KR930013155A - 고순도 강의 용제방법(溶製方法) - Google Patents
고순도 강의 용제방법(溶製方法) Download PDFInfo
- Publication number
- KR930013155A KR930013155A KR1019920025275A KR920025275A KR930013155A KR 930013155 A KR930013155 A KR 930013155A KR 1019920025275 A KR1019920025275 A KR 1019920025275A KR 920025275 A KR920025275 A KR 920025275A KR 930013155 A KR930013155 A KR 930013155A
- Authority
- KR
- South Korea
- Prior art keywords
- molten steel
- ladle
- steel
- cao
- vacuum
- Prior art date
Abstract
용선 예비 처리공정, 전로공정을 거친 용강의 2차 제련에 있어, 탈탄종료후의 용강을 수용한 레이들내 욕면위에 환원제나 플럭스를 첨가함으로써 그 욕면 위에 형성시키는 슬랙의 조성을 FeO및 MnO의 합계 농도가 5wt%이하가 되도록 조정하고, 이어서 RH 진공 탈가스장치를 사용하여 용강 속의 불순물을 극저 영역까지 효율좋게 저감하는 고순도 강의 용제방법.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 실시예를 나타낸 공정도,
제2도는 (FeO+Mn0)와 RH처리후 강 속의 전산소량과의 관계를 나타낸 그래프,
제3도는 RH 처리장치를 나타낸 모식도.
Claims (15)
- 전로(轉爐)에서 탈탄 종료후의 용강을 수용한 레이들내 욕면 위에 환원제나 플럭스를 첨가함으로써 이 용면위에 형성시키는 슬랙의 조성을 조정하고 RH 진공 탈가스장치를 사용하여 용강 속의 불순물을 극저 영역까지 효율좋게 저감하는 것을 특징으로 하는 고순도 강의 용제방법.
- (1)고로(高爐)로부터의 용선에 함유된 P및 S를 각각 0.05wt%이하, 0.01wt%이하로 억제하는 예비 처리공정, (2)상기 예비 처리 공정을 거친 용선을 전로에서 C:0.02~0.1wt%의 범위까지 탈탄하는 공정, (3)탈탄 종료후의 용강을 수용한 레이들내 욕면 위에 환원제나 플럭스를 첨가함으로써 그 욕면위에 형성되는 슬랙의 조성을 FeO및 MnO의 합계 농도가 5wt%이하가 되도록 조정하는 공정, (4) 이 레이들로부터 RH진공가스 장치의 진공조내에 도입하는 용각 욕면 위에 산화성 가스를 분석함으로써 이 용강의 산소농도 및 온도를 조정한후, 함유수소 분체를 분사하여 용강의 C 농도를 소정 범위로 조정하고, 그후 진공조 내에 탈산제를 첨가하여 용강의 탈산을 실시하는 공정을 거치는 것을 특징으로하는 고순도강의 용제방법.
- RH 진공 탈가스장치로 극저 탄소강을 용제할 때 우선 전로에서 탈탄한 용강을 레이들내에 수용하고, 그 레이들내의 욕면 위에 출강 중 또는 출강 후에 환원제를 첨가함으로써 FeO및 MnO의 합계 농도가 5wt%이하가 되도록 조정된 슬랙을 형셩하고, 이이서 그 레이들에 RH 진공 탈가스장치를 설치한후, 이 장치의 진공조내에 도입한 용강 욕면위에 적어도 RH 진공 탈가스처리의 일부 기간에 걸쳐 고소(高所) 분사 랜스로부터 산소성 가스를 분사하고, 이이서 RH 진공 탈가스처리의 종료후의 용강에 Al을 첨가하여, 계속해서 그 용강 욕면에 대하여 상기 고소 분사랜스로부터 CaO를 50wt%이상 함유하는 플러스 가루를 용강 1t당 3kg이상 분사하는 것을 특징으로 하는 고순도 강의 용제방법.
- 고소 분사 랜스를 갖추는 RH 진공 탈가스장치를 사용하여 레이들내의 용강을 탈황하는 방법에 있어서, 레이들내 용강의 표면에 존재하는 슬랙의 T·Fe 농도를 10%이하로 하고, 진공조내에 환류하는 용강의 표면에 대하여 연직으로 상기 고소 분사 랜스로부터 유속 10m/초 이상의 캐리어 가스를 통해서 CaO를 주성분으로 하여 CaF2및/또는 Al2O3을 5~40중량% 함유하는 플럭스를 아래 식에 나타낸 양만큼 분사하는 것을 특징으로 하는 고순도강의 용제방법.
- w/p0.015A
- 여기서 w:CaO를 주성분으로 하는 분체(kg) p:CaO를 주성분으로 하는 분체밀도(kg/㎡) A: 용강 표면 위치에서의 레이들의 단면적(㎡) 0.015:플럭스 층의 두께에 상당하는 계수
- RH 진공 탈가스장치의 진공조내에 레이들로부터의 환류 용강의 욕면 위에 캐리어 가스와 더불어 플럭스 가루를 분사하여 용강의 탈황을 실시할때, 상기 레이들내의 용강 위의 슬랙에 있는 산화철 및 산화 망간의 합계농도를 5wt%이하로 하고, 또한 레이들내 용강 속의 Al농도를 0.02wt%이상으로 조정하는 것을 특징으로 하는 고순도 강의 용제방법.
- 제4항에 있어서, 플럭스의 분사량이 용강 1t당 0.2kg/min 이상인 고순도 강의 용제방법.
- 레이들 슬랙속의 산화철과 산화망간의 합계 농도를 5wt% 이하로 함과 동시에 RH 진공 탈가스장치의 진공조내에 설치한 고소 분사 랜스로부터는 조내 강 욕면을 향하여 가스와 탈황제를 불어 넣어 용강을 탈황하는 방법에 있어서, 상기 고소 분사랜스로부터 진공조내의 강 욕면에 산소 또는 산화성 가스를 분사함과 동시에 알루미늄 또는 알루미늄 함유 환원제를 첨가하고, 그 후 그 고소 분사 랜스로부터 CaO를 주성분으로 하는 플럭스 분말을 적어도 1kg/t분사하는 것을 특징으로 하는 고순도 강의 용제방법.
- 레이들 슬랙속의 산화철과 산화망간의 합계 농도를 5wt%이하로 함과 동시에 RH 진공 탈가스장치의 진공조내에 설치한 고소 분사 랜스로 부터는 조내 강 욕면을 향하여 가스와 탈황제를 분사하여 용강을 탈황하는 방법 있어서, 상기 고소 분사 랜스로부터 CaO를 주성분으로 한 플럭스 분말을 적어도 1kg/t분사함과 동시에 상기 진공조내에 체류하는 용강의 욕 깊이를 저하시킴으로써 상기 분사 플럭스 분말을 용강과 더불어 진공조와 레이들사이에 순환시키는 것을 특징으로 하는 RH 진공 탈가스장치를 사용하는 고순도 강의 용제방법.
- 레이들 슬랙속의 산화철과 산화망간의 합계 농도를 5wt% 이하로 함과 동시에 RH진공 탈가스장치의 진공조내에 설치한 고소 분사 랜스로부터는 조내 강 욕면을 향하여 가스와 탈황제를 분사시켜서 용강을 탈황하는 방법에 있어서, 상기 고소 분사 랜스로부터 진공조내의 강 욕면에 산소 또는 산화성 가스를 분사한 후, 알루미늄 또는 알루미늄 함유 환원제를 첨가하고, 그 후 그 고소 분사 랜스로부터 CaO를 주성분으로 한 플럭스 분말을 적어도 1kg/t분사하며, 또한 레이들의 위치를 내려서 상기 진공조내에 체류하는 용강의 욕깊이를 저하시킴으로써 상기 분사 플럭스 분말을 용강과 더불어 진공조와 레이들 사이에 순환시키는 것을 특징으로 하는 RH 진공 탈가스장치를 사용하는 고순도 강의 용제방법.
- 고소 분사 랜스를 갖춘 RH진공 탈가스장치의 진공조내의 강 욕면 위에 CaO를 주성분으로 한 플럭스 가루를 고소 분사 랜스를 통해서 캐리어 가스와 더불어 분사함으로써 용강의 탈황을 실시하는 방법에 있어서 출강중 또는 출강후의 용강에 환원제를 첨가함으로써 레이들 슬랙의 성분이 그 속에 함유된 산화철과 산화망간의 합계량이 5wt%이하가 되도록 개질함과 동시에 출강 중 및 출강 후의 레이들내에 CaO를 투입하여 RH 진공 탈가스처리전의 레이들 슬랙의 성분 조성을 아래 식으로 하고, 그후 RH진공 탈가스처리에 있어서 진공조내의 강에 상기 고소 분사랜스로부터 CaO를 주성분으로 한 플럭스를 적어도 1.0kg/t 분사하는 것을 특징으로 하는 RH진공 탈가스장치를 사용하는 고순도 강의 용제방법.
- WCAO/(WA1203+2.5 WsiO2)0.9
- 식중 : WCaO: 슬랙 속의 CaO wt% WA1203:슬랙 속의 Al2O3wt% WsiO2 :슬랙 속의SiO2wt%
- ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.