TWI289543B - Glasses for flat panel displays - Google Patents
Glasses for flat panel displays Download PDFInfo
- Publication number
- TWI289543B TWI289543B TW093121549A TW93121549A TWI289543B TW I289543 B TWI289543 B TW I289543B TW 093121549 A TW093121549 A TW 093121549A TW 93121549 A TW93121549 A TW 93121549A TW I289543 B TWI289543 B TW I289543B
- Authority
- TW
- Taiwan
- Prior art keywords
- glass
- less
- patent application
- liquidus viscosity
- viscosity coefficient
- Prior art date
Description
1289543 九、發明說明: 【發明所屬之技術領域】 本發明係關於不含鹼金屬鋁矽酸鹽破璃,其呈現出平 板顯示器裝置基板之所需要物理以及化學特性。 【先前技彳标】 顯示器可廣泛地分成兩类員:放射性(例如為蕾 細示板OWM魏雜。後輕_於1顯示^ LCD),其依靠外界光源,顯示器只作為光線調節器。在液晶 顯,情況下,該外界光源可為外界光線(使用於反射性顯 示器)或專用光源(例如為直接取景顯示器)。 液曰日顯不為依罪液晶(LC )材料三種固有之特性調節光 線。苐一為LC促使偏極光線光學旋轉之能力。第二^ lc藉 由液晶機械性順應方向產生該轉動之能力。第二. 施加外界電場產生該機械性順應方向之能力。一…耩 、在製造單純扭轉向列液晶顯示器,兩塊基板圍繞著一 層液晶材料。在已知的Normally White顯示器中塗覆校 準層於基板内侧表面上將使液晶導引器產生9〇度旋轉。此 係捐進入液晶格-個表面線性偏梅匕光線之偏極性被液晶 材料產生90度旋轉。彼此朝向9〇度之偏極薄膜放置於勒反 之外侧表面上。 進入第一偏極薄膜之光線變為線性地偏極。通過液晶 格光線之偏極性轉動90度以及能夠離開通過第二偏極薄膜 。跨越液晶層所施加電場將液晶導引器與電場對準,其將 妨礙旋轉光線之能力。通過該液晶格線性偏極光線會使偏 極性旋轉以及_鄉二偏極_醜。以賴單形式加 以說明,液晶材料為光_,其具有能力藉由施加電場而控 制光線通過或阻絕。 /上述說明屬於在液晶顯示器中單一圖素之操作。高資 訊形式顯不H需飯合數百萬圖素鱗列形式,該圖素亦 1289543 ,為次。纽或施加電場麟有這些補素,同時使 定址速度最大化及存在於數個頻道間干擾較為最小。一項 定址次圖素之方法為利用位於每一次圖素之薄膜半導體控 制電場,其形成主動陣列液晶顯示器裝置(AMLCD)主要部^。 製造這些顯示器非常地複雜,以及基板玻璃特性非常 地重要。第一以及最為優先地,在製造AMLCD裝置中所使用 玻璃基板需要精密控制之物理尺寸。說明於美國第333· 6號專利(Dockerty)以及美國第3682609號專利(Dockerty) 下拉片/大或融合處理能夠產生該產物而不需要後級形成修 飾之操作例如為豐接以及拋光。非常不幸地,融合處理過 程將對玻璃特性產生相當嚴格之限制,其需要相當高之液 相線黏滯係氣優先地大於200000泊。 通常構成顯示器之兩塊基板分別地製造。一片彩色濾、 波板^有^色,藍色,綠色,以及黑色有機色素沉積於其上a ,。這些每一主要色彩必需精確地相對應主動板圖素電極 區域、。為了消除在製造兩塊板製造過程中所遭遇外界溫度 情況差異之影響,需要使用玻璃基板,其尺寸與熱學條件無 關(例如具有較低熱膨脹係數之玻璃)。不過,該特性需要 藉由在沉積薄膜與基板間產生之應力加以平衡,其由於膨 脹不相匹配所致。估計最佳熱膨脹係數在 範圍内。 所謂主動板係因為其包含主動薄膜半導體,其使用一 般半導體形式處理過程加以製造。這些處理過程包含噴塗 ,CVD,光石版印刷法,以及餘刻。在這些處理過程中玻璃需 要保持為未受改變的。因而,玻璃需要呈現出熱學以及化 學穩定性。 熱穩定(亦已知為熱壓縮或收縮)決定於特定玻璃組成 份之固有黏滞特性(以應變點表示)以及玻璃片受熱歷程, 其由製造處理過程決定。美國第537595號專利揭示出應變 第6 頁 1289543 點大於650 C之玻璃以及融合處理過程之熱學變化過程為 可接文之熱穩定性以作為負載於a—&薄膜半導體(μ)及 赵低溫p-Si TFT之主動性板。較高溫度處理過程(例如為 低溫p-Si TFT所需要的)需要玻璃基板退火步驟以確保埶 穩定性。 ”” 化學穩定性表示避免在製造處理過程中所使用各種腐 蝕巧溶液之侵襲。其一項特別優點在於能夠抵抗侧矽層 之乾#刻情況。為了顯現出乾燥餘刻情況,基板試樣暴露 於IlfBHF蝕刻溶液中。該測試包含將玻璃試樣浸潰於4〇t: 之1單位50%重量比HF以及10單位4〇%重量比NHF溶液中歷時 5分鐘。試樣依據重量損失以及外觀加以分級。 除了這些規格外,AMLCD製造商發現較大顯示器尺寸以 及規模經濟性兩項需求為促使其生產較大型尺寸之玻璃。 目如工業界標準為Gen III(550_c650mm)以及GEN 111.5( 600mmx720腿),但是未來嘗試將朝向Gen IV(lmxlm)尺寸, 以及可能為較大尺寸。此將增加數項令人關切的需求。第 二為玻璃之重量。由Gen III· 5提昇至Gen IV將使玻璃重 量增加50%將顯著地拌隨地需要使用機器手臂處理器以運 送玻璃到達以及通過處理操作台。除此,決定於玻璃密度 以及揚氏彈性模數之彈性彎曲隨著較大片尺寸而變為較嚴 重之問題,其影響負載,取出,以及間隔玻璃於工作匣中之 能力,該工作匣使用來運送玻璃於處理工作台之間。 因而需要提供顯示器裝置之玻璃組成份,其具有較低 密度以緩和較為大型片狀尺寸之問題,密度優先小於2.45 公克/立方公分以及液相線黏滯係數大於2〇〇, 〇〇〇泊。除此 ,玻璃熱膨脹係數在0-300°C需要界於28-35xlO_7/°C之間, 以及優先地界於28-33x10-7/°C。除此,玻璃應變點大於 650°C為有益的,以及玻璃能夠抵抗腐蝕劑之侵襲。 【發明内容】 第7 頁 1289543 本發明在於發現密度小於2· 45公克/立方公分之玻璃 以及液相線黏滯係數大於200, 〇〇〇泊,優先地大於4〇〇, 〇〇泊 ,更優先地大於600, 00泊,以及最為優先地大於8〇〇, 〇〇泊。 除此,本發明玻璃在0-300°C範圍内呈現出熱膨脹係數界於 28-35xl07/°C,以及優先地界於28-33xlO_7/°C,以及應變 點高於650°C。本發明玻璃熔融溫度小於i7〇〇°c。除此,在 浸潰於30°C之1單位50%重量比HF及1〇單位40%重量比NM 溶液中歷時5分鐘後玻璃重量損失小於〇· 5毫克/平方公分。 本發明玻璃組成份以氧化物莫耳百分比表示包含:65 一
75% Si〇2,7-13 Al2〇3,5-15 BA,〇-3 MgO,5-15 CaO ,O'SrO,以及實質上不含關。更優先地本發明玻璃組成 份以氧化物莫耳百分比表示包含67-73% Si〇2,8-115% AI2O3,8-12% B2O3,0-1% %0,5-11% CaO,0-5% SrO。 我們發現對於具有先前所說明物理特性以及組成份之 玻璃,其液相線黏滯係數強烈地受到驗土金屬氧化物(和 Mg,Ca, Sr)和與礬土之莫耳比值或 R〇/Al2〇KMg〇+Ca〇+Sr〇) /副^響。該比值表示為_ΐ2〇3,以及應該保持在〇· 9 至】· 2範圍内。最為優先地,該比值應該在〇. 92<Ra/Ai^< 0· 96以得到最高之液相線黏滯係數。 本發明玻璃主要不含Ba0,其係指玻璃優先地含有小於 〇· 1莫耳% BaO。本發明玻璃亦不含鹼金屬氧化物,並係 含澄清劑(例如騎,錄,錫氧化物,及/或鹵 化物,氣/鼠化物)。 ^發明另外-項為玻璃絲溫度小於j 7 t單位5幢量_及料=重量 /谷液中歷時5分鐘後玻璃«損失小於〇. 5毫克/平 。ί璃有用地使用作為平板顯示器之級。由本發 明玻璃所細紐平均_礙度簡子力酿 1289543 為小於0· 5nra以及由光學遲滯器量測平均内部應力小於j 5〇 psi 〇 ' 【實施方式】 本發明主要關於改善玻璃以使用作為平板顯示器基板 〇特別是,玻璃符合該基板所需要之各種特性。 本發明玻璃呈現出密度小於2· 45公克/立方公分,優先 地小於2· 40公克/立方公分,在〇—3〇〇t:溫度範圍内熱膨脹 係數界於28-35xl(T7/°C,優先地界於28-33χ1(Γ7/°(:,及應 變點高於650°C,優先地大於660°C。較高應變點可協助防止 平板在往後熱處理過程中由於壓縮/收縮產生之變形。 一對於說明於Dockey之美國第338696及3682609號專利 較為需要之製造條件例如為融合處理過程,其需要較高液 相線黏滯係數。因而在本發明優先實施例中,玻璃應該呈 現出密度小於2· 45公克/立方公分及液相線黏滞係數大於 2〇j),00泊,優先地大於4〇〇, 〇〇〇泊,更優先地大於6〇〇, 〇〇〇泊 ,最為優先地大於800, 000泊。雖然由本發明玻璃製造出基 板月b夠使用其他製造處理過程例如為浮式處理法生其 於數項理由熔融處理過程為優先的。首先,由融合處理& 程製造出玻璃基板並不需要拋光。目前玻璃基板抛光所製 造出玻璃基板之平均表面粗糙度大於〇· 5nm(Ra),其以原子 力顯微鏡量測。本發明及使用融合處理過程製造出玻璃基 板以原子力顯微鏡量測之平均表面粗糙度小於〇. 5咖。 化學耐久性包含抵抗使用於製造處理過程中所使用各 種腐#溶液之侵襲。特別優點在於抵抗乾燥腐姓條件之侵 蝕,其使用來姓刻矽層。乾燥蝕刻條件一項指標為暴露於 腐蝕溶液已知為110BHF。該測試包含浸潰玻璃試樣在3〇它 11體積單位50%重量比HF以及1〇體積單位鄕重量比Nm ,液中歷時5分鐘。化學抵抗性以毫克/平方公分單位進行 量測重量損失。該特性在表I中列為”110 Bfjp,,。 1289543 本發明玻璃包含65-75%莫耳比,優先地67-73%莫耳比 Si〇2作為主要玻璃形成劑。提高石夕石將改善液相線黏滯性 以及減小玻璃熱膨脹係數以及密度,但是過多矽石有害於 溶融溫度。玻璃亦包含7-13%莫耳比,優先地8-11· 5%莫耳 比AI2O3。增加Al2〇3含量將提高玻璃耐久性以及降低熱膨 脹係氣但是液相線溫度將提高。至少需要8%莫耳比以得 到最需要之應變點;不過大於11· 5%莫耳比將產生小於戶斤需 要之液相線溫度。 斤玻璃更進一步包含5-15%莫耳比,優先為8-;12%莫耳比 石朋氧化物。蝴氧化物降低液相線溫度以及密度以及優先地 存在至少8%莫耳比;不過大於12%莫耳比硼氧化物對玻璃應 變點產生負面影響。 存在於本發明玻璃中Mg〇含量在0—3%莫耳比,優先地為 0—1%莫耳比,MgO提高將降低液相線黏滯性,以及因而玻璃 中存在不超過3%莫耳比MgO。不過較小數量Mg〇有益於使宓 度減小。 、山
CaO有益於降低μ玻璃熔融以及液相線溫度;不過大於 11%莫耳比將導致小於所需要之應變點以及高於所需要之 熱膨脹係數。因而,本發明玻璃能夠包含5—15%莫耳比Ca〇, 但是優先地包含5. 5-11%莫耳比CaO。 ’ RO/AI2O3比值在〇· 9-1· 2範圍内。在該範圍内可發現 液相線溫度局部最小值,其相當於Ca〇—AI2O3-Si〇2主要系 =之溶融最低值。該系列玻璃之黏滯性曲線並不會顯著地 變化,因而這些液相線溫度變化主要為提高液相線黏滞性 之原因。 、,於對薄膜半導體(TFT)特性產生負面影響,鹼金屬例 如為氧化鐘,鍊打或驗水被排除於本發明組成份中。同樣 地,驗土金屬(SrO以及BaO)將為最小或加以排除,因為^發 月了包含0-5%莫耳比SrO。不過,本發明實質上不含Ba〇。 第1〇 頁 1289543 在此所明不含B〇係指組成份包含小於莫耳比之腳。 亦能夠存在澄清劑例如為_3, _,⑽,祕,α 去除玻璃中雜f。玻璃亦可包含商業化配 土玻璃中所發現之雜質。除此,能夠加入下列氧化物之含 量不超過1%莫耳比而不會超出先前所說明·,Zn〇,施 ,ΥΑ’ Μ特性之範圍。表I列出一此莫 =;璃舰其以莫耳百分比“。例 玻璃為本公司之1737玻璃。
、,本發明更進一步以下列範例列舉出,其為列舉性質以 及作為限制本發明申請專利範圍。表I揭示出以玻璃 原料氧^物莫耳百分比表示之範例性玻璃組成份。這些試 樣玻璃藉由在白金坩堝中溶融每一玻璃組成份j 〇〇〇—25〇〇 ^克原料配製出,其熔融溫度以及時間例如為在1625t歷 :4 16小時將產生相當均勻之玻璃組成份。其申亦揭示出 母一組成份之玻璃特性,其依據傳統玻璃技術揭示出。因 而在0-300°C範圍之線性熱膨脹係數以xl〇-y>c表示,軟化 點。(Soft· Pt·),退火點(Ann· pt·),及應變點(str. Pt.) 以c表示。這些由光纖拉伸技術測定出(分別地為Asm E228-85,以及C336文獻)。密度(Den)以公克/立方公分表 示由 Archimedes method (ASTM C693)表示。
藉由對尚溫黏滯性數據使用Fulcher公式標定而計算 出黏滯性係數為200泊之溫度(熔融溫度。c)(定義玻璃& 呈現出黏滯性為200泊[20Pa· s]之溫度),該黏滯性藉由旋 轉圓筒黏滯儀ASTM C965-81量測出。液相線溫度使用標準 液相線方法量測出。此包含放置壓碎玻璃顆粒於白金挑料 環中,放置挑料環於具有溫度梯度區域之高溫爐中,在適當 溫度區域中對挑料環加熱歷時24小時,以及藉由顯微鏡檢 視以測定出玻璃内部區域中呈現出晶體之最高溫度。液相 線黏滯係數(Liq· Vise,以泊表示)由該溫度以及Fulcher 第11 頁 1289543 公式之係數決定出。 一表I列出一些以氧化莫耳百分比表示之玻璃組成份,及 顯示出本發明組成份參數。各個組成份總和非常接近100, 實際上所邮數值可代表莫耳百分tb。實際原料組成份可 由任何材料材料所構成,其包含氧化物或其他化合物,當與 ,他原料組成份嫁融在一起時將轉化為所需要適當比例之 氧化物。例如SrC〇3,以及CaC〇3能夠分別地作為SrO與CaO 之來源。 範例^及19所顯示特性及組成份之玻璃目前視為代表 本發明之最佳模式,其產生本發明用途之最佳組合特性。 雖然本發明已對列舉目的詳細加以說明,人們了解該 詳細翻只作為該用途以及熟知此技術者能夠作出許多^ 化但是並不會脫離下列申請專利範圍所界定出之 神與範圍。 猶 【圖式簡單說明】 無 第12 頁 1289543 ΜΛ 誠份願 (mol%) 1 2 3 4 5 6 7 8 Si〇2 6975 69.78 69.75 69.8 70.7 70.57 69.1 70.85 AI2〇3 10.2 10.2 10.3 10.3 10 9.77 10.35 9.5 B2O3 9.7 9.7 9.5 9.5 10 9.95 10.25 10.1 Mg〇 0.8 0.8 0.8 0.8 0.12 0.15 1.25 Ca〇 7 7 8.5 8.5 9 9.17 9.8 6.7 SrO 2.2 2.2 0.8 0.8 1.3 Ba〇 AS2〇3 0.3 0.3 0.4 0.33 Sb2〇3 0.3 0.3 0.3 0.1 Ce〇2 0.2 丫2〇3 Sn〇2 0.05 0.02 0.05 0.05 0.02 0.02 Cl 0.2 0 0.2 0.2 0.2 RO/AI2O3 0.98 0.98 0.98 0.98 0.90 0.95 0.96 0.98 CTE_0oC_, xlO_7/〇C) 32.7 31.2 31.9 30.8 30.5 30.2 31.5 31.4 密度(g/cm3) 2.416 2.404 2.394 2.38 2.37 2.355 2.375 2.367 應麵。C) 672 674 673 679 671 666 673 664 727 731 729 734 728 729 729 720 mm°o 984 991 991 995 1001 1001 976 992 110 BHF (mg/cm2) 0.15 0.14 0.145 0.135 0.14 0.15 0.18 0.27 液機鑛。c) 1125 1120 1120 1125 1150 1135 1115 1140 mmmmm (P) 5.04E+05 7.06E+05 6.34E+05 6.30E+05 3.66E+05 5.95E+05 5.30E+05 4.77E+05 麵鑛。C) 1659 1668 1650 1659 1668 1680 1635 1686 第13 頁 1289543 表1(續肩Ί) 糸脈份原與 (mol%) 9 10 11 12 13 14 15 16 17 Si02 69.1 69.65 68.75 69.1 68.8 69.33 69.65 70.05 69.33 八丨2〇3 10.35 10.1 10.55 10.2 10.35 10.55 10.2 9.9 10.55 B2〇3 10.25 10.25 10.25 10.55 10.55 9.97 10.25 10.25 9.97 Mg〇 0.15 0.15 0.15 0.15 0.15 0.18 0.15 0.15 0.18 Ca〇 9.3 9.45 9.9 9.65 9.8 9.08 8.85 9.25 9.58 SrO 0.5 0.5 0.5 Ba〇 AS2Q3 0.33 0.4 0.4 0.33 0.33 0.37 0.4 0.4 0.37 Sb2〇3 Ce〇2 丫2〇3 Sn〇2 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Cl RO/AI2O3 0.96 0.95 0.95 0.96 0.96 0.93 0.93 0.95 0.93 CTE (0-300° C., xlO_7/°C) 32.2 31.4 31.8 32 31.8 31.5 30.9 30.8 31.4 密度(g/cm3) 2.377 2.366 2.371 2.364 2.366 2.376 2.369 2.357 2.366 應_占(。C) 671 669 674 666 667 676 671 668 674 退火點(。C) 727 725 729 722 723 731 728 726 730 mm°c) 983 985 986 980 980 985 987 992 987 110 BHF (mg/cm2) 0.15 0.12 0.12 液棚泉moc) 1095 1090 1100 1090 1115 1095 1100 1100 1120 mmmmm (P) 1.05E+06 1.23E+06 9.19E+05 1Ό7Ε+06 5.74E+05 1.19E+06 1.04E+06 112E+06 6.23E+05 隱容溫5 (〇C) 1649 1654 1650 1642 1650 1651 1657 1674 1654 1289543 表1 ί續言2} 糸脈份願斗 (mol%) 18 19 20 21 22 23 24 25 26 Si02 69.45 69.33 68.3 70.45 70 70.4 70.1 70 68.3 八丨2〇3 11 10.55 10.9 9.85 10.35 10.05 10 10.23 10.9 B2〇3 9 9.97 10.4 9.55 9.5 9.69 10.15 9.75 10.4 Mg〇 0.18 1.1 0.8 0.82 0.81 0.8 Ca〇 10 9.08 9.1 5.75 8.5 7.14 7.11 7 9.1 SrO 0.5 1 2.9 0.85 1.89 1.88 2.22 1.0 Ba〇 AS2〇3 0.4 0.3 Sb2〇3 0.3 0.37 0.3 Ce〇2 0.2 0.2 0.2 0.2 V2〇3 Sn〇2 0.05 0.02 0.05 0.05 Cl 0.2 0.2 R0/AI203 0.91 0.93 0.93 0.99 0.98 0.98 0.98 0.98 0.93 CTE (0-300° C., xlO_7/°C) 32 31.9 34.8 33.4 32.8 33.5 32.9 33.4 34.5 密度(g/cm3) 2.386 2.383 2.403 2.405 2.378 2.378 2.374 2.391 2.392 應_占(°c) 681 675 669 670 672 670 664 671 677 败點(。C) 737 730 725 727 728 727 720 727 732 mm°c) 993 984 978 996 988 989 984 989 979 j 110 BHF (mg/cm2) 0.16 0.3 0.39 0.18 0.17 0.19 0.19 ^ 液雛M°c) 1150 1100 1140 1165 1160 1140 1150 1150 1150 液讎顯纖 (P) 2.90E+05 1.06E+06 2.40E+05 2.88E+05 2.49E+05 4.29E+05 2.80E+05 3.11 E+05 2.14E+05 rnmrn (°〇) 1642 1655 1617 1682 1656 1668 1653 1656 1620 1289543 表1 (續頁31 糸脈份願斗 (mol%) 27 28 29 30 31 32 Comp Ex Si02 68 70 70.4 69.8 71 72 67.6 八丨2〇3 10.5 10 10.2 10.6 9.9 9.33 11.4 日2〇3 11 10 9.1 9 10 10 8.5 Mg〇 1.3 Ca〇 10.5 9 5.68 7.14 9.1 8.66 5.2 SrO 4.55 3.42 1.3 Ba〇 4.3 AS2O3 0.4 Sb2〇3 0.3 0.3 0.3 0.3 0.3 0.3 Ce〇2 Y2O3 Sn02 Cl RO/AI2O3 1.00 0.90 1.00 1.00 0.92 0.93 1.03 CTE (0-300° C., xlO_7/°C) 34.9 32.0 34.4 34.4 32.1 31.2 37.8 密度(g/cm3) 2.378 2.355 2.420 2.406 2.353 2.342 2.54 應變占(。C) 659 673 669 672 669 672 666 歡點(。C) 713 731 727 729 726 730 721 mm°c) 967 999 987 984 998 1012 975 110 BHF (mg/cm2) 0.23 0.18 0.2 液繼麵°c) 1120 1130 1130 1135 1120 1125 1050 mmmmm (P) 3.07E+05 5.99E+05 5.67E+05 4.38E+05 8.46E+05 8.79E+05 2.97E+06 (°o 1611 1670 1671 1657 1685 1703 1636 第16 頁
Claims (1)
- 修正 年月 a 1289543 ~ 十公 ^ 1· 一種呈現出密度小於z· 4b¥克/立方公分以及液相線黏 滯係數大於200, 000泊之鋁矽酸鹽玻璃,該玻璃以氧化物莫 耳百分比表示包含下列組成份:65-75% Si〇2,7-13% Al2〇3, 5-15% B2〇3,〇-3% MgO,5-15% CaO,〇-5% SrO,以及BaO大 於0%及小於〇·1%,及在〇_3〇〇°C溫度範圍内玻璃線性熱膨漲 係數在28-33xl(T7/°C之間。 2·依據申請專利範圍第1項之玻璃,其中R〇/Ai2〇3比值在 0.92及0.96之間,其中R表示Mg,Ca,Sr以及Ba。 3·依據申請專利範圍第1項之玻璃,其中玻璃應變點大於 65(TC。 4·依據申請專利範圍第1項之玻璃,其中玻璃應變點大於 660〇C 〇 5·依據申請專利範圍第1項之玻璃,其中玻璃熔融點溫度小 於 1700°C。 6·依據申請專利範圍第1項之玻璃,其中玻璃在浸潰於3〇°c 1單位40%重量比HF以及1 〇單位40%重量比NHF4溶液中歷時5 分鐘後呈現出重量損失為小於〇. 5毫克/立方公分。 7.依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於400, 〇〇〇泊。 8·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於600, 0〇〇泊。 9·依據申請專利範圍第1項之玻璃,其中當玻璃不含SrO時 玻璃含有0-1莫耳百分比Mg〇。 10·依據申請專利範圍第1項之玻璃,其中玻璃構成平板顯 1289543 不為之基板。 11·依據申請專利範圍第10項之玻璃,其中基板之平均表面 粗糙度小於0. 5nm。 12·依據申請專利範圍第1〇項之玻璃,其中基板之平均内部 應力小於150psi。 13·依據申請專利範圍第1項之玻璃,其中玻璃組成份以氧 化物莫耳百分比表示包含下列組成份:67-73% Si〇2,8-11.5%A1203,8-12°/gB2〇3,0-l%MgO,5.5-ll%CaO以及 0-5% SrO。 14·依據申請專利範圍第13項之玻璃,其中玻璃應變點大於 650〇C。 15 ·依據申請專利範圍第13項之玻璃,其中玻璃應變點大於 660〇C。 16·依據申請專利範圍第13項之玻璃,其中玻璃熔融點溫度小 於 1700〇C。 17·依據申請專利範圍第13項之玻璃,其中玻璃液相線黏滞係 數大於400, 〇〇〇泊。 18·依據申請專利範圍第13項之玻璃,其中玻璃液相線黏滞係 數大於800, 〇〇〇泊。 19·依據申請專利範圍第丨3項之玻璃,其中玻璃構成平板顯 示器之基板。 20·依據申請專利範圍第19項之玻璃,其中基板之平均表面 粗糙度小於0· 5nm。 21 ·依據申請專利範圍第19項之玻璃,其中基板之平均内部 1289543 應力小於150psi。 22·依據申請專利範圍第18項之玻璃,其中玻璃構成平板顯 示器之基板。 23·—種鋁矽酸鹽玻璃,該玻璃以氧化物莫耳百分比表示包 含:65-75% Si〇2,7-13% Al2〇3,5-15% B203,以及大於0%及小 於0· 1%莫耳百分比驗金屬氧化物,其中: (a) 玻璃R0/A1203比值在〇·9及1.2之間,其中R表示Mg,Ca,Sr以 及Ba; (b) 玻璃CaO濃度以氧化物莫耳百分比表示在5%及15%之間 ;以及 (c) 玻璃密度小於2. 45公克/立方公分,液相線黏滯係數大於 400, 000泊,以及在〇-300°C溫度範圍内玻璃線性熱膨漲係數 在28-33xl(T7/°C 之間。 24·依據申請專利範圍第23項之玻璃,其中玻璃組成份以氧 化物莫耳百分比表示包含下列組成份:67-73% Si〇2,8-11· 5% ΑΙΑ 8-12% B2〇3,以及5. 5-11% CaO。 25·依據申請專利範圍第23項之玻璃,其中R0/A1203比值在 〇·92及0.962之間,其中R表示Mg,Ca,Sr以及Ba。 26.依據申請專利範圍第23項之玻璃,其中玻璃應變點大於 650〇C。 27·依據申請專利範圍第23項之玻璃,其中玻璃應變點大於 660〇C 〇 28·依據申請專利範圍第23項之玻璃,其中玻璃熔融點溫度小 於 1700°C。 1289543 29·依據申請專利範圍第23項之玻璃,其中玻璃在浸潰於30°C 1單位40%重量比HF以及1 〇單位40%重量比NHF4溶液中歷時5 分鐘後呈現出重量損失為小於〇· 5毫克/立方公分。 30·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於400, 000泊。 31 ·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊。 32·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於800, 〇〇〇泊。 33·依據申請專利範圍第23項之玻璃,其中玻璃密度小於2. 40 公克/立方公分。 34.依據申請專利範圍第23項之玻璃,其中玻璃構成平板顯 示器之基板。 35·依據申請專利範圍第34項之玻璃,其中基板之平均表面 粗链度小於〇. 5nm。 36·依據申請專利範圍第34項之玻璃,其中基板之平均内部 應力小於150psi。 37·依據申請專利範圍第23項之玻璃,其中玻璃包含Ba〇小 於0.1%莫耳比。 38·依據申請專利範圍第19項之玻璃,其中玻璃包含鹼金屬 小於0.1%莫耳比。 39·依據申請專利範圍第1項之玻璃,其中玻璃包含鹼金屬 小於0·1°/◦莫耳比。 40·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 1289543 數大於800, 000治。 41 ·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於400, 000泊以及玻璃密度小於2· 公克/立方公分。 42.依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊以及玻璃密度小於2· 40公克/立方公分。 43 ·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於800, 000泊以及玻璃密度小於2· 40公克/立方公分。 44. 依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於400, 000泊,玻璃密度小於2. 40公克/立方公分,以 及應變點大於650°C。 45. 依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊,玻璃密度小於2. 40公克/立方公分,以 及應變點大於650°C。 46·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於800, 〇〇〇泊,玻璃密度小於2· 40公克/立方公分,以 及應變點大於650°C。 47·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於400, 〇〇〇泊,玻璃密度小於2· 40公克/立方公分,以 及應變點大於660°G。 48·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於600, 〇〇〇泊,玻璃密度小於2· 40公克/立方公分,以 及應變點大於660°C。 49·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於800, 〇〇〇泊,玻璃密度小於2. 40公克/立方公分,以 1289543 及應變點大於660°C。 50·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於400, 000泊,玻璃密度小於2. 40公克/立方公分,以 及在浸潰於30°C1單位40%重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇. 5毫克/立 方公分。 51 ·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊,玻璃密度小於2. 40公克/立方公分,以 及在浸潰於30°C1單位40%重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇· 5毫克/立 方公分。 52·依據申請專利範圍第1項之玻璃,其中玻璃液相線黏滯係 數大於800, 000泊,玻璃密度小於2· 40公克/立方公分,以 及在浸潰於3(TC1單位40%重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇· 5毫克/立 方公分。 53·依據申請專利範圍第1〇項之玻璃,其中未拋光基板之平 均表面粗糙度小於〇. 5nm。 54·依據申請專利範圍第1〇項之玻璃,其中基板之平均表面 粗糙度小於0· 5nm以及平均内部應力小於150psi。 55·依據申請專利範圍第41項之玻璃,其中玻璃構成平板顯 示器之基板,以及基板之平均表面粗糙度小於〇. 5nm。 56·依據申請專利範圍第42項之玻璃,其中玻璃構成平板顯 示器之基板,以及基板之平均表面粗糙度小於〇. 5nm。 1289543 57.依據申請專利範圍第43項之玻璃,其中玻璃構成平板顯 示器之基板,以及基板之平均表面粗糙度小於〇· 5nm。 58·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於400, 〇〇〇泊以及玻璃密度小於2. 40公克/立方公分。 59·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於600, 〇〇〇泊以及玻璃密度小於2. 40公克/立方公分。 60·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於800, 〇〇〇泊以及玻璃密度小於2. 40公克/立方公分。 61 ·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於400, 〇〇〇泊,玻璃密度小於2. 40公克/立方公分,以及應 變點大於650°C。 62·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊,玻璃密度小於2. 40公克/立方公分,以及應 變點大於650°C。 63 ·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於800, 000泊,玻璃密度小於2· 40公克/立方公分,以及應 變點大於650°C。 64·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於400, 〇〇〇泊,玻璃密度小於2· 40公克/立方公分,以及應 變點大於660°C。 65 ·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊,玻璃密度小於2· 40公克/立方公分,以及應 變點大於660°C。 66·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 1289543 數大於800, 000泊,玻璃密度小於2· 40公克/立方公分,以及應 變點大於660°C。 67·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於400, 000泊,玻璃密度小於2· 40公克/立方公分,以 及在浸潰於30°C 1單位40%重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇. 5毫克/立 方公分。 68 ·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於600, 000泊,玻璃密度小於2· 40公克/立方公分,以 及在浸潰於30°C 1單位40%重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇· 5毫克/立 方公分。 69·依據申請專利範圍第23項之玻璃,其中玻璃液相線黏滯係 數大於800, 000泊,玻璃密度小於2· 40公克/立方公分,以 及在浸潰於30°C 1單位40°/。重量比HF以及10單位40%重量比 NHF4溶液中歷時5分鐘後呈現出重量損失為小於〇· 5毫克/立 方公分。 70·依據申請專利範圍第34項之玻璃,其中未拋光基板之平 均表面粗链度小於0. 5nm。 71 ·依據申請專利範圍第34項之玻璃,其中基板之平均表面 粗糙度小於0· 5nm以及平均内部應力小於150psi。 72·依據申請專利範圍第58項之玻璃,其中玻璃構成平板顯 示器之基板,以及基板之平均表面粗糙度小於0. 5nm。 73 ·依據申請專利範圍第59項之玻璃,其中玻璃構成平板顯 1289543 示器之基板,以及基板之平均表面粗植度小於〇· 5nm。 74·依據申請專利範圍第60項之玻璃,其中玻璃構成平板顯 示器之基板,以及基板之平均表面粗糙度小於〇. 5nm。