US20130260245A1 - Electrode material and method for producing the same - Google Patents

Electrode material and method for producing the same Download PDF

Info

Publication number
US20130260245A1
US20130260245A1 US13/993,403 US201113993403A US2013260245A1 US 20130260245 A1 US20130260245 A1 US 20130260245A1 US 201113993403 A US201113993403 A US 201113993403A US 2013260245 A1 US2013260245 A1 US 2013260245A1
Authority
US
United States
Prior art keywords
electrode
aggregate
active material
carbonaceous film
particle size
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/993,403
Other languages
English (en)
Inventor
Takao Kitagawa
Hirofumi Yasumiishi
Masaru Uehara
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Osaka Cement Co Ltd
Original Assignee
Sumitomo Osaka Cement Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2010282353A external-priority patent/JP2012133888A/ja
Priority claimed from JP2011207833A external-priority patent/JP6077205B2/ja
Application filed by Sumitomo Osaka Cement Co Ltd filed Critical Sumitomo Osaka Cement Co Ltd
Assigned to SUMITOMO OSAKA CEMENT CO., LTD. reassignment SUMITOMO OSAKA CEMENT CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KITAGAWA, TAKAO, UEHARA, MASARU, YASUMIISHI, HIROFUMI
Publication of US20130260245A1 publication Critical patent/US20130260245A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
    • H01M4/624—Electric conductive fillers
    • H01M4/625—Carbon or graphite
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/133—Electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B32/00—Carbon; Compounds thereof
    • C01B32/05—Preparation or purification of carbon not covered by groups C01B32/15, C01B32/20, C01B32/25, C01B32/30
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/139—Processes of manufacture
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/362—Composites
    • H01M4/366—Composites as layered products
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/485—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
    • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
    • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
    • H01M4/5825—Oxygenated metallic salts or polyanionic structures, e.g. borates, phosphates, silicates, olivines
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
    • H01M4/583—Carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/62—Selection of inactive substances as ingredients for active masses, e.g. binders, fillers
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/021—Physical characteristics, e.g. porosity, surface area
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

  • the present invention relates to an electrode material and a method for producing the same, and more particularly, to an electrode material suitable for use in a positive electrode material for a battery, in particular, a positive electrode material for a lithium ion battery, and to a method for producing the electrode material.
  • the lithium ion battery includes positive electrode and negative electrode that have properties capable of reversibly intercalating and deintercalating lithium ions, and a non-aqueous electrolyte.
  • a negative electrode material of the lithium ion battery As a negative electrode-active material, Li-containing metal oxides such as a carbon-based material and lithium titanate (Li 4 Ti 5 O 12 ) that have properties capable of reversibly intercalating and deintercalating lithium ions have been used.
  • an electrode material mixture which contains a Li-containing metal oxide such as iron lithium phosphate (LiFePO 4 ) having properties capable of reversibly intercalating and deintercalating lithium ions as a positive electrode-active material, a binder, and the like, has been used.
  • this electrode material mixture is applied on a surface of metal foil called a current collector to form a positive electrode of the lithium ion battery.
  • the lithium ion battery Since the lithium ion battery is light in weight and small in size, and has high energy compared to a secondary battery such as a lead battery, a nickel-cadmium battery, a nickel-hydrogen battery, and the like in the related art, the lithium ion battery has been used as a power supply of portable electronic apparatuses such as a cellular phone and a note-type personal computer. In addition, in recent years, the lithium ion battery has been reviewed as a high-output power supply of an electric vehicle, a hybrid vehicle, an electromotive tool, and the like, and high-speed charge and discharge characteristics have been required for the battery that is used as the high-output power supply.
  • the electrode material which contains an electrode-active material, for example, the Li-containing metal oxide having properties capable of reversibly intercalating and deintercalating lithium ions, has a problem in that conductivity is low. Therefore, there is suggested an electrode material in which a particle surface of the electrode-active material is covered with an organic component that is a carbon source, the organic component are carbonized to form a carbonaceous film on a surface of the electrode-active material, and carbon of the carbonaceous film is interposed as an electronic conductive material to increase the conductivity of the electrode material (refer to PTL 1).
  • an electrode material in which a particle surface of the electrode-active material is covered with an organic component that is a carbon source, the organic component are carbonized to form a carbonaceous film on a surface of the electrode-active material, and carbon of the carbonaceous film is interposed as an electronic conductive material to increase the conductivity of the electrode material (refer to PTL 1).
  • the conductivity is requisite, and it is preferable that the conductivity of the electrode-active material be as high as possible.
  • an aromatic carbon compound generated due to thermal decomposition of the organic compound during the baking condenses, and thus a carbonaceous film is formed on a surface of the electrode-active material.
  • the aromatic carbon compound is volatile at a high temperature.
  • the concentration of the vaporized material of the aromatic carbon compound decreases, and the supporting amount of the carbonaceous film decreases as a whole or partially. Therefore, the thickness of the carbonaceous film decreases, and thus the coverage rate of the carbonaceous film decreases.
  • the invention has been made to solve the above-described problems, and an object thereof is to provide an electrode material in which unevenness in a supporting amount of the carbonaceous film is less when using an electrode-active material having a carbonaceous film formed on a surface thereof as the electrode material and which is capable of improving conductivity and a method for producing the electrode material.
  • the present inventors made a thorough investigation to solve the above-described problems. As a result, they found that with regard to a particle size distribution of an electrode-active material or a precursor of the electrode-active material in slurry containing the electrode-active material or the precursor of the electrode-active material, and an organic compound, when a ratio (D90/D10) of D90 to D10 of the particle size distribution is set to 5 to 30 during production of the electrode material, a volume density of an aggregate that is obtained may be set to 50 to 80 vol % of the volume density in a case in which the aggregate is a solid, and accordingly, a concentration of a vaporized material of an aromatic carbonaceous compound inside the aggregate may be raised, and as a result, a carbonaceous film in which unevenness is less may be supported on a surface of the electrode-active material inside the aggregate, and the present inventors accomplished the invention.
  • an electrode material including an aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface.
  • An average particle size of the aggregate is 0.5 to 100 ⁇ m.
  • a volume density of the aggregate is 50 to 80 vol % of the volume density in a case in which the aggregate is a solid.
  • the electrode material of the invention it is preferable that 80% or more of the surface of the electrode-active material be covered with the carbonaceous film.
  • the aggregate may be a shell-like aggregate having a void at the inside thereof, and it is preferable that a ratio of an average film thickness of the carbonaceous film in an outer peripheral portion and an inner peripheral portion of an outer shell of the shell-like aggregate (a thickness of the carbonaceous film in the inner peripheral portion/a thickness of the carbonaceous film in the outer peripheral portion) be 0.7 to 1.3.
  • an amount of carbon in the carbonaceous film be 0.6 to 10 parts by mass on the basis of 100 parts by mass of the electrode-active material. It is preferable that a tap density of the aggregate be 1.0 to 1.5 g/cm 3 .
  • the electrode-active material contain one kind selected from the group consisting of lithium cobaltate, lithium nickelate, lithium manganate, lithium titanate, and Li x A y D z PO 4 (provided that, A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr, D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5, and 0 ⁇ z ⁇ 1.5) as a main component.
  • A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr
  • D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5
  • a method for producing an electrode material includes: drying slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which a ratio (D90/D10) of D90 to D10 of a particle size distribution of the electrode-active material or the precursor of the electrode-active material is 5 to 30; and baking the resultant dried product that is obtained at 500° C. to 1,000° C. in a non-oxidizing atmosphere.
  • a ratio (D90/D10) of a particle size (D90) when an accumulated volume percentage of a particle size distribution of the electrode-active material or the precursor of the electrode-active material is 90% to a particle size (D10) when the accumulated volume percentage is 10% is 5 to 30 during production of the electrode material
  • a pore size (D50) when the accumulated volume percentage of the pore size distribution of the aggregate that is obtained is 50% may be set to 0.1 to 0.2 ⁇ m
  • an electrode material including an aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface.
  • An average particle size of the aggregate is 0.5 to 100 ⁇ m.
  • a pore size (D50) when an accumulated volume percentage of a pore size distribution of the aggregate is 50% is 0.1 to 0.2 ⁇ m.
  • Porosity of the aggregate is 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid.
  • the electrode material of the invention it is preferable that 80% or more of the surface of the electrode-active material be covered with the carbonaceous film.
  • the aggregate may be a shell-like aggregate having a void at the inside thereof, and it is preferable that a ratio of an average film thickness of the carbonaceous film in an outer peripheral portion and an inner peripheral portion of an outer shell of the shell-like aggregate (a thickness of the carbonaceous film in the inner peripheral portion/a thickness of the carbonaceous film in the outer peripheral portion) be 0.7 to 1.3.
  • an amount of carbon in the carbonaceous film be 0.6 to 10 parts by mass on the basis of 100 parts by mass of the electrode-active material.
  • a tap density of the aggregate be 1.0 to 1.5 g/cm 3 .
  • the electrode-active material contains one kind selected from the group consisting of lithium cobaltate, lithium nickelate, lithium manganate, lithium titanate, and Li x A y D z PO 4 (provided that, A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr, D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5, and 0 ⁇ z ⁇ 1.5) as a main component.
  • A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr
  • D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5
  • a method for producing an electrode material includes: drying slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which a ratio (D90/D10) of a particle size (D90) when an accumulated volume percentage of a particle size distribution of the electrode-active material or the precursor of the electrode-active material is 90% to a particle size (D10) when the accumulated volume percentage is 10% is 5 to 30; and baking the resultant dried product that is obtained at 500° C. to 1, 000° C. in a non-oxidizing atmosphere.
  • the average particle size of the aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface thereof is set to 0.5 to 100 ⁇ m, and a volume density of the aggregate is set to 50 to 80 vol % of the volume density in a case in which the aggregate is a solid, and thus unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material particles may be reduced, and as a result, unevenness in conductivity of the electrode-active material may be reduced. Accordingly, when the electrode-active material is used as an electrode material of a lithium ion battery, internal resistance may be reduced.
  • the electrode-active material in which the unevenness in conductivity is reduced is used as the electrode material of the lithium ion battery, a reaction related to intercalation and deintercalation of lithium ions may be uniformly carried out in the entirety of the surface of the electrode-active material, and thus the internal resistance may be reduced.
  • the internal resistance mentioned here represents internal resistance at a site at which reaction resistance related to intercalation and deintercalation of lithium ions is high in a particle, which does not have the carbonaceous film formed on a surface thereof or in which the thickness of the carbonaceous film is small, of the electrode-active material.
  • the internal resistance is shown as a magnitude of voltage drop at the final stage of discharge. That is, in an electrode-active material in which the intercalation and deintercalation reaction of lithium ions is uniformly carried out over the entirety of the surface of the electrode-active material, the voltage drop at the final stage of discharge is small. Conversely, in an electrode-active material in which the intercalation and deintercalation reaction resistance of lithium ions is high at a part of the surface of the electrode-active material, the voltage drop at the final stage of discharge becomes significant.
  • slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which a ratio (D90/D10) of D90 to D10 of a particle size distribution of the electrode-active material or the precursor of the electrode-active material is 5 to 30, is dried, and the resultant dried product that is obtained is baked at 500° C. to 1,000° C. in a non-oxidizing atmosphere. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on a surface of the electrode-active material may be reduced. As a result, an electrode material capable of reducing unevenness in conductivity of the electrode-active material may be easily produced.
  • an average particle size of the aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface is set to 0.5 to 100 ⁇ m, and a pore size (D50) when an accumulated volume percentage of a pore size distribution of the aggregate is 50% is set to 0.1 to 0.2 ⁇ m, and the porosity of the aggregate is set to 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material particles may be made small, and thus unevenness in conductivity of the electrode-active material may be reduced. As a result, when the electrode-active material is used as the electrode material of the lithium ion battery, the internal resistance may be reduced.
  • the electrode-active material in which the unevenness in conductivity is reduced is used as the electrode material of the lithium ion battery, a reaction related to intercalation and deintercalation of lithium ions may be uniformly carried out in the entirety of the surface of the electrode-active material, and thus the internal resistance may be reduced.
  • slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which a ratio (D90/D10) of D90 to D10 of a particle size distribution of the electrode-active material or the precursor of the electrode-active material is 5 to 30, is dried, and the resultant dried product that is obtained is baked at 500° C. to 1,000° C. in a non-oxidizing atmosphere. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material may be reduced. As a result, an electrode material capable of reducing unevenness in conductivity of the electrode-active material may be easily produced.
  • FIG. 1 is a diagram illustrating charge and discharge characteristics of Example 1 and Comparative Example 1 of the invention at room temperature, respectively.
  • FIG. 2 is a diagram illustrating charge and discharge characteristics of Example 5 and Comparative Example 4 of the invention at room temperature, respectively.
  • An electrode material of this embodiment includes an aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface, an average particle size of the aggregate is 0.5 to 100 ⁇ m, and a volume density of the aggregate is 50 to 80 vol % of the volume density in a case in which the aggregate is a solid.
  • a solid aggregate is an aggregate in which a void is not present at all, and a density of an actual aggregate is the same as a theoretical density of an electrode-active material.
  • the aggregate that is formed by aggregating each electrode-active material having the carbonaceous film formed on a surface thereof represents an aggregate in which the electrode-active materials having the carbonaceous film formed on a surface thereof are aggregated in a point contact state, and thus a contact portion of the electrode-active materials becomes a neck shape having a small cross-sectional area, whereby the electrode-active materials are strongly connected to each other.
  • the contact portion between the electrode-active materials has a neck shape having a small cross-sectional area, and thus channel-shaped (network-shaped) voids inside the aggregate have a three-dimensionally expanded structure.
  • the volume density of the aggregate is 50 vol % or more, the aggregate becomes dense, and the strength of the aggregate increases. Accordingly, for example, when the electrode-active material is mixed with a binder, a conductive auxiliary agent, and a solvent to prepare electrode slurry, the aggregate is not likely to collapse. As a result, an increase in viscosity of the electrode slurry is suppressed, and flowability is maintained. Accordingly, coating properties are improved, and filling properties of the electrode-active material in a coated film of the electrode slurry are also improved.
  • the electrode-active material contain one kind selected from the group consisting of lithium cobaltate, lithium nickelate, lithium manganate, lithium titanate, and Li x A y D z PO 4 (provided that, A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr, D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5, and 0 ⁇ z ⁇ 1.5) as a main component.
  • A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr
  • D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5
  • Co, Mn, Ni, and Fe are preferable, and with regard to D, Mg, Ca, Sr, Ba, Ti, Zn, and Al are preferable from the viewpoints of a high discharge potential, abundant resources, stability, and the like.
  • the rare-earth elements represent 15 elements of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu that belong to lanthanide series.
  • the electrode-active material 80% or more of a surface thereof is covered with a carbonaceous film, and preferably 90% or more in order for a reaction related to intercalation and deintercalation of lithium ions to be uniformly carried out over the entirety of the surface of the electrode-active material during use as an electrode material of a lithium ion battery.
  • a coverage rate of the carbonaceous film may be measured using a transmission electron microscope (TEM), and an energy dispersive X-ray spectrometer (EDX).
  • TEM transmission electron microscope
  • EDX energy dispersive X-ray spectrometer
  • an amount of carbon in the carbonaceous film be 0.6 to 10 parts by mass on the basis of 100 parts by mass of the electrode-active material, and more preferably 0.8 to 2.5 parts by mass.
  • the reason why the amount of carbon in the carbonaceous film is limited to the above-described range is as follows.
  • the amount of carbon is less than 0.6 parts by mass, the coverage rate of the carbonaceous film becomes less than 80%. Therefore, when a battery is formed, a discharge capacity at a high-speed charge and discharge rate decreases.
  • an average particle size of the aggregate be 0.5 to 100 ⁇ m, and more preferably 1 to 20 ⁇ m.
  • the reason why the average particle size of the aggregate is limited to the above-described range is as follows.
  • the average particle size is less than 0.5 ⁇ m, the aggregate is too fine, and thus there is a tendency for the aggregate to fly. Therefore, it is difficult to handle the aggregate during manufacturing of paste for electrode coating.
  • the average particle size exceeds 100 ⁇ m, when an electrode for a battery is manufactured, a possibility that an aggregate having a size larger than the film thickness of the electrode after being dried is present increases. Accordingly, it is difficult to maintain uniformity of the film thickness of the electrode.
  • the volume density of the aggregate may be measured using a mercury porosimeter, and it is preferable that the volume density be 50 to 80 vol % of the volume density in a case in which the aggregate is a solid, and more preferably, 55 to 75 vol %.
  • the volume density of the aggregate is less than 50 vol % of the volume density in the case in which the aggregate is a solid, a vapor concentration of an aromatic carbon compound in the void inside the aggregate of the electrode-active material becomes too low, and thus the film thickness of the carbonaceous film in the inner peripheral portion of the outer shell of the aggregate becomes small. Therefore, the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • the volume density of the aggregate exceeds 80 vol % of the volume density in the case in which the aggregate is a solid, the density inside the aggregate becomes too high, and thus a channel-shaped (network-shaped) void inside the aggregate decreases. As a result, a tarry material, which is generated during carbonization of the organic compound, is trapped inside the aggregate, and thus this range is not preferable.
  • a tap density of the aggregate be 1.0 to 1.5 g/cm 3 .
  • the tap density of the aggregate is less than 1.0 g/cm 3
  • an amount of a solvent that is maintained in the void inside the aggregate and an aggregate gap increases during preparation of the electrode slurry, and thus a concentration of a solid content of the electrode slurry decreases. Therefore, the time necessary to dry a coated film formed by application of the electrode slurry becomes long, and thus this range is not preferable.
  • the tap density of the aggregate exceeds 1.5 g/cm 3 , filling properties of the aggregate in the coated film obtained by the application of the electrode slurry increases too much. As a result, a solvent is not likely to vaporize at the time of drying the coated film, and thus this range is not preferable.
  • the size of the void that is formed inside the aggregate be 80% or less of a diameter of aggregate particles, and more preferably 70% or less.
  • the size of the void exceeds 80%, it is difficult to maintain a shell shape of the aggregate, and thus the concentration of the vapor of the aromatic carbon compound inside the void becomes too low. As a result, the film thickness of the carbonaceous film in the inner peripheral portion of the outer shell of the aggregate becomes small, and the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • a ratio of average film thickness of the carbonaceous film in the outer peripheral portion and the inner peripheral portion of the outer shell of the shell-like aggregate (the thickness of the carbonaceous film in the inner peripheral portion/the thickness of the carbonaceous film in the outer peripheral portion) be 0.7 to 1.3.
  • the thickness of the carbonaceous film in the outer peripheral portion or the inner peripheral portion of the outer shell of the aggregate becomes small. Therefore, the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • a method for producing an electrode material of this embodiment includes drying slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which with regard to a particle size distribution of the electrode-active material or the precursor of the electrode-active material, a ratio (D90/D10) of D90 to D10 of the particle size distribution is 5 to 30, and baking the resultant dried product that is obtained at 500° C. to 1,000° C. in a non-oxidizing atmosphere.
  • D90 represents a particle size when an accumulated vol % in the particle size distribution is 90%
  • D10 represents a particle size when the accumulated vol % in the particle size distribution is 10%
  • the electrode-active material contain one kind selected from the group consisting of lithium cobaltate, lithium nickelate, lithium manganate, lithium titanate, and Li x A y D z PO 4 (provided that, A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr, D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5, and 0 ⁇ z ⁇ 1.5) as a main component.
  • A is one or more kinds selected from the group consisting from Co, Mn, Ni, Fe, Cu, and Cr
  • D is one or more kinds selected from the group consisting of Mg, Ca, S, Sr, Ba, Ti, Zn, B, Al, Ga, In, Si, Ge, Sc, Y, and rare-earth elements, 0 ⁇ x ⁇ 2, 0 ⁇ y ⁇ 1.5
  • Co, Mn, Ni, and Fe are preferable, and with regard to D, Mg, Ca, Sr, Ba, Ti, Zn, and Al are preferable from the viewpoints of a high discharge potential, abundant resources, stability, and the like.
  • the rare-earth elements represent 15 elements of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu that belong to lanthanide series.
  • Li x A y D z PO 4 powder expressed by Li x A y D z PO 4
  • a compound, which is produced by a solid phase method, a liquid phase method, and a vapor phase method, or the like in the related art may be used.
  • a compound (Li x A y D z PO 4 powder) that is obtained by the following method may be appropriately used.
  • the method includes: hydrothermally synthesizing a slurry mixture, which is obtained by mixing a Li source selected from the group consisting of lithium salts such as lithium acetate (LiCH 3 COO) and lithium chloride (LiCl) or lithium hydroxide (LiOH), bivalent iron salts such as iron (II) chloride (FeCl 2 ), iron (II) acetate (Fe(CH 3 COO) 2 ), and iron (II) sulfate (FeSO 4 ), phosphate compounds such as phosphoric acid (H 3 PO 4 ), ammonium dihydrogen phosphate (NH 4 H 2 PO 4 ), diammonium hydrogen phosphate ((NH 4 ) 2 HPO 4 ), and water, using a pressure-resistant airtight container; washing a precipitation of the Li source selected from the group consisting of lithium salts such as lithium
  • the Li x A y D z PO 4 powder may be a crystalline particle, an amorphous particle, or a mixed crystal particle in which a crystalline particle and an amorphous particle coexist.
  • the reason why the Li x A y D z PO 4 powder may be an amorphous particle is that when being thermally treated in a non-oxidizing atmosphere at 500° C. to 1,000° C., the amorphous Li x A y D z PO 4 powder is crystalized.
  • the size of the electrode-active material is not particularly limited, but it is preferable that an average particle size of primary particles be 0.01 to 20 ⁇ m, and more preferably 0.02 to 5 ⁇ m.
  • the reason why the average particle size of the primary particles of the electrode-active material is limited to the above-described range is as follows.
  • the average particle size of the primary particles is less than 0.01 ⁇ m, it is difficult to sufficiently cover the surface of each of the primary particles with a thin film-shaped carbon, and thus a discharge capacity at a high-speed charge and discharge rate becomes low. As a result, it is difficult to realize a sufficient charge and discharge rate performance, and thus this range is not preferable.
  • the average particle size of the primary particles exceeds 20 ⁇ m, the internal resistance of the primary particles increases. Therefore, the discharge capacity at a high-speed charge and discharge rate becomes insufficient, and thus this range is not preferable.
  • the shape of the electrode-active material is not particularly limited. However, from the viewpoints that an electrode material constituted by secondary particles having a spherical shape, particularly, a real spherical shape may be easily generated, it is preferable that the shape of the electrode-active material be a spherical shape, particularly a real spherical shape.
  • the shape of the electrode-active material be a spherical shape is as follows.
  • a paste for a positive electrode by mixing an electrode-active material, a binder resin (binding agent), and a solvent, an amount of solvent may be reduced, and the paste for the positive electrode may be easily plated on a current collector.
  • the shape of the electrode-active material is a spherical shape
  • a surface area of the electrode-active material becomes the minimum, and thus a mixing amount of the binder resin (binding agent) that is added to an electrode material mixture may be the minimum. Accordingly, the internal resistance of the positive electrode that is obtained may be made small, and thus this shape is preferable.
  • the electrode-active material is closely packed, and thus a filled amount of the positive material per unit volume increases. Accordingly, an electrode density may be increased. As a result, high-capacity of the lithium ion battery may be realized, and thus this shape is preferable.
  • examples of the organic compound include polyvinyl alcohol, polyvinyl pyrrolidone, cellulose, starch, gelatin, carboxymethyl cellulose, methyl cellulose, hydroxymethyl cellulose, hydroxyethyl cellulose, polyacrylic acid, polystyrene sulfonate, polyacrylamide, polyvinyl acetate, glucose, fructose, galactose, mannose, maltose, sucrose, lactose, glycogen, pectin, alginic acid, glucomannan, chitin, hyaluronic acid, chondroitin, agarose, polyether, and polyvalent alcohols.
  • a mixing ratio of the electrode-active material and the organic compound be 0.6 to 10 parts by mass on the basis of 100 parts by mass of the electrode-active material, and more preferably 0.8 to 2.5 parts by mass.
  • the mixing ratio of the organic compound in terms of the amount of carbon is less than 0.6 parts by mass, the coverage rate of the carbonaceous film is less than 80%. Therefore, when a battery is formed, a discharge capacity at a high-speed charge and discharge rate decreases. As a result, it is difficult to realize a sufficient charge and discharge rate performance.
  • the mixing ratio of the organic compound in terms of the amount of carbon exceeds 10 parts by mass, the mixing ratio of the electrode-active material relatively decreases. Therefore, when a battery is formed, a battery capacity decreases, and the volume of the electrode-active material increases due to excessive supporting of the carbonaceous film. As a result, an electrode density decreases, and thus the battery capacity of the lithium ion battery per unit volume considerably decreases.
  • the electrode-active material and the organic compound may be dissolved or dispersed in water to prepare uniform slurry. During the dissolution or dispersion, a dispersant may be added.
  • a method of dissolving or dispersing the electrode-active material or the organic compound in water is not particularly limited as long as the electrode-active material may be dispersed, and the organic compound may be dissolved or dispersed.
  • a medium stirring type dispersing apparatus such as a planetary ball mill, a vibration ball mill, a bead mill, a painter shaker, and an attritor that stirs medium particles at a high speed is preferably used.
  • the stirring it is preferable to perform the stirring in such a manner that the electrode-active material is dispersed as a primary particle, and then the organic compound is dissolved. In this manner, a surface of the primary particle of the electrode-active material is covered with the organic compound. As a result, carbon originating from the organic compound is uniformly interposed between primary particles of the electrode-active material.
  • a ratio (D90/D10) of D90 to D10 of the particle size distribution becomes 5 to 30. According to this, a tap density of the aggregate that is obtained by spraying and drying the slurry becomes 1.0 g/cm 3 .
  • the slurry is sprayed and dried in the air and in a high-temperature atmosphere, for example, 70° C. to 250° C.
  • an average diameter of liquid droplets during the spraying be 0.05 to 100 ⁇ m, and more preferably 1 to 20 ⁇ m.
  • a dried product having an average particle size of 0.5 to 100 ⁇ m, and preferably 1 to 20 ⁇ m may be obtained.
  • the dried product is baked in a non-oxidizing atmosphere at a temperature within a range of 500° C. to 1,000° C., and preferably 600° C. to 900° C. for 0.1 hours to 40 hours.
  • an inert atmosphere of nitrogen (N 2 ), argon (Ar), or the like is preferable.
  • a reducing atmosphere containing a reducing gas such as hydrogen (H 2 ) is preferable.
  • a burnable or combustible gas such as oxygen (O 2 ) may be introduced to the inert atmosphere to remove an organic component that is vaporized in the non-oxidizing atmosphere during the baking.
  • the reason why the baking temperature is set to 500° C. to 1,000° C. is as follows.
  • the baking temperature is lower than 500° C.
  • the decomposition reaction of an organic compound contained in the dried product does not progress sufficiently, and thus carbonization of the organic compound becomes insufficient.
  • a highly resistive decomposed product of the organic material is generated in the aggregate that is obtained.
  • the baking temperature is higher than 1,000° C.
  • Li in the electrode-active material is evaporated, and a compositional deviation occurs in the electrode-active material, and grain growth of the electrode-active material is promoted.
  • the discharge capacity in the high charge and discharge rate decreases, and thus it is difficult to realize a sufficient charge and discharge rate performance.
  • the particle size distribution of the aggregate that is obtained may be controlled by appropriately adjusting conditions during the baking of the dried product, for example, a temperature rising rate, the maximum holding temperature, a holding time, and the like.
  • the surface of the primary particles of the electrode-active material is covered with carbon that is generated by the thermal decomposition of the organic compound in the dried product, and thus aggregate including secondary particles in which carbon is interposed between the primary particles of the electrode-active material may be obtained.
  • This aggregate is used as the electrode material of this embodiment.
  • the average particle size of the aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface thereof is set to 0.5 to 100 ⁇ m, and a volume density of the aggregate is set to 50 to 80 vol % of the volume density in a case in which the aggregate is a solid, and thus unevenness in a supporting amount of the carbonaceous film formed on a surface of the electrode-active material may be reduced, and thus unevenness in conductivity of the electrode-active material may be reduced. Accordingly, when the electrode-active material is used as an electrode material of a lithium ion battery, the internal resistance may be reduced.
  • slurry which contains an electrode-active material or a precursor of the electrode-active material, and an organic compound, and in which with regard to the particle size distribution of the electrode-active material or the precursor of the electrode-active material, a ratio (D90/D10) of D90 to D10 of the particle size distribution is 5 to 30, is dried, and the resultant dried product that is obtained is baked at 500° C. to 1,000° C. in a non-oxidizing atmosphere. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material may be reduced. As a result, an electrode material capable of reducing unevenness in conductivity of the electrode-active material may be easily produced.
  • metal Li is used for a negative electrode to reflect the behavior of the electrode material itself on data, but, a negative electrode material such as a carbon material, a Li alloy, and Li 4 Ti 5 O 12 may be used.
  • a solid electrolyte may be used instead of an electrolyte and a separator.
  • LiCH 3 COO LiCH 3 COO
  • iron (II) sulfate FeSO 4
  • H 3 PO 4 2 mol phosphoric acid
  • the slurry that was obtained was sprayed in the air atmosphere at 180° C. and was dried to obtain a dried product having an average particle size of 6 ⁇ m.
  • Example 1 the dried product that was obtained was baked in a nitrogen atmosphere at 700° C. for one hour to obtain an aggregate having an average particle size of 6 ⁇ m, and this aggregate was set as an electrode material of Example 1.
  • a volume density of the aggregate of the electrode material, a maximum void inside the aggregate, a ratio of an average film thickness of a carbonaceous film (a thickness of the carbonaceous film in an inner peripheral portion/a thickness of the carbonaceous film in an outer peripheral portion), a tap density, and a coverage rate of the carbonaceous film were evaluated, respectively.
  • the volume density of the aggregate was measured using a mercury porosimeter.
  • a cross-section of the aggregate was observed using a scanning electron microscope (SEM) to measure a maximum value of the void inside the aggregate.
  • SEM scanning electron microscope
  • the carbonaceous film of the aggregate was observed using a transmission electron microscope (TEM) to measure the thickness of the carbonaceous film in the inner peripheral portion of the aggregate and the thickness of the carbonaceous film in the outer peripheral portion thereof, and the ratio of the average film thickness of the carbonaceous film (the thickness of the carbonaceous film in the inner peripheral portion/the thickness of the carbonaceous film in the outer peripheral portion) was calculated.
  • TEM transmission electron microscope
  • the tap density was measured according to Japanese Industrial Standard JIS R 1628 “Test method for bulk density of fine ceramic powder.”
  • the carbonaceous film of the aggregate was observed using the transmission electron microscope (TEM) and an energy dispersive X-ray spectrometer (EDX) to calculate a ratio of a portion covered with the carbonaceous film on the surface of the aggregate, and this ratio was set to the coverage rate.
  • TEM transmission electron microscope
  • EDX energy dispersive X-ray spectrometer
  • the electrode material, polyvinylidene fluoride (PVdF) as a binder, and acetylene black (AB) as a conductive auxiliary agent were mixed in a mass ratio of 90:5:5, and N-methyl-2-pyrrolidone (NMP) as a solvent was further added to the resultant mixture to give flowability, whereby slurry was prepared.
  • PVdF polyvinylidene fluoride
  • AB acetylene black
  • NMP N-methyl-2-pyrrolidone
  • Example 1 a positive electrode of a lithium ion battery of Example 1 was prepared.
  • a lithium metal as a negative electrode was disposed with respect to the positive electrode of the lithium ion battery, a separator formed from porous polypropylene was disposed between the positive electrode and the negative electrode, and the resultant member was set as a member for a battery.
  • Example 1 a lithium ion battery of Example 1 was prepared.
  • An evaluation method is as follows.
  • a charge and discharge test of the above-described lithium ion battery was carried out under conditions of room temperature (25° C.), a cut-off voltage of 2 to 4.5 V, and a constant current at a charge and discharge rate of 1 C (discharge for one hour after charge of one hour).
  • the charge and discharge characteristics are shown in FIG. 1 .
  • voltage drop recognized at a final stage of discharge represents presence of the electrode-active material not covered with the carbonaceous film. Accordingly, a sample in which the voltage drop was significantly recognized was determined as a sample with high internal resistance.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 10. Then, evaluation was performed. Evaluation results are shown in Table 1.
  • Example 2 the same voltage drop at the final stage of discharge as Example 1 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 20. Then, evaluation was performed. Evaluation results are shown in Table 1.
  • Example 3 the same voltage drop at the final stage of discharge as Example 1 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 25. Then, evaluation was performed. Evaluation results are shown in Table 1.
  • Example 4 the same voltage drop at the final stage of discharge as Example 1 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 1.5. Then, evaluation was performed. Evaluation results are shown in Table 1, and the charge and discharge characteristics are shown in FIG. 1 , respectively.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 3. Then, evaluation was performed. Evaluation results are shown in Table 1.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 1 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 40. Then, evaluation was performed. Evaluation results are shown in Table 1.
  • the ratio of the average film thickness of the carbonaceous film was within a range of 0.7 to 1.3, the tap density and the coverage rate of the carbonaceous film was high compared to the electrode materials of Comparative Examples 1 to 3, and unevenness in the supporting amount of the carbonaceous film formed on the surface of the electrode-active material was small.
  • the internal resistance was low compared to the electrode materials of the Comparative Examples 1 to 3, and when being used as the electrode material of the lithium ion battery, the internal resistance may be reduced.
  • the electrode material of this embodiment includes an aggregate formed by aggregating electrode-active material particles having a carbonaceous film formed on a surface, an average particle size of the aggregate is 0.5 to 100 ⁇ m, a pore size (D50) when an accumulated volume percentage of a pore size distribution of the aggregate is 50% is 0.1 to 0.2 ⁇ m, and porosity of the aggregate is 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid.
  • a solid aggregate is an aggregate in which a void is not present at all, and a density of the solid aggregate is the same as a theoretical density of an electrode-active material.
  • the pore size distribution of the aggregate may be measured using a mercury porosimeter.
  • the pore size (D50) when the accumulated volume percentage of the pore size distribution of the aggregate is 50% is preferably 0.1 to 0.2 ⁇ m.
  • D50 of the pore size distribution of the aggregate is limited is as follows.
  • D50 is less than 0.1 ⁇ m, the density inside the aggregate becomes too high, and thus a channel-shaped (network-shaped) void inside the aggregate decreases.
  • a tarry material which is generated during carbonization of the organic compound, is trapped inside the aggregate, and thus this range is not preferable.
  • D50 exceeds 0.2 ⁇ m, a vapor concentration of an aromatic carbon compound in the void inside the aggregate of the electrode-active material becomes too low, and thus the film thickness of the carbonaceous film in the inner peripheral portion of the outer shell of the aggregate becomes small. Therefore, the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • the porosity of the aggregate may be measured using the mercury porosimeter.
  • the porosity of the aggregate be 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid, and more preferably 20 to 45 vol %.
  • the porosity of the aggregate when the porosity of the aggregate is less than 15 vol % with respect to the volume in a case in which the aggregate is a solid, the density inside the aggregate becomes too high, and thus a channel-shaped (network-shaped) void inside the aggregate decreases. As a result, a tarry material, which is generated during carbonization of the organic compound, is trapped inside the aggregate, and thus this range is not preferable.
  • the porosity exceeds 50 vol % with respect to the volume in a case in which the aggregate is a solid, a vapor concentration of an aromatic carbon compound in the void inside the aggregate of the electrode-active material becomes too low, and thus the film thickness of the carbonaceous film in the inner peripheral portion of the outer shell of the aggregate becomes small. Therefore, the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • the aggregate becomes dense, and the strength of the aggregate increases. Accordingly, for example, when the electrode-active material is mixed with the binder, the conductive auxiliary agent, and the solvent to prepare electrode slurry, the aggregate is not likely to collapse. As a result, an increase in viscosity of the electrode slurry is suppressed, and flowability is maintained. Accordingly, coating properties are improved, and filling properties of the electrode-active material in a coated film of the electrode slurry are also improved.
  • the size of the void that is formed inside the aggregate be 80% or less of a diameter of aggregate particles, and more preferably 70% or less.
  • the size (diameter) of the void exceeds 80% of the diameter of the aggregate particles, it is difficult to maintain a shell shape of the aggregate, and thus the concentration of the vapor of the aromatic carbon compound inside the void becomes too low. As a result, the film thickness of the carbonaceous film in the inner peripheral portion of the outer shell of the aggregate becomes small, and the internal resistance of the electrode-active material increases, and thus this range is not preferable.
  • the porosity of the aggregate is set to 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material particles may be made small, and thus unevenness in conductivity of the electrode-active material may be reduced.
  • the electrode-active material in which the unevenness in conductivity is reduced is used as the electrode material of the lithium ion battery, a reaction related to intercalation and deintercalation of lithium ions may be uniformly carried out in the entirety of the surface of the electrode-active material, and thus the internal resistance may be reduced.
  • the “internal resistance” described above represents internal resistance at a site at which reaction resistance related to intercalation and deintercalation of lithium ions is high in a particle, which does not have the carbonaceous film formed on a surface thereof or in which the thickness of the carbonaceous film is small, of the electrode-active material.
  • the internal resistance is shown as a magnitude of voltage drop at the final stage of discharge. That is, in an electrode-active material in which the intercalation and deintercalation reaction of lithium ions is uniformly carried out over the entirety of the surface of the electrode-active material, the voltage drop at the final stage of discharge is small.
  • the voltage drop at the final stage of discharge becomes significant.
  • the average particle size of the aggregate formed by aggregating electrode-active material particles having the carbonaceous film formed on a surface is set to 0.5 to 100 ⁇ m, and the pore size (D50) when the accumulated volume percentage of the pore size distribution of the aggregate is 50% is set to 0.1 to 0.2 ⁇ m, and the porosity of the aggregate is set to 15 to 50 vol % with respect to a volume in a case in which the aggregate is a solid. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material may be made small, and thus unevenness in conductivity of the electrode-active material may be reduced. As a result, when the electrode-active material is used as the electrode material of the lithium ion battery, the internal resistance may be reduced.
  • the slurry which contains the electrode-active material or the precursor of the electrode-active material, and the organic compound, and in which the ratio (D90/D10) of the particle size (D90) when the accumulated volume percentage of the particle size distribution of the electrode-active material or the precursor of the electrode-active material is 90% to the particle size (D10) when the accumulated volume percentage is 10% is 5 to 30, is dried; and the resultant dried product that is obtained is baked at 500° C. to 1,000° C. in a non-oxidizing atmosphere. Accordingly, unevenness in the supporting amount of the carbonaceous film formed on the surface of the electrode-active material may be reduced. As a result, an electrode material capable of reducing unevenness in conductivity of the electrode-active material may be easily produced.
  • LiCH 3 COO LiCH 3 COO
  • iron (II) sulfate FeSO 4
  • H 3 PO 4 2 mol phosphoric acid
  • the slurry that was obtained was sprayed in the air atmosphere at 180° C., and was dried to obtain a dried product having an average particle size of 6 ⁇ m.
  • the dried product that was obtained was baked in a nitrogen atmosphere at 700° C. for one hour to obtain an aggregate having an average particle size of 6 ⁇ m, and this aggregate was set as an electrode material of Example 5.
  • the pore size distribution (D50) of the aggregate of the electrode material, the porosity of the aggregate, the ratio of the average film thickness of the carbonaceous film (the thickness of the carbonaceous film in the inner peripheral portion/the thickness of the carbonaceous film in the outer peripheral portion), the tap density, and the coverage rate of the carbonaceous film were evaluated, respectively.
  • the pore size distribution (D50) was measured using the mercury porosimeter.
  • the porosity of the aggregate was measured using the mercury porosimeter.
  • the carbonaceous film of the aggregate was observed using a transmission electron microscope (TEM) to measure the thickness of the carbonaceous film in the inner peripheral portion of the aggregate and the thickness of the carbonaceous film in the outer peripheral portion thereof, and the ratio of the average film thickness of the carbonaceous film (the thickness of the carbonaceous film in the inner peripheral portion/the thickness of the carbonaceous film in the outer peripheral portion) was calculated.
  • TEM transmission electron microscope
  • the tap density was measured according to Japanese Industrial Standard JIS R 1628 “Test method for bulk density of fine ceramic powder.”
  • the carbonaceous film of the aggregate was observed using the transmission electron microscope (TEM) and an energy dispersive X-ray spectrometer (EDX) to calculate a ratio of a portion covered with the carbonaceous film on the surface of the aggregate, and this ratio was set to the coverage rate. Evaluation results are shown in Table 2.
  • the electrode material, polyvinylidene fluoride (PVdF) as a binder, and acetylene black (AB) as a conductive auxiliary agent were mixed in a mass ratio of 90:5:5, and N-methyl-2-pyrrolidone (NMP) as a solvent was further added to the resultant mixture to give flowability, whereby slurry was prepared.
  • PVdF polyvinylidene fluoride
  • AB acetylene black
  • NMP N-methyl-2-pyrrolidone
  • Example 5 a positive electrode of a lithium ion battery of Example 5 was prepared.
  • a lithium metal as a negative electrode was disposed with respect to the positive electrode of the lithium ion battery, a separator formed from porous polypropylene was disposed between the positive electrode and the negative electrode, and the resultant member was set as a member for a battery.
  • An evaluation method is as follows.
  • a charge and discharge test of the above-described lithium ion battery was carried out under conditions of room temperature (25° C.), a cut-off voltage of 2 to 4.5 V, and a constant current at a charge and discharge rate of 1 C (discharge for one hour after charge of one hour).
  • An initial discharge capacity is shown in Table 3, and the charge and discharge characteristics are shown in FIG. 2 , respectively.
  • voltage drop recognized at a final stage of discharge represents presence of the electrode-active material not covered with the carbonaceous film. Accordingly, a sample in which the voltage drop was significantly recognized was determined as a sample with high internal resistance.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 10. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • Example 6 the same voltage drop at the final stage of discharge as Example 5 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 20. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • Example 7 the same voltage drop at the final stage of discharge as Example 5 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 25. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • Example 8 the same voltage drop at the final stage of discharge as Example 5 was also recognized.
  • a precursor of an electrode-active material of Example 9 was obtained in the same manner as Example 5 except that manganese
  • An electrode material and a positive electrode of the lithium ion battery of Example 9 were prepared in the same manner as Example 5 except that a precursor of iron lithium phosphate as a carbonization catalyst was added to the aqueous polyvinyl alcohol solution in the same mass as that of a polyvinyl alcohol solid content in the aqueous polyvinyl alcohol solution. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • Example 9 the same voltage drop at the final stage of discharge as Example 5 was also recognized.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 1.5. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3, and charge and discharge characteristics are shown in FIG. 2 , respectively.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 3. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • An electrode material, and a positive electrode of the lithium ion battery were prepared in the same manner as Example 5 except that the stirring time of the ball mill was adjusted so that D90/D10 of the particle size distribution of the precursor particle of the electrode-active material in the slurry became 40. Then, evaluation was performed. Evaluation results are shown in Tables 2 and 3.
  • the ratio of the average film thickness of the carbonaceous film was within a range of 0.7 to 1.3, the tap density and the coverage rate of the carbonaceous film was high compared to the electrode materials of Comparative Examples 4 to 6, and unevenness in the supporting amount of the carbonaceous film formed on the surface of the electrode-active material was small.
  • the internal resistance was low compared to the electrode materials of the Comparative Examples 4 to 6, and when being used as the electrode material of the lithium ion battery, the internal resistance may be greatly reduced.
  • the average particle size of the aggregate formed by aggregating electrode-active material having the carbonaceous film formed on a surface thereof is set to 0.5 to 100 ⁇ m, and the volume density of the aggregate is set to 50 to 80 vol % of the volume density in a case in which the aggregate is a solid. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material may be reduced. As a result, unevenness in conductivity of the electrode-active material may be reduced. In addition, when the electrode material is used as the electrode material of the lithium ion battery, the internal resistance may be reduced.
  • the electrode material may be applied to a next-generation secondary battery in which better miniaturization, lightness, and high capacity are expected, and in the case of the next-generation secondary battery, the effect will be significant.
  • the average particle size of the aggregate formed by aggregating the electrode-active material particles having the carbonaceous film formed on a surface thereof is set to 0.5 to 100 ⁇ m
  • the pore size (D50) when the accumulated volume percentage of the pore size distribution of the aggregate is 50% is set to 0.1 to 0.2 ⁇ m
  • porosity of the aggregate is set to 15 to 50 vol % with respect to the volume in a case in which the aggregate is a solid. Accordingly, unevenness in a supporting amount of the carbonaceous film formed on the surface of the electrode-active material particles may be reduced. As a result, unevenness in conductivity of the electrode-active material may be reduced.
  • the electrode material when used as the electrode material of the lithium ion battery, the internal resistance may be greatly reduced. Accordingly, a new improvement in the discharge characteristics of the lithium ion battery may be made, and the electrode material may be applied to a next-generation secondary battery in which further miniaturization, lightness, and high capacity are expected, and in the case of the next-generation secondary battery, the effect will be significant.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Composite Materials (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Battery Electrode And Active Subsutance (AREA)
US13/993,403 2010-12-17 2011-11-28 Electrode material and method for producing the same Abandoned US20130260245A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
JP2010282353 2010-12-17
JP2010282353A JP2012133888A (ja) 2010-12-17 2010-12-17 電極材料及びその製造方法
JP2011207833 2011-09-22
JP2011207833A JP6077205B2 (ja) 2011-09-22 2011-09-22 電極材料及びその製造方法
PCT/JP2011/077394 WO2012081383A1 (fr) 2010-12-17 2011-11-28 Matériau d'électrode et son procédé de production

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/077394 A-371-Of-International WO2012081383A1 (fr) 2010-12-17 2011-11-28 Matériau d'électrode et son procédé de production

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/567,384 Continuation US9698425B2 (en) 2010-12-17 2014-12-11 Electrode material and method for producing the same

Publications (1)

Publication Number Publication Date
US20130260245A1 true US20130260245A1 (en) 2013-10-03

Family

ID=46244494

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/993,403 Abandoned US20130260245A1 (en) 2010-12-17 2011-11-28 Electrode material and method for producing the same
US14/567,384 Active US9698425B2 (en) 2010-12-17 2014-12-11 Electrode material and method for producing the same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/567,384 Active US9698425B2 (en) 2010-12-17 2014-12-11 Electrode material and method for producing the same

Country Status (7)

Country Link
US (2) US20130260245A1 (fr)
EP (1) EP2654110B1 (fr)
KR (1) KR20140051814A (fr)
CN (1) CN103270628B (fr)
CA (1) CA2821882A1 (fr)
TW (1) TW201232905A (fr)
WO (1) WO2012081383A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160036042A1 (en) * 2013-03-15 2016-02-04 Johnson Matthey Public Limited Company Lithium transition metal phosphate secondary agglomerates and process for its manufacture
US20160093878A1 (en) * 2014-09-30 2016-03-31 Sumitomo Osaka Cement Co., Ltd. Electrode material, electrode, and lithium ion battery
US20160172664A1 (en) * 2013-11-28 2016-06-16 Sumitomo Osaka Cement Co., Ltd. Electrode material and method for producing same
EP3142173A4 (fr) * 2014-05-07 2017-10-04 Eliiy Power Co., Ltd. Électrode positive pour accumulateurs à électrolyte non aqueux et accumulateur à électrolyte non aqueux
US9865868B2 (en) 2013-05-15 2018-01-09 Shin-Etsu Chemical Co., Ltd. Negative electrode material for use in non-aqueous electrolyte secondary battery, method of producing the same, and lithium-ion secondary battery
US11283059B2 (en) * 2017-02-21 2022-03-22 Panasonic Corporation Positive electrode active material for nonaqueous electrolyte secondary batteries, and nonaqueous electrolyte secondary battery

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2821882A1 (fr) 2010-12-17 2012-06-21 Sumitomo Osaka Cement Co., Ltd. Materiau d'electrode et son procede de production
JP5621740B2 (ja) * 2011-09-22 2014-11-12 住友大阪セメント株式会社 電極材料及び電極並びに電極材料の製造方法
TW201342697A (zh) * 2012-03-30 2013-10-16 Sumitomo Osaka Cement Co Ltd 電極材料
JP2014060142A (ja) * 2012-08-24 2014-04-03 Sumitomo Osaka Cement Co Ltd 電極材料とリチウムイオン電池用電極ペースト及びリチウムイオン電池用電極並びにリチウムイオン電池
EP2778127A1 (fr) * 2013-03-15 2014-09-17 Clariant International Ltd. Agglomérats secondaires de phosphate de métal de transition au lithium et leur procédé de fabrication
JP2014179291A (ja) 2013-03-15 2014-09-25 Sumitomo Osaka Cement Co Ltd 電極材料及び電極並びにリチウムイオン電池
JP6055453B2 (ja) * 2014-10-20 2016-12-27 住友大阪セメント株式会社 正極材料およびリチウムイオン電池
CN106784987A (zh) * 2015-11-23 2017-05-31 深圳市比克动力电池有限公司 锂离子电池负极材料、负极和锂离子电池
JP6848249B2 (ja) * 2016-07-29 2021-03-24 住友金属鉱山株式会社 非水系電解質二次電池用正極活物質とその製造方法、及び非水系電解質二次電池

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040214087A1 (en) * 1999-02-24 2004-10-28 Kyou-Yoon Sheem Negative active material for rechargeable lithium battery and method of preparing same
US20090142668A1 (en) * 2007-11-30 2009-06-04 Sony Corporation Cathode active material, cathode, and nonaqueous electrolyte secondary battery
US20100021820A1 (en) * 2006-11-10 2010-01-28 Kenta Ishii Negative electrode material for lithium ion secondary battery and method for producing the same
US20100233545A1 (en) * 2009-03-16 2010-09-16 Tdk Corporation Active material, method of manufacturing active material, electrode, and lithium-ion secondary battery
US20100261063A1 (en) * 2007-12-10 2010-10-14 Sumitomo Osaka Cement Co., Ltd. Electrode material, method for producing the same, electrode and battery
US20110195308A1 (en) * 2010-02-09 2011-08-11 So-Ra Lee Secondary particle and lithium battery including secondary particle

Family Cites Families (41)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000058040A (ja) * 1998-08-04 2000-02-25 Toyota Central Res & Dev Lab Inc リチウム二次電池用正極材料
EP1094533A1 (fr) 1999-04-06 2001-04-25 Sony Corporation Materiau actif pour plaque positive, cellule secondaire a electrolyte non aqueuse, et leurs procedes de fabrication respectifs
CA2270771A1 (fr) 1999-04-30 2000-10-30 Hydro-Quebec Nouveaux materiaux d'electrode presentant une conductivite de surface elevee
JP3921931B2 (ja) 2000-09-29 2007-05-30 ソニー株式会社 正極活物質及び非水電解質電池
US20030160215A1 (en) 2002-01-31 2003-08-28 Zhenhua Mao Coated carbonaceous particles particularly useful as electrode materials in electrical storage cells, and methods of making the same
JP3987853B2 (ja) 2002-02-07 2007-10-10 日立マクセル株式会社 電極材料およびその製造方法、並びに非水二次電池およびその製造方法
JP2003308845A (ja) 2002-04-17 2003-10-31 Mikuni Color Ltd リチウム二次電池用電極及びこれを用いたリチウム二次電池
KR100477970B1 (ko) * 2002-12-26 2005-03-23 삼성에스디아이 주식회사 리튬 이차 전지용 음극 활물질 및 그의 제조 방법
JP4190930B2 (ja) 2003-03-28 2008-12-03 住友大阪セメント株式会社 リチウム金属リン酸塩化合物微粒子およびその製造方法
JP4641375B2 (ja) 2003-10-20 2011-03-02 日立マクセル株式会社 オリビン型リン酸リチウムと炭素材料との複合体の製造方法
DE10353266B4 (de) 2003-11-14 2013-02-21 Süd-Chemie Ip Gmbh & Co. Kg Lithiumeisenphosphat, Verfahren zu seiner Herstellung und seine Verwendung als Elektrodenmaterial
JP2005158401A (ja) 2003-11-25 2005-06-16 Toyota Motor Corp 正極活物質およびその製造方法ならびにリチウムイオン二次電池
JP4794833B2 (ja) 2004-07-21 2011-10-19 日本コークス工業株式会社 リチウムイオン二次電池用正極材料、その製造方法、及びリチウムイオン二次電池
JP4519592B2 (ja) 2004-09-24 2010-08-04 株式会社東芝 非水電解質二次電池用負極活物質及び非水電解質二次電池
JP2007173134A (ja) 2005-12-26 2007-07-05 Sumitomo Osaka Cement Co Ltd リチウムイオン電池の電極用材料、リチウムイオン電池の電極形成用スラリーおよびリチウムイオン電池
JP2007250417A (ja) 2006-03-17 2007-09-27 Sumitomo Osaka Cement Co Ltd 電極材料及びその製造方法並びにリチウムイオン電池
US8535829B2 (en) 2006-04-07 2013-09-17 Mitsubishi Chemical Corporation Lithium transition metal-based compound powder for positive electrode material in lithium rechargeable battery, method for manufacturing the powder, spray dried product of the powder, firing precursor of the powder, and positive electrode for lithium rechargeable battery and lithium rechargeable battery using the powder
CA2569991A1 (fr) * 2006-12-07 2008-06-07 Michel Gauthier Nanoparticules traitees au c, agglomerat et composite comportant ces nanoparticules comme materiaux pour cathode a polyanion de matal de transition et procede pour les fabriquer
CA2672952C (fr) 2006-12-22 2014-08-05 Umicore Synthese d'une poudre de limnpo4 nanometrique cristalline electroactive
US8771877B2 (en) 2006-12-28 2014-07-08 Gs Yuasa International Ltd. Positive electrode material for nonaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery including the same, and method for producing the same
JP2009129587A (ja) * 2007-11-20 2009-06-11 Agc Seimi Chemical Co Ltd 電池用電極活物質及びその製造方法
US20090155689A1 (en) 2007-12-14 2009-06-18 Karim Zaghib Lithium iron phosphate cathode materials with enhanced energy density and power performance
CN101540398A (zh) * 2008-03-17 2009-09-23 中国科学院物理研究所 一种用于锂二次电池的介孔结构磷酸盐材料及其制备方法
CN101999187A (zh) 2008-04-25 2011-03-30 住友大阪水泥股份有限公司 锂离子电池用正极活性物质的制造方法、由该制造方法获得的锂离子电池用正极活性物质、锂离子电池用电极、及锂离子电池
EP2339675B1 (fr) * 2008-10-22 2013-10-02 Lg Chem, Ltd. Matériau actif pour électrode positive ayant une efficacité d'électrode et des caractéristiques de densité d'énergie améliorées
JP5957728B2 (ja) * 2008-10-22 2016-07-27 エルジー・ケム・リミテッド オリビン構造を有するリン酸リチウム鉄の製造方法
JP2010157405A (ja) * 2008-12-26 2010-07-15 Toda Kogyo Corp 非水電解質二次電池用ポリアニオン系正極活物質及びその製造方法、並びに非水電解質二次電池
JP5436896B2 (ja) * 2009-03-17 2014-03-05 日本化学工業株式会社 リチウムリン系複合酸化物炭素複合体、その製造方法、リチウム二次電池用正極活物質及びリチウム二次電池
JP2010232091A (ja) * 2009-03-27 2010-10-14 Sumitomo Osaka Cement Co Ltd リチウムイオン電池用正極活物質の製造方法とリチウムイオン電池用正極活物質及びリチウムイオン電池用電極並びにリチウムイオン電池
JP5509918B2 (ja) * 2009-03-27 2014-06-04 住友大阪セメント株式会社 リチウムイオン電池用正極活物質の製造方法とリチウムイオン電池用正極活物質及びリチウムイオン電池用電極並びにリチウムイオン電池
KR20170091774A (ko) 2009-04-27 2017-08-09 바티움 캐나다 인크. 리튬 전기화학 전지용 전극 및 전극 물질
US9682861B2 (en) 2009-05-04 2017-06-20 Meecotech, Inc. Electrode active composite materials and methods of making thereof
DE102009020832A1 (de) * 2009-05-11 2010-11-25 Süd-Chemie AG Verbundmaterial enthaltend ein gemischtes Lithium-Metalloxid
JP5359614B2 (ja) 2009-07-01 2013-12-04 セイコーエプソン株式会社 入出力インターフェース回路、集積回路装置および電子機器
CN102246333A (zh) 2009-09-18 2011-11-16 松下电器产业株式会社 非水电解质二次电池用电极及其制造方法以及非水电解质二次电池
JP2011076820A (ja) 2009-09-30 2011-04-14 Hitachi Vehicle Energy Ltd リチウム二次電池及びリチウム二次電池用正極
JP2011210649A (ja) 2010-03-30 2011-10-20 Mitsui Eng & Shipbuild Co Ltd 二次電池用の炭素被覆電極材料の製造方法及び炭素被覆電極材料
JP2012104290A (ja) 2010-11-08 2012-05-31 Sony Corp 非水電解質電池用正極活物質、非水電解質電池用正極および非水電解質電池
JP2012133888A (ja) 2010-12-17 2012-07-12 Sumitomo Osaka Cement Co Ltd 電極材料及びその製造方法
CA2821882A1 (fr) 2010-12-17 2012-06-21 Sumitomo Osaka Cement Co., Ltd. Materiau d'electrode et son procede de production
JP2014179291A (ja) 2013-03-15 2014-09-25 Sumitomo Osaka Cement Co Ltd 電極材料及び電極並びにリチウムイオン電池

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040214087A1 (en) * 1999-02-24 2004-10-28 Kyou-Yoon Sheem Negative active material for rechargeable lithium battery and method of preparing same
US20100021820A1 (en) * 2006-11-10 2010-01-28 Kenta Ishii Negative electrode material for lithium ion secondary battery and method for producing the same
US20090142668A1 (en) * 2007-11-30 2009-06-04 Sony Corporation Cathode active material, cathode, and nonaqueous electrolyte secondary battery
US20100261063A1 (en) * 2007-12-10 2010-10-14 Sumitomo Osaka Cement Co., Ltd. Electrode material, method for producing the same, electrode and battery
US20100233545A1 (en) * 2009-03-16 2010-09-16 Tdk Corporation Active material, method of manufacturing active material, electrode, and lithium-ion secondary battery
US20110195308A1 (en) * 2010-02-09 2011-08-11 So-Ra Lee Secondary particle and lithium battery including secondary particle

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160036042A1 (en) * 2013-03-15 2016-02-04 Johnson Matthey Public Limited Company Lithium transition metal phosphate secondary agglomerates and process for its manufacture
US10707479B2 (en) * 2013-03-15 2020-07-07 Johnson Matthey Public Limited Company Lithium transition metal phosphate secondary agglomerates and process for its manufacture
US9865868B2 (en) 2013-05-15 2018-01-09 Shin-Etsu Chemical Co., Ltd. Negative electrode material for use in non-aqueous electrolyte secondary battery, method of producing the same, and lithium-ion secondary battery
US20160172664A1 (en) * 2013-11-28 2016-06-16 Sumitomo Osaka Cement Co., Ltd. Electrode material and method for producing same
US9716269B2 (en) * 2013-11-28 2017-07-25 Sumitomo Osaka Cement Co., Ltd. Electrode material and method for producing same
EP3142173A4 (fr) * 2014-05-07 2017-10-04 Eliiy Power Co., Ltd. Électrode positive pour accumulateurs à électrolyte non aqueux et accumulateur à électrolyte non aqueux
US20160093878A1 (en) * 2014-09-30 2016-03-31 Sumitomo Osaka Cement Co., Ltd. Electrode material, electrode, and lithium ion battery
US9716270B2 (en) * 2014-09-30 2017-07-25 Sumitomo Osaka Cement Co., Ltd Electrode material, electrode, and lithium ion battery
US11283059B2 (en) * 2017-02-21 2022-03-22 Panasonic Corporation Positive electrode active material for nonaqueous electrolyte secondary batteries, and nonaqueous electrolyte secondary battery

Also Published As

Publication number Publication date
CA2821882A1 (fr) 2012-06-21
EP2654110B1 (fr) 2016-07-06
EP2654110A1 (fr) 2013-10-23
CN103270628B (zh) 2016-06-29
TW201232905A (en) 2012-08-01
US20150099175A1 (en) 2015-04-09
US9698425B2 (en) 2017-07-04
CN103270628A (zh) 2013-08-28
WO2012081383A1 (fr) 2012-06-21
KR20140051814A (ko) 2014-05-02
EP2654110A4 (fr) 2015-04-22

Similar Documents

Publication Publication Date Title
US9698425B2 (en) Electrode material and method for producing the same
JP6077206B2 (ja) 電極材料及びその製造方法並びに電極、リチウムイオン電池
JP5861661B2 (ja) 電極材料及び電極並びにリチウムイオン電池
JP5621740B2 (ja) 電極材料及び電極並びに電極材料の製造方法
JP2013191540A (ja) 正極活物質およびその製造方法並びにこれを利用した２次電池
US20150325846A1 (en) Electrode material
US20180277887A1 (en) Electrode material for lithium-ion secondary battery and lithium-ion secondary battery
US9356286B1 (en) Electrode material, paste for electrodes, and lithium ion battery
JP2012133888A (ja) 電極材料及びその製造方法
JP6077205B2 (ja) 電極材料及びその製造方法
US10680240B2 (en) Electrode material for lithium ion battery and lithium ion battery
JP2021150081A (ja) リチウムイオン二次電池用正極材料、リチウムイオン二次電池用正極及びリチウムイオン二次電池
US9680149B2 (en) Electrode material, paste for electrodes, and lithium ion battery
JP5790745B2 (ja) リチウムイオン二次電池用電極材料およびその製造方法
US9343741B2 (en) Electrode material, electrode and lithium ion battery
US20170092938A1 (en) Electrode material for lithium-ion rechargeable battery, electrode for lithium-ion rechargeable battery and lithium-ion rechargeable battery
JP6725022B1 (ja) リチウムイオン二次電池用正極材料、リチウムイオン二次電池用正極、及びリチウムイオン二次電池
EP3462523B1 (fr) Matériau d'électrode pour batterie au lithium-ion et batterie au lithium-ion
KR20130099341A (ko) 리튬 이차 전지용 전극 활물질, 그 제조방법, 이를 포함하는 리튬 이차 전지용 전극 및 이를 채용한 리튬 이차 전지
US10074853B2 (en) Electrode material for lithium-ion rechargeable battery, electrode for lithium-ion rechargeable battery, and lithium-ion rechargeable battery
JP2017103137A (ja) リチウムイオン二次電池用負極活物質、リチウムイオン二次電池用負極及びリチウムイオン二次電池
JP5843038B2 (ja) リチウムイオン二次電池用電極材料
JP2014146514A (ja) 電極材料及び電極並びにリチウムイオン電池
JP2013258036A (ja) 電極材料とその製造方法及びリチウムイオン電池の正極並びにリチウムイオン電池
CN114506830A (zh) 磷酸盐包覆正极活性材料的制备方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: SUMITOMO OSAKA CEMENT CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KITAGAWA, TAKAO;YASUMIISHI, HIROFUMI;UEHARA, MASARU;REEL/FRAME:030595/0925

Effective date: 20130607

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION