WO1995027603A1 - Pieces mecaniques de haute precision en resine ignifuge pour equipement de bureautique - Google Patents
Pieces mecaniques de haute precision en resine ignifuge pour equipement de bureautique Download PDFInfo
- Publication number
- WO1995027603A1 WO1995027603A1 PCT/JP1995/000703 JP9500703W WO9527603A1 WO 1995027603 A1 WO1995027603 A1 WO 1995027603A1 JP 9500703 W JP9500703 W JP 9500703W WO 9527603 A1 WO9527603 A1 WO 9527603A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- precision
- resin
- flame
- parts
- weight
- Prior art date
Links
- 239000003063 flame retardant Substances 0.000 title claims abstract description 49
- RNFJDJUURJAICM-UHFFFAOYSA-N 2,2,4,4,6,6-hexaphenoxy-1,3,5-triaza-2$l^{5},4$l^{5},6$l^{5}-triphosphacyclohexa-1,3,5-triene Chemical compound N=1P(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP=1(OC=1C=CC=CC=1)OC1=CC=CC=C1 RNFJDJUURJAICM-UHFFFAOYSA-N 0.000 title claims abstract description 43
- 229920005989 resin Polymers 0.000 title claims description 92
- 239000011347 resin Substances 0.000 title claims description 92
- 239000011342 resin composition Substances 0.000 claims abstract description 70
- 239000011256 inorganic filler Substances 0.000 claims abstract description 40
- 229910003475 inorganic filler Inorganic materials 0.000 claims abstract description 40
- 238000000465 moulding Methods 0.000 claims abstract description 34
- 229920005992 thermoplastic resin Polymers 0.000 claims abstract description 29
- 238000001746 injection moulding Methods 0.000 claims abstract description 23
- 150000002148 esters Chemical class 0.000 claims abstract description 15
- 239000011521 glass Substances 0.000 claims description 49
- 230000007246 mechanism Effects 0.000 claims description 24
- 238000000034 method Methods 0.000 claims description 20
- 239000007789 gas Substances 0.000 claims description 17
- 239000012763 reinforcing filler Substances 0.000 claims description 15
- 125000004432 carbon atom Chemical group C* 0.000 claims description 8
- 125000004435 hydrogen atom Chemical group [H]* 0.000 claims description 8
- 125000000217 alkyl group Chemical group 0.000 claims description 6
- 239000010445 mica Substances 0.000 claims description 6
- 229910052618 mica group Inorganic materials 0.000 claims description 6
- 125000002496 methyl group Chemical group [H]C([H])([H])* 0.000 claims description 4
- 239000000446 fuel Substances 0.000 claims 1
- IISBACLAFKSPIT-UHFFFAOYSA-N bisphenol A Chemical compound C=1C=C(O)C=CC=1C(C)(C)C1=CC=C(O)C=C1 IISBACLAFKSPIT-UHFFFAOYSA-N 0.000 abstract description 24
- 229930185605 Bisphenol Natural products 0.000 abstract description 9
- 238000004891 communication Methods 0.000 abstract description 4
- 125000002467 phosphate group Chemical group [H]OP(=O)(O[H])O[*] 0.000 abstract description 3
- 230000008901 benefit Effects 0.000 abstract description 2
- 230000000740 bleeding effect Effects 0.000 abstract description 2
- 239000002131 composite material Substances 0.000 abstract description 2
- 230000008020 evaporation Effects 0.000 abstract 1
- 238000001704 evaporation Methods 0.000 abstract 1
- 230000000391 smoking effect Effects 0.000 abstract 1
- 229910019142 PO4 Inorganic materials 0.000 description 41
- 235000021317 phosphate Nutrition 0.000 description 41
- 230000008859 change Effects 0.000 description 40
- 239000010452 phosphate Substances 0.000 description 40
- -1 phosphorus compound Chemical class 0.000 description 38
- NBIIXXVUZAFLBC-UHFFFAOYSA-K phosphate Chemical compound [O-]P([O-])([O-])=O NBIIXXVUZAFLBC-UHFFFAOYSA-K 0.000 description 27
- 238000012360 testing method Methods 0.000 description 22
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N Phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 description 18
- 230000000052 comparative effect Effects 0.000 description 18
- 229920001955 polyphenylene ether Polymers 0.000 description 18
- PPBRXRYQALVLMV-UHFFFAOYSA-N Styrene Chemical compound C=CC1=CC=CC=C1 PPBRXRYQALVLMV-UHFFFAOYSA-N 0.000 description 17
- 238000013461 design Methods 0.000 description 16
- 239000004793 Polystyrene Substances 0.000 description 13
- 150000003014 phosphoric acid esters Chemical class 0.000 description 13
- 229910052751 metal Inorganic materials 0.000 description 12
- 239000002184 metal Substances 0.000 description 12
- 229920013636 polyphenyl ether polymer Polymers 0.000 description 12
- 238000011156 evaluation Methods 0.000 description 11
- 239000000945 filler Substances 0.000 description 11
- 229920002223 polystyrene Polymers 0.000 description 11
- 238000005094 computer simulation Methods 0.000 description 10
- 239000003365 glass fiber Substances 0.000 description 10
- 238000002347 injection Methods 0.000 description 10
- 239000007924 injection Substances 0.000 description 10
- 230000003287 optical effect Effects 0.000 description 10
- 239000004417 polycarbonate Substances 0.000 description 10
- HIXDQWDOVZUNNA-UHFFFAOYSA-N 2-(3,4-dimethoxyphenyl)-5-hydroxy-7-methoxychromen-4-one Chemical compound C=1C(OC)=CC(O)=C(C(C=2)=O)C=1OC=2C1=CC=C(OC)C(OC)=C1 HIXDQWDOVZUNNA-UHFFFAOYSA-N 0.000 description 9
- 239000011324 bead Substances 0.000 description 9
- RTZKZFJDLAIYFH-UHFFFAOYSA-N ether Substances CCOCC RTZKZFJDLAIYFH-UHFFFAOYSA-N 0.000 description 9
- 239000000203 mixture Substances 0.000 description 9
- 229920001577 copolymer Polymers 0.000 description 8
- 238000002845 discoloration Methods 0.000 description 8
- 238000004519 manufacturing process Methods 0.000 description 8
- 229920000642 polymer Polymers 0.000 description 8
- GHMLBKRAJCXXBS-UHFFFAOYSA-N resorcinol Chemical compound OC1=CC=CC(O)=C1 GHMLBKRAJCXXBS-UHFFFAOYSA-N 0.000 description 8
- 239000000779 smoke Substances 0.000 description 8
- 229920000122 acrylonitrile butadiene styrene Polymers 0.000 description 7
- 238000013016 damping Methods 0.000 description 7
- 229910052736 halogen Inorganic materials 0.000 description 7
- 150000002367 halogens Chemical class 0.000 description 7
- 229920005669 high impact polystyrene Polymers 0.000 description 7
- 239000004797 high-impact polystyrene Substances 0.000 description 7
- 229920005668 polycarbonate resin Polymers 0.000 description 7
- 239000004431 polycarbonate resin Substances 0.000 description 7
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 7
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 6
- 150000001875 compounds Chemical class 0.000 description 6
- 229920001971 elastomer Polymers 0.000 description 6
- 238000005259 measurement Methods 0.000 description 6
- 238000002156 mixing Methods 0.000 description 6
- 239000008188 pellet Substances 0.000 description 6
- 229920000388 Polyphosphate Polymers 0.000 description 5
- 229910052782 aluminium Inorganic materials 0.000 description 5
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 5
- 229910052739 hydrogen Inorganic materials 0.000 description 5
- 239000001257 hydrogen Substances 0.000 description 5
- 230000001771 impaired effect Effects 0.000 description 5
- 150000002989 phenols Chemical class 0.000 description 5
- 230000000704 physical effect Effects 0.000 description 5
- 239000001205 polyphosphate Substances 0.000 description 5
- 235000011176 polyphosphates Nutrition 0.000 description 5
- QIGBRXMKCJKVMJ-UHFFFAOYSA-N Hydroquinone Chemical compound OC1=CC=C(O)C=C1 QIGBRXMKCJKVMJ-UHFFFAOYSA-N 0.000 description 4
- NBIIXXVUZAFLBC-UHFFFAOYSA-N Phosphoric acid Chemical compound OP(O)(O)=O NBIIXXVUZAFLBC-UHFFFAOYSA-N 0.000 description 4
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 4
- 238000010521 absorption reaction Methods 0.000 description 4
- 238000006243 chemical reaction Methods 0.000 description 4
- 229920003023 plastic Polymers 0.000 description 4
- 239000004033 plastic Substances 0.000 description 4
- 239000002243 precursor Substances 0.000 description 4
- VPWNQTHUCYMVMZ-UHFFFAOYSA-N 4,4'-sulfonyldiphenol Chemical class C1=CC(O)=CC=C1S(=O)(=O)C1=CC=C(O)C=C1 VPWNQTHUCYMVMZ-UHFFFAOYSA-N 0.000 description 3
- 125000004203 4-hydroxyphenyl group Chemical group [H]OC1=C([H])C([H])=C(*)C([H])=C1[H] 0.000 description 3
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 description 3
- YMWUJEATGCHHMB-UHFFFAOYSA-N Dichloromethane Chemical compound ClCCl YMWUJEATGCHHMB-UHFFFAOYSA-N 0.000 description 3
- WSFSSNUMVMOOMR-UHFFFAOYSA-N Formaldehyde Chemical compound O=C WSFSSNUMVMOOMR-UHFFFAOYSA-N 0.000 description 3
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 3
- 239000005062 Polybutadiene Substances 0.000 description 3
- 239000007864 aqueous solution Substances 0.000 description 3
- 125000003118 aryl group Chemical group 0.000 description 3
- 238000000354 decomposition reaction Methods 0.000 description 3
- 230000006866 deterioration Effects 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 239000000806 elastomer Substances 0.000 description 3
- 229910052742 iron Inorganic materials 0.000 description 3
- 239000000463 material Substances 0.000 description 3
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 description 3
- 229910052698 phosphorus Inorganic materials 0.000 description 3
- 239000011574 phosphorus Substances 0.000 description 3
- 229920002285 poly(styrene-co-acrylonitrile) Polymers 0.000 description 3
- 229920002857 polybutadiene Polymers 0.000 description 3
- 229920000515 polycarbonate Polymers 0.000 description 3
- 238000006116 polymerization reaction Methods 0.000 description 3
- 229920005990 polystyrene resin Polymers 0.000 description 3
- 238000007639 printing Methods 0.000 description 3
- 239000005060 rubber Substances 0.000 description 3
- 229920003048 styrene butadiene rubber Polymers 0.000 description 3
- QQOMQLYQAXGHSU-UHFFFAOYSA-N 2,3,6-Trimethylphenol Chemical compound CC1=CC=C(C)C(O)=C1C QQOMQLYQAXGHSU-UHFFFAOYSA-N 0.000 description 2
- NXXYKOUNUYWIHA-UHFFFAOYSA-N 2,6-Dimethylphenol Chemical compound CC1=CC=CC(C)=C1O NXXYKOUNUYWIHA-UHFFFAOYSA-N 0.000 description 2
- QTWJRLJHJPIABL-UHFFFAOYSA-N 2-methylphenol;3-methylphenol;4-methylphenol Chemical compound CC1=CC=C(O)C=C1.CC1=CC=CC(O)=C1.CC1=CC=CC=C1O QTWJRLJHJPIABL-UHFFFAOYSA-N 0.000 description 2
- VEORPZCZECFIRK-UHFFFAOYSA-N 3,3',5,5'-tetrabromobisphenol A Chemical compound C=1C(Br)=C(O)C(Br)=CC=1C(C)(C)C1=CC(Br)=C(O)C(Br)=C1 VEORPZCZECFIRK-UHFFFAOYSA-N 0.000 description 2
- JDCCCHBBXRQRGU-UHFFFAOYSA-N 5-phenylpenta-2,4-dienenitrile Chemical class N#CC=CC=CC1=CC=CC=C1 JDCCCHBBXRQRGU-UHFFFAOYSA-N 0.000 description 2
- CIWBSHSKHKDKBQ-JLAZNSOCSA-N Ascorbic acid Chemical compound OC[C@H](O)[C@H]1OC(=O)C(O)=C1O CIWBSHSKHKDKBQ-JLAZNSOCSA-N 0.000 description 2
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 2
- KAKZBPTYRLMSJV-UHFFFAOYSA-N Butadiene Chemical compound C=CC=C KAKZBPTYRLMSJV-UHFFFAOYSA-N 0.000 description 2
- VTYYLEPIZMXCLO-UHFFFAOYSA-L Calcium carbonate Chemical compound [Ca+2].[O-]C([O-])=O VTYYLEPIZMXCLO-UHFFFAOYSA-L 0.000 description 2
- RRHGJUQNOFWUDK-UHFFFAOYSA-N Isoprene Chemical compound CC(=C)C=C RRHGJUQNOFWUDK-UHFFFAOYSA-N 0.000 description 2
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 description 2
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 description 2
- YSMRWXYRXBRSND-UHFFFAOYSA-N TOTP Chemical compound CC1=CC=CC=C1OP(=O)(OC=1C(=CC=CC=1)C)OC1=CC=CC=C1C YSMRWXYRXBRSND-UHFFFAOYSA-N 0.000 description 2
- 230000002378 acidificating effect Effects 0.000 description 2
- 229910000147 aluminium phosphate Inorganic materials 0.000 description 2
- ADCOVFLJGNWWNZ-UHFFFAOYSA-N antimony trioxide Chemical compound O=[Sb]O[Sb]=O ADCOVFLJGNWWNZ-UHFFFAOYSA-N 0.000 description 2
- 125000004429 atom Chemical group 0.000 description 2
- PXKLMJQFEQBVLD-UHFFFAOYSA-N bisphenol F Chemical compound C1=CC(O)=CC=C1CC1=CC=C(O)C=C1 PXKLMJQFEQBVLD-UHFFFAOYSA-N 0.000 description 2
- 229910052799 carbon Inorganic materials 0.000 description 2
- 238000002485 combustion reaction Methods 0.000 description 2
- 238000007796 conventional method Methods 0.000 description 2
- 230000002596 correlated effect Effects 0.000 description 2
- 230000000875 corresponding effect Effects 0.000 description 2
- 230000007797 corrosion Effects 0.000 description 2
- 238000005260 corrosion Methods 0.000 description 2
- 229930003836 cresol Natural products 0.000 description 2
- 239000012153 distilled water Substances 0.000 description 2
- 238000005516 engineering process Methods 0.000 description 2
- 230000007613 environmental effect Effects 0.000 description 2
- 125000004185 ester group Chemical group 0.000 description 2
- 238000001125 extrusion Methods 0.000 description 2
- 239000000835 fiber Substances 0.000 description 2
- 229920001519 homopolymer Polymers 0.000 description 2
- 230000006872 improvement Effects 0.000 description 2
- 238000004898 kneading Methods 0.000 description 2
- 239000004816 latex Substances 0.000 description 2
- 229920000126 latex Polymers 0.000 description 2
- 239000007788 liquid Substances 0.000 description 2
- 230000007774 longterm Effects 0.000 description 2
- FPYJFEHAWHCUMM-UHFFFAOYSA-N maleic anhydride Chemical compound O=C1OC(=O)C=C1 FPYJFEHAWHCUMM-UHFFFAOYSA-N 0.000 description 2
- 239000007769 metal material Substances 0.000 description 2
- 125000000843 phenylene group Chemical group C1(=C(C=CC=C1)*)* 0.000 description 2
- 229920000098 polyolefin Polymers 0.000 description 2
- 229920006389 polyphenyl polymer Polymers 0.000 description 2
- 239000011591 potassium Substances 0.000 description 2
- 229910052700 potassium Inorganic materials 0.000 description 2
- FZHAPNGMFPVSLP-UHFFFAOYSA-N silanamine Chemical compound [SiH3]N FZHAPNGMFPVSLP-UHFFFAOYSA-N 0.000 description 2
- 239000002904 solvent Substances 0.000 description 2
- 239000003381 stabilizer Substances 0.000 description 2
- 150000003440 styrenes Chemical class 0.000 description 2
- XZZNDPSIHUTMOC-UHFFFAOYSA-N triphenyl phosphate Chemical compound C=1C=CC=CC=1OP(OC=1C=CC=CC=1)(=O)OC1=CC=CC=C1 XZZNDPSIHUTMOC-UHFFFAOYSA-N 0.000 description 2
- 210000000689 upper leg Anatomy 0.000 description 2
- 229920002554 vinyl polymer Polymers 0.000 description 2
- 230000000007 visual effect Effects 0.000 description 2
- MFFNRVNPBJQZFO-UHFFFAOYSA-N (2,6-dimethylphenyl) dihydrogen phosphate Chemical compound CC1=CC=CC(C)=C1OP(O)(O)=O MFFNRVNPBJQZFO-UHFFFAOYSA-N 0.000 description 1
- 125000001140 1,4-phenylene group Chemical group [H]C1=C([H])C([*:2])=C([H])C([H])=C1[*:1] 0.000 description 1
- QEDJMOONZLUIMC-UHFFFAOYSA-N 1-tert-butyl-4-ethenylbenzene Chemical compound CC(C)(C)C1=CC=C(C=C)C=C1 QEDJMOONZLUIMC-UHFFFAOYSA-N 0.000 description 1
- XRUGBBIQLIVCSI-UHFFFAOYSA-N 2,3,4-trimethylphenol Chemical compound CC1=CC=C(O)C(C)=C1C XRUGBBIQLIVCSI-UHFFFAOYSA-N 0.000 description 1
- QWBBPBRQALCEIZ-UHFFFAOYSA-N 2,3-dimethylphenol Chemical compound CC1=CC=CC(O)=C1C QWBBPBRQALCEIZ-UHFFFAOYSA-N 0.000 description 1
- KXGFMDJXCMQABM-UHFFFAOYSA-N 2-methoxy-6-methylphenol Chemical compound [CH]OC1=CC=CC([CH])=C1O KXGFMDJXCMQABM-UHFFFAOYSA-N 0.000 description 1
- NZGQHKSLKRFZFL-UHFFFAOYSA-N 4-(4-hydroxyphenoxy)phenol Chemical compound C1=CC(O)=CC=C1OC1=CC=C(O)C=C1 NZGQHKSLKRFZFL-UHFFFAOYSA-N 0.000 description 1
- JLBJTVDPSNHSKJ-UHFFFAOYSA-N 4-Methylstyrene Chemical compound CC1=CC=C(C=C)C=C1 JLBJTVDPSNHSKJ-UHFFFAOYSA-N 0.000 description 1
- HXDOZKJGKXYMEW-UHFFFAOYSA-N 4-ethylphenol Chemical compound CCC1=CC=C(O)C=C1 HXDOZKJGKXYMEW-UHFFFAOYSA-N 0.000 description 1
- WISWLZYHZLVSMO-UHFFFAOYSA-N 6-phenyl-2-(4-phenylphenyl)-1,3-benzoxazole Chemical compound C1=CC=CC=C1C1=CC=C(C=2OC3=CC(=CC=C3N=2)C=2C=CC=CC=2)C=C1 WISWLZYHZLVSMO-UHFFFAOYSA-N 0.000 description 1
- DUGLMATUSUVYMV-UHFFFAOYSA-N 7-oxabicyclo[2.2.1]hepta-1,3,5-triene Chemical compound C1=C(O2)C=CC2=C1 DUGLMATUSUVYMV-UHFFFAOYSA-N 0.000 description 1
- NLHHRLWOUZZQLW-UHFFFAOYSA-N Acrylonitrile Chemical compound C=CC#N NLHHRLWOUZZQLW-UHFFFAOYSA-N 0.000 description 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- 229920000049 Carbon (fiber) Polymers 0.000 description 1
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 1
- KCXVZYZYPLLWCC-UHFFFAOYSA-N EDTA Chemical compound OC(=O)CN(CC(O)=O)CCN(CC(O)=O)CC(O)=O KCXVZYZYPLLWCC-UHFFFAOYSA-N 0.000 description 1
- 229920000181 Ethylene propylene rubber Polymers 0.000 description 1
- 244000043261 Hevea brasiliensis Species 0.000 description 1
- CERQOIWHTDAKMF-UHFFFAOYSA-N Methacrylic acid Chemical compound CC(=C)C(O)=O CERQOIWHTDAKMF-UHFFFAOYSA-N 0.000 description 1
- VVQNEPGJFQJSBK-UHFFFAOYSA-N Methyl methacrylate Chemical compound COC(=O)C(C)=C VVQNEPGJFQJSBK-UHFFFAOYSA-N 0.000 description 1
- NHDHWGAUSXSAEF-UHFFFAOYSA-N P(=O)(O)(O)O.P(=O)(O)(O)O.P(=O)(O)(O)O.C=1(O)C(O)=CC=CC1 Chemical compound P(=O)(O)(O)O.P(=O)(O)(O)O.P(=O)(O)(O)O.C=1(O)C(O)=CC=CC1 NHDHWGAUSXSAEF-UHFFFAOYSA-N 0.000 description 1
- YGYAWVDWMABLBF-UHFFFAOYSA-N Phosgene Chemical compound ClC(Cl)=O YGYAWVDWMABLBF-UHFFFAOYSA-N 0.000 description 1
- 239000004698 Polyethylene Substances 0.000 description 1
- BLRPTPMANUNPDV-UHFFFAOYSA-N Silane Chemical compound [SiH4] BLRPTPMANUNPDV-UHFFFAOYSA-N 0.000 description 1
- 239000002174 Styrene-butadiene Substances 0.000 description 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 1
- SNWNLRQYQRTOBP-UHFFFAOYSA-N [O--].[S--].[Zn++].[Zn++] Chemical compound [O--].[S--].[Zn++].[Zn++] SNWNLRQYQRTOBP-UHFFFAOYSA-N 0.000 description 1
- 239000002253 acid Substances 0.000 description 1
- 150000008065 acid anhydrides Chemical class 0.000 description 1
- 229920000800 acrylic rubber Polymers 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 150000001335 aliphatic alkanes Chemical class 0.000 description 1
- 125000002947 alkylene group Chemical group 0.000 description 1
- XYLMUPLGERFSHI-UHFFFAOYSA-N alpha-Methylstyrene Chemical class CC(=C)C1=CC=CC=C1 XYLMUPLGERFSHI-UHFFFAOYSA-N 0.000 description 1
- 238000000137 annealing Methods 0.000 description 1
- 239000003963 antioxidant agent Substances 0.000 description 1
- 150000001491 aromatic compounds Chemical class 0.000 description 1
- 229920006164 aromatic vinyl copolymer Polymers 0.000 description 1
- VCCBEIPGXKNHFW-UHFFFAOYSA-N biphenyl-4,4'-diol Chemical group C1=CC(O)=CC=C1C1=CC=C(O)C=C1 VCCBEIPGXKNHFW-UHFFFAOYSA-N 0.000 description 1
- MTAZNLWOLGHBHU-UHFFFAOYSA-N butadiene-styrene rubber Chemical compound C=CC=C.C=CC1=CC=CC=C1 MTAZNLWOLGHBHU-UHFFFAOYSA-N 0.000 description 1
- 229910000019 calcium carbonate Inorganic materials 0.000 description 1
- 238000004364 calculation method Methods 0.000 description 1
- 239000006229 carbon black Substances 0.000 description 1
- 239000004917 carbon fiber Substances 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- 239000003795 chemical substances by application Substances 0.000 description 1
- 239000003086 colorant Substances 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 239000007822 coupling agent Substances 0.000 description 1
- 238000005336 cracking Methods 0.000 description 1
- 238000005520 cutting process Methods 0.000 description 1
- 230000003247 decreasing effect Effects 0.000 description 1
- 125000000664 diazo group Chemical group [N-]=[N+]=[*] 0.000 description 1
- 238000004512 die casting Methods 0.000 description 1
- ROORDVPLFPIABK-UHFFFAOYSA-N diphenyl carbonate Chemical compound C=1C=CC=CC=1OC(=O)OC1=CC=CC=C1 ROORDVPLFPIABK-UHFFFAOYSA-N 0.000 description 1
- WNAHIZMDSQCWRP-UHFFFAOYSA-N dodecane-1-thiol Chemical compound CCCCCCCCCCCCS WNAHIZMDSQCWRP-UHFFFAOYSA-N 0.000 description 1
- 239000003995 emulsifying agent Substances 0.000 description 1
- 229920006351 engineering plastic Polymers 0.000 description 1
- SUPCQIBBMFXVTL-UHFFFAOYSA-N ethyl 2-methylprop-2-enoate Chemical compound CCOC(=O)C(C)=C SUPCQIBBMFXVTL-UHFFFAOYSA-N 0.000 description 1
- 239000011790 ferrous sulphate Substances 0.000 description 1
- 235000003891 ferrous sulphate Nutrition 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 239000012530 fluid Substances 0.000 description 1
- 238000001879 gelation Methods 0.000 description 1
- 230000009477 glass transition Effects 0.000 description 1
- 229920000578 graft copolymer Polymers 0.000 description 1
- 230000012447 hatching Effects 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 230000007062 hydrolysis Effects 0.000 description 1
- 238000006460 hydrolysis reaction Methods 0.000 description 1
- BAUYGSIQEAFULO-UHFFFAOYSA-L iron(2+) sulfate (anhydrous) Chemical compound [Fe+2].[O-]S([O-])(=O)=O BAUYGSIQEAFULO-UHFFFAOYSA-L 0.000 description 1
- 229910000359 iron(II) sulfate Inorganic materials 0.000 description 1
- 239000000314 lubricant Substances 0.000 description 1
- 230000005389 magnetism Effects 0.000 description 1
- 125000005397 methacrylic acid ester group Chemical group 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 229920003052 natural elastomer Polymers 0.000 description 1
- 229920001194 natural rubber Polymers 0.000 description 1
- 229910052757 nitrogen Inorganic materials 0.000 description 1
- 229920003986 novolac Polymers 0.000 description 1
- 150000002903 organophosphorus compounds Chemical class 0.000 description 1
- 230000010355 oscillation Effects 0.000 description 1
- 239000002245 particle Substances 0.000 description 1
- 150000002978 peroxides Chemical class 0.000 description 1
- 239000005011 phenolic resin Substances 0.000 description 1
- 229920001568 phenolic resin Polymers 0.000 description 1
- CMPQUABWPXYYSH-UHFFFAOYSA-N phenyl phosphate Chemical compound OP(O)(=O)OC1=CC=CC=C1 CMPQUABWPXYYSH-UHFFFAOYSA-N 0.000 description 1
- 150000003013 phosphoric acid derivatives Chemical class 0.000 description 1
- 125000002270 phosphoric acid ester group Chemical group 0.000 description 1
- OXHXATNDTXVKAU-UHFFFAOYSA-N phosphoric acid zinc Chemical class [Zn].OP(O)(O)=O OXHXATNDTXVKAU-UHFFFAOYSA-N 0.000 description 1
- 150000003017 phosphorus Chemical class 0.000 description 1
- 150000003018 phosphorus compounds Chemical class 0.000 description 1
- 229920000058 polyacrylate Polymers 0.000 description 1
- 229920006122 polyamide resin Polymers 0.000 description 1
- 229920001707 polybutylene terephthalate Polymers 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 229920000573 polyethylene Polymers 0.000 description 1
- 229920000139 polyethylene terephthalate Polymers 0.000 description 1
- 239000005020 polyethylene terephthalate Substances 0.000 description 1
- 229920002451 polyvinyl alcohol Polymers 0.000 description 1
- USHAGKDGDHPEEY-UHFFFAOYSA-L potassium persulfate Chemical compound [K+].[K+].[O-]S(=O)(=O)OOS([O-])(=O)=O USHAGKDGDHPEEY-UHFFFAOYSA-L 0.000 description 1
- 230000008569 process Effects 0.000 description 1
- 238000010298 pulverizing process Methods 0.000 description 1
- 238000010926 purge Methods 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 239000002990 reinforced plastic Substances 0.000 description 1
- 239000012744 reinforcing agent Substances 0.000 description 1
- 230000003014 reinforcing effect Effects 0.000 description 1
- 230000004044 response Effects 0.000 description 1
- 150000003839 salts Chemical class 0.000 description 1
- 229920006395 saturated elastomer Polymers 0.000 description 1
- 229910000077 silane Inorganic materials 0.000 description 1
- 239000000344 soap Substances 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 238000003756 stirring Methods 0.000 description 1
- 239000011115 styrene butadiene Substances 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
- 125000001424 substituent group Chemical group 0.000 description 1
- 230000001629 suppression Effects 0.000 description 1
- 230000008961 swelling Effects 0.000 description 1
- 238000009864 tensile test Methods 0.000 description 1
- 238000010998 test method Methods 0.000 description 1
- 229920001169 thermoplastic Polymers 0.000 description 1
- 229920002725 thermoplastic elastomer Polymers 0.000 description 1
- 239000004416 thermosoftening plastic Substances 0.000 description 1
- AYEKOFBPNLCAJY-UHFFFAOYSA-O thiamine pyrophosphate Chemical compound CC1=C(CCOP(O)(=O)OP(O)(O)=O)SC=[N+]1CC1=CN=C(C)N=C1N AYEKOFBPNLCAJY-UHFFFAOYSA-O 0.000 description 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 description 1
- 238000005809 transesterification reaction Methods 0.000 description 1
- QLORRTLBSJTMSN-UHFFFAOYSA-N tris(2,6-dimethylphenyl) phosphate Chemical compound CC1=CC=CC(C)=C1OP(=O)(OC=1C(=CC=CC=1C)C)OC1=C(C)C=CC=C1C QLORRTLBSJTMSN-UHFFFAOYSA-N 0.000 description 1
- 238000011179 visual inspection Methods 0.000 description 1
- 239000011800 void material Substances 0.000 description 1
- 239000013585 weight reducing agent Substances 0.000 description 1
- 150000003739 xylenols Chemical class 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
- B29C45/0001—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor characterised by the choice of material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
- B29C45/0013—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor using fillers dispersed in the moulding material, e.g. metal particles
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/49—Phosphorus-containing compounds
- C08K5/51—Phosphorus bound to oxygen
- C08K5/52—Phosphorus bound to oxygen only
- C08K5/521—Esters of phosphoric acids, e.g. of H3PO4
- C08K5/523—Esters of phosphoric acids, e.g. of H3PO4 with hydroxyaryl compounds
Definitions
- the present invention relates to a flame-retardant resin mechanism component for OA equipment, which is injection-molded from a thermoplastic resin composition. More specifically, the present invention is directed to a thermoplastic resin composition containing (A) an amorphous thermoplastic resin, (B) a scaly inorganic filler, and (C) a specific phosphate. It relates to high-precision mechanical parts made of molded flame-retardant resin for OA equipment that are required to function with high accuracy and precision.
- the high-precision mechanism component of the present invention has no smoke emission, volatilization and MD (mold deposit) of the flame retardant during molding, and has no flame retardant bleed during use.
- the high-precision mechanism component of the present invention has high accuracy because of its low anti-reduction molding shrinkage, and has extremely low linear expansion coefficient anisotropy and excellent vibration characteristics. Mechanical properties.
- the high-precision mechanism parts of the present invention include, for example, a computer, a game machine, a music player AV device, a copier, a printer, a facsimile, a personal computer, a word processor, a portable communication device, It can be used very advantageously for precision equipment that needs to function with high accuracy and precision in various environments, such as those complex equipment.
- thermoplastic resins with excellent mechanical properties and moldability such as polyphenylene ether-based flame-retardant resins and polycarbonate-based flame-retardant resins.
- sheet metal and aluminum die cast have been used, but the use of resin for the above mechanical parts has been studied.
- the characteristics required for resin-made OA equipment components are molding properties, mechanical properties (rigidity, strength), heat resistance, flame resistance, dimensional accuracy, and dimensional stability.
- non-crystalline thermoplastic resins other than polyphenylene ether-based resins include well-known aromatic haeogen compounds, such as tetrabromobisphenol A (TBA) and poly (vinyl alcohol).
- Bromobifenyloxide (PBBO) is widely used, but in recent years it has been difficult to use it together with halogen-based flame retardants and halogen-based flame retardants due to environmental impacts and safety issues on the human body. ⁇ obtain refrain the use of antimony trioxide is retardant auxiliary (S b 2 ⁇ 3) request has increased.
- Polyphenylene ether resin compositions and polycarbonate resin compositions using a phosphorus compound as a non-halogen flame retardant are known (GB Publication No. 20443083, U.S. Pat. No. 5,204,394).
- Organic phosphoric acid ester compounds for example, triphenylenophosphate, cresinolesifeninophosphate, tricresyl phosphate, and the like are widely used industrially.
- such additives that are conventionally used cause smoke and volatilization during molding, generate MD (mold deposit) on the mold cavity wall, and cause the surface of the molded article to be undesired.
- the flame retardant had disadvantages such as discoloration, swelling, and cracking caused by bleeding. '
- molding products have problems such as corrosion of molds during molding, and under high temperature and high humidity conditions, electrical characteristics, flame retardancy, and product appearance deteriorate due to water absorption, modification of flame retardants, etc.
- drawbacks such as poor heat and moisture resistance.
- the conventional technology has various problems, and it has not been possible to replace a metal mechanical component for OA equipment with a resin using a non-halogen flame retardant. It has been difficult to obtain mechanical parts for OA equipment with excellent mechanical properties, dimensional accuracy, moldability, and flame retardancy using resin compositions containing non-halogen flame retardants.
- a scaly inorganic filler such as glass flakes and a specific phosphoric acid having a structure in which a phosphate group is bonded via bisphenol to non-crystalline thermoplastic resin
- the mechanical parts obtained by injection molding a thermoplastic resin composition containing an ester as a flame retardant surprisingly have no smoke emission, volatilization and MD (mo Id deposit) of the flame retardant during molding. Also, when used, there is no flame retardant bleed.
- one of the main objects of the present invention is to replace mechanical parts made of sheet metal and aluminum die-cast as mechanical parts for OA equipment that require not only excellent mechanical properties but also high dimensional accuracy and precision.
- An object of the present invention is to provide a high-precision mechanical component made of a flame-retardant reinforced resin that can be used.
- FIG. 1 (a) is a perspective view of a tray-shaped mechanical component formed in Examples 1 to 30;
- FIG. 1 (b) is a cross-sectional view of the tray-shaped mechanism component of FIG. 1 (a) along the line IB-IB;
- FIG. 2 is a perspective view of a mechanical component, which is a chassis for holding an optical element, formed in Examples 31 to 36.
- a to F Measurement points of dimensional accuracy [For A to D, measure the clearance with the surface plate. For E and F, use the design values (4.1 mm and 6.1 mm) shown in Fig. 1 (b). The gap was examined. ]
- hatched area indicates the point where flatness was measured.
- the present invention provides a flame-retardant resin high-precision mechanism component for OA equipment, which is required to function with high accuracy and high precision, which is injection-molded from a thermoplastic resin composition including:
- QQ 2 , Q 3 , and Q 4 each independently represent an alkyl group having 1 to 6 carbon atoms or a hydrogen atom
- R 1 , R 2 , R 3 , and R 4 each independently represent a methyl group or a hydrogen atom.
- n represents an integer of 1 or more
- nl and n2 each independently represent an integer of 0 to 2
- ml, m2, m3, and m4 each independently represent an integer of 1 to 3.
- thermoplastic resin composition containing 3 to 50 phosphoric acid esters represented by the general formula (I).
- High precision mechanical parts made of flame-retardant resin for OA equipment.
- QQ 2 , Q 3 , and Q 4 each independently represent an alkyl group having 1 to 6 carbon atoms or a hydrogen atom
- I 1 , R 2 , R 3 , and R 4 each independently represent a methyl group or a hydrogen atom.
- n represents an integer of 1 or more
- nl and n 2 each independently represent an integer of 0 to 2
- ml, m 2, m 3 and m 4 each independently represent an integer of 1 to 3 Represents.
- thermoplastic resin composition further includes a fibrous reinforced filler, and the total weight of the scaly inorganic filler and the fibrous reinforced filler is 150 parts by weight or less. High-precision mechanism parts made of the flame-retardant resin described.
- the ratio of the fibrous reinforced filler is 25 to 75 weight based on the total weight of the scaly inorganic filler and the fibrous reinforced filler. 6.
- the high-precision mechanical part made of flame-retardant resin according to the above item 6, wherein the ratio is / 0 .
- the non-crystalline thermoplastic resin composition constituting the high-precision mechanical component for the 0 A device of the present invention contains a scaly inorganic filler. is necessary. Specific examples of the scaly inorganic filler include glass flake and my strength.
- the resin composition has a long diameter in the resin composition of l OOO jm or less, preferably in a range of 1 to 500 ⁇ , and a weight average aspect ratio.
- the ratio (the ratio of the weight average major axis to the weight average thickness) is 5 or more, preferably 10 or more, and more preferably 30 or more.
- Examples of commercially available flaky glass flakes which can be preferably used in the present invention include Micro Glass Flaker (trademark of glass flakes sold by Nihon Sheet Glass Co., Ltd., Japan). As the glass flakes, commercially available glass flakes can be used as they are, but they may be used after appropriately pulverizing them before blending with the resin.
- the above glass flake has a long diameter
- the above glass flakes For the purpose of improving the affinity with the resin, glass flakes surface-treated with various coupling agents such as silane (for example, aminosilane) and titanate can also be used.
- the my strength used in the present invention is scaly, and, for example, Szolite Mica (trademark of Sica Lite Mica, Canada) can be used favorably.
- the flakes in the resin composition preferably have a weight average diameter of 100 m or less, preferably 500 yum or less, and more preferably 20 Oum or less.
- the cut ratio (weight average diameter of the flakes Z weight average thickness) is 10 or more, preferably 30 or more, and more preferably 100 or more in terms of imparting rigidity.
- the lower limit of the weight average diameter of commercially available My-power flakes is about 2 Om.
- the glass flakes when the my force is mixed with other components to prepare a resin composition, the my force is broken and the size is reduced.
- the size of my force in the resin composition can be measured in the same manner as in the case of glass flakes.
- the above-mentioned my strength in order to improve the affinity with the resin, for example, the my strength whose surface has been treated with the above-mentioned cutting agent can be particularly preferably used.
- the resin composition constituting the OA equipment mechanism component of the present invention is composed of 100 to 150 parts by weight of the amorphous thermoplastic resin and 5 to 150 parts by weight, preferably 10 to 100 parts by weight of the scaly inorganic filler.
- a resin composition having a filler content of 20 to 70 parts by weight has the best balance of moldability, thermal properties, mechanical properties, dimensional accuracy, and the like.
- the thermoplastic resin composition in order to improve the strength of the mechanical component, can further include a fibrous reinforcing filler, in which case, the scaly inorganic filler and the fibrous reinforcing filler are used. Is less than 150 parts by weight based on 100 parts by weight of the amorphous thermoplastic resin.
- examples of the usage of the inorganic filler and the fibrous reinforcing filler include a scaly glass flake alone, a combination of a glass flake and a fibrous reinforced filler, and a combination of a glass flake and a my reinforcing filler.
- my force alone the mechanical parts obtained have high dimensional accuracy, but the mechanical properties, especially the Izod impact strength, tend to decrease. Therefore, when using my force as the scaly inorganic filler, it is preferable to use it in combination with at least one selected from glass flakes and fibrous reinforced fillers.
- fibrous reinforcing filler used in combination with the scaly inorganic filler
- fibrous reinforcing agents such as glass fiber, carbon fiber, ceramic fiber, and metal fiber.
- fibrous reinforced filler Glass fibers are most preferred in view of the balance of cost, moldability, and mechanical properties of the resin composition containing the same.
- the diameter and average length of the glass fiber are most preferred in view of the balance of cost, moldability, and mechanical properties of the resin composition containing the same.
- the diameter and average length of the glass fiber is relatively short in terms of dimensional accuracy.
- the average length of the glass fiber in the resin composition is preferably 0.1 to 1 mm, more preferably 0.15 to 0.7 mm.
- a fibrous reinforcing filler is used, its amount is preferably 25-75% by weight, more preferably 25%, based on the total weight of the scaly inorganic filler and the fibrous reinforcing filler. ⁇ 50 weight. / 0 . If the amount of the fibrous reinforcing filler exceeds 75% by weight, the dimensional accuracy (molding shrinkage, linear expansion coefficient anisotropy) cannot be sufficiently improved.
- the phosphate used in the present invention is represented by the above general formula (I).
- Q 1 Q 2 , Q 3 and Q 4 are preferably each a methyl group.
- n is an integer of 1 or more, and the heat resistance and processability of the obtained resin composition differ depending on the number of n. Specifically, as n increases, the heat resistance of the resin composition increases, and the processability tends to decrease. On the other hand, when n becomes small, the opposite tendency occurs.
- the preferred range for n is 1-5.
- the phosphoric ester may be a mixture of n-mers.
- the phosphoric acid ester represented by the general formula (I) Ters can be used alone or in combination.
- the above-mentioned phosphoric ester used has a structure in which a phosphoric ester group is bonded via bisphenol and a terminal structure of a monofunctional phenol.
- bisphenols examples include 2,2-bis (4-hydroxyphenyl) propane (commonly known as bisphenol A), 2,2-bis (4-hydroxy-13-methyl phenyl) prononone, bis (4—Hydroxyphenyl) methane, bis (4—Hydroxy-1,3,5-dimethyldimethylphenyl) methane, 1,1bis
- Bisphenols such as (4—hydroxyphenyl) ethane are listed.
- Bisphenol A is particularly preferred.
- Examples of monofunctional phenols include phenol, monoalkylphenol, dialkylphenol, and trialkylphenol. These can be used alone or as a mixture of two or more. Particularly preferred are phenol, cresol, dimethylphenol (mixed xylenol), 2,6-dimethylphenol and trimethylphenol.
- the phosphoric acid ester has a structure in which the phosphoric acid ester group is bonded via bisphenol, and thus the volatility is increased. It has been greatly reduced.
- phosphate groups are bonded via conventional polyphosphates such as resorcinol and hydroquinone. The following advanced performance, which could not be achieved with the above, is shown.
- a product obtained by molding the resin composition constituting the present invention is a product formed from a resin composition using a conventional polyphosphate, which is a discoloration or a color change generated under high temperature and high humidity conditions. Deterioration of appearance such as blisters can be suppressed.
- a product formed from a resin composition containing a phosphoric acid ester using monoalkyl phenol, dialkyl phenol, or trialkyl phenol as a monofunctional phenol As compared with the case of using a phosphate compound having a terminal structure of an unsubstituted monofunctional phenol, thermal stability and hydrolysis resistance are further improved.
- the phosphoric ester used in the present invention has both the structure in which the phosphoric ester group is bonded via bisphenols and the terminal structure of the alkyl-substituted monofunctional phenol,
- the resulting molded article shows excellent properties that maintain its initial electrical properties, flame retardancy, and appearance even when it comes into contact with moisture in a heated atmosphere.
- a part where the molding machine comes into contact with the resin composition due to an acidic component generated by the decomposition of the phosphate ester that is, a metal member such as a barrel or a screw, or an inner wall surface of a mold cavity.
- a metal member such as a barrel or a screw, or an inner wall surface of a mold cavity.
- the high-precision mechanical parts of the present invention have not only no hydrolyzability in a high-temperature and high-humidity environment, but also excellent heat stability during molding, and smoke, volatilization, and MD during molding. Not only does it not deteriorate electrical properties, flame retardancy, and appearance due to water absorption and water absorption, but also significantly reduces the decomposability of the resin composition and makes contact with metal parts and molded products of molding machinery. Corrosion of the metal parts that solves the problem.
- the phosphoric ester represented by the formula (I) is obtained by converting bisphenol and monofunctional phenol to oxychlorinated phosphorus. It can be obtained by reacting.
- the method for producing the phosphoric acid ester represented by the formula (I) for example, US Pat. No. 3,492,373 can be referred to.
- the amount of the phosphate is 100 parts by weight of the amorphous thermoplastic resin, and 3 to 50 parts by weight. Preferably, it is 5 to 20 parts by weight. If the amount of the phosphoric acid ester is smaller than the above range, the flame retardancy is insufficient, and if it is too large, the heat resistance is impaired, which is not preferred.
- a phosphate other than the phosphate represented by the formula (I) may be contained as long as the effects of the invention are not impaired.
- the total weight of the phosphate represented by the formula (I) and the other phosphates is 3 to 50 parts by weight based on 100 parts by weight of the component (A).
- the amount of the other phosphoric ester is generally 50% by weight or less, preferably 30% by weight, based on the total weight of the phosphoric ester represented by the formula (I) and the other phosphoric esters. % Or less.
- Examples of further phosphoric esters include triphenyl phosphate, tricresyl phosphate, trixyleninolephosphate, cresinoresifeninophosphate, zinc Phosphoric acid esters such as resino-resin phenol phosphate and hydroxy phenol di-phosphoric acid phosphate, compounds obtained by modifying these with various substituents, phosphoric acid esters of various condensed types, etc. Can be mentioned.
- the amorphous thermoplastic resin is not particularly limited as long as the moldability of the resin composition and the excellent properties of the high-precision mechanical component for OA equipment of the present invention obtained therefrom are not impaired, (A) Polyphenylene ether resin, (b) Polycarbonate resin, and (c) Styrene resin are preferable from the viewpoint of compatibility with the phosphate represented by the formula (I). Can be used for
- PPE resin Polyphenylene ether resin
- PS resin polystyrene resin
- PPE resin a homopolymer or a copolymer having the following general formula ( ⁇ -1) or ( ⁇ -2) as a repeating unit can be used.
- R 5 , R 6 , R 7 , R 8 , R 9 , R 1 Q are each independently And an alkyl group having 4 carbon atoms, an aryl group having 6 to 8 carbon atoms, halogen or hydrogen, provided that R 9 and R 1 ° are not hydrogen at the same time.
- PPE resins include poly (2,6-dimethyl-14-phenylene) ether, poly (2-methyl-6-ethyl-1, 4—phenylene) ether, poly (2 2-Ethyl-6-n-Propyl-1,4-phenylene Athenole, poly (2,6—di-n-Propyl-1,4, phenylene) ether, poly (2-methyl-6) — N—butynole 1,4-phenylene ether, poly (2-ethyl-1-6-isopropyl-1,4-phenylene) ether, poly (2-methyl-1-6—h) Homopolymers such as droxetil 4-phenylene) ether are listed. Of these, particularly preferred is poly (2,6-dimethyl-1,1,4-phenylene) ether.
- alkyl-substituted phenol such as 2, 3, 6-trimethyl phenol represented by the following general formula ( ⁇ -3);
- ⁇ -3 an alkyl-substituted phenol
- a polyphenylene ether copolymer mainly composed of a polyphenylene structure obtained by copolymerizing with cresol or the like can also be used.
- R 11 R 12 , R 13 and R 14 are each independently an alkyl group having 1 to 4 carbon atoms, halogen or hydrogen, provided that R 11 , R 12 , R 13 and R 14 are simultaneously hydrogen. Absent. )
- a styrene compound is grafted to the above PPE resin, or a copolymer of a styrene compound and a compound copolymerizable therewith, for example, a copolymer of a styrene compound and maleic anhydride.
- Etc. can be graphed and used.
- PC resin Polycarbonate resin
- m-1 Polycarbonate resin
- This PC resin is prepared, for example, by a solvent method, that is, a carbonate precursor such as divalent phenol and phosgene in a solvent such as methylene chloride in the presence of a known acid acceptor and molecular weight regulator. Or a transesterification reaction between a divalent phenol and a force-ponate precursor such as diphenyl carbonate.
- a solvent method that is, a carbonate precursor such as divalent phenol and phosgene in a solvent such as methylene chloride in the presence of a known acid acceptor and molecular weight regulator.
- a transesterification reaction between a divalent phenol and a force-ponate precursor such as diphenyl carbonate.
- the divalent phenols that can be used here include 2,2-bis (4-hydroxyphenyl) propane (commonly known as bisphenol A), and Non, 4, 4 'dihydroxy diphenyl, bis (4-hydroxyphenyl) alkane, bis (4-hydroxyphenyl) cycloanolecan, bis (4-hydroxyphenyl) ) Compounds such as snorefide, bis (4-hydroxypheno), snorehon, bis (4—hydroxyfenyl), snorefoxid, bis (4-hydroxyphenyl) ether Can be mentioned. In particular, it is preferable to use bisphenol A alone or as a mixture with another divalent phenol. In addition, these divalent phenols are homologs of divalent phenol.
- the PC resin used in the present invention is a thermoplastic random branched polycarbonate obtained by reacting a polyfunctional aromatic compound with a carbonate precursor or a carbonate precursor and divalent phenol.
- divalent phenols see, for example, Japanese Patent Application Laid-Open No. HEI 2-1152, Japanese Patent Application Laid-Open No. 63-289056, etc. Can be done.
- the resin that can be used by being mixed with the PC resin includes styrene resins such as PS resin, HIPS resin, AS resin, and ABS resin, as well as PPE resin and polyolefin.
- Resins polyamide resins, thermoplastic elastomers, polyethylene terephthalate, polybutylene terephthalate, acryl resin, phenolic resin, phenolic novolak, etc. It is not limited to these. Of these, ABS resin, HIPS resin, and AS resin can be mixed particularly favorably.
- styrene resin in the present invention a vinyl aromatic polymer or a rubber-modified vinyl aromatic polymer is used.
- biel aromatic polymers examples include styrene, such as 0-methylstyrene, p-methylstyrene, m-methylinostyrene, 24 dimethylenostyrene, ethynorestyrene, and p-tert-butylstyrene.
- ⁇ -Alkyl such as alkyl-substituted styrene such as len, ⁇ -methyl styrene, ⁇ -methyl ⁇ -methyl butyl styrene
- Examples include polymers such as substituted styrene, and copolymers of one or more of these and at least one or more other compound.
- Compounds that can be copolymerized with vinyl aromatic compounds include methyl methacrylate, ethyl methacrylate, and other methacrylic acid esters, acrylonitrile, and methacrylic acid.
- examples include unsaturated nitrile compounds such as rilonitrile, and acid anhydrides such as maleic anhydride.
- particularly preferred polymers are polystyrene and styrene-acrylonitrile copolymer (AS resin).
- Examples of the rubber used for the rubber-modified bullet aromatic copolymer include polybutadiene, styrene-butadiene copolymer, rubber-modified styrene-acrylonitrile copolymer (ABS resin), and polystyrene.
- Examples include isoprene, butadiene-isoprene copolymer, natural rubber, and ethylene-propylene copolymer.
- ABS resin rubber-modified styrene-acrylonitrile copolymer
- HIPS Rubber-modified polystyrene
- polybutadiene in which more than 10% of the double bonds are hydrogenated is most preferred because of its excellent thermal stability.
- Each component used in the present invention that is, a non-crystalline thermoplastic resin, a phosphate ester represented by the formula (I), a scaly inorganic filler, and a fibrous reinforcing filler optionally used
- the method for preparing the thermoplastic resin composition is not particularly limited, and any method can be used.
- thermoplastic resin composition used in the present invention generally known mixers such as an extruder, a heating roll, a kneader, and a Banbury mixer can be used.
- thermoplastic resin composition used in the production of the high-precision mechanical parts for OA equipment of the present invention includes phenol-based, phosphorus-based, hindered phenol-based, etc. as long as the effects of the invention are not impaired.
- Antioxidants, stabilizers, coloring agents such as titanium oxide and carbon black, lubricants such as metal soaps, flow improvers, styrene-butadiene block-based, polyester elastomer-based reinforcing elastomers The required amount of first-class can be added. As those amounts, amounts generally used conventionally can be used.
- high-precision mechanical parts for OA equipment are collectively referred to as high-precision mechanical parts used in precision equipment such as OA equipment that are required to function with high precision and accuracy.
- the high-precision mechanism components as described above are not particularly limited.
- Examples include, but are not limited to, mechanical parts that are required to operate.
- Examples of the mechanical components described in (1) above include a CD-ROM drive device chassis, a write-type optical (or magnetic) disk drive device chassis, and an FD (floppy disk) drive.
- Examples of the mechanical components in the above (2) include chassis used for printers, copiers, personal computers, and footwear.
- An example of the mechanical component of the above (3) is a tray of a drive device for CD-R0M.
- the high-precision mechanical parts for OA equipment of the present invention are not limited to these examples.
- the equipment in which the high-precision mechanism component of the present invention is used For example, copying machines, printers, fax machines, personal computers, word processors, portable communication devices and their composite devices, CDs (compact disks), CD-ROMs, LDs (lasers Discs such as optical discs, magneto-optical discs (MD (trademark discs), etc.), optical discs, FDs (floppy discs), and HDs (hard discs) can be used as information media.
- CDs compact disks
- CD-ROMs compact disks
- LDs lasers Discs such as optical discs, magneto-optical discs (MD (trademark discs), etc.)
- MD magneto-optical discs
- FDs floppy discs
- HDs hard discs
- the properties required for these mechanical parts are molding properties, mechanical properties (rigidity, strength), heat resistance, flame retardancy, dimensional accuracy, and dimensional stability. Must be able to be adequately maintained. That is, high temperature
- the temperature should be about 30 ° C lower than the heat distortion temperature
- the performance of the mechanical components under high humidity conditions must not be impaired.
- the requirements regarding dimensional accuracy and dimensional stability of mechanical parts are particularly severe, and it is required that dimensional changes such as warpage and dimensional distortion at high temperature and high humidity are small.
- the mechanical parts obtained by injection molding with a reinforced resin to which a known fibrous inorganic filler such as glass fiber has been added have an anisotropic linear expansion coefficient in the molded product surface due to the orientation of the fibrous inorganic filler. Dimensional deviation and distortion due to warpage under high humidity conditions.
- the high-precision mechanism component of the present invention can surprisingly maintain high dimensional accuracy even in a wet heat environment.
- the high-precision mechanism component of the present invention contains a scaly inorganic filler, so that the rigidity and strength within the molded product are anisotropic. It was found that the vibration characteristics were excellent because of the low vibration characteristics. Important characteristics of the vibration characteristics are the vibration suppression and the natural resonance frequency.
- Vibration damping refers to the property of damping vibration, and plastic exhibits viscoelastic behavior, so its vibration damping properties are generally better than that of metal materials such as sheet metal and aluminum die cast. .
- plastics are not stiff enough and are usually reinforced by incorporating fibrous inorganic fillers.However, such reinforced plastics tend to have poor damping properties. Is well known.
- the mechanical component of the present invention composed of the resin composition containing the scaly inorganic filler has better vibration damping properties than the conventional one containing the fibrous inorganic filler. I found it to be excellent. The exact mechanism has not been elucidated yet, but it is presumed that this is probably due to the dispersive nature of the oscillation.
- This vibration damping property is achieved by a resin component having a glass transition point (T g) in a temperature range close to room temperature, for example, a rubber component such as acrylic rubber, an elastomer component such as ethylene propylene rubber, and a polyolefin. It is further improved by adding a small amount of resin components such as resin.
- T g glass transition point
- the natural resonance frequency is the natural resonance frequency of the product, which is determined by the shape, product shape, material rigidity, and density. For the same product shape, it is proportional to the square root of the stiffness of the material divided by the density. Compared to metal materials such as sheet metal and aluminum die-cast, plastic has a lower density, but its rigidity is overwhelmingly low, The natural resonance frequency is small.
- the natural resonance frequency required for precision equipment and mechanical parts is in the region where they do not resonate, since the vibration of the motor mounted on the equipment and the vibration from the outside are generally less than 300 Hz. It is said that it is preferable to be above 0 Hz.
- the mechanical component of the present invention which is made of a specific resin composition, actually exhibits the resonance characteristic value (natural resonance frequency) required by computer simulation and the vibration of the molded product as compared with the conventional resin mechanical component. It was found that the resonance characteristics obtained from the measurements matched well, and the reproducibility of the resonance characteristics was extremely high.c On the other hand, the conventional resin composition containing only a fibrous inorganic filler was molded. It was found that the mechanical parts obtained in this manner exhibited complex resonance characteristics that did not always match the design values obtained from the flexural modulus and density in the Computer Simulation Physical Properties Table. As in the case of the mechanical component of the present invention, the fact that the resonance characteristics predicted by computer simulation and the actual resonance characteristics match well is extremely advantageous in designing a high-precision mechanical component.
- the mechanical components as described above require extremely high dimensional accuracy.
- a hook that holds an optical lens that reads information Optical chassis, CD-ROM drive base traverse base chassis, etc., require dimensional accuracy on the order of tens of ⁇ m to accurately read information.
- these mechanical components are required to maintain sufficient dimensional accuracy against environmental temperature changes. That is, it is required that the coefficient of linear expansion and the anisotropy of the coefficient of linear expansion be small.
- the high-precision mechanism of the present invention has, for example, the following dimensional accuracy.
- the dimensional tolerance is 100 111111, ⁇ 100111, preferably ⁇ 50 m, and more preferably ⁇ 25 ⁇ .
- the method for molding the resin composition for producing the mechanical component for OA equipment of the present invention is not particularly limited, but an injection molding method can generally be advantageously used.
- injection molding it is preferable to minimize the flow strain generated in a molded product during molding. If the flow strain is large, strong molecular orientation strain remains in the molded product, and the molding shrinkage tends to be distorted or warped due to the influence of the molecular orientation strain, and the practical heat resistance is affected by the molecular orientation strain. It causes problems such as lowering. Set the mold gate design and molding conditions so that the flow strain is as small as possible. Is preferred.
- gas assist molding When gas-assist molding is used to mold the resin composition for manufacturing the 0A machine mechanism component of the present invention, the dimensional accuracy is dramatically improved as compared with the case where ordinary injection molding is performed. I knew it. That is, it was found that when forming the resin composition used in the present invention, gas assist molding was very effective in suppressing the flow distortion of the resin. It is particularly effective for thin products with a flow strain of 1.5 mm or less.
- the gas assist injection molding method includes a method of using a liquid as well as a gas as a pressurized fluid. For the gas assist injection molding method, see, for example, U.S. Pat. Nos. 4,824,732, 4,923,666, 4,101,61,5. , 173, 224.
- gas assist molding not only excels in dimensional accuracy at room temperature but also significantly improves dimensional stability at high temperatures, as compared with ordinary injection molding. This is unpredictable from the conventionally known effects of gas assist molding.
- the use of gas assist molding minimizes the influence of the flow orientation of the filler and the influence of the molecular orientation (residual strain) of the resin, and further increases the dimensional accuracy of the mechanical parts for OA equipment. Can be obtained.
- Cleave resistance is one of the characteristics required for mechanical parts.
- the high-precision resin mechanical parts of the present invention surprisingly have better creep resistance than conventional resin mechanical parts. In other words, the rate of deformation progression under long-term stress is low. The reason has not been clarified yet, but is presumed to be due to the specific flame retardant used in the present invention.
- test pieces are prepared by injection molding of the thermoplastic resin composition and evaluated according to the following test methods. -
- Izod impact strength Use ASTM-D256, a 1/4 inch thick test piece with a notch.
- Anti-Ri Measured by Asahi Kasei method: Measure the maximum anti-Ri (thigh) using a clearance gauge with a 150 x 150 x 3 thigh plate. The smaller the value, the better the dimensional accuracy.
- Anisotropy of linear expansion coefficient Anisotropy of linear expansion coefficient referred to in the present invention
- the property is the value obtained by dividing the value in the direction perpendicular to the flow direction by the value in the flow direction. Resin compositions having a value closer to -1 have lower anisotropy. As a material for high-precision mechanical parts for OA equipment, it is necessary that this anisotropy is 2 or less.
- High-temperature and high-humidity exposure test The PPE resin is exposed by exposing a 6-inch thick tanzak-type test piece at 121 ° C and 2 atmospheres of saturated steam for 96 hours.
- the PC resin is obtained by immersing the test piece in hot water at 95 ° C for 150 hours.
- Phosphate A is bisphenol A polyphosphate phosphate represented by the following formula (IV)
- Phosphoric ester B is bisphenol A polyxylenyl phosphate represented by the following formula (V).
- n an integer of 1 to 3.
- the phosphoric ester C is bisphenol A poly (2,6-xylenyl) phosphate represented by the following formula (VI).
- n an integer of 1 to 3.
- the phosphoric acid ester D is a bisphenol polydiphenyl phosphate represented by the following formula ( ⁇ ).
- n an integer of 1 to 3.
- the phosphate E is a resorcinol polyphenyl phosphate represented by the following formula ().
- n an integer of 1 to 3.
- the phosphate F is a hydroquinone polyphenyl phosphate represented by the following formula (K).
- n an integer of 1 to 3.
- Phosphoric acid ester G is a triphenyl phosphate represented by the following formula (X).
- TPP manufactured by Daihachi Chemical Co., B
- Example 4 Comparative Examples 1-3
- a poly (2,6-dimethyl-1,4-furene) ether (hereinafter abbreviated as “ ⁇ ”) having an intrinsic viscosity [] of 0.52 measured at 30 ° C in a black mouth form; Rubber-modified polystyrene resin
- Extrusion kneading repellets are obtained with a PCM-30 twin-screw extruder (manufactured by Ikegai Iron Works, Japan) set at a cylinder temperature of 32 ° C [The chemical name of Mark 22 is Tri (2,4—Ct-butylphenylphosphite)] is used to perform injection molding at a cylinder temperature of 290 ° C and a 1Z16 inch thick combustion test Get a piece. Using this test piece, flammability evaluation and high-temperature and high-humidity exposure test are performed. Next, as an evaluation of the mechanical components mounted on the CD-ROM drive, the tray-shaped product shown in Fig.
- PPE having an intrinsic viscosity [77] of 0.52 measured at 30 ° C in a black mouth form HIPS (Asahi Kasei Polystyrene H 9104, Japan, manufactured by Asahi Kasei Corporation) , PS (Asahi Kasei Polystyrene 685, manufactured by Asahi Kasei Kogyo Co., Ltd.) and the above-mentioned phosphoric acid ester flame retardant A are combined with glass fiber (RES 03 — TP 1051 Japan, 0 Honita Glass Co., Ltd.), glass flakes (sold by Mycro Dallas Freyforce REFG-302, sold by Nippon Sheet Glass Co., Ltd.) and my abilities (Szolite Mica 200 KI Japan, Kuraray Co., Ltd.) PCM-30 twin screw extruder (Ikegai, Japan) used together with one or two fillers selected from the group below) and in the proportions shown in Table 2 at a cylinder temperature of 320 ° C Iron Works
- Polycarbonate resin [Mitsubishi Engineers Lining Plastics, Ltd., Japan: Iupiron (trademark) S-1000] was added to the above-mentioned phosphate ester flame retardants A to G, and an inorganic filler. And glass flakes (trademark Micro Glass Glass REF G-302) with the ratio shown in Table 5 and a PCM-30 twin-screw extruder set at a cylinder temperature of 310 ° C [Japan, manufactured by Ikekai Tekko Co., Ltd.] Extrusion kneading pellets are obtained. Injection molding is performed using this pellet at a cylinder temperature of 280 ° C to obtain a combustion test specimen with a thickness of 116 inches.
- the tray-shaped product shown in Fig. 1 was subjected to injection molding at a cylinder temperature of 280 ° C and a mold temperature of 80 ° C for 10,000 shots.
- a volatility evaluation of the resin composition after continuous molding visual inspection of the amount of smoke generated from the nozzle of the injection molding machine when purging the resin composition, and evaluation of the appearance of the molded product and the inner wall surface of the mold cavity Do. Table 5 shows the results.
- Polycarbonate resin [Mitsubishi Engineering Plastics Co., Ltd .: Iupiron TM S-1000], phosphate ester A flame retardant, and RES 03 — TP as glass fiber 1051 (made by Nippon Sheet Glass Co., Ltd., Japan), Microglass Freka REFG-302 as glass flakes, and Repco S200 HG-CT (Japan) surface-treated with aminosilane as my strength Country, manufactured by Repco Corporation) at the rates shown in Table 6. Used, cylinder temperature 310. Extrude and knead pellets with a PCM-30 twin screw extruder [Ikegai Iron Works Co., Ltd., Japan] set to C and determine the physical properties of the pellets. Table 7 shows the results.
- the tray-shaped product shown in Fig. 1 was used at a cylinder temperature of 280. C, mold Injection molding is carried out at a temperature of 80 ° C, and the dimensional accuracy (return) is measured. Table 8 shows the results.
- Comparative Example 9 of Table 7 the resin composition using glass fiber alone has a large resilience and a large anisotropy of linear expansion coefficient (a measure of dimensional accuracy). Comparative Example 1 using glass beads alone
- the resin composition of No. 0 is not preferable because the anisotropy of the coefficient of linear expansion is small, but the flexural modulus is lowered.
- 75 parts by weight of butadiene latex having an average particle size of 0.3 O jm (40 parts by weight in terms of rubber) and 1 part by weight of an emulsifier (disproportionated potassium rosinate) are charged into a polymerization tank and stirred.
- the produced graft copolymer latex is coagulated with a dilute sulfuric acid aqueous solution, washed, dehydrated and dried to obtain a white ABS resin.
- the dimensional evaluation results of the tray-shaped molded products were the same as those of the polycarbonates of Examples 15 to 20 and Comparative Examples 9 to 10, except for the resin composition using glass beads alone. It correlates with the results for resin.
- the molded articles of Examples 21 to 26 all had a value of the natural resonance frequency that matched the design value obtained by computer simulation.
- Each of the PPE resin compositions of Examples 5 to 6 and the PC resin composition of Examples 15 to 16 were tray-formed at a cylinder temperature of 280 ° C and a mold temperature of 80 ° C. Perform gas assist molding of the product.
- the gas (N 2 ) injection conditions were such that the injection amount of the resin was 95% of the full shot, and injection was performed from the gate at the same time as the injection of the resin was completed, and the gas pressure was maintained at 150 kg Zcm 2 for 20 seconds. After cooling, remove for 1 minute.
- the dimensional accuracy (return) was evaluated. Table 10 shows the results. Examples 27 to 30 have improved dimensional accuracy compared to the normal injection molded products of Examples 5 to 6 and Examples 15 to 16. Has been improved.
- the PPE resin compositions of Examples 5 to 6 and the PC resin compositions of Examples 15 to 16 were mixed under the conditions of a cylinder temperature of 280 ° C and a mold temperature of 80 ° C. ⁇ 2 2? Under the conditions of a cylinder temperature of 260 and a mold temperature of 60 ° C, the resin composition was molded into a gas-assisted mold using the chassis mechanism parts for holding the optical element shown in Fig. 2. Injection molding is performed, and the flatness of the plane of the hatched portion of the molded product is measured. Then, expose in a 6.0 ° C oven for 250 hours and measure dimensional change (change in flatness).
- the gas (N 2 ) injection conditions were such that the injection amount of the resin was 97% of the full shot, gas was injected directly into the product section at the same time as the injection of the resin, and the gas pressure was 200 kg / cm 2 . Hold for 12 seconds, then cool for 1 minute and remove.
- the dimensional accuracy of the molded product is measured by fixing the molded product on the surface plate and measuring the flatness of the plane indicated by the hatching in Fig. 2 with a 3D dimension measuring machine (AE122, Mitutoyo, Japan). Using a measurement program (Geopack 400, Mitutoyo, Japan).
- the flatness measured by the above program is Assuming two planes parallel to each other on both sides of the calculation plane calculated by the least-squares method from multiple (15 or more) measurement points on the measurement plane, the total distance between the two planes is calculated. The minimum distance (mm) between two planes to include the measurement point. The higher the value of the flatness, the lower the flatness. Table 11 shows the results.
- Example Comparative example Composition 1 2 3 4 1 2 3 Poly (2,6-dimethyl-1,4-phenylene) ether 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40 40
- # is the design value
- the numerical values in the examples for E and F are the value of the design value + the reverse value.
- # is the design value
- the numerical values in the examples related to peri, E, and F are the value of the design value + the reverse value.
- a S resin 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 Estenole phosphate A 10 10 10 10 10 10 10 10 10 10 Microphone ⁇ Glass flexure REFG-302 30 15 15 7.5
- # is the design value of the embodiment for peri, E and F
- the numerical value is the design value + the value of the counter value.
- the high-precision mechanical parts made of flame-retardant resin for OA equipment of the present invention have excellent dimensional accuracy and mechanical properties (mechanical strength, vibration damping, ), And can be used very advantageously as mechanical parts for various 0A equipment that are required to function with high accuracy and high precision.
Landscapes
- Chemical & Material Sciences (AREA)
- Medicinal Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Manufacturing & Machinery (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Dispersion Chemistry (AREA)
- Materials Engineering (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Manufacture Of Macromolecular Shaped Articles (AREA)
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP52624795A JP3295429B2 (ja) | 1994-04-08 | 1995-04-10 | Oa機器用難燃樹脂製高精度機構部品 |
EP95914554A EP0754531B2 (en) | 1994-04-08 | 1995-04-10 | High-precision mechanical parts made from flame-retardant resin for office automation equipment |
DE69519161T DE69519161T3 (de) | 1994-04-08 | 1995-04-10 | Hochgenaue mechanische Teile hergestellt aus flammenhemmender Harz für Büroautomationsgeräte |
US08/704,791 US5961915A (en) | 1994-04-08 | 1995-04-10 | Flame retardant, high precision resin mechanical part for use in an office automation machine |
KR1019960704527A KR0180852B1 (ko) | 1994-04-08 | 1995-04-10 | 사무 자동화 기기용 난연 수지제 고정밀도 기구 부품 |
HK98113029A HK1017571A1 (en) | 1994-04-08 | 1998-12-09 | High-precision mechanical parts made from flame-retardant resin for office automation equipment |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP6/71044 | 1994-04-08 | ||
JP6071044A JPH07278318A (ja) | 1994-04-08 | 1994-04-08 | 難燃性cd−rom帰属部品 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1995027603A1 true WO1995027603A1 (fr) | 1995-10-19 |
Family
ID=13449135
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP1995/000703 WO1995027603A1 (fr) | 1994-04-08 | 1995-04-10 | Pieces mecaniques de haute precision en resine ignifuge pour equipement de bureautique |
Country Status (10)
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008143997A (ja) * | 2006-12-08 | 2008-06-26 | Mitsubishi Engineering Plastics Corp | ポリカーボネート樹脂組成物 |
JP6475401B1 (ja) * | 2017-10-13 | 2019-02-27 | 三菱エンジニアリングプラスチックス株式会社 | ポリカーボネート樹脂組成物 |
WO2019073818A1 (ja) * | 2017-10-13 | 2019-04-18 | 三菱エンジニアリングプラスチックス株式会社 | ポリカーボネート樹脂組成物 |
Families Citing this family (33)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2295617B (en) | 1994-12-03 | 1998-11-04 | Courtaulds Plc | Thermoplastic resin compositions and articles containing delaminated fillers |
DE19734667A1 (de) | 1997-08-11 | 1999-02-18 | Bayer Ag | Flammwidrige, verstärkte Polycarbonat-ABS-Formmassen |
DE19734661A1 (de) * | 1997-08-11 | 1999-02-18 | Bayer Ag | Flammwidrige, spannungsrißbeständige Polycarbonat ABS-Formmassen |
US6613820B2 (en) * | 1997-08-29 | 2003-09-02 | General Electric Company | Polycarbonate resin composition |
US6486241B2 (en) | 1997-08-29 | 2002-11-26 | General Electric Company | Polycarbonate resin composition |
GB9719929D0 (en) * | 1997-09-18 | 1997-11-19 | Kobe Steel Europ Ltd | Flame retardant polycarbonate-styrene(or acrylate)polymers,and/or copolymers and/or graft polymer/copolymer mixtures |
GB2329639B (en) * | 1997-09-25 | 2002-02-20 | Samyang Corp | Flame retardant resin composition |
DE19851676A1 (de) | 1998-11-10 | 2000-05-11 | Bayer Ag | Thermoplastische Formmassen mit verbesserten mechanischen Eigenschaften |
DE19914137A1 (de) * | 1999-03-27 | 2000-09-28 | Bayer Ag | Flammwidrige mit Pfropfpolymerisat modifizierte Polycarbonat-Formmassen |
DE19914139A1 (de) | 1999-03-27 | 2000-09-28 | Bayer Ag | Flammwidrige, schlagzähmodifizierte Polycarbonat-Formmassen |
DE19962930A1 (de) * | 1999-12-24 | 2001-06-28 | Bayer Ag | Flammwidrige Polycarbonat-Formmassen mit Talk besonderer Reinheit |
DE10010941A1 (de) * | 2000-03-06 | 2001-09-13 | Bayer Ag | Flammwidrige Polycarbonat-Formmassen |
US6453760B1 (en) * | 2000-07-03 | 2002-09-24 | Advanced Micro Device, Inc. | Automated detection of unacceptable warpage of trays for holding integrated circuit packages |
US7037865B1 (en) * | 2000-08-08 | 2006-05-02 | Moldite, Inc. | Composite materials |
KR100360208B1 (ko) * | 2000-10-05 | 2002-11-11 | 주식회사 사나테크 | 유기인계 난연제 및 이를 함유하는 난연 열가소성 수지조성물 |
AU2002210943A1 (en) | 2000-10-26 | 2002-05-06 | Nippon A And L Incorporated | Flame-retardant and electromagnetic interference attenuating thermoplastic resincomposition |
DE10103237A1 (de) * | 2001-01-25 | 2002-08-01 | Bayer Ag | Polycarbonat-Zusammensetzungen mit reduziertem Eisengehalt |
DE10103238A1 (de) | 2001-01-25 | 2002-08-01 | Bayer Ag | Flammwidrige, mineralverstärkte Polycarbonatzusammensetzungen mit hoher Bindenahtfestigkeit |
DE10209521B4 (de) * | 2001-03-08 | 2004-04-08 | Asahi Kasei Kabushiki Kaisha | Harzzusammensetzung |
DE10152318A1 (de) * | 2001-10-26 | 2003-05-08 | Bayer Ag | Schlagzähmodifizierte flammwidrig ausgerüstete Polycarbonat-Formmassen |
DE10201291A1 (de) * | 2002-01-15 | 2003-07-31 | Krauss Maffei Kunststofftech | Verfahren zum Herstellen von schlagzähmodifizierten Thermoplast-Kunststoffteilen |
EP1489140B1 (en) * | 2002-03-27 | 2008-08-13 | Teijin Chemicals, Ltd. | Flame-retardant aromatic polycarbonate resin composition |
DE10235754A1 (de) * | 2002-08-05 | 2004-02-19 | Bayer Ag | Flammwidrige mit Pfropfpolymerisat modifizierte Polycarbonat-Formmassen |
US8829100B2 (en) * | 2006-12-19 | 2014-09-09 | Sabic Innovative Plastics Ip B.V. | Reinforced amorphous polymer composition |
US8057873B2 (en) * | 2008-04-28 | 2011-11-15 | Sabic Innovative Plastics Ip B.V. | Injection molded article and method for the manufacture thereof |
JP2010116478A (ja) * | 2008-11-13 | 2010-05-27 | Shin Kobe Electric Mach Co Ltd | 断熱パネル用熱可塑性樹脂シート及び断熱パネル |
DE102010018234A1 (de) | 2010-04-23 | 2012-03-29 | Bayer Materialscience Aktiengesellschaft | Leichtfließende Polycarbonat/ABS-Formmassen mit guten mechanischen Eigenschaften und guter Oberfläche |
DE102010041388A1 (de) | 2010-09-24 | 2012-03-29 | Bayer Materialscience Aktiengesellschaft | Flammgeschützte schlagzähmodifizierte Batteriegehäuse auf Polycarbonatbasis II |
US9670337B2 (en) * | 2012-03-13 | 2017-06-06 | Basf Se | Flame-retardant thermoplastic polyurethane comprising coated metal hydroxides based on aluminum |
JP5965684B2 (ja) * | 2012-03-14 | 2016-08-10 | ユーエムジー・エービーエス株式会社 | めっき加工されたプラスチックシャーシ |
WO2014065519A1 (ko) * | 2012-10-24 | 2014-05-01 | 주식회사 엘지화학 | 폴리카보네이트 수지 조성물 |
JP2021155511A (ja) * | 2020-03-25 | 2021-10-07 | 富士フイルムビジネスイノベーション株式会社 | 樹脂組成物及び樹脂成形体 |
CN115698157A (zh) * | 2020-05-29 | 2023-02-03 | 蓝立方知识产权有限责任公司 | 反应型磷酸盐及制备工艺 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5757092B2 (US07576128-20090818-C00048.png) * | 1978-05-22 | 1982-12-02 | Teijin Ltd | |
JPH04348157A (ja) * | 1991-05-27 | 1992-12-03 | Mitsubishi Kasei Corp | 光学系機器シャーシ用材料 |
JPH06207089A (ja) * | 1993-01-11 | 1994-07-26 | Teijin Chem Ltd | 芳香族ポリカーボネート樹脂成形品 |
JPH0753876A (ja) * | 1992-08-06 | 1995-02-28 | Asahi Chem Ind Co Ltd | 樹脂組成物 |
Family Cites Families (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1313749A (en) † | 1969-10-02 | 1973-04-18 | Canadian Patents Dev | Polymeric high performance composites |
US4156663A (en) * | 1974-05-18 | 1979-05-29 | Kanebo, Ltd. | Flame resistant polymer composition containing phosphorus and bromine containing polymer |
US4222928A (en) * | 1977-11-09 | 1980-09-16 | Teijin Limited | Polyester composition |
US4404125A (en) * | 1981-10-14 | 1983-09-13 | General Electric Company | Polyphenylene ether resin compositions for EMI electromagnetic interference shielding |
EP0085438B1 (en) * | 1982-02-03 | 1987-01-07 | Showa Denko Kabushiki Kaisha | Styrene-based resin composition |
US4564491A (en) † | 1982-03-01 | 1986-01-14 | General Motors Corporation | Preparing glass flake reinforced reaction injection molded polymers |
US4560715A (en) † | 1983-03-31 | 1985-12-24 | Kuraray Co., Ltd. | Mica flake mass and resin composition with the same incorporated therein |
GB2139548B (en) † | 1983-05-11 | 1986-11-19 | James Watson Hendry | Injection moulding |
JPS6147222A (ja) † | 1984-08-14 | 1986-03-07 | Olympus Optical Co Ltd | レンズ鏡筒等の射出成形加工方法 |
JPH06104758B2 (ja) * | 1985-11-08 | 1994-12-21 | 旭化成工業株式会社 | 射出成形用熱可塑性樹脂組成物 |
US5002827A (en) * | 1987-10-26 | 1991-03-26 | Nippon Glass Fiber Co., Ltd. | Agglomerated glass flakes |
JPH01225660A (ja) * | 1988-03-04 | 1989-09-08 | Polyplastics Co | ポリアリーレンサルファイド樹脂組成物 |
GB2217644A (en) * | 1988-04-22 | 1989-11-01 | Cinpres Ltd | Injection moulding |
US5204394A (en) * | 1988-09-22 | 1993-04-20 | General Electric Company | Polymer mixture having aromatic polycarbonate, styrene I containing copolymer and/or graft polymer and a flame-retardant, articles formed therefrom |
US4987175A (en) † | 1988-11-21 | 1991-01-22 | Battelle Memorial Institute | Enhancement of the mechanical properties by graphite flake addition |
WO1990007415A1 (en) † | 1988-12-26 | 1990-07-12 | Asahi Kasei Kogyo Kabushiki Kaisha | Method and apparatus for injection molding of hollow article |
JPH064739B2 (ja) * | 1989-04-12 | 1994-01-19 | 旭化成工業株式会社 | 低反りスチレン系樹脂組成物 |
DE4123041A1 (de) * | 1991-07-12 | 1993-01-14 | Bayer Ag | Thermoplastische polycarbonatformmassen mit flammwidrigen eigenschaften |
JPH0822945B2 (ja) * | 1991-08-12 | 1996-03-06 | ゼネラル・エレクトリック・カンパニイ | 難燃化された導電性のポリフェニレンエーテル系組成物 |
JP3353789B2 (ja) † | 1991-10-25 | 2002-12-03 | ゼネラル・エレクトリック・カンパニイ | Ic用トレー |
WO1994003535A1 (en) * | 1992-08-06 | 1994-02-17 | Asahi Kasei Kogyo Kabushiki Kaisha | Resin composition |
-
1994
- 1994-04-08 JP JP6071044A patent/JPH07278318A/ja active Pending
-
1995
- 1995-04-08 TW TW084103362A patent/TW267180B/zh not_active IP Right Cessation
- 1995-04-10 WO PCT/JP1995/000703 patent/WO1995027603A1/ja active IP Right Grant
- 1995-04-10 KR KR1019960704527A patent/KR0180852B1/ko not_active IP Right Cessation
- 1995-04-10 DE DE69519161T patent/DE69519161T3/de not_active Expired - Lifetime
- 1995-04-10 MY MYPI95000918A patent/MY121205A/en unknown
- 1995-04-10 EP EP95914554A patent/EP0754531B2/en not_active Expired - Lifetime
- 1995-04-10 US US08/704,791 patent/US5961915A/en not_active Expired - Lifetime
- 1995-04-10 CN CN95191703A patent/CN1060717C/zh not_active Expired - Lifetime
- 1995-04-10 JP JP52624795A patent/JP3295429B2/ja not_active Expired - Lifetime
-
1998
- 1998-12-09 HK HK98113029A patent/HK1017571A1/xx not_active IP Right Cessation
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5757092B2 (US07576128-20090818-C00048.png) * | 1978-05-22 | 1982-12-02 | Teijin Ltd | |
JPH04348157A (ja) * | 1991-05-27 | 1992-12-03 | Mitsubishi Kasei Corp | 光学系機器シャーシ用材料 |
JPH0753876A (ja) * | 1992-08-06 | 1995-02-28 | Asahi Chem Ind Co Ltd | 樹脂組成物 |
JPH06207089A (ja) * | 1993-01-11 | 1994-07-26 | Teijin Chem Ltd | 芳香族ポリカーボネート樹脂成形品 |
Non-Patent Citations (1)
Title |
---|
See also references of EP0754531A4 * |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008143997A (ja) * | 2006-12-08 | 2008-06-26 | Mitsubishi Engineering Plastics Corp | ポリカーボネート樹脂組成物 |
JP6475401B1 (ja) * | 2017-10-13 | 2019-02-27 | 三菱エンジニアリングプラスチックス株式会社 | ポリカーボネート樹脂組成物 |
WO2019073818A1 (ja) * | 2017-10-13 | 2019-04-18 | 三菱エンジニアリングプラスチックス株式会社 | ポリカーボネート樹脂組成物 |
US11198785B2 (en) | 2017-10-13 | 2021-12-14 | Mitsubishi Engineering-Plastics Corporation | Polycarbonate resin composition |
Also Published As
Publication number | Publication date |
---|---|
EP0754531B2 (en) | 2006-09-13 |
DE69519161D1 (de) | 2000-11-23 |
DE69519161T3 (de) | 2007-11-22 |
EP0754531A1 (en) | 1997-01-22 |
EP0754531A4 (en) | 1997-07-16 |
JPH07278318A (ja) | 1995-10-24 |
US5961915A (en) | 1999-10-05 |
CN1060717C (zh) | 2001-01-17 |
MY121205A (en) | 2006-01-28 |
JP3295429B2 (ja) | 2002-06-24 |
HK1017571A1 (en) | 1999-11-19 |
KR970701121A (ko) | 1997-03-17 |
CN1141609A (zh) | 1997-01-29 |
DE69519161T2 (de) | 2001-05-23 |
KR0180852B1 (ko) | 1999-05-15 |
EP0754531B1 (en) | 2000-10-18 |
TW267180B (US07576128-20090818-C00048.png) | 1996-01-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO1995027603A1 (fr) | Pieces mecaniques de haute precision en resine ignifuge pour equipement de bureautique | |
US20040178383A1 (en) | Flame-retardant aromatic polycarbonate resin composition | |
WO2006062031A1 (ja) | ポリカーボネート樹脂組成物及び成形体 | |
US20100298475A1 (en) | Ignition resistant carbonate polymer composition containing an aromatic phosphonate | |
JP4971544B2 (ja) | ポリカーボネート樹脂組成物及び成形品 | |
JP7386159B2 (ja) | 熱可塑性樹脂組成物およびこれから形成された成形品 | |
US7642305B2 (en) | Reinforced thermoplastic resin composition and molded products thereof | |
JP4753349B2 (ja) | 強化熱可塑性樹脂組成物 | |
JP4399347B2 (ja) | 強化熱可塑性樹脂組成物、およびこれを用いた成型品。 | |
US6495621B1 (en) | Molding material for OA machine parts with improved vibration damping properties | |
JP5794863B2 (ja) | 熱可塑性樹脂組成物 | |
JPH08115589A (ja) | 寸法精度に優れたpc系樹脂製cd−rom機構部品 | |
JPH0711119A (ja) | 難燃性熱可塑性樹脂組成物 | |
JPH08115588A (ja) | 寸法精度に優れた変性ppe樹脂製cd−rom機構部品 | |
KR102672294B1 (ko) | 열가소성 수지 조성물 및 이를 이용한 성형품 | |
KR20220118666A (ko) | 열가소성 수지 조성물 및 이로부터 제조된 성형품 | |
WO2023199726A1 (ja) | 樹脂組成物および成形品 | |
KR20160039059A (ko) | 난연성 열가소성 수지 조성물 및 이를 포함하는 성형품 | |
JP2004091692A (ja) | 機構部品 | |
JP2024030168A (ja) | 樹脂組成物、ペレット、および、成形品 | |
JPH1180535A (ja) | 熱可塑性樹脂組成物 | |
JPH09291208A (ja) | 難燃性樹脂組成物 | |
JPH07278349A (ja) | 難燃性oa機器部品用成形体 | |
KR20200082437A (ko) | 열가소성 수지 조성물 및 이로부터 형성된 성형품 | |
JPH09176374A (ja) | 加工性に優れた難燃樹脂製部品 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 95191703.X Country of ref document: CN |
|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): CN JP KR SG US VN |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 1995914554 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1199690123 Country of ref document: VN Ref document number: 1019960704527 Country of ref document: KR |
|
WWE | Wipo information: entry into national phase |
Ref document number: 08704791 Country of ref document: US |
|
WWP | Wipo information: published in national office |
Ref document number: 1995914554 Country of ref document: EP |
|
WWG | Wipo information: grant in national office |
Ref document number: 1995914554 Country of ref document: EP |