Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
  • B01J37/0018—Addition of a binding agent or of material, later completely removed among others as result of heat treatment, leaching or washing,(e.g. forming of pores; protective layer, desintegrating by heat)
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
  • B01J21/04—Alumina
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
  • B01J21/12—Silica and alumina
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
  • B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/66—Silver or gold
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
  • C01F7/00—Compounds of aluminium
  • C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D301/00—Preparation of oxiranes
  • C07D301/02—Synthesis of the oxirane ring
  • C07D301/03—Synthesis of the oxirane ring by oxidation of unsaturated compounds, or of mixtures of unsaturated and saturated compounds
  • C07D301/04—Synthesis of the oxirane ring by oxidation of unsaturated compounds, or of mixtures of unsaturated and saturated compounds with air or molecular oxygen
  • C07D301/08—Synthesis of the oxirane ring by oxidation of unsaturated compounds, or of mixtures of unsaturated and saturated compounds with air or molecular oxygen in the gaseous phase
  • C07D301/10—Synthesis of the oxirane ring by oxidation of unsaturated compounds, or of mixtures of unsaturated and saturated compounds with air or molecular oxygen in the gaseous phase with catalysts containing silver or gold
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/61—Surface area
  • B01J35/612—Surface area less than 10 m2/g
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/63—Pore volume
  • B01J35/633—Pore volume less than 0.5 ml/g
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/63—Pore volume
  • B01J35/635—0.5-1.0 ml/g
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
  • B01J35/66—Pore distribution
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/12—Surface area
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/14—Pore volume
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/16—Pore diameter
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/16—Pore diameter
  • C01P2006/17—Pore diameter distribution
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/90—Other properties not specified above

Definitions

• the present invention relates to ceramic catalyst carriers and particularly to carriers for catalysts useful in the epoxidation of olefins such as for example the oxidation of ethylene to ethylene oxide, ("EO").
• EO ethylene to ethylene oxide
• Catalyst performance is assessed on the basis of selectivity and reactor temperature.
• the selectivity is the percentage of the olefin in the feed stream converted to the desired product under standard flow conditions aimed at converting a fixed percentage of the olefin in the feed stream and in the commercial production of ethylene oxide this figure is usually in the 80's.
• the percentage of olefin reacted normally decreases with time and to maintain the constant level the temperature of the reaction is increased. However this adversely affects the selectivity of the conversion to the desired product.
• the equipment used can tolerate temperatures only up to a certain level so that it is necessary to terminate the reaction when the temperature reaches a level inappropriate for the reactor.
• Epoxidation catalysts usually comprise a silver component, usually with a modifier co-deposited therewith on a ceramic carrier. It has been found that the nature of this carrier exerts a very significant influence of the performance of the catalyst carried thereon but that the reasons for that influence are not completely clear. Carriers are typically formed of a temperature resistant ceramic oxide such as alpha alumina and in general higher purity has been found to correlate with better performance. However it has been found for example that the presence of minor amounts of elemental impurities in the carrier such as alkali metals and some forms of silica can have a beneficial effect.
• a carrier for a catalyst for the epoxidation of an olefin comprises at least 95% alpha alumina with a surface area of from 1.0 to 2.6 m 2 /g and a water absorption of from 35 to 55%.
• the carrier has pores which are distributed such that at least 70% of the pore volume is in the form of pores having pore diameters from 0.2 to 10
• a method of making a carrier for an olefin epoxidation catalyst includes forming a mixture comprising from 50 to 90% by weight of a first5 particulate alpha alumina having an average particle size (d 50 ) of from 10 to 90 micrometers, from 10 to 50% by weight, based on the total alpha alumina weight, of a second particulate alpha alumina having an average particle size (d 50 ) of from 2 to 6 micrometers, from 2 to 5% by weight of an alumina hydrate; from 0.2.
• the present invention provides a carrier for an olefin epoxidation catalyst which comprises at least 95% alpha alumina with a surface area of from 1.0 to 2.6 m 2 /g and preferably at least 1.6 to 2.2 m 2 /g and a water absorption of from 35 to 55%, wherein the pores are distributed such that at least 70%, and preferably at least 80% o of the pore volume is provided by pores that have pore diameters from 0.2 to 10 micrometers and provide a pore volume of at least 0.27 mL/g of the carrier.
• pores with diameters greater than 10 micrometers represent from 0 to 20%> and preferably from 0 to 15% of the total pore volume.
• pores with pore sizes less than 0.2 micrometer represent from 0 to 10% of the total pore volume.
• the mercury pore volume is typically up to 0.56 mL/g and more commonly from 0.35 to 0.45mL/g.
• Surface area as the term is used herein is. understood to refer to the surface area as determined by the BET (Brunauer, Emmett and Teller) method as described in Journal of the American Chemical Society 60 (1938) pp309-316. While the surface area correlates with the number and sizes of the pores and hence the pore volume, it should be noted that as a practical matter the carriers need to have a certain minimum crush strength which in turn is related to the thickness of the walls surrounding the pores. Reducing this thickness makes the walls more likely to rupture under normal loading conditions such that there is a practical limitation to the surface
• the pore volume and the pore size distribution are measured by a conventional mercury intrusion device in which liquid mercury is forced into the pores of the carrier. Greater pressure is needed to force the mercury into the smaller pores and the measurement of pressure increments corresponds to volume increments in the pores penetrated and hence to the size of the pores in the incremental volume.
• the pore volume in the following description was determined by mercury intrusion under pressures increased by degrees to a pressure of 3.0 x 10 8 Pa using a Micromeritics Autopore 9200 model (130° contact angle and mercury with a surface tension of 0.473 N/m).
• the pore volume of the carriers according to the invention is at least 0.27 mL/g it is preferred that pores that have pore diameters from 0.2 to 10 microns provide a pore volume between 0.30 to 0.56 mL/g to ensure that the carriers have commercially acceptable physical properties.
• Water absorption is measured by measuring the weight of water that can be absorbed into the pores of the carrier as a percentage of the total weight of the carrier. As indicated above this can be in the range 35 to 55% but preferred carriers have a water absorption of 38 to 50% and most preferably from 40 to 45%.
• the invention also comprises a method of making a carrier for an olefin epoxidation catalyst which comprises forming a mixture comprising: a) from 50 to 90 % by weight of a first particulate alpha alumina having an average particle size (d 50 ) of from 10 to 90, preferably from 10 to 60, and most preferably from 20 to 40 micrometers; and b) from 10 to 50 % by weight, based on the total alpha alumina weight, of a second particulate alpha alumina having an average particle size (dso) of from 2.0 to 6.0 micrometers; c) from 2 to 5 % by weight of an alumina hydrate; d) from 0.2 to 0.8% of an amorphous silica compound, measured as silica; and e) from 0.05 to 0.3% of an alkali metal compound measured as the alkali metal oxide; all percentages being based on the total alpha alumina content of the mixture, and then forming the mixture into particles and firing the particles at
• the average particle size is the value as measured by a Horiba (or similar) particle size analyzer after five minutes of sonification and represents the particle diameter at which there are equal volumes of particles larger and smaller than the stated average particle size.
• the method of the invention is well adapted to produce "the carriers of the invention in view of the careful matching of particles sizes of the alumina components. Adjustments to the water absorption can be achieved by incorporation of conventional burnout materials which are typically finely divided organic compounds such as granulated polyolefins, particularly polyethylene and polypropylene, and walnut shell flour.
• burnout materials typically finely divided organic compounds such as granulated polyolefins, particularly polyethylene and polypropylene, and walnut shell flour.
• b ⁇ rnout material is used primarily to ensure the preservation of a porous structure during the green , (or unfired), phase in which the mixture may be shaped into particles by molding or extrusion processes. It is totally removed during the firing to produce the finished carrier.
• the above pore size limitations mean that the carriers according to the invention do not have excessive numbers of large pores, (that is pores larger than about 10 micrometers), and have relatively few pores below 0.2 micrometer than is usually the case.
• the carriers of the invention are preferably made with the inclusion of a bond material comprising silica with an alkali metal compound in sufficient amount to substantially prevent the formation of crystalline silica compounds.
• the bond also contains a hydrated alumina component such as boehmite or gibbsite.
• the silica component can be a silica sol, a precipitated silica, an amorphous silica or an amorphous alkali metal silicate or aluminosilicate.
• the alkali metal compound can be for example a salt such as a sodium or potassium salt.
• a convenient bond material to be incorporated with the alumina particles used to form the carrier is a mixture of boehmite, an ammonia stabilized silica sol and a soluble sodium salt.
• Alumina based carriers can be made in a number of different ways, each of which may affect the pore size distribution. Generally they are made by firing particulate mineral components at an elevated temperature until the particles sinter together. Porosity can be affected by the size of the particles sintered together as well as the time of sintering. In a preferred embodiment of the present invention alumina particles with two different median particle size distributions are used: large particles and small particles. These may be added as separate components of the formulation from which the carrier is formed or they may be generated in situ by milling friable agglomerates until the blend of particle sizes obtains has the desired bimodal distribution. Thus, in theory it is also possible to achieve the carriers of the invention by starting with alumina particles with a single distribution mode.
• the use of a bond material reduces the length of sintering time required to bond the particles together and since sintering is commonly associated with reduction in pore volume, the use of such a bond is a feature of this invention.
• the selection of the bond can also act to produce a more receptive earner surface.
• the bond materials include silica in some form together with an alkali metal component which ensures that the silica is in an amorphous form.
• the preferred alumina hydrate is boehmite though gibbsite, bayerite or diaspore could also be used. It is also preferred that the carrier be prepared in the form of pellets, the size of which is in general determined by the dimensions of the reactor in which they are to be deposited. Generally however it is found very convenient to use pellets in the form of hollow cylinders with length and cross- sectional dimensions about the same and from 5 to 10 mm.
• the pellets can be formed from the mixture by any convenient molding process but preferably they are formed by extrusion of the mixture.
• the mixture is usually compounded with up to about 25% and preferably from 10 to 20% by weight based on the mixture weight of extrusion aids and burnouts and thereafter enough water is added to make the mixture extrudable.
• Extrusion aids are well known in the art and include materials such as vaseline, polyolefin oxides and polyethylene glycol.
• organic bumouts are well known in the art and include materials such as granulated polyolefins, powdered walnut shells and other fine organic particulates.
• extrusion aids are added in the amounts necessary to facilitate extrusion of the specific formulation and this will be influenced by the particle sizes, amount of bond material, (if any) and water present and the design of the extruder.
• the actual amount of extrusion aids to be used is not critical to the final product and appropriate amounts will be readily apparent to the man of skill in the art. They are removed completely upon firing.
• the burnout materials are also added in amounts as desired to cause an increase in the water absorption of the product prepared in accordance with the invention. It is possible that either extrusion aids or bumouts, in appropriate circumstances, could provide the whole of the combined weight of such additives, (as indicated above), that could be added to the formulation.
• the shaped pellets are then dried and fired at a temperature high enough to ensure that the alumina particles are joined together by a sintering action or by the formation of bond posts formed from a bond material incorporated in the mixture or by a mixture of the two mechanisms.
• Generally firing takes place between about 1250 and 1470°C and preferably about 1300 to 1440°C for a period of up to about 5 hours and preferably for from 2 to 4 hours.
• P.V. refers to pore volume
• the carriers of the invention can be prepared in a number of ways that would be understood by the man of skill in the art.
• a preferred carrier (INV-1)
• a mixture was made of the following ingredients, all proportions being by weight as the components exist in the fired carrier: 1. 67.4% of an alpha alumina with an average particle size, (d50), of 29 micrometers;
• silica in the form of an ammonia stabilized silica sol
• sodium oxide in the form of sodium acetate
• silica and sodium acetate were used together with the boehmite to provide a bond conferring green strength.
• To this mixture were added 5% by weight of petroleum jelly, 9%> of a mixture of fine particulate organic burnouts and 0.1% of the mixture weight of boric acid. Water was then added in an amount to make the mixture extrudable and this mixture was then extruded to form hollow cylinders that are about 8mm in diameter and 8mm long. These were then dried and fired in a kiln at 1425°C to produce the porous alumina carrier of the invention.
• the INV-2 carrier was prepared in exactly the same way as INV- 1 except that the mixture contained 14% of the mixture of fine particulate organic burnouts rather than 9%.
• the INV-3 carrier was prepared with 14% of petroleum jelly and 8% fine organic burnouts
• the COMP-A carrier was made according to the process described in Example 1 of USP 5,100, 859.
• the carriers evaluated were all made from aluminas and the proportions and average particle sizes, dso, of these components are shown in the following Table 2. The balance of the proportions, to make 100% was bond material.
• the comparative carrier was then evaluated against the INV.-l carrier of the present invention.
• the carriers were used to prepare ethylene oxide catalysts using the method generally described in USP 5,380,697.
• the performance of the carrier according to the invention was then evaluated against the comparative carriers under equivalent conditions.
• the catalysts were used to produce ethylene oxide from ethylene and oxygen. To do this, 1.5 to 2 g. of crushed catalyst were loaded into a 6.35 mm. inside diameter stainless steel U-shaped tube. The tube was immersed in a molten metal bath (heat medium) and the ends were connected to a gas flow system. The weight of catalyst used and the inlet gas flow rate were adjusted to give a gas hourly space velocity of 6800 cc/cc of catalyst/hr. The inlet gas pressure was 210 psig.
• Performance data at this conversion level are usually obtained when the catalyst has been on stream for a total of at least 1-2 days.
• the catalysts based on the Carrier COMP-A had a selectivity value significantly below that based on the INV- 1 carrier and required much higher temperatures.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• Geology (AREA)
• Inorganic Chemistry (AREA)
• Catalysts (AREA)
• Epoxy Compounds (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Publications (1)

Family

ID=27753171

Family Applications (1)

Country Status (15)

Cited By (11)

Families Citing this family (61)

Citations (5)

Family Cites Families (31)

• 2002
  • 2002-02-25 US US10/082,761 patent/US6831037B2/en not_active Expired - Lifetime
• 2003
  • 2003-01-27 MY MYPI20030266A patent/MY130801A/en unknown
  • 2003-02-07 TW TW092102533A patent/TWI228433B/zh not_active IP Right Cessation
  • 2003-02-25 EP EP03743238.2A patent/EP1478458B1/en not_active Expired - Lifetime
  • 2003-02-25 BR BRPI0307963-5B1A patent/BR0307963B1/pt active IP Right Grant
  • 2003-02-25 JP JP2003570979A patent/JP5139622B2/ja not_active Expired - Lifetime
  • 2003-02-25 RU RU2004126091/04A patent/RU2282497C2/ru not_active IP Right Cessation
  • 2003-02-25 KR KR1020047013272A patent/KR100591031B1/ko not_active Expired - Lifetime
  • 2003-02-25 MX MXPA04008258A patent/MXPA04008258A/es active IP Right Grant
  • 2003-02-25 AU AU2003216412A patent/AU2003216412A1/en not_active Abandoned
  • 2003-02-25 WO PCT/US2003/005719 patent/WO2003072244A1/en not_active Ceased
  • 2003-02-25 CN CNB038079399A patent/CN100531897C/zh not_active Expired - Lifetime
  • 2003-02-25 CA CA002477067A patent/CA2477067C/en not_active Expired - Lifetime
  • 2003-02-25 EP EP17164712.6A patent/EP3254756A1/en not_active Withdrawn
  • 2003-02-25 DK DK03743238.2T patent/DK1478458T3/en active
• 2004
  • 2004-03-08 US US10/795,627 patent/US20040170556A1/en not_active Abandoned
  • 2004-08-24 IN IN1883CH2004 patent/IN2004CH01883A/en unknown
  • 2004-12-13 US US11/010,488 patent/US20050096219A1/en not_active Abandoned
• 2008
  • 2008-12-22 JP JP2008326255A patent/JP2009072787A/ja active Pending

Patent Citations (6)

Also Published As

Similar Documents

Legal Events