WO2006038490A1 - ガラス繊維被覆用塗布液およびそれを用いたゴム補強用ガラス繊維 - Google Patents

ガラス繊維被覆用塗布液およびそれを用いたゴム補強用ガラス繊維 Download PDF

Info

Publication number
WO2006038490A1
WO2006038490A1 PCT/JP2005/017725 JP2005017725W WO2006038490A1 WO 2006038490 A1 WO2006038490 A1 WO 2006038490A1 JP 2005017725 W JP2005017725 W JP 2005017725W WO 2006038490 A1 WO2006038490 A1 WO 2006038490A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass fiber
rubber
coating
weight
coating solution
Prior art date
Application number
PCT/JP2005/017725
Other languages
English (en)
French (fr)
Inventor
Toshiya Monden
Hiroyuki Hyakutake
Katsuhiko Ogaki
Original Assignee
Central Glass Company, Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2004290183A external-priority patent/JP4410648B2/ja
Priority claimed from JP2005254244A external-priority patent/JP4410739B2/ja
Priority claimed from JP2005254242A external-priority patent/JP4410738B2/ja
Priority claimed from JP2005254245A external-priority patent/JP4410740B2/ja
Priority claimed from JP2005254243A external-priority patent/JP4440190B2/ja
Application filed by Central Glass Company, Limited filed Critical Central Glass Company, Limited
Priority to PL05788382T priority Critical patent/PL1795645T3/pl
Priority to US11/664,114 priority patent/US8455097B2/en
Priority to CA 2581748 priority patent/CA2581748C/en
Priority to EP05788382.9A priority patent/EP1795645B1/en
Publication of WO2006038490A1 publication Critical patent/WO2006038490A1/ja
Priority to US13/790,928 priority patent/US9091325B2/en

Abstract

フェノール樹脂とビニルピリジン－スチレン－ブタジエン共重合体（Ｂ）とクロロスルホン化ポリエチレン（Ｃ）とを水に分散させエマルジョンとしたガラス繊維コードに被覆するためのガラス繊維被覆用塗布液が開示されている。この塗布液は、前記フェノール樹脂が、モノヒドロキシベンゼン（Ｄ）とホルムアルデヒド（Ｅ）を反応させてなるモノヒドロキシベンゼン－ホルムアルデヒド樹脂（Ａ）であることを特徴とする。

Description

明 細 書
ガラス繊維被覆用塗布液およびそれを用レ、たゴム補強用ガラス繊維 技術分野
[0001] 本発明は、各種ゴム製品の補強用に用いるガラス繊維と母材ゴムとの接着を高める ための被覆層を設けるためのガラス繊維被覆用塗布液およびそれを用 Vヽたゴム補強 用ガラス繊維に関する。
発明の背景
[0002] 伝動ベルト、タイヤ等のゴム製品に引っ張り強さおよび寸法安定性を付与するため に、ガラス繊維、ナイロン繊維およびポリエステル繊維等の強度の高い繊維を母材ゴ ムに補強材として埋設することは一般的に行われ、母材ゴムに埋設するゴム補強用 繊維には、母材であるゴムとの密着性がよぐ界面が強固で剥離しないことが必要と される。し力しながら、ガラス繊維をそのまま使用しても全く密着しないか、密着したと しても密着性が弱く界面が剥離してしま 、補強材としての要をなさな 、。
[0003] そのため、例えば、伝動ベルトには、母材ゴムとガラス繊維の密着性を向上させ、界 面の剥離を防止するために、通常、フィラメントをより合わせてヤーンとしたガラス繊維 コード'、に、レゾルシン一ホルムアルデヒド榭脂と各種ラテックスとを水に分散させたガ ラス繊維被覆用塗布液を塗布した後、乾燥させ被覆層としたゴム補強用ガラス繊維 が用いられる。該被覆層は、高温下で、ゴム補強用ガラス繊維を母材ゴムに埋め込 んで伝動ベルトに成形する際、母材ゴムとガラス繊維とを接着させる効果を有するが 、接着力、即ち、接着強さは必ずしも十分な強さではない。例えば、自動車用伝動べ ルトはエンジンル―ム内の高温の環境下で使用されるため、母材ゴムには、耐熱ゴム である水素化-トリルゴム（以下、 HNBRと略する）等が用いられる。前記被覆処理の みを行ったゴム補強用ガラス繊維を埋設した伝動ベルトは、高温下にお ヽて屈曲し 続ける走行状況下において、初期の接着強さが持続されず、長時間の走行におい ては、ゴム補強用ガラス繊維と母材ゴムとの界面の剥離をきたすこともある。
[0004] 架橋された HNBRとゴム補強用ガラス繊維との接着強さを持続し界面の剥離をきた さず、高温の環境下の走行にぉ 、ても長期信頼性のある伝動ベルトを提供するため のゴム補強ガラス繊維として、ガラス繊維コードに上述の被覆処理を行った後に得ら れた被覆を 1次被覆層として、該 2次被覆層上に異なる組成の第 2液を塗布し乾燥さ せて 2次被覆層としたゴム補強用ガラス繊維が特許文献 1〜6に開示されている。
[0005] 例えば、特許文献 1にお 、て、ハロゲン含有ポリマーとイソシァネートを含む第 2液 で処理する方法が開示されて!、る。
[0006] また、特許文献 2には、ゴム補強用ガラス繊維に、レゾルシン—ホルマリン縮合物と ゴムラテックスを含む処理剤を塗布し乾燥硬化させ第 1被覆層とし、当該第 1被覆層 上にさらに異なる処理剤を塗布し乾燥硬化させ形成させた第 2被覆層を有するゴム 補強用ガラス繊維コードであって、当該第 2被覆層用の処理剤が、ゴム配合物、加硫 剤およびマレイミド系加硫助剤を主成分とすることを特徴とするゴム補強用コードが 開示されている。
[0007] また、特許文献 3には、ゴム補強用繊維に、レゾルシン'ホルマリン縮合物とゴムラテ ッタスとを含む処理剤を塗布し乾燥硬化させ第 1被覆層とし、当該第 1被覆層上にさ らに異なる処理剤を塗布し乾燥硬化させ形成させた第 2被覆層を有するゴム補強用 繊維コードにおいて、当該第 2被覆層用の処理剤力 ゴム配合物、加硫剤およびジメ タクリレート系加硫助剤を主成分とすることを特徴とするゴム補強用コードが開示され 、ゴム配合物に水素化-トリルゴムとメタクリル酸亜鉛を分散させた水素化-トリルゴ ムとからなる混合ゴムの溶解物が使用される。
[0008] また、特許文献 4には、ゴムラテックス、レゾルシン ホルムアルデヒド水溶性縮合 物及びトリアジンチオールを含有するゴム補強用繊維処理剤が開示されている。
[0009] また、本出願人の特許出願に関わる特許文献 5には、ガラス繊維にアクリル酸エス テル系榭脂とビュルピリジン スチレン ブタジエン共重合体とレゾルシン ホルム アルデヒド榭脂とを水に分散させェマルジヨンとしたガラス繊維被覆用塗布液を塗布 した後、乾燥させてなる被覆層を設け、ハロゲン含有ポリマーの重量に対して 0. 3重 量％〜10. 0重量％のビスァリルナジイミドとを有機溶剤に分散させたガラス繊維被 覆用塗布液を塗布し、更なる被覆層を設けてなることを特徴とするゴム補強用ガラス 繊維が開示されている。該ゴム補強用ガラス繊維は、 HNBRとの接着において、好ま しい接着強さを示した。 [0010] また、本出願人の特許出願に関わる特許文献 6には、レゾルシン ホルムアルデヒ ド榭脂とゴムラテックスとを水に分散させてなるガラス繊維被覆用第 1液をガラス繊維 に塗布し塗膜を形成した後に乾燥硬化させ 1次被覆層とした後で、該 1次被覆層上 に異なる組成のガラス繊維被覆用第 2液を塗布し塗膜を形成した後に乾燥硬化させ て 2次被覆層としたゴム補強用ガラス繊維にぉ 、て、ガラス繊維被覆用第 2液がビス ァリルナジイミドとゴムエラストマ一と加硫剤と無機充填材とを有機溶剤に分散させて なることを特徴とするゴム補強用ガラス繊維が記載されて 、る。該ゴム補強用ガラス 繊維は、 HNBRとの接着において、好ましい接着強さを示し、 HNBRに埋設し伝動 ベルトとして、高温下、長時間走行後も、引張り強さの低下がなく優れた耐熱性を有 するものであった。
[0011] このように、従来の耐熱性の伝動ベルトは、レゾルシン ホルムアルデヒド榭脂、ビ -ルピリジン スチレン ブタジエン共重合体、クロロスルホン化ポリエチレンからな るガラス繊維被覆用塗布液を用いガラス繊維コードに塗布乾燥させたゴム補強用ガ ラス繊維を耐熱ゴムとしての HNBRに埋設し作製された。また、該ゴム補強用ガラス 繊維に更なる 2次被覆層を設け耐熱ゴムとしての HNBRに埋設し作製された。 特許文献 1 :特公平 2— 4715号公報
特許文献 2：特許第 3201330号公報
特許文献 3 :特許第 3201331号公報
特許文献 4：特開平 10— 25665号公報
特許文献 5：特開 2004 - 203730号公報
特許文献 6：特開 2004 - 244785号公報
発明の概要
[0012] 伝動ベルトを製造する際に母材ゴムに埋設して使用するゴム補強用ガラス繊維には 、母材ゴムとの接着性を改善するための被覆材がガラス繊維コードに塗布被覆され たものが用いられる。
[0013] 従来の伝動ベルトにおいて、ガラス繊維コードに被覆材を塗布したゴム補強用ガラス 繊維と母材ゴムとの初期の接着強さは得られたが、伝動ベルトとしての多湿高温下で 長時間走行させた後において、走行前の引っ張り強度を持続し、寸法変化のない優 れた耐水性および耐熱性を併せ持つものがなぐ特に耐水性が劣って 、ると言う問 題があった。
[0014] 特に、自動車用伝動ベルトには、エンジンの熱に対する耐熱性と雨天走行における 耐水性が必要であり、高温下および多湿下での長時間の走行後において、引っ張り 強さを持続し寸法安定性に優れていること、即ち、耐熱性、耐水性が要求される。
[0015] 特許文献 1〜6に記載されているゴム補強用ガラス繊維を耐熱ゴムの中に埋設して なる従来の伝動ベルトに比較して、同等以上のゴム補強用ガラス繊維と耐熱ベルトの 接着強さを有し、高温下において長時間走行させても被覆層が初期の接着強さを持 続する耐熱性に加え、伝動ベルトに水をかけつつ長時間走行させても被覆層が初期 の接着強さを持続するとともに、ガラス繊維コードへの水の浸透を防ぐことで耐水性を 併せ持つ伝動ベルトおよびそれを与えるゴム補強用ガラス繊維の開発が待たれてい る。
[0016] 本発明者らが鋭意検討した結果、ビュルピリジン—スチレン—ブタジエン共重合体 とクロロスルホン化ポリエチレンに、モノヒドロキシベンゼンにホルムアルデヒドを反応 させてなるモノヒドロキシベンゼン一ホルムアルデヒド榭脂をカ卩えてガラス繊維被覆用 塗布液とし、ガラス繊維被覆用塗布液をガラス繊維コードに塗布した後に乾燥させて 被覆層とし、その上に更なる 2次被覆層を設けゴム補強用ガラス繊維とすると、 HNB Rに埋設し伝動ベルトとした際に、ゴム補強用ガラス繊維と耐熱ゴムの好ま 、接着 強さを得、伝動ベルトに優れた耐水性および耐熱性を併せ持たせる、言い換えれば 、高温下および注水下の長時間の走行後も引っ張り強さを維持し、伝動ベルトに優 れた寸法安定性を与えるゴム補強用ガラス繊維が提供されることが判った。
[0017] 即ち、本発明は、フエノール榭脂とビュルピリジン一スチレン一ブタジエン共重合体（ B)とクロロスルホン化ポリエチレン（C)とを水に分散させェマルジヨンとしたガラス繊 維コードに被覆するためのガラス繊維被覆用塗布液であって、前記フエノール榭脂 1S モノヒドロキシベンゼン（D)とホルムアルデヒド（E)を反応させてなるモノヒドロキシ ベンゼン一ホルムアルデヒド榭脂 (A)であることを特徴とするガラス繊維被覆用塗布 液を提供する。
図面の簡単な説明 [0018] [図 1]ゴム補強用ガラス繊維を耐熱ゴムに埋設させて作製した伝動ベルトを切断した 際の斜視図である。
[図 2]伝動ベルトの耐水走行疲労性能試験機の概略側面図である。
[図 3]伝動ベルトの耐熱耐屈曲走行疲労性能試験機の概略側面図である。
詳細な説明
[0019] 本発明によるガラス繊維被覆用塗布液を塗布しガラス繊維コードに被覆層を設け てなるゴム補強用ガラス繊維は、耐熱ゴムである、例えば、硫黄により、または過酸化 物により架橋された HNBRへ埋設した際に、ガラス繊維と架橋された HNBRとに優 れた接着強さを有する。更に、架橋された HNBRへ埋設して伝動ベルトとした際に耐 水性を与えたことで、耐水性および耐熱性を併せ持たせ、高温多湿下における伝動 ベルトとしての長時間の使用後、言い換えれば、走行後において、ガラス繊維と耐熱 ゴムの界面が剥離する懸念がなく該伝動ベルトは引っ張り強さを維持し寸法安定性 に優れる。
[0020] 本発明は、フエノール榭脂に属するモノヒドロキシベンゼン ホルムアルデヒド榭脂
(A)とビュルピリジン スチレン ブタジエン共重合体（B)とクロロスルホン化ポリエ チレン (C)とを水に分散させたガラス繊維被覆用塗布液であり、該塗布液をガラス繊 維コードに塗布後、乾燥させて、ガラス繊維コードへの水の浸透を防ぐ働きを有する と考えられる被覆層を設けた後、別のガラス繊維 2次被覆用塗布液を塗布し乾燥させ て更なる 2次被覆層を設け乾燥させてなるゴム補強用ガラス繊維を提供する。
[0021] 本発明のゴム補強用ガラス繊維は、従来のゴム補強用ガラス繊維に比較して、耐熱 ゴム、例えば架橋された HNBRに埋設して伝動ベルトとした際に、ガラス繊維コード への水の浸透を防ぐことで伝動ベルトに優れた耐水性を与え、耐水性および耐熱性 を併せ持たせる。
[0022] 本発明にお ヽて、ガラス繊維コードに塗布し被覆層を形成するガラス繊維被覆用 塗布液には、モノヒドロキシベンゼン—ホルムアルデヒド榭脂（A)とビュルピリジン— スチレン ブタジエン共重合体 (B)とクロロスルホンィ匕ポリエチレン (C)とを水に分散 させたガラス繊維被覆用塗布液を用 ヽる。
[0023] 尚、本発明において、伝動ベルトとは、エンジン、その他機械を運転するために、ェ ンジン、モーター等の駆動源の駆動力を伝えるベルトのことであり、かみ合い伝動で 駆動力を伝える歯付きベルト、摩擦伝動で駆動力を伝える Vベルトが挙げられる。 自 動車用伝動ベルトとは自動車のエンジンルーム内で用いられる耐熱性の前記伝動 ベルトのことである。タイミングベルトとは、前記自動車用伝動ベルトの中で、カムシャ フトを有するエンジンにおいて、クランクシャフトの回転をタイミングギヤに伝え力ムシ ャフト駆動させバルブの開閉を設定されたタイミングで行うための、プーリーの歯とか み合う歯を設けた歯付きベルトのことである。
[0024] 本発明のガラス繊維被覆用塗布液に用いる前記モノヒドロキシベンゼン一ホルムァ ルデヒド榭脂 (A)としては、モノヒドロキシベンゼン（D)に対するホルムアルデヒド (E) のモル比が 0. 5以上、 3. 0以下、即ち、 EZD=0. 5〜3. 0で、塩基性の触媒で反 応させた水溶性もしくは水溶媒レゾール型榭脂が挙げられる。ホルムアルデヒド (E) のモル比が 0. 5未満では、ゴム補強用ガラス繊維と耐熱ゴムとの接着強さに劣り、 3. 0を越えるとガラス繊維被覆用塗布液が、ゲル化し易い。好ましくは、 0. 3〜1. 2の範 囲である。
[0025] 本発明のガラス繊維被覆用塗布液に使用されるモノヒドロキシベンゼン一ホルムァ ルデヒド榭脂 (A)として、例えば、工業用フエノール榭脂として市販されている群栄化 学工業株式会社制、商品名、レジトップ、型番 PL— 4667が挙げられる。
[0026] 尚、前記塩基性の触媒としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム 、水酸化マグネシウム、水酸ィ匕カルシウムおよび水酸化バリウム等が挙げられる。
[0027] 本発明のガラス繊維被覆用塗布液の組成物として用いるビュルピリジン スチレン ブタジエン共重合体（B)には、ビュルピリジン:スチレン：ブタジエンの比力 重量 比で 10〜20： 10〜20： 80〜60の範囲で重合させてなるビュルピリジン スチレン —ブタジエン共重合体 (B)を用いることが好ましぐ市販の日本エイアンドエル株式 会社製、商品名、ビラテクス、 JSR株式会社製、商品名、 0650、および日本ゼオン株 式会社製、商品名、 Nipol、型番、 1218FS等が挙げられる。尚、前記重量比を外れ たビュルピリジン スチレン ブタジエン共重合体 (B)を用いたガラス繊維被覆用塗 布液を使用した後、塗布後乾燥させてガラス繊維コードに被覆を施し作製したゴム補 強用ガラス繊維は、母材ゴムとの接着強さに劣る。 [0028] 本発明のガラス繊維被覆用塗布液の組成物として用いるクロロスルホンィ匕ポリェチ レン (C)は、重量百分率で表して、塩素含有量が 20. 0%〜40. 0%、スルホン基中 の硫黄含有量が 0. 5%〜2. 0%のものが好適に用いられ、例えば、固形分約 40重 量％のラテックスとして、住友精化株式会社製、商品名、 CSM— 450が市販されて おり、本発明のガラス繊維被覆用塗布液に使用される。尚、前述の塩素含有量及び スルホン基中の硫黄含有量を外れたクロロスルホンィ匕ポリエチレン (C)を用いたガラ ス繊維被覆用塗布液を使用し、ガラス繊維コードに被覆を施し作製したゴム補強用 ガラス繊維は、母材である架橋された HNBRとの接着性に劣る。
[0029] 伝動ベルトに使用した際のゴム補強用ガラス繊維と母材ゴムに、所望の接着強さを 得るには、ガラス繊維被覆用塗布液に含まれるモノヒドロキシベンゼン ホルムアル デヒド榭脂（A)とビニルピリジン一スチレン一ブタジエン共重合体 (B)とクロロスルホ ン化ポリエチレン (C)とを合わせた重量を 100%基準として、重量百分率で表して、 モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)が 1. 0%以上、 15. 0%以下、即 ち、 AZ (A+B + C) = 1. 0%〜15. 0%、ビニノレピリジン一スチレン一ブタジエン共 重合体 (B)が 45. 0%以上、 82. 0%以下、即ち、 BZ (A+B + C) =45. 0%〜82 . 0%、クロロスルホンィ匕ポリエチレン (C)が 3. 0%以上、 40. 0%以下、即ち、 CZ ( A+B+C) =3. 0%〜40. 0%の範囲で含まれることが好ましい。
[0030] ガラス繊維被覆用塗布液中の、モノヒドロキシベンゼン ホルムアルデヒド榭脂 (A) の含有が 1. 0%より少ないと、ガラス繊維コードの被覆材とした際に、ガラス繊維と母 材ゴムの接着強さが弱くなり、伝動ベルトにした際に好ましい耐水性、耐熱性が得難 い。モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)の含有が 15. 0%を超えると 、ガラス繊維被覆用塗布液が凝集沈殿を起こし易く使用不能となる。よって、本発明 のガラス繊維被覆用塗布液における好適なモノヒドロキシベンゼン一ホルムアルデヒ ド榭脂 (A)の含有範囲は、ガラス繊維被覆用塗布液に含まれるビュルピリジン一スチ レン ブタジエン共重合体（B)とクロロスルホン化ポリエチレン（C)を合わせた重量を 100%基準として、 AZ (A+B + C) = 1. 0%〜15. 0%の範囲である。更に、好まし くは、が AZ (A+B + C) =2. 0%〜10. 0%の範囲である。
[0031] また、ガラス繊維被覆用塗布液中の、ビュルピリジン一スチレン一ブタジエン共重 合体 (B)の含有が 45. 0%より少ないと、ガラス繊維と架橋された HNBRとの接着強 さが弱くなり、伝動ベルトにした際に好ましい耐熱性が得難い。ビュルピリジンースチ レン ブタジエン共重合体 (B)の含有が 82. 0%を超えると、ガラス繊維コードの被 覆とした際に、被覆に粘着性が生じ被覆層が転写し易くなり、工程が汚れる等の不具 合が生じる。よって、本発明のガラス繊維被覆用塗布液におけるビュルピリジン—ス チレン ブタジエン共重合体 (B)の好適な含有範囲は、ガラス繊維被覆用塗布液に 含まれるモノヒドロキシベンゼン一ホルムアルデヒド榭脂（A)とビュルピリジン一スチレ ン—ブタジエン共重合体 (B)とクロロスルホン化ポリエチレン (C)とを合わせた重量を 100%基準として、 B/ (A+B + C) =45. 0%〜82. 0%の範囲である。更に、好ま しくは、 BZ (A+B + C) = 55. 0%〜75. 0%の範囲である。
[0032] 前記被覆層中のクロロスルホン化ポリエチレン（C) 1S 3. 0%より少ないと、伝動べ ルトにした際に所望の耐熱性が得難ぐクロロスルホン化ポリエチレン (C)が 40. 0% より多いと、ガラス繊維と母材ゴムの接着強さが弱くなり、伝動ベルトにした際に好まし い耐熱性が得難い。本発明のガラス繊維被覆用塗布液において、好適なクロロスル ホンィ匕ポリエチレン (C)の含有範囲は、ガラス繊維被覆用塗布液に含まれるモノヒド ロキシベンゼン ホルムアルデヒド榭脂（A)とビニルピリジン スチレン ブタジエン 共重合体 (B)とクロロスルホン化ポリエチレン (C)とを合わせた重量を 100%基準とし て、 CZ (A+B + C) = 3. 0%〜40. 0%の範囲である。更に、好ましくは、 C/ (A+ B + C) = 20. 0%〜35. 0%の範囲である。
[0033] 本発明のゴム補強用ガラス繊維に用いるガラス繊維被覆用塗布液の組成物の一つ であるビュルピリジン スチレン ブタジエン共重合体（B)の一部を、他のゴムエラス トマ一に替えても良い。ビュルピリジン スチレン ブタジエン共重合体のみでは、ゴ ム補強用ガラス繊維の被覆に粘着性が生じ被覆層が転写し易くなり、工程が汚れた りして作業性が悪くなる。他のゴムエラストマ一としてカルボキシル基変性スチレン— ブタジエンゴム、アクリロニトリル一ブタジエンゴム等も挙げられる力 ビュルピリジン一 スチレン ブタジエン共重合体（B)との相性が良!、スチレン ブタジエン共重合体（ F)が特に好適に使用され、本発明のゴム補強用ガラス繊維の特徴である母材ゴムと の接着性、および母材ゴムとしての耐熱ゴムに埋設し伝動ベルトとした際の耐熱性を 損なわない。
[0034] ビュルピリジン スチレン ブタジエン共重合体（B)の重量を 100%基準として、 重量0 /0で表して、スチレン ブタジエン共重合体（F)を、 FZB = 5. 0%〜80. 0% の範囲で、ビュルピリジン スチレン ブタジエン共重合体（B)に替えて使用できる 。 5. 0%未満では、ゴム補強用ガラス繊維の被覆に粘着性が生じ、被覆層が転写し 易くなることを抑制する効果がない。好ましくは、 25. 0%以上である。 80. 0%を超え ると、母材ゴムとの接着性および母材ゴムとしての耐熱ゴムに埋設し、伝動ベルトとし た際の耐熱性が失われる。好ましくは、 55. 0%以下である。
[0035] このようなスチレン ブタジエン共重合体（F)として、例えば、 日本エイアンドエル 株式会社から、商品名、 J— 9049が市販されており、本発明のゴム補強用ガラス繊維 の被覆層を形成するためのガラス繊維被覆用塗布液に使用される。
[0036] 本発明のガラス繊維被覆用塗布液には、老化防止剤、 pH調整剤、安定剤等を含 有させても良い。老化防止剤にはジフヱ-ルァミン系化合物、 pH調整剤にはアンモ ユアが挙げられる。
[0037] 本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて 1次被 覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けたゴム補強 用ガラス繊維の第 1の態様について説明する。
[0038] 本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて被覆 層としたゴム補強用ガラス繊維に、更にハロゲン含有ポリマー（G)とビスァリルナジィ ミド (H)とを有機溶剤に分散させたガラス繊維 2次被覆用塗布液を塗布し、 2次被覆 層を設けることが好ましい。該 2次被覆層を設け、種々の母材ゴム、特に架橋された HNBR等の耐熱ゴムに埋設し伝動ベルトとすると、ガラス繊維コードと母材ゴムの優 れた接着性が得られ、本発明のゴム補強用ガラス繊維は伝動ベルトの補強材として 有効に働く。更に、前記伝動ベルトは、高温多湿の環境下における長時間の使用に おいて、被覆層が初期の接着強さを持続し且つ寸法安定性に優れ、即ち、耐熱性 および耐水性に優れる。有機溶剤としては、例えば、キシレンが挙げられる。
[0039] 従来の伝動ベルトに比較して、モノヒドロキシベンゼン（D)をホルムアルデヒド（E)に 反応させたモノヒドロキシベンゼン一ホルムアルデヒド榭脂（A)、ビュルピリジン一ス チレン—ブタジエン共重合体 (B)、クロロスルホンィ匕ポリエチレン (C)からなる本発明 のガラス繊維被覆用塗布液を用い、ガラス繊維コードに塗布乾燥させた後、ハロゲン 含有ポリマー（G)と、ハロゲン含有ポリマー（G)を 100%基準として、ビスァリルナジ イミド (H)を、重量百分率で表して、 0. 3%以上、 10. 0%以下、即ち、 HZG = 0. 3 %〜10. 0%の範囲で加え、有機溶剤に分散させたガラス繊維 2次被覆用塗布液を 塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の重量を基準とするハロゲン含 有ポリマー（G)の含有量力 重量百分率で表して 10. 0%〜70. 0%となる本発明の ゴム補強用ガラス繊維を架橋された HNBRゴムに埋設し作製した伝動ベルトは、多 湿下および高温下おける長時間の走行後も、被覆層によるガラス繊維と架橋された HNBRの初期の接着強さが持続され、引っ張り強さを持続し寸法安定性に優れてお り、耐水性、耐熱性を併せ持つ。
[0040] 2次被覆層中のハロゲン含有ポリマーの含有力 10. 0%より少ないと、前述の優れ た耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接着強さが 弱くなり作製した伝動ベルトは耐久性に劣る。好ましくは、 25. 0%以上、 60. 0%以 下である。
[0041] その際、ガラス繊維 2次被覆層用塗布液中のビスァリルナジイミド (H)は、ハロゲン含 有ポリマー（G)の重量を 100%基準として、重量百分率で表して、 0. 3%以上、 10. 0%以下、即ち、 HZG = 0. 3%〜10. 0%であることが好ましい。ビスァリルナジイミ ド (H)の含有が、 0. 3%より少ないと、前述の優れた耐熱性が得難い。 10. 0%を超 えると、ガラス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルトは、耐 久性に劣る。更に、好ましくは、 H/G = 0. 3〜2. 0%の範囲である。
[0042] ビスァリルナジイミド (H)は熱硬化性イミド榭脂の一種であり、低分子量のビスァリル ナジイミド (H)は他の樹脂との相溶性に優れており、硬化後のビスァリルナジイミド榭 脂は、ガラス転移点が 300°C以上で、前記伝動ベルトの耐熱性を高める効果がある
[0043] ビスァリルナジイミド（H)としては、 N— N'—へキサメチレンジァリルナジイミド、 N— Ν'— (m—キシリレン）ジァリルナジイミド、または N— Ν'— (4、 4≡—ジフエ-ルメタ ン）ジァリルナジイミドが挙げられ、特に、 N— N'—へキサメチレンジァリルナジイミド が本発明に好適に用いられる。
[0044] ビスァリルナジイミドは、丸善石油化学株式会社より BANI— M、 BANI— H、 BANI —X等の商品名で市販され、本発明のゴム補強用ガラス繊維に好適に用いられる。
[0045] 次いで、本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させ て 1次被覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けた ゴム補強用ガラス繊維の第 2の態様について説明する。
[0046] 本発明のガラス繊維被覆用塗布液を塗布後、乾燥させて被覆層としたゴム補強用ガ ラス繊維に、更にハロゲン含有ポリマー（G)とメタクリル酸亜鉛 (I)とを有機溶剤に分 散させたガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けることが好ま ヽ。 該 2次被覆層を設け、種々の母材ゴム、特に架橋された HNBR等の耐熱ゴムに埋設 し伝動ベルトとすると、ガラス繊維コードと母材ゴムの優れた接着性が得られ、本発明 のゴム補強用ガラス繊維は伝動ベルトの補強材として有効に働く。更に、前記伝動べ ルトは、高温多湿の環境下における長時間の使用において、被覆層が初期の接着 強さを持続し且つ寸法安定性に優れ、即ち、耐熱性および耐水性に優れる。有機溶 剤としては、例えば、キシレンが挙げられる。
[0047] 従来の伝動ベルトに比較して、モノヒドロキシベンゼン（D)をホルムアルデヒド（E) に反応させたモノヒドロキシベンゼン ホルムアルデヒド榭脂（A)、ビニルピリジン スチレン ブタジエン共重合体（B)、クロロスルホン化ポリエチレン（C)からなる本発 明のガラス繊維被覆用塗布液を用い、ガラス繊維コードに塗布乾燥させた後、ハロゲ ン含有ポリマー（G)とメタクリル酸亜鉛 (I)と、ハロゲン含有ポリマー（G)を 100%基準 として、有機ジイソシァネートを C を、重量百分率で表して、 5. 0%以上、 50. 0%以 下、即ち、 JZG = 5. 0%〜50. 0%の範囲で加え、有機溶剤に分散させたガラス繊 維 2次被覆用塗布液を塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の重量を 基準とするハロゲン含有ポリマー（G)の含有量力 重量百分率で表して 10. 0%〜7 0. 0%となる本発明のゴム補強用ガラス繊維を架橋された HNBRゴムに埋設し作製 した伝動ベルトは、多湿下および高温下おける長時間の走行後も、被覆層によるガ ラス繊維と架橋された HNBRの初期の接着強さが持続され、引っ張り強さを持続し寸 法安定性に優れており、耐水性、耐熱性を併せ持つ。 [0048] 2次被覆層中のハロゲン含有ポリマーの含有力 10. 0%より少ないと、前述の優れ た耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接着強さが 弱くなり作製した伝動ベルトは耐久性に劣る。好ましくは、 25. 0%以上、 60. 0%以 下である。
[0049] ガラス繊維 2次被覆層用塗布液中の有機ジィオシァネート COが、ハロゲン含有ポリ マー（G)の重量を 100%基準として、重量百分率で表して、 5. 0%以上、 50. 0%以 下、即ち、 JZG = 5. 0%〜50. 0%であることが好ましい。有機ジイソィァネート (J) の含有が、 5. 0%より少ないと、前述の優れた耐熱性が得難い。 50. 0%を超えると、 ガラス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルトは、耐久性に 劣る。
[0050] 前記有機ジイソシァネート (J)としては、へキサメチレンジイソシァネート、イソホロン ジイソシァネート、メチレンビス（4—シクロへキシルイソシァネート）、トルエンジィソシ ァネート、キシレンジイソシァネート、ナフタレンジイソシァネートまたはメチレンビス（ フエ-ルイソシァネート）が挙げられ、特にメチレンビス（フエ-ルイソシァネート）、へ キサメチレンジイソシァネートが本発明に好適に用いられる。
[0051] 更に、上記のガラス繊維 2次被覆用塗布液において、ハロゲン含有ポリマー（G)と 有機ジイソシァネート (J)と、ハロゲン含有ポリマー（G)を 100%基準として、メタクリル 酸亜鉛 (I)を重量百分率で表して、 0. 001%以上、 3. 0%以下、即ち IZG = 0. 00 1%〜3. 0%のメタクリル酸亜鉛 (I)を有機溶剤に分散させたルことが好ましぐ更な る 2次被覆層を設けてなり、 2次被覆層の重量を基準とするハロゲン含有ポリマー（G )の含有量が、重量百分率で表して 10. 0%〜70. 0%となる本発明のゴム補強用ガ ラス繊維を架橋された HNBRゴムに埋設し作製した伝動ベルトは、多湿下および高 温下おける長時間の走行後も、被覆層によるガラス繊維と架橋された HNBRの初期 の接着強さが持続され、引っ張り強さを持続し寸法安定性に優れており、耐水性、耐 熱性を併せ持つ。
[0052] 2次被覆層中のハロゲン含有ポリマーの含有が、 10. 0%より少ないと、前述の優れ た耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接着強さが 弱くなり作製した伝動ベルトは耐久性に劣る。好ましくは、 25. 0%以上、 60. 0%以 下である。
[0053] ガラス繊維 2次被覆層用塗布液中のメタクリル酸亜鉛 (I)力 ハロゲン含有ポリマー（ G)の重量を 100%基準として、重量百分率で表して、 0. 001%以上、 3. 0%以下、 即ち、 JZG = 0. 001%〜3. 0%であることが好ましい。メタクリル酸亜鉛 (I)の含有 1S 0. 001%より少ないと、前述の優れた耐熱性が得難い。 3. 0%を超えると、ガラ ス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルトは、耐久性に劣る
[0054] 次いで、本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させ て 1次被覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けた ゴム補強用ガラス繊維の第 3の態様について説明する。
[0055] 本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて被覆層 としたゴム補強用ガラス繊維に、更にハロゲン含有ポリマー（G)とマレイミド (K)とを有 機溶剤に分散させたガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けること が好ましい。該 2次被覆層を設け、種々の母材ゴム、特に架橋された HNBR等の耐 熱ゴムに埋設し伝動ベルトとすると、ガラス繊維コードと母材ゴムの優れた接着性が 得られ、本発明のゴム補強用ガラス繊維は伝動ベルトの補強材として有効に働く。更 に、前記伝動ベルトは、高温多湿の環境下における長時間の使用において、被覆層 が初期の接着強さを持続し且つ寸法安定性に優れ、即ち、耐熱性および耐水性に 優れる。有機溶剤としては、例えば、キシレンが挙げられる。
[0056] 従来の伝動ベルトに比較して、モノヒドロキシベンゼン（D)をホルムアルデヒド（E) に反応させたモノヒドロキシベンゼン ホルムアルデヒド榭脂（A)、ビニルピリジン スチレン ブタジエン共重合体（B)、クロロスルホン化ポリエチレン（C)からなる本発 明のガラス繊維被覆用塗布液を用い、ガラス繊維コードに塗布乾燥させた後、ハロゲ ン含有ポリマー（G)と、ハロゲン含有ポリマー（G)とマレイミド (K)を加えた重量を 10 0%基準として、マレイミド (K)を、重量百分率で表して、 20. 0%以上、 90. 0%以下 、即ち、 K/ (G+K) = 20. 0%〜90. 0%の範囲で加え、有機溶剤に分散させたガ ラス繊維 2次被覆用塗布液を塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の 重量を基準とするハロゲン含有ポリマー（G)の含有量力 重量百分率で表して 10. 0 %〜70. 0%となる本発明のゴム補強用ガラス繊維を架橋された HNBRゴムに埋設 し作製した伝動ベルトは、多湿下および高温下おける長時間の走行後も、被覆層に よるガラス繊維と架橋された HNBRの初期の接着強さが持続され、引っ張り強さを持 続し寸法安定性に優れており、耐水性、耐熱性を併せ持つ。
[0057] 2次被覆層中のハロゲン含有ポリマーの含有力 10. 0%より少ないと、前述の優れ た耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接着強さが 弱くなり作製した伝動ベルトは耐久性に劣る。好ましくは、 25. 0%以上、 60. 0%以 下である。
[0058] ガラス繊維 2次被覆層用塗布液中のマレイミド (K)が、ハロゲン含有ポリマー（G)と マレイミド (K)をカ卩えた重量の重量を 100%基準として、重量百分率で表して、 20. 0 %以上、 90. 0%以下、即ち、 JZG = 20. 0%〜90. 0%であることが好ましい。マレ イミド (K)の含有が、 20. 0%より少ないと、前述の優れた耐熱性が得難い。 90. 0% を超えると、ガラス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルト は、耐久性に劣る。
[0059] 前記、マレイミド（K)としては、 N、 N—m—フエ-レンジマレイミド、 4、 4'—ジフエ- ルメタンビスマレイミド、ポリフエ-ルメタンマレイミド、 m—フエ-レンビスマレイミド、 4 —メチルー 1、 3—フエ-レンビスマレイミド、 4、 4'—ジフエ-ルエーテルビスマレイミ ド、 4、 4'ージフエニノレスノレホンビスマレイミド、クロ口フエ二ノレマレイミド、メチルフエ二 ルマレイミド、ヒドロキシフエ-ルマレイミド、カルボキシフエ-ルマレイミド、ドデシルマ レイミド、シクロへキシルマレイミドが挙げられる。望ましくは、 N、 N—m—フエ-レン ジマレイミドが挙げられる
[0060] 次いで、本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させ て 1次被覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けた ゴム補強用ガラス繊維の第 4の態様について説明する。
[0061] 本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて被覆 層としたゴム補強用ガラス繊維に、更にハロゲン含有ポリマー（G)と加硫剤 (L)とトリ アジン系化合物 (M)と無機充填剤 (N)とを有機溶剤に分散させたガラス繊維 2次被 覆用塗布液を塗布し、 2次被覆層を設けることが好ましい。該 2次被覆層を設け、種 々の母材ゴム、特に架橋された HNBR等の耐熱ゴムに埋設し伝動ベルトとすると、ガ ラス繊維コードと母材ゴムの優れた接着性が得られ、本発明のゴム補強用ガラス繊維 は伝動ベルトの補強材として有効に働く。更に、前記伝動ベルトは、高温多湿の環境 下における長時間の使用において、被覆層が初期の接着強さを持続し且つ寸法安 定性に優れ、即ち、耐熱性および耐水性に優れる。有機溶剤としては、例えば、キシ レンが挙げられる。
[0062] 従来の伝動ベルトに比較して、モノヒドロキシベンゼン（D)をホルムアルデヒド（E)に 反応させたモノヒドロキシベンゼン一ホルムアルデヒド榭脂（A)、ビュルピリジン一ス チレン—ブタジエン共重合体 (B)、クロロスルホンィ匕ポリエチレン (C)からなる本発明 のガラス繊維被覆用塗布液を用い、ガラス繊維コードに塗布乾燥させた後、ハロゲン 含有ポリマー（G)を 100%基準として、ハロゲン含有ポリマー（G)の重量に対して、 重量百分率で表して、トリアジン系化合物を、 MZG = 0. 3%〜10. 0%の範囲で加 え、有機溶剤に分散させたガラス繊維 2次被覆用塗布液を塗布し、更なる 2次被覆層 を設けなり、 2次被覆層の重量を基準とするハロゲン含有ポリマー (G)の含有量が、 重量百分率で表して 10. 0%〜70. 0%となる本発明のゴム補強用ガラス繊維を架 橋された HNBRゴムに埋設し作製した伝動ベルトは、多湿下および高温下おける長 時間の走行後も、被覆層によるガラス繊維と架橋された HNBRの初期の接着強さが 持続され、引っ張り強さを持続し寸法安定性に優れており、耐水性、耐熱性を併せ持 つ。
[0063] 2次被覆層中のハロゲン含有ポリマーの含有力 10. 0%より少ないと、前述の優れ た耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接着強さが 弱くなり作製した伝動ベルトは耐久性に劣る。好ましくは、 25. 0%以上、 60. 0%以 下である。
[0064] その際、ガラス繊維 2次被覆層用塗布液中のトリアジン系化合物（M)は、ハロゲン 含有ポリマー（G)の重量を 100%基準として、重量百分率で表して、 0. 3%以上、 1 0. 0%以下、即ち、 MZG = 0. 3%〜10. 0%であることが好ましい。トリアジンィ匕合 物 (L)の含有が、 0. 3%より少ないと、前述の優れた耐熱性が得難い。 10. 0%を超 えると、ガラス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルトは、耐 久性に劣る。
[0065] 前記、トリアジン系化合物（M)としては、トリァリルシアヌレートまたはトリアリルイソシァ ヌレートが挙げられる。
[0066] また、本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて 1 次被覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けたゴム 補強用ガラス繊維ゴム補強用ガラス繊維の前記第 1〜第 4の態様におけるガラス繊 維 2次被覆用塗布液中に加硫剤 (L)を加えることが好ま Uヽ。加硫剤 (L)を加える範 囲は、ハロゲン含有ポリマー（G)の重量を 100%基準として、重量百分率で表して、 0. 5%以上、 50. 0%以下、即ち、 LZG = 0. 5%〜50. 0%であることが好ましい。 加硫剤 (L)の含有が、 0. 5%より少ないと、前述の優れた耐熱性が得難い。 50. 0% を超えると、ガラス繊維コードと母材ゴムとの接着強さが弱くなり作製した伝動ベルト は、耐久性に劣る。
[0067] 前記加硫剤 (L)としては、ニトロソ化合物および Zまたは亜鉛ィ匕合物が挙げられる。
[0068] また、本発明のガラス繊維被覆用塗布液をガラス繊維コードに塗布後、乾燥させて 1 次被覆層とし、更にガラス繊維 2次被覆用塗布液を塗布し、 2次被覆層を設けたゴム 補強用ガラス繊維ゴム補強用ガラス繊維の前記第 1〜第 4の態様におけるガラス繊 維 2次被覆用塗布液中に加硫剤 (L)を加えることが好ま Uヽ。ガラス繊維 2次被覆層 用塗布液中の無機充填剤 (N)は、ハロゲン含有ポリマー（G)の重量を 100%基準と して、重量百分率で表して、 10. 0%以上、 70. 0%以下、即ち、 NZG= 10. 0%〜 70. 0%であることが好ましい。無機充填剤 (N)の含有が、 10. 0%より少ないと、前 述の優れた耐熱性が得難い。 70. 0%を超えると、ガラス繊維コードと母材ゴムとの接 着強さが弱くなり作製した伝動ベルトは、耐久性に劣る。
[0069] 前記無機充填剤 (N)としては、カーボンブラック、酸ィ匕マグネシウムが挙げられる。
[0070] 更に、加硫剤としての-トロソ化合物、例えば、 p— -トロソベンゼン、無機充填剤、例 えばカーボンブラックまたは酸ィ匕マグネシウムを同時に前記ガラス繊維 2次被覆用塗 布液に添加し、ゴム補強用ガラス繊維に 2次被覆層に加えることは、該ゴム補強用ガ ラス繊維をゴムに埋設して作製した伝動ベルトの耐熱性を高める一層の効果がある。
[0071] 具体的には、ガラス繊維 2次被覆用塗布液に、塗布液中のハロゲン含有ポリマー（ G)の重量を 100%基準として、重量百分率で表して、加硫剤を 0. 5%以上、 20. 0 %以下、無機充填材を 10. 0%以上、 70. 0%以下の範囲で添加した 2次被覆層を 設けてなる本発明のゴム補強用ガラス繊維を耐熱ゴムに埋設し作製された伝動ベル トは、いっそうの耐熱性を発揮する。加硫剤の含有が 0. 5%より少ない、無機充填材 の含有が 10. 0%より少ないと耐熱性を向上させる効果が発揮されず、加硫剤を、 20 . 0%を超えて、無機充填材を、 70. 0%を超えてカ卩える必要はない。
[0072] 耐熱性のためには、前記ハロゲン含有ポリマー（G)には、クロロスルホン化ポリェチ レン (C)を用いることが好ま 、。
実施例
[0073] 本発明のガラス繊維被覆用塗布液であるモノヒドロキシベンゼン ホルムアルデヒド 榭脂（A)とビュルピリジン スチレン ブタジエン共重合体（B)とクロロスルホン化ポ リエチレン (C)とを水に分散させてェマルジヨンとした本発明のガラス繊維被覆用塗 布液をガラス繊維コードに塗布後乾燥させ、更に、ハロゲン含有ポリマー（G)とビスァ リルナジイミド (H)、あるいはハロゲン含有ポリマー（G)と有機ジイソシァネート ωお よびメタクリル酸亜鉛 (I)、ある 、はハロゲン含有ポリマー（G)とマレイミド (Κ)、ある ヽ はハロゲン含有ポリマー (G)とトリアジン系化合物 (Μ)とを有機溶剤に分散させたガ ラス繊維 2次被覆用塗布液を塗布し被覆層としたゴム補強用ガラス繊維を作製した。 (実施例 1〜8)
[0074] 次いで、本発明の範疇にないゴム補強用ガラス繊維を作製した。（比較例 1〜3)。
これら本発明のゴム補強用ガラス繊維 (実施例 1〜8)、本発明の範疇にないゴム補 強用ガラス繊維 (比較例 1〜3)の耐熱ゴムに対する接着強さ評価試験を行い、評価 結果を比較した。
[0075] また、これら、本発明のゴム補強用ガラス繊維、または本発明の範疇にな!、ゴム補 強用ガラス繊維を耐熱ゴムに埋設させた伝動ベルトを作製した。次いで、これら伝動 ベルトをプーリーにセットして、耐水性を評価するために、伝動ベルトに水をかけつつ 長時間走行させて、被覆層が初期の接着強さを持続した結果として長時間走行後も 引っ張り強さが変化せず、寸法安定性に優れることを評価するための耐水走行疲労 性能評価試験を行い、本発明のゴム補強用ガラス繊維 (実施例 1、 2、 4、 5、 6、 7、 8 )を埋設した伝動ベルト、本発明の範疇にないゴム補強用ガラス繊維 (比較例 1〜3) を埋設した伝動ベルトにおける評価結果を比較した。また、耐熱性を評価するために 、伝動ベルトに高温下複数のプーリーを用いて、長時間の屈曲走行をさせて、被覆 層が初期の接着強さを持続した結果として長時間走行後も引っ張り強さが変化せず 、寸法安定性に優れることを評価するための耐熱耐屈曲走行疲労性能評価試験を 行い、本発明のゴム補強用ガラス繊維 (実施例 2、 4、 5、 6、 7、 8)を埋設した伝動べ ルト、本発明の範疇にないゴム補強用ガラス繊維 (比較例 1、 2)を埋設した伝動ベル トにおける評価結果を比較した。
[0076] 以下、詳細に述べる。
実施例 1
[0077] (本発明のガラス繊維被覆用塗布液の調製）
最初に、モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)の合成について述べる 。還流冷却器、温度計、攪拌機をつけた三つ口セパラブルフラスコに、モノヒドロキシ ベンゼン（D)、 100重量部、 37. 0重量％の濃度のホルムアルデヒド（E)水溶液、 15 7重量部（モル比で表せば、 EZD= 1. 8)、 10重量％の濃度の水酸ィ匕ナトリウム水 溶液、 5重量部を仕込み、 80°Cに加熱した状態で 3時間攪拌した。攪拌を止め、冷 却した後、 1重量％濃度の水酸化ナトリウム水溶液、 370重量部を加え、モノヒドロキ シベンゼン—ホルムアルデヒド榭脂 (A)を重合した。
[0078] 次 、で、前述の手順で合成したモノヒドロキシベンゼン一ホルムアルデヒド榭脂 (A) を用い、市販のビュルピリジン スチレン ブタジエン共重合体（B)ェマルジヨンと、 クロロスルホン化ポリエチレン（C)ェマルジヨンとにアンモニア水と水を添カ卩し、本発 明のガラス繊維被覆用塗布液を調製した。
[0079] 詳しくは、モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)、 42重量部と、ビュル ピリジン、スチレン、ブタジエンを、ビニルピリジン：スチレン：ブタジエン = 15 : 15 : 70 重量比となるように重合したビュルピリジン スチレン ブタジエン重合体（B)ェマル ジョンとしての日本エイアンドエル株式会社製、商品名、ピラテックス（固形分濃度、 4 1. 0重量0 /0) 476重量部と、クロロスルホン化ポリエチレン（C)ェマルジヨンとしての住 友精化株式会社製、商品名、 CSM450 (固形分濃度、 40. 0重量％) 206重量部と 、 PH調整剤としてアンモニア水 (濃度、 25. 0重量％) 22重量部とに、全体として 10 00重量部になるように水を添加して、本発明のガラス繊維被覆用塗布液を調製した
[0080] ガラス繊維被覆用塗布液中の各成分の含有割合は、モノヒドロキシベンゼン ホル ムアルデヒド榭脂 (A)とビュルピリジン スチレン ブタジエン共重合体（B)とクロ口 スルホンィ匕ポリエチレン (C)を合わせた重量を 100%基準として、重量百分率で表し て、モノヒドロキシベンゼン一ホルムアルデヒド榭脂（A)が、 A/ (A+B + C) = 3. 6 %、ビュルピリジン—スチレン—ブタジエン共重合体（B)力 B/ (A+B + C) =67. 8%、クロロスルホン化ポリエチレン（C)、が CZ(A+B+C) = 28. 6%である。尚、 ガラス繊維被覆用塗布液中のビュルピリジン スチレン ブタジエン共重合体 (B)、 クロロスルホン化ポリエチレン（C)の重量は、前記ビラテックスおよび CSM450の固 形分濃度から、固形分に換算して求めた。
[0081] (本発明のゴム補強用ガラス繊維の作製）
次いで、クロロスルホン化ポリエチレン（C)と、 p ジニトロソベンゼンと、ビスァリル ナジイミド (G)に属するへキサメチレンジァリルナジイミドとに、カーボンブラックをカロえ 、キシレンに分散させた、本発明のゴム補強用ガラス繊維に 2次被覆層を設けるため のガラス繊維 2次被覆用塗布液を調製した。
[0082] 詳しくは、クロロスルホン化ポリエチレン (C)としての東ソー株式会社製、商品名、 T S— 430、 100重量部と、 p ジニトロソベンゼン、 40重量部と、 N—N≡—へキサメ チレンジァリルナジイミドとしての丸善石油化学株式会社製、商品名、 BANI— H、 0 . 3重量部とに、カーボンブラック、 30重量部を加え、キシレン、 1315重量部に分散 させてガラス繊維 2次被覆用塗布液を調製した。即ち、クロロスルホン化ポリエチレン (C)の重量に対して、ビスァリルナジイミド（G)に属する N— N≡—へキサメチレンジ ァリルナジイミドを HZG = 0. 3重量0 /0、加硫剤である p ジニトロソベンゼンを 40重 量％、無機充填材であるカーボンブラックを 30重量％となるようにしてガラス繊維 2次 被覆用塗布液を調製した。
[0083] 径 9 μ mのガラス繊維フィラメントを 200本集束したガラス繊維コード 3本を引き揃え た後、前述の手順で作製したガラス繊維被覆用塗布液を塗布し、その後、温度、 28 0°C下で、 22秒間乾燥させて被覆層を設けた。
[0084] この時の固形分付着率、即ち、被覆層の重量割合は、被覆層を設けたガラス繊維 束の全重量に対して 19. 0重量％であった。
[0085] 前記被覆層を設けたガラス繊維コードを、 2. 54cm当たり 2. 0回の下撚りを与え、 更に 13本引き揃えて下撚りと逆方向に 2. 54cm当たり 2. 0回の上撚りをする作業を 施した。その後、前述の手順で作製したガラス繊維 2次被覆用塗布液を塗布した後、 110°Cで 1分間の乾燥を行い、 2次被覆層を設け、本発明のゴム補強用ガラス繊維（ 実施例 1)を作製した。このようにして、下練りと上練りの方向を各々逆方向とした 2種 類のゴム補強用ガラス繊維を作製した。各々、 s練り、 Z練りと称する。
[0086] この時の固形分付着率、即ち、 2次被覆層の重量割合は、 1次および 2次被覆層を 設けたガラス繊維束の重量に対して、 3. 5重量％であった。
実施例 2
[0087] 実施例 1のガラス繊維被覆用塗布液に対して、前記モノヒドロキシベンゼン ホル ムアルデヒド榭脂 (A)の添加量を 83重量部、ビニルピリジンとスチレンとブタジエンと を、 15 : 15 : 70の重量割合となるように重合してなるビュルピリジン スチレンーブタ ジェン共重合体 (B)ェマルジヨン（日本エイアンドエル株式会社製、商品名、ビラテツ タス、固形分、 41. 0重量％)の添加量を 451重量部に変えた以外は、実施例 1と同 様に本発明のガラス繊維被覆用塗布液を調製した。即ち、ガラス繊維被覆用塗布液 中のモノヒドロキシベンゼン ホルムアルデヒド榭脂（A)とビュルピリジン スチレン ブタジエン共重合体（B)とクロロスルホン化ポリエチレン（C)を合わせた重量を 10 0%基準として、重量百分率で表して、モノヒドロキシベンゼン ホルムアルデヒド榭 脂（A)が、 A/ (A+B + C) = 7. 2%、ビニノレピリジン スチレン ブタジエン共重合 体（B)が、 B/ (A+B + C) =64. 2%、クロロスルホン化ポリエチレン（C)が、 C/ (A + B + C) = 28. 6%とした。
[0088] 次 、で、実施例 1に示した手順で、実施例 1と同様のガラス繊維被覆用 2次液を調 製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層を 設け本発明のゴム補強用ガラス繊維 (実施例 2)を作製した。
実施例 3 [0089] 実施例 1のガラス繊維被覆用塗布液に対して、前記モノヒドロキシベンゼン ホル ムアルデヒド榭脂 (A)の添力卩量を 124重量部、ビニルピリジンとスチレンとブタジエン とを、 15 : 15 : 70の重量割合となるように重合してなるビュルピリジン スチレンーブ タジェン共重合体 (B)ェマルジヨン（日本エイアンドエル株式会社製、商品名、ピラテ ッタス、固形分、 41. 0重量％)の添加量を 426重量部に変えた以外は、実施例 1と 同様に、本発明のガラス繊維被覆用塗布液を調製した。即ち、ガラス繊維被覆用塗 布液中のモノヒドロキシベンゼン ホルムアルデヒド榭脂（A)とビニルピリジンースチ レン ブタジエン共重合体（C)とクロロスルホン化ポリエチレンを合わせた重量を 10 0%基準として、重量百分率で表して、モノヒドロキシベンゼン ホルムアルデヒド榭 脂（A)が、 A/ (A+B + C) = 10. 8%、ビ-ノレピリジン一スチレン一ブタジエン共重 合体（B)が、 B/ (A+B + C) = 60. 6%、クロロスルホン化ポリエチレン（C)が、 C/ (A+B+C) = 28. 6%となるよう調整した。
[0090] 次 、で、実施例 1に示した手順で、実施例 1と同様のガラス繊維被覆用 2次液を調 製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層を 設け本発明のゴム補強用ガラス繊維 (実施例 3)を作製した。
実施例 4
[0091] モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)に市販のモノヒドロキシベンゼン —ホルムアルデヒド榭脂 (A) (群栄化学工業社製、商品名、レジトップ、型番 PL— 46 67、固形分、 50重量％)を 1重量％濃度の水酸ィ匕ナトリウム水溶液で 2倍の重量割 合で希釈したものを用いた。
[0092] 実施例 1のガラス繊維被覆用塗布液に対してモノヒドロキシベンゼン ホルムアルデ ヒド榭脂（A)としての前記レジトップ、型番 PL— 4667の添力卩量を 83重量部、ビュル ピリジンとスチレンとブタジエンとを、 15 : 15 : 70の重量割合となるように重合したビ- ルビリジン—スチレン—ブタジエン共重合体（B)ェマルジヨン（日本エイアンドエル株 式会社製、商品名、ピラテックス、固形分、 41重量％)の添加量を 451重量部に変え た以外は、実施例 1と同様に本発明のガラス繊維被覆用塗布液を調製した。即ち、 ガラス繊維被覆用塗布液中のモノヒドロキシベンゼン一ホルムアルデヒド榭脂 (A)と ビュルピリジン一スチレン ブタジエン共重合体（B)とクロロスルホン化ポリエチレン（ c)を合わせた重量を 100%基準としてとして、重量百分率で表して、モノヒドロキシ ベンゼン—ホルムアルデヒド榭脂（A)が AZ (A+B + C) = 7. 2%、ビュルピリジン スチレン ブタジエン共重合体が（B)が BZ (A+B + C) =64. 2%、クロロスルホ ン化ポリエチレン (C)が、 C/ (A+B + C) = 28. 6%、となるように調整した。
[0093] 次 、で、実施例 1に示した手順で、実施例 1と同様のガラス繊維被覆用 2次液を調 製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層を 設け本発明のゴム補強用ガラス繊維 (実施例 4)を作製した。
実施例 5
[0094] 実施例 1に示した手順で、実施例 2と同様のガラス繊維被覆用塗布液を調製し、実施 例 1と同様の手順で作業を行い、ガラス繊維コードに被覆層を設けた。
[0095] 次!、で、ハロゲン含有ポリマー（G)であるクロロスルホン化ポリエチレンとしての東ソ 一株式会社製、商品名、 TS— 430、 100重量部と、 p ジニトロソベンゼン、 40重量 部と、有機ジイソシァネート (J)としてのへキサメチレンジジイソシァネートとメタクリル 酸亜鉛 (I)とをそれぞれ 25重量部と 3. 0重量部に、カーボンブラック、 30重量部をカロ え、キシレン、 1315重量部に分散させてガラス繊維 2次被覆用塗布液を調製した。 即ち、クロロスルホン化ポリエチレンの重量に対して、へキサメチレンジジイソシァネ ートが JZG = 25. 0重量％、メタクリル酸亜鉛 (I)力 ZG = 3. 0重量％、無機充填材 であるカーボンブラックを 30重量％となるようにしてガラス繊維 2次被覆用塗布液を 調製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層 を設け本発明のゴム補強用ガラス繊維 (実施例 5)を作製した。
実施例 6
[0096] 実施例 1に示した手順で、実施例 2と同様のガラス繊維被覆用塗布液を調製し、実施 例 1と同様の手順で作業を行い、ガラス繊維コードに覆層を設けた。
[0097] 次!、で、ハロゲン含有ポリマー（G)であるクロロスルホン化ポリエチレンとしての東ソ 一株式会社製、商品名、 TS— 430、 100重量部と、 p ジニトロソベンゼン、 40重量 部と、マレイミド（K)に属する N、 N— mフエ-レンジマレイミドを KZG = 50. 0重量 %になるように加え、更に、カーボンブラック、 30重量部をカ卩え、キシレン、 1315重 量部に分散させてガラス繊維 2次被覆用塗布液を調製した。即ち、クロロスルホンィ匕 ポリエチレンの重量に対して、マレイミドに属する N、 N—mフエ-レンジマレイミドを 5 0. 0重量％、加硫剤であるメタクリル酸亜鉛を KZG = 3. 0重量％、無機充填材であ るカーボンブラックを 30. 0重量％となるようにしてガラス繊維 2次被覆用塗布液を調 製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層を 設け本発明のゴム補強用ガラス繊維 (実施例 6)を作製した。
実施例 7
[0098] 実施例 1に示した手順で、実施例 2と同様のガラス繊維被覆用塗布液を調製し、実 施例 1と同様の手順で作業を行い、ガラス繊維コードに覆層を設けた。
[0099] 次!、で、ハロゲン含有ポリマー（G)であるクロロスルホン化ポリエチレンとしての東ソ 一株式会社製、商品名、 TS— 430、 100重量部と、 p—ジニトロソベンゼン、 40重量 部と、トリァジン化合物（M)としてのトリァリルシアヌレートを MZG = 2. 0重量0 /0にな るように加え、カーボンブラック、 30重量部をカ卩え、キシレン、 1315重量部に分散さ せてガラス繊維 2次被覆用塗布液を調製した。即ち、クロロスルホンィ匕ポリエチレンの 重量に対して、加硫剤である p—ジニトロソベンゼンを 40重量％、トリアジン系化合物 に属するトリァリルシアヌレートを MZG = 2. 0重量0 /0、無機充填材であるカーボンブ ラックを 30重量％となるようにしてガラス繊維 2次被覆用塗布液を調製し、実施例 1と 同様の手順で作業を行 ヽ、ガラス繊維コードに更なる 2次被覆層を設け本発明のゴ ム補強用ガラス繊維 (実施例 7)を作製した。
実施例 8
[0100] 実施例 1に示した手順で、実施例 2と同様のガラス繊維被覆用塗布液を調製し、実 施例 1と同様の手順で作業を行 、、ガラス繊維コードに 1被覆層を設けた。
[0101] 次!、で、ハロゲン含有ポリマー（G)であるクロロスルホン化ポリエチレンとしての東ソ 一株式会社製、商品名、 TS— 430、 100重量部と、 p—ジニトロソベンゼン、 40重量 部と、トリァジン化合物（M)であるトリアリルイソシァヌレートを MZG = 2. 0重量0 /0に なるように加え、更に、カーボンブラック、 30重量部を加え、キシレン、 1315重量部 に分散させてガラス繊維 2次被覆用塗布液を調製した。即ち、クロロスルホンィ匕ポリエ チレンの重量に対して、加硫剤である p—ジニトロソベンゼン、 40重量部、トリアジン 系化合物（M)に属するトリアリルイソシァヌレートを MZG = 2. 0重量％、無機充填 材であるカーボンブラックを 30. 0重量％となるようにしてガラス繊維 2次被覆用塗布 液を調製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被 覆層を設け本発明のゴム補強用ガラス繊維コード (実施例 8)を作製した。
比較例 1
[0102] 従来のレゾルシン ホルムアルデヒド榭脂とビュルピリジン一スチレン一ブタジエン 共重合体ェマルジヨンとクロロスルホン化ポリエチレンとからなるゴム補強用ガラス繊 維塗布液を調製した。
[0103] 実施例 1と異なり、モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)に替えてレゾ ルシン—ホルムアルデヒド榭脂（レゾルシンとホルムアルデヒドとのモル比、 1. 0 : 1. 0 で反応させたもの、固形分、 8. 7重量％)を 239重量部使用し、ビュルピリジンとスチ レンとブタジエンとを、 15 : 15 : 70の重量割合で含有するビュルピリジン—スチレン— ブタジエンェマルジヨン（日本エイアンドエル株式会社製、商品名、ピラテックス、固 形分、 41. 0重量％)の添加量を 451重量部に変えた以外は、実施例 1と同様にガラ ス繊維被覆用塗布液を調製した。即ち、ガラス繊維被覆用塗布液中のレゾルシン ホルムアルデヒド榭脂とビュルピリジン スチレン ブタジエン共重合体とクロロスル ホンィ匕ポリエチレン合わせた重量を 100%基準として、重量百分率で表して、レゾル シン—ホルムアルデヒド榭脂（A)が、 A/ (A+B + C) = 7. 2%、ビュルピリジン—ス チレン一ブタジエン共重合体（B)が、 B/ (A+B+C) =64. 2%、クロロスルホンィ匕 ポリエチレン (C)が、 CZ (A+B + C) = 28. 6%、となるように調整した。
[0104] 次いで、実施例 1に示した手順で、実施例 1と同様のガラス繊維被覆用 2次液を調 製し、実施例 1と同様の手順で作業を行い、ガラス繊維コードに更なる 2次被覆層を 設けゴム補強用ガラス繊維 (比較例 1)を作製した。
比較例 2
[0105] 実施例 1と同じガラス繊維被覆用塗布液を用い、次!、で、クロロスルホンィ匕ポリェチ レン (東ソ一株式会社製、商品名、 TS— 430)、 100重量部と、 4、 4≡ージフエ-ルメ タンジイソシァネート、 40重量部と、カーボンブラック、 30重量部と、キシレン、 1315 重量部からなるガラス繊維 2次被覆用塗布液を用い、実施例 1に示した手順で作業 を行 ヽ、被覆層および 2次被覆層を設けたゴム補強用ガラス繊維 (比較例 2)を作製 した。即ち、ガラス繊維 2次被覆用塗布液中のクロロスルホンィ匕ポリエチレンの重量に 対して、 40. 0重量0 /0の 4、 4≡ージフエ-ルメタンジイソシァネート、 30. 0重量％の カーボンブラックを用いた。
比較例 3
[0106] 実施例 2と同じガラス繊維被覆用塗布液を用い、次 、で、比較例 2と同じガラス繊維 2次被覆用塗布液を調製し、実施例 1に示した手順で、 1次被覆層および 2次被覆層 を設けたゴム補強用ガラス繊維 (比較例 3)を作製した。
[0107] (接着強さの評価試験）
接着強さの評価試験を説明する前に、試験に使用した耐熱ゴムを説明する。
[0108] 母材ゴムとしての HNBR(日本ゼオン株式会社製、型番、 2020)、 100重量部に対 して、カーボンブラック、 40重量部と、亜鉛華、 5重量部と、ステアリン酸、 0. 5重量部 と、硫黄、 0. 4重量部と、加硫促進剤、 2. 5重量部と、老化防止剤、 1. 5重量部とを 配合してなる HNBRを架橋した耐熱ゴム（以後、耐熱ゴム Aとする）、また HNBR(日 本ゼオン株式会社製、型番、 2010)、 100重量部に対して、カーボンブラック、 40重 量部と、亜鉛華、 5重量部と、ステアリン酸、 0. 5重量部と、 1、 3 ジ (t プチルぺロ キシイソプロピル)ベンゼン、 5重量部と、老化防止剤、 1. 5重量部とを配合してなる HNBRを架橋した耐熱ゴム（以後、耐熱ゴム Bとする）を接着強さの評価試験に使用 した。
[0109] 試験片は而熱ゴム Aまたは而熱ゴム Bからなる 3mm厚、 25mm幅のゴムシート上に 前記ゴム補強用ガラス繊維コード (実施例 1〜4、比較例 1〜3)を 20本並べ、その上 力も布をかぶせ、耐熱ゴム Aについては、温度、 150°C下、 196-ユートン/ cm2 (以 後、ニュートンを Nと略す）、また耐熱ゴム Bについては、温度、 170°C下、 196NZc m2の条件で端部を除き押圧し、 30分間加硫させつつ成形して、接着強さ評価のた めの試験片、言い換えればゴムシートを得た。この試験片の接着強さの測定を、端部 において各々のゴムシートとゴム補強用ガラス繊維を個別にクランプにて挟み、剥離 速度を 50mmZminとし、ゴムシートからゴム補強用ガラス繊維を剥がす際の最大の 抵抗値を測定し、剥離強さとした。剥離強さが大きいほど接着強さに優れる。
(接着強さの評価結果） 接着強さの評価結果を表 1に示す。
[表 1]
Figure imgf000028_0001
表 1にお 、て、ガラス繊維とゴムが界面力も剥離して 、な 、破壊状態をゴム破壊とし
、界面力 一部のみでも剥離している破壊状態を界面剥離とした。ゴム破壊の方が、 界面剥離より接着強さに優れる。
[0110] 実施例 1の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Aについては 314Nであり、而熱ゴム Bについては 284Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0111] 実施例 2の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Αについては 333Νであり、而熱ゴム Bについては 304Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0112] 実施例 3の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Aについては 323Nであり、而熱ゴム Bについては 309Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0113] 実施例 4の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Αについては 343Νであり、而熱ゴム Bについては 345Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0114] 実施例 5の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Αについては 313Νであり、而熱ゴム Bについては 305Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0115] 実施例 6の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Αについては 325Νであり、而熱ゴム Bについては 312Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0116] 実施例 7の本発明のゴム補強用ガラス繊維は、表 1に示すように、剥離強さを測定 したところ、而熱ゴム Αについては 333Νであり、而熱ゴム Bについては 352Nであり、 双方のゴムに対して接着性は良好であり、接着強さに優れて 、た。
[0117] 実施例 8の本発明のゴム補強用ガラス繊維は、表 1の実施例 8に示すように、耐熱 ゴム Αについては 314Nであり、而熱ゴム Bについては 323Nであり、双方のゴムに対 して接着性は良好であり、接着強さに優れていた。
[0118] また、破壊状態は、本発明の実施例 1〜8のゴム補強用ガラス繊維は、表 1の実施 例 1〜8に示すように、耐熱ゴム Αを使用した場合、耐熱ゴム Bを使用した場合ともに ゴム破壊であり、接着強さに優れていた。
[0119] 比較例 1の本発明の範疇に属さないゴム補強用ガラス繊維は、実施例 1と同様の手 順で、試験片をつくり、接着強さの評価を行ったところ、表 1の比較例 1に示すように、 而す熱ゴム Aについては 323N、而熱ゴム Bについては 314Nであり、双方のゴムに対 して接着特性は良好であり、接着強さに優れていた。破壊状態は、耐熱ゴム Αを使用 した場合、耐熱ゴム Bを使用した場合、ともに破壊状態はゴム破壊であり、接着強さに 優れていた。 [0120] 比較例 2の本発明の範疇に属さないゴム補強用ガラス繊維は、実施例 1と同様の手 順で、試験片をつくり、接着強さの評価を行ったところ、表 1の比較例 2に示すように、 耐熱ゴム Aについては 294Nで良好な接着強さであった力 耐熱ゴム Bについては 1 27Nであり、接着力が弱く接着強さに劣っていた。
[0121] 比較例 3の本発明の範疇に属さないゴム補強用ガラス繊維は、実施例 1と同様の手 順で、試験片をつくり、接着強さの評価を行ったところ、表 1の比較例 3に示すように、 耐熱ゴム Aについては 319Nで良好な接着強さであった力 耐熱ゴム Bについては 1 18Nであり、接着力が弱く接着強さに劣っていた。
(耐水性評価）
[0122] 実施例 2、 4、 5、 6、 7、 8および比較例 1〜3で作製したゴム補強用ガラス繊維を 補強材として、母材ゴムに前記耐熱ゴム Bを用い、巾 19mm、長さ 876mmの伝動べ ルトを各々作製し、耐水性を評価するための耐水走行疲労試験を実施した。耐水性 は、注水下、伝動ベルトを、歯車、即ち、プーリーを用いて走行させ、一定時間経過 の引っ張り強さ保持率、即ち、耐水走行疲労性能で評価する。
[0123] 図 1は、ゴム補強用ガラス繊維を耐熱ゴムに埋設させて作製した伝動ベルトを切断 した際の斜視図である。
[0124] 伝動ベルト 1はプーリーに嚙み合わせるための高さ 3. 2mmの突起部 1Aを多数有 し、突起部を除く背部 1Bの厚みが 2. Ommで、伝動ベルトの該背部 1Bには、断面に 見られるように上撚りと下撚りの練り方向が異なる S撚り、 6本 Z撚り、 6本、合わせて 1 2本の各ゴム補強用ガラス繊維 (ゴム補強用ガラス繊維コード） 2が、 S撚りと Z撚りとが 交互になるように埋設されて!ヽる。
[0125] 図 2は、伝動ベルトの耐水走行疲労試験機の概略側面図である。
[0126] 図 2に示すように、各々の伝動ベルト 1を図示しない駆動モーターと発電機を備え た耐水走行疲労試験機に装着し耐水性を測定する。
[0127] 伝動ベルト 1は駆動モーターにより回転駆動される駆動プーリー（駆動モーターに 連結） 3の駆動力により、従動プーリー 4および 5を回転させつつ走行する。従動ブー リー 5には図示しない発電機が連結されており、発電機を駆動し lkwの電力を発生さ せる。アイドラー 6は、耐水走行疲労試験における走行中に回転しつつ伝動ベルト 1 を張る役割を有し、伝動ベルト 1を張るための荷重として 500Nを伝動ベルト 1に与え る。従動プーリー 4、 5は、径、 60mm,歯数、 20Tであり、駆動プーリー 3は、径 120 mmであり、歯数、 40Tである。耐水走行疲労試験中の駆動プーリーの 1分間あたり の回転数は、 3000rpm、従動プーリー 4、 5の 1分間あたりの回転数は、 6000rpmで ある。回転方向は、伝動ベルト 1に平行な矢印で示す。
[0128] 常温において、図 2に示すように、 1時間当たり 6000mlの水 7を、駆動プーリー 3と 従動プーリー 4の間において、伝動ベルト 1に均等に滴下させつつ、駆動プーリー 3 を 3000rpmで回転させ、伝動ベルト 1を従動プーリー 4および 5、アイドラー 6を用い て走行させた。このようにして、 36時間、伝動ベルト 1を走行させる耐水走行疲労試 験を実施した。耐水走行疲労試験前の伝動ベルト 1の引っ張り強さ、および耐水走 行疲労試験後の引っ張り強さを測定し、数 1の式により試験前に対する試験後の伝 動ベルト 1の引っ張り強さ保持率を求め、実施例 1、 2、 4、 5、 6、 7、 8及び比較例 1〜 3のゴム補強用ガラス 2を用いて作製した伝動ベルト 1の耐水性を比較評価した。 (引張り強さ測定）
[0129] 引張り強さ測定に供する試験片の長さは 257mmであり、 1本の伝動ベルトから 3本 切り取り得られる。これら試験片の端部各々をクランプ間距離 145mmのクランプにて はさみ、引張り速度を 50mmZ分とし、ベルトが破壊されるまでの最大の抵抗値を引 張り強さとした。 1本のベルトから 3回、抵抗値を測定し、その平均値を伝動ベルトの 引張り強さとした。なお、試験前の引張り強さは、同様に作製した 10本のベルトから 各 3回、抵抗値を測定して、その平均値を初期値として用いた。
[数 1] 引っ張り強さ保持率 (¾) 後の引っ張リ強さ ÷Ktt前の引っ張り強さ X I 0 0 各々の伝動ベルトの耐水走行疲労試験後の引張り強さ保持率を表 2に示す。
[表 2] 実施 実施 実施 実施 実施 実施 実施 比較 比較 比較
例 1 例 2 例 4 例 5 例 6 例 7 例 8 例 1 例 2 例 3
引っ張り強さ
56 61 63 58 59 63 54 47 39 51
保持率 （％)
[0130] 表 2に示すように、実施例 1、 2、 4、 5、 6、 7、 8及び比較例 3のモノヒドロキシベンゼ ンーホルムアルデヒド榭脂、ビュルピリジン スチレン ブタジエン共重合体とクロ口 スルホンィ匕ポリエチレンとを組成物としたガラス繊維被覆用塗布液をガラス繊維コー ドに塗布乾燥させた被覆層および更なる 2次被覆層を有するのゴム補強用ガラス繊 維 2を用 、た伝動ベルト 1の走行試験後の弓 Iつ張り強さ保持率は、実施例 1のゴム補 強用ガラス繊維 2を用いた場合は 56%であり、実施例 2のゴム補強用ガラス繊維 2を 用いた場合は 61%であり、実施例 4のゴム補強用ガラス繊維 2を用いた場合は 63% であり、実施例 5のゴム補強用ガラス繊維 2を用いた場合は 58%であり、実施例 6の ゴム補強用ガラス繊維 2を用いた場合は 59%であり、実施例 7のゴム補強用ガラス繊 維 2を用いた場合は 63%であり、実施例 8のゴム補強用ガラス繊維 2を用いた場合は 54%であり、比較例 3のゴム補強用ガラス繊維 2を用いた場合は 51%であった。
[0131] それに対して、比較例 1および比較例 2に示すように、モノヒドロキシベンゼンーホ ルムアルデヒド榭脂を用 、な 、替わりにレゾルシン ホルムアルデヒド榭脂を用 、て 作製した、レゾルシン ホルムアルデヒド榭脂、ビュルピリジン スチレンーブタジェ ン共重合体とクロロスルホンィ匕ポリエチレンとを組成物としたガラス繊維被覆用塗布 液をガラス繊維コードに塗布乾燥させた被覆層および更なる 2次被覆層を有するゴム 補強用ガラス繊維 2の引っ張り強さ保持率は、比較例 1のゴム補強用ガラス繊維 2を 用いた場合は 47%であり、比較例 2のゴム補強用ガラス繊維 2を用いた場合は 39% であり、耐水性に劣っていた。尚、実施例 2のゴム補強用ガラス繊維 2を用いた場合 には引っ張り強さ保持率は 61 %であって、比較例 3のゴム補強用ガラス繊維 2を用 ヽ た場合の 51 %に比較して大き 、。
[0132] この耐水走行疲労試験の結果より、従来のゴム補強用ガラス繊維 2に比較して、モ ノヒドロキシベンゼン ホルムアルデヒド榭脂（A)と、ビュルピリジン スチレンーブタ ジェン共重合体 (B)と、クロロスルホンィ匕ポリエチレン (C)とを組成物とした本発明の ガラス繊維被覆用塗布液を塗布後乾燥させてなる被覆層を有し、ビスァリルナジイミ ド（H)に属する N— N≡—へキサメチレンジァリルナジイミド、ハロゲン含有ポリマー（ G)としてのクロロスルホン化ポリエチレンと、 p ジ-トロソベンゼンとを組成物とした 更なる 2次被覆層を有した本発明のゴム補強用ガラス繊維 2を用いた伝動ベルト 1が 優れた耐水性を有することが判った。
[0133] この耐水走行疲労試験の結果より、従来のゴム補強用ガラス繊維 2に比較して、モ ノヒドロキシベンゼン ホルムアルデヒド榭脂（A)と、ビュルピリジン スチレンーブタ ジェン共重合体 (B)と、クロロスルホンィ匕ポリエチレン (C)とを組成物とした本発明の ガラス繊維被覆用塗布液を塗布後乾燥させてなる被覆層を有し、メタクリル酸亜鉛 (I )と有機ジイソシァネート (J)に属するへキサメチレンジイソシァネート、ハロゲン含有 ポリマー（G)としてのクロロスルホン化ポリエチレンと、 p ジ-トロソベンゼンとを組成 物とした更なる 2次被覆層を有した本発明のゴム補強用ガラス繊維 2を用いた伝動べ ルト 1が優れた耐水性を有することが判った。
[0134] この耐水走行疲労試験の結果より、従来のゴム補強用ガラス繊維 2に比較して、モ ノヒドロキシベンゼン ホルムアルデヒド榭脂（A)と、ビュルピリジン スチレンーブタ ジェン共重合体 (B)と、クロロスルホンィ匕ポリエチレン (C)とを組成物とした本発明の ガラス繊維被覆用塗布液を塗布後乾燥させてなる被覆層を有し、マレイミド (K)に属 する N、 N—m—フエ-レンジマレイミド、ハロゲン含有ポリマー（G)としてのクロロスル ホンィ匕ポリエチレンと、 p ジニトロソベンゼンとを組成物とした更なる 2次被覆層を有 した本発明のゴム補強用ガラス繊維 2を用いた伝動ベルト 1が優れた耐水性を有する ことが判った。
[0135] この耐水走行疲労試験の結果より、従来のゴム補強用ガラス繊維 2に比較して、モ ノヒドロキシベンゼン ホルムアルデヒド榭脂（A)と、ビュルピリジン スチレンーブタ ジェン共重合体 (B)と、クロロスルホンィ匕ポリエチレン (C)とを組成物とした本発明の ガラス繊維被覆用塗布液を塗布後乾燥させてなる被覆層を有し、トリアジン系化合物 (M)に属するトリァリルシアヌレートまたはトリアリルイソシァヌレート、ハロゲン含有ポ リマー（G)としてのクロロスルホン化ポリエチレンと、 p ジ-トロソベンゼンとを組成物 とした更なる 2次被覆層を有した本発明のゴム補強用ガラス繊維 2を用 ヽた伝動ベル ト 1が優れた耐水性を有することが判った。
(耐熱性評価）
[0136] 次いで、実施例 2、 4、 5、 6、 7、 8及び比較例 1、 2で作製したゴム補強用ガラス繊 維コードを補強材として、母材ゴムに前記耐熱ゴム Bを用い、前述の耐水性評価と同 様に、巾 19mm、長さ 876mmの伝動ベルトを各々作製し、耐熱性を評価するための 耐熱耐屈曲走行疲労試験を実施した。耐熱性は、高温下、伝動ベルトを、複数の歯 車、即ち、プーリーを用いて、屈曲させつつ走行させ、一定時間経過の引っ張り強さ 保持率、即ち、耐熱耐屈曲走行疲労性能で評価する。
[0137] 図 3は、伝動ベルトの耐熱耐屈曲走行疲労試験機の概略側面図である。
[0138] 図 3に示すように、各々の伝動ベルト 1を図示しない駆動モーターを備えた耐熱耐 屈曲走行疲労試験機に装着し耐熱性を測定する。伝動ベルト 1は駆動モーターによ り回転駆動される駆動プーリー 8の駆動力により、 3個の従動プーリー 9、 9 9 "を回 転させつつ走行する。アイドラー 10は、耐熱耐屈曲走行疲労試験における走行中に 伝動ベルト 1を張るためのもので、伝動ベルト 1を張る役割を有し、伝動ベルト 1を張る ための荷重として 500Nを伝動ベルト 1に与える。駆動プーリー 8は、径、 120mm、 歯数、 40Tであり、従動プーリー 9、 9 9 "は、径 60mmであり、歯数、 20Tである。 耐熱耐屈曲走行疲労試験中の駆動プーリー 8の 1分間あたりの回転数は、 3000rp m、従動プーリー 9、 9 9 "の 1分間あたりの回転数は、 6000rpmである。回転方向 は、伝動ベルト 1に平行な矢印で示す。
[0139] 温度、 130°Cの環境下で、図 3に示すように、駆動プーリー 8を、 3000rpmで回転 させ、伝動ベルト 1を従動プーリー 9、 9 9 "、アイドラー 10を用いて屈曲させつつ走 行させた。このようにして、 500時間、伝動ベルト 1を走行させ耐熱耐屈曲走行疲労 試験を実施した。耐熱耐屈曲走行疲労試験前の伝動ベルト 1の引っ張り強さ、およ び耐熱耐屈曲走行疲労試験後の引っ張り強さを測定し、数 1の式より試験前に対す る試験後の伝動ベルト 1の引っ張り強さ保持率を求め、実施例 2、 4、 5、 6、 7、 8、比 較例 1、 2のゴム補強用ガラス繊維 2を用いて作製した伝動ベルト 1の耐熱耐屈曲走 行疲労性能、即ち、耐熱性を比較評価した。 [0140] 各々の伝動ベルトの耐熱耐屈曲走行疲労試験後の引っ張り強さ保持率を表 3に示 す。
[表 3]
Figure imgf000035_0001
[0141] 表 3に示すように、実施例 2、 4、 5、 6、 7及び 8のゴム補強用ガラス繊維 2を用い作 製した伝動ベルト 1の耐熱耐屈曲走行疲労試験後の引っ張り強さ保持率は、各々 91 %、 93%、 95%、 92%、 92%及び 93%であり、比較例 1、 2のゴム補強用ガラス繊 維 2を用いた伝動ベルト 1の、耐熱耐屈曲走行疲労試験後の引っ張り強さ保持率、 各々 90%、 80%より優れており、優れた耐熱性を有する。
[0142] この耐熱耐屈曲走行疲労試験の結果より、モノヒドロキシベンゼン ホルムアルデヒ ド榭脂（A)と、ビュルピリジン スチレン ブタジエン共重合体（B)と、クロロスルホン 化ポリエチレン (C)とを組成物とした本発明のガラス繊維被覆用塗布液を塗布後乾 燥させてなる被覆層を有し、ビスァリルナジイミド (H)に属する N— N≡—へキサメチ レンジァリルナジイミド、ハロゲン含有ポリマー（G)に属するクロロスルホン化ポリェチ レンと、 P ジニトロソベンゼンとを組成物とした更なる 2次被覆層を有した本発明のゴ ム補強用ガラス繊維 2を用いた伝動ベルト 1が、優れた耐熱性を有することが判った。
[0143] この耐熱耐屈曲走行疲労試験の結果より、モノヒドロキシベンゼン ホルムアルデヒ ド榭脂（A)と、ビュルピリジン スチレン ブタジエン共重合体（B)と、クロロスルホン 化ポリエチレン (C)とを組成物とした本発明のガラス繊維被覆用塗布液を塗布後乾 燥させてなる被覆層を有し、メタクリル酸亜鉛 (I)と有機ジイソシァネート ωに属する へキサメチレンジイソシァネート、ハロゲン含有ポリマー（G)に属するクロロスルホン 化ポリエチレンと、 ρ ジニトロソベンゼンとを糸且成物とした更なる 2次被覆層を有した 本発明のゴム補強用ガラス繊維 2を用いた伝動ベルト 1が、優れた耐熱性を有するこ とが半 ljつた。
[0144] この耐熱耐屈曲走行疲労試験の結果より、モノヒドロキシベンゼン ホルムアルデヒ ド榭脂（A)と、ビュルピリジン スチレン ブタジエン共重合体（B)と、クロロスルホン 化ポリエチレン (C)とを組成物とした本発明のガラス繊維被覆用塗布液を塗布後乾 燥させてなる被覆層を有し、マレイミド (K)に属する N、 N—m—フエ-レンジマレイミ ド、ハロゲン含有ポリマー（G)に属するクロロスルホン化ポリエチレンと、 p ジニトロソ ベンゼンとを組成物とした更なる 2次被覆層を有した本発明のゴム補強用ガラス繊維 2を用いた伝動ベルト 1が、優れた耐熱性を有することが判った。
[0145] この耐熱耐屈曲走行疲労試験の結果より、モノヒドロキシベンゼン ホルムアルデヒ ド榭脂（A)と、ビュルピリジン スチレン ブタジエン共重合体（B)と、クロロスルホン 化ポリエチレン (C)とを組成物とした本発明のガラス繊維被覆用塗布液を塗布後乾 燥させてなる被覆層を有し、トリアジン系化合物（M)に属するトリァリルシアヌレートま たはトリアリルイソシァヌレート、ハロゲン含有ポリマー（G)に属するクロロスルホンィ匕 ポリエチレンと、 p ジニトロソベンゼンとを組成物とした更なる 2次被覆層を有した本 発明のゴム補強用ガラス繊維 2を用いた伝動ベルト 1が、優れた耐熱性を有すること が判った。
[0146] 実施例 1〜4のゴム補強用ガラス繊維 2は架橋された HNBRとの優れた接着強さを 有し、実施例 1〜4のゴム補強用ガラス繊維 2を用い作製した伝動ベルトは、優れた 耐水性、耐熱性を有することより、高温多湿下で長時間使用するタイミングベルト等 の自動車用伝動ベルトの芯線として使用するに好適である。
[0147] 本発明により、ガラス繊維コードと前記母材ゴムとしての架橋された HNBRの接着 に対し、好ま 、接着強さを与えるガラス繊維コードの被覆層を設けるためのガラス 繊維被覆用塗布液を得て、更に、ガラス繊維コードに該ガラス繊維塗布液を塗布後 乾燥させて被覆し被覆層としたゴム補強用ガラス繊維を、架橋された HNBRに埋設 し伝動ベルトとした際に優れた耐水性を与え、伝動ベルトに優れた耐水性と耐熱性を 併せ持たせた。よって、エンジン、モーター等の駆動源の駆動力を伝えるための伝動 ベルトに補強用として埋設し、特にタイミングベルト等の自動車用伝動ベルトに使用 するために、 HNBRに埋め込み、自動車用伝動ベルトとしての多湿高温下における 引っ張り強さの維持および寸法安定性を与えるゴム補強用ガラス繊維として使用され る。

Claims

請求の範囲
[1] フエノール榭脂とビュルピリジン スチレン ブタジエン共重合体（B)とクロロスルホ ン化ポリエチレン (C)とを水に分散させェマルジヨンとしたガラス繊維コードに被覆す るためのガラス繊維被覆用塗布液であって、前記フエノール榭脂が、モノヒドロキシべ ンゼン（D)とホルムアルデヒド（E)を反応させてなるモノヒドロキシベンゼン ホルムァ ルデヒド榭脂 (A)であることを特徴とするガラス繊維被覆用塗布液。
[2] モノヒドロキシベンゼン ホルムアルデヒド榭脂（A)力 モノヒドロキシベンゼン（D)に 対するホルムアルデヒド (E)のモル比を、 E/D=0. 5〜3. 0とし塩基性の触媒で反 応させたレゾール型榭脂であることを特徴とする請求項 1に記載のガラス繊維被覆用 塗布液。
[3] 重量百分率で表して、モノヒドロキシベンゼン—ホルムアルデヒド榭脂（A)が AZ (A
+ B + C) = 1. 0%〜15. 0%、ビュルピリジン—スチレン—ブタジエン共重合体（B) 力 ¾Z(A+B + C) =45. 0%〜82. 0%、クロロスルホン化ポリエチレン（C)が CZ ( A+B+C) = 3. 0%〜40. 0%の範囲に含まれてなることを特徴とする請求項 1また は請求項 2に記載のガラス繊維被覆用塗布液。
[4] 前記ビュルピリジン—スチレン—ブタジエン共重合体（B)を、スチレン—ブタジエン 共重合体 (F)に、重量百分率で表して、 F/B = 5. 0%〜80. 0%の範囲で替えて なることを特徴とする請求項 1乃至請求項 3のいずれか 1項に記載のガラス繊維被覆 用塗布液。
[5] 請求項 1乃至請求項 4の ヽずれか 1項に記載のガラス繊維被覆用塗布液を塗布後、 乾燥させたゴム補強用ガラス繊維に、ハロゲン含有ポリマー（G)に対して、重量百分 率で表して、 H/G = 0. 3%〜10. 0%のビスァリルナジイミド (H)を有機溶剤に分 散させたガラス繊維 2次被覆用塗布液を塗布し、更なる 2次被覆層を設けてなり、 2次 被覆層の重量を基準とするハロゲン含有ポリマー（G)の含有量が、重量百分率で表 して 10. 0%〜70. 0%となることを特徴とするゴム補強用ガラス繊維。
[6] ビスァリルナジイミド（H)が N— N' へキサメチレンジァリルナジイミド、 N-N' - (m —キシリレン）ジァリルナジイミド、または N— Ν'— (4、 4≡—ジフエ-ルメタン）ジァリ ルナジイミドであることを特徴とする請求項 5に記載のゴム補強用ガラス繊維。
[7] 請求項 1乃至請求項 4の ヽずれか 1項に記載のガラス繊維被覆用塗布液を塗布後、 乾燥させたゴム補強用ガラス繊維に、ハロゲン含有ポリマー（G)とメタクリル酸亜鉛 (I )と、ハロゲン含有ポリマー（G)の重量に対する重量百分率で表して、 JZG = 5. 0% 以上、 50. 0%以下の有機ジイソシァネート ωとを有機溶剤に分散させたガラス繊維 2次被覆用塗布掖を塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の重量を基 準とするハロゲン含有ポリマー（G)の含有量力 重量百分率で表して 10. 0%〜70. 0%となることを特徴とするゴム補強用ガラス繊維。
[8] 有機ジイソシァネート (J)がへキサメチレンジイソシァネート、イソホロンジイソシァネー ト、メチレンビス（4—シクロへキシルイソシァネート）、トルエンジイソシァネート、キシ レンジイソシァネート、ナフタレンジイソシァネートまたはメチレンビス（フエ二ルイソシ ァネート）であることを特徴とする請求項 7に記載のゴム補強用ガラス繊維。
[9] 請求項 1乃至請求項 4の ヽずれか 1項に記載のガラス繊維被覆用塗布液を塗布後、 乾燥させたゴム補強用ガラス繊維に、ハロゲン含有ポリマー（G)と有機ジイソシァネ ート C と、ハロゲン含有ポリマー（G)の重量に対して、重量百分率で表して、 I/G = 0. 001%〜3. 0%のメタクリル酸亜鉛 (I)を有機溶剤に分散させたガラス繊維被覆 用塗布液を塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の重量を基準とする ハロゲン含有ポリマー（G)の含有量力 重量百分率で表して 10. 0%〜70. 0%とな ることを特徴とする請求項 7または 8に記載のゴム補強用ガラス繊維。
[10] 請求項 1乃至請求項 4の ヽずれか 1項に記載のガラス繊維被覆用塗布液を塗布後、 乾燥させたゴム補強用ガラス繊維に、ハロゲン含有ポリマー（G)に対して、重量百分 率で表して KZG = 20. 0%〜90. 0%のマレイミド (K)を有機溶剤に分散させたガ ラス繊維 2次被覆用塗布液を塗布し、更なる 2次被覆層を設けてなり、 2次被覆層の 重量を基準とするハロゲン含有ポリマー（G)の含有量力 重量百分率で表して 10. 0 %〜70. 0%となることを特徴とするゴム補強用ガラス繊維。
[11] マレイミド（K)が、 N、 N—m—フエ-レンジマレイミド、 4、 4' ジフエ-ルメタンビスマ レイミド、ポリフエ-ルメタンマレイミド、 m—フエ-レンビスマレイミド、 4—メチル 1、 3 フエ二レンビスマレイミド、 4、 4'ージフエ二ノレエーテルビスマレイミド、 4、 4'ージフ ェニルスルホンビスマレイミド、クロ口フエニルマレイミド、メチルフエニルマレイミド、ヒド ロキシフエ-ルマレイミド、カルボキシフエ-ルマレイミド、ドデシルマレイミド、シクロへ キシルマレイミドから選ばれることを特徴とする請求項 10に記載のゴム補強用ガラス 繊維。
[12] 請求項 1乃至請求項 4の ヽずれか 1項に記載のガラス繊維被覆用塗布液を塗布後、 乾燥させたゴム補強用ガラス繊維に、ハロゲン含有ポリマー（G)の重量に対する重 量百分率で表して、 M/G = 0. 3%〜10. 0%以下のトリアジン系化合物（M)を有 機溶剤に分散させたェマルジヨンを塗布乾燥して更なる 2次被覆層を設けてなり、 2 次被覆層の重量を基準とするハロゲン含有ポリマー（G)の含有量が、重量百分率で 表して 10. 0%〜70. 0%となることを特徴とするゴム補強用ガラス繊維。
[13] トリアジン系化合物（M)がトリァリルシアヌレートまたはトリアリルイソシァヌレートであ ることを特徴とする請求項 12に記載のゴム補強用ガラス繊維。
[14] ハロゲン含有ポリマー（G)がクロロスルホンィ匕ポリエチレンであることを特徴とする請 求項 5乃至請求項 13のいずれか 1項に記載のゴム補強用ガラス繊維。
[15] 請求項 5乃至請求項 14の ヽずれか 1項に記載のゴム補強用繊維を母材ゴムに埋設 させてなることを特徴とする伝動ベルト。
[16] 請求項 5乃至請求項 14の 、ずれか 1項に記載のゴム補強用繊維を水素化-トリルゴ ムに埋設させてなることを特徴とする自動車用タイミングベルト。
PCT/JP2005/017725 2004-10-01 2005-09-27 ガラス繊維被覆用塗布液およびそれを用いたゴム補強用ガラス繊維 WO2006038490A1 (ja)