RU2009144271A - Противообрастающая покрывающая композиция на основе полиорганосилоксанполиоксиалкиленовых отверждаемых сополимеров - Google Patents
Противообрастающая покрывающая композиция на основе полиорганосилоксанполиоксиалкиленовых отверждаемых сополимеров Download PDFInfo
- Publication number
- RU2009144271A RU2009144271A RU2009144271/05A RU2009144271A RU2009144271A RU 2009144271 A RU2009144271 A RU 2009144271A RU 2009144271/05 A RU2009144271/05 A RU 2009144271/05A RU 2009144271 A RU2009144271 A RU 2009144271A RU 2009144271 A RU2009144271 A RU 2009144271A
- Authority
- RU
- Russia
- Prior art keywords
- groups
- crosslinking agent
- reactive groups
- coating composition
- block copolymer
- Prior art date
Abstract
1. Способ физического сдерживания биологического обрастания подложки в водной среде обитания биологических организмов, включающий формирование на подложке, перед воздействием на нее указанной окружающей среды, покрывающей композиции, содержащей (i) отверждаемый полиорганосилоксанполиоксиалкиленовый блок-сополимер, имеющий, по крайней мере, две реакционноспособные группы X, находящиеся в цепи сополимера и (ii) кремнийорганический сшивающий агент и/или катализатор. ! 2. Способ по п.1, где указанные группы X взаимодействуют друг с другом и где покрывающая композиция содержит катализатор и, необязательно, сшивающий агент. ! 3. Способ по п.1, где указанные группы X не взаимодействуют друг с другом, и где покрывающая композиция содержит кремнийорганический сшивающий агент, имеющий, по крайней мере, две группы Y взаимодействующие с указанными группами X. ! 4. Способ по п.3, где полиорганосилоксанполиоксиалкиленовый блок-сополимер имеет две реакционноспособные группы X в полиорганосилоксановом блоке на молекулу и где кремнийорганический сшивающий агент в среднем имеет более двух реакционноспособных групп Y на молекулу. ! 5. Способ по любому из предшествующих пунктов, где полиорганосилоксанполиоксиалкиленовый блок-сополимер является блок-сополимером вида PS-(A-PO-A-PS)n, где PS представляет полиорганосилоксановый блок, PO представляет полиоксиалкиленовый блок, A представляет двухвалентный фрагмент, и n имеет значение, по крайней мере, 1. ! 6. Способ по п.3, где реакционноспособные группы X являются Si-H группами, и сшивающий агент содержит этиленовоненасыщенные группы Y. ! 7. Способ по п.6, где покрывающая композиция содержит катализа�
Claims (15)
1. Способ физического сдерживания биологического обрастания подложки в водной среде обитания биологических организмов, включающий формирование на подложке, перед воздействием на нее указанной окружающей среды, покрывающей композиции, содержащей (i) отверждаемый полиорганосилоксанполиоксиалкиленовый блок-сополимер, имеющий, по крайней мере, две реакционноспособные группы X, находящиеся в цепи сополимера и (ii) кремнийорганический сшивающий агент и/или катализатор.
2. Способ по п.1, где указанные группы X взаимодействуют друг с другом и где покрывающая композиция содержит катализатор и, необязательно, сшивающий агент.
3. Способ по п.1, где указанные группы X не взаимодействуют друг с другом, и где покрывающая композиция содержит кремнийорганический сшивающий агент, имеющий, по крайней мере, две группы Y взаимодействующие с указанными группами X.
4. Способ по п.3, где полиорганосилоксанполиоксиалкиленовый блок-сополимер имеет две реакционноспособные группы X в полиорганосилоксановом блоке на молекулу и где кремнийорганический сшивающий агент в среднем имеет более двух реакционноспособных групп Y на молекулу.
5. Способ по любому из предшествующих пунктов, где полиорганосилоксанполиоксиалкиленовый блок-сополимер является блок-сополимером вида PS-(A-PO-A-PS)n, где PS представляет полиорганосилоксановый блок, PO представляет полиоксиалкиленовый блок, A представляет двухвалентный фрагмент, и n имеет значение, по крайней мере, 1.
6. Способ по п.3, где реакционноспособные группы X являются Si-H группами, и сшивающий агент содержит этиленовоненасыщенные группы Y.
7. Способ по п.6, где покрывающая композиция содержит катализатор, содержащий металл платиновой группы, и ее пакуют в два контейнера, так чтобы полиорганосилоксанполиоксиалкиленовый блок-сополимер, сшивающий агент и катализатор не находились все вместе в одной упаковке.
8. Способ по п.1, где реакционноспособные группы X являются Si-алкоксигруппами, которые взаимодействуют друг с другом и, в случае присутствия кремнийорганического сшивающего агента, реакционноспособные группы Y также являются Si-алкоксигруппами.
9. Способ по п.8, в котором реакционноспособная группа X выражается формулой -Si(R')2(OR), где R представляет собой алкильную группу, имеющую от 1 до 4 углеродных атомов, и каждый R' представляет собой алкильную группу, имеющую от 1 до 6 углеродных атомов, фенильную группу или алкоксигруппу формулы -OR.
10. Способ по п.8 или 9, в котором композиция содержит катализатор конденсации силоксанов, и композицию пакуют во влагонепроницаемый контейнер.
11. Способ по п.8 или 9, где каждый блок PS является полидиметилсилоксановым блоком.
12. Способ по п.1, где реакционноспособные группы X являются Si-алкоксигруппами, которые взаимодействуют друг с другом, и, в случае присутствия кремнийорганического сшивающего агента, реакционноспособные группы Y являются силаноловыми группами.
13. Способ по п.1, где реакционноспособные группы X являются силаноловыми группами, которые способны к взаимодействию друг с другом, и, если присутствует кремнийорганический сшивающий агент, реакционноспособные группы Y выбирают из алкокси, ацетокси, кетоксимных, амидных или гидроксильных групп, связанных с кремнием.
14. Подложка, покрытая покрытием, получаемым путем:
a) нанесения на поверхность покрывающей композиции, содержащей (i) отверждаемый полиорганосилоксанполиоксиалкиленовый блок-сополимер, имеющий в сополимере, по крайней мере, две реакционноспособные группы X, и (ii) кремнийорганический сшивающий агент и/или катализатор, и
b) и последующего отверждения покрывающей композиции.
15. Подложка по п.14, где подложка представляет собой подводную конструкцию.