JP5473935B2 - ポリウレタンフォーム用発泡性組成物及びポリウレタンフォーム - Google Patents
ポリウレタンフォーム用発泡性組成物及びポリウレタンフォーム Download PDFInfo
- Publication number
- JP5473935B2 JP5473935B2 JP2010536661A JP2010536661A JP5473935B2 JP 5473935 B2 JP5473935 B2 JP 5473935B2 JP 2010536661 A JP2010536661 A JP 2010536661A JP 2010536661 A JP2010536661 A JP 2010536661A JP 5473935 B2 JP5473935 B2 JP 5473935B2
- Authority
- JP
- Japan
- Prior art keywords
- polyol
- polyurethane foam
- phenol resin
- foamable composition
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(2)水酸基価(mgKOH/g)は、JIS K 1557に準じて測定した。
(3)数平均分子量及び未反応フェノール量は、東ソー株式会社製ゲル濾過クロマトグラフ8020シリーズビルドアップシステム(カラム:G1000HXL+G2000HXL、検出器:UV254nm、キャリア:テトラヒドロフラン1mL/min、カラム温度:38℃)を用いて測定した。なお、数平均分子量は標準ポリスチレン換算値であり、また、未反応フェノール量は、ピーク高さを測定して、フェノール検量線から求めた。
撹拌装置を備えた反応容器内に、フェノール9400g、92%パラホルムアルデヒド1630g、酸触媒としてシュウ酸19gを仕込んだ後、撹拌混合しながら100℃で、4時間、反応させた。その後、減圧下で水分を溜去した後、引き続き、所定の温度になるまで、減圧下において未反応フェノールを溜去することにより、ノボラック型フェノール樹脂a,b,cを調製した。なお、この得られたノボラック型フェノール樹脂aの未反応フェノール含有量は30%、数平均分子量は160、80℃における粘度は90mPa・sであり、またノボラック型フェノール樹脂bの未反応フェノール含有量は10%、数平均分子量は260、80℃における粘度は5000mPa・sであり、更にノボラック型フェノール樹脂cの未反応フェノール含有量は5%、数平均分子量は300、80℃における粘度は8000mPa・sであった。
撹拌装置を備えた耐圧反応容器内に、下記表1に示されるように、上記ノボラック型フェノール樹脂a,b,c,dのうちの何れかを4kg、アルカリ触媒としての水酸化カリウムの200gと共に仕込んだ後、撹拌混合しながら、150℃の温度で、エチレンオキサイド(EO)又はEO及びプロピレンオキサイド(PO)を下記表1に示される配合量となるように加えて、ノボラック型フェノール樹脂に付加させた。なお、EO及びPOの両方を付加させる場合には、先ず、エチレンオキサイドを付加させた後、プロピレンオキサイドを次に付加させた。その後、水酸化カリウムを酢酸で中和して、6種類のフェノール樹脂系ポリオール(A,B,C,D,E,F)を調製した。得られたフェノール樹脂系ポリオールについて、水酸基価及び25℃における粘度を測定し、その結果を下記表1に示した。
撹拌装置を備えた耐圧反応容器内に、トリレンジアミンの1kgと、反応触媒としての水酸化カリウムの20gを仕込み、撹拌混合しながら、115℃の温度下で、加圧下に、EOの3.4kgを付加せしめた。その後、触媒を酢酸にて中和することにより、目的とするトリレンジアミン系ポリオールNを得た。なお、この得られたポリオールの粘度は、3200mPa・s/25℃であり、水酸基価は、400mgKOH/gであった。
撹拌装置を備えた耐圧反応容器内に、トリレンジアミンの1kgと、反応触媒としての水酸化カリウムの20gを仕込み、撹拌混合しながら、115℃の温度下で、加圧下に、EOの1.7kg及びPOの2.2kgを付加せしめた。その後、触媒を酢酸にて中和することにより、目的とするトリレンジアミン系ポリオールOを得た。なお、この得られたポリオールの粘度は、11000mPa・s/25℃であり、水酸基価は、400mgKOH/gであった。
先ず、ポリオール成分として、上記で準備したフェノール樹脂系ポリオールBとトリレンジアミン系ポリオールMとを用い、下記表2に示されるように、このフェノール樹脂系ポリオールBの50部とトリレンジアミン系ポリオールMの50部に対し、シリコーン整泡剤(商品名:SH−193、東レ・ダウコーニング社製)2部、樹脂化触媒(商品名:カオライザーNo.25、花王株式会社製)0.5部、アミン系泡化触媒(商品名:カオライザーNo.26、花王株式会社製)3部、発泡剤源としての水5部、難燃剤(トリスクロロプロピルフォスフェート)30部及び起泡剤(リシノール酸カリウム)1部を混合して、ポリオール配合液を調製した。
フェノール樹脂系ポリオールとトリレンジアミン系ポリオールの種類と配合割合を、下記表2及び表3に示されるようにしたこと以外は、実施例1と同様にして、ポリオール配合液を調製した。そして、その得られたポリオール配合液を用いて、実施例1と同様にして、それぞれポリウレタンフォーム用発泡性組成物を調製し、板状のポリウレタンフォームを得た。なお、実施例4及び5において用いたエチレンジアミン系ポリオールは、EXCENOL−450ED(旭硝子ウレタン株式会社製)であった。
ポリオール成分として、フェノール樹脂系ポリオールBのみを使用すること(比較例1)、又はトリレンジアミン系ポリオールMのみを使用すること(比較例2)、又はフェノール樹脂系ポリオールBとトリレンジアミン系ポリオールMの合計量をポリオール成分全体の60%未満としたこと(比較例3,4,5)以外は、それぞれ、実施例1と同様にして、ポリオール配合液を調製した。そして、その得られたポリオール配合液を用いて、実施例1と同様にして、ポリウレタンフォーム用発泡性組成物を調製し、板状のポリウレタンフォームを得た。そして、この得られたポリウレタンフォームについて、更に実施例1と同様にして、密度、熱伝導率及び熱伝導率の経時変化、寸法安定性、難燃性の測定を行ない、その得られた結果を、下記表4及び表5に示した。
ポリオール成分としてフェノール樹脂系ポリオールBの50部を用い且つアルキレンオキサイドの付加されていないトリレンジアミンの50部を用いること(比較例6)以外は、又は、ポリオール成分としてトリレンジアミン系ポリオールMの50部を用い且つアルキレンオキサイドの付加されていないノボラック型フェノール樹脂の50部を用いること(比較例7)以外は、それぞれ、実施例1と同様にして、ポリオール配合液を調製し、更に、その得られたポリオール配合液に対して、クルードMDIを加え、ホモディスパーにて高速攪拌混合したところ、混合不良及び脆性が発現して、良好な発泡体を得ることができなかった。
Claims (14)
- ポリオール成分とポリイソシアネート成分とを反応、発泡させることにより得られるポリウレタンフォームの製造に使用される発泡性組成物であって、
前記発泡に二酸化炭素が用いられると共に、前記ポリオール成分として、遊離フェノール類を5〜50質量%の割合で含有するノボラック型フェノール樹脂にアルキレンオキサイドを付加させて得られるフェノール樹脂系ポリオールと、芳香族ジアミンにアルキレンオキサイドを付加させて得られる芳香族アミン系ポリオールとを、それらの合計量がポリオール成分の60質量%以上を占める割合で用いたことを特徴とするポリウレタンフォーム用発泡性組成物。 - 前記二酸化炭素が、水とポリイソシアネート成分との反応により発生せしめられる請求項1に記載のポリウレタンフォーム用発泡性組成物。
- 前記ノボラック型フェノール樹脂が、遊離フェノール類を5〜35質量%の割合で含有している請求項1又は請求項2に記載のポリウレタンフォーム用発泡性組成物。
- 前記ノボラック型フェノール樹脂が、遊離フェノール類を10〜30質量%の割合で含有している請求項1乃至請求項3の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記芳香族ジアミンが、トリレンジアミン若しくはその誘導体、4,4’−ジアミノジフェニルメタン、p−フェニレンジアミン、o−フェニレンジアミン、及びナフタレンジアミンからなる群より選ばれる請求項1乃至請求項4の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記芳香族ジアミンが、トリレンジアミンである請求項1乃至請求項5の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記ノボラック型フェノール樹脂又は前記芳香族ジアミンに付加せしめられるアルキレンオキサイドが、エチレンオキサイド、プロピレンオキサイド又はこれらの混合物である請求項1乃至請求項6の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記ノボラック型フェノール樹脂に付加せしめられるアルキレンオキサイドが、エチレンオキサイド、又は50質量%以上のエチレンオキサイドと50質量%以下のプロピレンオキサイドとの組合せからなるものである請求項1乃至請求項7の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記ノボラック型フェノール樹脂に付加せしめられるアルキレンオキサイドの10〜100質量%が、プロピレンオキサイドである請求項1乃至請求項7の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記芳香族ジアミンに付加せしめられるアルキレンオキサイドの10〜100質量%が、プロピレンオキサイドである請求項1乃至請求項7の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記フェノール樹脂系ポリオールと前記芳香族アミン系ポリオールとが、それぞれ、前記ポリオール成分の30質量%以上を占める割合で含有せしめられている請求項1乃至請求項10の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記フェノール樹脂系ポリオールと前記芳香族アミン系ポリオールとが、それぞれ、前記ポリオール成分の40質量%以上を占める割合で含有せしめられている請求項1乃至請求項10の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 前記フェノール樹脂系ポリオールと前記芳香族アミン系ポリオールとが、質量比にて、3/7〜7/3の割合において含有せしめられている請求項1乃至請求項12の何れか1項に記載のポリウレタンフォーム用発泡性組成物。
- 請求項1乃至請求項13の何れか1項に記載のポリウレタンフォーム用発泡性組成物を発泡、硬化させて得られるポリウレタンフォーム。