CN102785491A - 一种热转印碳带及其制备方法 - Google Patents

一种热转印碳带及其制备方法 Download PDF

Info

Publication number
CN102785491A
CN102785491A CN2012103051985A CN201210305198A CN102785491A CN 102785491 A CN102785491 A CN 102785491A CN 2012103051985 A CN2012103051985 A CN 2012103051985A CN 201210305198 A CN201210305198 A CN 201210305198A CN 102785491 A CN102785491 A CN 102785491A
Authority
CN
China
Prior art keywords
parts
coating emulsion
heat
layer coating
matrix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103051985A
Other languages
English (en)
Other versions
CN102785491B (zh
Inventor
虞友义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUZHOU KINGDOM COATING INDUSTRY Co Ltd
Original Assignee
HUZHOU KINGDOM COATING INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUZHOU KINGDOM COATING INDUSTRY Co Ltd filed Critical HUZHOU KINGDOM COATING INDUSTRY Co Ltd
Priority to CN201210305198.5A priority Critical patent/CN102785491B/zh
Publication of CN102785491A publication Critical patent/CN102785491A/zh
Application granted granted Critical
Publication of CN102785491B publication Critical patent/CN102785491B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种热转印碳带，包括油墨层、离型剂层、基材和耐温层，所述油墨层包括水性树脂、无机纳米级颜料、有机颜料、分散剂、固化剂、消泡剂和去离子水，离型剂层包括有机硅树脂、水性蜡乳液、滑石粉和去离子水，基材包括聚酯薄膜和导热硅脂，耐温层包括氟碳、有机硅树脂和去离子水，本发明还公开了一种热转印碳带的制备方法，包括搅拌、混合、烘干等步骤。本发明通过以聚酯薄膜为基材的原材料，并添加导热硅脂，提高了碳带的使用温度，提高了碳带的耐热性和适用性，且加速了印刷速度；通过在碳带中添加耐温层，提高了产品的性能，通过添加离型剂层，使油墨更易与基材分离，可剥离度高，打印效果更好，字迹更清晰，通过采用去离子水为溶剂，降低生产成本，产品性价比更好。

Description

一种热转印碳带及其制备方法
【技术领域】
本发明涉及一种热转印碳带，以及该热转印碳带的制备方法。
【背景技术】
热转印碳带是打印必须的消耗材料，也是决定热转印成像质量的核心材料。目前市面上的热转印碳带主要有蜡基热转印碳带、树脂热转印碳带及蜡基树脂混合型热转印碳带，蜡基热转印碳带打印能耗低，打印效果好，但耐用性较低，耐腐蚀性和可剥离性较其他碳带有欠缺；树脂热转印碳带打印清晰，图像耐久性、耐磨性、耐热性等均较好，但能耗大，成本高；蜡基树脂混合型热转印碳带性价比较高，耐用性好，但在硬度、耐热性、打印清晰度方面存在缺点。
【发明内容】
本发明的目的就是解决现有技术中的问题，提出一种热转印碳带及其制备方法，能够生产出耐磨性、耐热性好，且成像清晰，可剥离度高，又低耗能的热转印碳带，且产品性价比高，生产成本低。
为实现上述目的，本发明提出了一种热转印碳带及其制备方法，其特征在于：依次包括油墨层、离型剂层、基材和耐温层，所述油墨层、离型剂层、基材和耐温层的质量比例为2:1:1:1，所述油墨层包括水性树脂、无机纳米级颜料、有机颜料、分散剂、固化剂、消泡剂和去离子水，所述离型剂层包括有机硅树脂、水性蜡乳液、滑石粉和去离子水，所述基材包括聚酯薄膜和传热介质，所述耐温层包括氟碳、有机硅树脂和去离子水，
所述油墨层中各组分质量比例为：
Figure BDA00002054574100021
所述离型剂层中各质量比例为：
Figure BDA00002054574100022
所述基材中各组分质量比例为：
聚酯薄膜                        85～95份
传热介质                        8～12份；
所述耐温层中各组分质量比例为：
氟碳                            15～25份
有机硅树脂                      45～55份
去离子水                        25～35份。
作为优选，所述油墨层中各组分质量比例为：
Figure BDA00002054574100023
Figure BDA00002054574100031
所述离型剂层中各质量比例为：
Figure BDA00002054574100032
所述基材中各组分质量比例为：
聚酯薄膜                        90份
传热介质                        10份；
所述耐温层中各组分质量比例为：
氟碳                            20份
有机硅树脂                      50份
去离子水                        30份。
作为优选，所述传热介质为导热硅脂，所述无机纳米级颜料包括炭黑、钛白粉、锌钡白、铅铬黄、铁蓝中的一种或多种，所述有机颜料包括大红粉、偶氮黄、酞菁蓝、喹吖啶酮中的一种或多种。
作为优选，所述分散剂为六偏磷酸钠，固化剂为脂肪族多胺，消泡剂为聚醚类。
本发明还提出了一种热转印碳带的制备方法，首先将5～9份无机纳米级颜料、5～9份有机颜料、0.2～0.7份分散剂加入到36～40份去离子水中，以1800～2200r/min的转速下搅拌1～2h，形成油墨基料，然后在油墨基料中加入40～60份水性树脂，搅拌0.5h，然后再加入0.5～1.5份固化剂和0.2～0.7份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将1～3份滑石粉加入到26～30份去离子水中，以1300～1700r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入25～35份机硅树脂和35～45份水性蜡乳液，搅拌10～30min得到离型剂层涂层乳液；然后在85～95份聚酯薄膜上均匀涂抹8～12份传热介质，形成基体；然后将15～25份氟碳和45～55份有机硅树脂混合加入到25～35份去离子水中，并在800～1200r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在80～90℃下烘干0.5～1.5h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以80～90℃烘干0.5～1.5h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以80～90℃烘干0.5～1.5h。
作为优选，所述油墨基料制作过程中转速为2000r/min，所述滑石粉和去离子水混合过程中，转速为1500r/min，搅拌时间为20min，所述耐温层涂层乳液制作过程中转速为1000r/min，所述烘干温度均为85℃，烘干时间均为1h。
作为优选，首先7份无机纳米级颜料、7份有机颜料、0.5份分散剂加入到38份去离子水中，以2000r/min的转速下搅拌1.5h，形成油墨基料，然后在油墨基料中加入50份水性树脂，搅拌0.5h，然后再加入1份固化剂和0.5份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将2份滑石粉加入到28份去离子水中，以1500r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入30份机硅树脂和40份水性蜡乳液，搅拌20min得到离型剂层涂层乳液；然后在90份聚酯薄膜上均匀涂抹10份传热介质，形成基体；然后将20份氟碳和50份有机硅树脂混合加入到30份去离子水中，并在1000r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在85℃下烘干1h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以85℃烘干1h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以85℃烘干1h。
本发明的有益效果：本发明通过以聚酯薄膜为基材的原材料，并添加导热硅脂，提高了碳带的使用温度，提高了碳带的耐热性和适用性，且加速了印刷速度；通过在碳带中添加耐温层，提高了产品的性能，通过添加离型剂层，使油墨更易与基材分离，可剥离度高，打印效果更好，字迹更清晰，通过采用去离子水为溶剂，降低生产成本，产品性价比更好。
【具体实施方式】
下面给出本发明的实施例及制造工艺和效果。
本发明一种热转印碳带：
实施例一
6份无机纳米级颜料、6份有机颜料、0.4份分散剂、1份固化剂、0.5份消泡剂、45份水性树脂、1.5份滑石粉、28份机硅树脂、38份水性蜡乳液、88份聚酯薄膜、9份导热硅脂、18份氟碳、48份有机硅树脂、92份去离子水。
本发明的制备工艺：首先将6份无机纳米级颜料、6份有机颜料、0.5份分散剂加入到38份去离子水中，以2000r/min的转速下搅拌1.5h，形成油墨基料，然后在油墨基料中加入45份水性树脂，搅拌0.5h，然后再加入1份固化剂和0.4份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将1.5份滑石粉加入到27份去离子水中，以1500r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入28份机硅树脂和38份水性蜡乳液，搅拌20min得到离型剂层涂层乳液；然后在88份聚酯薄膜上均匀涂抹9份导热硅脂，形成基体；然后将18份氟碳和48份有机硅树脂混合加入到27份去离子水中，并在1000r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在85℃下烘干1h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以85℃烘干1h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以85℃烘干1h，得到成品。
实施例二
7份无机纳米级颜料、7份有机颜料、0.5份分散剂、1份固化剂、0.5份消泡剂、50份水性树脂、2份滑石粉、30份机硅树脂、40份水性蜡乳液、90份聚酯薄膜、10份导热硅脂、20份氟碳、50份有机硅树脂、95份去离子水。
本发明的制备工艺：首先将7份无机纳米级颜料、7份有机颜料、0.5份分散剂加入到38份去离子水中，以2000r/min的转速下搅拌1.5h，形成油墨基料，然后在油墨基料中加入50份水性树脂，搅拌0.5h，然后再加入1份固化剂和0.5份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将2份滑石粉加入到27份去离子水中，以1500r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入30份机硅树脂和40份水性蜡乳液，搅拌20min得到离型剂层涂层乳液；然后在90份聚酯薄膜上均匀涂抹10份导热硅脂，形成基体；然后将20份氟碳和50份有机硅树脂混合加入到30份去离子水中，并在1000r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在85℃下烘干1h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以85℃烘干1h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以85℃烘干1h，得到成品。
实施例三
8份无机纳米级颜料、8份有机颜料、0.6份分散剂、1.2份固化剂、0.6份消泡剂、55份水性树脂、2.5份滑石粉、28份机硅树脂、38份水性蜡乳液、92份聚酯薄膜、11份导热硅脂、22份氟碳、52份有机硅树脂、98份去离子水。
本发明的制备工艺：首先将8份无机纳米级颜料、8份有机颜料、0.6份分散剂加入到38份去离子水中，以2000r/min的转速下搅拌1.5h，形成油墨基料，然后在油墨基料中加入55份水性树脂，搅拌0.5h，然后再加入1.2份固化剂和0.6份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将2.5份滑石粉加入到28份去离子水中，以1500r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入28份机硅树脂和38份水性蜡乳液，搅拌20min得到离型剂层涂层乳液；然后在92份聚酯薄膜上均匀涂抹11份导热硅脂，形成基体；然后将22份氟碳和52份有机硅树脂混合加入到32份去离子水中，并在1000r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在85℃下烘干1h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以85℃烘干1h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以85℃烘干1h，得到成品。
本产品耐磨性高、耐热性好，成像清晰，可剥离度高，低耗能，，产品性价比高，生产成本低。
上述实施例是对本发明的说明，不是对本发明的限定，任何对本发明简单变换后的方案均属于本发明的保护范围。

Claims (7)

1.一种热转印碳带，其特征在于：包括依次设置的油墨层、离型剂层、基材和耐温层，所述油墨层、离型剂层、基材和耐温层的质量比例为2:1:1:1，所述油墨层由水性树脂、无机纳米级颜料、有机颜料、分散剂、固化剂、消泡剂和去离子水组成，所述离型剂层由有机硅树脂、水性蜡乳液、滑石粉和去离子水组成，所述基材由聚酯薄膜和传热介质组成，所述耐温层由氟碳、有机硅树脂和去离子水组成，
所述油墨层中各组分质量比例为：
所述离型剂层中各质量比例为：
Figure FDA00002054574000012
所述基材中各组分质量比例为：
聚酯薄膜                    85～95份
传热介质                    8～12份；
所述耐温层中各组分质量比例为：
氟碳                            15～25份
有机硅树脂                      45～55份
去离子水                        25～35份。
2.如权利要求1所述的一种热转印碳带，其特征在于：
所述油墨层中各组分质量比例为：
Figure FDA00002054574000021
所述离型剂层中各质量比例为：
Figure FDA00002054574000022
所述基材中各组分质量比例为：
聚酯薄膜                        90份
传热介质                        10份；
所述耐温层中各组分质量比例为：
氟碳                            20份
有机硅树脂                      50份
去离子水                        30份。
3.如权利要求1所述的一种热转印碳带，其特征在于：所述传热介质为导热硅脂，所述无机纳米级颜料包括炭黑、钛白粉、锌钡白、铅铬黄、铁蓝中的一种或多种，所述有机颜料包括大红粉、偶氮黄、酞菁蓝、喹吖啶酮中的一种或多种。
4.如权利要求1所述的一种热转印碳带，其特征在于：所述分散剂为六偏磷酸钠，固化剂为脂肪族多胺，消泡剂为聚醚类。
5.一种热转印碳带的制备方法，其特征在于：首先将5～9份无机纳米级颜料、5～9份有机颜料、0.2～0.7份分散剂加入到36～40份去离子水中，在1800～2200r/min的转速下搅拌1～2h，形成油墨基料，然后在油墨基料中加入40～60份水性树脂，搅拌0.5h，然后再加入0.5～1.5份固化剂和0.2～0.7份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将1～3份滑石粉加入到26～30份去离子水中，以1300～1700r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入25～35份机硅树脂和35～45份水性蜡乳液，搅拌10～30min得到离型剂层涂层乳液；然后在85～95份聚酯薄膜上均匀涂抹8～12份传热介质，形成基体；然后将15～25份氟碳和45～55份有机硅树脂混合加入到25～35份去离子水中，并在800～1200r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在80～90℃下烘干0.5～1.5h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以80～90℃烘干0.5～1.5h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以80～90℃烘干0.5～1.5h。
6.如权利要求5所述的一种热转印碳带的制备方法，其特征在于：所述油墨基料制作过程中转速为2000r/min，所述滑石粉和去离子水混合过程中，转速为1500r/min，搅拌时间为20min，所述耐温层涂层乳液制作过程中转速为1000r/min，所述烘干温度均为85℃，烘干时间均为1h。
7.如权利要求5或6所述的一种热转印碳带的制备方法，其特征在于：首先7份无机纳米级颜料、7份有机颜料、0.5份分散剂加入到38份去离子水中，以2000r/min的转速下搅拌1.5h，形成油墨基料，然后在油墨基料中加入50份水性树脂，搅拌0.5h，然后再加入1份固化剂和0.5份消泡剂，充分搅拌0.5h，形成油墨涂层乳液；然后将2份滑石粉加入到28份去离子水中，以1500r/min的转速下搅拌1h，然后在1000r/min的搅拌速度下加入30份机硅树脂和40份水性蜡乳液，搅拌20min得到离型剂层涂层乳液；然后在90份聚酯薄膜上均匀涂抹10份传热介质，形成基体；然后将20份氟碳和50份有机硅树脂混合加入到30份去离子水中，并在1000r/min的转速下搅拌1h，形成耐温层涂层乳液，然后将基体在85℃下烘干1h，在烘干后的基体的一面均匀涂敷耐温层涂层乳液，在基体的另一面均匀涂敷离型剂层涂层乳液，并将涂敷有耐温层涂层乳液和离型剂层涂层乳液的基体以85℃烘干1h，然后在涂敷有离型剂层涂层乳液的基体面上涂敷油墨涂层乳液，并以85℃烘干1h。
CN201210305198.5A 2012-08-24 2012-08-24 一种热转印碳带的制备方法 Expired - Fee Related CN102785491B (zh)