TW202102733A - 碳化矽基板 - Google Patents
碳化矽基板 Download PDFInfo
- Publication number
- TW202102733A TW202102733A TW109115745A TW109115745A TW202102733A TW 202102733 A TW202102733 A TW 202102733A TW 109115745 A TW109115745 A TW 109115745A TW 109115745 A TW109115745 A TW 109115745A TW 202102733 A TW202102733 A TW 202102733A
- Authority
- TW
- Taiwan
- Prior art keywords
- silicon carbide
- carbide substrate
- main surface
- chamfered portion
- atoms
- Prior art date
Abstract
本發明之碳化矽基板具有第1主面、第2主面、及倒角部。第2主面位於與第1主面相反之側。倒角部連接於第1主面及第2主面之各者。最大直徑為150 mm以上。倒角部中之表面錳濃度為1×1011
atoms/cm2
以下。
Description
本發明係關於一種碳化矽基板。本案主張基於2019年5月17日提出申請之日本專利申請即日本專利特願2019-093883號之優先權。該日本專利申請所記載之所有記載內容藉由參照而被引用至本說明書中。
於國際專利公開第2016/063632號(專利文獻1)中記載有洗淨碳化矽基板之方法。
[先前技術文獻]
[專利文獻]
[專利文獻1]國際專利公開第2016/063632號
[發明所欲解決之問題]
本發明之目的在於提供一種淨化度較高之碳化矽基板。
本發明之碳化矽基板具備第1主面、第2主面、及倒角部。第2主面位於與第1主面相反之側。倒角部連接於第1主面及第2主面之各者。最大直徑為150 mm以上。倒角部中之表面錳濃度為1×1011
atoms/cm2
以下。
[發明之效果]
根據本發明,可提供一種淨化度較高之碳化矽基板。
[本發明之實施形態之說明]
首先,列舉本發明之實施形態進行說明。
(1)本發明之碳化矽基板100具備第1主面1、第2主面2、及倒角部6。第2主面2位於與第1主面1相反之側。倒角部6連接於第1主面1及第2主面2之各者。最大直徑為150 mm以上。倒角部6中之表面錳濃度為1×1011
atoms/cm2
以下。
(2)如上述(1)之碳化矽基板100中,亦可為,倒角部6中之算術平均粗糙度大於第1主面1及第2主面2之各者中之算術平均粗糙度。
(3)如上述(1)或(2)之碳化矽基板100中,亦可為,倒角部6中之表面鈉濃度為1×108
atoms/cm2
以上。
(4)如上述(1)至(3)中任一項之碳化矽基板100中,亦可為,倒角部6中之表面鈉濃度為3×1011
atoms/cm2
以下。
(5)如上述(1)至(4)中任一項之碳化矽基板100中,亦可為,倒角部6中之表面鉀濃度為1×1011
atoms/cm2
以下。
(6)如上述(1)至(5)中任一項之碳化矽基板100中,亦可為,倒角部6中之表面鐵濃度為1×1011
atoms/cm2
以下。
[本發明之實施形態之詳細內容]
以下,基於圖式說明本發明之實施形態。再者,於以下之圖式中,對相同或相當之部分標記相同之參照編號,不重複其說明。於本說明書中之結晶學記載中,分別用[]表示個別方位,用<>表示集合方位,用()表示個別面,用{}表示集合面。又,關於負之指數,結晶學上,將“-”(橫條)標記於數字之上,於本說明書中,於數字之前標記負之符號。
<碳化矽基板之構成>
首先,對本實施形態之碳化矽基板100之構成進行說明。圖1係表示本實施形態之碳化矽基板100之構成之俯視模式圖。圖2係沿圖1之II-II線之剖面模式圖。
如圖1及圖2所示,本實施形態之碳化矽基板100主要具有第1主面1、第2主面2、及倒角部6。第2主面2位於與第1主面1相反之側。倒角部6連接於第1主面1及第2主面2之各者。第1主面1及第2主面2之各者為平坦面。第1主面1係供磊晶層(未圖示)形成之面。碳化矽基板100例如包含多型4H之六方晶體碳化矽單晶。碳化矽基板100例如包含氮等n型雜質。
第1主面1係例如{0001}面或相對於{0001}面偏離8°以下而成之面。具體而言,第1主面1係例如(0001)面或相對於(0001)面偏離8°以下而成之面。第1主面1亦可為例如(000-1)面或相對於(000-1)面偏離8°以下而成之面。於第1主面1為(0001)面之情形時,第2主面2為(000-1)面。
如圖2所示,倒角部6具有第1彎曲區域3、外周端部5、及第2彎曲區域4。第1彎曲區域3連接於第1主面1。第1彎曲區域3位於較第1主面1更外側。第2彎曲區域4連接於第2主面2。第2彎曲區域4位於較第2主面2更外側。如圖2所示,於與第1主面1垂直之剖面中,第1彎曲區域3及第2彎曲區域4之各者為圓弧狀。第1彎曲區域3及第2彎曲區域4之各者以向外側突出之方式彎曲。
外周端部5係於與第1主面1平行之徑向上位於最外側之部分。外周端部5連接於第1彎曲區域3及第2彎曲區域4之各者。於徑向上,第1彎曲區域3位於第1主面1與外周端部5之間。同樣地,於徑向上,第2彎曲區域4位於第2主面2與外周端部5之間。
如圖1所示,外周端部5具有定位平面部7、及圓弧狀部8。圓弧狀部8連接於定位平面部7。定位平面部7沿著第1方向101延伸。第1方向101及第2方向102之各者與第1主面1平行。第2方向102係與第1方向101垂直之方向。第1方向101係例如<11-20>方向。第2方向102係例如<1-100>方向。
於第1主面1相對於{0001}面傾斜之情形時,第1方向101亦可為例如將<11-20>方向投影於第1主面1之方向。於第1主面1相對於{0001}面傾斜之情形時,第2方向102亦可為例如將<1-100>方向投影於第1主面1之方向。
如圖1所示,碳化矽基板100之最大直徑(第1寬度W1)為150 mm以上。於與第1主面1垂直之方向觀察,碳化矽基板100之最大直徑亦可作為包含圓弧狀部8之圓之直徑而計算。第1寬度W1亦可為200 mm以上,亦可為250 mm以上。第1寬度W1之上限並無特別限定,例如亦可為300 mm以下。
如圖1所示,於與第1主面1垂直之方向觀察,倒角部6之寬度(第2寬度W2)例如為0.1 mm以上0.3 mm以下。就另一觀點而言,於與第1主面1垂直之方向觀察,自第1主面1與倒角部6之交界至外周端部5為止之距離例如為0.1 mm以上0.3 mm以下。
圖3係圖2之區域III之放大模式圖。如圖3所示,於倒角部6形成有複數個階差(研削痕9)。研削痕9例如沿著圓周方向形成。
於倒角部6形成有研削痕9。因此,倒角部6中之算術平均粗糙度(Ra)大於第1主面1及第2主面2之各者中之算術平均粗糙度。第1主面1及第2主面2之各者中之算術平均粗糙度例如為0.056 nm。第1主面1及第2主面2之各者中之算術平均粗糙度例如亦可為0.03 nm以上0.2 nm以下。倒角部6中之算術平均粗糙度(Ra)例如為0.1 μm。倒角部6中之算術平均粗糙度(Ra)例如亦可為0.05 μm以上0.5 μm以下。
其次,對於算術平均粗糙度(Ra)之測定方法進行說明。
算術表面粗糙度(Ra)可使用原子力顯微鏡(AFM:Atomic Force Microscope)或觸針式表面粗糙度測定器進行測定。作為AFM,例如可使用Veeco公司製造之「Dimension300」。作為懸臂(探針),例如可使用Bruker公司製造之型號「NCHV-10V」。作為觸針式表面粗糙度測定器,例如可使用東京精密公司製造之「Surfcom 1800G」。
AFM之測定範圍設為自第1主面1與倒角部6之交界10至外周端部5為止之區域。將第1主面1與倒角部6之交界10與外周端部5相連之直線A為基準高度。作為AFM之測定條件,例如將測定模式設為輕敲模式,將間距設為40 nm,及將測定深度設為1.0 μm。輕敲模式中之取樣係例如將掃描速度設為每1個週期5秒,將每1個掃描線之資料數設為512個點,且將掃描線數設為512。又,懸臂之位移控制例如設定為15.50 nm。
其次,對於倒角部6中之金屬雜質之濃度進行說明。
研削痕9容易附著有包含錳之沈澱物。於本實施形態之碳化矽基板100中,減少倒角部6中之包含錳(Mn)之沈澱物。具體而言,倒角部6中之錳之濃度為1×1011
atoms/cm2
以下。倒角部6中之錳之濃度較佳為1×1010
atoms/cm2
以下,進而較佳為1×109
atoms/cm2
以下。倒角部6中之錳之濃度之下限並無特別限定,例如為1×108
atoms/cm2
以上。
於本實施形態之碳化矽基板100中,倒角部6中之鈉(Na)之濃度例如為1×108
atoms/cm2
以上。倒角部6中之鈉之濃度例如亦可為1×109
atoms/cm2
以上,亦可為1×1010
atoms/cm2
以上。倒角部6中之鈉之濃度之上限並無特別限定,例如亦可為3×1011
atoms/cm2
以下。
於本實施形態之碳化矽基板100中,倒角部6中之鉀(K)之濃度例如為1×1011
atoms/cm2
以下。倒角部6中之鉀之濃度例如亦可為8×1010
atoms/cm2
以下,例如亦可為6×1010
atoms/cm2
以下。倒角部6中之鉀之濃度之下限並無特別限定,例如為1×108
atoms/cm2
以上。
於本實施形態之碳化矽基板100中,倒角部6中之鐵(Fe)之濃度例如為1×1011
atoms/cm2
以下。倒角部6中之鐵之濃度例如亦可為8×1010
atoms/cm2
以下。倒角部6中之鐵之濃度之下限並無特別限定,例如為1×108
atoms/cm2
以上。
其次,對於倒角部6中之金屬雜質之濃度之測定方法進行說明。
首先,使用水平型基板檢查裝置,將酸滴加至碳化矽基板100之倒角部6之全周(定位平面部7除外),藉此倒角部6上之金屬雜質被酸吸收。其次,自倒角部6之全周全量回收包含金屬雜質之酸。再者,試樣製備係於潔淨度100之無塵室內設置之潔淨度10之潔淨通風室(clean draft)內實施。
金屬雜質之濃度可藉由ICP-MS(Inductively Coupled Plasma Mass Spectrometry,感應耦合電漿質譜儀)進行測定。作為測定裝置,例如可使用Agillent公司製造之ICP-MS8800。將測定所得之金屬雜質元素之質量(ng)除以各元素之原子量並換算成莫耳數後,乘以亞佛加厥數轉換成原子數。其次,藉由將該原子數除以倒角部6之面積,而換算出每單位面積之原子數。金屬雜質之濃度係每單位面積之原子數。再者,於碳化矽基板100之最大直徑為150 mm之情形時,倒角部6之面積約為3.78 cm2
。倒角部6之面積係作為就與第1主面1垂直之方向觀察到的將碳化矽基板100之外周端部5之長度設為長邊,且將倒角部6之寬度(第2寬度W2)設為短邊之長方形之面積而計算(參照圖1)。
其次,對於第1主面1中之金屬雜質之濃度進行說明。
於第1主面1亦可存在錳。於第1主面1中,錳之濃度亦可為1×109
atoms/cm2
以下。第1主面1中之錳之濃度低於倒角部6中之錳之濃度。
於第1主面1亦可存在鈉。於第1主面1中,鈉之濃度亦可為5×1010
atoms/cm2
以下。第1主面1中之鈉之濃度低於倒角部6中之鈉之濃度。
第1主面1亦可存在鉀。於第1主面1中,鉀之濃度亦可為2×1010
atoms/cm2
以下。第1主面1中之鉀之濃度低於倒角部6中之鉀之濃度。
於第1主面1亦可存在鐵。於第1主面1中,鐵之濃度亦可為5×109
atoms/cm2
以下。第1主面1中之鐵之濃度低於倒角部6中之鐵之濃度。
於第1主面1亦可存在硫(S)。於第1主面1中,硫之濃度亦可為5×1010
atoms/cm2
以上。於第1主面1中,硫之濃度亦可為1×1012
atoms/cm2
以上。
於第1主面1亦可存在氯(Cl)。於第1主面1中,氯之濃度亦可為5×1010
atoms/cm2
以上。於第1主面1中,氯之濃度亦可為1×1012
atoms/cm2
以上。
其次,對於第1主面1中之金屬雜質之濃度之測定方法進行說明。
金屬雜質之濃度可藉由全反射螢光X射線分析裝置進行測定。作為分析裝置,例如可使用Rigaku股份有限公司製造之TXRF-3760。該分析裝置具有複數種激發X射線源,可使用最適合測定元素之激發X射線自輕元素之Na測定至重元素之U。具體而言,對於Na,使用W-Ma(1.78 keV)之激發X射線。對於K、S、Fe、Cl及Mn,使用W-Lb(9.67 keV)之激發X射線。
X射線功率例如為35 kV-255 mA。入射方位為39°。W-Ma之入射角度為0.500°。W-Ma之測定時間為10秒/點。W-Lb之入射角度為0.100°。W-Lb之測定時間為10秒/點。又,該分析裝置具有XY驅動平台,可對測定元素之面內分佈進行測定。例如可將第1主面1等面積地分割成101個部位之區域,於該101個部位中對測定元素之濃度進行測定。第1主面中之金屬雜質之濃度設為該101個部位之濃度之平均值。金屬雜質之濃度係每單位面積之原子數。
<碳化矽基板之製造方法>
其次,對於本實施形態之碳化矽基板100之製造方法進行說明。如圖4所示,本實施形態之碳化矽基板100之製造方法包括:結晶準備步驟(S10)、切片步驟(S20)、倒角步驟(S25)、雙面機械研磨步驟(S30)、化學機械研磨步驟(S40)、硫酸過氧化氫混合物洗淨步驟(S50)、氨水過氧化氫混合物洗淨步驟(S60)、鹽酸過氧化氫混合物洗淨步驟(S70)、氫氟酸洗淨步驟(S80)、及乾燥步驟(S90)。
首先,實施結晶準備步驟(S10)。於結晶準備步驟(S10)中,例如藉由昇華法而形成有碳化矽錠塊。其次,實施切片步驟(S20)。於切片步驟(S20)中,碳化矽錠塊藉由切割鋼絲切成複數個碳化矽基板100。碳化矽基板100例如包含多型4H之六方晶體碳化矽單晶。如圖5所示,碳化矽基板100具有第1主面1、第2主面2、及外周端部5。於該時間點,未形成有倒角部6。
其次,實施倒角步驟(S25)。於倒角步驟(S25)中,使用研削裝置25。於倒角步驟中,例如使用金剛石研磨粒。如圖6所示,碳化矽基板100之第1主面1與外周端部5之交界附近壓抵於旋轉之研削裝置25。同樣地,如圖7所示,碳化矽基板100之第1主面1與外周端部5之交界附近壓抵於旋轉之研削裝置25。藉由以上,於碳化矽基板100形成有倒角部6(參照圖2)。於倒角步驟(S25)中,可於倒角部6形成研削痕。
其次,實施雙面機械研磨步驟(S30)。具體而言,碳化矽基板100以第1主面1與第1壓盤(未圖示)相對向,且第2主面2與第2壓盤(未圖示)相對應之方式配置於第1壓盤與第2壓盤之間。其次,於第1主面1與第1壓盤之間及第2主面2與第2壓盤之間導入有漿料。漿料例如包括金剛石研磨粒及水。金剛石研磨粒之直徑例如為0.5 μm以上3 μm以下。藉由第1壓盤對第1主面1施加負載,且藉由第2壓盤對第2主面2施加負載,藉此對碳化矽基板100之雙面進行機械研磨。
其次,實施化學機械研磨步驟(S40)。具體而言,首先,於碳化矽基板100之第1主面1中,進行CMP(Chemical Mechanical Polishing,化學機械研磨)。作為研磨粒,例如使用膠體氧化矽。使用包含高錳酸鹽之研磨液。於壓盤安裝有研磨布。研磨布例如為不織布。加工壓力例如為300 g/cm2
。研磨液之流量例如為50 cc/分鐘。壓盤之轉速例如為40 rpm。加工時間例如為2小時。
其次,實施硫酸過氧化氫混合物洗淨步驟(S50)。於硫酸過氧化氫混合物洗淨步驟(S50)中,使用超音波洗淨裝置。如圖8所示,超音波洗淨裝置20主要具有超音波發生源19、第1洗淨槽12、及第2洗淨槽13。第2洗淨槽13配置於第1洗淨槽12上。第2洗淨槽13架設於第1洗淨槽12之開口部。於第1洗淨槽12中放入有第1洗淨液14(具體而言為水)。於第2洗淨槽13中放入有第2洗淨液15(具體而言為硫酸過氧化氫混合物)。碳化矽基板100浸漬於硫酸過氧化氫混合物。超音波發生源19配置於第2洗淨槽13之底。第2洗淨槽13配置於超音波發生源19上。
於硫酸過氧化氫混合物洗淨步驟(S50)中,為了提高金屬雜質之去除效果,於超音波照射至硫酸過氧化氫混合物之狀態下洗淨碳化矽基板100。超音波之頻率例如為450 kHz以上2 MHz以下。藉由超音波促進化學反應。藉此,提高金屬雜質對於硫酸過氧化氫混合物之反應性。又,藉由由超音波照射所引起之空穴效應,可有效地去除進入至倒角部6之研削痕之包含錳之沈澱物。
於硫酸過氧化氫混合物洗淨步驟(S50)中,主要去除有機物及金屬雜質等。硫酸過氧化氫混合物係硫酸、過氧化氫水、與超純水混合而成之溶液。作為硫酸,例如可使用質量百分率濃度為96%之濃硫酸。作為過氧化氫水,例如可使用質量百分率濃度為30%之過氧化氫水。對於之後之步驟中所使用之過氧化氫水亦相同。
硫酸過氧化氫混合物所包含之硫酸、過氧化氫水、與超純水之體積比率例如為10(硫酸):1(過氧化氫水):1(超純水)至10(硫酸):3(過氧化氫水):1(超純水)。換言之,硫酸之體積為超純水之體積之10倍。過氧化氫水之體積為超純水之體積之1倍以上3倍以下。碳化矽基板100之浸漬時間例如為5分鐘以上。硫酸過氧化氫混合物之溫度例如為室溫。
其次,實施氨水過氧化氫混合物洗淨步驟(S60)。於氨水過氧化氫混合物洗淨步驟(S60)中,主要去除研磨劑及灰塵。氨水過氧化氫混合物係氨水溶液、過氧化氫水、與超純水混合而成之溶液。作為氨水溶液,例如可使用質量百分率濃度為28%之氨水溶液。於氨水過氧化氫混合物洗淨步驟(S60)中,亦可於超音波照射至氨水過氧化氫混合物之狀態下洗淨碳化矽基板100。
氨水過氧化氫混合物所包含之氨水溶液、過氧化氫水、與超純水之體積比率為1(氨水溶液):1(過氧化氫水):5(超純水)至1(氨水溶液):1(過氧化氫水):10(超純水)。換言之,氨水溶液之體積為超純水之體積之1/10倍以上1/5倍以下。又,過氧化氫水之體積為超純水之體積之1/10倍以上1/5倍以下。碳化矽基板100之浸漬時間例如為5分鐘以上。硫酸過氧化氫混合物之溫度例如為室溫。
其次,實施鹽酸過氧化氫混合物洗淨步驟(S70)。於鹽酸過氧化氫混合物洗淨步驟(S70)中,主要去除重金屬之鹽酸過氧化氫混合物係鹽酸、過氧化氫水、與超純水混合而成之溶液。作為鹽酸,例如可使用質量百分率濃度為98%之濃鹽酸。於鹽酸過氧化氫混合物洗淨步驟(S70)中,亦可於超音波照射至鹽酸過氧化氫混合物之狀態下洗淨碳化矽基板100。
鹽酸過氧化氫混合物所包含之鹽酸、過氧化氫水、與超純水之體積比率例如為1(鹽酸):1(過氧化氫水):5(超純水)至1(鹽酸):1(過氧化氫水):10(超純水)。換言之,鹽酸之體積為超純水之體積之1/10倍以上1/5倍以下。又,過氧化氫水之體積為超純水之體積之1/10倍以上1/5倍以下。碳化矽基板100之浸漬時間例如為5分鐘以上。硫酸過氧化氫混合物之溫度例如為室溫。
其次,實施氫氟酸洗淨步驟(S80)。於氫氟酸洗淨步驟(S80)中,藉由氫氟酸去除氧化矽膜,表面藉由氟終止。氫氟酸與超純水混合而成之混合液中之氫氟酸之濃度例如為10%以上40%以下。碳化矽基板100之浸漬時間例如為5分鐘以上。硫酸過氧化氫混合物之溫度例如為室溫。於氫氟酸洗淨步驟(S80)中,亦可於超音波照射至氫氟酸之狀態下洗淨碳化矽基板100。
其次,實施乾燥步驟(S90)。於乾燥步驟(S90)中,例如使用旋轉乾燥機30,使碳化矽基板100乾燥。如圖9所示,旋轉乾燥機30具備本體部31、蓋32、開口部34、及排氣口33。旋轉乾燥機30配置於相當於潔淨度100之無塵室。向旋轉乾燥機30投入碳化矽基板100前,於打開旋轉乾燥機30之蓋32之狀態下,使空氣自旋轉乾燥機30之開口部34向排氣口33通過。本體部之容積例如為127000 cm3
。開口部34之面積例如為2700 cm2
。空氣之通過量例如為60 m3
。
其次,碳化矽基板100配置於旋轉乾燥機30之本體部31,蓋32閉合。碳化矽基板100於通過排氣口33進行減壓之狀態下,繞著與第1主面1大致垂直之旋轉軸旋轉。碳化矽基板100之轉速例如為800 rpm。旋轉時間例如為300秒。藉此,藉由離心力去除附著於碳化矽基板100之洗淨液。
其次,對於本實施形態之作用效果進行說明。
近年,為了提高研磨效果,於碳化矽基板100之研磨步驟中,利用包含高錳酸鹽之研磨液。包含高錳酸鹽之研磨液對於碳化矽基板100之研磨效率較高,另一方面,具有容易作為雜質殘留於碳化矽基板100之性質。由例如高錳酸鉀用作著色料之原料亦可知,高錳酸鉀鹽容易成為泥狀之沈澱物,附著於碳化矽基板100。
特別是,於碳化矽基板100之倒角部6,藉由倒角步驟(S25)之研削加工形成有研削痕9。包含高錳酸鹽之沈澱物容易與研磨粒等一起進入至研削痕9。一旦沈澱物進入至研削痕9,則難以藉由一般之洗淨方法去除。
於本實施形態之碳化矽基板100之硫酸過氧化氫混合物洗淨步驟(S50)中,於超音波照射至硫酸過氧化氫混合物之狀態下洗淨碳化矽基板100。藉由超音波促進化學反應。藉此,提高錳等金屬雜質對於硫酸過氧化氫混合物之反應性。又,藉由由超音波照射所引起之空穴效應,可有效地去除進入至倒角部6之研削痕9之包含錳之沈澱物。因此,可降低倒角部6中之錳之濃度。具體而言,可將倒角部6中之錳之濃度設為1×1011
atoms/cm2
以下。藉此,可獲得淨化度較高之碳化矽基板100。結果,於使用碳化矽基板100製作碳化矽半導體裝置時,可抑制因錳等金屬雜質而使碳化矽半導體裝置之電特性變差。
[實施例]
(樣品準備)
首先,準備樣品1之碳化矽基板100、及樣品2之碳化矽基板100。樣品1之碳化矽基板100為實施例。樣品2之碳化矽基板100為比較例。碳化矽基板100之最大直徑(直徑)設為150 mm。
樣品1之碳化矽基板100藉由本實施形態之製造方法而製造。具體而言,於硫酸過氧化氫混合物洗淨步驟(S50)中,超音波照射至硫酸過氧化氫混合物。超音波之頻率設為950 kHz。硫酸過氧化氫混合物所包含之硫酸、過氧化氫水、與超純水之體積比率設為10(硫酸):1(過氧化氫水):1(超純水)。碳化矽基板100之浸漬時間設為30分鐘。硫酸過氧化氫混合物之溫度設為室溫。另一方面,根據樣品2之碳化矽基板100之製造方法,於硫酸過氧化氫混合物洗淨步驟(S50)中,超音波未照射至硫酸過氧化氫混合物。其他製造條件與樣品1之碳化矽基板100之製造方法相同。
(測定方法)
其次,使用水平型基板檢查裝置,將酸滴加至碳化矽基板100之倒角部6之全周(定位平面部7除外),自倒角部6之全周回收包含金屬雜質之酸。金屬雜質之濃度藉由ICP-MS進行測定。作為測定裝置,例如使用Agillent公司製造之ICP-MS8800。將測定所得之金屬雜質元素之質量除以各元素之原子量並換算成莫耳數後,乘以亞佛加厥數轉換成原子數。其次,藉由將該原子數除以倒角部6之面積,而換算出每單位面積之原子數。再者,碳化矽基板100之倒角部6之面積為3.78 cm2
。又,使用觸針式表面粗糙度測定器,測定倒角部中之算術平均粗糙度(Ra)。作為測定裝置,使用東京精密公司製造之Surfcom 1800G。
(測定結果)
[表1]
元素 | 樣品1 | 樣品2 |
單位 | 1010 atms/cm2 | 1010 atoms/cm2 |
Na | 11.0 | 46.0 |
K | 4.7 | 4.1 |
Mn | - | 12.0 |
Fe | 7.2 | 21.0 |
表1表示倒角部6中之金屬雜質之濃度。如表1所示,於樣品1之碳化矽基板100之倒角部6中,鈉(Na)之濃度為11.0×1010
atoms/cm2
。鉀(K)之濃度為4.7×1010
atoms/cm2
。未檢測到錳(Mn)。鐵(Fe)之濃度為7.2×1010
atoms/cm2
。
如表1所示,於樣品2之碳化矽基板100之倒角部6中,鈉(Na)之濃度為46.0×1010
atoms/cm2
。鉀(K)之濃度為4.1×1010
atoms/cm2
。錳(Mn)為12.0×1010
atoms/cm2
。鐵(Fe)之濃度為21.0×1010
atoms/cm2
。
[表2]
表2表示倒角部6中之算術平均粗糙度(Ra)。如表2所示,樣品1之碳化矽基板100之倒角部6中之算術平均粗糙度(Ra)為0.1 μm。另一方面,樣品2之碳化矽基板100之倒角部6中之算術平均粗糙度(Ra)為0.1 μm。
樣品1 | 樣品2 | |
算術平均粗糙度(Ra) | 0.1 μm | 0.1 μm |
如上所示,可確認,藉由於超音波照射至硫酸過氧化氫混合物之狀態下洗淨碳化矽基板100,可去除附著於倒角部6之包含錳(Mn)之沈澱物,從而製造倒角部6中之錳之濃度較低之碳化矽基板100。
應認為此次揭示之實施形態及實施例於所有方面皆為例示,並非限制。本發明之範圍由申請專利範圍表示而並非由上述說明表示,且意圖包含與申請專利範圍均等之含義、及範圍內之所有變更。
1:第1主面
2:第2主面
3:第1彎曲區域
4:第2彎曲區域
5:外周端部
6:倒角部
7:定位平面部
8:圓弧狀部
9:研削痕
10:交界
12:第1洗淨槽
13:第2洗淨槽
14:第1洗淨液
15:第2洗淨液
19:超音波發生源
20:超音波洗淨裝置
25:研削裝置
30:旋轉乾燥機
31:本體部
32:蓋
33:排氣口
34:開口部
100:碳化矽基板
101:第1方向
102:第2方向
A:直線
W1:第1寬度
W2:第2寬度
圖1係表示本實施形態之碳化矽基板之構成之俯視模式圖。
圖2係沿圖1之II-II線之剖面模式圖。
圖3係圖2之區域III之放大模式圖。
圖4係概略性地表示本實施形態之碳化矽基板之製造方法之流程圖。
圖5係表示本實施形態之碳化矽基板之製造方法之第1步驟的剖面模式圖。
圖6係表示本實施形態之碳化矽基板之製造方法之第2步驟的剖面模式圖。
圖7係表示本實施形態之碳化矽基板之製造方法之第3步驟的剖面模式圖。
圖8係表示本實施形態之碳化矽基板之製造方法之第4步驟的剖面模式圖。
圖9係表示本實施形態之碳化矽基板之製造方法之第5步驟的剖面模式圖。
1:主面
3:第1彎曲區域
5:外周端部
6:倒角部
7:定位平面部
8:圓弧狀部
100:碳化矽基板
101:第1方向
102:第2方向
W1:第1寬度
W2:第2寬度
Claims (17)
- 一種碳化矽基板,其具備:第1主面; 第2主面,其與上述第1主面為相反側;及 倒角部,其連接於上述第1主面及上述第2主面之各者; 最大直徑為150 mm以上,且 上述倒角部中之表面錳濃度為1×1011 atoms/cm2 以下。
- 如請求項1之碳化矽基板,其中上述倒角部中之算術平均粗糙度大於上述第1主面及上述第2主面之各者中之算術平均粗糙度。
- 如請求項1或2之碳化矽基板,其中上述倒角部中之表面鈉濃度為1×108 atoms/cm2 以上。
- 如請求項1或2之碳化矽基板,其中上述倒角部中之表面鈉濃度為3×1011 atoms/cm2 以下。
- 如請求項3之碳化矽基板,其中上述倒角部中之表面鈉濃度為3×1011 atoms/cm2 以下。
- 如請求項1或2之碳化矽基板,其中上述倒角部中之表面鉀濃度為1×1011 atoms/cm2 以下。
- 如請求項3之碳化矽基板,其中上述倒角部中之表面鉀濃度為1×1011 atoms/cm2 以下。
- 如請求項4之碳化矽基板,其中上述倒角部中之表面鉀濃度為1×1011 atoms/cm2 以下。
- 如請求項5之碳化矽基板,其中上述倒角部中之表面鉀濃度為1×1011 atoms/cm2 以下。
- 如請求項1或2之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項3之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項4之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項5之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項6之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項7之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項8之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。
- 如請求項9之碳化矽基板,其中上述倒角部中之表面鐵濃度為1×1011 atoms/cm2 以下。