KR960015612A - 희토 원소-철-붕소(R-Fe-B) 영구 자석의 제조 방법 - Google Patents

희토 원소-철-붕소(R-Fe-B) 영구 자석의 제조 방법 Download PDF

Info

Publication number
KR960015612A
KR960015612A KR1019950034256A KR19950034256A KR960015612A KR 960015612 A KR960015612 A KR 960015612A KR 1019950034256 A KR1019950034256 A KR 1019950034256A KR 19950034256 A KR19950034256 A KR 19950034256A KR 960015612 A KR960015612 A KR 960015612A
Authority
KR
South Korea
Prior art keywords
less
magnetic field
lubricant
koe
magnet
Prior art date
Application number
KR1019950034256A
Other languages
English (en)
Other versions
KR100202161B1 (ko
Inventor
유지 가네코
나오유키 이시가키
Original Assignee
오카모토 유지
스미토모 도쿠슈 긴조쿠 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP6270618A external-priority patent/JPH08111307A/ja
Priority claimed from JP27061994A external-priority patent/JP3459477B2/ja
Priority claimed from JP33169894A external-priority patent/JP3777199B2/ja
Priority claimed from JP33169994A external-priority patent/JP3383448B2/ja
Application filed by 오카모토 유지, 스미토모 도쿠슈 긴조쿠 가부시키가이샤 filed Critical 오카모토 유지
Publication of KR960015612A publication Critical patent/KR960015612A/ko
Application granted granted Critical
Publication of KR100202161B1 publication Critical patent/KR100202161B1/ko

Abstract

본 발명은 잉곳 연마, Ca 환원 확산 또는 스트립 주조중에 의해 수득한 미세 분말을 사용하여 탁월한 압축 충전특성, 고도의 결정 자기 방향의 배연 및 59.5 이상인 (BH)max(MGOe)값인 A와 iHc (kOe)값인 B의 합, A+B을 갖는 고성능 R-Fe-B 영구 자석의 제조 방법에 관한 것이다. 본원에서는 소정의 조성을 갖는 주조 또는 연마된 합금을 기계적 분쇄 또는 H2 흡착 및 분해법에 의해 조립질로 분쇄한 후, 기계적 분쇄 또는 제트 밀에 의해 미세하게 분쇄하여 평균 입자 크기가 1.0 내지 10㎛인 R-Fe-B 미세 분말을 수득한다. 그 후, 그 분말을 1.4 내지 3.5g/㎠의 충전 밀도로 주형내에 충전시키고 자기화 방향으로 반복하여 역전시키기 위해 10 kOe 보다 큰 세기의 펄스 자기장을 걷어 주고 마지막으로 정류 자기장에서 저온으로 등압 압축을 수행한다.

Description

희토 원소-철-붕소(R-Fe-B) 영구 자석의 제조 방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (21)

  1. 평균 입자 크기가 1.0 내지 10㎛인 R-Fe-B 자석의 미세 분말을 주형내로 충전시키고, 반복적으로 역전하는 펄스 자기장을 걸어 배향시킨 후, 저온으로 등압 압축하고, 소결하고, 숙성시키는 단계를 포함하는 R-Fe-B 영구자석을 제조하는 방법.
  2. 제1항에 있어서, R-Fe-B 자석의 미세 분말을 1.4 내지 3.5g/㎠의 충전 밀도로 주형내에 충전시키는 방법.
  3. 제1항에 있어서, 반복적으로 역전하는 펄스 자기장은 10 kOe 이상의 세기 및 1μ초 내지 10초의 펄스 너비를 가지며, 상기 자기장을 반복적으로 역전시키면서 1 내지 10회 걸어주는 방법.
  4. 제3항에 있어서, 반복적으로 역전하는 펄스 자기장은 20 내지 60 kOe의 세기 및 5μ초 내지 100m초의 펄스 너비를 가지며, 상기 자기장을 반복적으로 역전시키면서 2 내지 8회 걸어주는 방법.
  5. 제1항에 있어서, 저온으로 등압 압축하는 단계를 1톤/㎠ 내지 3톤/㎠의 압축 압력에서 20 내지 80의 쇼어 경도(Hs)를 갖는 저온 등압 압축 주형을 사용하여 수행하는 방법.
  6. 제1항에 있어서, 저온으로 등압 압축하는 단계를 일정한 정류 자기장에서 수행하는 방법.
  7. 제6항에 있어서, 상기 정류 자기장의 세기는 5 내지 20 kOe인 방법.
  8. 제1항에 있어서, 잉곳을 가황하여 수득한 분쇄된 합금 또는 스트립 주조 법에 의해 수득한 주조된 합금을 기계적 분쇄 또는 H2흡착 및 분해법에 의해 조립질로 분쇄하고, 그 후, 기계적 분쇄 또는 제트 밀에 의해 분쇄하여 자석의 미세 분말을 수득하는 방법.
  9. 제8항에 있어서, H2흡착 및 분해법에 의해 수득한 조립질로 분말을 100℃ 내지 750℃로 가열하여 H2제거처리를 수행하는 방법.
  10. 제1항에 있어서, Ca 환원 확산에 의해 수득한 원료 분말을 기계적 분쇄 또는 제트 밀에 의해 미세하게 분쇄하여 자석의 미세 분말을 수득하는 방법.
  11. 제8항 또는 제10항에 있어서, 평균 입자 크기가 10 내지 500㎛인 원료 분말 또는 조립질의 분말을 0.02 내지 5.0중량%의 윤활제와 화합시킨 후, 그것을 미세하게 분쇄하는 방법.
  12. 제11항에 있어서, 상기 윤활제는 액체 윤활제인 방법.
  13. 제12항에 있어서, 상기 액체 윤활제는 지방산 에스테르 또는 붕산 에스테르 중 하나 이상이 용해되어 있는 윤활제인 방법.
  14. 제11항에 있어서, 상기 윤활제는 고체 윤활제인 방법.
  15. 제14항에 있어서, 상기 윤활제는 아연 스테아레이트, 구리 스테아레이트, 알루미늄 스테아레이트 또는 에틸렌-비닐아미도 중 하나 이상으로 이루어진 윤활제인 방법.
  16. 제1항에 있어서, R-Fe-B 자석의 미세 분말의 조성은 R(즉, Y를 비롯한 희토 원소 중 1종 이상)이 10 내지 30%이고, B는 2 내지 28%이고, Fe는 42 내지 88%(즉, Fe는 Co 또는 Ni 중 하나 또는 둘 모두에 의해 부분적으로 대체 가능함)인 방법.
  17. 제16항에 있어서, 상기 조성은 R이 12 내지 16%이고, B는 4 내지 12%이고, Fe는 72 내지 84%인 방법.
  18. 제16항에 있어서, 상기 B중 층 4.0% 이하를 4.0% 이하의 C, 3.5% 이하의 P, 2.5% 이하의 S, 또는 3.5% 이하의 Cu 중 하나 이상에 의해 부분적으로 대체하는 방법.
  19. 제16항 내지 제18항 중 어느 한 항에 있어서, 9.5% 이하의 Al, 4.5% 이하의 Ti, 9.5% 이하의 V, 8.5% 이하의 Cr, 8.0% 이하의 Mn, 5.0% 이하의 Bi, 12.5% 이하의 Nb, 10.5% 이하의 Ta, 9.5% 이하의 Mo, 9.5% 이하의 W, 2.5% 이하의 Sb, 7% 이하의 Ge, 3.5% 이하의 Sn, 5.5% 이하의 Zr, 또는 5.5% 이하의 Hff중 하나 이상을 첨가제로 포함하는 방법.
  20. 제1항에 있어서, (BH)max(MGOe)값인 자기 특성 A와 iHc (kOe)값인 B의 합, A+B가 59.5 이상인 방법.
  21. 제20항에 있어서, (BH)max(MGOe)값인 자기 특성 A와 iHc (kOe)값인 B의 합, A+B가 62 이상인 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019950034256A 1994-10-07 1995-10-06 희토류 원소-철-붕소 영구자석의 제조방법 KR100202161B1 (ko)