RU2011103769A - Привитой полиэтилен - Google Patents
Привитой полиэтилен Download PDFInfo
- Publication number
- RU2011103769A RU2011103769A RU2011103769/04A RU2011103769A RU2011103769A RU 2011103769 A RU2011103769 A RU 2011103769A RU 2011103769/04 A RU2011103769/04 A RU 2011103769/04A RU 2011103769 A RU2011103769 A RU 2011103769A RU 2011103769 A RU2011103769 A RU 2011103769A
- Authority
- RU
- Russia
- Prior art keywords
- group
- polyethylene
- silane
- bond
- unsaturated silane
- Prior art date
Abstract
1. Способ прививки гидролизуемых силановых групп к полиэтилену, включающий взаимодействие полиэтилена при температуре свыше 140°C с ненасыщенным силаном, имеющим, по меньшей мере, одну гидролизуемую группу, связанную с Si, в присутствии соединения или средств, способных генерировать свободно-радикальные центры в полиэтилене, отличающийся тем, что силан имеет формулу R"-CH=CH-Z (I) или R"-C≡C-Z (II), в которой Z означает электроноакцепторную составляющую, замещенную группой -SiRaR'(3-а), где R означает гидролизуемую группу; R' означает гидрокарбильную группу с 1-6 атомами углерода; а имеет значение в диапазоне от 1 до 3 включительно; и R" означает водород или группу, обладающую электроноакцепторным или любым другим активирующим действием в отношении -СН=СН- или -С≡С- связи. ! 2. Способ по п.1, отличающийся тем, что каждая группа R в ненасыщенном силане (I) или (II) представляет собой алкоксигруппу. ! 3. Способ по п.1, отличающийся тем, что ненасыщенный силан (I) или (II) является частично гидролизованным и конденсированным до олигомеров. ! 4. Способ по п.1, отличающийся тем, что силан имеет формулу R"-CH=CH-X-Y-SiRaR'(3-а) (III) или R"-C≡C-X-Y-SiRaR'(3-а) (IV), в которых Х означает химическую мостиковую связь, обладающую электроноакцепторным действием в отношении -СН=СН- или -С≡С- связи, и Y означает двухвалентную органическую спейсерную мостиковую связь, содержащую, по меньшей мере, один атом углерода, отделяющий мостиковую связь Х от атома Si. ! 5. Способ по п.4, отличающийся тем, что силан имеет формулу R"-CH=CH-X-Y-SiRaR'(3-а) (III) и составляющая R"-CH=CH-X-Y- представляет собой акрилоксиалкильную группу. ! 6. Способ по п.5, отличающийся тем, что ненасыщенный силан (I) включает γ-акрилоксипропилтр
Claims (21)
1. Способ прививки гидролизуемых силановых групп к полиэтилену, включающий взаимодействие полиэтилена при температуре свыше 140°C с ненасыщенным силаном, имеющим, по меньшей мере, одну гидролизуемую группу, связанную с Si, в присутствии соединения или средств, способных генерировать свободно-радикальные центры в полиэтилене, отличающийся тем, что силан имеет формулу R"-CH=CH-Z (I) или R"-C≡C-Z (II), в которой Z означает электроноакцепторную составляющую, замещенную группой -SiRaR'(3-а), где R означает гидролизуемую группу; R' означает гидрокарбильную группу с 1-6 атомами углерода; а имеет значение в диапазоне от 1 до 3 включительно; и R" означает водород или группу, обладающую электроноакцепторным или любым другим активирующим действием в отношении -СН=СН- или -С≡С- связи.
2. Способ по п.1, отличающийся тем, что каждая группа R в ненасыщенном силане (I) или (II) представляет собой алкоксигруппу.
3. Способ по п.1, отличающийся тем, что ненасыщенный силан (I) или (II) является частично гидролизованным и конденсированным до олигомеров.
4. Способ по п.1, отличающийся тем, что силан имеет формулу R"-CH=CH-X-Y-SiRaR'(3-а) (III) или R"-C≡C-X-Y-SiRaR'(3-а) (IV), в которых Х означает химическую мостиковую связь, обладающую электроноакцепторным действием в отношении -СН=СН- или -С≡С- связи, и Y означает двухвалентную органическую спейсерную мостиковую связь, содержащую, по меньшей мере, один атом углерода, отделяющий мостиковую связь Х от атома Si.
5. Способ по п.4, отличающийся тем, что силан имеет формулу R"-CH=CH-X-Y-SiRaR'(3-а) (III) и составляющая R"-CH=CH-X-Y- представляет собой акрилоксиалкильную группу.
6. Способ по п.5, отличающийся тем, что ненасыщенный силан (I) включает γ-акрилоксипропилтриметоксисилан.
7. Способ по п.5, отличающийся тем, что ненасыщенный силан (I) включает акрилоксиметилтриметоксисилан.
8. Способ по п.5, отличающийся тем, что ненасыщенный силан (I) включает смесь γ-акрилоксипропилтриметоксисилана с акрилоксиметилтриметоксисиланом, или смесь γ-акрилоксипропилтриметоксисилана и/или акрилоксиметилтриметоксисилана с винилтриметоксисиланом.
9. Способ по п.4, отличающийся тем, что группа R" в ненасыщенном силане (I) или (II) является электроноакцепторной группой формулы -X-Y-SiRaR'(3-а).
10. Способ по п.9, отличающийся тем, что ненасыщенный силан (I) включает бис(триалкоксисилилалкил)фумарат и/или бис(триалкоксисилилалкил)малеат.
11. Способ по п.1, отличающийся тем, что ненасыщенный силан (I) или (II) присутствует во время реакции прививки при 0,5-15 мас.% от общей композиции.
12. Способ по п.1, отличающийся тем, что соединение, способное генерировать свободно-радикальные центры в полиэтилене, преимущественно представляет собой органический пероксид и присутствует во время реакции прививки при 0,01-0,5 мас.% от общей композиции.
13. Способ по любому из пп.1-12, отличающийся тем, что силанолсодержащее силиконовое соединение добавляют после реакции прививки.
14. Способ по п.13, отличающийся тем, что силанолсодержащий силикон представляет собой твердую смолу MQ, содержащую 2-6 мас.% силанольных групп.
15. Способ по п.14, отличающийся тем, что силанолсодержащее соединение присутствует при 1-10 мас.% от общей композиции, полученной после реакции прививки.
16. Способ по п.1, отличающийся тем, что ненасыщенный силан (I) или (II) наносят на наполнитель перед осуществлением взаимодействия с полиэтиленом.
17. Полиэтилен, привитой гидролизуемыми силановыми группами, отличающийся тем, что полиэтилен содержит привитые составляющие формулы R"-CH(РЕ)-CH2-X-Y-SiRaR'(3-а) и/или привитые составляющие формулы R"-CH2-CH(РЕ)-X-Y-SiRaR'(3-а), где R означает гидролизуемую группу; R' означает гидрокарбильную группу с 1-6 атомами углерода; а имеет значение в диапазоне от 1 до 3 включительно; Х означает химическую мостиковую связь, обладающую электроноакцепторным действием в отношении -СН=СН- или -С≡С- связи; Y означает двухвалентную органическую спейсерную мостиковую связь, содержащую, по меньшей мере, один атом углерода, отделяющий мостиковую связь Х от Si атома; R" означает водород или группу формулы -X-Y-SiRaR'(3-а) и РЕ означает полиэтиленовую цепь.
18. Применение ненасыщенного силана формулы R"-CH=CH-Z (I) или R"-C≡C-Z (II), в которой Z означает электроноакцепторную составляющую, замещенную группой -SiRaR'(3-а), где R означает гидролизуемую группу; R' означает гидрокарбильную группу с 1-6 атомами углерода; а имеет значение в диапазоне от 1 до 3 включительно и R" означает водород или группу, обладающую электроноакцепторным или любым другим активирующим действием в отношении -СН=СН- или -С≡С- связи; в прививке гидролизуемых силановых групп к полиэтилену, что дает повышенную прививку по сравнению с олефиново-ненасыщенным силаном, не содержащим CH=CH-Z- или C≡C-Z составляющей.
19. Способ сшивки полиэтилена, отличающийся тем, что привитой полиэтилен по п.17 или полученный способом по любому из пп.1-16 сшивают под действием влаги необязательно в присутствии катализатора конденсации силанола.
20. Способ по п.19, отличающийся тем, что привитой полиэтилен формуют в изделие и впоследствии сшивают под действием влаги.
21. Способ по п.20, отличающийся тем, что привитой полиэтилен формуют в трубу и сшивают под действием воды, текущей сквозь трубу.