- battery
- forming polymer
- separator
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
- H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
- H01M10/0565—Polymeric materials, e.g. gel-type or solid-type
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/403—Manufacturing processes of separators, membranes or diaphragms
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
- H01M50/417—Polyolefins
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
- H01M50/42—Acrylic resins
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
- H01M50/426—Fluorocarbon polymers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
- H01M50/457—Separators, membranes or diaphragms characterised by the material having a layered structure comprising three or more layers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
- H01M50/491—Porosity
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M2300/00—Electrolytes
- H01M2300/0085—Immobilising or gelification of electrolyte
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/46—Separators, membranes or diaphragms characterised by their combination with electrodes
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T29/00—Metal working
- Y10T29/49—Method of mechanical manufacture
- Y10T29/49002—Electrical device making
- Y10T29/49108—Electric battery cell making
- Y10T29/49115—Electric battery cell making including coating or impregnating
Definitions
- the invention is directed to a battery separator for lithium polymer or “gel” batteries.
- a lithium polymer battery or a lithium gel battery is known. See, for example, U.S. Patent Publication No. 2002/0168564A1 which is incorporated herein by reference. These lithium polymer batteries are different from lithium-ion secondary batteries. Two significant differences are: the use of a gel electrolyte versus the use of a liquid electrolyte, and the flexible packaging for containing the active battery elements versus the rigid can (button or cylindrical or prismatic) for containing the elements.
- the gel electrolyte separator is replaced with a gel polymer coated microporous membrane that is subsequently impregnated with a liquid electrolyte.
- the inclusion of the membrane overcomes the aforementioned problems with the gel electrolyte separator.
- the membranes can provide the shutdown capability and have the mechanical strength to withstand the rigors of the battery manufacturing process.
- Exemplary coated separators are described in U.S. Pat. Nos. 5,639,573; 5,681,357; 5,688,293; 5,750,284; 5,837,015; 5,853,916; 6,322,923; 6,328,770; 6,337,101; U.S. Patent Publication No. 2002/0168564; WO99/54953; WO01/39296; and WO01/39297, each is incorporated herein by reference.
- the separator comprises a microporous membrane having a coating.
- the coating is made from a mixture of a gel forming polymer, a plasticizer, and a solvent.
- the solvent dissolves the gel forming polymer and the plasticizer so that the mixture may be easily and evenly applied to the membrane. Also, the solvent is relatively volatile, compared to the other components, so that it may be easily removed.
- the remaining coated separator i.e., coating comprising gel forming polymer and plasticizer
- the plasticizer is the pore-forming agent.
- the plasticizer for example an ester-base phthalate or an organic carbonate, must be extracted to form the pores. This extraction step adds to the cost of the separator.
- a battery separator for a lithium battery has a microporous membrane and a coating thereon.
- the coating is made from a mixture of a gel forming polymer, a first solvent, and a second solvent.
- the first solvent is more volatile than the second solvent.
- the second solvent acts as a pore former for the gel-forming polymer.
- a battery comprises an anode, a cathode, a separator, and an electrolyte.
- the anode and cathode sandwich the separator.
- the electrolyte resides in the separator and is in electrochemical communication with the anode and cathode. These components are then sealed within a package.
- the components of this battery are conventional and well known. For example see: Linden, D., Handbook of Batteries, 2nd Edition, McGraw Hill, New York, N.Y. (1995) and Besenhard, J. O., Handbook of Battery Materials, Wiley-VCH, New York, N.Y. (1999).
- a lithium polymer (or gel) battery is known. See Linden, Ibid., pgs. 36.37-36.42, Besenhard, Ibid., pgs. 513-517, U.S. Pat. Nos. 5,418,091; 5,456,000; and 5,460,904; each is incorporated herein by reference.
- the use of microporous membranes as part of the separator for a polymer battery is also known. See U.S. Pat. Nos.
- the separator for the gel polymer battery is a microporous membrane having a coating thereon.
- the coating will be discussed in greater detail after the following discussion of the microporous membrane.
- the microporous membrane refers to any suitable microporous membrane.
- the membrane may be a symmetric membrane or an asymmetric membrane.
- the membrane may be made from a polyolefin.
- Exemplary polyolefins include, but are not limited to, polyethylene (PE, including LDPE, LLDPE, HDPE), ultra high molecular weight polyethylene (UHMWPE), polypropylene (PP), polymethylpentene (PMP), copolymers of any of the foregoing, and mixtures thereof.
- the membrane may be made by either a dry stretch process (also known as the CELGARD® process) or a solvent extraction process (also known as the gel extrusion or phase separation or phase inversion process).
- the membrane may have the following characteristics: an air permeability (Gurley) of no more than 300 sec/100 cc (preferably ⁇ 200 sec/100 cc, most preferably ⁇ 150 sec/100 cc); a thickness ranging from 5 to 500 microns ( ⁇ ) (preferably 10 to 100 ⁇ , most preferably 10 to 50 ⁇ ); pore diameters ranging from 0.01 to 10 microns ( ⁇ ) (preferably 0.02 to 5 ⁇ , most preferably 0.02 to 0.5 ⁇ ); and a porosity ranging from 35 to 85% (preferably 40 to 80%).
- the membrane may be a single layer membrane, a tri-layer membrane (e.g., PP/PE/PP or PE/PP/PE), or a multi-layer membrane.
- the membrane is preferably a shutdown separator, for example see U.S. Pat. Nos. 4,650,730; 4,731,304; 5,281,491; 5,240,655; 5,565,281; 5,667,911; 5,952,120; Japanese Patent No. 2642206; and Japanese Patent Application Nos. 98395/1994 (filed May 12, 1994); 7/56320 (filed Mar. 15, 1995); and UK Patent Application No. 9604055.5 (filed Feb. 27, 1996); all of which are incorporated herein by reference.
- Suitable membranes are commercially available from Celgard Inc., Charlotte, N.C., USA; Asahi Chemical Industry Co. Ltd., Tokyo, Japan; Tonen Corporation, Tokyo, Japan; Ube Industries, Tokyo, Japan; Nitto Denko KK, Osaka, Japan; and Entek International, Lebanon, Oreg., USA.
- the coating is added to at least one external surface of the membrane.
- the coating is applied to both external surfaces of the membrane.
- the coating does not substantially (e.g., ⁇ 25% by volume) penetrate into the pores of membrane; most preferably, the coating does not penetrate into the pores.
- the surface density of the coating based upon the gel-forming polymer alone, ranges from 0.12 mg/cm 2 to 0.7 mg/cm 2 , preferably from 0.15 mg/cm 2 to 0.3 mg/cm 2 , and most preferably about 0.25 mg/cm 2 .
- the coating is intended to facilitate bonding of the laminate structure, namely the anode/separator/cathode structure. Additionally, the coating helps retain liquid electrolyte within the laminate structure and thereby reduces the risk of electrolyte leakage.
- the coating is applied to the membrane as a mixture of a gel forming polymer, a first solvent, and a second solvent.
- the gel-forming polymer described in greater detail below, facilitates bonding of the membrane to the electrodes and retention of the electrolyte within the laminate structure.
- the solvents both the first solvent and the second solvent, are preferably organic liquids having a vapor pressure of at least 760 mm Hg at a temperature of 150° C. or less.
- the first solvent described in greater detail below, is used to dissolve the gel forming polymer and second solvent. The first solvent allows the gel-forming polymer and second solvent to be intimately mixed and facilitates the even application of mixture over the surface of the membrane.
- the first solvent should be able to form at least a 20% solution of the other components.
- the first solvent also is easily driven out of the mixture.
- the first solvent has a boiling point of ⁇ 90° C. Easily driven off preferably refers to a solvent that will evaporate with little or no application of drying energy (e.g., heat).
- the second solvent described in greater detail below, is also referred to as the pore former for the gel-forming polymer; is a weaker solvent or a non-solvent when compared to the first solvent; and may swell the gel-forming polymer, but does not have to completely dissolve the gel-forming polymer. After the first solvent leaves the mixture, the remaining components form a non-porous coating on the surface of membrane.
- the second solvent When the second solvent is driven from the coating, a porous coating of gel forming polymer resides on the surface of the membrane.
- the second solvent is less volatile than the first solvent (i.e., it is not as easily driven off as the first solvent), so that it remains (or substantially remains) while the first solvent is removed.
- the second solvent has a boiling point of about 20° C. or more than the first solvent, preferably, about 30° C. or more above the first solvent.
- the second solvent has a boiling point no greater than about 150° C.
- the second solvent may be driven off by the application of drying energy (e.g., heat).
- the gel-forming polymer may be selected from, but is not limited to, polyvinylidene fluoride (PVDF); polyurethane, polyethylene oxide (PEO), polypropylene oxide (PPO); polyacrylonitrile (PAN), polyacrylamide, polymethylacrylate, polymethylmethacrylate, polyvinylacetate, polyvinylpyrrolidnone, polytetraethylene glycol diacrylate; copolymers of the foregoing, and combinations thereof.
- PVDF polyvinylidene fluoride
- PEO polyethylene oxide
- PPO polypropylene oxide
- PAN polyacrylonitrile
- polyacrylamide polymethylacrylate
- polymethylmethacrylate polyvinylacetate
- polyvinylpyrrolidnone polytetraethylene glycol diacrylate
- copolymers of the foregoing, and combinations thereof copolymers of the foregoing, and combinations thereof.
- One criteria for comonomer selection is the comonomer's ability to modify the
- Suitable comonomers include, but are not limited to, hexafluoropropylene (HFP), octofluoro-1-butane, octofluoroisobutane, and tetrafluoroethylene.
- the comonomer content preferably ranges from 3 to 20% by weight, preferably 7 to 15%.
- the gel-forming polymer is a copolymer of polyvinylidenefluoride.
- the PVDF copolymer is a copolymer of polyvinylidenefluoride and hexafluoropropylene (PVDF:HFP), and most preferred is PVDF:HFP with a weight ratio of 91:9.
- PVDF:HFP polyvinylidenefluoride and hexafluoropropylene
- the PVDF polymer and copolymers are commercially available from Atochem, Philadelphia, Pa., USA, Solvay SA, Brussels, Belgium, and Kureha Chemicals Industries, Ltd., Ibaraki, Japan.
- a preferred PVDF:HFP copolymer is KYNAR 2800 from Atochem.
- the first solvent may be selected from, but is not limited to, tetrahydrofuran, methylethylketone, acetone, low molecular weight glymes, and combinations thereof.
- the first solvent is the major component of the mixture that forms the coating.
- the mixture is a dilute solution, where the first solvent forms from 80-99% by weight of the mixture, preferably 85-95%, and most preferably 86-88%.
- the preferred first solvent is acetone.
- the second solvent is the pore former for the gel-forming polymer.
- the first solvent is more volatile than the second solvent (e.g., the second solvent has a lower vapor pressure at the same temperature than the first solvent).
- the second solvent may be selected from, but is not limited to, propanol, isopropanol, butanol, and mixture thereof.
- some water may be added.
- the weight ratio of gel forming polymer to second solvent may be 1:0.5 to 1:4, preferably in the range of 1:2 to 1:3.
- the water to second solvent ratio is in the range of 0.25:1 to 2:1, preferably 0.5:1.
- the second solvent is not a plasticizer.
- Plasticizers are, for example, phthalate based esters, cyclic carbonates, polymeric carbonates, and mixtures thereof.
- Phthalate-based esters are selected from, but are not limited to, dibutylphthalate.
- Cyclic carbonates are selected from, but not limited to, ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), and mixtures thereof.
- Polymeric carbonates are selected from, but are not limited to, polyvinylene carbonate and linear propylene carbonates.
- the mixture is prepared.
- the mixture may be applied to the membrane in any conventional manner, e.g., coating, immersion, spraying.
- the mixture is applied by a double side, dip coating process.
- the first solvent is allowed to evaporate, preferably without the use of heat.
- the second solvent is evaporated, preferably in an oven with the application of heat.
- Uniformity of resistance of the coated separator is of paramount importance to the battery manufacturer. Uniformity of resistance, as measured by McMullin Number, is controlled by controlling the relative humidity (% RH) during the coating process.
- the separator In the manufacture of a lithium polymer battery with the foregoing separator, prior to the lamination of the foregoing separator between the anode and the cathode, the separator should be treated with a solvent and/or plasticizer to plasticize (or soften) the coating, so that it can bond to the electrodes when they are laminated together. Lamination occurs by the application of heat and pressure usually applied via nip rollers.
- the treatment is preferably a solution comprising a plasticizer and a solvent. This solution preferably comprises between 10 to 30% by weight of plasticizer in the solution, most preferably 15 to 20%.
- the plasticizers include alkylene carbonates, dialkyl phthalates, dialkyl succinates, dialkyl adipates, dialkyl sebacates, trialkyl phosphates, polyalkylene glycol ethers, and mixtures thereof.
- the solvents include lower alcohols, ketones, esters, aliphatic hydrocarbons, halogenated solvents, chlorinates hydrocarbons, chlorinated fluorocarbons, and mixtures thereof.
- the solution may be applied in any conventional manner, such as coating, dipping, or spraying.
- the mixture comprised 280-285 pounds (127-130 kg) acetone; 8.5 pounds (3.8 kg) PVDF:HFP copolymer (Kynar FLEX® 2800 from Atofina Chemicals, Inc., Philadelphia, Pa.); 22.7 pounds (10.3 kg) isopropanol; and 11.3 pounds (5.1 kg) water.
- the mixture was applied by a double side, dip coating process. Add-on was controlled in the range of about 0.25 mg/cm 2 .
- Acetone was allowed to evaporate.
- the isopropanol/water was removed by evaporation in an oven.
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Electrochemistry (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Dispersion Chemistry (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- Cell Separators (AREA)
- Secondary Cells (AREA)
- Primary Cells (AREA)
Priority Applications (10)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/446,380 US20040241550A1 (en) | 2003-05-28 | 2003-05-28 | Battery separator for lithium polymer battery |
SG200401543A SG115647A1 (en) | 2003-05-28 | 2004-03-23 | Battery separator for lithium polymer battery |
CA002462294A CA2462294A1 (en) | 2003-05-28 | 2004-03-29 | Battery separator for lithium polymer battery |
TW093109520A TWI299587B (en) | 2003-05-28 | 2004-04-06 | Battery separator for lithium polymer battery |
CNB2004100354002A CN1309102C (zh) | 2003-05-28 | 2004-04-26 | 锂聚合物电池的电池隔板 |
EP20040011616 EP1482578A1 (en) | 2003-05-28 | 2004-05-15 | Battery separator for lithium polymer battery |
KR1020040037128A KR100628606B1 (ko) | 2003-05-28 | 2004-05-25 | 리튬 중합체 전지용 전지 격리판 |
JP2004158524A JP2004356102A (ja) | 2003-05-28 | 2004-05-28 | リチウムポリマー電池用の電池セパレータ |
US11/671,486 US7794511B2 (en) | 2003-05-28 | 2007-02-06 | Battery separator for lithium polymer battery |
JP2011044180A JP5309171B2 (ja) | 2003-05-28 | 2011-03-01 | リチウムポリマー電池用の電池セパレータ |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/446,380 US20040241550A1 (en) | 2003-05-28 | 2003-05-28 | Battery separator for lithium polymer battery |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/671,486 Division US7794511B2 (en) | 2003-05-28 | 2007-02-06 | Battery separator for lithium polymer battery |
Publications (1)
Publication Number | Publication Date |
---|---|
US20040241550A1 true US20040241550A1 (en) | 2004-12-02 |
Family
ID=33131562
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/446,380 Abandoned US20040241550A1 (en) | 2003-05-28 | 2003-05-28 | Battery separator for lithium polymer battery |
US11/671,486 Expired - Lifetime US7794511B2 (en) | 2003-05-28 | 2007-02-06 | Battery separator for lithium polymer battery |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/671,486 Expired - Lifetime US7794511B2 (en) | 2003-05-28 | 2007-02-06 | Battery separator for lithium polymer battery |
Country Status (8)
Country | Link |
---|---|
US (2) | US20040241550A1 (ja) |
EP (1) | EP1482578A1 (ja) |
JP (2) | JP2004356102A (ja) |
KR (1) | KR100628606B1 (ja) |
CN (1) | CN1309102C (ja) |
CA (1) | CA2462294A1 (ja) |
SG (1) | SG115647A1 (ja) |
TW (1) | TWI299587B (ja) |
Cited By (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070292750A1 (en) * | 2006-06-16 | 2007-12-20 | Kirby Beard | Optimized microporous structure of electrochemical cells |
US20080176139A1 (en) * | 2007-01-22 | 2008-07-24 | Physical Sciences Inc. | Three dimensional battery |
US20090208832A1 (en) * | 2008-02-17 | 2009-08-20 | Porous Power Technologies, Llc | Lamination Configurations for Battery Applications Using PVDF Highly Porous Film |
US20090226683A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Porous Material Uses in Furniture |
US20090223155A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Building Construction Applications for Porous Material |
US20090222995A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Bedding Applications for Porous Material |
US20090227163A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Protective Apparel with Porous Material Layer |
US20090291368A1 (en) * | 2007-08-17 | 2009-11-26 | Aron Newman | Carbon Foam Based Three-Dimensional Batteries and Methods |
US20100124702A1 (en) * | 2008-11-17 | 2010-05-20 | Physical Sciences, Inc. | High Energy Composite Cathodes for Lithium Ion Batteries |
US20100166961A1 (en) * | 2004-01-20 | 2010-07-01 | Beard Kirby W | Production of high porosity open-cell membranes |
US20100178567A1 (en) * | 2008-12-24 | 2010-07-15 | Porous Power Technologies, Llc | Mat Forming Spacers in Microporous Membrane Matrix |
US20100297489A1 (en) * | 2009-05-20 | 2010-11-25 | Porous Power Technolgies, Llc. | Treatment and Adhesive for Microporous Membranes |
CN102140762A (zh) * | 2011-01-10 | 2011-08-03 | 武汉理工大学 | 一种增强型纳米纤维多孔膜及其制备方法 |
US20110229768A1 (en) * | 2008-12-19 | 2011-09-22 | Changzhou Zhongke Laifang Power Development Co., Ltd. | Microporous polymer membrane modified by aqueous polymer, manufacturing method and use thereof |
CN102270756A (zh) * | 2010-09-25 | 2011-12-07 | 上海市凌桥环保设备厂有限公司 | 锂离子电池用复合隔膜 |
US20120121967A1 (en) * | 2010-11-17 | 2012-05-17 | Sony Corporation | Non-Aqueous Electrolyte Battery |
EP2541645A3 (en) * | 2006-04-28 | 2013-08-28 | LG Chem, Ltd. | Separator for battery with gel polymer layer |
US20140038025A1 (en) * | 2012-07-31 | 2014-02-06 | Jeong-Ki Ha | Separator, lithium battery including the separator, and method of preparing the separator |
DE102013106021A1 (de) | 2013-06-10 | 2014-12-11 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Ungefüllte und gefüllte Gussmasse, insbesondere zur Herstellung beschichteter Metallfolien, und deren Verwendung für Elektroden oder Separatoren in Akkumulatoren |
US9269937B2 (en) | 2006-04-28 | 2016-02-23 | Lg Chem, Ltd. | Method for preparing separator for battery with gel polymer layer |
WO2016114849A1 (en) * | 2015-01-15 | 2016-07-21 | Google Inc. | Hybrid rechargeable battery |
US9711775B2 (en) | 2014-08-29 | 2017-07-18 | Sumitomo Chemical Company, Limited | Laminated body, separator, and nonaqueous secondary battery |
CN111244374A (zh) * | 2019-12-25 | 2020-06-05 | 武汉中兴创新材料技术有限公司 | 一种结构改进的涂层隔膜及其制备方法 |
US10700331B2 (en) | 2012-08-23 | 2020-06-30 | Samsung Sdi Co., Ltd. | Separator for rechargeable lithium battery |
CN112160166A (zh) * | 2020-09-28 | 2021-01-01 | 湘潭大学 | 一种聚丙烯腈/聚环氧乙烷复合纤维膜及其制备方法和应用 |
US11456456B2 (en) | 2016-06-23 | 2022-09-27 | United States Of America As Represented By The Secretary Of The Air Force | Bendable, creasable, and printable batteries with enhanced safety and high temperature stability—methods of fabrication, and methods of using the same |
Families Citing this family (45)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR20060038219A (ko) * | 2004-10-29 | 2006-05-03 | 주식회사 디지털텍 | 겔형 고분자 전해질의 제조 방법 및 이에 의하여 제조된겔형 고분자 전해질을 포함하는 전지 |
CA2602827A1 (en) * | 2005-03-31 | 2006-10-12 | Tonen Chemical Corporation | Microporous polyolefin membrane and method for producing the same |
US20110143184A1 (en) * | 2008-02-14 | 2011-06-16 | Firefly International Energy Group, Inc. | Battery with electrolyte diffusing separator |
JP5337549B2 (ja) | 2008-03-31 | 2013-11-06 | 日東電工株式会社 | 電池用セパレータとこれを用いてなる電池 |
JP5337550B2 (ja) * | 2008-03-31 | 2013-11-06 | 日東電工株式会社 | 電池用セパレータとこれを用いてなる電池 |
EP2111915A1 (en) * | 2008-04-24 | 2009-10-28 | Tonen Chemical Corporation | Microporous polymeric membrane, battery separator and battery |
JP2009295483A (ja) * | 2008-06-06 | 2009-12-17 | Du Pont Teijin Advanced Paper Kk | 薄葉材、その製造方法およびそれを用いた電気・電子部品 |
CN101409366B (zh) * | 2008-11-19 | 2010-09-15 | 江苏双登集团有限公司 | 一种凝胶聚合物锂离子电池的制造方法 |
JP2013503456A (ja) * | 2009-08-31 | 2013-01-31 | ポーラス パワー テクノロジーズ,エルエルシー | 積層アセンブリを用いる電池の製造 |
JP5495210B2 (ja) * | 2010-07-21 | 2014-05-21 | 東レバッテリーセパレータフィルム株式会社 | 複合多孔質膜、複合多孔質膜の製造方法並びにそれを用いた電池用セパレーター |
CN101894933A (zh) * | 2010-08-06 | 2010-11-24 | 天津力神电池股份有限公司 | 一种新型锂离子电池隔膜的制作方法 |
US10451897B2 (en) | 2011-03-18 | 2019-10-22 | Johnson & Johnson Vision Care, Inc. | Components with multiple energization elements for biomedical devices |
US9196920B2 (en) | 2011-10-18 | 2015-11-24 | Johnson Controls Technology Llc | Electrochemical cell having a safety device |
US8857983B2 (en) | 2012-01-26 | 2014-10-14 | Johnson & Johnson Vision Care, Inc. | Ophthalmic lens assembly having an integrated antenna structure |
US20140030606A1 (en) * | 2012-03-12 | 2014-01-30 | Hitachi, Ltd. | Separator for electrochemical device, method for producing the same, and electrochemical device |
US9177721B2 (en) | 2012-03-14 | 2015-11-03 | Rutgers, The State University Of New Jersey | Electrochemical devices and methods of fabrication |
KR101529210B1 (ko) * | 2012-09-10 | 2015-06-17 | 주식회사 엘지화학 | 리튬 이차 전지용 분리막과, 이를 포함하는 리튬 이차 전지 |
CN103531735B (zh) * | 2013-09-22 | 2015-12-02 | 佛山市金辉高科光电材料有限公司 | 一种锂离子电池用聚烯烃多层微多孔膜及其制备方法 |
KR20170009838A (ko) | 2014-05-20 | 2017-01-25 | 데이진 가부시키가이샤 | 비수계 이차전지용 세퍼레이터, 그 제조 방법 및 비수계 이차전지 |
US10627651B2 (en) | 2014-08-21 | 2020-04-21 | Johnson & Johnson Vision Care, Inc. | Methods and apparatus to form biocompatible energization primary elements for biomedical devices with electroless sealing layers |
US9715130B2 (en) | 2014-08-21 | 2017-07-25 | Johnson & Johnson Vision Care, Inc. | Methods and apparatus to form separators for biocompatible energization elements for biomedical devices |
US10361404B2 (en) | 2014-08-21 | 2019-07-23 | Johnson & Johnson Vision Care, Inc. | Anodes for use in biocompatible energization elements |
US9383593B2 (en) | 2014-08-21 | 2016-07-05 | Johnson & Johnson Vision Care, Inc. | Methods to form biocompatible energization elements for biomedical devices comprising laminates and placed separators |
US10381687B2 (en) * | 2014-08-21 | 2019-08-13 | Johnson & Johnson Vision Care, Inc. | Methods of forming biocompatible rechargable energization elements for biomedical devices |
US9941547B2 (en) | 2014-08-21 | 2018-04-10 | Johnson & Johnson Vision Care, Inc. | Biomedical energization elements with polymer electrolytes and cavity structures |
US9793536B2 (en) | 2014-08-21 | 2017-10-17 | Johnson & Johnson Vision Care, Inc. | Pellet form cathode for use in a biocompatible battery |
US9599842B2 (en) | 2014-08-21 | 2017-03-21 | Johnson & Johnson Vision Care, Inc. | Device and methods for sealing and encapsulation for biocompatible energization elements |
US10361405B2 (en) | 2014-08-21 | 2019-07-23 | Johnson & Johnson Vision Care, Inc. | Biomedical energization elements with polymer electrolytes |
CN107210414A (zh) | 2015-03-24 | 2017-09-26 | 帝人株式会社 | 非水系二次电池用隔膜及非水系二次电池 |
CN105679984A (zh) * | 2016-03-29 | 2016-06-15 | 浙江地坤键新能源科技有限公司 | 一种无孔隔膜及其应用 |
US10056590B2 (en) | 2016-08-31 | 2018-08-21 | GM Global Technology Operations LLC | Methods of making separators for lithium ion batteries |
US10680222B2 (en) | 2017-12-19 | 2020-06-09 | GM Global Technology Operations LLC | Method of making thermally-stable composite separators for lithium batteries |
US11094925B2 (en) | 2017-12-22 | 2021-08-17 | Zenlabs Energy, Inc. | Electrodes with silicon oxide active materials for lithium ion cells achieving high capacity, high energy density and long cycle life performance |
CN108636737A (zh) * | 2018-04-12 | 2018-10-12 | 连云港海创电子科技有限公司 | 一种聚合物动力锂离子电池材料的转移涂覆式防腐方法 |
CN110444803A (zh) * | 2018-05-03 | 2019-11-12 | 苏州华骞时代新能源科技有限公司 | 一种半固态的锂离子电池结构及其制备方法 |
US11380935B2 (en) | 2018-05-31 | 2022-07-05 | Kureha Corporation | Resin composition for nonaqueous electrolyte secondary battery, separator for nonaqueous electrolyte secondary battery using same, resin composition for electrode mixture layer, electrode for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery |
CN108682863B (zh) * | 2018-06-11 | 2020-12-18 | 珠海辰玉新材料科技有限公司 | 一种锂电池聚合物凝胶电解质 |
CN111732858A (zh) * | 2019-03-19 | 2020-10-02 | 河北金力新能源科技股份有限公司 | 油系pvdf喷涂浆料、涂覆有油系pvdf喷涂浆料的隔膜及其制备方法和应用 |
US11973178B2 (en) | 2019-06-26 | 2024-04-30 | Ionblox, Inc. | Lithium ion cells with high performance electrolyte and silicon oxide active materials achieving very long cycle life performance |
CN112151788B (zh) | 2019-06-26 | 2024-10-01 | 伊翁布洛克斯有限公司 | 具有高性能电解质和氧化硅活性材料的锂离子电池 |
CN110429228B (zh) * | 2019-08-15 | 2022-04-19 | 宁德卓高新材料科技有限公司 | 具有高粘结性聚合物涂膜的复合隔膜的制备方法 |
CN110444718B (zh) * | 2019-08-15 | 2022-04-19 | 宁德卓高新材料科技有限公司 | 具有高粘结性聚合物涂膜的陶瓷复合隔膜的制备方法 |
JP7303987B2 (ja) * | 2020-03-06 | 2023-07-06 | トヨタ自動車株式会社 | セパレータ一体型電極の製造方法 |
JP7237049B2 (ja) | 2020-10-15 | 2023-03-10 | プライムプラネットエナジー&ソリューションズ株式会社 | 樹脂多孔質体の製造方法 |
US12006387B1 (en) | 2022-11-14 | 2024-06-11 | Piersica, Inc. | Polymer composition and methods for making same |
Citations (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US168564A (en) * | 1875-10-11 | Improvement in brick-machines | ||
US4464238A (en) * | 1983-05-09 | 1984-08-07 | The Dow Chemical Company | Porous separators for electrolytic processes |
US4650730A (en) * | 1985-05-16 | 1987-03-17 | W. R. Grace & Co. | Battery separator |
US5240655A (en) * | 1991-12-20 | 1993-08-31 | W. R. Grace & Co.-Conn. | Process of making a battery separator |
US5281491A (en) * | 1991-12-20 | 1994-01-25 | W. R. Grace & Co. | Battery separator |
US5418091A (en) * | 1993-03-05 | 1995-05-23 | Bell Communications Research, Inc. | Polymeric electrolytic cell separator membrane |
US5456000A (en) * | 1993-03-05 | 1995-10-10 | Bell Communications Research, Inc. | Method of making an electrolyte activatable lithium-ion rechargeable battery cell |
US5518838A (en) * | 1995-08-10 | 1996-05-21 | Motorola, Inc. | Electrochemical cell having solid polymer electrolyte and asymmetric inorganic electrodes |
US5565281A (en) * | 1994-12-02 | 1996-10-15 | Hoechst Celanese Corporation | Shutdown, bilayer battery separator |
US5631103A (en) * | 1996-09-27 | 1997-05-20 | Motorola, Inc. | Highly filled solid polymer electrolyte |
US5639573A (en) * | 1995-08-24 | 1997-06-17 | Motorola, Inc. | Polymer gel electrolyte |
US5716421A (en) * | 1997-04-14 | 1998-02-10 | Motorola, Inc. | Multilayered gel electrolyte bonded rechargeable electrochemical cell and method of making same |
US5750284A (en) * | 1997-01-08 | 1998-05-12 | Motorola, Inc. | Electrolyte composition for rechargeable electrochemical cells |
US5849433A (en) * | 1997-03-10 | 1998-12-15 | Motorola, Inc. | Polymer blend electrolyte system and electrochemical cell using same |
US5853916A (en) * | 1996-10-28 | 1998-12-29 | Motorola, Inc. | Multi-layered polymeric gel electrolyte and electrochemical cell using same |
US5952120A (en) * | 1997-04-15 | 1999-09-14 | Celgard Llc | Method of making a trilayer battery separator |
US6322923B1 (en) * | 1998-01-30 | 2001-11-27 | Celgard Inc. | Separator for gel electrolyte battery |
US6328770B1 (en) * | 1999-11-23 | 2001-12-11 | Valence Technology (Nevada), Inc. | Method of making multi-layer electrochemical cell devices |
US6337101B1 (en) * | 1999-11-23 | 2002-01-08 | Valence Technology (Nevada), Inc. | Method of treating separator for use in electrochemical cell devices |
US20020110732A1 (en) * | 2000-12-20 | 2002-08-15 | Polystor Corporation | Battery cell fabrication process |
US20020187401A1 (en) * | 2000-08-12 | 2002-12-12 | Seung-Jin Lee | Multi-component composite film method for preparing the same |
US20030157408A1 (en) * | 2001-12-28 | 2003-08-21 | Luying Sun | Microporous membrane and its uses thereof |
US6881438B2 (en) * | 2000-03-07 | 2005-04-19 | Teijin Limited | Process for production of composite porous film |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2642206B2 (ja) | 1989-12-28 | 1997-08-20 | 旭化成工業株式会社 | 防爆型二次電池 |
US5667911A (en) | 1994-11-17 | 1997-09-16 | Hoechst Celanese Corporation | Methods of making cross-ply microporous membrane battery separator, and the battery separators made thereby |
JPH08244152A (ja) | 1995-03-15 | 1996-09-24 | Nitto Denko Corp | 多孔質フィルムおよびその製造法 |
JPH08250097A (ja) | 1995-03-15 | 1996-09-27 | Kureha Chem Ind Co Ltd | 電気化学的装置用極間セパレーター |
US5688293A (en) | 1996-05-15 | 1997-11-18 | Motorola, Inc. | Method of making a gel electrolyte bonded rechargeable electrochemical cell |
US5681357A (en) | 1996-09-23 | 1997-10-28 | Motorola, Inc. | Gel electrolyte bonded rechargeable electrochemical cell and method of making same |
US5665265A (en) | 1996-09-23 | 1997-09-09 | Motorola, Inc., | Non woven gel electrolyte for electrochemical cells |
FR2766295B1 (fr) * | 1997-07-17 | 1999-09-24 | Alsthom Cge Alcatel | Separateur polymerique, procede de fabrication et generateur electrochimique le comprenant |
US5837015A (en) | 1997-09-26 | 1998-11-17 | Motorola, Inc. | Method of making a multilayered gel electrolyte bonded rechargeable electrochemical cell |
US6753114B2 (en) | 1998-04-20 | 2004-06-22 | Electrovaya Inc. | Composite electrolyte for a rechargeable lithium battery |
EP1243038A1 (en) | 1999-11-23 | 2002-09-25 | Valence Technology (Nevada), Inc. | Multi-layer electrochemical cell devices |
US6579643B1 (en) | 1999-11-23 | 2003-06-17 | Valence Technology, Inc. | Separator having a plasticizer coating for use in electrochemical cell devices |
AU2001236687A1 (en) * | 2000-02-04 | 2001-08-14 | Amtek Research International Llc | Freestanding microporous separator including a gel-forming polymer |
JP4449164B2 (ja) * | 2000-05-16 | 2010-04-14 | 株式会社デンソー | 非水電解液二次電池用電極およびその製造方法、並びに非水電解液二次電池 |
JP5156158B2 (ja) * | 2001-02-22 | 2013-03-06 | 東レバッテリーセパレータフィルム株式会社 | 複合膜およびその製造方法 |
US6881515B2 (en) | 2001-05-08 | 2005-04-19 | Celgard Inc. | Separator for polymer battery |
JP3984008B2 (ja) * | 2001-08-02 | 2007-09-26 | Tdk株式会社 | 電気化学デバイスの製造方法 |
JP4752993B2 (ja) * | 2001-09-10 | 2011-08-17 | 日産化学工業株式会社 | ポリイミド多孔質膜およびその製造法 |
AU2005254448A1 (en) * | 2004-01-20 | 2005-12-29 | Kirby W. Beard | Highly microporous polymers and methods for producing and using the same |
WO2007147167A2 (en) * | 2006-06-16 | 2007-12-21 | Porous Power Technologies, Llc | Optimized microporous structure of electrochemical cells |
-
2003
- 2003-05-28 US US10/446,380 patent/US20040241550A1/en not_active Abandoned
-
2004
- 2004-03-23 SG SG200401543A patent/SG115647A1/en unknown
- 2004-03-29 CA CA002462294A patent/CA2462294A1/en not_active Abandoned
- 2004-04-06 TW TW093109520A patent/TWI299587B/zh not_active IP Right Cessation
- 2004-04-26 CN CNB2004100354002A patent/CN1309102C/zh not_active Expired - Lifetime
- 2004-05-15 EP EP20040011616 patent/EP1482578A1/en not_active Withdrawn
- 2004-05-25 KR KR1020040037128A patent/KR100628606B1/ko active IP Right Review Request
- 2004-05-28 JP JP2004158524A patent/JP2004356102A/ja active Pending
-
2007
- 2007-02-06 US US11/671,486 patent/US7794511B2/en not_active Expired - Lifetime
-
2011
- 2011-03-01 JP JP2011044180A patent/JP5309171B2/ja not_active Expired - Fee Related
Patent Citations (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US168564A (en) * | 1875-10-11 | Improvement in brick-machines | ||
US4464238A (en) * | 1983-05-09 | 1984-08-07 | The Dow Chemical Company | Porous separators for electrolytic processes |
US4650730A (en) * | 1985-05-16 | 1987-03-17 | W. R. Grace & Co. | Battery separator |
US4731304A (en) * | 1985-05-16 | 1988-03-15 | W. R. Grace & Co. | Battery separator |
US5240655A (en) * | 1991-12-20 | 1993-08-31 | W. R. Grace & Co.-Conn. | Process of making a battery separator |
US5281491A (en) * | 1991-12-20 | 1994-01-25 | W. R. Grace & Co. | Battery separator |
US5418091A (en) * | 1993-03-05 | 1995-05-23 | Bell Communications Research, Inc. | Polymeric electrolytic cell separator membrane |
US5456000A (en) * | 1993-03-05 | 1995-10-10 | Bell Communications Research, Inc. | Method of making an electrolyte activatable lithium-ion rechargeable battery cell |
US5460904A (en) * | 1993-08-23 | 1995-10-24 | Bell Communications Research, Inc. | Electrolyte activatable lithium-ion rechargeable battery cell |
US5565281A (en) * | 1994-12-02 | 1996-10-15 | Hoechst Celanese Corporation | Shutdown, bilayer battery separator |
US5518838A (en) * | 1995-08-10 | 1996-05-21 | Motorola, Inc. | Electrochemical cell having solid polymer electrolyte and asymmetric inorganic electrodes |
US5604660A (en) * | 1995-08-10 | 1997-02-18 | Motorola, Inc. | Electrochemical cell having solid polymer electrolyte and asymmetric inorganic electrodes |
US5639573A (en) * | 1995-08-24 | 1997-06-17 | Motorola, Inc. | Polymer gel electrolyte |
US5631103A (en) * | 1996-09-27 | 1997-05-20 | Motorola, Inc. | Highly filled solid polymer electrolyte |
US5853916A (en) * | 1996-10-28 | 1998-12-29 | Motorola, Inc. | Multi-layered polymeric gel electrolyte and electrochemical cell using same |
US5750284A (en) * | 1997-01-08 | 1998-05-12 | Motorola, Inc. | Electrolyte composition for rechargeable electrochemical cells |
US5849433A (en) * | 1997-03-10 | 1998-12-15 | Motorola, Inc. | Polymer blend electrolyte system and electrochemical cell using same |
US5716421A (en) * | 1997-04-14 | 1998-02-10 | Motorola, Inc. | Multilayered gel electrolyte bonded rechargeable electrochemical cell and method of making same |
US5834135A (en) * | 1997-04-14 | 1998-11-10 | Motorola, Inc. | Multilayered gel electrolyte bonded rechargeable electrochemical cell |
US5952120A (en) * | 1997-04-15 | 1999-09-14 | Celgard Llc | Method of making a trilayer battery separator |
US6322923B1 (en) * | 1998-01-30 | 2001-11-27 | Celgard Inc. | Separator for gel electrolyte battery |
US6328770B1 (en) * | 1999-11-23 | 2001-12-11 | Valence Technology (Nevada), Inc. | Method of making multi-layer electrochemical cell devices |
US6337101B1 (en) * | 1999-11-23 | 2002-01-08 | Valence Technology (Nevada), Inc. | Method of treating separator for use in electrochemical cell devices |
US6881438B2 (en) * | 2000-03-07 | 2005-04-19 | Teijin Limited | Process for production of composite porous film |
US20020187401A1 (en) * | 2000-08-12 | 2002-12-12 | Seung-Jin Lee | Multi-component composite film method for preparing the same |
US20020110732A1 (en) * | 2000-12-20 | 2002-08-15 | Polystor Corporation | Battery cell fabrication process |
US20030157408A1 (en) * | 2001-12-28 | 2003-08-21 | Luying Sun | Microporous membrane and its uses thereof |
Cited By (37)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100166961A1 (en) * | 2004-01-20 | 2010-07-01 | Beard Kirby W | Production of high porosity open-cell membranes |
EP2541645A3 (en) * | 2006-04-28 | 2013-08-28 | LG Chem, Ltd. | Separator for battery with gel polymer layer |
US9269937B2 (en) | 2006-04-28 | 2016-02-23 | Lg Chem, Ltd. | Method for preparing separator for battery with gel polymer layer |
US20070292750A1 (en) * | 2006-06-16 | 2007-12-20 | Kirby Beard | Optimized microporous structure of electrochemical cells |
US8323815B2 (en) * | 2006-06-16 | 2012-12-04 | Porous Power Technology, LLC | Optimized microporous structure of electrochemical cells |
US20080176139A1 (en) * | 2007-01-22 | 2008-07-24 | Physical Sciences Inc. | Three dimensional battery |
US7709139B2 (en) | 2007-01-22 | 2010-05-04 | Physical Sciences, Inc. | Three dimensional battery |
US20090291368A1 (en) * | 2007-08-17 | 2009-11-26 | Aron Newman | Carbon Foam Based Three-Dimensional Batteries and Methods |
US20090208832A1 (en) * | 2008-02-17 | 2009-08-20 | Porous Power Technologies, Llc | Lamination Configurations for Battery Applications Using PVDF Highly Porous Film |
US20090226683A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Porous Material Uses in Furniture |
US20090227163A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Protective Apparel with Porous Material Layer |
US20090222995A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Bedding Applications for Porous Material |
US20090223155A1 (en) * | 2008-03-05 | 2009-09-10 | Bernard Perry | Building Construction Applications for Porous Material |
US20100124702A1 (en) * | 2008-11-17 | 2010-05-20 | Physical Sciences, Inc. | High Energy Composite Cathodes for Lithium Ion Batteries |
US8808925B2 (en) | 2008-12-19 | 2014-08-19 | Changzhou Zhongke Laifang Power Development Co., Ltd. | Microporous polymer membrane modified by aqueous polymer, manufacturing method and use thereof |
US20110229768A1 (en) * | 2008-12-19 | 2011-09-22 | Changzhou Zhongke Laifang Power Development Co., Ltd. | Microporous polymer membrane modified by aqueous polymer, manufacturing method and use thereof |
US20100178567A1 (en) * | 2008-12-24 | 2010-07-15 | Porous Power Technologies, Llc | Mat Forming Spacers in Microporous Membrane Matrix |
US9752063B2 (en) | 2009-05-20 | 2017-09-05 | Samsung Electronics Co., Ltd. | Treatment and adhesive for microporous membranes |
US9276246B2 (en) | 2009-05-20 | 2016-03-01 | Samsung Electronics Co., Ltd. | Treatment and adhesive for microporous membranes |
US20100297489A1 (en) * | 2009-05-20 | 2010-11-25 | Porous Power Technolgies, Llc. | Treatment and Adhesive for Microporous Membranes |
CN102270756A (zh) * | 2010-09-25 | 2011-12-07 | 上海市凌桥环保设备厂有限公司 | 锂离子电池用复合隔膜 |
US20120121967A1 (en) * | 2010-11-17 | 2012-05-17 | Sony Corporation | Non-Aqueous Electrolyte Battery |
US9947959B2 (en) * | 2010-11-17 | 2018-04-17 | Murata Manufacturing Co., Ltd. | Non-aqueous electrolyte battery having porous polymer layer between laminate film and battery device |
CN102140762A (zh) * | 2011-01-10 | 2011-08-03 | 武汉理工大学 | 一种增强型纳米纤维多孔膜及其制备方法 |
US20140038025A1 (en) * | 2012-07-31 | 2014-02-06 | Jeong-Ki Ha | Separator, lithium battery including the separator, and method of preparing the separator |
US9105909B2 (en) * | 2012-07-31 | 2015-08-11 | Samsung Sdi Co., Ltd. | Separator, lithium battery including the separator, and method of preparing the separator |
US10700331B2 (en) | 2012-08-23 | 2020-06-30 | Samsung Sdi Co., Ltd. | Separator for rechargeable lithium battery |
DE102013106021A1 (de) | 2013-06-10 | 2014-12-11 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Ungefüllte und gefüllte Gussmasse, insbesondere zur Herstellung beschichteter Metallfolien, und deren Verwendung für Elektroden oder Separatoren in Akkumulatoren |
EP2819213A2 (de) | 2013-06-10 | 2014-12-31 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Ungefüllte und gefüllte Gussmasse, insbesondere zur Herstellung beschichteter Metallfolien, und deren Verwendung für Elektroden oder Separatoren in Akkumulatoren |
US9865857B2 (en) | 2014-08-29 | 2018-01-09 | Sumitomo Chemical Company, Limited | Laminated body, separator, and nonaqueous secondary battery |
US9711776B2 (en) | 2014-08-29 | 2017-07-18 | Sumitomo Chemical Company, Limited | Laminated body, separator, and nonaqueous secondary battery |
US9711775B2 (en) | 2014-08-29 | 2017-07-18 | Sumitomo Chemical Company, Limited | Laminated body, separator, and nonaqueous secondary battery |
US10014506B2 (en) | 2014-08-29 | 2018-07-03 | Sumitomo Chemical Company, Limited | Laminated body, separator, and nonaqueous secondary battery |
WO2016114849A1 (en) * | 2015-01-15 | 2016-07-21 | Google Inc. | Hybrid rechargeable battery |
US11456456B2 (en) | 2016-06-23 | 2022-09-27 | United States Of America As Represented By The Secretary Of The Air Force | Bendable, creasable, and printable batteries with enhanced safety and high temperature stability—methods of fabrication, and methods of using the same |
CN111244374A (zh) * | 2019-12-25 | 2020-06-05 | 武汉中兴创新材料技术有限公司 | 一种结构改进的涂层隔膜及其制备方法 |
CN112160166A (zh) * | 2020-09-28 | 2021-01-01 | 湘潭大学 | 一种聚丙烯腈/聚环氧乙烷复合纤维膜及其制备方法和应用 |
Also Published As
Publication number | Publication date |
---|---|
EP1482578A1 (en) | 2004-12-01 |
CN1309102C (zh) | 2007-04-04 |
US20070134548A1 (en) | 2007-06-14 |
TWI299587B (en) | 2008-08-01 |
JP5309171B2 (ja) | 2013-10-09 |
CA2462294A1 (en) | 2004-11-28 |
US7794511B2 (en) | 2010-09-14 |
KR20040103310A (ko) | 2004-12-08 |
JP2011119276A (ja) | 2011-06-16 |
CN1574419A (zh) | 2005-02-02 |
SG115647A1 (en) | 2005-10-28 |
JP2004356102A (ja) | 2004-12-16 |
KR100628606B1 (ko) | 2006-09-26 |
TW200427122A (en) | 2004-12-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7794511B2 (en) | Battery separator for lithium polymer battery | |
US6322923B1 (en) | Separator for gel electrolyte battery | |
US6881515B2 (en) | Separator for polymer battery | |
US7087343B2 (en) | High melt integrity battery separator for lithium ion batteries | |
US5830603A (en) | Separator film for a storage battery | |
KR20030020258A (ko) | 다층 전기화학 전지 장치의 제조 방법 | |
WO2002050929A2 (en) | Battery cell separator and fabrication process | |
KR20020080337A (ko) | 전기화학 전지 장치에 사용하기 위한 격리판 | |
KR100897683B1 (ko) | 선택적 이온 수송이 가능한 리튬/이산화망간 배터리 분리대 | |
US6426165B1 (en) | Electrochemical cell separators with high crystallinity binders | |
KR20020070439A (ko) | 전기화학 전지 장치에 사용하기 위한 격리판의 처리 방법 | |
KR20020070438A (ko) | 다층 전기화학 전지 장치 | |
EP4251422A1 (en) | Dry-process polyethylene membranes, coated membranes, separators, and related methods | |
KR20210119917A (ko) | 전기화학소자용 분리막의 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CELGARD INC., NORTH CAROLINA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WENSLEY, C. GLEN;CHAMBERS, KEVIN D.;REEL/FRAME:014414/0103;SIGNING DATES FROM 20030804 TO 20030811 |
|
AS | Assignment |
Owner name: CELGARD, LLC, SOUTH CAROLINA Free format text: CHANGE OF NAME;ASSIGNOR:CELGARD, INC.;REEL/FRAME:014822/0710 Effective date: 20040630 |
|
AS | Assignment |
Owner name: JPMORGAN CHASE BANK, AS ADMINISTRATIVE AGENT, TEXA Free format text: SECURITY AGREEMENT;ASSIGNOR:CELGARD, LLC;REEL/FRAME:015348/0137 Effective date: 20041109 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |