PL4006178T3 - Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME - Google Patents

Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME

Info

Publication number
PL4006178T3
PL4006178T3 PL22151717.0T PL22151717T PL4006178T3 PL 4006178 T3 PL4006178 T3 PL 4006178T3 PL 22151717 T PL22151717 T PL 22151717T PL 4006178 T3 PL4006178 T3 PL 4006178T3
Authority
PL
Poland
Prior art keywords
manufacture
hardened part
lme
issues
lme issues
Prior art date
Application number
PL22151717.0T
Other languages
English (en)
Inventor
Christian Allely
Tiago MACHADO AMORIM
Raisa Grigorieva
David DUSSAUSSOIS
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of PL4006178T3 publication Critical patent/PL4006178T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/02—Stamping using rigid devices or tools
    • B21D22/022—Stamping using rigid devices or tools by heating the blank or stamping associated with heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • C22C21/08—Alloys based on aluminium with magnesium as the next major constituent with silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Articles (AREA)
  • Coating With Molten Metal (AREA)
PL22151717.0T 2015-07-30 2016-07-11 Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME PL4006178T3 (pl)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2015/001284 WO2017017484A1 (en) 2015-07-30 2015-07-30 Method for the manufacture of a hardened part which does not have lme issues

Publications (1)

Publication Number Publication Date
PL4006178T3 true PL4006178T3 (pl) 2025-06-23

Family

ID=54015126

Family Applications (2)

Application Number Title Priority Date Filing Date
PL22151717.0T PL4006178T3 (pl) 2015-07-30 2016-07-11 Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME
PL16745498T PL3329021T3 (pl) 2015-07-30 2016-07-11 Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME

Family Applications After (1)

Application Number Title Priority Date Filing Date
PL16745498T PL3329021T3 (pl) 2015-07-30 2016-07-11 Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME

Country Status (16)

Country Link
US (6) US11162153B2 (pl)
EP (3) EP4006178B1 (pl)
JP (1) JP6630431B2 (pl)
KR (1) KR102075278B1 (pl)
CN (1) CN107849628B (pl)
BR (1) BR112018000450B1 (pl)
CA (1) CA2991548C (pl)
ES (2) ES2909307T3 (pl)
FI (1) FI4006178T3 (pl)
HU (2) HUE071788T2 (pl)
MA (1) MA42520B1 (pl)
MX (1) MX2018001308A (pl)
PL (2) PL4006178T3 (pl)
RU (1) RU2685617C1 (pl)
UA (1) UA119821C2 (pl)
WO (2) WO2017017484A1 (pl)

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017484A1 (en) 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
MX2019010190A (es) * 2017-02-28 2019-11-28 Tata Steel Ijmuiden Bv Metodo para producir una tira de acero con una capa de recubrimiento de aleacion de aluminio.
US11884998B2 (en) 2017-03-31 2024-01-30 Nippon Steel Corporation Surface treated steel sheet
RU2019142469A (ru) * 2017-06-02 2021-07-09 Ниппон Стил Корпорейшн Горячештампованный элемент
RU2765968C1 (ru) 2018-09-13 2022-02-07 Арселормиттал Сборочная единица, содержащая по меньшей мере две металлические подложки
MA53611A (fr) * 2018-09-13 2021-12-22 Arcelormittal Procédé de soudage pour la fabrication d'un ensemble d'au moins 2 substrats métalliques
JP7194269B2 (ja) 2018-09-13 2022-12-21 アルセロールミタル 少なくとも２枚の金属基材の組立体
CN109324619B (zh) * 2018-09-25 2021-10-22 苏州大学 液态金属电致驱动小车及其运动控制方法
KR102354447B1 (ko) 2018-09-27 2022-03-21 주식회사 포스코 용접액화취성에 대한 저항성과 도금밀착성이 우수한 고내식 도금강판
WO2020111230A1 (ja) 2018-11-30 2020-06-04 日本製鉄株式会社 アルミめっき鋼板、ホットスタンプ部材及びホットスタンプ部材の製造方法
WO2020109849A1 (en) 2018-11-30 2020-06-04 Arcelormittal Wire injection
KR102153194B1 (ko) * 2018-12-18 2020-09-08 주식회사 포스코 액상금속취화(lme) 균열 저항성이 우수한 초고강도 고연성 냉연강판, 도금강판 및 이들의 제조방법
CN113557316B (zh) * 2019-04-01 2022-10-04 日本制铁株式会社 热冲压成形品和热冲压用钢板、以及它们的制造方法
KR102633542B1 (ko) * 2019-04-01 2024-02-06 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 그 제조 방법
WO2020208399A1 (en) 2019-04-09 2020-10-15 Arcelormittal Assembly of an aluminium component and of a press hardened steel part having an alloyed coating comprising silicon, iron, zinc, optionally magnesium, the balance being aluminum
WO2021084304A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084302A1 (en) 2019-10-30 2021-05-06 Arcelormittal A press hardening method
KR20210078277A (ko) * 2019-12-18 2021-06-28 주식회사 포스코 알루미늄합금 도금강판, 열간성형 부재 및 이들의 제조방법
WO2022096921A1 (en) * 2020-11-06 2022-05-12 Arcelormittal Rear underfloor structure for a motor vehicle
KR102888145B1 (ko) 2021-01-14 2025-11-19 닛폰세이테츠 가부시키가이샤 핫 스탬프 부재
JP7510087B2 (ja) * 2021-01-14 2024-07-03 日本製鉄株式会社 めっき鋼材
KR20240032138A (ko) 2021-10-12 2024-03-08 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
WO2024028642A1 (en) * 2022-08-04 2024-02-08 Arcelormittal Steel sheet having excellent powdering properties after press-hardening and method for manufacturing the same
WO2024028641A1 (en) * 2022-08-04 2024-02-08 Arcelormittal Steel sheet having excellent corrosion properties after press hardening and method for manufacturing the same
WO2024028640A1 (en) * 2022-08-04 2024-02-08 Arcelormittal Steel sheet with variable thickness having a reduced risk of delayed fracture after press hardening, a press hardening method, a press hardened coated steel part
WO2024070812A1 (ja) * 2022-09-29 2024-04-04 日本製鉄株式会社 切断加工品、及びガードレール
CN120435574A (zh) * 2022-12-09 2025-08-05 安赛乐米塔尔公司 具有低环境影响的制造钢压制部件的方法
WO2024122117A1 (ja) 2022-12-09 2024-06-13 日本製鉄株式会社 ホットスタンプ成形体
EP4632095A1 (en) 2022-12-09 2025-10-15 Nippon Steel Corporation Plated steel sheet
WO2024122125A1 (ja) 2022-12-09 2024-06-13 日本製鉄株式会社 ホットスタンプ成形体
WO2024122124A1 (ja) 2022-12-09 2024-06-13 日本製鉄株式会社 ホットスタンプ成形体
WO2024122119A1 (ja) 2022-12-09 2024-06-13 日本製鉄株式会社 ホットスタンプ成形体
KR20240087218A (ko) * 2022-12-12 2024-06-19 주식회사 포스코 도금강판 및 그 제조방법
WO2024161173A1 (en) * 2023-01-30 2024-08-08 Arcelormittal A method to produce press hardened parts at high productivity
WO2024033721A1 (en) 2023-06-30 2024-02-15 Arcelormittal Crack-containing hot-stamped coated steel part with excellent spot-weldability and excellent painting adhesion
WO2024033722A1 (en) * 2023-06-30 2024-02-15 Arcelormittal Crack-containing hot-stamped steel part with a thin coating with excellent spot-weldability and excellent painting adhesion

Family Cites Families (74)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS464045Y1 (pl) 1967-05-29 1971-02-12
JPS60162763A (ja) 1984-01-31 1985-08-24 Nisshin Steel Co Ltd 溶融アルミニウムめつき鋼板の製造法
JPH04293759A (ja) 1991-03-20 1992-10-19 Nippon Steel Corp 耐食性に優れた溶融アルミニウムめっき鋼板
KR0146986B1 (ko) 1995-08-29 1998-11-02 서정욱 알루미늄 도금강판의 인산염처리성을 향상시키는 방법
JP3267178B2 (ja) * 1996-12-18 2002-03-18 住友金属工業株式会社 加工性に優れたＺｎ−Ａｌ合金めっき鋼板
JPH11279735A (ja) * 1998-03-27 1999-10-12 Nisshin Steel Co Ltd Ａｌ−Ｓｉ−Ｍｇ−Ｚｎ系溶融Ａｌ基めっき鋼板
JP2000104153A (ja) 1998-09-28 2000-04-11 Daido Steel Sheet Corp 亜鉛−アルミニウム合金めっき鋼板
JP4199404B2 (ja) 1999-03-15 2008-12-17 新日本製鐵株式会社 高耐食性めっき鋼板
KR100317680B1 (ko) 1999-04-29 2001-12-22 이계안 알루미늄 합금 및 강판을 동시에 처리할 수 있는 도장 하지용 표면처리제
JP4267184B2 (ja) 1999-06-29 2009-05-27 新日本製鐵株式会社 耐食性、外観に優れた溶融アルミめっき鋼板及びその製造法
JP4136286B2 (ja) 1999-08-09 2008-08-20 新日本製鐵株式会社 耐食性に優れたＺｎ−Ａｌ−Ｍｇ−Ｓｉ合金めっき鋼材およびその製造方法
JP2001214280A (ja) 2000-01-28 2001-08-07 Nippon Steel Corp 潤滑性に優れたＣｒを使用しない皮膜を被覆するＳｎ系，Ａｌ系めっき鋼板
JP3452017B2 (ja) 2000-03-16 2003-09-29 Ｊｆｅスチール株式会社 溶融金属めっき浴中ロールの付着物除去装置、及び溶融金属めっき金属帯の押疵発生防止方法
JP2002012959A (ja) 2000-04-26 2002-01-15 Nippon Steel Corp 加工部及び端面耐食性に優れたＡｌ系めっき鋼板
JP2002322527A (ja) 2001-04-25 2002-11-08 Nippon Steel Corp Ａｌ−Ｚｎ−Ｍｇ系合金めっき鉄鋼製品
KR100836282B1 (ko) 2001-06-15 2008-06-09 신닛뽄세이테쯔 카부시키카이샤 고강도 알루미늄계 합금 도금 강판
RU2202649C1 (ru) 2001-12-26 2003-04-20 Закрытое акционерное общество "Межотраслевое юридическое агентство "Юрпромконсалтинг" Способ нанесения алюминиевых покрытий на изделия из чугуна и стали
JP2003251272A (ja) * 2002-02-28 2003-09-09 Kansai Paint Co Ltd 自動車車体の塗装方法
CN2553128Y (zh) 2002-06-04 2003-05-28 王泽民 汽油发动机节油器
DE10246164B4 (de) 2002-10-02 2014-03-20 Benteler Automobiltechnik Gmbh Verfahren zum Herstellen von Strukturbauteilen
JP2004339530A (ja) 2003-05-13 2004-12-02 Nippon Steel Corp 加工性に優れたＭｇ含有めっき鋼材およびその製造方法
MXPA06000826A (es) 2003-07-29 2006-08-23 Voestalpine Stahl Gmbh Metodo para producir lamina de acero.
JP2005060728A (ja) 2003-08-11 2005-03-10 Nippon Steel Corp 低比重溶融アルミめっき鋼板及びそのプレス加工方法
JP2005290418A (ja) 2004-03-31 2005-10-20 Jfe Steel Kk プレス加工性に優れた溶融Ａｌ−Ｚｎ系めっき鋼板及びその製造方法
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP2006193776A (ja) 2005-01-12 2006-07-27 Nisshin Steel Co Ltd 摺動性に優れたＺｎ−Ａｌ−Ｍｇ系合金めっき鋼板及び摺動部材
JP4889224B2 (ja) * 2005-02-10 2012-03-07 日新製鋼株式会社 テーラードブランク材の製造方法
JP4410718B2 (ja) 2005-04-25 2010-02-03 新日本製鐵株式会社 塗料密着性、塗装後耐食性に優れたＡｌ系めっき鋼板及びこれを用いた自動車部材並びにＡｌ系めっき鋼板の製造方法
JP4733522B2 (ja) 2006-01-06 2011-07-27 新日本製鐵株式会社 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法
JP4967360B2 (ja) * 2006-02-08 2012-07-04 住友金属工業株式会社 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
WO2007118939A1 (fr) 2006-04-19 2007-10-25 Arcelor France Procede de fabrication d'une piece soudee a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
JP4932376B2 (ja) 2006-08-02 2012-05-16 新日本製鐵株式会社 めっき性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP4919427B2 (ja) 2006-10-03 2012-04-18 日新製鋼株式会社 溶融めっき鋼板の温間加工方法
EP1947210A1 (fr) 2007-01-16 2008-07-23 ARCELOR France Procede de revetement d'un substrat, installation de mise en oeuvre du procede et dispositif d'alimentation en metal d'une telle installation
CN101617059A (zh) 2007-02-23 2009-12-30 克里斯塔尔公司 热机械形成具有很高强度的最终产品的方法及由此制备的产品
WO2008110670A1 (fr) * 2007-03-14 2008-09-18 Arcelormittal France Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
EP2025771A1 (en) * 2007-08-15 2009-02-18 Corus Staal BV Method for producing a coated steel strip for producing taylored blanks suitable for thermomechanical shaping, strip thus produced, and use of such a coated strip
JP2009218518A (ja) 2008-03-12 2009-09-24 Toshiba Corp 半導体装置の製造方法、マスク管理方法および露光量補正情報の取得方法
CA2721266C (en) 2008-04-22 2015-05-26 Nippon Steel Corporation Plated steel sheet and method of hot-stamping plated steel sheet
JP5600868B2 (ja) * 2008-09-17 2014-10-08 Ｊｆｅスチール株式会社 溶融Ａｌ−Ｚｎ系めっき鋼板の製造方法
ES2524071T3 (es) * 2009-01-16 2014-12-04 Nippon Steel & Sumitomo Metal Corporation Material de acero revestido con una aleación de Zn-Al-Mg-Si-Cr por inmersión en caliente, con excelente resistencia a la corrosión
WO2010085983A1 (en) * 2009-02-02 2010-08-05 Arcelormittal Investigacion Y Desarrollo S.L. Fabrication process of coated stamped parts and parts prepared from the same
JP4825882B2 (ja) * 2009-02-03 2011-11-30 トヨタ自動車株式会社 高強度焼き入れ成形体及びその製造方法
DE102009007909A1 (de) 2009-02-06 2010-08-12 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines Stahlbauteils durch Warmformen und durch Warmformen hergestelltes Stahlbauteil
EP2406408B1 (en) * 2009-03-13 2020-10-14 Bluescope Steel Limited Corrosion protection with al / zn-based coatings
JP5404126B2 (ja) 2009-03-26 2014-01-29 日新製鋼株式会社 耐食性に優れたＺｎ−Ａｌ系めっき鋼板およびその製造方法
DE102009017326A1 (de) 2009-04-16 2010-10-21 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung von pressgehärteten Bauteilen
WO2011016518A1 (ja) 2009-08-06 2011-02-10 新日本製鐵株式会社 輻射伝熱加熱用金属板及びその製造方法、並びに異強度部分を持つ金属加工品及びその製造方法
DE102009043926A1 (de) 2009-09-01 2011-03-10 Thyssenkrupp Steel Europe Ag Verfahren und Vorrichtung zur Herstellung eines Metallbauteils
CN104388870B (zh) 2009-12-29 2017-04-12 Posco公司 一种热压模塑部件
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CN102011082A (zh) 2010-11-12 2011-04-13 上海大学 Al-Zn-Si-Mg合金镀层的热浸镀工艺方法
TWI447261B (zh) 2010-11-26 2014-08-01 Jfe Steel Corp 熔融Ａｌ－Ｚｎ系鍍敷鋼板
JP2012112010A (ja) 2010-11-26 2012-06-14 Jfe Steel Corp 熱間プレス用めっき鋼板、それを用いた熱間プレス部材の製造方法および熱間プレス部材
JP2012126993A (ja) 2010-11-26 2012-07-05 Jfe Steel Corp 溶融Ａｌ−Ｚｎ系めっき鋼板およびその製造方法
EP2655672B1 (de) 2010-12-24 2020-12-16 Voestalpine Stahl GmbH Verfahren zum erzeugen gehärteter bauteile mit bereichen unterschiedlicher härte und/oder duktilität
KR20130132623A (ko) 2011-04-01 2013-12-04 신닛테츠스미킨 카부시키카이샤 도장 후 내식성이 우수한 핫 스탬핑 성형된 고강도 부품 및 그 제조 방법
UA109963C2 (uk) * 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
DE202012000616U1 (de) * 2012-01-24 2012-02-29 Benteler Automobiltechnik Gmbh Struktur- und/oder Karosseriebauteil für ein Kraftfahrzeug mit verbesserten Crasheigenschaften und Korrosionsschutz
KR101974182B1 (ko) 2012-02-14 2019-04-30 닛폰세이테츠 가부시키가이샤 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법
JP6169319B2 (ja) 2012-02-15 2017-07-26 理想科学工業株式会社 封筒用紙
JP6001884B2 (ja) * 2012-03-09 2016-10-05 株式会社神戸製鋼所 プレス成形品の製造方法およびプレス成形品
MX358552B (es) 2012-04-17 2018-08-23 Arcelormittal Investigacion Y Desarrollo Sl Lámina de acero provista de un revestimiento que ofrece protección catódica de sacrificio, método para la producción de una parte usando tal lámina y parte resultante.
NZ706336A (en) * 2012-10-17 2019-02-22 Bluescope Steel Ltd Method of producing metal-coated steel strip
EP2848709B1 (de) 2013-09-13 2020-03-04 ThyssenKrupp Steel Europe AG Verfahren zum Herstellen eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils und Stahlbauteil
JP6171872B2 (ja) * 2013-11-12 2017-08-02 新日鐵住金株式会社 ホットスタンプ鋼材の製造方法、ホットスタンプ用鋼板の製造方法及びホットスタンプ用鋼板
ES2753390T3 (es) 2014-05-15 2020-04-08 Nippon Steel Corp Elemento de plancha de acero formado en caliente
WO2016120669A1 (fr) 2015-01-30 2016-08-04 Arcelormittal Procédé de préparation d'une tôle revêtue comprenant l'application d'une solution aqueuse comprenant un aminoacide et utilisation associée pour améliorer la résistance à la corrosion
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
KR20170122242A (ko) * 2015-03-02 2017-11-03 제이에프이 코우반 가부시키가이샤 용융 Al-Zn-Mg-Si 도금 강판과 그 제조 방법
WO2017017484A1 (en) 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
ES2683239T3 (es) * 2016-02-05 2018-09-25 Panthronics Ag Sincronizador de reloj para sincronizar un reloj de dispositivo con un reloj de un dispositivo remoto

Also Published As

Publication number Publication date
JP2018527462A (ja) 2018-09-20
US20210395855A1 (en) 2021-12-23
US11162153B2 (en) 2021-11-02
EP3329021A1 (en) 2018-06-06
HUE058024T2 (hu) 2022-06-28
JP6630431B2 (ja) 2020-01-15
MX2018001308A (es) 2018-04-30
ES2909307T3 (es) 2022-05-06
EP3329021B1 (en) 2022-02-23
MA42520B1 (fr) 2022-02-28
WO2017017484A1 (en) 2017-02-02
CA2991548A1 (en) 2017-02-02
BR112018000450A2 (pt) 2018-09-11
HUE071788T2 (hu) 2025-09-28
CA2991548C (en) 2021-05-04
US20210395854A1 (en) 2021-12-23
CN107849628A (zh) 2018-03-27
KR20180022874A (ko) 2018-03-06
WO2017017514A1 (en) 2017-02-02
UA119821C2 (uk) 2019-08-12
KR102075278B1 (ko) 2020-02-07
BR112018000450B1 (pt) 2022-02-22
EP4006178B1 (en) 2025-05-14
ES3035633T3 (en) 2025-09-05
MA42520A (fr) 2018-06-06
PL3329021T3 (pl) 2022-05-16
EP4553182A3 (en) 2025-07-16
FI4006178T3 (fi) 2025-07-08
US20210395853A1 (en) 2021-12-23
RU2685617C1 (ru) 2019-04-22
CN107849628B (zh) 2020-09-22
EP4006178A1 (en) 2022-06-01
US20210395856A1 (en) 2021-12-23
US20250305080A1 (en) 2025-10-02
EP4553182A2 (en) 2025-05-14
US12416058B2 (en) 2025-09-16
US20180223386A1 (en) 2018-08-09
US12351886B2 (en) 2025-07-08

Similar Documents

Publication Publication Date Title
PL4006178T3 (pl) Sposób wytwarzania hartowanej części, która nie wykazuje problemów z LME
GB201510632D0 (en) A method for adjusting a component of a vehicle
HUE050722T2 (hu) Eljárás cement összetétel elõállítására
PT3352896T (pt) Método de produção de isocianatos
EP3322554C0 (de) Verfahren zur additiven herstellung von metallischen bauteilen
IL266044B (en) Method for the production of 3-alkylsulfanyl-2-chloro-n-(1-alkyl-h1-tetrazol-5-yl)-4-trifluoromethyl-benzamides
GB201505620D0 (en) Specification for method of abandoning a well
IL256154B (en) A method for producing a tampon
IL264307B (en) Production method for a pyrazole-amide compound
GB201402036D0 (en) Method for determination of the status of a disease
IL258301A (en) A method for producing phosphinates
SG11201907182QA (en) Method for producing perfluoroalkadiene compounds
IL258148B (en) Methods for producing flumetamol
HUE047039T2 (hu) Eljárás izocianátok elõállítására
EP3271096C0 (en) PROCESS FOR PRODUCING FLUTES
SG11201704523WA (en) A process for the manufacture of idalopirdine
PL3186049T3 (pl) Sposób wytwarzania betonowego korpusu
SG11201802495UA (en) Method for producing l-methionine
SG11201802624YA (en) Method for producing l-methionine
PL3299394T3 (pl) Sposób wytwarzania zmodyfikowanych ksylopolisacharydów
PL3489218T3 (pl) Sposób wytwarzania fenyloaminohydroksyantrachinonów
SG11202003954QA (en) Method for producing dihydroxyindoles
IL255093A0 (en) A method for the production of levoglucosenon
IL254934B (en) A method for the production of acylsulfamoylbenzamides
PL3383615T3 (pl) Sposób formowania części