WO2017034001A1 - 非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池 - Google Patents

非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池 Download PDF

Info

Publication number
WO2017034001A1
WO2017034001A1 PCT/JP2016/074843 JP2016074843W WO2017034001A1 WO 2017034001 A1 WO2017034001 A1 WO 2017034001A1 JP 2016074843 W JP2016074843 W JP 2016074843W WO 2017034001 A1 WO2017034001 A1 WO 2017034001A1
Authority
WO
WIPO (PCT)
Prior art keywords
positive electrode
lithium
active material
electrode active
powder
Prior art date
Application number
PCT/JP2016/074843
Other languages
English (en)
French (fr)
Inventor
寛子 大下
一臣 漁師
元彬 猿渡
Original Assignee
住友金属鉱山株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友金属鉱山株式会社 filed Critical 住友金属鉱山株式会社
Priority to US15/754,726 priority Critical patent/US10586983B2/en
Priority to KR1020187005207A priority patent/KR102632822B1/ko
Priority to CN201680048965.5A priority patent/CN107925079B/zh
Publication of WO2017034001A1 publication Critical patent/WO2017034001A1/ja

Abstract

正極合材ペーストのゲル化を抑制し、さらに耐候性に優れた非水系電解質二次電池用正極活物質とその製造方法などを提供する。　一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物からなる粉末を、水酸化リチウム以外の水溶性リチウム塩から選ばれる１種類以上のリチウム塩を含む水溶液により洗浄すること、および、洗浄後の前記粉末を乾燥すること、を含むことを特徴とする非水系電解質二次電池用正極活物質の製造方法などによる。

Description

非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
　本発明は、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池に関する。
　近年、携帯電話やノート型パソコンなどの携帯電子機器の普及に伴い、高いエネルギー密度を有する小型で軽量な非水系電解質二次電池の開発が要求されている。また、ハイブリッド自動車を始めとする電気自動車用の電池として、高出力の非水系電解質二次電池の開発も要求されている。このような要求を満たす非水系電解質二次電池として、リチウムイオン二次電池がある。リチウムイオン二次電池は、負極、正極、電解液などで構成され、負極および正極の活物質には、リチウムを脱離および挿入することが可能な材料が用いられている。
　リチウムイオン二次電池については、現在、研究開発が盛んに行われているところである。中でも、層状またはスピネル型のリチウム金属複合酸化物を正極活物質に用いたリチウムイオン二次電池は、４Ｖ級の高い電圧が得られるため、高いエネルギー密度を有する電池として実用化が進んでいる。これまで主に提案されているリチウム金属複合酸化物としては、合成が比較的容易なリチウムコバルト複合酸化物（例えば、ＬｉＣｏＯ２）や、コバルトよりも安価なニッケルを用いたリチウムニッケル複合酸化物（例えば、ＬｉＮｉＯ２）、リチウムニッケルコバルトマンガン複合酸化物（例えば、ＬｉＮｉ１／３Ｃｏ１／３Ｍｎ１／３Ｏ２）、リチウムマンガン複合酸化物（例えば、ＬｉＭｎ２Ｏ４）などが挙げられる。
　リチウムコバルト複合酸化物を正極活物質として用いた電池では、優れた初期容量特性やサイクル特性を得るための開発がこれまで数多く行われており、すでにさまざまな成果が得られている。しかし、リチウムコバルト複合酸化物は、原料に高価なコバルト化合物が用られる。このため、リチウムコバルト複合酸化物は、これを用いた電池の容量あたりの単価がニッケル水素電池より大幅に高く、正極活物質として適用可能な用途がかなり限定される。したがって、携帯機器用の小型二次電池についてだけではなく、電力貯蔵用や電気自動車用などの大型二次電池についても、正極活物質のコストを下げ、より安価なリチウムイオン二次電池の製造を可能とすることに対する期待は大きく、その実現は、工業的に大きな意義があるといえる。
　コバルトよりも安価なニッケルを用いたリチウムニッケル複合酸化物は、リチウムコバルト複合酸化物よりも低い電気化学ポテンシャルを示すため、電解液の酸化による分解が問題になりにくく、より高容量が期待でき、コバルト系と同様に高い電池電圧を示すことから、開発が盛んに行われている。しかし、純粋にニッケルのみで合成したリチウムニッケル複合酸化物は、これを正極材料としてリチウムイオン二次電池を作製した場合、コバルト系と比較してサイクル特性が劣り、また、高温環境下で使用や保存により比較的電池性能を損ないやすいという欠点を有する。そのため、例えば特許文献１に開示されるように、ニッケルの一部をコバルトやアルミニウムで置換したリチウムニッケル複合酸化物が一般的に知られている。
　正極活物質であるリチウムニッケル複合酸化物の一般的な製造方法としては、中和晶析法により前駆体であるニッケル複合水酸化物を作製し、この前駆体を水酸化リチウムなどのリチウム化合物と混合して焼成し、リチウムニッケル複合酸化物を得る方法が知られている。しかしながら、この方法で合成したリチウムニッケル複合酸化物には未反応の水酸化リチウムが残留している。未反応の水酸化リチウムは、正極活物質を正極合材ペーストに混練する際に、正極合材ペーストのゲル化を引き起こす原因になる。さらに正極活物質が高温環境下で充電される場合、未反応の水酸化リチウムが酸化分解しガス発生を引き起こす要因にもなる。
　そこで、特許文献２によれば合成後のリチウムニッケル複合酸化物に自然水を加えて攪拌し、水酸化リチウムを除去する方法が提案されている。また、特許文献３によれば焼成後のリチウムニッケル複合酸化物に含まれる未反応のアルカリ分を水洗により除去する方法が提案されている。
　また、特許文献４によれば合成後のリチウムニッケル複合酸化物に自然水を加えて攪拌し、水酸化リチウムを除去した後、酸素濃度が８０容量％以上の酸素雰囲気下、１２０℃以上５５０℃以下の温度で熱処理する方法が提案されている。この方法で得られる正極活物質は、水洗時に欠損した表面のリチウムが、粒子内部から補填されるため、その表面にリチウム欠損が存在せず、電池の正極抵抗を低減させることができるとしている。
特開平０５－２４２８９１号公報 特開２００７－２７３１０８号公報 特開１９９６－１３８６６９号公報 国際公開第２０１４／１８９１０８号
　しかしながら、特許文献２および特許文献３の水洗による洗浄方法は、水洗の際に、リチウムニッケル複合酸化物に含まれる水酸化リチウムが除去されるのみならず、リチウムニッケル複合酸化物の結晶格子内からもリチウムが引き抜かれ、リチウム化合物が多く溶出することにより、その表面の結晶でリチウムイオンの欠損が生じ、電池容量の低下や電池抵抗が増大するという問題点がある。また、上記特許文献４に記載される方法では、正極活物質粒子内部から粒子表面へリチウムがごく少量ではあるが補充されており、正極活物質全体から見たリチウム欠損の解決には改善の余地があった。
　本発明の目的はこのような問題に鑑みて、正極合材ペーストのゲル化を抑制し、さらに、二次電池に用いた場合、高容量が得られ、かつ、正極抵抗が低減された非水系電解質二次電池用正極活物質とその製造方法を提供することを目的とする。
　本発明者は、上記課題を解決するため、非水系電解質二次電池用正極活物質として用いられているリチウム金属複合酸化物およびその製造方法に関して鋭意研究を重ねた結果、リチウムニッケル複合酸化物からなる粉末を、リチウム塩を含む水溶液により洗浄することによって、未反応の水酸化リチウムや原料由来の不純物を除去するとともに、リチウムニッケル複合酸化物の格子内からのリチウム引き抜きを防止することが可能であるとの知見を得て、本発明を完成した。
　本発明の第１の態様では、一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物からなる粉末を、水酸化リチウム以外の水溶性リチウム塩から選ばれる１種類以上のリチウム塩を含む水溶液により洗浄すること、および、洗浄後の前記粉末を乾燥すること、を含む非水系電解質二次電池用正極活物質の製造方法が提供される。
　また、水溶液は、リチウム濃度が０．１ｇ／Ｌ以上５．０ｇ／Ｌ以下であることが好ましい。また、洗浄は、粉末を含む水溶液のスラリー濃度が１００ｇ／Ｌ以上３０００ｇ／Ｌの状態で洗浄することが好ましい。
　本発明の第２の態様では、一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物の粉末からなる非水系電解質二次電池用正極活物質であって、水酸化リチウム含有量が０．５質量％以下であり、かつ、Ｘ線光電子分光法により測定される前記粉末表面のＬｉとＬｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）との組成比（Ｌｉ／（Ｎｉ＋Ｃｏ＋Ｍ））が０．８０以上１．５以下である非水系電解質二次電池用正極活物質が提供される。
　また、上記粉末を水に分散させた５質量％の懸濁溶液における粉体ｐＨが、１１．５以下であることが好ましい。
　本発明の第３の態様では、上記非水系電解質二次電池用正極活物質を正極に含む非水系電解質二次電池が提供される。
　本発明の正極活物質によれば、正極合材ペーストのゲル化を抑制し、さらに、二次電池に用いた場合、高容量が得られ、かつ、正極抵抗が低減された非水系電解質二次電池用正極活物質が得られる。さらに、本発明の製造方法は、この正極活物質を容易に生産でき、特に工業的規模での大量生産に適するため、その工業的価値は極めて大きい。
図１は、本実施形態に係る非水系電解質二次電池用正極活物質の製造方法の一例を示すフローチャートである。 図２は、電池評価に使用したコイン型電池の概略断面図である。 図３は、インピーダンス測定法によるナイキストプロット（上段）及び等価回路（下段）を示す図である。
１．非水系電解質二次電池用正極活物質の製造方法
　以下、図を参照して、本発明の実施形態の一例を説明する。図１は、本実施形態に係る非水系電解質二次電池用正極活物質（以下、「正極活物質」ともいう。）の製造方法を示すフローチャートである。なお、以下の説明は、製造方法の一例であって、本発明の製造方法を限定するものではない。
　図１に示すように、リチウムニッケル複合酸化物からなる粉末を炭酸リチウム水溶液により洗浄する（ステップＳ１）。まず、母材として、リチウムニッケル複合酸化物からなる粉末（以下、単に「粉末」ともいう。）を準備する。粉末は、一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表される。
　粉末の製造方法は、特に限定されず、公知の方法で製造できる。粉末の製造方法は、例えば、リチウムを含む化合物と、リチウム以外の金属（ニッケル、コバルトなどの遷移金属やアルミニウム等）を含む化合物とを混合し、焼成する方法や、リチウムとリチウム以外の金属を含む水溶液を噴霧熱分解処理する方法や、中和晶析法により得られたリチウム以外の金属を含む水酸化物、あるいは該水酸化物を熱処理して得られる酸化物と、リチウム化合物とを混合し、焼成する方法などが挙げられる。これらの中でも、中和晶析法により得られたリチウム以外の金属を含む水酸化物を用いる方法は、得られる粉末の比表面積などを所望の範囲に容易に制御できる。また、粉末の原料として、水酸化物などを用い、粉末中にこれらに由来する物質が残留している場合、本実施形態の製造方法を好適に用いることができる。
　粉末は、水酸化リチウム以外の水溶性リチウム塩から選ばれる１種類以上のリチウム塩を含む水溶液（以下、「リチウム塩水溶液」ともいう。）により洗浄される。洗浄は、例えば、粉末をリチウム塩水溶液中に分散させて、撹拌することにより行う。このリチウム塩を含む水溶液による洗浄により、粉末表面に存在する水酸化リチウムなどの不純物が除去されると同時に、粉末表面の結晶格子内からのリチウム引き抜きが抑制される。これにより、正極合材ペーストのゲル化を抑制しつつ、さらに電池の正極抵抗を低減して高容量かつ出力特性に優れた正極活物質が得られる。
　洗浄に用いられる水溶液は、水酸化リチウム以外の水溶性リチウム塩から選ばれる１種類以上のリチウム塩を溶質として含む。水酸化リチウム以外の水溶性リチウム塩としては、特に限定されず、公知のリチウム塩を用いることができ、例えば、炭酸リチウム、炭酸水素リチウム、クエン酸リチウム、酢酸リチウム、シュウ酸リチウム、酒石酸リチウム、硫酸リチウム、硝酸リチウム、塩化リチウム、臭化リチウム、ヨウ化リチウムなどを用いることができる。また、水溶性リチウム塩として硝酸リチウム、硫酸リチウムを用いることにより、より正極抵抗（以下、「反応抵抗」ともいう。）を低減することができる。また、硫酸根の残留量を低減するという観点から、硫酸塩以外の水溶性リチウム塩を用いることが好ましい。また、リチウム塩は、１種類単独で用いられてもよいし、２種類以上が併用されてもよい。なお、発明の効果を阻害しない範囲であれば、水溶性リチウム塩以外の溶質を含んでもよい。
　なお、水酸化リチウムを含む水溶液を用いて洗浄した場合、正極活物質に残留した水酸化リチウムが、正極合材ペーストのゲル化を引き起こす原因の一つとなる。また、この正極活物質を高温環境下で充電した場合、残留した水酸化リチウムが酸化分解しガス発生を引き起こす要因の一つとなる。
　リチウム塩水溶液のリチウム濃度は、特に限定されず、水に可溶な範囲とすることができる。リチウム濃度は、例えば、０．１ｇ／Ｌ以上５．０ｇ／Ｌ以下である。リチウム濃度が０．１ｇ／Ｌ未満である場合、粉末表面の結晶格子内からのリチウム引き抜きを防止する効果が十分でなく、期待される効果が得られ難いことがある。一方、５．０ｇ／Ｌを超える場合、過度のリチウム化合物が正極活物質中に残留し、電池性能が低下する恐れがある。
　リチウム塩水溶液のリチウム濃度は、好ましくは０．３ｇ／Ｌ以上５．０ｇ／Ｌ以下であり、より好ましくは０．５ｇ／Ｌ以上３．０ｇ／Ｌ以下、さらに好ましくは１．０ｇ／Ｌ以上２．５ｇ／Ｌ以下である。リチウム濃度が上記範囲であることにより、より効率的に正極活物質中のリチウム含有量などを容易に所望の範囲に調整することができる。
　粉末を含むリチウム塩水溶液のスラリー濃度は、特に限定されず、リチウム塩水溶液中に粉末が均一に分散されればよい。スラリー濃度は、例えば、１００ｇ／Ｌ以上３０００ｇ／Ｌ以下である。ここで、スラリー濃度の単位であるｇ／Ｌは、スラリー中の炭酸リチウム水溶液量（Ｌ）に対する粉末量（ｇ）を意味する。スラリー濃度が上記範囲である場合、スラリー濃度が高いほどスラリー中に含まれる粉末量は多くなり、大量の粉末を処理することができる。スラリー濃度が１００ｇ／Ｌ未満である場合、粉末表面の結晶格子内からのチリウムの引き抜きを防止する効果が十分でなく、期待される効果が得られない場合がある。一方、スラリー濃度が３０００ｇ／Ｌを超えると、スラリー粘度が非常に高くなり攪拌が困難となったり、水酸化リチウムが十分に除去されなかったりする場合がある。
　粉末を含むリチウム塩水溶液のスラリー濃度は、好ましくは１００ｇ／Ｌ以上２５００ｇ／Ｌ以下、より好ましくは２００ｇ／Ｌ以上２０００ｇ／Ｌ以下、さらに好ましくは４００ｇ／Ｌ以上２０００ｇ／Ｌ以下である。スラリー濃度が上記範囲である場合、スラリーの粘度が適切な範囲となり、水酸化リチウムなどをより効率的に除去することができる。
　上記以外の洗浄の条件は、特に限定されず、粉末に残留した水酸化リチウムや硫酸根を十分除去し、炭酸リチウムの含有量が所望の範囲となるように、適宜調整することができる。例えば、粉末を含む炭酸リチウム水溶液を攪拌する場合、攪拌時間は、５分～１時間程度とすることができる。また、洗浄の温度は、例えば、１０℃～３０℃程度とすることができる。
　なお、洗浄の際、粉末中のリチウムがスラリー中に溶出し、洗浄前後で粉末のＬｉの原子比が異なるものとなることがある。この場合、洗浄によって変化する原子比は主にＬｉであり、洗浄前のＬｉ以外の金属の原子比は洗浄後も維持される。上記の洗浄により減少するＬｉの原子比は、例えば、０．０３～０．０８程度とする。リチウム塩水溶液を用いた洗浄は、通常の水を用いた洗浄と比較して、洗浄により減少するＬｉの原子比の値が小さく、Ｌｉの減少は緩和される傾向にある。洗浄後のＬｉの原子比は、予め洗浄条件を同じにした予備試験によって洗浄前後でのＬｉの原子比の減少量を確認し、母材としてＬｉの原子比を調整したリチウム金属複合酸化物粉末を用いることにより制御することができる。
　次に、図１に示すように、炭酸リチウム水溶液により洗浄した後、粉末を含むスラリーを濾過する（ステップＳ２）。濾過の方法は、特に限定されず、公知の方法で行うことができる。濾過は、例えば、吸引濾過機、フィルタープレスや遠心機などの通常用いられる濾過装置を用いて、行うことができる。濾過を行うことにより、スラリーの固液分離の際、粉末表面に残存する付着水の量を減少させることができる。付着水が多い場合、液中に溶解したリチウム塩が再析出し、乾燥後のリチウムニッケル複合酸化物粒子の表面に存在するリチウム量が期待する範囲から外れることがある。なお、ステップＳ２を行うか否かは任意である。ステップ２Ｓを行なわない場合、例えば、スラリーを静置し、又は、遠心し、上澄みを除去することなどにより、付着水を除去してもよい。
　次に、図１に示すように、濾過後、得られた粉末を乾燥する（ステップＳ３）。乾燥温度は、特に限定されず、粉末に含まれる水分が十分除去される温度であればよい。乾燥温度は、例えば、８０℃以上３５０℃以下であるのが好ましい。乾燥温度が８０℃未満の場合、洗浄後の粉末の乾燥が遅くなるため、粉末表面と粉末内部との間でリチウム濃度の勾配が生じ、得られる正極活物質の電池特性が低下することがある。一方、乾燥温度が３５０℃を超える場合、粉末表面付近の結晶構造が崩れ、得られる正極活物質の電池特性が低下することがある。これは、洗浄後の粉末の表面付近の結晶構造は、化学量論比にきわめて近いか、もしくは若干リチウムが脱離して充電状態に近い状態になっており、崩れやすくなっているためであると考えられる。
　乾燥時間は、特に限定されず、乾燥後の粉末の水分率が０．２質量％以下、より好ましくは０．１質量％以下、さらに好ましくは０．０５質量％以下となる時間で乾燥することが好ましい。乾燥時間は、例えば、１時間以上２４時間以下である。なお、粉末の水分率は、カールフィッシャー水分計により気化温度３００℃で測定することができる。
　乾燥雰囲気は、炭素および硫黄を含む化合物成分を含有しないガス雰囲気下、または真空雰囲気下で乾燥することが好ましい。粉末中の炭素および硫黄量は、洗浄（ステップＳ１）により容易に制御できる。乾燥（ステップＳ３）時に、さらに炭素および硫黄化合物成分を含有する雰囲気下、または真空雰囲気下で乾燥すると、粉末中の炭素量および硫黄量が変化し、期待する効果が得られないことがある。
２．非水系電解質二次電池用正極活物質
　本実施形態に係る正極活物質は、一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物の粉末からなる正極活物質であって、水酸化リチウム含有量が０．５質量％以下であり、かつ、Ｘ線光電子分光法により測定される前記粉末表面のＬｉとＬｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）との組成比（Ｌｉ／（Ｎｉ＋Ｃｏ＋Ｍ））が０．８０以上１．５以下である。以下、正極活物質の実施形態の一例について説明する。
　［粉末全体組成］
　非水系電解質二次電池用正極活物質は、一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物からなる。
　上記一般式中、ｚは、リチウムニッケル複合酸化物中のＬｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）の原子比を１としたときの、Ｌｉの原子比を示す。ｚの範囲は、０．９５≦ｚ≦１．１０である。ｚが上記範囲である場合、ｚの値が大きくなるに応じて充放電容量は増加する。ｚが０．９５未満である場合、正極の反応抵抗が大きくなり、電池出力が低くなることがある。一方、ｚが１．１０を超える場合、二次電池の安全性が低下することがある。電池出力及び安全性のバランスの観点から、ｚの範囲は、好ましくは０．９７≦ｚ≦１．０５、より好ましくは０．９７≦ｚ≦１．００である。上述したように、リチウムニッケル複合酸化物からなる粉末を母材として洗浄した場合、この粉末からＬｉが溶出することがある。したがって、洗浄する場合、洗浄前後でのＬｉの減少量を予備実験により確認し、洗浄後のＬｉの元素比が上記範囲となるように、洗浄前の粉末を準備することにより、Ｌｉの原子比を上記範囲とすることができる。
　上記一般式中、ｘは、Ｌｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）の原子比を１としたときの、Ｃｏの元素比を示す。ｘの範囲は、０≦ｘ≦０．３５であり、好ましくは０＜ｘ≦０．３５である。正極活物質にコバルトを含有させることで、良好なサイクル特性を得ることができる。これは、結晶格子のニッケルの一部をコバルトに置換することにより、充放電に伴うリチウムの脱挿入による結晶格子の膨張収縮挙動を低減できるためである。
　ｘの範囲は、二次電池のサイクル特性向上の観点から、好ましくは、０．０３≦ｘ≦０．３５であり、より好ましくは０．０５≦ｘ≦０．３５である。また、ｘの範囲は、二次電池の電池容量の観点から、好ましくは、０．０３≦ｘ≦０．１５であり、より好ましくは０．０５≦ｘ≦０．１５である。また、ｘの範囲は、熱安定性の観点から、好ましくは０．０７≦ｘ≦０．２５であり、より好ましくは０．１０≦ｘ≦０．２０である。
　上記一般式中、ｙは、Ｌｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）の原子比を１としたときの、Ｍ（添加元素）の元素比を示す。Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素である。ｙの範囲は、０≦ｙ≦０．１０であり、好ましくは、Ｍを必ず含む０＜ｙ≦０．１０、より好ましくは０＜ｙ≦０．０５である。Ｍを正極活物質中に添加することにより、この正極活物質を含む二次電池の耐久特性や安全性を向上させることができる。一方、ｙが０．１０を超えると、酸化還元反応（Ｒｅｄｏｘ反応）に貢献する金属元素が減少し、電池容量が低下することがある。また、Ｍがアルミニウムである場合、正極活物質の安全性がより向上する。
　また、上記一般式中、ニッケルの元素比は、Ｌｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）の原子比を１とした場合、０．５５以上１以下である。リチウムニッケル複合酸化物中の各金属元素の原子比は、Ｌｉ、Ｎｉ、Ｃｏ及びＭを含む原料の混合比を調整することにより上記範囲とすることができる。
［水酸化リチウム含有量］
　本実施形態の正極活物質は、水酸化リチウム含有量が０．５質量％以下、好ましくは０．２質量％以下である。正極活物質中の水酸化リチウム含有量が、０．５質量％を超えると、正極活物質をペーストに混練する際にゲル化を引き起こす原因の一つになる。さらに正極活物質が高温環境下で充電される場合、水酸化リチウムが酸化分解しガス発生を引き起こす原因の一つになる。また、正極活物質中の水酸化リチウム含有量の下限は、特に限定されないが、例えば、０．０１質量％以上である。
　ここで、正極活物質に含有される水酸化リチウムは、正極活物質を製造する際に用いた原料由来の水酸化リチウムを含む。例えば、ニッケル複合水酸化物又はニッケル複合酸化物などと水酸化リチウムなどのリチウム化合物を混合し、焼成して、リチウムニッケル複合酸化物を得る際の未反応物を含む。なお、水酸化リチウム含有量は、得られた正極活物質に純水を添加し、攪拌した後、この純水に溶出したリチウム（Ｌｉ）量を、１ｍｏｌ／リットルの塩酸で中和滴定より測定し、その後、溶出したリチウム（Ｌｉ）量から洗浄で用いたリチウム塩に由来するリチウム（Ｌｉ）量を差し引いた値を水酸化リチウム由来のリチウム（Ｌｉ）量とし、これをＬｉＯＨに換算することにより求めた値である。ここで、リチウム塩に由来するリチウム（Ｌｉ）量は、リチウム塩に含まれるＬｉ以外の１種以上の量を化学分析により求め、リチウム塩の量に換算することで求めた。
［粉末表面のＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）］
　本実施形態の正極活物質は、Ｘ線光電子分光法により測定される前記粉末表面のＬｉとＬｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）との組成比（Ｌｉ／（Ｎｉ＋Ｃｏ＋Ｍ））が０．８０以上１．５以下であり、好ましくは０．８０以上１．４５以下、より好ましくは０．９３以上１．４５以下、さらに好ましくは０．９５以上１．４５以下、特に好ましくは１．００以上１．４５以下である。粉末表面のＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が０．８０未満である場合、粒子表面でリチウムイオン欠損が生じるため、二次電池の正極に用いた場合、リチウムイオンの伝導パスが阻害されて放電容量が低下したり、反応抵抗が増加したりする要因の一つとなる。反応抵抗が低減されることで、電池内で損失される電圧が減少し、実際に負荷側に印加される電圧が相対的に高くなるため、高出力が得られる。一方、粉末表面のＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が１．５を超えると、粉末表面に過剰な水酸化リチウムなどのリチウム化合物が存在し、正極合材ペーストのゲル化を引き起こす要因の一つとなる。さらに、過剰なリチウム化合物がその表面に存在する正極活物質を高温環境下で充電した場合、リチウム化合物が分解しガス発生を引き起こし、電池特性が低下することがある。また、充放電に寄与しないリチウム化合物が存在する場合、電池を構成する際、正極活物質の不可逆容量に相当する分の負極材料を余計に使用することになる。その結果、電池全体としての重量当たり及び体積当たりの容量が小さくなることもある上、不可逆容量として負極に蓄積された余分なリチウムは安全性の面からも問題となることもある。
　なお、粉末表面のＬｉとＬｉ以外の金属との組成比（Ｌｉ／（Ｎｉ＋Ｃｏ＋Ｍ））は、後述の実施例に詳述されるように、Ｘ線光電子分光法により測定できる。また、粉体表面とは、Ｘ線光電子分光（ＸＰＳ）装置（アルバック・ファイ株式会社製、Ｖｅｒｓａ　ＰｒｏｂｅＩＩ）により測定される正極活物質の表面から中心方向に向かって深さ数ｎｍ～１０ｎｍ程度までの領域を意味する。
［粉体ｐＨ］
　本実施形態の正極活物質は、粉末を水に分散させた５質量％の懸濁溶液における粉体ｐＨが、１１．５以下である。ｐＨが１１．５を超えると、正極活物質をペーストに混練する際に正極合材ペーストがゲル化することがある。粉体ｐＨの下限は、特に限定されないが、例えば、好ましくは１０．５以上、より好ましくは１１．０以上である。
［平均粒径］
　本実施形態の正極活物質の平均粒径は、特に限定されないが、例えば、３μｍ以上２５μｍ以下であることにより、正極活物質の容積あたりの電池容量を大きくすることができ、安全性が高く、サイクル特性が良好な二次電池を得ることができる。なお、平均粒径は、レーザ回折式粒度分布計により測定される体積積算値から求めた体積平均粒径ＭＶの値である。
［比表面積］
　本実施形態の正極活物質の比表面積は、特に限定されないが、例えば、１．０ｍ２／ｇ以上７．０ｍ２／ｇ以下である場合、電解液との接触できる粒子表面が十分となる。比表面積が１．０ｍ２／ｇ未満になると、電解液と接触できる粒子表面が少なくなり、十分な充放電容量が得られないことがある。一方、比表面積が７．０ｍ２／ｇを超えると、電解液と接触する粒子表面が多くなり過ぎて安全性が低下することがある。なお、比表面積は、窒素ガス吸着法によるＢＥＴ法を用いて比表面積測定装置により測定される値である。
　本実施形態の正極活物質は、上述した正極活物質の製造方法を用いることにより、容易に、かつ、工業的規模で大量に生産することができる。
３．　非水系電解質二次電池
　本実施形態に係る非水系電解質二次電池は、上記正極活物質を正極に含む。本実施形態の非水系電解質二次電池は、一般の非水系電解質二次電池と同様に、正極、負極、セパレータ、および非水電解液から構成することができる。以下、非水系電解質二次電池の実施形態について、各構成要素、および電池の形状と構成について詳しく説明する。
　［正極］
　正極を形成する正極合材及びそれを構成する各材料について説明する。本発明の粉末状の正極活物質と、導電材、結着剤とを混合し、さらに必要に応じて活性炭、粘度調整などの目的の溶剤を添加し、これを混練して正極合材ペーストを作製する。正極合材中のそれぞれの材料の混合比も、リチウム二次電池の性能を決定する重要な要素となる。
　正極合材中の各材料の混合比は、特に限定されないが、一般のリチウム二次電池の正極と同様、溶剤を除いた正極合材の固形分の全質量１００質量％に対して、それぞれ、正極活物質を６０質量％以上９５質量％以下、導電材を１質量％以上２０質量％以下、結着剤（バインダー）を１質量％以上２０質量％以下含有することが望ましい。
　得られた正極合材ペーストは、例えば、アルミニウム箔製の集電体の表面に塗布し、乾燥して溶剤を飛散（蒸発）させる。必要に応じ、電極密度を高めるべくロールプレスなどにより加圧することもある。このようにしてシート状の正極を作製することができる。シート状の正極は、目的とする電池に応じて適当な大きさに裁断などし、電池の作製に供することができる。ただし、正極の作製方法は、上記例示のものに限られることなく、他の方法に依ってもよい。
　上記正極の作製にあたって、導電材としては、例えば、黒鉛（天然黒鉛、人造黒鉛、膨張黒鉛など）やアセチレンブラック、ケッチェンブラックなどのカーボンブラック系材料などを用いることができる。
　また、結着剤は、活物質粒子をつなぎ止める役割を果たすもので、としては、例えば、ポリフッ化ビニリデン、ポリテトラフルオロエチレン、エチレンプロピレンジエンゴム、フッ素ゴムなどの含フッ素樹脂、スチレンブタジエン、セルロース系樹脂、ポリアクリル酸、ポリプロピレン、ポリエチレンなどの熱可塑性樹脂などを用いることができる。
　また、必要に応じて、正極活物質、導電材、活性炭を分散させ、結着剤を溶解する溶剤を正極合材に添加してもよい。添加する溶剤としては、一例として、Ｎ－メチル－２－ピロリドンなどの有機溶剤を用いることができる。また、正極合材には電気二重層容量を増加させるために活性炭を添加してもよい。
　［負極］
　負極には、金属リチウム、リチウム合金など、又は、リチウムイオンを吸蔵・脱離できる負極活物質に、結着剤を混合し、適当な溶剤を加えてペースト状にした負極合材を、銅などの金属箔集電体の表面に塗布、乾燥し、必要に応じて電極密度を高めるべく圧縮して形成したものを使用する。
　負極活物質としては、例えば、天然黒鉛、人造黒鉛、フェノール樹脂などの有機化合物焼成体、コークスなどの炭素物質の粉状体を用いることができる。この場合、負極結着剤としては、正極同様、ポリフッ化ビニリデンなどの含フッ素樹脂などを用いることができ、これら活物質及び結着剤を分散させる溶剤としてはＮ－メチル－２－ピロリドンなどの有機溶剤を用いることができる。
　［セパレータ］
　正極と負極との間にはセパレータを挟み込んで配置する。セパレータは、正極と負極とを分離し電解質を保持するものであり、ポリエチレン、ポリプロピレンなどの薄い膜で、微少な穴を多数有する膜を用いることができる。
［非水系電解液］
　非水系電解液は、支持塩としてのリチウム塩を有機溶媒に溶解したものである。有機溶媒としては、エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネート、トリフルオロプロピレンカーボネートなどの環状カーボネート、また、ジエチルカーボネート、ジメチルカーボネート、エチルメチルカーボネート、ジプロピルカーボネートなどの鎖状カーボネート、さらに、テトラヒドロフラン、２－メチルテトラヒドロフラン、ジメトキシエタンなどのエーテル化合物、エチルメチルスルホン、ブタンスルトンなどの硫黄化合物、リン酸トリエチル、リン酸トリオクチルなどのリン化合物などから選ばれる１種を単独で、あるいは２種以上を混合して用いることができる。
　支持塩としては、ＬｉＰＦ６、ＬｉＢＦ４、ＬｉＣｌＯ４、ＬｉＡｓＦ６、ＬｉＮ（ＣＦ３ＳＯ２）２など、及びそれらの複合塩を用いることができる。さらに、非水系電解液は、ラジカル補足剤、界面活性剤及び難燃剤などを含んでいてもよい。
　［電池の形状および構成］
　本実施形態に係るリチウム二次電池の形状は、円筒型、積層型など、種々の形状とすることができる。いずれの形状を採る場合であっても、セパレータを介して正極及び負極を積層させ、電極体とし、この電極体に上記非水電解液を含浸させる。正極集電体と外部に通ずる正極端子との間、並びに負極集電体と外部に通ずる負極端子との間に集電用リードなどを用いて接続する。以上の構成のものを電池ケースに密閉して電池を完成させることができる。
　以下、実施例及び比較例により本発明を説明するが、本発明は以下の実施例に限定されるものではない。なお、実施例及び比較例は、以下の装置及び方法を用いた測定結果により評価した。
　［粒子全体組成］
　母材として用いたリチウムニッケル複合酸化物の粉末を硝酸で溶解した後、ＩＣＰ発光分光分析装置（株式会社島津製作所製、ＩＣＰＳ－８１００）により、各成分の組成比を測定した。また、得られた正極活物質を上記と同様の方法で測定した。
　［粒子表面組成］
　得られた正極活物質をＸ線光電子分光装置（アルバック・ファイ株式会社製、Ｖｅｒｓａ　ＰｒｏｂｅＩＩ）を用いて測定した。この際、Ｘ線源として、単色化したＡｌ－Ｋα線（１４８６．７ｅＶ）を使用し、傾斜角（ｔｉｌｔ　ａｎｇｌｅ）を４５°、パスエナジーを１８７．８５ｅＶ、真空度を１０－７Ｐａとした。
　［水酸化リチウム含有量］
　得られた正極活物質粉末１０ｇに超純水を１００ｍｌ添加して５分間攪拌し、ろ過した後、ろ液を１ｍｏｌ／リットルの塩酸で滴定し第二中和点まで測定した。塩酸で中和されたアルカリ分の量を、水酸化リチウム（ＬｉＯＨ）および洗浄に用いたリチウム塩に由来するリチウム量（Ｌｉ）の合計量とした。そして、下記式に示すように、中和滴定で中和されたアルカリ分の量から、洗浄に用いたリチウム塩由来のＬｉ量を引いた量を、水酸化リチウム（ＬｉＯＨ）由来のＬｉ量とした。なお、洗浄に用いたリチウム塩に由来するリチウム（Ｌｉ）量は、下記の方法でそれぞれ求めたリチウム塩含有量から算出した。
（水酸化リチウム由来のＬｉ量）＝（塩酸で中和されたアルカリ分の量）－（洗浄に用いたリチウム塩由来のＬｉ量）・・・（式）
　上記式により算出した水酸化リチウム（ＬｉＯＨ）由来のＬｉ量をＬｉＯＨ量に換算することにより、水酸化リチウム含有量とした。
（炭酸リチウム、クエン酸リチウム及び／または酢酸リチウム）
　これらのリチウム塩含有量は、炭素硫黄分析装置（ＬＥＣＯ社製ＣＳ－６００）で全炭素元素（Ｃ）含有量を測定し、この測定された全炭素元素の量をそれぞれのリチウム塩に換算することにより求めた。
（硫酸リチウム）
　硫酸リチウム含有量は、ＩＣＰ発光分析により硫黄元素（Ｓ）含有量を測定し、この測定された硫黄元素（Ｓ）含有量を硫酸リチウムに換算することにより求めた。
（硝酸リチウム）
　硝酸リチウム含有量は、正極活物質粉末を超純水中で撹拌して硝酸リチウムを溶出させた後、ろ過し、ろ液をイオンクロマトグラフィー法により硝酸根含有量を測定し、この測定された硝酸根含有量を硝酸根リチウムに換算することにより求めた。
　［粉末ｐＨ］
　得られた正極活物質粉末５．０ｇを１００ｍｌの蒸留水に分散させた５質量％の懸濁液を作製し、２５℃室温で３０分間攪拌した懸濁液のｐＨ値を測定した。
　［ペーストのゲル化の判定］
　得られた正極活物質２０ｇに対して、ＰＶＤＦ（呉羽化学工業製、型番ＫＦポリマー＃１１００）２．２ｇと、ＮＭＰ（関東化学製）９．６ｍｌと容器に入れ、ニーダ（日本精機製作所、製品名ノンバブリングニーダ、型番ＮＢＫ－１）で２０００ｒｐｍの回転速度で１０分間十分に混合しペーストを作製した。得られたペーストをガラス瓶に移し、密栓した後、温度２５℃、露点－４０℃のドライボックス中に保管し、２４時間放置後のペーストの流動性を観察した。２４時間放置後、ペーストの流動性に変化のないものを◎、ペーストの流動性はあるが、流動性が変化したものを○、ゲル化したものを×と評価した。
　［電池特性の評価］
（１）評価用コイン電池の作製
　得られた正極活物質７０質量％に、アセチレンブラック２０質量％及びＰＴＦＥ１０質量％を混合し、ここから１５０ｍｇを取り出してペレットを作製し、正極とした。負極としてリチウム金属を用い、電解液として、１ＭのＬｉＣｌＯ４を支持塩とするエチレンカーボネート（ＥＣ）とジエチルカーボネート（ＤＥＣ）の等量混合溶液（富山薬品工業製）を用い、露点が－８０℃に管理されたＡｒ雰囲気のグローブボックス中で、図１に示すような２０３２型のコイン型電池を作製した。２０３２型の評価用コイン型電池ＢＡは、負極にリチウム金属負極１と、電解液を含浸させたセパレータ２と、正極３と、ガスケット４と、負極缶５と、正極缶６と、集電体７とを備える。
（２）放電容量
　作製したコイン型電池ＢＡを２４時間程度放置し、開路電圧ＯＣＶ（ｏｐｅｎ　ｃｉｒｃｕｉｔ　ｖｏｌｔａｇｅ）が安定した後、正極に対する電流密度を０．５ｍＡ／ｃｍ２としてカットオフ電圧４．３Ｖまで充電して充電容量とし、１時間の休止後カットオフ電圧３．０Ｖまで放電したときの容量を放電容量として評価した。
（３）正極抵抗
　作製したコイン型電池ＢＡを充電電位４．１Ｖで充電して、周波数応答アナライザおよびポテンショガルバノスタット（ソーラトロン製、１２５５Ｂ）を使用して交流インピーダンス法により測定した。図３上段は、得られたナイキストプロットを示す。このナイキストプロットは、溶液抵抗、負極抵抗とその容量、および、正極抵抗とその容量を示す特性曲線の和として表しているため、このナイキストプロットに基づき図３下段に示す等価回路を用いてフィッティング計算を行い、正極抵抗の値を算出した。正極抵抗は実施例１を１００とした相対値を評価値とした。
（実施例１）
　ニッケルを主成分とする酸化物粉末と水酸化リチウムを混合して焼成する公知技術で得られた、Ｌｉ１．０３Ｎｉ０．８８Ｃｏ０．０９Ａｌ０．０３Ｏ２で表されるリチウムニッケル複合酸化物の焼成粉末を得た。この粉末を母材として用いた。この粉末の平均粒径は１２．０μｍであり、比表面積は１．２ｍ２／ｇであった。なお、平均粒径はレーザ回折式粒度分布計（日機装株式会社製、マイクロトラック）用いて測定し、比表面積は比表面積測定装置（ユアサアイオニクス株式会社製、カンタソーブＱＳ－１０）を用いて、窒素ガス吸着によるＢＥＴ法を用いて評価した。
　上記リチウムニッケル複合酸化物粉末（母材）に、リチウム量が１．５ｇ／Ｌとなるように調製した炭酸リチウム水溶液を加えて、スラリー濃度を７５０ｇ／Ｌとした。このスラリーを３０分間攪拌して洗浄した後、濾過して取り出した粉末を、真空雰囲気下で、温度２１０℃で１４時間保持しながら乾燥して、リチウムニッケル複合酸化物からなる正極活物質を得た。得られた正極活物質をＩＣＰ発光分光分析装置で測定したところ、Ｌｉの原子比ｚは、０．９９２であった。
（実施例２）
　実施例２では、炭酸リチウム水溶液の濃度をリチウム量が０．３ｇ／Ｌとなるように調製した以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例３）
　実施例３では、炭酸リチウム水溶液の濃度をリチウム量が０．７ｇ／Ｌとなるように調製した以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例４）
　実施例４では、炭酸リチウム水溶液の濃度をリチウム量が１．０ｇ／Ｌとなるように調製した以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例５）
　実施例５では、炭酸リチウム水溶液の濃度をリチウム量が２．５ｇ／Ｌとなるように調製した以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例６）
　実施例６では、炭酸リチウム水溶液の濃度をリチウム量が３．０ｇ／Ｌとなるように調製した以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例７）
　実施例７では、スラリーの濃度を１００ｇ／Ｌとなるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例８）
　実施例８では、スラリーの濃度を３７５ｇ／Ｌとなるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例９）
　実施例９では、スラリーの濃度を１５００ｇ／Ｌとなるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例１０）
　実施例１０では、スラリーの濃度を３０００ｇ／Ｌとなるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例１１）
　実施例１１では、炭酸リチウム水溶液をクエン酸リチウム水溶液となるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例１２）
　実施例１２では、炭酸リチウム水溶液を酢酸リチウム水溶液となるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例１３）
　実施例１３では、炭酸リチウム水溶液を硝酸リチウム水溶液となるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（実施例１４）
　実施例１４では、炭酸リチウム水溶液を硫酸リチウム水溶液となるようにした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（比較例１）
　比較例１では、炭酸リチウム水溶液で洗浄する工程を行わなかったこと以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（比較例２）
　比較例２では、炭酸リチウム水溶液の代わりに純水を用いた以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（比較例３）
　比較例３では、炭酸リチウム水溶液の代わりに純水を用い、スラリー濃度を３７５ｇ／Ｌとした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（比較例４）
　比較例４では、炭酸リチウム水溶液の代わりに純水を用い、スラリー濃度を３０００ｇ／Ｌとした以外は、実施例１と同様にして正極活物質を得るとともに評価した。
（比較例５）
　比較例５では、炭酸リチウム水溶液の代わりに水酸化リチウム水溶液を用いた以外は、実施例１と同様にして正極活物質を得るとともに評価した。
Figure JPOXMLDOC01-appb-T000001
（評価）
　実施例および、比較例で得られた正極活物質の製造条件及び評価結果を表１に示す。
　表１から明らかなように、実施例１～１４により得られた正極活物質は、水酸化リチウム含有量が０．５質量％以下かつ、得られた正極活物質の粉末表面のＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が０．８０以上１．５以下である。また、得られた正極活物質は、ペースト混練時のゲル化が抑制されるとともに、放電容量が高く、正極抵抗が低いものであり、正極活物質として有用であることが分かる。
　一方、比較例１では、リチウム塩水溶液で洗浄する工程を行わなかったため、水酸化リチウム含有量が１．０６と高く、粉末表面のＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が６．２８と高い。また、得られた正極活物質は、ペースト混練時のゲル化が観察され、さらに放電容量が低く、実施例と比較して、電池性能に劣る。
　比較例２および３では、純水を用いて洗浄したため、粉末表面の組成比を表すＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が０．８０以下と低い。また、得られた正極活物質は、放電容量が低く、さらに正極抵抗が高くなり、実施例と比較して電池性能に劣る。
　比較例４では、純水を用いてスラリー濃度を３０００ｇ／Ｌで洗浄したため、水酸化リチウム含有量が０．５１と高く、粉末表面の組成比を表すＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が２．０１と高い。また、得られた正極活物質は、ペースト混練時のゲル化が観察され、実施例と比較して電池性能に劣る。
　比較例５では、水酸化リチウム水溶液を用いて洗浄したため、水酸化リチウム含有量が０．７８と高く、粉末表面の組成比を表すＬｉ／（Ｎｉ＋Ｃｏ＋Ｍ）が４．６９と高い。また、得られた正極活物質は、ペースト混練時にゲル化が観察され、さらに放電容量が低くなり、実施例と比較して電池性能に劣る。
　以上の結果より、本実施形態の製造方法を用いて、得られた正極活物質は、電池の正極材に用いられた場合に正極合材ペーストのゲル化を抑制でき、さらに電池の正極抵抗を低減して、高容量かつ出力特性に優れている。また、本実施形態の正極活物質は、非水系電解質二次電池の正極活物質として有用であることがわかる。
　本発明により得られる正極活物質を正極に含む非水系電解質二次電池は、常に高容量を要求される小型携帯電子機器（ノート型パソコンや携帯電話端末など）の電源に好適に用いられることができ、高出力が要求される電気自動車用電池にも好適に用いられることができる。
　また、本発明に係る非水系電解質二次電池は、優れた安全性を有し、小型化、高出力化が可能であることから、搭載スペースに制約を受ける電気自動車用電源として好適に用いられることができる。なお、本発明に係る非水系電解質二次電池は、純粋に電気エネルギーで駆動する電気自動車用の電源のみならず、ガソリンエンジンやディーゼルエンジンなどの燃焼機関と併用するいわゆるハイブリッド車用の電源としても用いることができる。
　また、法令で許容される限りにおいて、日本特許出願である特願２０１５－１６７５３０、及び上述の実施形態などで引用した全ての文献、の内容を援用して本文の記載の一部とする。
　ＢＡ・・・評価用コイン型電池
　１・・・リチウム金属負極
　２・・・セパレータ（電解液含浸）
　３・・・正極（評価用電極）
　４・・・ガスケット
　５・・・負極缶
　６・・・正極缶
　７・・・集電体
 

Claims (6)

  1. 　一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物からなる粉末を、水酸化リチウム以外の水溶性リチウム塩から選ばれる１種類以上のリチウム塩を含む水溶液により洗浄すること、および、洗浄後の前記粉末を乾燥すること、を含むことを特徴とする非水系電解質二次電池用正極活物質の製造方法。
  2. 　前記水溶液は、リチウム濃度が０．１ｇ／Ｌ以上５．０ｇ／Ｌ以下であることを特徴とする請求項１に記載の非水系電解質二次電池用正極活物質の製造方法。
  3. 　前記洗浄は、前記粉末を含む前記リチウム塩水溶液のスラリー濃度が１００ｇ／Ｌ以上３０００ｇ／Ｌ以下の状態で洗浄することを特徴とする請求項１又は２に記載の非水系電解質二次電池用正極活物質の製造方法。
  4. 　一般式ＬｉｚＮｉ１－ｘ－ｙＣｏｘＭｙＯ２（ただし、０≦ｘ≦０．３５、０≦ｙ≦０．１０、０．９５≦ｚ≦１．１０、Ｍは、Ｍｎ、Ｖ、Ｍｇ、Ｍｏ、Ｎｂ、ＴｉおよびＡｌから選ばれる少なくとも１種の元素）で表されるリチウムニッケル複合酸化物の粉末からなる非水系電解質二次電池用正極活物質であって、水酸化リチウム含有量が０．５質量％以下であり、かつ、Ｘ線光電子分光法により測定される前記粉末表面のＬｉとＬｉ以外の金属（Ｎｉ、Ｃｏ及びＭ）との組成比（Ｌｉ／（Ｎｉ＋Ｃｏ＋Ｍ））が０．８０以上１．５以下であることを特徴とする非水系電解質二次電池用正極活物質。
  5. 　前記粉末を水に分散させた５質量％の懸濁溶液における粉体ｐＨが１１．５以下である請求項４に記載の非水系電解質二次電池用正極活物質。
  6. 　請求項４または５に記載の非水系電解質二次電池用正極活物質を正極に含むことを特徴とする非水系電解質二次電池。
     
PCT/JP2016/074843 2015-08-27 2016-08-25 非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池 WO2017034001A1 (ja)