CN103753997B - 一种d2t2染料热升华打印相纸 - Google Patents
一种d2t2染料热升华打印相纸 Download PDFInfo
- Publication number
- CN103753997B CN103753997B CN201410001860.7A CN201410001860A CN103753997B CN 103753997 B CN103753997 B CN 103753997B CN 201410001860 A CN201410001860 A CN 201410001860A CN 103753997 B CN103753997 B CN 103753997B
- Authority
- CN
- China
- Prior art keywords
- emulsion
- thermal dye
- printing paper
- dye sublimation
- print printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及染料热升华转移成像技术领域,公开了一种D2T2染料热升华打印相纸及制造方法,所述打印相纸包括:抗卷曲层、纸基、影像接收层,所述纸基的一面设有抗卷曲层,另一面设有影像接受层;所述影像接受层由水性树脂组合物构成;所述水性树脂组合物包括:水性乳液、增白剂、离型剂。本发明的结构简单、安全实用,其采用水性树脂混合物作为打印相纸的影像接收层,替代以往的溶剂型涂料的接受层,在制造D2T2染料热升华打印相纸生产过程中实现了零VOC排放,避免了对环境的污染,同时保护了生产现场安全,并使之有更好的染料接受性能、耐热性能、分离性能,使D2T2染料热升华打印相纸有完美的色彩还原性和良好的耐久性能。
Description
技术领域
本发明涉及Dye Diffusion Thermal Transfer(D2T2)染料热升华转移成像技术领域,特别涉及一种D2T2染料热升华打印相纸。
背景技术
数码相机的发展和普及,取代了传统的胶卷相机,使柯达、富士、乐凯三大胶卷厂商先后停止胶卷的生产。照片输出也从传统的银盐感光相纸转到D2T2染料热升华打印相纸。热升华打印机热敏头采用256阶温度控制,按黄、品红、青三元色色序叠加打印,实现1677万种色彩输出。在打印时,色带和打印介质紧密贴合,同步通过打印头,在打印头下被加热,色带的染料升华,同时相纸表面的高分子聚合物涂层受热活化,被染料染色而形成色域宽广、分辨率高、层次丰富、连续色调的影像。
D2T2染料热升华打印相纸采用高分子聚合物作为影像接受层,其具有耐水、耐候、耐微生物、耐指纹、耐污染、耐紫外等性能,大大高于明胶涂层的传统感光冲印照片,并且可以实现即时打印输出,广泛的应用于人像摄影,医疗影像,证件照片等领域。染料热升华数码打印技术除了可以打印出超过传统的银盐相纸质量的照片,最大优势是染料热升华干法成像,色带中使用的染料不溶于水,塑料色带盒完全可以回收再生,循环使用,最终的色带盒也回收方便,可以重新造粒用于其它行业,对环境完全没有污染。
目前,生产D2T2染料热升华打印相纸接受层均使用溶剂型涂料,如美国专利US6,995,118,中国专利 200710021120,中国专利CN201080001386.8,日本专利特开2006-263897,大量的使用甲苯,丁酮,环己酮等溶剂,不仅容易污染环境,而且使生产现场存在安全风险。
发明内容
本发明的目的是:为了解决采用溶剂型涂料作为打印相纸接收层容易污染环境,且在生产区存在安全隐患的技术问题,提供一种D2T2染料热升华打印相纸,在制造D2T2染料热升华打印相纸生产过程中实现了零VOC排放,避免了对环境的污染,同时保护了生产现场安全。
为达到上述目的,本发明采用的技术方案是:提供了一种D2T2染料热升华打印相纸,包括:抗卷曲层1、纸基2、影像接受层3,所述纸基2的一面设有抗卷曲层1,另一面设有影像接受层3;所述影像接受层3由水性树脂组合物和去离子水构成;所述水性树脂组合物包括:水性乳液、增白剂、离型剂;所述影像接受层3含有下列质量份数的各组份:90份水性乳液、1份增白剂、0.5份离型剂、20份去离子水。
其中:所述水性乳液包括:水性丙烯酸树脂乳液、水性聚氨酯乳液、苯丙乳液、聚醋酸乙烯-乙烯乳液、氯醋乳液、聚四氟乙烯乳液、水性有机硅乳液、乙酸乙烯-丙烯酸酯共聚物乳液中的一种或几种。
其中:所述水性丙烯酸树脂乳液含有羟基和羧基,并有较高的玻璃化温度;所述水性聚氨酯乳液含有肼基,并能和丙烯酸树脂乳液中的酮羰基交联。
其中:所述水性乳液中含有60份的水性丙烯酸树脂乳液和30份水性聚氨酯树脂乳液。
其中:所述抗卷曲层1中含有下列质量份数的各组份:10份水性胶粘剂、0.8份交联剂、20份防滑剂、1份抗静电剂。
其中:所述水性胶粘剂为聚乙烯醇、明胶、改性淀粉、VAE乳液、丙烯酸乳液,苯丙乳液、丁苯乳液中的一种或几种。
其中:所述交联剂为硼酸、硼砂、乙二醛、戊二醛、碳酸锆铵、聚酰胺聚脲树脂、三聚氢胺甲醛树脂、剂聚酰胺聚脲环氧氯丙烷树脂、水性异氰酸酯的一种或几种。
其中:所述抗静电剂为季铵盐、聚季铵盐、脂肪醇醚磷酸酯,脂肪醇醚磷酸酯钾盐中的一种或几种。
本发明还公开了一种D2T2染料热升华打印相纸的制造方法,首先,在纸基2的一面采用丝棒涂布方式形成抗卷曲层1,这种涂布方式可以获得较凹版涂布方式更厚的涂层。然后,在纸基2的另一面采用坡流挤压涂布方式形成染料影像接受层3,坡流挤压涂布方式不受纸基厚度变化的影响,可以获得厚度均匀一致的涂层。
其中:所述影像接受层3的涂覆干膜厚度为3-8μm,低于3μm,影像的饱和度较差,厚度大于8μm,则增加成本。
其中:所述影像接受层3的涂层干膜厚度为4-6μm。
其中:所述抗卷曲层1的涂覆干膜厚度在5-10μm,低于5μm质感较差,高于10μm会使成本增加。
本发明的有益效果是:本发明的结构简单、安全实用,其采用水性树脂混合物作为打印相纸的影像接受层,替代以往的溶剂型涂料的接受层,在制造D2T2染料热升华打印相纸生产过程中实现了零VOC排放,避免了对环境的污染,同时保护了生产现场安全,并使之有更好的染料接受性能、耐热性能、分离性能,使D2T2染料热升华打印相纸有完美的色彩还原性和良好的耐久性能。
附图说明
图1为本发明一种D2T2染料热升华打印相纸的结构示意图。
附图标识:1-抗卷曲层,2-纸基,3-染料影像接受层。
具体实施方式
下面结合附图和实施例对本发明进行详细说明。
参照图1,本发明一种D2T2染料热升华打印相纸,包括:抗卷曲层1、纸基2、影像接受层3;所述纸基2为多层复合专用纸基,该纸基2具有一定的弹性模量和较低的导热系数,其一面设有抗卷曲层1,另一面设有影像接受层3;所述影像接受层3由水性树脂组合物和去离子水构成;所述水性树脂组合物包括:水性乳液、增白剂、离型剂;所述影像接受层3含有下列质量份数的各组份:90份水性乳液、1份增白剂、0.5份离型剂、20份去离子水,上述各组分按顺序加入带搅拌的制料桶内,开动搅拌器,搅拌3小时,使物料混合均匀,用325目滤网过滤,装入储存桶内密封保存待用。
所述使用经过处理的去离子水的目的是避免自然界的水中杂离子对染料影像接受层涂料成膜性带来影响。
所述水性乳液包括:水性丙烯酸树脂乳液、水性聚氨酯乳液、苯丙乳液、聚醋酸乙烯-乙烯乳液、氯醋乳液、聚四氟乙烯乳液、水性有机硅乳液、乙酸乙烯-丙烯酸酯共聚物乳液中的一种或几种。
所述水性丙烯酸树脂乳液含有羟基和羧基,并有较高的玻璃化温度;所述水性聚氨酯乳液含有肼基,并能和丙烯酸树脂乳液中的酮羰基交联形成立体网状结构,提高耐热性,并且乳液的粒径应低于0. 2μm,这样可以获得较高光泽度的涂层。
所述水性乳液中含有60份的水性丙烯酸树脂乳液和30份水性聚氨酯树脂乳液。
为了提高D2T2染料热升华打印相纸的遮盖性、白度、色相和质感,染料影像接受层3中还可以含有:钛白粉、荧光增白剂;染料影像接受层3中也可能含有离型剂,以提高和色带的分离性能;为了改善染料影像接受层3的涂布性能,其中也可能含有各种助剂,如流平剂,润湿剂,分散剂,消泡剂。
所述抗卷曲层1的目的是平衡染料影像接受层3的张力,使得D2T2染料热升华打印相纸在自然存放过程中平整,易于对热升华打印照片的整理和保存。所述抗卷曲层1中含有下列质量份数的各组份:10份水性胶粘剂、0.8份交联剂、20份防滑剂、1份抗静电剂,上述各组分按顺序加入带搅拌的制料桶内,开动搅拌器,搅拌3小时,使物料混合均匀,用200目滤网过滤,装入储存桶内密封保存待用。
所述水性胶粘剂可以是聚乙烯醇、VAE乳液、丙烯酸树脂乳液;防滑剂可以是二氧化硅、树脂型消光粉、轻质碳酸钙、重质碳酸钙、高龄土、膨润土;所述交联剂为硼酸、硼砂、乙二醛、戊二醛、碳酸锆铵、聚酰胺聚脲树脂、三聚氢胺甲醛树脂、剂聚酰胺聚脲环氧氯丙烷树脂、水性异氰酸酯的一种或几种。
所述抗静电剂为季铵盐、聚季铵盐、脂肪醇醚磷酸酯,脂肪醇醚磷酸酯钾盐中的一种或几种。
本发明一种D2T2染料热升华打印相纸的制造方法: 首先,在纸基2的一面采用丝棒涂布方式形成抗卷曲层1,这种涂布方式可以获得较凹版涂布方式更厚的涂层。然后,在纸基2的另一面采用坡流挤压涂布方式形成染料影像接受层3,坡流挤压涂布方式不受纸基厚度变化的影响,厚度均匀一致。
以往染料热升华打印相纸接受层均使用溶剂型涂料,含有甲苯,丁酮,环己酮等溶剂,不能使用坡流挤压涂布方式涂覆形成染料影像接受层,本发明所采用的水性树脂组合物制备的D2T2染料热升华打印相纸接受层,可以采用坡流挤压涂布方式形成染料影像接受层,能获得比凹版涂布更厚的涂层,有效保证获得厚度均匀一致的涂层。
所述影像接受层3的涂覆干膜厚度为3-8μm,低于3μm,影像的饱和度较差,厚度大于8μm,则增加成本。
所述影像接受层3的涂层干膜厚度为4-6μm。
所述抗卷曲层1的涂覆干膜厚度在5-10μm,低于5μm质感较差,高于10μm会使成本增加。
实施例1
本发明D2T2染料热升华打印相纸的制造方法,包括以下步骤:
步骤1:抗卷曲层1涂料的制备;
准确称取质量份10份聚乙烯醇溶液、0.8份交联剂、20份防滑剂、1份抗静电剂,按顺序加入搅拌桶内,开动搅拌器,搅拌1小时,使物料混合均匀,用200目滤网过滤,装入储存桶内密封保存待用。
步骤2:抗卷曲层1的涂布;
使用计量棒涂布机,把制备好的抗卷曲层1涂料用线径0.3mm的计量棒涂在纸基上,经过气流冲击干燥,得到干膜厚度5-10μm的抗卷曲层1,收卷后存放,待涂布染料影像接受层3;所述抗卷曲层1可以采用多种涂覆方式形成涂层,如辊涂,吻涂,计量棒涂布,凹版涂布;优选为计量棒涂布方式。
步骤3染料影像接受层3涂料的制备;
准确称取质量份60份水性丙烯酸树脂乳液、30份水性聚氨酯树脂乳液、1份荧光增白剂、0.5份的离型剂、20份去离子水,按顺序加入搅拌桶内,开动搅拌器,搅拌3小时,使物料混合均匀,用325目滤网过滤,装入储存桶内密封保存待用。
步骤4:染料影像接受层3的涂布;
使用坡流挤压式涂布机,把制备好的染料影像接受层3涂料涂覆在已经涂布过抗卷曲层1的纸基2上,该纸基2在涂覆染料影像接受层3涂料之前,须经电晕处理;染料影像接受层3经过气流冲击干燥,得到干膜厚度4-6μm的染料影像接受层3,经分切整理、包装,即成为D2T2染料热升华打印相纸成品。所述染料影像接受层3可以采用多种涂覆方式形成涂层,如逗号刮刀涂布,辊涂,吻涂,计量棒涂布,坡流挤压涂布;优选为挤压涂布方式。
以上内容是结合优选技术方案对本发明所做的进一步详细说明,不能认定发明的具体实施仅限于这些说明。对本发明所属技术领域的普通技术人员来说,在不脱离本发明的构思的前提下,还可以做出简单的推演及替换,都应当视为本发明的保护范围。
Claims (7)
1.一种D2T2染料热升华打印相纸,包括:抗卷曲层(1)、纸基(2)、影像接受层(3),所述纸基(2)的一面设有抗卷曲层(1),另一面设有影像接受层(3);其特征在于:所述影像接受层(3)由水性树脂组合物和去离子水构成;所述水性树脂组合物包括:水性乳液、增白剂、离型剂;所述影像接受层(3)含有下列质量份数的各组份:90份水性乳液、1份增白剂、0.5份离型剂、20份去离子水,所述抗卷曲层(1)中含有下列质量份数的各组份:10份水性胶粘剂、0.8份交联剂、20份防滑剂、1份抗静电剂。
2.根据权利要求1所述的D2T2染料热升华打印相纸,其特征在于:所述水性乳液包括:水性丙烯酸树脂乳液、水性聚氨酯乳液、苯丙乳液、聚醋酸乙烯-乙烯乳液、氯醋乳液、聚四氟乙烯乳液、水性有机硅乳液、乙酸乙烯-丙烯酸酯共聚物乳液中的一种或几种。
3.根据权利要求2所述的D2T2染料热升华打印相纸,其特征在于:所述水性丙烯酸树脂乳液含有羟基和羧基;所述水性聚氨酯乳液含有肼基,并能和丙烯酸树脂乳液中的酮羰基交联。
4.根据权利要求1所述的D2T2染料热升华打印相纸,其特征在于:所述水性乳液中含有60份的水性丙烯酸树脂乳液和30份水性聚氨酯树脂乳液。
5.根据权利要求1所述的D2T2染料热升华打印相纸,其特征在于:所述水性胶粘剂为聚乙烯醇、明胶、改性淀粉、VAE乳液、丙烯酸乳液、苯丙乳液、丁苯乳液中的一种或几种。
6.根据权利要求1所述的D2T2染料热升华打印相纸,其特征在于:所述交联剂为硼酸、硼砂、乙二醛、戊二醛、碳酸锆铵、聚酰胺聚脲树脂、三聚氢胺甲醛树脂、剂聚酰胺聚脲环氧氯丙烷树脂、水性异氰酸酯中的一种或几种。
7.根据权利要求1所述的D2T2染料热升华打印相纸,其特征在于:所述抗静电剂为季铵盐、聚季铵盐、脂肪醇醚磷酸酯,脂肪醇醚磷酸酯钾盐中的一种或几种。