CN102089451A - 快速加热热压用镀铝钢板及其制造方法、以及使用该镀铝钢板的快速加热热压方法 - Google Patents
快速加热热压用镀铝钢板及其制造方法、以及使用该镀铝钢板的快速加热热压方法 Download PDFInfo
- Publication number
- CN102089451A CN102089451A CN2009801270166A CN200980127016A CN102089451A CN 102089451 A CN102089451 A CN 102089451A CN 2009801270166 A CN2009801270166 A CN 2009801270166A CN 200980127016 A CN200980127016 A CN 200980127016A CN 102089451 A CN102089451 A CN 102089451A
- Authority
- CN
- China
- Prior art keywords
- aludip
- quality
- hot pressing
- rapid heating
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
C | Si | Mn | P | S | Al | N | Ti | Cr | B |
0.22 | 0.21 | 1.22 | 0.02 | 0.004 | 0.027 | 0.003 | 0.02 | 0.12 | 0.0034 |
C | Si | Mn | P | S | Al | N | Ti | Cr | B | Hv | |
A | 0.02 | 0.19 | 1.21 | 0.02 | 0.004 | 0.023 | 0.003 | 0.02 | 0.13 | 0.0030 | 260 |
B | 0.10 | 0.20 | 1.21 | 0.02 | 0.005 | 0.021 | 0.003 | 0.02 | 0.13 | 0.0033 | 390 |
C | 0.15 | 0.20 | 1.21 | 0.02 | 0.005 | 0.023 | 0.002 | 0.02 | 0.13 | 0.0031 | 440 |
Claims (9)