TWI261026B - Photocatalyst sheet, method for adhesion and producing the same - Google Patents
Photocatalyst sheet, method for adhesion and producing the same Download PDFInfo
- Publication number
- TWI261026B TWI261026B TW93138687A TW93138687A TWI261026B TW I261026 B TWI261026 B TW I261026B TW 93138687 A TW93138687 A TW 93138687A TW 93138687 A TW93138687 A TW 93138687A TW I261026 B TWI261026 B TW I261026B
- Authority
- TW
- Taiwan
- Prior art keywords
- photocatalyst
- coated
- layer
- rubber
- sheet
- Prior art date
Description
1261026 九、發明說明: 【發明所屬之技術領域】 本發明係有關經由光觸媒粒子使基材或光觸媒含有層 之樹脂或橡膠不會被分解之光觸媒片、其接合方法及其製 造方法,尤其是有關光觸媒片之間容易接合且可獲得光觸
媒光氧化還原效用之弁觸姐y _ A &尤觸媒片、其接合方法及其製造方法。 【先前技術】 由於光觸媒具有消臭、抗菌、防污之機能 …因、防〉可之機能,目前已 ^皮利用料種領域。例如對於具有光觸媒粒子之片若 3於曰光等之紫外線照射, a H ^ ^ ^ U ^ 、產生先虱化逖原反應,將 者於片表面之有機物等污物 作用於污染物質等,3 一方面,光觸媒不/ 、亦㈢刀解纖維或塑膠本身,所以可· 慮在光觸媒氧化鈦表面以 — _ 7尤觸媒壬不活性之多孔性石悉? ㈣加以包覆(例如特許文獻…)。 外 弟8圖為含有以往来網 片1〇具有如下所干之7叙#之斷面構造®。以往: ,、月y r ηχ不之四層播皮 纖維或無機纖維織物等纖。’、p,由成為基質之合月 飞观寺缄維組成之第一声n , , ^ ^ y 成樹脂或橡膠組成之第二層12 _曰 ^復由e
層13,更於中間層J 3上勺费 Λ / 12上包覆中fE 成之光觸媒層14(例如特獻:化鈦等光觸媒粒子15相 光觸媒H4所含之光角_立; 生氧化還原反應,則經由…二」5右爾照射而潑 底層之第二層D或第—/羊還原反應,在不使構成 φ OB S 1 ^ 層1 ]之樹脂或纖唯箄法' # 丁 ^ 中間層U介於第二層12與 減之寺:化下’將 T曰i 4之間。亦即,中間 1261026 層1 3具有一種保護黏著層 —〆+ 曰之柃月匕。此外,光觸媒粒子之固 疋係使用氟樹脂等難分解性材料。 第9圖為含有與笫s ^ 、 /、 圖不同光觸媒之片之斷面構造 0。弟8圖為在第一層1]之 1 ^ 丄 表或晨中一方之面上以第二芦 1 2、中間層1 3及光觸嬋芦 曰 ^ ^ 呆層14之順序包覆之片10。如第9 圖所示,第一層Π之矣言工 „ ια 表晨兩面對稱地以第二層12、中間 層13、及光觸媒層14之順序包覆之片10a。 以往片1〇與心間之接合方法使用如下所述之方法 第10(a)圖為以往將片1〇 / ..u 牧口 <刖P白奴之斷面圖,(^ 為接合階段之斷面圖。於前 I ) u 1A 、月j ^丰又,如弟10(a)圖所示,僅蔣 片10a間將接合之寬度d怂杠立人 1重將 ^ ?, 攸任何接合之片10a經由 去光觸媒層14及中間屑n 石除 ..^ 層13使其中一方之面露出可埶炉 者之树脂層之第二層12。 …、备 八接著,在接合階段,如第10(b)圖所示,將寬度 &面合併 '熱熔著。亦即,在構成第二層12之樹脂 ·)谷融固化。熱熔著之方法有熱風熔著、熱板溶著、古= 溶著、超音波溶著、熱固定式溶著等。亦可經 劑或雙面膠使接合。對於光觸媒層14僅單面包覆之:占者 ^相同’刖階段需除去接合寬度d之光觸媒層14及中間: 如此,將具有介於第二層n與光觸媒層14之 間:η而使光觸媒粒子15引發之光氧化還原反應 一層12或第一層1]無不良影響之片10、]0a接合0士,、昂 需除去接合寬度d之光觸媒層]4及中間層]3(例如^ ’僅 3]6575 !261〇26 獻7)。 [特許文獻]]特許第3275032號公報([0006],[0009]) [特許文獻2]特開平^2675:19號公報([0004],[0009]) [特許文獻3]特開2〇〇〇_1631號公報(標題頁) [特許文獻4]W〇〇i/〇17680號公報(標題頁) [特許文獻5]特開2〇〇〇_ ^ 9957號公報([0009]) [特許文獻6]特開平】0_237769號公報([⑻〇4]、[〇〇〇5]) [特許文獻7]特許第2889224號公報([0007]) 13 差 但是,若在第二層12及光觸媒層】4之間設置中間層 則在製造片1 〇、1 〇a上會增加作業工程、生產效率變 成本變高。又必需進行以往將片10,10a之間接合時 =所明非除去接合寬度之光觸媒層不可之接合工程上之煩 t作業。x ’將光觸媒粒子固定時需使用氟樹脂等難分解 ,原材料,使得加工固難且成本變高。 、 【發明内容】 本名X明以上述課題為借鏡 μ^^^^ ^以美供基材或光觸媒含有 層之树脂或橡勝不會被光觸媒有 獲得光觸婢之弁^ 5之間谷易接合且可 其製造方法為目的。 a觸媒片、其接合方法及 為了達成上述目的,本發明 至少在表面固定有經•灰石包,二媒片之第—構成’係 片,Α ώ 已设之光觸媒粒子之朵鍁姐 /、中以上述光觸媒片彼此之 先觸媒 各接合面係由可埶著 。刀目重豐、接合之 申者之材㈣成為其特徵者。 μ寸利乾圍第2項揭示之發 V、由以磷灰石包 -^16575 7 叫026 之光觸媒粒子及將該光觸 之光觸媒片,其中以 :、: *定在表面之基材所成 晶 4立 、入上述各光觸媒片之一邦八77扣杳 宜、接合之基材之各接八 。媒片之。卩分互相重 特徵者。 。面知由可熱熔著之材料形成為其 本發明光觸媒片之第- 材之單面或雙面之覆系由基材及包覆在該基 有以磷灰石包覆之光觸V:子之/以上述㈣^ 者。 1媒拉子之光觸媒含有層為其特徵 本發明光觸媒片之第r 材之單面或雙面之第係由基材及包覆在該基 之皆两 復版層與包覆在上述第一雩胺展卜 之罘二覆膜層組成,其 k弟復fe層上 包覆之光觸媒粒子之光後M層係固定有以磷灰石 上述来網拔A先觸媒έ有層為其特徵者。 萄媒3有層表面之以磷灰石勺步 ’以具有從光觸媒含有層 ::觸媒粒 以勉石包覆之光觸媒粒子’二=刀者較佳。上述 用鱗灰石包覆之粒子ϋ洛 力觸媒粒子表面之-部分 覆之粒子較佳。又,勺受 用夕孔性石拜灰石包 晋,·、, + U、、 匕復上述光觸媒粒子之磷灰石之勺舜 里,以在上述光觸姐y 匕復 照射i小時後上、+ ^ ^經強度^讀/⑽2之紫外線 町^ J峙俊上述光觸媒片全 ^ 以下之量。弁網财』7 之重里減少率較好在1〇% I之里先觸媒粒子以紫外線應答型 任何一種或兩種者較佳。 見先C合型之 上述光觸媒粒子以含 、, 石、碳酸磷灰石、?述磷灰石以羥磷灰 午人石 虱磷灰石及氯磷方石少k y 等之混合物較佳。L τ其 / 、、,、 可一種類或該 处土材以由洋麻、黃麻及其他天 316575 8 1261026 、准=酿胺系纖維、聚芳醯胺系纖維、聚酷系纖維、聚氣 乙細_、聚偏氣乙稀系纖維、丙歸 醇糸纖維、聚丙稀系纖維、聚乙烤系纖維及其 纖細 維組成者較佳。 武石滅維及其他無機纖 用碟灰石包覆之光觸媒粒子,以使用構成上述光 =有層之樹脂或橡膠加以固定者較佳。相對於該樹脂 或橡私,以石舞灰石包覆之光觸媒粒子之比例較好在⑺ 9J重,範圍。又,上述樹脂較佳為氯乙稀樹脂、聚乙 : 乙稀-乙酸峨共聚物、聚胺基甲酸醋、敦 树月曰、本乙烯、丙烯腈-丁二烯_苯乙烯共聚物、、 丙烯酸系樹脂、聚碳酸醋,戊 一述橡咖爾丁二稀= 聚乙烯橡膠、天然橡膠、丁二稀系„、苯乙_ =化 丁基系橡踢、腈橡膠、丙稀酸系橡膠、胺基甲酸^橡界、 石夕乳燒系橡膠、說橡膠、乙稀_丙婦系橡膠中之任何拳 上述㈣脂較好為聚四敦乙烯(PTFE)、四氟 。 共聚_、四氣乙稀他基乙稀鱗共 = 氟乙烯(PVF)、聚偏氟乙烯(pvDF)之任何一種。 )♦ :發:之光觸媒片,光觸媒片表面之光觸媒含有層由 a在表面路出樹脂或橡膠,所以可直接熱熔 或雙面膠接合,在光觸媒片間之二:者Μ 工程’可容易地接合。又,由於在該光之 固定㈣灰石包覆之光觸媒粒子’所以可獲得光^^乍 316575 9 1261026 用。而且由於光觸媒粒子 不會影響光觸媒含 =火石包仅’所以光觸媒作用 之第-覆膜層及在基二=媒以外之材料、於第三構成 原反應而分解。尤A是於!即,基材幾乎不會因光氧化還 第二覆膜層與基材之間介::構成,作為光觸媒含有層之 後之同—原材_叙第㈣含有層除去光觸媒 以很薄,可大幅产減讀層’所以光觸媒含有層可 覆之光觸媒粒子之量^疋2觸媒含有層之經石粦灰石包 包覆之光觸媒粒子,所以不2觸媒使用經磷灰石 f可使用氟―灰石包覆之光觸:: 媒二方:成:J明::媒片之接合方法為本發明光觸 乐一構成或弟二構成之光觸媒片之接合方 不除去光觸媒片之光觸媒含有層 在 該接合面之間接合為其特徵二=面之間合併而使 … 使存在於上述接合面夕 =㈣橡膠之間經熱炼著而接合者較佳。於光觸媒含有芦嫌 於用 +來固定經磷灰石包覆之光觸媒粒子之樹脂: 〜乡、,忒矬知灰石包覆之光觸媒粒子之比例較好在⑺ 60重量%之範圍。 根據本發明之光觸媒片之接合方法,盥以往々方法不 X由於不需經過除去接合寬度之先觸媒層而使i脂層露 出表面之前階段處理’所以可容易地進行接合。尤立在埶 熔著時,相對於樹脂或橡膠之經石舞灰石包覆之光觸媒粒子 之比例在10至6。重量。/。之範圍,可以充分之接合強度接 316575 10 1261026 合。 本發明光觸媒月之製造方法,係 之單面或雙面之覆膜層組成,覆膜層之:卜^仅在基材 磷灰石包覆令朵鈣Μ 、θ取上層是固定有經 I设之先觸媒粒子之光觸媒含有岸 造方法,光觸媒含有層係由樹脂或橡勝^成^片之製 有經墙灰石包覆之光觸媒粒子之分係由塗佈含 層為其特徵者。 ^㈣W觸媒含有 本發明光觸媒片之製造方法,係由 , 之單面或雙面之覆膜層組;…基材 造方法,光觸觸媒含有層之光觸媒片之製 # h 有層係由樹脂或橡谬組成,係由人右r 磷灰石包覆之光觸媒粒 ,、由3有、、坐 入七& 卞之树月日或橡膠形成片妝$古i若丄甘 含有層,再將該片狀之光觸媒含有之先觸媒 上層而形成光觸媒片為其特徵者有層貼在上述覆膜層之最 造方法中,分散液較好由樹 石包復之光觸媒粒子、 体/用、灰 層中,相對於用來固定經磷灰2構成。在光觸媒含有 或橡膠,經磷灰石包覆之丄已復之光觸媒粒子之樹脂 %範圍。再者,八今、广先觸媒子之量為10至90重量 之光觸媒粒子、:VI 子由樹脂或橡膠、用磷灰石包覆 用來固定經石粦灰石h Α。在光觸媒含有層中,相對於 灰石包覆之光觸嬋光觸媒粒子之樹脂或橡膠,經_ 柜^ 粒子之比例為]0至90重量%。 根據本發明光觸婢制 層之含有經磷灰石自爱、之衣k方法,將設置於基材最上 、 後之光觸媒之光觸媒含有層,用分散 1^575 11 1261026 液金抹等方、、土 i — 今万去可容易製造。 【實施方式】 (實施本發明之最佳形態) 以下詳細說明本發明並以表示本發明之數個實施形態 、 固表為基礎’使本發明更容易被暸解°然而,該等 丨付^圖表所不之種種實施例不是特定或限定本發明之意, 而疋單純為了使本發明可容易說明及瞭解之目的。 ^ ’將本發明之實施形態經由圖表加以詳細說明。 第1圖為本發明光觸媒片之斷面圖。第1圖之光觸媒 片1由基材2以及將經磷灰石包覆之光觸媒粒子4分 固定之覆膜層3組成。
於包含申請專利範圍之本說明 «品本體以及該製品所使用之材料之概念,包^^ =才枓)表面經表面處理劑包覆之狀態或包覆前之狀能_ ='二基材2可列舉例如棒球場、集會場等圓屋項或L 育館,設施等 錄棚卡車車逄、療養被單、易蠻宏哭努处 一 或防雨衣、書包、椅子等你 ^σσ、吏用之基材, 等機械用纖維補強樹脂之基材送帶、定時夸 :麻、黃麻其他之天然纖維或聚酿二:纖 纖維、聚醋系纖維、聚氯乙烯系來烷鉍月女系 丙烯酸系纖維、聚乙_系纖广^ 系纖等合成纖維或玻璃纖維〜么〃、、、: 、准、4乙稀 等無機纖維等,經加工成為織物^^'纖碓、玄武岩纖維 3!6575 12 1261026 覆膜層3為將經鱗灰石包覆之光觸媒 脂或橡膠而成之光觸媒含有層。由 ^ =樹 、經被碌灰石包覆,所以用來固定、_灰石包=^^已 二尸4?固定劑不需為說樹脂等難分解性之原㈣。:! 月吴層J在不除去朵阴Μ人士 復 時,為了=1]媒含有層下將光觸媒U之間熱炫著 灰石21:之接合強度,相對於樹脂或橡躍,用碌 已设一先觸媒粒子4之比例較好為1G至6G重量%。 :脂:列舉例如氯乙稀樹脂(pvc)、聚乙烯㈣、聚丙 _二[乙酸乙稀酯共聚物(叫聚胺基甲酸醋 ,咖、聚苯乙娜)、丙烯腈丁二稀-苯乙婦共聚 p BS) * S&胺(PA、尼龍(註冊商標))、丙烯酸系樹脂 A)、'曰聚碳酸醋(PC)、曱基戊稀樹脂(TPX)等合成樹脂或 :寺之此合物。氟樹脂可列舉聚四氟乙烯(PTFE)、四氟乙 稀一六1氣丙烯共聚物(卿)、四氟乙烯-全氟烧基乙刺共聚 7(PFA)、聚氟乙烯(PVF)、聚偏氟乙烯(PVDF)等氟樹脂單 體^聚合物。橡膠可列舉氯丁二烯系橡膠(CR)、氣磺化聚 乙烯橡膠(CSM)、天然橡膠(NR)、丁二烯系橡膠(BR)、苯 乙烯乐橡膠(SBR)、丁基系橡膠(IIR)、腈系橡膠(NBR)、丙 少市酸糸橡膠(ACM)、胺基曱酸酯系橡膠、矽氧烷系橡膠 (Sl)、氟橡膠(FPM)、乙烯-丙烯系橡膠(EPDM)等。 固定於覆膜層3之磷灰石包覆之光觸媒粒子4,為光 觸媒粒子表面之一部分以島狀或全部,以對光觸媒呈惰性 之鱗灰石包覆而成之粒子。包覆光觸媒粒子之磷灰石之包 t ’為基材或樹脂等不會被光觸媒分解程度之量。例如 316575 1261026 f光觸媒片表面照射強度1驗/‘之紫外 時,以經由光觸媒作 ’小時 在贈。以下之量者二: 全體之重量減少率 360·左右旅生7外^7 照射主要使用設計在 …系外線放射之高塵水銀燈或營光严、七 燈、不可見光燈等之光。 皮尤/且、矾 覆之光觸媒粒子4為在光觸媒表面全部-〜灰石包覆之粒子時,碌灰石必需為多孔性,:: 狀態。_卩作為搞狀讀光編以為露出之 此需之光觸媒為亦稱為光半導體之材料, 1〇〇疆之銳鈦礦⑼她叫型Ti〇2(二氧化鈦,林— 3.2eV,波長388麵)等之光觸媒微 二π見 中除了銳鈦0肌之外,*化鈦(鈦氧化物) —波長―或三氧化 將該等光觸,稱為適當氧化鈦。光觸媒亦可使用链 (ZnO^ ^ t t 3.2eV ^ 388nm) ^ ltS^,(SrTl〇 " , ^ 二:38一氧化鎢— 光觸媒粒子不僅是用紫外線產生光氧 外線應答型,亦可為用包括室内光之可見光線產生it 還原反應之可見光線應答型,亦可將該等混合使用。 石舞灰石係以石舞酸妈作為主成分,可列舉_灰石㈣ 碟灰外碳㈣灰石、“灰石、氯碟灰 ^ 等之混合物。 Ί j為这 ^16575 14 1261026 、亦即,磷灰石只要實質上由羥磷灰石(Ca^p〇4)6(〇H)2) 組成者即可,容許含有少量之其他成分。亦可為將該經鱗 ,石之Ca側、p〇4側、〇H側以其他元素或分子取代或使 部分固溶之種種化合物構造之磷灰石。Ca側之鈣可經勰、 鋇、斜、録、鐘等取代,或使斂、纪、鑭、猛、鐵、鋅、 姥^氫等兀素部分固溶。鉛側之外〇4可經、As〇4、
Cr〇4等取代,亦可你 ^
使C〇3、HP〇4、b〇3等部分固溶。〇H 側之OH可經氟、氯1、氧、c〇3、b〇2等取代。 碟灰石以不容易析出之水難溶性者較佳。又,以用多 孔性石粦灰石包覆者較佳 #總拔主1 為王多孔性所以在細孔中存在 光觸媒表面未經被霜而言山 生m “ 部分,該部分用光照射而產 昭射T ^ ^ , 在先,尤其在紫外線或可見光線 光觸媒產生之電子及正電孔之光氧化還原反 害物質以及其他有:::〜灰石所吸著之有機物質或有 六、寻光觸媒作用。使用可見光應艾 ^ 光觸媒片時,經由 ;觸 M S屋内使用 污染物質分解。又,蜀媒反應而將室内之環境 觸角成為“。。以下’由於將片 = 觸媒片作為膜構造建築物或帳 …所以在將光 滴落下。 ㊉錢科,可防止凝結之水 由於用磷灰石將光觸媒 之光觸媒粒子4之樹脂或橡 媒表面。又,由於該磷灰石 包覆,用來固定經磷灰石包覆 膠’實質上不會直接接觸光觸 對於光觸媒呈惰性’即使混入 3]6575 1261026 用來固綱灰石包覆之光觸媒粒子4之覆 磷灰石伴偏戈橡膠之介質中使用,亦可將樹脂或橡膠用 觸焊光不易產生樹脂或橡膠等介質本身之分解。光 良影響,可提昇光觸媒片!之耐^基材2不會造成不 臭源灰石具有吸附雜菌、空氣中之細菌、病毒、惡 等有害物質之性二 有機化合物(voc) 經碟灰石包覆之光觸:::被固疋於光觸媒含有層表面之 時,亦可將所% 在吸附該等有害物質之同 、 ϋ付之有告物質經由光觸媒 貫且有效率地消滅或分解。 九觸媒之強魏力,確 不僅疋用该鱗灰石包 之光觸媒粒子4,亦可為:用=媒”之經鱗灰石包覆 之表面部分等、、Β岛、 Η火石包覆時在光觸媒粒子 1刀寺化入鉑、鍺、釕、 加逮經由光觸姐你田^ ° ^銅、鋅等金屬而 觸媒粒子4。/、 Μ化分解速度之經磷灰石包覆之光 用碟灰石包覆之光觸媒粒 膜層3之光觸媒含” 。勻分散在作為覆 子4至二在光觸媒含有層表面之用•灰石包声之光觸❹ 千4,從覆膜層3, 匕仅之先觸媒粒 曰光等光所含之紫外線^角蜀媒含有層表面露出者,經由 應,可容易獲得光觸;:=〜容易引發光氧化還原反 …面積::層:出之經伽包覆⑽ 夕牛灰石包覆之光觸媒粒子4之粒徑 316575 16 1261026 以適度小者較理想。 與如以往之片1〇(镇 粒子15者不同,於本發明^係在、光觸媒層14填充光觸媒 3之光觸媒含有層 :、:分散、固定於作為覆膜層 磷灰石包覆之先觸媒粒子4去則不需準備必要以上之用 為了在光觸媒片〗賦予導 在覆膜層3添加金屬材料或光:增強光觸媒效果,可 材料可列舉銀、铭入一 f某機能補助物質等。金屬 m::、銅、鐵、銦、銀、錦、鐵、錯、 ^ 1^ 録、鋅、供笙。▽ 丄 媒片1之用途,、天^ 在覆膜層3可配合光觸 性碳、蹲石等吸收劑。、貝或有告物負等吸收之活 第二==:圖:同之本發明光觸媒片之斷面圖。 -覆膜声 材2、包覆基材2之單面之第 所構成广.以及包覆於第-覆膜層5上之第二覆膜層3a 二層構造二覆膜層%為使經碌灰石包覆之光 :::子4分散並固定之光觸媒含有層。基材2與第W 伯f:2相同,第二覆膜層^與第i圖之覆膜層3相同, =兀觸媒片la之第二覆膜層3a比光觸媒片 者為薄。 v牙上 劳弟—覆膜層5由在第二覆膜層3a用來固定經磷灰石包 设之光觸媒粒子4之樹脂或橡膠構成。其他與第丨 觸媒片相同。 根據該構成,可減低分散、固定於作為第二覆膜層3a 之光觸媒含有層之用磷灰石包覆之光觸媒粒子4之量,在 316575 17 1261026 降低成本之同時,於光觸媒片la之強度方面亦不會比第! 圖之光觸媒片!遜色,又,在將光觸媒片]a之間進行接人 時亦可與第1圖時同樣進行。 。 p弟3圖與第】圖及第2圖不同,為本發明光觸媒片之 斷面圖。第3圖之光觸媒片lb與如第]圖之光觸媒片】 之在基村2之單面以覆膜層3包覆之片不同,係 之雙面以覆膜層3包覆 材2 各層與第】圖相同。 此處,基材2、覆膜層3之 :第3圖所示,在光觸媒片^之雙面具有光觸媒含有( 曰之復胲層3時,在光觸媒片】b單面上之覆膜層3铲 將紫外線應答型之光觸媒粒 二:吏用 粒子4,光觸婵lb之另而華 包後而成之光觸媒 写呆lb之另一面之覆膜層3則係 應答型之光觸媒粒子以磷灰 將可見光 跄少女闽全 包覆而成之光觸媒粒子4。 雖侧表,但是第2圖之光觸媒片h t基材2之雙面包覆第一覆膜層再在第-覆膜ΓΓ 包覆第二覆膜層3a而成之片。 層5上 第4圖與第i圖至第3圖不同, ( 斷面圖。第4圖之光觸媒片卜為在美材1光觸媒片之 媒粒子7而成之片。基材6俜 表面固定光觸 合面之基材6之表面可熱炫著之原 =觸:“間之接 :6之材質可列舉上述之各種樹脂或橡膠。又例:::為基 表面固定有用磷灰石8包覆 基材6之 媒粒子7之-部分用伽8包先=77。所固定光觸 亦即未經磷灰石8包覆之表 、同媒粒子7之表面, 、路出在大氣侧者較 1261026 Γ 則光觸媒粒子7容易受光而發揮w土 作用。第4圓雖然只在基材 二^土之光觸媒 7,但是若在基材6雙方之表 表面固疋光觸媒粒子 時不^ {麵軸子7,在接合 心接合面所以接合作業容易進行。 接者,對於本發明光觸媒片】、 僅列舉將第3圖光觸媒片】b之間接人 =合方法, 說明。 之方法作為例子加以 弟5圖為將第3圖光觸媒片之間接 :觸媒片“之表裏兩面都具有覆膜層3,心::圖。 用崦灰石包覆之光觸媒粒子4分散、二"曰3為將 有層。光觸媒含有層不是填充用鱗灰石某含 而是使之分散,在表面或其内 =觸媒粒子 石包覆之光觸媒粒子4之樹脂。 有用來固疋經磷灰 將光觸媒片】b之間互相接合 】上之接合面對齊後將接合面熱熔著,X:=絲媒片 有層之樹脂之間熔融固化而將光二易將先觸媒含 方法可列舉埶風扠著、# ” b接合。熱熔著之 使用超音波溶:::用:熱板炫著、使用高周波熔著、 曰及/合者、使用熱鏟熔著等。 以上之接合方法在已說明之1他 由於在各光觸媒片之表面存在同樣1、等: 不需作任何變更即可同樣適用。 、δ有層,所以 如以上之說明,光觸媒片係使用經鱗勺 知粒子,且將該用磷灰、^復先萄 m ,, 之九知媒粒子用樹脂戍橡膠 …此則光觸媒之作用,亦即光氧化還原反二 316575 19 1261026 以外之原材料 同時在接合時 以及第2圖 不需移除多 不會波及光觸媒含有層之光觸媒 光觸媒片之第―覆膜層及基材,、 餘的地方。 將該光觸媒片之間接合時,以往 或中間層除去,但是如以 夕备'之光觸媒層 只要將光觸媒片之接入&#4十 男而要^去之地方, 低生產成本’同時’以往經由移除而會產二r可減 ρ 刀,所以不會產生廢棄物。 =對本發明光觸媒片之製造方法加以說明。 ❹/之先觸媒片可經由在聚酯纖維織物或破璃纖唯 =兩面將經氣乙稀樹脂包覆之片(以 ::= 片)或經™包覆之片(以下稱為適宜删片)^nc 下^ μ媒之合成樹脂分散液,在既^之溫户 下“既定時間,再經由自然冷卻製成。 4 3有用ν灰石包覆之光觸媒之合成樹脂分散液,為在 曱基乙基酮(ΜΕΚ)乃/十田#斤丄 马在 人、 )及/或曱本寺有機溶劑添加氣乙烯或丙 、Ρ寺口成魏、用·石包覆之光觸媒粉末、ΜΕΚ等稀釋 dI進仃心合 '攪拌而成者。有機溶劑及稀釋劑只要多 溶解上述之合成樹脂或橡膠等者即可,並不只限於::
者。又’有機溶劑若添加到使分散液之黏度在1_心· $ 以下,則其塗抹性變佳。 e S 用Η灰石匕板之光觸媒粉末可不使用有機溶劑而直护 ^料氣乙稀或丙稀等合成樹脂中,但是若考慮到製造二 率或混合容S度,⑽使用有機溶震齡散體進行塗抹 "HxS75 20 1261026
)使用PVC或椟狀铪A $ y + 〜月乡夸亂U脂以外之合成樹 放液時,在最外表面層 f月曰作為分 ηπ / 2 丁 ’至抹Β寸之塗抹量以s & η] #父佳,乾燥溫度隨使用 Ώ 至]2(TC較佳。 $铖而異,以7crc 氟樹脂驗分散液時, 僅是水系分散體,亦可使$ 、虱樹脂不 柯 便用乙酸丁酯等溶劑,作忐垄、才、入 科之形態加以利用。又,pVF 心乍成尤漆塗 ,進行溶融。該等有機溶劑 ^擇^之有機 二,脂之最外表面層進行塗佈時之塗佈量: J〇g/m2 較佳。 m 至 塗抹方法只要是棒塗覆法、照相凹版塗覆法 、目凹版塗覆法、微照相凹版塗覆照 2軲塗復法、滾壓塗覆法、逆輥塗覆法、浸 觸塗覆法、梦朔泠φ、+ 七各 、土设法、接 以法、流動塗覆法等可均-塗抹之方法 可,可使用任何一種方法。 本發明光觸媒片之製造方法 外夕人二、此— 下使用氣樹脂以 ,5成樹月曰或橡膠時可將含有用磷灰石包覆之 :觸媒粒子之樹脂或橡膠經由壓延機加工等使片 “形成光觸媒含有層’再將該片化之光觸媒含 “貼合在基材之最上層而製成。 士具體而言,係使經碟灰石包覆之光觸媒粒子以及必要 ::將增塑劑、加工助劑、耐氣候安定劑、抗氧化劑、顏料 寺破包含於合成樹脂或橡膠中,再進行炫融、混練、片化。 將該經片化之光觸媒含有層貼合在基材之最上層’即可製 316575 1261026 成本發明之弁艄 尤_媒片。該美士 覆之基材。 丞材亦可為經合成樹脂或橡膠包
[貫施例1 J 百先對於將用磷灰石 维兩面用氯乙稀樹脂包承…觸媒粒子固定於聚醋纖 實施例1至5及1 设之PVC片之表面之光觸媒片之 〜,及其比較例1至6加以說明。 ^例1為添加a乙稀樹脂 (大曰精化公司製造, 有表面處理劑 1上5wt〇/〇(重量%))1〇〇公 軍钱成分 仆敍#鎞加 克用外灰石包覆之銳鈦礦型-羞 化鈦先觸媒粉末(昭 亡坐一孔 ΠΛ 丄 不%公司製造F1S02(<^妗軲斤 90nm、磷灰石包覆量 η (+句拉徑 ΜΕΚ3.5公克,麫、曰人° · △、以及作為稀釋劑之 、''工此5、攪拌調製成溶 氯乙烯樹脂(P Vn乃△ 八 d冷液A之 c)及丙烯酸系樹脂(PMA)與鱗 化鈦之比率為90: 1〇。 外及石包後氧 接著,將該溶液A以棒塗法塗佈在 用氯乙烯樹脂包覆之PVCHm…曰、'滅、准之兩面 匕復之PVC片之早面。該塗膜 於100〇C加埶乾焯?八妒χ ,, Α Λ1 λ 币皿把/本後 …、紅4 2义知,再經自然冷卻製成實施 試料&。 、心 [實施例2] 除了用磷灰石包覆之二氧化鈦光觸媒粉末I 0·34公 克以外’與實施例1同樣操作,調製成溶液Β ,製成實^ 例2之試料,。溶液Β之氣乙稀樹脂及丙稀酸系:脂 灰石包覆二氧化鈦之比率為8〇 : 20。 [實施例3 ] ^16575 1261026 除了用磷灰石包覆之二氧化鈦光觸媒 克以外,與實施例!同樣操作,調製成 、·、0.90公 例3之試料c。溶液C之氯乙稀樹脂及丙烯❸=實施 灰石包覆二氧化鈦之比率為6〇:4〇。 〜樹脂與- [實施例4] 除了用碟灰石包覆之二氧化鈦光觸媒粉 克以外,與實施例1同樣操作,調製成溶液^制=么 例4之試料d。溶液D之氯乙稀樹脂及丙稀酸系:= 灰石包覆二氧化鈦之比率為4〇 : 6〇。 曰,、石夕牛 [實施例5 ] 了用磷灰石包覆之二氧化鈦光觸媒
克以外,與實施例1同樣操作,調製成溶液E,制二A 例5之試料e。溶液E之氯乙稀樹脂及丙歸酸系:二Π 灰石包覆二氧化鈦之比率為30: 70。 ’、、曰/、石夕牛 (比較例1) 將在實施例1使用之聚醋纖維之兩面用 覆,以不塗抹光觸媒之片單體作為比 ^脂包 (比較例2) 〈忒抖f。 除了使用未包覆磷灰石之銳鈦礦型二氧 末(石原產業公司製造ST01、〗-欠初a外7 先觸媒粉 “人粒約7nm)〇 15八古 外,與實施例1同樣操作,調製成溶液G,f成比2以 之試料g。溶液G之氣乙稀樹脂及丙稀 :列2 磷灰石之二氧化鈦之比率為9〇: 1〇。 未包覆 (比較例3) 1261026 除了將比較例2之未向考石东女 士沐* 包復n灰石之二氧化鈦光觸媒於 末改為0.34公克之外,I竇你仓丨1门 η 一貝施例1同樣操作,調絮 製成比較例3之試料h。溶f Η = $ 7 ρ Η, ,,Ht ^ + ^ 合液乙烯樹脂及丙烯酸年 柄月曰人未包後碩灰石之二氧化鈦之比率為8〇: 2〇。、 (比較例4) 除了將比較例2之未包覆碟灰石之二氧化欽 末改為〇·9公克之外,|實$ ②,、叙 制士 ”男、鈿例1同樣操作,調製溶液I, 衣成比較例4之試料i 〇溶、、存τ 备 脂盘未…… 她旨及丙烯酸系樹 月曰,、未包覆磷灰石之二氧化鈦之比率為6〇:4〇。 (比較例5) 除了將比較例2之未包霜磘方 卜 末改為90。\* 1才匕後η灰石之二氧化鈦光觸媒粉 不改為2.0j公克之外,|廢 制士 a ^ 貝施例1同樣操作,調製溶液j, 衣成比較例5之試料卜、玄、為τ7 Μ 脂盥未自费#ft ' 1 虱乙烯樹脂及丙烯酸系樹 月曰/、未包復磷灰石之二氧化鈦之比率為40:60。 (比較例6) 除了將比較例2之去4 末改為3.15公克夕外^復拜之二氧化欽光觸媒粉 f成比ρ 、,14貫施例1同樣操作,調製溶液Κ, 之試料k。溶液K之氯乙烯樹脂及丙烯酸李 广曰與未包覆鱗灰石之二氧化欽之比率為30:7。。 [實施例6] 接著對於將用磷灰 維織物兩面細PT£F :: 觸媒粒子固定於破璃纖 例6至】“1 包覆之片表面而成之光觸媒片之實施 至1〇及其比較例7加以說明。 對4加用鱗灰石包覆之銳敍鑛型二氧化叙光觸媒之水 316575 24 l26l〇26 =體(昭和電工公司製造f]SQ2FS(平均粒經9〇_ 久石包霜I 9 〇/ 牛 克、由卿^固體成分25wt%)10公克、精製水]〇公 石々— 水系分散體(固體成分54wt%)41 7公吉 界面活性劑〇.6公克(全體之]重量分)而成之 1容 _ '授拌,調製成溶液M(FEP/用石粦灰石包覆 一氣化鈦=90/ 1〇)。 接著,在玻璃纖維之兩面用PTFE包覆, 口二: C片,經由棒塗覆法將溶液Μ ,、土布灰早面。該塗膜在常溫乾燥後於6〇。〇加埶 鐘:更於爾加熱燒成3分鐘,自然冷卻。再用= 期矾老化儀在放射照度丨8〇w/ m2(波長3〇〇至4〇〇n 紫外線照射24小時之漂白處理,製成實施例6之 仃 [實施例7] ° m。 除了將實施例6之由FEP組成之水系分散體改為U 公克以外,與實施例6同樣操作,調製溶液n,製成每= 例7之試料n。溶液N之FEp與用磷灰貝施 之比率為80: 20。 K羊'化敎 [實施例8] 除了將實施例6之由FEP經成之水系分散體改為6 公克以外,與實施例6同樣操作,調製溶液p,製成杏^ 例8之試料p。溶液P之FEP與用磷灰石包覆之:&只施 之比率為60 ·· 40。 氣化鈇 [實施例9] 除了將實施例6之由FEP組成之水系分散體改為3 3»6575 1261026 二與實施例6同樣操作,調製溶液Q,製成實施 八枓q。溶液Q之FEP與用磷灰石包覆之二 之比率為40: 6〇。 虱化鈦
[貫施例1 Q J 公克L了卜將實施例6之由FEP組成之水系分散體改為2.0 ,轉實施例6同樣操作,調製溶液R,製成實施 之比率為灰石包覆之二氧化鈦 (比較例7) 片,例6之PTFE片之最表面層$FEP包覆而成之 _ *周期氙老化儀在放射照度180W/m2(波f ^進行紫外線照射24小時之漂白處理’= 例7之試料s。 、衣成比較 接著進行實施例丨至10之含有用磷灰石包一 鈦光觸媒之光觸媒片及比較-乳化 γ η 主/之片取上層之朵銪丄甘 之評估熱接合特性、以及因光氧化分解造叙質量變;率 来J 6Ρ圖表示實施例1至5之用鱗灰石包覆之二氧化敘 先觸媒PVC片、以及比較例i 我化斌 性、熱接合特性、以及因光氧|^ 層之光觸媒活 二 九乳化分解造成之質量蠻 :估結果。光觸媒活性之還原作㈣根據•銀^ 色反應後之色差(ΛΕ)進行評估。 / h 莫耳/公升((M當量濃度)之功Λ 式枓次、;貝於〇·] 里辰度)之确酸銀水溶液中之 ι]ηλν/cm2之紫外線i分鐘, 心π射 王現王色反應者為具有光觸 316575 1261026 媒反應,以◦表示,未呈現呈色反應者 λΑλ /r/x /\ 不^不。
以冰 之評估1可明瞭,未含有光觸媒之W 之含有光觸媒之實施例】至6及比較例2幻乂例] 某片具光觸媒反應,記錄為〇。 之光觸 拉入其次,熱接合為將PVC片之光觸媒面聊〜 接&。熱接合使用安裝有4公分χ 3〇八八“進行熱 凹凸、無齒型之平面狀帝極^ ^ w A刀之平板電極(無 尼塔(股)公司製造,YC]_F型,功率 山本畢 件為使比較例2之試料f充分熔著之…一接合條丨 設定值10、調諧7〇、炫著時間4秒、;逮度 後,接合部經由拉伸試驗機以5〇毫米/ 心。炫著 聚酯纖维或玻璃纖維剝離時為良好,刀、度剝離,從 媒層呈現殘餘剝離外觀 表不,部分光觸 判斷為未熔著,以在光觸媒層間剝離時 從第6圖之評估2可明瞭含有用碟灰 一 鈦光觸媒之實施例!至3及比 、:-乳化 良好(〇)、實施例4為△、勺% 之拉伸试驗結果i 炫著〇〇。 ^ ^例5、比較例5、6為不能 由此可知,方6眚始Μ,^ ^ 脂及丙稀酸系樹脂與用伽包之=烯: 4〇:6〇以上至9〇:1〇者,熱接合性佳。之比平在 接著,對經由光氧化分解造成之走… 估。從各試料切出5公分χ 5公分之試驗 卞進^平 測定質量,然後將各試驗片放用叫早位 ⑺巩塏之老化儀(斯卡試 316575 27 1261026 驗卿造,照射波長至㈣、照射強度:18mw/ Μ 1小時及24小時後測定質量之mg單位,叶管 與試驗前之質量變化率。 早位。十开 …t/VC片時’經由照射紫外線發生增塑劑等之揮發。 貝置受化量為試驗片全體之變化量。由於 於光觸媒含有樹脂層附近 以作二^匕干者眼 量(此次設^為約】Gg/m2,; ;\所以作為相對於塗抹 ^ / 母 25cirr 試驗 A 25 古 *、> 質量變化率,由於考慮 、”)之 作為基準(參照第6圖評估曰3)土/寻之揮發分’將比較们 口此,5亥數之正值越大⑴ 及丙烯樹脂表面處 H吼乙烯樹脂 對地,負值越大卜抑制增塑劑之揮發。相 負值較小者可視騎= 觸媒分解之影響,又, 視為車乂不易文到光觸媒 如第6圖之評估3可知,含^ 光觸媒之實施例】至5之質:火石包覆之氧化敍 光觸媒之影響。相對地,比較例2至千6為+,可明瞭為不受 可明瞭會受到光觸媒分解之影響。<質量變化率為-,ξ 接著對於實施例6至1〇及比較例 某活性、熱接合特性、以及 ^㉟之光觸 率之評估加以說明。 虱化刀%造成之質量變化 弟7圖為實施例6至]〇以含有細 光觸媒之FEP層作為最上層之ρτρ^人石匕覆之氧化鈦 最上層之光觸媒活性、熱 、以及比較例7之 成之質量變化率之評话結果氧化分解造 万法除了 mE片之熱 28 1261026 接合條件外均與實施例】至 略。 方法相同,將說明省 PTFE片之熱接合性,為將各試料 用安裝10公分X 40公分熱板(無凹n 層重S,使 極)之熱板融接機。接合條件為使 (;之:面狀電 之溫度⑽、厂…鳥一炼著β = 時間20秒。 了間7〇秒、冷卻 從第7圖之評估〗明 以外,含右尖勰讲^ J木3有先觸媒之比較例7 乂外3有先觸媒之實施例5至】〇 反應,記錄為〇。 ⑨某片具有光觸媒 由第7圖之5平估2可知,孰接合 包覆之二氧化鈦光觸媒之實施例有石 貝轭例5至9及PTFE單體片夕 比較例7之拉伸試驗為良 Θ荽〜、丄 為良好(0)或可(△),實施例10為未 :者(X)。由此明瞭於實施例… 與用輪包覆之二氧化鈦之比率為4。:6〇以上中至= 1 〇者之熱接合性良好。 併t弟7 11之評估3可知,實施例6至1G及比較例7 ^里變化及其變化率均為〇,可明瞭未受到光觸媒之影 從上述實施例之結果明瞭在實施例1 i 1G,其最上層 ^光觸媒活性及經先氧化分解造成之質量變化率,對於二 車乂例1至7為良好。又,於實施例1 S 4及6至9更明瞭 熱接合特性良好。 μ 本發明並不只限於實施上述發明之最佳形態,可在申 316575 29 1261026 石月專利範圍戶斤一 於本發明之二二發明範圍内作種種變更,該等亦包含 觸媒片等片之用語本說明書及申請專利範圍中,使用光 [產業上利用之可能性] 曰〜物之意。 根據本發明之光觸媒片及苴 光觸媒片之間互相接合之光觸媒;^法’可獲得容易將 之光觸媒粒子分散、固定觸:將^灰石包覆 :乍用產生之光氧化還原反應幾乎不 ==因光觸媒 觸媒含有層之表面在接合時存在“ 午。又,光 之材料,在接合時盥 、工 相丈谷融固化結合 其是如本發明光觸媒片:Π構ΓΓ前階段處理。尤 之第二覆膜層與基封之間;:::二作為光觸媒含有層 觸媒之同-材料構成之第有二攸光觸媒含有層除去光 薄,可大幅度減少固定於光:二可使光觸媒含有層變 光觸媒粒子之量。又2觸媒含有層之用罐灰石包覆之 為光觸媒粒子,將用磷灰石、=灰:包覆之光觸媒粒子作 使用氟樹脂等難分解性η㈤媒粒子固定時不需 困難。又,亦適用於用:二本不會變高,加工亦不 子固定之情況。光觸媒粒=用磷灰石包覆之光觸媒粒 用可見光應答型,在屋内::::紫外線應答型,亦採 媒之作用。相對於樹脂或橡於τ況即可獲得作為光觸 粒子之比例作成10至9〇重;。:將用;f灰石包覆之光觸媒 會劣化,可獲得充分之光^ ° ’則樹脂、橡膠或基材不 丄, 九觸媒之作用效果。 本發明光觸媒片之接八 〇法,在光觸媒含有層表面亦 316575 1261026 -火石包覆之光觸媒粒子分 由於作為固定劑之樹脂亦存在於 如此則 面膠將兩光觸媒片接人:所以用黏著劑或雙 觸媒含有層之門产tr ,可將光觸媒片之光 在接合時 去之前階段處理,可大幅度縮先:媒:部分除 著時對於樹脂或橡膠,將用磷灰石包=;進:熱溶 充分之接合強度。 在將切心之間接合時可獲^ 本發明之光觸媒片可適 帳篷、内f 、圓屋頂寺膜構造建築物、 迷 Μ表材、可撓曲袋狀交哭、 明光觸媒片之接人方、1 π 建梁用片等,本發 片接合時。方法可利用於以各種期望之大小容易將 【圖式簡單說明】 f1圖為本發明光觸媒片之斷面圖。 第2圖為與第1圖不同之本發明 第3圖為與第^圖^”之斷面圖。( 斷面圖。 $ ®不同之本發明光觸媒片之 第4圖為與第1圖至第 斷面圖。 ^圖不同之本發明光觸媒片之 第5圖為將本發明光觸 斷面圖。 某片〜接合方法以模式呈現之 弟ό圖為貫施例1至5 >田+七 總诚· μ κ 之用破灰石包覆之二氧化鈦光 觸媒pvc片及比較例】至6之最上層之光觸媒活性、熱= 316575 3] 1261026 μ 、及、工光氧化分解造成之質量變化率之評估結果。 化欽為以含有實施例6至10之經麟灰石包覆之二氧 7 =觸媒之fep層作為最上層^侧片、以及比較例 =上層之域媒活性、熱接合特性、以及經光氧化分 角牛&成之質量變化率之評估結果。 第8圖為以往之光觸媒片之斷面圖。 第:9圖為與第8圖不同之以往之光觸媒片之斷面圖。 ^第1〇圖為將以往之光觸媒片之接合方法以模式呈 ()為削卩白^又之_面圖’(b)為接合階段之斷面圖。 【主要元件符號說明】 基材 第二覆膜層 第一覆膜層 片 第二層 光觸媒層
Ua〜lc 光觸媒片 2,6 覆膜層 3a 4,7,15 光觸媒粒子 5 7a 未經鱗灰石包覆之表面 8 石粦灰石 l〇JOa 11 第一層 12 13 中間層 14 316575
Claims (1)
1261026 十、申請專利範圍: 1. 一種光觸媒片,係至少在表面固定有經磷灰石包覆之光 觸媒粒子之光觸媒片,其特徵為上述光觸媒片彼此之一 部分互相重疊、接合之各接合面係由可熱熔著之材料構 成者。 2. —種光觸媒片,係由經磷灰石包覆之光觸媒粒子及將該 光觸媒粒子固定在表面之基材所構成之光觸媒片,其特 徵為: 與上述各光觸媒片之一部分互相重疊、接合之基材 之各接合面係由可熱溶著之材料構成者。 3. —種光觸媒片,係由基材及包覆在該基材之單面或雙面 之覆膜層組成,其特徵為: 上述覆膜層係固定有經磷灰石包覆之光觸媒粒子 之光觸媒含有層者。 4. 一種光觸媒片,係由基材、包覆在該基材之單面或雙面 之第一覆膜層、以及包覆在上述第一覆膜層上之第二覆 膜層所構成,其特徵為: 上述第二覆膜層係固定有經磷灰石包覆之光觸媒 粒子之光觸媒含有層者。 5. 如申請專利範圍第3項或第4項之光觸媒片,其中該固 定於上述光觸媒含有層之經磷灰石包覆之光觸媒粒子 係具有從該光觸媒含有層表面露出之部分者。 6. 如申請專利範圍第1項至第4項中任一項之光觸媒片, 其中前述經磷灰石包覆之光觸媒粒子係光觸媒粒子表 316575 1261026 面之°卩刀破磷灰石包覆而成之粒子,或光觸媒粒子表 面係被多孔性磷灰石勺受而★ 衣 二 河I石包覆而成之粒子。 7·二申#專利乾圍 6項之光觸媒片,其中包覆上述光觸 …:"^之^灰石之包覆量,係以強度18mW/cm2之紫 袭、射則逃光觸媒片表面1小時後,前述光觸媒片全 月豆之重量減少率在10%以下之量。 8·:!!專利範圍第1項至第4項中任-項之光觸媒片, ^4之光觸媒粒子係、為紫外線應答型、可見光應答 尘之任何一種或兩種。 9 ·如申请專利範圍第1 μ — 員至弟4項中任一項之光觸媒片, 其中:述光觸媒粒子係含有氧化鈦, 、〕l :灰石係為羥磷灰石、碳酸磷灰石、氟磷灰 ^'以及氣鱗灰石之任何—種類或該等之混合物。 10·如申請專利範圍第3 贫丄、,固昂j項或乐4項之光觸媒片,其中前述 ::洋麻汽麻及其他天然纖維;聚醯胺系纖維、 聚务酿胺系纖維、聚西旨么 ^ ΛΚ酉曰不緘維、聚氯乙烯系纖維、聚偏 氣/、“尔、截、准@稀酸糸纖維、聚乙稀醇系纖維、聚丙 細糸纖維、聚乙燁系纖維及其他合成纖維;以及 維、矽氧烷系纖維、玄被山峨从 ^ 纖 玄武石緘維及其他無機纖維所構成 者。 11. 如申請專利範圍第3項或第 一士 Λ矛4工貞之先觸媒片,其中前述 、、工外灰石包復之光觸媒粒子係以構成前述光觸媒含有 層之樹脂或橡膠使之固定。 12. 如申請專利範圍第U項 、之光觸媒片,其中前述經磷灰 316575 34 1261026 石包復之光觸媒粒子相對於前述樹脂或橡膠之比 10至90重量%。 … 1 3 ·如申請專利笳圚笼 ^ ^ ' 員之光觸媒片,其中前述樹脂為 虱乙烯樹脂、聚乙烯、聚丙烯、乙烯-乙酸乙烯酯共聚 物二“女基曱酸酯、氟樹脂、$苯乙烯、丙烯腈-丁二 烯-苯乙稀共聚物、聚醒胺、“ 甲基戊之任何—種或料之混合物; β 前述橡膠為氯丁二烯系橡膠、氯石黃化聚乙烯橡膠、 ί = 丁,稀系橡膠、苯乙稀系橡膠、丁基系橡膠、 冃卞’,丙烯酸系橡膠、胺基曱酸酯系橡膠、矽氧严 系橡膠、氟橡膠、乙稀-丙稀系橡膠之任何一種。兀 ^:請專利範圍第13項之光觸媒片,其中前述氣樹脂 w四氟^希(PTFE)、四1乙稀_六氣丙稀共聚物 (fEP)、四氟乙烯全氟烷基乙烯醚共聚物(PFA)、聚氟乙 浠(PVF)來偏氟乙烯(PVDF)之任何一種。 :::::之接合方法’其中上述光觸媒片係由基材 广復在錢材之單面或雙面之覆膜層所構成,上述步 膜層係固定有經鱗灰石包覆之光觸媒粒子之光觸婢: 有層;或者 乐s ^述光觸媒片係由基材、包覆在該基材之單面或雙 面之第-包覆膜層、以及包覆在該第—覆膜層上之第: ,覆膜層所構成,上述第二覆膜層係固定有經磷灰:: 覆之光觸媒粒子之光觸媒含有層, 、^ 該方法之特徵為 在不除去上述光觸媒片 之上述光 316575 1261026 觸媒、含有芦 曰5私接合面重疊並使該接八而5 士 1 6 ·如申請專利簕圖楚 ° 互相接合。 執圍弟1 5項之光觸媒片接八 存在於前诚拉八二 4 °方法’其中使 合。〜接&面之樹脂或橡膠彼此進㈣ 17. 如申請專利範圍第16項之光觸媒片接 述光觸媒含有属 _ 方法’其中前 於用來固定經鱗灰石包覆之光觸媒粒子相對 橡膠之比例為;之光觸媒粒子之樹脂或 1 J 4 10至60重量%。 18. —種光觸媒片 在#其4方法,该光觸媒片係由基材及包覆 在5亥基材之單面或雙面之覆膜層所構成’且 上述覆膜層之最上層係 觸媒粒子之光觸媒含有層;K石包覆之光 該方法之特徵為: 上述光觸媒含有層包含樹脂或橡膠,而 覆之光觸媒含有層係由塗佈含有上述經磷灰石包 復之先觸媒粒子之分散液而形成。 19· 一種光觸媒片之劐 在該美 衣&方法,该光觸媒片係由基材及包覆 土 1早卸或雙面經之覆膜層所構成,且 、、復膜層之敢上層係固定有經碟方石勺孕夕决 觸媒粒子之光觸媒含有層;灰石包-之先 該方法之特徵為: 上述光觸媒含有層係由樹脂或橡膠組成, 光觸含有層係由使含有經•灰石包覆之 ” 之树月曰或橡膠形成片狀, 3(5 316575 1261026 ^ 再將該片狀之光觸媒含有層貼合在上述覆膜層之 取上層而形成上述光觸媒片。 2〇·^請專利範圍» 18項之光觸媒片製造方法,其中前 述7刀散液係由樹脂或橡膠、經磷灰石包覆之光觸媒粒 乂及有機溶劑所構成,該經填灰石包覆之光觸媒粒 子相對於上述光觸媒含有層中用來固定上述經磷灰石 包覆之光觸媒粒子之樹脂或橡膠之比例在10至90重量 %之範圍。 21·如申請專利範圍第18項之光觸媒片製造方法,其中前 述分散液係由樹脂或橡膠,經磷灰石包覆之 子、以及水所構成,該經磷灰石包覆之光觸媒粒子相對 於上述光觸媒含有層中用來固定經磷灰石包覆之光觸 媒粒子之樹脂或橡膠之比例為丨〇至9〇重量%之範圍。
316575