JPS647012B2 - - Google Patents

Info

Publication number
JPS647012B2
JPS647012B2 JP58126908A JP12690883A JPS647012B2 JP S647012 B2 JPS647012 B2 JP S647012B2 JP 58126908 A JP58126908 A JP 58126908A JP 12690883 A JP12690883 A JP 12690883A JP S647012 B2 JPS647012 B2 JP S647012B2
Authority
JP
Japan
Prior art keywords
sio
glass
specific gravity
cao
components
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP58126908A
Other languages
English (en)
Other versions
JPS6021828A (ja
Inventor
Hiroharu Sagara
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hoya Corp
Original Assignee
Hoya Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hoya Corp filed Critical Hoya Corp
Priority to JP58126908A priority Critical patent/JPS6021828A/ja
Priority to US06/604,224 priority patent/US4612295A/en
Priority to GB08410895A priority patent/GB2145407B/en
Priority to DE19843420306 priority patent/DE3420306A1/de
Priority to FR848411206A priority patent/FR2549033B1/fr
Publication of JPS6021828A publication Critical patent/JPS6021828A/ja
Publication of JPS647012B2 publication Critical patent/JPS647012B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
本発明はηd≧1.79、νd＝32〜38、比重＜3.6を
有する眼鏡レンズ用ガラス組成物に係る。 眼鏡レンズの矯正率は使用レンズの屈折率及び
両面の曲率に依存するが、近視又は遠視の度が進
んでくると、これを補正するためのレンズは外縁
部又は中心部が厚くなり、外見上の美観をそこな
うばかりか重量が増して使用者に不快感を与え
る。この問題を改善するにはガラス素材の屈折率
を高めてやれば良いが、一般にガラスの屈折率を
高めると比重も大きくなる傾向が有る。そこで、
高屈折率でしかも低比重のガラスが望まれること
になるが、そうしたガラスは例えば特公昭56−
51141号公報や特開昭55−126549号公報に開示さ
れている。しかし、これらはいずれも低比重を得
るのに多量のTiO2を含有させているのでアツベ
数が小さい。 しかるにアツベ数の小さなガラスを眼鏡レンズ
として使用すると、外縁部の色収差が大きくなる
という弊害があり、特に高いジオプトリー値を有
する眼鏡レンズの場合にはその色収差は無視し難
いものとなる。そのため、屈折率が高いと同時に
アツベ数も大きい軽量ガラスが望まれることにな
る。 本発明は屈折率ηd1.79以上で、比較的大きなア
ツベ数νd32〜38を有し、かつ3.6未満の比重を有
する眼鏡レンズ用ガラスを提供することを目的と
し、屈折率を高める成分である３価以上の高原子
価酸化物と屈折率を低める成分であるガラス形成
酸化物及びアルカリ酸化物との比率を厳密に規定
するとともに、アツベ数を高める成分及び比重を
大きくする成分の範囲を限定したSiO2（又は
B2O3）―CaO―Nb2O5系を基本系としたガラス
系が上記目的に適していることを見い出して完成
されたものである。 すなわち、本発明のガラスは重量％でSiO2＋
B2O322〜36、SiO20〜36、B2O30〜36、CaO＋
MgO16〜42、CaO8〜42、MgO0〜22、TiO2＋
Nb2O514〜36、TiO20〜19、Nb2O51〜35、ZrO20
〜13、La2O30〜14、Y2O30〜17、Gd2O30〜10、
Ta2O50〜10、WO30〜12、Li2O＋Na2O＋K2O0
〜５未満、BaO0〜14、SrO0〜16、ZnO0〜14、
Al2O30〜14、P2O50〜10なる成分範囲で、かつ３
価以上の高原子価成分の合計≧1.05×〔SiO2＋
B2O3＋Al2O3＋P2O5＋アルカリ金属酸化物〕な
る組成を有する。ここにSiO2、B2O3はガラスの
骨格となる成分であり、その和が36％超では所望
の高屈折率が得られず、22％未満では所望の軽さ
のガラスが得られない。CaOはガラスの失透に対
する安定化のために少なくとも８％必要である
が、42％超では逆に強い失透傾向を示す。MgO
は比重の増大を招くことなくCaOとの置換が可能
であるが、MgO22％超では失透傾向が増加する。
MgOとCaOの合量は16〜42％であることが必要
である。TiO2とNb2O5は高屈折率と低比重を得
るのに有効な成分で、合量で14％以上必要である
が、アツベ数を小さくするという欠点を持つた
め、夫々19％及び35％、合量で36％以下に限定し
なければならない。又、失透防止のため、Nb2O5
は必須成分として１％以上含む必要がある。その
他の成分はかならずしも必須ではないが、バツチ
熔融性、耐失透性、成形性等の改善や光学恒数の
調整等の目的で添加される。しかし、ZrO2、ア
ルカリ金属酸化物、Al2O3、P2O5は夫々13％、５
％、14％、10％を越えると急激に耐失透性が悪化
する。又、BaO、SrO、ZnO、La2O3、Y2O3、
Gd2O3、Ta2O5、WO3はいずれも比重を大きくす
る成分であるから、夫々14％、16％、14％、15
％、17％、10％、10％、12％を越えて添加すべき
ではない。そして更に、所望の高屈折率を維持す
るために、３価以上の高原子価成分の合計≧1.05
×〔SiO2＋B2O3＋Al2O3＋P2O5＋アルカリ金属酸
化物〕であることが必要である。ちなみに、ガラ
ス形成酸化物を２価以上の成分に置換することに
よつて、屈折率を高めることができることは一般
に公知であるが、その置換は耐失透性の悪化を伴
うのが普通であつて、しかもガラス形成酸化物の
量が変化することによつて、安定なガラス領域も
変動する。従つて、本発明が企図するような高屈
折率で低比重でアツベ数が大きいガラスを得るた
めには、２価成分や高原子価成分の種類と量を上
記した如く規定すると共に、 ３価以上の高原子価酸化物の合計≧ 1.05×〔SiO2＋B2O3＋Al2O3＋ P2O5＋アルカリ金属酸化物〕 とすることが重要なのである。その他、清澄、熔
融性改善等の理由で、少量のAsO3、Sb2O3、F2、
GeO2、PbO等を特性を悪化させない程度に添加
するのを本発明は妨げない。 本発明の好ましい実施態様では、SiO2とB2O3
の和は高屈折率を得るため33％以下、低比重を得
るため26％以上に限定されるが、B2O3の比率が
増えるに従つて化学的耐久性が劣化するので、
B2O3は０〜15％の範囲が良く、SiO2は15〜33％
の範囲が良い。CaOとMgOの２成分及びTiO2と
Nb2O5の２成分は夫々耐失透性が特に良い範囲と
いうことで限定すると前の２成分及び後の２成分
とも合量で20〜36％になり、単独ではCaO12〜36
％、MgO0〜15％、TiO24〜16％、Nb2O54〜30
％になる。ZrO2は防失透効果が大きく、TiO2、
Nb2O5に比べて低分散にする効果も有るので２〜
10％が有利である。La2O3、Y2O3はTiO2、
Nb2O5、ZrO2に比べて低分散にする効果があり、
アツベ数の大きなガラスを得るのに有利である
が、比重を大きくするから、夫々０〜10％、０〜
14％、合量で０〜14％が望ましい。Li2O、
Na2O、K2Oはバツチの熔融性を良くする効果が
あるが、耐失透性の点から合量で４％以下が有利
である。BaO、SrO、ZnOは耐失透性の改善に効
果が有るが、いずれも比重を大きくするので合量
で10％以下が望ましい。そして、所望の高屈折率
を維持するうえで、３価以上の高原子価成分の合
計≧1.05×〔SiO2＋B2O3＋アルカリ金属酸化物〕
であることが好ましい。 従つて、本発明の最も有利な実施態様は重量％
でSiO2＋B2O326〜33、SiO215〜33、B2O30〜15、
CaO＋MgO20〜36、CaO12〜36、MgO0〜15、
TiO2＋Nb2O520〜36、TiO24〜16、Nb2O54〜30、
ZrO22〜10、La2O3＋Y2O30〜14、La2O30〜10、
Y2O30〜14、Li2O＋Na2O＋K2O0〜４、BaO＋
SrO＋ZnO0〜10なる成分範囲で、かつ ３価以上の高原子価酸化物の合計≧ 1.05×〔SiO2＋B2O3＋アルカリ金属酸化物〕 なる条件を満たす組成のガラスであつて、このガ
ラスはηd≧1.795、νd＝32〜36、比重≦3.55の特
性を示す。 次に本発明の実施例（各成分は重量％）を次表
に示す。
【表】
【表】 これらのガラスは通常使用される硅石粉、硼
酸、炭酸カルシウム、炭酸マグネシウム、酸化チ
タン、酸化ニオブ等の混合物を白金製るつぼ内で
1300〜1400℃で熔融し、撹拌して充分均質化、泡
切れを行つた後、適当な温度で予熱した金型に鋳
込み徐冷することによつて製造できる。

Claims (1)

  1. 【特許請求の範囲】 １ 重量％で SiO2＋B2O3 22〜36 SiO2 ０〜36 B2O3 ０〜36 CaO＋MgO 16〜42 CaO ８〜42 MgO ０〜22 TiO2＋Nb2O5 14〜36 TiO2 ０〜19 Nb2O5 １〜35 ZrO2 ０〜13 La2O3 ０〜14 Y2O3 ０〜17 Gd2O3 ０〜10 Ta2O5 ０〜10 WO3 ０〜12 Li2O＋Na2O＋K2O ０〜５未満 BaO ０〜14 SrO ０〜16 ZnO ０〜14 Al2O3 ０〜14 P2O5 ０〜10 なる成分範囲で、かつ ３価以上の高原子価酸化物の合計≧ 1.05×〔SiO2＋B2O3＋Al2O3＋P2O5＋アルカ
    リ金属酸化物〕 なる条件を満たす組成を有し、ηd≧1.79、νd＝32
    〜38及び比重＜3.6なる特性を有する眼鏡レンズ
    用ガラス。 ２ 重量％で SiO2＋B2O3 26〜33 SiO2 15〜33 B2O3 ０〜15 CaO＋MgO 20〜36 CaO 12〜36 MgO ０〜15 TiO2＋Nb2O5 20〜36 TiO2 ４〜16 Nb2O5 ４〜30 ZrO2 ２〜10 La2O3＋Y2O3 ０〜14 La2O ０〜10 Y2O3 ０〜14 Li2O＋Na2O＋K2O ０〜４ BaO＋SrO＋ZnO ０〜10 なる成分範囲で、かつ ３価以上の高原子価酸化物の合計≧ 1.05×〔SiO2＋B2O3＋アルカリ金属酸化物〕 なる条件を満たす組成を有し、ηd≧1.795、νd＝
    32〜36、比重≦3.55なる特性を有する特許請求の
    範囲第１項に記載のガラス。
JP58126908A 1983-07-14 1983-07-14 眼鏡レンズ用ガラス Granted JPS6021828A (ja)