the aspect ratio is preferably from 2/1 to 1/1, particularly preferably from 1.5/1 to 1/1.
• the first particles preferably have a shape as close to spheres as possible.
• the small particles of lithium-cobalt composite oxide do not necessarily have a specific shape but they may have various shapes such as spheres, columns and blocks.
• the mixture ratio of the first particles and the second particles is required to be from 1/2 to 9/1 on the basis of mass. If the mixture ratio of the former/the latter is lower than 1/2, the press density of the mixture tends to decrease, and on the other hand, if it is higher than 9/1, the press density of the mixture tends to decrease.
• the mixture ratio of the former/the latter is preferably from 6/4 to 85/15, particularly preferably from 7/3 to 8/2.
• the first particles are preferably large particles of lithium-cobalt composite oxide
• the second particles are preferably small particles of lithium-cobalt composite oxide.
• the large particles are required to have an average particle size D50 of from 7 to 20 ⁇ m and a substantially spherical shape. If the average particle size D50 is smaller than 7 ⁇ m, the press density of the mixed powder tends to be low, and on the other hand, if the average particle size D50 is larger than 20 ⁇ m, the discharge properties at a large current tend to decrease. Particularly, it tends to be difficult to achieve a volume capacity density.
• the average particle size D50 of the large particles is preferably from 9 to 15 ⁇ m, particularly preferably from 10 to 14 ⁇ m.
• the small particles preferably have an average particle size D50 of from 10 to 30% of D50 of the above large particles. If the average particle size D50 of the small particles is smaller than 10% of D50 of the large particles, the press density of the mixture tends to decrease, and the safety tends to decrease. On the other hand, if it is larger than 30% of D50 of the large particles, the effect of improving the press density of the mixture tends to decrease. Accordingly, the average particle size D50 of the small particles is preferably from 15 to 25% of D50 of the large particles.
• the large particles and the small particles of lithium-cobalt composite oxide preferably have press densities of from 2.8 to 3.2 g/cm 3 and from 2.7 to 3.2 g/cm 3 , respectively.
• the press density means an apparent press density when the particle powder is press-compressed under a pressure of 0.3 t/cm 2 , unless otherwise specified. If the press density of the large particles or the small particles is lower than the above range, the press density of the mixture tends to decrease, and on the other hand, if it is higher than the above range, the discharge properties at a large current tend to decrease.
• the large particles and the small particles have press densities of from 2.9 to 3.1 g/cm 3 and from 2.8 to 3.0 g/cm 3 , respectively.
• the lithiuml composite oxide has a remaining alkali amount contained therein of preferably at most 0.02 mass %, particularly preferably at most 0.01 mass %.
• the positive electrode active material comprising the lithium-cobalt composite oxide of the present invention may be produced by various processes.
• One of preferred processes is that the first particles and the second particles of the lithium-cobalt composite oxide are produced and mixed, and the obtained mixture is pressed.
• the first particles and the second particles are produced by various methods, and the production methods are not particularly limited, however, they are produced preferably as follows. For example, a mixture containing a cobalt source, a lithium source, and an element M source and a fluorine source used as the case requires, is fired in an oxygen-containing atmosphere.
• the cobalt source may, for example, be tricobalt tetraoxide, cobalt oxyhydroxide or cobalt hydroxide
• the lithium source may, for example, be lithium carbonate or lithium hydroxide.
• the physical property values such as the size, the shape and the particle size distribution of the lithium-cobalt composite oxide particles to be produced can be controlled particularly by controlling the particle size, the particle shape, the particle size distribution and the specific surface area of the above cobalt source.
• a mixture comprising the obtained mixture and a lithium source, and a material of the element M and a fluorine source used as the case requires, added, is fired in an oxygen-containing atmosphere at from 700 to 1,050° C., particularly preferably from 900 to 1,000° C., for preferably from 5 to 20 hours.
• the large particles of cobalt hydroxide or tricobalt tetraoxide are required to have an average particle size D10 of at least 50% of the average particle size D50 and an average particle size D90 of at most 150% of the average particle size D50, whereby an effect of improving the press density of the positive electrode will be obtained.
• the large particles of cobalt hydroxide or tricobalt tetraoxide have a press density of from 1.7 to 3.0 g/cm 3 and that the small particles of cobalt hydroxide or tricobalt tetraoxide have a press density of from 1.7 to 3.0 g/cm 3 .
• each of the large particles and the small particles of cobalt hydroxide or tricobalt tetraoxide have a specific surface area of from 2 to 20 m 2 /g.
• the half value widths are within the above ranges, effects of improving the safety and the press density of the positive electrode will be obtained.
• Still another preferred process for producing the positive electrode active material comprising the lithium-cobalt composite oxide of the present invention is as follows. Namely, as a cobalt source, a mixture containing substantially spherical cobalt hydroxide or tricobalt tetraoxide having such a sharp particle size distribution that the average particle size D50 is from 7 to 20 ⁇ m, the average particle size D10 is at least 50% of the average particle size D50, the average particle size D90 is at most 150% of the average particle size D50, and the average particle size of secondary particles formed by agglomeration of primary particles is from 8 to 20 ⁇ m, and cobalt oxyhydroxide having an average particle size of secondary particles formed by agglomeration of primary particles of from 7 to 20 ⁇ m, in a proportion of from 5:1 to 1:5 as the cobalt atomic ratio, is used, and the mixture is fired in an oxygen-containing atmosphere at from 700 to 1,050° C.
• a cobalt source a mixture containing substantially
• the cobalt oxyhydroxide is required to have an average particle size of secondary particles formed by agglomeration of primary particles of from 7 to 20 ⁇ m, preferably from 9 to 14 ⁇ m. If the average particle size of the secondary particles is smaller than 7 ⁇ m, the press density of the positive electrode tends to decrease, and on the other hand, if it exceeds 20 ⁇ m, the large current discharge properties tend to decrease.
• the shape of the particles being substantially spherical includes a spherical shape, a rugby ball shape, a polygonal shape, etc.
• the major axis/minor axis, i.e. the aspect ratio is preferably from 3/1 to 1/1, particularly preferably from 2.0/1 to 1/1.
• the particles preferably have a shape as spherical as possible.
• the cobalt hydroxide or tricobalt tetraoxide to be mixed with the cobalt oxyhydroxide is required to have a substantially spherical shape with an average particle size of secondary particles formed by agglomeration of primary particles of from 7 to 20 ⁇ m, preferably from 9 to 15 ⁇ m. If the average particle size of the secondary particles is smaller than 8 ⁇ m, the press density of a lithiated product tends to decrease. On the other hand, if it exceeds 20 ⁇ m, the discharge properties at a large current may decrease, or a smooth electrode surface is hardly formed.
• the shape of such particles is also preferably substantially spherical.
• the cobalt hydroxide or tricobalt tetraoxide preferably has a narrow particle size distribution.
• the produced cobalt-lithium composite oxide has a press density higher than expected. It is considered to be because when the particle size distribution is narrow, the cobalt hydroxide or tricobalt tetraoxide itself is likely to be highly packed when a pressure is applied from the outside, and thus a high packing fraction of secondary particles can be obtained.
• the cobalt hydroxide or tricobalt tetraoxide has an average particle size D10 of at least 50%, preferably at least 65% of the average particle size D50, and an average particle size D90 of at most 150%, preferably at most 135% of the average particle size D50. Further, the cobalt hydroxide or the tricobalt tetraoxide preferably has a press density of from 1.2 to 2.5 g/cm 3 .
• the specific surface area is preferably from 2 to 30 m 2 /g, particularly preferably from 3 to 8 m 2 /g.
• the specific surface area is preferably from 2 to 10 m 2 /g, particularly preferably from 3 to 8 m 2 /g.
• a mixture containing the cobalt oxyhydroxide and the cobalt hydroxide or tricobalt tetraoxide is used as a cobalt source.
• the proportion of the former/the latter is from 5/1 to 1/5 on the basis of the cobalt atomic ratio. If the proportion is higher than 5/1, the press density of the positive electrode powder tends to decrease, and on the other hand, if it is lower than 1/5, the press density of the positive electrode powder tends to decrease.
• the proportion is preferably from 2/1 to 1/3.
• the cobalt oxyhydroxide, cobalt hydroxide and tricobalt tetraoxide having the above specific physical properties, to be used for production of the lithium-cobalt composite oxide of the present invention may be produced by various methods, and the production methods are not particularly limited.
• the cobalt oxyhydroxide is prepared by adding an oxidizing agent and caustic soda and ammonium hydroxide to an aqueous solution containing bivalent cobalt such as cobalt chloride or cobalt sulfate. Otherwise, it may be produced by a method of firstly preparing cobalt hydroxide without adding an oxidizing agent and then reacting an oxidizing agent.
• cobalt hydroxide by continuously mixing a mixture of an aqueous cobalt sulfate solution and ammonium hydroxide, with an aqueous sodium hydroxide solution, a slurry containing cobalt hydroxide can easily be produced. And, at that time, by changing reaction conditions such as the pH or stirring, the cobalt hydroxide having the physical properties of the present invention can be obtained. Further, the tricobalt tetraoxide is also produced, for example, by oxidizing the cobalt hydroxide, and at that time, by changing the crystal structure of the cobalt hydroxide as a material or the oxidizing conditions, various oxides may be produced.
• the lithium source is lithium carbonate. If a lithium source other than lithium carbonate, for example lithium hydroxide is used, the material will be expensive.
• the lithium carbonate is preferably in a form of a powder having an average particle size D50 of from 1 to 50 ⁇ m and a specific surface area of from 0.1 to 10 m 2 /g.
• a hydroxide, an oxide, a carbonate or a fluoride is preferably selected.
• a metal fluoride, LiF, MgF 2 etc. is selected.
• the lithium-cobalt composite oxide of the present invention has a remaining alkali amount contained therein, of preferably at most 0.03 mass %, particularly preferably at most 0.01 mass %.
• a carbon type conductive material such as acetylene black, graphite or Ketjenblack and a binding material are mixed with a powder of the composite oxide.
• the binding material preferably polyvinylidene fluoride, polytetrafluoroethylene, polyamide, carboxymethyl cellulose or acrylic resin may, for example, be used.
• the powder of the lithium-cobalt composite oxide, the conductive material and the binding material are formed into a slurry or a kneaded product by using a solvent or a dispersion medium, which is supported on a positive electrode current collector such as aluminum foil or stainless steel foil by e.g. coating to form a positive electrode plate for a lithium secondary battery.
• a porous polyethylene or a porous propylene film may be used as the separator.
• various solvents may be used as a solvent of the electrolyte solution of the battery.
• a carbonate ester is preferred.
• the carbonate ester each of a cyclic type and a chain type can be used.
• the cyclic carbonate ester propylene carbonate or ethylene carbonate (EC) may, for example, be mentioned.
• chain carbonate ester dimethyl carbonate, diethyl carbonate (DEC), ethyl methyl carbonate (EMC), methyl propyl carbonate or methyl isopropyl carbonate may, for example, be mentioned.
• the carbonate ester may be used alone or by mixing at least two types. Further, it may be used by mixing with another solvent. Further, according to the material of the negative electrode active material, if the chain carbonate ester is used together with the cyclic carbonate ester, there is a case where the discharge properties, the cyclic durability or the charge and discharge efficiency can be improved.
• a gel polymer electrolyte containing a vinylidene fluoride-hexafluoropropylene copolymer for example, KYNAR manufactured by ELF Atochem
• a vinylidene fluoride-perfluoropropyl vinyl ether copolymer may be employed.
• solute to be added to the electrolyte solvent or the polymer electrolyte at least one member of lithium salts is preferably used, wherein e.g.
• ClO 4 —, CF 3 SO 3 —, BF 4 —, PF 6 —, AsF 6 —, SbF 6 —, CF 3 CO 2 — or (CF 3 SO 2 ) 2 N— is anion. It is preferably added at a concentration of from 0.2 to 2.0 mol/L to the electrolyte solvent or the polymer electrolyte comprising the lithium salt. If the concentration departs from this range, ionic conductivity will decrease, and the electrical conductivity of the electrolyte will decrease. More preferably, it is from 0.5 to 1.5 mol/L.
• the negative electrode active material a material which can occlude and discharge lithium ions may be used.
• the material forming the negative electrode active material is not particularly limited, however, lithium metal, a lithium alloy, a carbon material, an oxide comprising, as a main body, a metal of Group 14 or Group 15 of the Periodic Table, a carbon compound, a silicon carbide compound, a silicone oxide compound, titanium sulfide or a boron carbide compound may, for example, be mentioned.
• the carbon material an organic material which is subjected to thermal decomposition under various thermal decomposition conditions, artificial graphite, natural graphite, soil graphite, exfoliated graphite or squamation graphite etc. can be used.
• the oxide a compound comprising tin oxide as a main body can be used.
• the negative electrode current collector a copper foil, a nickel foil etc. can be used. The negative electrode is produced preferably by kneading the active material with an organic solvent to form a slurry, which is coated on the metal foil current collector, dried and pressed.
• the shape of the lithium battery using the lithium-cobalt composite oxide of the present invention as the positive electrode active material is not particularly limited. Sheet, film, folding, winding type cylinder with bottom or button shape etc. is selected according to use.
• Examples 1 to 4, 10 to 13, 15 to 21 and 25 to 27 are Examples of the present invention, and Examples 5 to 9, 14 and 22 to 24 are Comparative Examples.
• the fired product was crushed, and the particle size distribution of the obtained large particle size LiCoO 2 powder formed by agglomeration of primary particles was measured by using a laser scattering type particle size distribution measuring apparatus and as a result, the average particle size D50 was 13.4 ⁇ m, D10 was 10.2 ⁇ m, and D90 was 17.4 ⁇ m, and a large particle size spherical LiCoO 2 powder having a specific surface area of 0.32 m 2 /g as obtained by BET method was obtained.
• the LiCoO 2 powder had D10/D50 of 76% and D90/D50 of 130%, and has a considerably narrow particle size distribution.
• a particulate cobalt hydroxide powder having average particle sizes D50 of 0.6 ⁇ m, D10 of 0.3 ⁇ m and D90 of 1.3 ⁇ m and a specific surface area of 17.1 m 2 /g, and a lithium carbonate powder having a specific surface area of 1.2 m 2 /g were mixed. They were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. After dry mixing of these two types of powders, the mixture was fired in the air atmosphere at 950° C. for 12 hours.
• the fired product was crushed, and the particle size distribution of the obtained small particle size LiCoO 2 powder was measured by using a laser scattering type particle size distribution measuring apparatus and as a result, the average particle size D50 was 2.6 ⁇ m, D10 was 1.5 ⁇ m and D90 was 5.6 ⁇ m, and an aggregated LiCoO 2 powder having a specific surface area of 0.53 m 2 /g as obtained by BET method was obtained.
• the above small particle size spherical LiCoO 2 powder will be referred to as “powder B”.
• the powder B had a D50 of 19% of D50 of the powder A.
• 60 Parts by weight of the powder A and 40 parts by weight of the powder B were mixed, and the obtained mixed powder was pressed by an oil hydraulic pressing machine under 0.3 t/cm 2 , whereupon the apparent density after pressing was 3.20 g/cm 3 .
• 10 g of the LiCoO 2 powder was dispersed in 100 g of pure water, and after filtration, the remaining alkali amount was obtained by potentiometric titration with 0.1 N HCl and found to be 0.02 wt %.
• the above LiCoO 2 mixed powder, acetylene black and a polyvinylidene fluoride powder were mixed in a mass ratio of 90/5/5, and N-methylpyrrolidone was added thereto to prepare a slurry, which was coated on one side of an aluminum foil having a thickness of 20 ⁇ m by using a Doctor Blade. After drying, roll press rolling was carried out once to prepare a positive electrode body sheet for a lithium battery. The density of the electrode layer was measured from the thickness of the positive electrode body after rolling and the weight per unit area of the electrode layer and found to be 3.37 g/cm 3 .
• One of these batteries employing the EC+DEC (1:1) solution as the electrolyte solution was charged up to 4.3 V at a load current of 75 mA per 1 g of the positive electrode active material at 250C, and discharged down to 2.5 V at a load current of 75 mA per 1 g of the positive electrode active material, whereby the initial discharge capacity was obtained. Further, the volume capacity density was obtained from the density of the electrode layer and the capacity per weight. With respect to this battery, the charge and discharge cycle test was further carried out 30 times. As a result, the initial volume capacity density of the positive electrode layer at 25° C.
• the other battery was charged for 10 hours at 4.3 V, and then broken down in the argon globe box.
• the positive electrode body sheet was picked up after charge, and after the positive electrode body sheet was washed, it was punched out at a radius of 3 mm, and then sealed in an aluminum capsule with EC. And then, it was heated at a rate of 5° C./min by using a scanning differential calorimeter, whereby the heat generation starting temperature was measured. As a result, the heat generation starting temperature of the 4.3 V charged product was 160° C.
• a mixed powder was obtained in the same manner as in Example 1 except that 80 parts by weight of the powder A and 20 parts by weight of the powder B were mixed.
• the mixed powder after pressing had an apparent density of 3.23 g/cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 160 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.5%
• the heat generation starting temperature was 163° C.
• a mixed powder was obtained in the same manner as in Example 1 except that 40 parts by weight of the powder A and 60 parts by weight of the powder B were mixed.
• the mixed powder after pressing had an apparent density of 3.13 g/cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 160 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.2%
• the heat generation starting temperature was 163° C.
• Example 1 a spherical cobalt hydroxide powder from a material having a different particle size distribution was used as the material cobalt hydroxide for large particles, instead of the powder A.
• the powder was mixed with lithium carbonate and fired, and the fired product was crushed, and the particle size distribution of the obtained large particle size LiCoO 2 powder was measured by using a laser scattering type particle size distribution measuring apparatus and as a result, the average particle size D50 was 13.0 ⁇ m, D10 was 7.9 ⁇ m and D90 was 18.9 ⁇ m, and a large particle size spherical LiCoO 2 powder having a specific surface area of 0.35 m 2 /g as obtained by BET method was obtained.
• This LiCoO 2 powder had D10/D50 of 61% and D90/D50 of 145%, and has a narrow particle size distribution.
• LiCoO 2 powder With respect to this LiCoO 2 powder, observation by an electron microscope at magnifications of 1,000 and 5,000 was carried out to measure the average of the proportion of the major axis to the minor axis (aspect ratio) of 500 spherical particles at each magnification. As a result, the average was 1.14, and the particles were found to have a shape close to spheres.
• the above large particle size spherical LiCoO 2 powder will be referred to as “powder E”.
• a mixed powder was obtained in the same manner as in Example 1 except that 60 parts by weight of the powder E and 40 parts by weight of the powder B were mixed.
• the powder B had a D50 of 20% of D50 of the powder E.
• the mixed powder after pressing had an apparent density of 3.14 g/cm 3 .
• Example 2 a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 160 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.4%
• the heat generation starting temperature was 161° C.
• Example 1 The apparent density after pressing obtained in the same manner as in Example 1 except that the powder A alone was used in Example 1 was 2.95 g/cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 160 mAh/g-LiCoO 2
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.1%
• the heat generation starting temperature of a 4.3 V charged product was 163° C.
• the apparent density after pressing obtained in the same manner as in Example 1 except that the powder B alone was used in Example 1 was 2.78 g ⁇ cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 159 mAh/g-LiCoO 2
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.0%
• the heat generation starting temperature of a 4.3 V charged product was 158° C.
• a mixed powder was obtained in the same manner as in Example 1 except that 20 parts by weight of the powder A and 80 parts by weight of the powder B were mixed in Example 1.
• the mixed powder after pressing had an apparent density of 3.03 g/cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 159 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.0%
• the heat generation starting temperature was 159° C.
• a mixed powder was obtained in the same manner as in Example 1 except that 95 parts by weight of the powder A and 5 parts by weight of the powder B were mixed in Example 1.
• the mixed powder after pressing had an apparent density of 3.05 g/cm 3 .
• a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 159 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.0%
• the heat generation starting temperature was 1580C.
• the apparent density after pressing obtained in the same manner as in Example 1 except that the powder E alone was used in Example 4 was 3.02 g/cm 3 . Further, by using this powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the weight capacity density was 159 mAh/g
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.0%
• the heat generation starting temperature was 160° C.
• cobalt hydroxide was used as small particle size cobalt hydroxide. As a result of observation by a scanning electron microscope of the small particle size cobalt hydroxide, it was found that aggregated secondary particles consisting of several to about twenty primary particles were formed.
• the cobalt hydroxide particles consisting of the secondary particles had a specific surface area of 2.4 m 2 /g, and had an apparent density of 2.21 g/cm 3 after pressed by an oil hydraulic pressing machine under 0.3 t/cm 2 .
• the particle size distribution of the powder of the secondary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 3.5 ⁇ m, D10 was 0.3 ⁇ m and D90 was 7.6 ⁇ m.
• a mixed liquid of an aqueous cobalt sulfate solution and ammonium hydroxide, and an aqueous caustic soda solution were continuously mixed to continuously synthesize a cobalt hydroxide slurry by a known method, and by means of aggregation, filtration and drying steps, a large particle size substantially spherical cobalt hydroxide powder was obtained.
• the particle size distribution of the powder of the secondary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 16.7 ⁇ m, D10 was 13.4 ⁇ m and D90 was 21.1 ⁇ m, and D10 was 80% of D50 and D90 was 126% of D50. Further, the specific surface area was 3.6 m 2 /g, the press density was 2.11 g/cm 3 , and as a result of observation by a scanning electron microscope, the powder was a cobalt hydroxide powder consisting of substantially spherical large particles formed by strong agglomeration of dozens or more needle primary particles. Further, the aspect ratio was obtained with respect to 500 particles and as a result, the proportion of major axis/minor axis was 1.20/1 on the average.
• the fired product was crushed, and the particle size distribution of the obtained LiCoO 2 powder formed by agglomeration of the primary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 14.6 ⁇ m, D10 was 12.1 ⁇ m and D90 was 18.0 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.37 m 2 /g as obtained by BET method was obtained.
• the LiCoO 2 powder had a press density of 3.27 g/cm 3 .
• the alkali content was 0.02 wt %.
• Example 2 By using the above LiCoO 2 powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial volume capacity density was 465 mAh/cm 3 electrode layer
• the initial weight capacity density was 160 mAh/g-LiCoO 2
• the capacity retention ratio after 30 times of charge and discharge cycle was 97.2
• the heat generation starting temperature was 161° C.
• Example 10 In the same manner as in Example 1 except that the mixture ratio of the large particle size cobalt hydroxide to the small particle size cobalt hydroxide was 50:50 (weight ratio) in Example 10, a LiCoO 2 powder was synthesized.
• the small particle size cobalt hydroxide had a D50 of 21% of D50 of the large particle size cobalt hydroxide.
• the cobalt hydroxide powders and the cobalt carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing.
• LiCoO 2 had average particle sizes D50 of 12.5 ⁇ m, D10 of 10.3 ⁇ m and D90 of 17.2 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.42 m 2 /g as obtained by BET method was obtained.
• an X-ray diffraction spectrum was obtained by using an X-ray diffraction apparatus (RINT 2100 manufactured by Rigaku Corporation).
• RINT 2100 manufactured by Rigaku Corporation
• the obtained LiCoO 2 powder had a press density of 3.24 g/cm 3 .
• Example 2 By using this powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 161 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.5%. Further, the heat generation starting temperature of a 4.3 V charged product was 162° C.
• Example 10 large particle size cobalt hydroxide was fired in the air atmosphere at a firing temperature of 900° C. for 12 hours to synthesize large particle size substantially spherical tricobalt tetraoxide.
• the average particle size D50 was 15.5 ⁇ m
• D10 was 12.8 ⁇ m
• D90 was 19.1 ⁇ m
• the specific surface area was 3.6 m 2 /g
• the press density was 2.30 g/cm 3
• the powder was a substantially spherical tricobalt tetraoxide powder formed by strong agglomeration of needle primary particles.
• Example 11 In the same manner as in Example 11 except that the substantially spherical large particle size tricobalt tetraoxide powder and the small particle size cobalt hydroxide of Example 11 were used, a LiCoO 2 powder was synthesized.
• the mixture ratio of the tricobalt tetraoxide powder to the small particle size cobalt hydroxide of Example 11 was 75:25 as the cobalt atomic ratio.
• the small particle size cobalt hydroxide had a D50 of 23% of D50 of the large particle size tricobalt tetraoxide.
• the cobalt hydroxide, the tricobalt tetraoxide and lithium carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing.
• LiCoO 2 had average particle sizes D50 of 14.3 ⁇ m, D10 of 11.5 ⁇ m and D90 of 18.1 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.40 m 2 /g as obtained by BET method was obtained.
• an X-ray diffraction spectrum was obtained by using an X-ray diffraction apparatus (RINT 2100 manufactured by Rigaku Corporation).
• RINT 2100 manufactured by Rigaku Corporation
• the obtained LiCoO 2 powder had a press density of 3.26 g/cm 3 .
• Example 2 By using this powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 161 mAh/g-LiCoO 2 , the capacity retention ratio after 30 times of charge and discharge cycle was 97%. Further, the heat generation starting temperature of a 4.3 V charged product was 164° C.
• Example 10 In the same manner as in Example 11 except that a titanium oxide powder and a lithium fluoride powder were further added when the two types of the cobalt hydroxide powders and the lithium carbonate powder were mixed in Example 10, a positive electrode active material was synthesized. As a result of elemental analysis, the positive electrode active material was found to be LiCo 0.997 Ti 0.003 O 1.998 F 0.002 .
• the fired product was crushed, and the particle size distribution of the obtained powder of the above composition, formed by agglomeration of primary particles, was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 13.2 ⁇ m, D10 was 10.1 ⁇ m and D90 was 16.3 ⁇ m, and a substantially spherical LiCoO 2 powder having a specific surface area of 0.48 m 2 /g as obtained by BET method was obtained.
• an X-ray diffraction spectrum was obtained by using an X-ray diffraction apparatus (RINT 2100 manufactured by Rigaku Corporation).
• RINT 2100 manufactured by Rigaku Corporation
• the powder had an apparent density of 3.26 g/cm 3 after pressed by an oil hydraulic pressing machine under 0.3 t/cm 2 .
• titanium and fluorine were found to be localized on the surface.
• the positive electrode had a remaining alkali amount of 0.02 mass %.
• Example 2 By using the above powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 161 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 99.5%. Further, the heat generation starting temperature of a 4.3 V charged product was 178° C.
• Example 12 LiCoO 2 was synthesized. The tricobalt tetraoxide and the cobalt carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. The obtained LiCoO 2 powder had an apparent density of 2.95 g/cm 3 after pressing. By using this powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured. The initial weight capacity density was 161 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.2%. Further, the heat generation starting temperature of a 4.3 V charged product was 162° C.
• a positive electrode active material was synthesized in the same manner as in Example 13 except that aluminum hydroxide was used instead of titanium oxide in Example 13. As a result of chemical analysis, the positive electrode active material was found to be LiCo 0.997 Al 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.25 g/cm 3 . Further, aluminum and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %.
• a positive electrode active material was synthesized in the same manner as in Example 13 except that magnesium hydroxide was used instead of titanium oxide in Example 13. As a result of chemical analysis, the positive electrode active material was found to be LiCo 0.997 Mg 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.25 g/cm 3 . Further, magnesium and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %.
• a positive electrode active material was synthesized in the same manner as in Example 13 except that zirconium oxide was used instead of titanium oxide in Example 13.
• the positive electrode active material was found to be LiCo 0.997 Zr 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.26 g/cm 3 Further, zirconium and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %.
• a positive electrode was produced, batteries were assembled, and the properties were measured. The initial capacity was 160 mAh/g, the capacity retention ratio after 30 cycles was 99.5%, and the heat generation starting temperature was 174° C.
• a mixed liquid of an aqueous cobalt sulfate solution and ammonium hydroxide and an aqueous caustic soda solution were continuously mixed to continuously synthesize a cobalt hydroxide slurry by a known method, and by means of agglomeration, filtration and drying steps, a cobalt hydroxide powder was obtained.
• the particle size distribution of the powder of secondary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 16.5 ⁇ m, D10 was 13.2 ⁇ m and D90 was 21.0 ⁇ m, and accordingly D10 was 80% of D50 and D90 was 127% of D50. Further, the tap density was 2.1 g/cm 3 , the press density was 2.11 g/cm 3 , and the powder was a substantially spherical cobalt hydroxide powder formed by strong agglomeration of needle primary particles. 500 Cobalt hydroxide particles were observed by a scanning electron microscope and as a result, the aspect ratio (proportion of major axis/minor axis) was 1.21, and the particles were substantially spherical.
• the tap density was obtained in accordance with the heavy bulk density as defined in JIS R9301-2-3.
• the above cobalt oxyhydroxide, the above cobalt hydroxide and a lithium carbonate powder having a specific surface area of 1.2 m 2 /g were mixed.
• the mixture ratio of the former cobalt oxyhydroxide to the latter cobalt hydroxide was 50:50 (cobalt atomic ratio), and these two types of the cobalt materials and the lithium carbonate powder were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. After dry mixing of these three types of powders, the mixture was fired in the air atmosphere at 950° C. for 12 hours.
• the fired product was crushed, and the particle size distribution of the obtained LiCoO 2 powder formed by agglomeration of primary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 11.5 ⁇ m, D10 was 7.6 ⁇ m and D90 was 18.5 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.37 m 2 /g as obtained by BET method was obtained.
• Example 2 By using the above LiCoO 2 powder, in the same manner as in Example 1 except that roll press rolling was carried out five times, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial volume capacity density was 513 mAh/cm 3 electrode layer
• the initial weight capacity density was 161 mAh/g-LiCoO 2
• the capacity retention ratio after 30 times of charge and discharge cycles was 97.3%.
• the heat generation starting temperature of a 4.3 V charged product was 162° C.
• Example 18 In the same manner as in Example 18 except that the mixture ratio of the former substantially spherical cobalt hydroxide to the latter cobalt oxyhydroxide was 75:25 (cobalt atomic ratio) in Example 18, a LiCoO 2 powder was synthesized. The cobalt hydroxide, the cobalt oxyhydroxide and the lithium carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. LiCoO 2 had average particle sizes D50 of 13.3 ⁇ m, D10 of 8.9 ⁇ m and D90 of 18.9 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.34 m 2 /g as obtained by BET method was obtained.
• Example 18 By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 163 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.4%. Further, the heat generation starting temperature of a 4.3 V charged product was 164° C.
• Example 18 the obtained former substantially spherical cobalt hydroxide was fired in the air atmosphere at 800° C. for 12 hours to synthesize substantially spherical tricobalt tetraoxide.
• the average particle size D50 was 15.0 ⁇ m
• D10 was 12.2 ⁇ m and D90 was 19.0 ⁇ m
• the specific surface area was 3.4 m 2 /g
• the tap density was 2.2 g/cm 3
• the press density was 2.30 g/cm 3
• the powder was a substantially spherical tricobalt tetraoxide powder formed by strong agglomeration of needle primary particles.
• the aspect ratio proportion of major axis to minor axis
• Example 18 In the same manner as in Example 18 except that the substantially spherical tricobalt tetraoxide powder and the cobalt oxyhydroxide of Example 18 were used, a LiCoO 2 powder was synthesized. The mixture ratio of the tricobalt tetraoxide powder to the cobalt oxyhydroxide of Example 18 was 1:1 by the weight ratio. The cobalt oxyhydroxide, the tricobalt tetraoxide and the lithium carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing.
• LiCoO 2 had average particle sizes D50 of 13.3 ⁇ m, D10 of 6.5 ⁇ m and D90 of 18.3 ⁇ m, and a LiCoO 2 powder having a specific surface area of 0.35 m 2 /g as obtained by BET method was obtained.
• Example 18 By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 162 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.3%. Further, the heat generation starting temperature of a 4.3 V charged product was 164° C.
• Example 18 In the same manner as in Example 18 except that an aluminum hydroxide powder and a lithium fluoride powder were further added when the substantially spherical cobalt hydroxide, the cobalt oxyhydroxide and the lithium carbonate were mixed in Example 18, a positive electrode active material was synthesized. As a result of elemental analysis, the positive electrode active material was found to be LiCo 0.997 Al 000.3 O 1.998 F 0.002 .
• the fired product was crushed, and the particle size distribution of the obtained powder formed by agglomeration of primary particles was measured by using a laser scattering type particle size distribution measuring apparatus employing water as a dispersion medium and as a result, the average particle size D50 was 13.2 ⁇ m, D10 was 7.3 ⁇ m and D90 was 18.3 ⁇ m, and the specific surface area was 0.52 m 2 /g as obtained by BET method.
• an X-ray diffraction spectrum was obtained by using an X-ray diffraction apparatus (RINT 2100 manufactured by Rigaku Corporation).
• RINT 2100 manufactured by Rigaku Corporation
• the power had a press density of 3.13 g/cm 3 .
• XPS spectral analysis
• Example 18 By using the above powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 160 mAh/g, and the capacity retention ratio after 30 times of charge and discharge cycle was 99.6%. Further, the heat generation starting temperature of a 4.3 V charged product was 178° C.
• Example 18 In the same manner as in Example 1 except that the former substantially spherical cobalt hydroxide was not used, and the latter cobalt oxyhydroxide alone was used as a cobalt source in Example 18, LiCoO 2 was synthesized. The cobalt oxyhydroxide and the cobalt carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. The obtained LiCoO 2 powder had a press density of 3.00 g/cm 3 .
• Example 18 By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 160 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.0%. Further, the heat generation starting temperature of a 4.3 V charged product was 163° C., and the initial volume capacity density was 490 mAh/cm 3 .
• Example 18 In the same manner as in Example 18 except that the latter cobalt oxyhydroxide was not used, and the former substantially spherical cobalt hydroxide alone was used as a cobalt source in Example 18, LiCoO 2 was synthesized. The cobalt hydroxide and the cobalt carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. The obtained LiCoO 2 powder had a press density of 2.95 g/cm 3 .
• Example 18 By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 161 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.5%. Further, the heat generation starting temperature of a 4.3 V charged product was 161° C.
• Example 20 In the same manner as in Example 20 except that the latter cobalt oxyhydroxide was not used, and the former tricobalt tetraoxide alone was used as a cobalt source in Example 20, LiCoO 2 was synthesized. The tricobalt tetraoxide and the cobalt carbonate were blended in such a mixture ratio that the composition would be LiCoO 2 after firing. The obtained LiCoO 2 powder had a press density of 2.93 g/cm 3 .
• Example 2 By using this powder, in the same manner as in Example 1, a positive electrode was produced, batteries were assembled, and the properties were measured.
• the initial weight capacity density was 161 mAh/g-LiCoO 2 , and the capacity retention ratio after 30 times of charge and discharge cycle was 97.1%. Further, the heat generation starting temperature of a 4.3 V charged product was 160° C.
• Example 21 In the same manner as in Example 21 except that titanium oxide was used instead of aluminum hydroxide in Example 21, a positive electrode active material was synthesized. As a result of chemical analysis, the positive electrode active material was found to be LiCo 0.997 Ti 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.12 g/cm 3 . Further, titanium and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %.
• Example 21 In the same manner as in Example 21 except that magnesium hydroxide was used instead of aluminum hydroxide in Example 21, a positive electrode active material was synthesized. As a result of chemical analysis, the positive electrode active material was found to be LiCo 0.997 Mg 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.13 g/cm 3 . Further, magnesium and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %. By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured. The initial capacity was 160 mAH/g, the capacity retention ratio after 30 cycles was 99.8%, and the heat generation starting temperature was 187° C.
• Example 21 In the same manner as in Example 21 except that zirconium oxide was used instead of aluminum hydroxide in Example 21, a positive electrode active material was synthesized. As a result of chemical analysis, the positive electrode active material was found to be LiCo 0.997 Zr 0.003 O 1.998 F 0.002 , and the powder had a press density of 3.12 g/cm 3 . Further, zirconium and fluorine were found to be present on the surface. The remaining alkali amount was 0.02 mass %. By using this powder, in the same manner as in Example 18, a positive electrode was produced, batteries were assembled, and the properties were measured. The initial capacity was 160 mAH/g, the capacity retention ratio after 30 cycles was 99.3%, and the heat generation starting temperature was 173° C.
• a positive electrode active material for a lithium secondary battery which has a large volume capacity density, has a high safety, is excellent in uniform coating properties, and is excellent in charge and discharge cyclic durability and low temperature characteristics, a positive electrode for a lithium secondary battery employing it, and a lithium secondary battery, are provided.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Inorganic Chemistry (AREA)
• Manufacturing & Machinery (AREA)
• Materials Engineering (AREA)
• Battery Electrode And Active Subsutance (AREA)
• Secondary Cells (AREA)

Priority Applications (2)

Applications Claiming Priority (5)

Related Child Applications (1)

Publications (1)

Family

ID=32044629

Family Applications (3)

Family Applications After (2)

Country Status (6)

Cited By (39)

Families Citing this family (33)

Citations (7)

Family Cites Families (18)

• 2003
  • 2003-09-25 KR KR1020067022575A patent/KR100895225B1/ko not_active IP Right Cessation
  • 2003-09-25 AU AU2003266620A patent/AU2003266620A1/en not_active Abandoned
  • 2003-09-25 CN CNB038224852A patent/CN100382363C/zh not_active Expired - Fee Related
  • 2003-09-25 KR KR1020047019838A patent/KR100700962B1/ko not_active IP Right Cessation
  • 2003-09-25 US US10/529,289 patent/US20060263690A1/en not_active Abandoned
  • 2003-09-25 WO PCT/JP2003/012259 patent/WO2004030125A1/ja active Application Filing
  • 2003-09-26 TW TW097103627A patent/TW200830619A/zh not_active IP Right Cessation
  • 2003-09-26 TW TW092126711A patent/TW200410438A/zh not_active IP Right Cessation
• 2008
  • 2008-07-18 US US12/175,652 patent/US7824803B2/en not_active Expired - Lifetime
• 2010
  • 2010-08-03 US US12/849,435 patent/US7981547B2/en not_active Expired - Fee Related

Patent Citations (7)

Also Published As

Similar Documents

Legal Events