US20120178868A1 - Crosslinked, Melt-Shapped Articles and Compositions for Producing Same - Google Patents

Crosslinked, Melt-Shapped Articles and Compositions for Producing Same Download PDF

Info

Publication number
US20120178868A1
US20120178868A1 US13/496,430 US201013496430A US2012178868A1 US 20120178868 A1 US20120178868 A1 US 20120178868A1 US 201013496430 A US201013496430 A US 201013496430A US 2012178868 A1 US2012178868 A1 US 2012178868A1
Authority
US
United States
Prior art keywords
melt
crosslinked
ethylene
polyolefin
silane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/496,430
Other languages
English (en)
Inventor
Mohamed Esseghir
Jeffrey M. Cogen
Saurav S. Senggupta
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US13/496,430 priority Critical patent/US20120178868A1/en
Publication of US20120178868A1 publication Critical patent/US20120178868A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C08J3/244—Stepwise homogeneous crosslinking of one polymer with one crosslinking system, e.g. partial curing
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L23/04—Homopolymers or copolymers of ethene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C67/00—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00
    • B29C67/24—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00 characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
    • B29C45/0001—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C45/00—Injection moulding, i.e. forcing the required volume of moulding material through a nozzle into a closed mould; Apparatus therefor
    • B29C45/16—Making multilayered or multicoloured articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C70/00—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts
    • B29C70/88—Shaping composites, i.e. plastics material comprising reinforcements, fillers or preformed parts, e.g. inserts characterised primarily by possessing specific properties, e.g. electrically conductive or locally reinforced
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
    • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
    • C08F220/10—Esters
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C08J3/246—Intercrosslinking of at least two polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/56—Organo-metallic compounds, i.e. organic compounds containing a metal-to-carbon bond
    • C08K5/57—Organo-tin compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L23/04—Homopolymers or copolymers of ethene
    • C08L23/08—Copolymers of ethene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L43/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing boron, silicon, phosphorus, selenium, tellurium or a metal; Compositions of derivatives of such polymers
    • C08L43/04—Homopolymers or copolymers of monomers containing silicon
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
    • C08L51/06—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers grafted on to homopolymers or copolymers of aliphatic hydrocarbons containing only one carbon-to-carbon double bond
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L83/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
    • C08L83/04—Polysiloxanes
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L83/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
    • C08L83/04—Polysiloxanes
    • C08L83/06—Polysiloxanes containing silicon bound to oxygen-containing groups
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B19/00—Apparatus or processes specially adapted for manufacturing insulators or insulating bodies
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/18—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances
    • H01B3/20—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances liquids, e.g. oils
    • H01B3/22—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances liquids, e.g. oils hydrocarbons
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/18—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances
    • H01B3/30—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes
    • H01B3/307—Other macromolecular compounds
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/18—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances
    • H01B3/30—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes
    • H01B3/46—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes silicones
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B7/00—Insulated conductors or cables characterised by their form
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/04—Polymers of ethylene
    • B29K2023/06—PE, i.e. polyethylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/04—Polymers of ethylene
    • B29K2023/06—PE, i.e. polyethylene
    • B29K2023/0608—PE, i.e. polyethylene characterised by its density
    • B29K2023/0625—LLDPE, i.e. linear low density polyethylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/18—Polymers of hydrocarbons having four or more carbon atoms, e.g. polymers of butylene, e.g. PB, i.e. polybutylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0005—Condition, form or state of moulded material or of the material to be shaped containing compounding ingredients
    • B29K2105/0014—Catalysts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0058—Liquid or visquous
    • B29K2105/0067—Melt
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0085—Copolymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0088—Blends of polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/24—Condition, form or state of moulded material or of the material to be shaped crosslinked or vulcanised
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0083—Creep
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
    • B29K2995/0037—Other properties
    • B29K2995/0094—Geometrical properties
    • B29K2995/0097—Thickness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2009/00—Layered products
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/34—Electrical apparatus, e.g. sparking plugs or parts thereof
    • B29L2031/3462—Cables
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
    • C08G77/04—Polysiloxanes
    • C08G77/14—Polysiloxanes containing silicon bound to oxygen-containing groups
    • C08G77/16—Polysiloxanes containing silicon bound to oxygen-containing groups to hydroxyl groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
    • C08G77/42—Block-or graft-polymers containing polysiloxane sequences
    • C08G77/442—Block-or graft-polymers containing polysiloxane sequences containing vinyl polymer sequences
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2383/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen, or carbon only; Derivatives of such polymers
    • C08J2383/04—Polysiloxanes
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2423/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2423/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • C08J2423/04—Homopolymers or copolymers of ethene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2203/00—Applications
    • C08L2203/20—Applications use in electrical or conductive gadgets
    • C08L2203/202—Applications use in electrical or conductive gadgets use in electrical wires or wirecoating
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2207/00—Properties characterising the ingredient of the composition
    • C08L2207/32—Properties characterising the ingredient of the composition containing low molecular weight liquid component
    • C08L2207/322—Liquid component is processing oil

Definitions

  • This disclosure relates to crosslinked, melt-shaped articles.
  • the disclosure relates to a process for producing crosslinked, melt-shaped articles while in another aspect, the disclosure relates to such a process in which the articles are crosslinked using a organopolysiloxane containing two or more functional end groups.
  • the disclosure relates to such a process in which the crosslinking is accomplished without requiring the use of post-shaping external heat or moisture.
  • compositions used in the manufacture of crosslinkable articles typically require cross-linking after final shaping.
  • Various crosslinking methods are practiced in the art, two of which are in wide usage, i.e., peroxide crosslinking and moisture cure (the latter of which usually employs a silane grafted or copolymerized polyolefin).
  • Moisture cure systems have the advantage in that they can be processed within a wide range of melt temperatures but are generally limited to thin wall constructions because the crosslinking relies on diffusion of external moisture into the article.
  • Peroxide cure compositions are preferred for thick wall constructions, e.g. medium voltage (MV) cable insulation and molded cable accessories.
  • MV medium voltage
  • These curable compounds need to be processed at temperatures which are below the peroxide decomposition temperature in order to avoid premature crosslinking (scorch) prior to forming the article. Once the article is formed, it needs to be heated uniformly to the peroxide decomposition temperature, and then held at that temperature for the time necessary to achieve the desired level of crosslinking. This can keep the production rate for such articles low due to poor heat transfer through the article walls.
  • oil extender additives for improving flexibility to crosslinked articles. Addition of oil extender to crosslinked articles, however, has its drawbacks. In particular, addition of oil extender results in a decrease in dielectric strength (ACBD) for the crosslinked article.
  • ACBD dielectric strength
  • the present disclosure is directed to crosslinked polyolefin articles with improved flexibility and high dielectric strength.
  • the present crosslinked articles include a crosslinked polyolefin and a liquid polymer modifier.
  • the polyolefin is crosslinked by way of a unique silane linkage.
  • the liquid polymer modifier improves flexibility without negatively effecting dielectric strength.
  • the present disclosure provides a crosslinkable mixture which includes a polyolefin, an alkoxysilane, an organopolysiloxane, a free radical initiator, and a liquid polymer modifier.
  • the organopolysiloxane contains two or more hydroxyl end groups.
  • the crosslinkable mixture contains a crosslinking catalyst.
  • the present disclosure provides another crosslinkable mixture which includes a silane-grafted polyethylene, an organopolysiloxane; and a liquid polymer modifier.
  • the organopolysiloxane contains two or more hydroxyl end groups.
  • the crosslinkable mixture contains a crosslinking catalyst.
  • FIG. 3 is a graph reporting the DMA of the cross-linked insulation layer of FIG. 2 .
  • Ambient conditions and like terms means temperature, pressure and humidity of the surrounding area or environment of an article.
  • the ambient conditions of a typical office building or laboratory include a temperature of 23° C. and atmospheric pressure.
  • Blend means a blend of two or more polymers. Such a blend may or may not be miscible. Such a blend may or may not be phase separated. Such a blend may or may not contain one or more domain configurations, as determined from transmission electron spectroscopy, light scattering, x-ray scattering, and any other method known in the art.
  • Catalytic amount means an amount of catalyst necessary to promote the crosslinking of an ethylene-vinylsilane polymer at a detectable level, preferably at a commercially acceptable level.
  • composition and like terms mean a mixture or blend of two or more components.
  • a composition would include at least one ethylene polymer, at least one vinyl silane, and at least one free radical initiator.
  • a composition would include an ethylene-vinylsilane copolymer, a catalyst cure system and any desired additives such as lubricants, fillers, anti-oxidants and the like.
  • Crosslinkable mixture is a polymeric mixture that, when subjected to melt shaping, forms a link (i.e., a crosslink) between at least two individual polymer chains of the polymer.
  • Polymer means a compound prepared by reacting (i.e., polymerizing) monomers, whether of the same or a different type.
  • the generic term polymer thus embraces the term “homopolymer”, usually employed to refer to polymers prepared from only one type of monomer, and the term “interpolymer” as defined below.
  • Propylene polymer “Propylene polymer,” “polypropylene” and like terms mean a propylene polymer containing units derives from propylene. Propylene polymer typically comprise at least 50 mole percent (mol %) units derived from propylene.
  • the polyolefin may be one or more C 2 -C 12 polyolefin and combinations thereof.
  • suitable polyolefins include one or more propylene polymers, one or more ethylene polymers, and any combination thereof.
  • the catalyst is preferably mono-cyclopentadienyl, mono-indenyl or mono-fluorenyl CGC.
  • the solution process is preferred.
  • U.S. Pat. No. 5,064,802, WO93/19104 and WO95/00526 disclose constrained geometry metal complexes and methods for their preparation.
  • Variously substituted indenyl containing metal complexes are taught in WO95/14024 and WO98/49212.
  • polymerization can be accomplished at conditions well-known in the art for Ziegler-Natta or Kaminsky-Sinn type polymerization reactions, that is, at temperatures from 0-250° C., preferably 30-200° C., and pressures from atmospheric to 10,000 atmospheres (1013 megaPascal (MPa)). Suspension, solution, slurry, gas phase, solid state powder polymerization or other process conditions may be employed if desired.
  • the catalyst can be supported or unsupported, and the composition of the support can vary widely.
  • Silica, alumina or a polymer especially poly(tetrafluoroethylene) or a polyolefin) are representative supports, and desirably a support is employed when the catalyst is used in a gas phase polymerization process.
  • the support is preferably employed in an amount sufficient to provide a weight ratio of catalyst (based on metal) to support within a range of from 1:100,000 to 1:10, more preferably from 1:50,000 to 1:20, and most preferably from 1:10,000 to 1:30.
  • the molar ratio of catalyst to polymerizable compounds employed is from 10 ⁇ 12 :1 to 10 ⁇ 1 :1, more preferably from 10 ⁇ 9 :1 to 10 ⁇ 5 :1.
  • Inert liquids serve as suitable solvents for polymerization.
  • Examples include straight and branched-chain hydrocarbons such as isobutane, butane, pentane, hexane, heptane, octane, and mixtures thereof; cyclic and alicyclic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane, and mixtures thereof; perfluorinated hydrocarbons such as perfluorinated C 4-10 alkanes; and aromatic and alkyl-substituted aromatic compounds such as benzene, toluene, xylene, and ethylbenzene.
  • the ethylene polymers useful in the practice of this disclosure include ethylene/ ⁇ -olefin interpolymers having an ⁇ -olefin content of between about 15, preferably at least about 20 and even more preferably at least about 25, wt % based on the weight of the interpolymer. These interpolymers typically have an ⁇ -olefin content of less than about 50, preferably less than about 45, more preferably less than about 40 and even more preferably less than about 35, wt % based on the weight of the interpolymer.
  • the ⁇ -olefin content is measured by 13 C nuclear magnetic resonance (NMR) spectroscopy using the procedure described in Randall ( Rev. Macromol. Chem. Phys ., C29 (2&3)).
  • NMR nuclear magnetic resonance
  • the ⁇ -olefin is preferably a C 3-20 linear, branched or cyclic ⁇ -olefin.
  • C 3-20 ⁇ -olefins include propene, 1-butene, 4-methyl-1-pentene, 1-hexene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, and 1-octadecene.
  • the ⁇ -olefins also can contain a cyclic structure such as cyclohexane or cyclopentane, resulting in an ⁇ -olefin such as 3-cyclohexyl-1-propene (allyl cyclohexane) and vinyl cyclohexane.
  • a cyclic structure such as cyclohexane or cyclopentane
  • an ⁇ -olefin such as 3-cyclohexyl-1-propene (allyl cyclohexane) and vinyl cyclohexane.
  • cyclic olefins such as norbornene and related olefins, particularly 5-ethylidene-2-norbornene, are ⁇ -olefins and can be used in place of some or all of the ⁇ -olefins described above.
  • styrene and its related olefins are ⁇ -olefins for purposes of this disclosure.
  • Illustrative ethylene polymers include ethylene/propylene, ethylene/butene, ethylene/1-hexene, ethylene/1-octene, ethylene/styrene, and the like.
  • Illustrative terpolymers include ethylene/propylene/1-octene, ethylene/propylene/butene, ethylene/butene/1-octene, ethylene/propylene/diene monomer (EPDM) and ethylene/butene/styrene.
  • the copolymers can be random or blocky.
  • the ethylene polymers used in the practice of this disclosure can be used alone or in combination with one or more other ethylene polymers, e.g., a blend of two or more ethylene polymers that are “different from one another,” which means the ethylene polymers are uncommon by way of at least one property such as: monomer/comonomer composition and content, melt index, melt temperature, degree of branching, catalytic method of preparation, etc.
  • the ethylene polymer is a blend of two or more ethylene polymers, then the ethylene polymer can be blended by any in-reactor or post-reactor process.
  • the in-reactor blending processes are preferred to the post-reactor blending processes, and the processes using multiple reactors connected in series are the preferred in-reactor blending processes. These reactors can be charged with the same catalyst but operated at different conditions, e.g., different reactant concentrations, temperatures, pressures, etc, or operated at the same conditions but charged with different catalysts.
  • ethylene polymers made with high pressure processes include (but are not limited to) low density polyethylene (LDPE), ethylene silane reactor copolymer (such as SiLINK® made by The Dow Chemical Company), ethylene vinyl acetate copolymer (EVA), ethylene ethyl acrylate copolymer (EEA), and ethylene silane acrylate terpolymers.
  • LDPE low density polyethylene
  • ethylene silane reactor copolymer such as SiLINK® made by The Dow Chemical Company
  • EVA ethylene vinyl acetate copolymer
  • ESA ethylene ethyl acrylate copolymer
  • ethylene silane acrylate terpolymers examples include (but are not limited to) low density polyethylene (LDPE), ethylene silane reactor copolymer (such as SiLINK® made by The Dow Chemical Company), ethylene vinyl acetate copolymer (EVA), ethylene ethyl acrylate copolymer (EEA), and ethylene silane acrylate terpolymers
  • VLDPE very low density polyethylene
  • FLEXOMER® ethylene/1-hexene polyethylene made by The Dow Chemical Company
  • homogeneously branched, linear ethylene/ ⁇ -olefin copolymers e.g., TAFMER® by Mitsui Petrochemicals Company Limited and EXACT® by Exxon Chemical Company
  • homogeneously branched, substantially linear ethylene/ ⁇ -olefin polymers e.g., AFFINITY® and ENGAGE® polyethylene available from The Dow Chemical Company
  • ethylene block copolymers e.g., INFUSE® polyethylene available from The Dow Chemical Company
  • the more preferred ethylene polymers are the homogeneously branched linear and substantially linear ethylene copolymers.
  • the substantially linear ethylene copolymers are especially preferred, and are more fully described in U.S. Pat. Nos. 5,272,236, 5,278,272 and 5,986,028.
  • the crosslinkable mixture includes a first polyethylene and a second polyethylene that is different than the first polyethylene.
  • the first polyethylene has at least one uncommon (not the same) property or structure when compared to the second polyethylene.
  • the polyethylene that is copolymerized with silane functionality is made using a high pressure process.
  • the crosslinkable mixture includes an alkoxysilane.
  • Any alkoxysilane that will effectively copolymerize with ethylene, or graft to and crosslink an ethylene polymer, can be used in the practice of this disclosure, and those described by the following formula are exemplary:
  • R 1 is a hydrogen atom or methyl group
  • x and y are 0 or 1 with the proviso that when x is 1, y is 1
  • m and n are independently an integer from 0 to 12 inclusive, preferably 0 to 4, and each R′′ independently is a hydrolyzable organic group such as an alkoxy group having from 1 to 12 carbon atoms (e.g. methoxy, ethoxy, butoxy), aryloxy group (e.g. phenoxy), araloxy group (e.g. benzyloxy), aliphatic acyloxy group having from 1 to 12 carbon atoms (e.g.
  • alkoxysilane may be copolymerized with ethylene in a reactor, such as a high pressure process.
  • alkoxysilane may also be grafted to a suitable ethylene polymer by the use of a suitable quantity of organic peroxide, either before or during a shaping or molding operation. Additional ingredients such as heat and light stabilizers, pigments, scorch retardants etc., also may be included in the formulation.
  • the phase of the process during which the crosslinks are created is commonly referred to as the “cure phase” and the process itself is commonly referred to as “curing”. Also included is alkox ysilane that adds to unsaturation in the polymer via free radical processes such as mercaptopropyl trialkoxysilane.
  • Suitable alkoxysilanes include unsaturated silanes that comprise an ethylenically unsaturated hydrocarbyl group, such as a vinyl, allyl, isopropenyl, butenyl, cyclohexenyl or gamma-(meth)acryloxy allyl group, and a hydrolyzable group, such as, for example, a hydrocarbyloxy, hydrocarbonyloxy, or hydrocarbylamino group.
  • hydrolyzable groups include methoxy, ethoxy, formyloxy, acetoxy, proprionyloxy, and alkyl or arylamino groups.
  • Preferred alkoxysilanes are the unsaturated alkoxy silanes which can be grafted onto the polymer or copolymerized in-reactor with other monomers (such as ethylene and acrylates). These alkoxysilanes and their method of preparation are more fully described in U.S. Pat. No. 5,266,627 to Meverden, et al. Vinyl trimethoxy silane (VTMS), vinyl triethoxy silane, vinyl triacetoxy silane, gamma-(meth)acryloxy propyl trimethoxy silane and mixtures of these silanes are the preferred silane crosslinkers for use in this disclosure.
  • VTMS Vinyl trimethoxy silane
  • vinyl triethoxy silane vinyl triacetoxy silane
  • gamma-(meth)acryloxy propyl trimethoxy silane and mixtures of these silanes are the preferred silane crosslinkers for use in this disclosure.
  • the amount of alkoxysilane crosslinker used in the practice of this disclosure can vary widely depending upon the nature of the polymer, the alkoxysilane, the processing or reactor conditions, the grafting or copolymerization efficiency, the ultimate application, and similar factors, but typically at least 0.5, preferably at least 0.7, weight percent is used. Considerations of convenience and economy are two of the principal limitations on the maximum amount of alkoxysilane crosslinker used in the practice of this disclosure, and typically the maximum amount of alkoxysilane crosslinker does not exceed 5, preferably it does not exceed 3, weight percent.
  • the alkoxysilane crosslinker is grafted to the polymer by any conventional method, typically in the presence of a free radical initiator, e.g. peroxides or by ionizing radiation, etc.
  • a free radical initiator e.g. peroxides or by ionizing radiation, etc.
  • Organic initiators are preferred, such as any one of the peroxide initiators, for example, dicumyl peroxide, di-tert-butyl peroxide, t-butyl perbenzoate, benzoyl peroxide, cumene hydroperoxide, t-butyl peroctoate, methyl ethyl ketone peroxide, 2,5-dimethyl-2,5-di(t-butyl peroxy)hexane, lauryl peroxide, and tert-butyl peracetate.
  • the amount of initiator can vary, but it is typically present in an amount of at least 0.01, preferably at least 0.06, parts per hundred resin (wt. %). Typically, the initiator does not exceed 0.15, preferably it does not exceed about 0.10, wt. %.
  • the weight ratio of silane crosslinker to initiator also can vary widely, but the typical crosslinker:initiator weight ratio is between 10:1 to 500:1, preferably between 18:1 and 250:1. As used in parts per hundred resin or phr, “resin” means the olefinic polymer.
  • one preferred method is blending the two with the initiator in the first stage of a reactive extrusion or mixing process, such as a Buss kneader or a twin-screw extruder.
  • the grafting conditions can vary, but the melt temperatures are typically between 160 and 260° C., preferably between 190 and 230° C., depending upon the residence time and the half life of the initiator.
  • Copolymerization of vinyl trialkoxysilane crosslinkers with ethylene and other monomers may be done in a high-pressure reactor that is used in the manufacture of ethylene homopolymers and copolymers with vinyl acetate and acrylates.
  • the crosslinkable mixture includes an organopolysiloxane, such as a polyfunctional organopolysiloxane with two or more functional end groups.
  • organopolysiloxane such as a polyfunctional organopolysiloxane with two or more functional end groups.
  • the oligomers containing functional end groups useful in the present process comprise from 2 to 100,000 or more units of the formula R 2 SiO in which each R is independently selected from a group consisting of alkyl radicals comprising one to 12 carbon atoms, alkenyl radicals comprising two to about 12 carbon atoms, aryls, and fluorine substituted alkyl radicals comprising one to about 12 carbon atoms.
  • the radical R can be, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, dodecyl, vinyl, allyl, phenyl, naphthyl, tolyl, and 3,3,3-trifluoropropyl. Preferred is when each radical R is methyl.
  • the organopolysiloxane contains two or more hydroxyl end groups such as a hydroxyl-terminated polydimethylsiloxane containing at least two hydroxyl end groups.
  • hydroxyl-terminated polydimethylsiloxane containing at least two hydroxyl end groups.
  • polydimethylsiloxanes are commercially available, for example as silanol-terminated polydimethylsiloxane from Gelest, Inc.
  • polydimethylsiloxanes having other terminal groups that can react with grafted silanes may be used e.g. polydimethylsiloxanes with amine end groups and the like.
  • the polydimethylsiloxane is of the formula
  • n in which Me is methyl and n is in the range of 1 to 100,000 or more.
  • the value “n” can have a lower limit of 1, or 2, or, 3, or, 4, or 5, or, 10, or 15, or 20 and an upper limit of 50, or 75, or, 100, or, 120, or 400, or 1000, or 100,000.
  • suitable polyfunctional organopolysiloxanes are the silanol-terminated polydimethylsiloxane DMS-15 (Mn of 2,000-3,500, viscosity of 45-85 centistokes, —OH level of 0.9-1.2%) from Gelest Corp., and Silanol Fluid Q1-3563 (viscosity 55-90 centistokes, —OH level of 1-1.7%) from Dow Corning Corp.
  • the polyfunctional organopolysiloxane comprises branches such as those imparted by Me-SiO 3/2 or SiO 4/2 groups (known as T or Q groups to those skilled in silicone chemistry).
  • the amount of polyfunctional organopolysiloxane used in the practice of this disclosure can vary widely depending upon the nature of the polymer, the alkoxysilane, the polyfunctional organopolysiloxane, the processing or reactor conditions, the ultimate application, and similar factors, but typically at least 0.5, preferably at least 2, weight percent is used. Considerations of convenience, polymer acceptance and economy are some of the principal limitations on the maximum amount of polyfunctional organopolysiloxane used in the practice of this disclosure, and typically the maximum amount of polyfunctional organopolysiloxane does not exceed 20, preferably it does not exceed 10, weight percent.
  • the crosslinkable mixture optionally includes a crosslinking catalyst.
  • Crosslinking catalysts include the Lewis and Br ⁇ nsted acids and bases.
  • Lewis acids are chemical species that can accept an electron pair from a Lewis base.
  • Lewis bases are chemical species that can donate an electron pair to a Lewis acid.
  • Lewis acids that can be used in the practice of this disclosure include the tin carboxylates such as dibutyl tin dilaurate (DBTDL), dimethyl hydroxy tin oleate, dioctyl tin maleate, di-n-butyl tin maleate, dibutyl tin diacetate, dibutyl tin dioctoate, stannous acetate, stannous octoate, and various other organo-metal compounds such as lead naphthenate, zinc caprylate and cobalt naphthenate.
  • DBTDL is a preferred Lewis acid.
  • Lewis bases that can be used in the practice of this disclosure include, but are not limited to, the primary, secondary and tertiary amines. These catalysts are typically used in moisture cure applications.
  • Br ⁇ nsted acids are chemical species that can lose or donate a hydrogen ion (proton) to a Br ⁇ nsted base.
  • Br ⁇ nsted bases are chemical species that can gain or accept a hydrogen ion from a Br ⁇ nsted acid.
  • Br ⁇ nsted acids that can be used in the practice of this disclosure include sulfonic acid.
  • the minimum amount of crosslinking catalyst used in the practice of this disclosure is a catalytic amount. Typically this amount is at least 0.01, preferably at least 0.02 and more preferably at least 0.03, weight percent (wt %) of the combined weight of ethylene-vinylsilane polymer and catalyst.
  • the only limit on the maximum amount of crosslinking catalyst in the ethylene polymer is that imposed by economics and practicality (e.g., diminishing returns), but typically a general maximum comprises less than 5, preferably less than 3 and more preferably less than 2, wt % of the combined weight of ethylene polymer and condensation catalyst.
  • the crosslinkable mixture includes a liquid polymer modifier.
  • a “liquid polymer modifier,” as used herein, is a non-functionalized plasticizer (NFP).
  • NFP non-functionalized plasticizer
  • an “NFP” is a hydrocarbon liquid, which does not include to an appreciable extent functional groups selected from hydroxide, aryls and substituted aryls, halogens, alkoxys, carboxylates, esters, carbon unsaturation, acrylates, oxygen, nitrogen, and carboxyl.
  • aromatic moieties including any compound whose molecules have the ring structure characteristic of benzene, naphthalene, phenanthrene, anthracene, etc.
  • naphthenic moieties including any compound whose molecules have a saturated ring structure such as would be produced by hydrogenating benzene, naphthalene, phenanthrene, anthracene, etc.
  • substantially absent it is meant that these compounds are not added deliberately to the compositions and if present at all, are present at less than 0.5 wt %, preferably less than 0.1 wt % by weight of the NFP.
  • the NFP does not contain olefinic unsaturation to an appreciable extent.
  • “appreciable extent of olefinic unsaturation” it is meant that the carbons involved in olefinic bonds account for less than 10% of the total number of carbons in the NFP, preferably less than 8%, 6%, 4%, 2%, 1%, 0.7%, 0.5%, 0.3%, 0.1%, 0.05%, 0.01%, or 0.001%.
  • the percent of carbons of the NFP involved in olefinic bonds is between 0.001 and 10% of the total number of carbon atoms in the NFP, preferably between 0.01 and 5%, preferably between 0.1 and 2%, more preferably between 0.1 and 1%.
  • the liquid polymer modifier is an NFP that is a phthalate-free hydrogenated C 8 to C 12 poly-alpha-olefin.
  • the phthalate-free hydrogenated C 8 to C 12 poly-alpha-olefin is naturally inert and does not affect the cure chemistry of the crosslinkable mixture as do conventional modifiers like mineral oil, white oil and paraffinic oils.
  • the present liquid polymer modifier does not affect other chemistries, such as, for example, antioxidant chemistry, filler chemistry, adhesion chemistry or the like.
  • the present liquid polymer modifier has high permanence, good compatibility with polyethylenes and ethylene copolymers, and narrow molecular weight distribution (Mw/Mn or MWD).
  • Mw/Mn or MWD narrow molecular weight distribution
  • applications using the present liquid polymer modifier have a surprising combination of desired properties including high cure efficiency, improved flexibility and toughness and easy processing. Such applications display excellent surface properties and exceptional retention of properties over time.
  • a nonlimiting example of a suitable liquid polymer modifier is polymer modifier sold under the tradename Elevast, such as Elevast R-150. Elevast polymer modifier is available from the ExxonMobil Chemical Company, Houston, Tex.
  • the liquid polymer modifier advantageously replaces oil extenders (paraffin oil and/or mineral oil) in the crosslinked, melt-shaped article.
  • oil extenders paraffin oil and/or mineral oil
  • a crosslinked, melt-shaped article containing the present liquid polymer modifier unexpectedly exhibits improved softness (i.e., lower Shore A Hardness value), increased flexibility, (i.e., increase in M100), greater elongation, enhanced elasticity, and improved processability (lower viscosity)—all with no decrease in dielectric strength of the crosslinked, melt-shaped article.
  • the foregoing physical improvements from the liquid polymer modifier are surprising and unexpected in view of conventional oil extenders because oil extenders decrease dielectric strength in the resultant crosslinked product.
  • Nonlimiting applications of crosslinked, melt-shaped article containing the present liquid polymer modifier and exhibiting the foregoing physical improvements (without loss of dielectric strength) include wire and cable, and other applications where good dielectric properties are required.
  • the liquid polymer modifier may be added during different steps of the production process.
  • the liquid polymer modifier is added to a crosslinkable mixture composed of (1) organopolysiloxane (with two or more hydroxyl end groups) and (2) a silane-grafted or silane-copolymerized polyolefin.
  • This crosslinkable mixture is subsequently melt-shaped, partially crosslinked, cooled, and further cross-linked upon exposure to ambient conditions.
  • the liquid polymer modifier is added to a crosslinkable mixture composed of (1) organopolysiloxane containing two or more hydroxyl end groups, (2) polyolefin, (3) silane, and (4) peroxide.
  • the crosslinkable mixture is subsequently melt-shaped, partially crosslinked, cooled and further crosslinked when exposed to ambient conditions.
  • the liquid polymer modifier is added with the crosslinking catalyst.
  • a silane-grafted polyolefin is prepared to which a hydroxyl-terminated polydimethylsiloxane is added.
  • the mixture is melt-shaped into a storage article.
  • the storage article is introduced into a second melt-shaping operation wherein the storage article is melt-shaped into a finished article.
  • the process includes introducing the crosslinking catalyst and the liquid polymer modifier during or after the second melt-shaping operation.
  • the process further includes cooling and crosslinking the finished article from the second melt-shaping operation.
  • the composition from which the crosslinked article, e.g., cable insulation layer or protective jacket, injection molded elastomeric connector, etc., or other article of manufacture, e.g., seal, gasket, shoe sole, etc., is made can be filled or unfilled. If filled, then the amount of filler present should preferably not exceed an amount that would cause unacceptably large degradation of the electrical and/or mechanical properties of the crosslinked composition. Typically, the amount of filler present is between 2 and 80, preferably between 5 and 70, weight percent (wt %) based on the weight of the polymer.
  • Representative fillers include kaolin clay, magnesium hydroxide, silica, calcium carbonate and carbon blacks. The filler may or may not have flame retardant properties.
  • the filler is coated with a material that will prevent or retard any tendency that the filler might otherwise have to interfere with the silane cure reaction.
  • Stearic acid is illustrative of such a filler coating.
  • Filler and catalyst are selected to avoid any undesired interactions and reactions, and this selection is well within the skill of the ordinary artisan.
  • compositions of this disclosure can also contain additives such as, for example, antioxidants (e.g., hindered phenols such as, for example, IRGANOXTM 1010 a registered trademark of Ciba Specialty Chemicals), phosphites (e.g., IRGAFOSTM 168 a registered trademark of Ciba Specialty Chemicals), UV stabilizers, cling additives, light stabilizers (such as hindered amines), plasticizers (such as dioctylphthalate or epoxidized soy bean oil), scorch inhibitors, mold release agents, tackifiers (such as hydrocarbon tackifiers), waxes (such as polyethylene waxes), processing aids (such as oils, organic acids such as stearic acid, metal salts of organic acids), oil extenders (such as paraffin oil and mineral oil), colorants or pigments to the extent that they do not interfere with desired physical or mechanical properties of the compositions of the present disclosure.
  • antioxidants e.g., hinder
  • the crosslinkable mixture may comprise two or more embodiments disclosed herein.
  • Compounding of the polyolefin, alkoxysilane, polyfunctional organopolysiloxane, liquid polymer modifier, free radical initiator, optional crosslinking catalyst, optional filler and optional additives, if any, can be performed by standard means known to those skilled in the art.
  • Examples of compounding equipment are internal batch mixers, such as a Banbury or Bolling internal mixer.
  • continuous single or twin screw mixers can be used, such as a Farrel continuous mixer, a Werner and Pfleiderer twin screw mixer, or a Buss kneading continuous extruder.
  • the type of mixer utilized, and the operating conditions of the mixer, will affect properties of the composition such as viscosity, volume resistivity, and extruded surface smoothness.
  • the components of the composition are typically mixed at a temperature and for a length of time sufficient to fully homogenize the mixture but insufficient to cause the material to gel.
  • the crosslinking catalyst is typically added via an additive masterbatch to ethylene-vinylsilane copolymer or grafted silane polyolefin prior to shaping the article.
  • the components are mixed together in a melt-mixing device. The mixture is then shaped into an article.
  • the temperature of compounding and article fabrication should be above the melting point of the ethylene-vinylsilane copolymer or grafted silane polyolefin but below about 250° C.
  • either or both of the crosslinking catalyst and the additives are added as a pre-mixed masterbatch.
  • masterbatches are commonly formed by dispersing the catalyst and/or additives into an inert plastic resin, e.g., a low density polyethylene. Masterbatches are conveniently formed by melt compounding methods.
  • one or more of the components are dried before compounding, or a mixture of components is dried after compounding, to reduce or eliminate potential scorch that may be caused from moisture present in or associated with the component, e.g., filler.
  • crosslinkable silicone-modified polyolefin mixtures are prepared in the absence of a crosslinking catalyst for extended shelf life, and the crosslinking catalyst is added as a final step in the preparation of a melt-shaped article.
  • the disclosure is a process for the manufacture of crosslinked, melt-shaped articles, the process comprising the steps of:
  • crosslinking can be promoted by the addition of a catalyst to the mixture before or during melt-shaping, or to the melt-shaped article (e.g., by diffusion from an adjoining layer if the article is a layer in a multilayer construction.
  • a catalyst to the mixture before or during melt-shaping, or to the melt-shaped article (e.g., by diffusion from an adjoining layer if the article is a layer in a multilayer construction.
  • compounding the crosslinkable mixture containing these components produces a stable thermoplastic composition which can be shaped and partially crosslinked by melt processing into an article, but upon storage at ambient conditions undergoes thorough crosslinking without the need for external moisture or heat.
  • the morphology of such a blend shows greater compatibility between the silicone and the polyolefin phases compared to either a physical (unreacted) siloxane/polyolefin blend or a physical, i.e., unreacted, blend of a siloxane and a silane-grafted polyolefin.
  • the process of this disclosure eliminates the reliance on external moisture diffusion that is required in conventional moisture cure.
  • the process of this disclosure is particularly useful for manufacturing thick-wall (greater than (>) 0.2, more typically >0.5 and even more typically >1, millimeter (mm)), crosslinked constructions such as in high and medium voltage cable insulation, wire and cable molded elastomeric connectors and accessories, and molded automotive heat resistant parts.
  • thick-wall greater than (>) 0.2, more typically >0.5 and even more typically >1, millimeter (mm)
  • crosslinked constructions such as in high and medium voltage cable insulation, wire and cable molded elastomeric connectors and accessories, and molded automotive heat resistant parts.
  • the cure step continues off mold to achieve full cure. This approach improves manufacturing cycle time and achieves higher productivity (units per time).
  • hydroxyl-terminated organopolysiloxane is reacted with an alkoxysilane (or silanol) that is grafted to a polyolefin or other polymer.
  • alkoxysilane or silanol
  • Methods for preparation of such grafted polymers are well known.
  • vinyltrimethoxysilane VTMS
  • various reactor copolymers are available, such as SI-LINKTM, which is a copolymer of VTMS and ethylene available from The Dow Chemical Company.
  • the disclosure is a process for the manufacture of crosslinked, melt-shaped articles, the process comprising the steps of:
  • the disclosure is a process for the manufacture of crosslinked, melt-shaped articles, the process comprising the steps of:
  • the storage article is typically pellets which are re-melted and optionally mixed with a crosslinking catalyst to form the finished molded or extruded article.
  • the crosslinkable mixture forms unique polysiloxane linkages between polymer chains of the polyolefin when the crosslinkable mixture is subjected to a melt-shape, or melt-shaping, procedure. It is believed that during melt shaping, the hydroxyl-terminated organopolysiloxane reacts with the alkoxysilane (or silanol) that is grafted to the polyolefin to form a polysiloxane linkage between at least two individual polymer chains of the polyolefin.
  • the polysiloxane linkage has the structure (I) below.
  • n is from 1 to 100,000.
  • the term “n” can have a lower limit of 1, or 2, or, 3, or 4, or 5, or, 10, or 15, or 20 and an upper limit of 50, or 75, or, 100, or, 120, or 400, or 1000, or 100,000.
  • the polysiloxane linkage (I) is unique compared to linkages formed by way of conventional peroxide crosslinking and/or conventional silane graft/moisture cure.
  • Conventional silane crosslinked polyolefin contains a “—Si—O—Si—” linkage between polymer chains.
  • the present polysiloxane linkage of structure (I) has a minimum of three (3) silicon atoms between polymer chains Applicant has discovered that the unique polysiloxane linkage (I) surprisingly results in a composition showing greater compatibility between polyolefin and silicone than would be obtained in a physical blend of silicone and polyolefin as demonstrated in FIGS. 4 and 5 .
  • the hydroxyl-terminated organopolysiloxane reacted with the silane-grafted polyethylene in the presence of a catalyst surprisingly improves compatibility of the organopolysiloxane (i.e., PDMS) component within the polyolefin resulting in unique phase morphology.
  • organopolysiloxane i.e., PDMS
  • FIGS. 4A (250 ⁇ ) and 4 B (500 ⁇ ) are electron micrographs of polyethylene mixtures made of VTMS silane-grafted polyethylene mixed with hydroxy-terminated polydimethylsiloxane (PDMS).
  • PDMS hydroxy-terminated polydimethylsiloxane
  • FIGS. 5A (250 ⁇ ) and 5 B (500 ⁇ ) show crosslinked polyethylene made by way of the present process which utilizes hydroxyl-terminated organopolysiloxane and avoids moisture cure.
  • FIGS. 5A and 5B show electron micrographs of VTMS silane-grafted polyethylene mixed with hydroxy-terminated polydimethylsiloxane in the presence of a catalyst and crosslinked in accordance with an embodiment of the present disclosure.
  • Present in the crosslinked polyethylene of FIGS. 5A and 5B are polysiloxane linkages of structure (I) linking individual polyethylene chains.
  • 5A and 5B show a uniform morphology—evidence of the improved compatibility between the hydroxyl-terminated organopolysiloxane and the polyethylene due to the incorporation of the silicone into the linkage of structure (I). Formation of the polysiloxane linkage (I) does not require moisture (i.e., water) as required by conventional moisture cure.
  • the composition of this disclosure can be applied to a cable as a sheath or insulation layer in known amounts and by known methods (for example, with the equipment and methods described in U.S. Pat. Nos. 5,246,783 and 4,144,202).
  • the composition is prepared in a reactor-extruder equipped with a cable-coating die and after the components of the composition are formulated, the composition is extruded over the cable as the cable is drawn through the die. Cure may begin in the reactor-extruder.
  • the melt-shaped article does not require post-treatment, e.g., after de-molding or passing through a shaping die, cure conditions, e.g., temperature above ambient and/or moisture from an external source such as a water bath or “sauna”. While not necessary or preferred, the melt-shaped article can be exposed to either or both elevated temperature and external moisture and if an elevated temperature, it is typically between ambient and up to but below the melting point of the polymer for a period of time such that the article reaches a desired degree of crosslinking.
  • the temperature of any post-shaping cure should preferably be above 0° C.
  • the melt-shaped article may comprise two or more embodiments disclosed herein.
  • ENGAGETM 8200 plastomer an ethylene-octene copolymer of 5MI, 0.870 density, solid pellets
  • the polymer pellets are heated at 40° C. for two hours then tumble blended with a mixture of VTMS and LUPEROX 101 peroxide (2,5-dimethyl-2,5-di(t-butylperoxy)hexane available from Arkema) and left to soak in a glass jar using a jar roller until the pellets are visibly dry.
  • a Brabender batch mixer (250 gram) is used for grafting VTMS to the polymer. Compounding is conducted at 190° C. for 15 minutes. The grafted polymer is pressed into a plaque at room temperature and sealed in a foil bag for subsequent experiments with polydimethylsiloxane (PDMS).
  • PDMS polydimethylsiloxane
  • a Brabender mixer (45 cc) is used to compound the grafted resin, silanol-terminated PDMS and catalyst. Compounding was performed at a set temperature of 150° C. as follows. First, the mixer was loaded with VTMS-grafted ENGAGE 8200, fluxed and mixed for 2 minutes at 45 revolutions per minute (rpm). Silanol-terminated PDMS (Gelest DMS-S15) is added gradually over a period of approximately 3 minutes and after addition is completed, the blend is further mixed for 2 minutes at 45 rpm. Catalysts (DBTDL, sulfonic acid or mixture) are then added and mixed for 15 minutes at 45 rpm. If the resulting compound is thermoplastic, i.e. no significant crosslinking is visible, it is pressed into a 50 mil ( ⁇ 1.3 mm) plaque immediately after removal from the mixer and stored overnight in a sealed aluminum foil bag at 25° C.
  • Samples are then cut to analyze for cure via hot creep analysis (200° C. oven, 15 min) in which percent elongation under 20N/cm 2 load is measured.
  • a common standard for adequate crosslinking is elongation of less than or equal to ( ⁇ ) 100%. Measurements are obtained on triplicate samples.
  • Si-g-PE is silane grafted ENGAGE 8200 plastomer.
  • Sil-PDMS is Gelest DMS-S15 silanol-terminated PDMS.
  • Sulfonic acid is B-201 available from King Industries.
  • DBTDL is FASTCAT 4202 dibutyl tin dilaurate. Hot Creep Test Percent Elongation measured at 200° C., 0.2 MPa load held for 15 minutes by IEC 60811-2-1.
  • compositions that can be homogenously mixed to produce a thermoplastic material that exhibit excellent crosslinking without the need for external moisture exposure which is desirable for thick articles such as molded parts or medium voltage and high voltage cable coating.
  • the composition of sample E is repeated in another experiment, the sample made is subjected to a DMA analysis, with a temperature sweep from ⁇ 150° C. to 200° C.
  • the modulus of the reactively-modified PDMS-ENGAGE blend exhibits a plateau past the melting point, indicating a good temperature resistance compared to the base resin.
  • sample E shows a predominantly single homogeneous phase with only a small amount of dispersed silicone domains.
  • other compositions tested resulted in morphologies typical of highly immiscible systems containing distinct dispersed domains of silicone visible as droplets within the polyolefin matrix.
  • Molded part 10 ( FIG. 2 ) comprises insulation layer 11 made out of an elastomer resin system which is grafted with vinyltrimethoxysilane in the presence of OH-PDMS.
  • Molded part 10 is a 35 KV prototype connector comprising outer ( 12 ) and an inner ( 13 ) semicon layers sandwiching insulation layer 11 .
  • Insulation layer 11 comprises a composition of this disclosure. The semicon layers are first molded separately and peroxide-cured in a first molding step, then mounted together in a second mold where the insulation layer is injected between them.
  • the insulation compound (pellets) is premixed with a tin catalyst masterbatch (also pellets), injection is conducted in a fully thermoplastic fashion, and the part is de-molded upon cooling (1-5 minutes molding time depending on the test run).
  • Inner semicon layer 13 is about 4 mm thick and covers most of the insulation, except towards the ends.
  • Outer semicon layer 12 is about 3.5 mm thick and covers the entire insulation layer, i.e. no external exposure.
  • Insulation layer 11 is about 11.6 mm thick and becomes a molded article post-injection.
  • Sample 1 is about 3 mm inside the layer
  • Sample 2 is about 5 mm inside the layer
  • Sample 3 is about 7 mm inside the layer.
  • the part is handled under normal shipping and lab storage conditions prior to testing, i.e. no special heat or moisture exposure and was tested for cross-linking days after molding.
  • the DMA data in FIG. 3 shows a plateau modulus at a temperature above the melting point for each of the samples or in other words, complete cure of the material.
  • Insulation materials, sample 2, sample 5 and sample 6 are prepared via reactive extrusion in a ZSK-30 twin-screw extruder.
  • Alternating current breakdown (ACBD) strength is the minimum alternating current voltage that causes a portion of a material (such as an insulator) to become electrically conductive. ACBD is determined in accordance with ASTM D 149 (kV/mm).
  • a crosslinkable mixture is provided and includes a polyolefin, an alkoxysilane, an organopolysiloxane containing two or more hydroxyl end groups, a free radical initiator, and a liquid polymer modifier.
  • n 1 to 100,000.
  • E3 The crosslinkable mixture of E2 wherein additional polysiloxane linkages of the structure (I) form when the melt-shaped article is exposed to ambient temperature.
  • E4 The crosslinkable mixture of any of E1-E3 comprising a crosslinking catalyst.
  • E5. The crosslinkable mixture of any of claims E1-E4 wherein the polyolefin is a polyethylene.
  • E6 The crosslinkable mixture of any of E1-E5 comprising a first polyethylene crosslinked to a second polyethylene by way of the polysiloxane linkage (I).
  • E7 The crosslinkable mixture of any of E1-E6 wherein the alkoxysilane is vinyltrimethoxysilane.
  • E9. The crosslinkable mixture of any of E1-E8 wherein the liquid polymer modifier is a non-functionalized plasticizer comprising a phthalate-free hydrogenated C 8 -C 12 poly-alpha-olefin.
  • Another crosslinkable mixture (E10) includes a silane-grafted polyethylene, an organopolysiloxane containing two or more hydroxyl end groups, and a liquid polymer modifier.
  • E11 The crosslinkable mixture of E10 wherein the crosslinkable mixture forms a crosslinked polymeric composition comprising polysiloxane linkages between the polymer chains of the polyolefin when the crosslinkable mixture is melt-shaped into an article, the polysiloxane linkages having the structure (I)
  • n 1 to 100,000.
  • a melt-shaped article includes a crosslinked polyethylene composition comprising polysiloxane linkages between the polymer chains of the polyethylene, the polysiloxane linkages having the structure (I)
  • n 1 to 100,000; and a liquid polymer modifier.
  • E13. The melt-shaped article of E12 comprising a first polyethylene is crosslinked to a second polyethylene by way of the polysiloxane linkage of structure (I).
  • E14. The melt shaped article of any of E12-13 wherein the melt shaped article is selected from the group consisting of an insulation layer, a cable coating, and an electric power cable.
  • An insulation layer of an electric cable comprises a crosslinked polyethylene composition comprising polysiloxane linkages between the polyethylene chains, the silane linkages having the structure (I)
  • a melt-shaped article comprises a crosslinked polyethylene composition, an organopolysiloxane containing two or more hydroxyl end groups, and a liquid polymer modifier.
  • E18. The melt-shaped article of E17 wherein the organopolysiloxane containing two or more hydroxyl end groups is hydroxyl-terminated polydimethylsiloxane.
  • E19. The melt-shaped article of any of E17-E18 comprising a crosslinking catalyst.
  • E20. The melt-shaped article of any of E17-E19 comprising polysiloxane linkages between the polyethylene chains, the polysiloxane linkages having the structure (I)
  • n 1 to 100,000.
  • E21. The melt-shaped article of any of E17-E20 wherein the melt shaped article is selected from the group consisting of an insulation layer, a cable coating, and an electric power cable.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Spectroscopy & Molecular Physics (AREA)
  • Physics & Mathematics (AREA)
  • Mechanical Engineering (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Composite Materials (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Processes Of Treating Macromolecular Substances (AREA)
  • Organic Insulating Materials (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Graft Or Block Polymers (AREA)
US13/496,430 2009-09-16 2010-09-14 Crosslinked, Melt-Shapped Articles and Compositions for Producing Same Abandoned US20120178868A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US13/496,430 US20120178868A1 (en) 2009-09-16 2010-09-14 Crosslinked, Melt-Shapped Articles and Compositions for Producing Same

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US24285709P 2009-09-16 2009-09-16
US13/496,430 US20120178868A1 (en) 2009-09-16 2010-09-14 Crosslinked, Melt-Shapped Articles and Compositions for Producing Same
PCT/US2010/048727 WO2011034838A1 (en) 2009-09-16 2010-09-14 Crosslinked, melt-shaped articles and compositions for producing same

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/048727 A-371-Of-International WO2011034838A1 (en) 2009-09-16 2010-09-14 Crosslinked, melt-shaped articles and compositions for producing same

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/192,319 Division US9272469B2 (en) 2009-09-16 2014-02-27 Crosslinked, melt-shaped articles and compositions for producing same

Publications (1)

Publication Number Publication Date
US20120178868A1 true US20120178868A1 (en) 2012-07-12

Family

ID=43066821

Family Applications (4)

Application Number Title Priority Date Filing Date
US13/496,430 Abandoned US20120178868A1 (en) 2009-09-16 2010-09-14 Crosslinked, Melt-Shapped Articles and Compositions for Producing Same
US13/496,410 Active 2030-10-01 US8835548B2 (en) 2009-09-16 2010-09-14 Process for producing crosslinked, melt-shaped articles
US14/192,319 Active US9272469B2 (en) 2009-09-16 2014-02-27 Crosslinked, melt-shaped articles and compositions for producing same
US14/457,692 Active 2030-09-30 US9387625B2 (en) 2009-09-16 2014-08-12 Process for producing crosslinked, melt-shaped articles

Family Applications After (3)

Application Number Title Priority Date Filing Date
US13/496,410 Active 2030-10-01 US8835548B2 (en) 2009-09-16 2010-09-14 Process for producing crosslinked, melt-shaped articles
US14/192,319 Active US9272469B2 (en) 2009-09-16 2014-02-27 Crosslinked, melt-shaped articles and compositions for producing same
US14/457,692 Active 2030-09-30 US9387625B2 (en) 2009-09-16 2014-08-12 Process for producing crosslinked, melt-shaped articles

Country Status (10)

Country Link
US (4) US20120178868A1 (ja)
EP (2) EP2478041B1 (ja)
JP (2) JP5723372B2 (ja)
KR (2) KR101740080B1 (ja)
CN (2) CN102630236B (ja)
BR (2) BR112012006019B1 (ja)
CA (2) CA2774280C (ja)
MX (2) MX342552B (ja)
TW (2) TW201116561A (ja)
WO (2) WO2011034836A1 (ja)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130177282A1 (en) * 2010-09-29 2013-07-11 Buo Chen Flexible Strength Members for Wire Cables
WO2014105292A1 (en) * 2012-12-31 2014-07-03 Dow Global Technologies Llc A composition, articles made therefrom, and method of making the articles
WO2016176034A1 (en) 2015-04-30 2016-11-03 Dow Global Technologies Llc Hydroxyl-terminated pdms as cure control additive for the silane crosslinking of polyolefins
WO2019027955A1 (en) * 2017-07-31 2019-02-07 Dow Global Technologies Llc HUMIDITY-CURABLE COMPOSITION FOR ISOLATION AND SHEATH LAYERS OF WIRES AND CABLE
US20200199397A1 (en) * 2017-07-31 2020-06-25 Dow Global Technologies Llc Moisture Curable Composition for Wire and Cable Insulation and Jacket Layers
US11460654B2 (en) * 2017-09-13 2022-10-04 Hexatronic Cables & Interconnect Systems Ab Cable sheath material
US11884821B2 (en) 2018-02-01 2024-01-30 Dow Silicones Corporation Composition, polymer composite article formed therewith, and method of preparing same

Families Citing this family (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120178868A1 (en) * 2009-09-16 2012-07-12 Mohamed Esseghir Crosslinked, Melt-Shapped Articles and Compositions for Producing Same
MX346691B (es) 2012-01-31 2017-03-29 Dow Global Technologies Llc Composiciones semiconductoras, termoplasticas.
RU2498435C1 (ru) * 2012-03-21 2013-11-10 Российская Федерация, От Имени Которой Выступает Министерство Промышленности И Торговли Российской Федерации Способ изготовления электрического провода
JP2016502979A (ja) * 2012-12-07 2016-02-01 ダウ グローバル テクノロジーズ エルエルシー パーソナルケア用途におけるシリコーン変性ポリオレフィン
CN105025877B (zh) 2012-12-19 2018-01-23 陶氏环球技术有限责任公司 个人护理应用中的含硅聚烯烃
MX2015012396A (es) * 2013-03-14 2016-02-03 Arkema Inc Metodos para la reticulacion de composiciones polimeras en presencia de oxigeno atmosferico.
BR112015028197A2 (pt) * 2013-05-10 2017-07-25 Procter & Gamble produtos destinados ao consumidor que compreendem óleos modificados por silano
US10040888B1 (en) 2013-06-14 2018-08-07 Cooper-Standard Automotive Inc. Composition including silane-grafted polyolefin
CN105452384B (zh) * 2013-06-25 2020-11-27 陶氏环球技术有限责任公司 聚烯烃弹性体和聚硅氧烷掺合物
US10100139B2 (en) * 2013-08-01 2018-10-16 Cooper-Standard Automotive Inc. Hose, composition including silane-grafted polyolefin, and process of making a hose
US10308829B2 (en) 2013-11-25 2019-06-04 Dow Global Technologies Llc Moisture-and peroxide-crosslinkable polymeric compositions
WO2015196459A1 (en) * 2014-06-27 2015-12-30 Dow Global Technologies Llc Cold shrink article for electrical device
US10371292B2 (en) 2014-07-02 2019-08-06 Cooper-Standard Automotive Inc. Hose, abrasion resistant composition, and process of making a hose
US10308782B2 (en) * 2014-08-15 2019-06-04 Dow Global Technologies Llc Polydimethylsiloxane grafted polyethylene foam
JP2017040299A (ja) * 2015-08-19 2017-02-23 株式会社ブリヂストン 架橋ポリオレフィンパイプ
WO2018044414A1 (en) 2016-08-30 2018-03-08 Dow Global Technologies Llc Method for thermally insulating subsea structures
KR102136703B1 (ko) 2016-12-10 2020-07-22 쿠퍼-스탠다드 오토모티브 인코포레이티드 신발창, 조성물, 및 이들의 제조 방법
CN110268033A (zh) 2016-12-10 2019-09-20 库珀标准汽车公司 组合密封件、制造其的组合物和方法
WO2019023008A1 (en) * 2017-07-25 2019-01-31 Dow Silicones Corporation PROCESS FOR THE PREPARATION OF A GRAFT COPOLYMER HAVING A POLYOLEFIN SKELETON AND POLYORGANOSILOXANE PENDANT GROUPS
JP7378411B2 (ja) 2018-03-19 2023-11-13 ダウ シリコーンズ コーポレーション ポリオレフィン－ポリジオルガノシロキサンブロックコポリマーおよびその合成のための加水分解反応方法
US11814555B2 (en) 2018-03-19 2023-11-14 Dow Silicones Corporation Hot melt adhesive compositions containing polyolefin-polydiorganosiloxane copolymers and methods for the preparation and use thereof
WO2019182718A1 (en) 2018-03-19 2019-09-26 Dow Silicones Corporation Hot melt adhesive composition containing a polyolefin - polydiorganosiloxane copolymer and methods for the preparation and use thereof
US10150868B1 (en) 2018-03-28 2018-12-11 Dow Global Technologies Llc Flooding composition with polysiloxane
US10162141B1 (en) * 2018-03-28 2018-12-25 Dow Global Technologies Llc Flooding composition with polysiloxane
US20210238370A1 (en) * 2018-04-27 2021-08-05 Dow Global Technologies Llc Foamed Polyolefin Compositions for Wire and Cable Coating
JP7334195B2 (ja) * 2018-07-17 2023-08-28 ダウ シリコーンズ コーポレーション ポリシロキサン樹脂－ポリオレフィンコポリマー並びにその調製方法及び使用方法
RU2770612C1 (ru) * 2018-10-02 2022-04-19 Бореалис Аг Высокоскоростное сшивание привитых пластомеров
EP3738745A1 (en) * 2019-05-13 2020-11-18 Henkel AG & Co. KGaA Reactive printable composition with elastomeric properties
BR112022003038A2 (pt) * 2019-08-29 2022-05-10 Dow Global Technologies Llc Método para produzir uma mistura homogênea de sólidos de poliolefina e um aditivo sólido particulado sem fundir os sólidos de poliolefina ou o aditivo sólido particulado durante a produção, e, produto curado moldado
EP4172256A1 (en) * 2020-06-24 2023-05-03 Dow Global Technologies LLC Cure and functionalization of olefin/silane interpolymers
JP2024515644A (ja) 2021-05-18 2024-04-10 サン－ゴバン パフォーマンス プラスティックス コーポレイション 複合管及び製造方法
WO2023141494A1 (en) * 2022-01-24 2023-07-27 Dow Global Technologies Llc An article made from an elastomeric polymer composition

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2640129B2 (ja) * 1987-12-24 1997-08-13 鐘淵化学工業株式会社 硬化性樹脂組成物
US20060173123A1 (en) * 2002-08-12 2006-08-03 Yang Henry W Modified polyethylene compositions

Family Cites Families (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE794718Q (fr) 1968-12-20 1973-05-16 Dow Corning Ltd Procede de reticulation d'olefines
CA1022633A (en) * 1974-05-04 1977-12-13 Shuji Yamamoto Dual coated power cable with calcium oxide filler
US4144202A (en) 1977-12-27 1979-03-13 Union Carbide Corporation Dielectric compositions comprising ethylene polymer stabilized against water treeing with epoxy containing organo silanes
DE3587828T2 (de) * 1984-07-26 1994-09-29 Kanegafuchi Chemical Ind Vernetzbare Polymerzusammensetzung.
JPH066661B2 (ja) * 1985-12-18 1994-01-26 日本合成ゴム株式会社 耐熱性エチレン−α−オレフイン系共重合体組成物の製造方法
JPS63225610A (ja) * 1986-10-16 1988-09-20 Japan Synthetic Rubber Co Ltd グラフト共重合体およびグラフト共重合体組成物
JPS63146303A (ja) * 1986-12-08 1988-06-18 ジェイエスアール株式会社 電気絶縁材料
JPS63172757A (ja) * 1987-01-09 1988-07-16 Japan Synthetic Rubber Co Ltd ゴム組成物
US4806594A (en) * 1987-06-17 1989-02-21 Union Carbide Corporation Water curable compositions of silane containing ole36in polymers
US5169900A (en) 1988-08-05 1992-12-08 Du Pont Canada Inc. Polyolefin coatings and films having release characteristics
US5064802A (en) 1989-09-14 1991-11-12 The Dow Chemical Company Metal complex compounds
US5272236A (en) 1991-10-15 1993-12-21 The Dow Chemical Company Elastic substantially linear olefin polymers
US5266627A (en) 1991-02-25 1993-11-30 Quantum Chemical Corporation Hydrolyzable silane copolymer compositions resistant to premature crosslinking and process
US5246783A (en) 1991-08-15 1993-09-21 Exxon Chemical Patents Inc. Electrical devices comprising polymeric insulating or semiconducting members
US5278272A (en) 1991-10-15 1994-01-11 The Dow Chemical Company Elastic substantialy linear olefin polymers
US5783638A (en) 1991-10-15 1998-07-21 The Dow Chemical Company Elastic substantially linear ethylene polymers
US5374696A (en) 1992-03-26 1994-12-20 The Dow Chemical Company Addition polymerization process using stabilized reduced metal catalysts
CA2090793A1 (en) * 1992-10-09 1994-04-10 Ronald Sinclair Nohr Nonwoven webs having improved tensile strength characteristics
CA2084361A1 (en) * 1992-12-02 1994-06-03 Haridoss Sarma Silane-crosslinkable copolymer compositions
AU681678B2 (en) 1993-06-24 1997-09-04 Dow Chemical Company, The Titanium(II) or zirconium(II) complexes and addition polymerization catalysts therefrom
WO1995014024A1 (fr) 1993-11-18 1995-05-26 Idemitsu Kosan Co., Ltd. Compose de metal de transition, catalyseur de polymerisation d'olefines et procede pour produire un polymere d'olefines en utilisant ce catalyseur
SE502171C2 (sv) * 1993-12-20 1995-09-04 Borealis Holding As Polyetenkompatibla sulfonsyror som silanförnätningskatalysatorer
US5824718A (en) 1995-04-20 1998-10-20 The Dow Chemical Company Silane-crosslinkable, substantially linear ethylene polymers and their uses
JP3186542B2 (ja) * 1995-09-27 2001-07-11 住友ベークライト株式会社 難燃発泡架橋ポリオレフィン絶縁電線の製造方法
WO1998010724A1 (en) * 1996-09-13 1998-03-19 Dupont Canada Inc. Silicone-containing polyolefin film
US6465107B1 (en) * 1996-09-13 2002-10-15 Dupont Canada Inc. Silicone-containing polyolefin film
WO1998049212A1 (en) 1997-04-30 1998-11-05 The Dow Chemical Company Ethylene/alpha-olefin/diene interpolymers and their preparation
CA2291316A1 (en) * 1999-01-08 2000-07-08 Nicholas A. Farkas Silicone-containing low surface tension film
US6496629B2 (en) 1999-05-28 2002-12-17 Tycom (Us) Inc. Undersea telecommunications cable
JP4061824B2 (ja) * 2000-07-25 2008-03-19 三井化学株式会社 ゴム組成物
DE60142680D1 (de) * 2001-05-11 2010-09-09 Borealis Tech Oy Verfahren zur Vernetzung von Polymerartikeln
US6714707B2 (en) 2002-01-24 2004-03-30 Alcatel Optical cable housing an optical unit surrounded by a plurality of gel layers
KR20070085655A (ko) * 2004-12-03 2007-08-27 다우 글로벌 테크놀로지스 인크. 탄성 폴리올레핀 섬유의 방출 특성 개선 방법
US20120178868A1 (en) * 2009-09-16 2012-07-12 Mohamed Esseghir Crosslinked, Melt-Shapped Articles and Compositions for Producing Same
JP6006661B2 (ja) * 2013-02-27 2016-10-12 ミネベア株式会社 ブラシレスモータ

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2640129B2 (ja) * 1987-12-24 1997-08-13 鐘淵化学工業株式会社 硬化性樹脂組成物
US20060173123A1 (en) * 2002-08-12 2006-08-03 Yang Henry W Modified polyethylene compositions

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Machine Translation of JP 2640129 B2 *

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130177282A1 (en) * 2010-09-29 2013-07-11 Buo Chen Flexible Strength Members for Wire Cables
US8995810B2 (en) * 2010-09-29 2015-03-31 Dow Global Technologies Llc Flexible strength members for wire cables
WO2014105292A1 (en) * 2012-12-31 2014-07-03 Dow Global Technologies Llc A composition, articles made therefrom, and method of making the articles
US20160200909A1 (en) * 2012-12-31 2016-07-14 Dow Global Technologies Llc A Composition, Articles Made Therefrom, and Method of Making the Articles
WO2016176034A1 (en) 2015-04-30 2016-11-03 Dow Global Technologies Llc Hydroxyl-terminated pdms as cure control additive for the silane crosslinking of polyolefins
KR20180008487A (ko) * 2015-04-30 2018-01-24 다우 글로벌 테크놀로지스 엘엘씨 폴리올레핀의 실란 가교결합을 위한 경화 조절 첨가제로서 하이드록실-말단화된 pdms
KR102602891B1 (ko) 2015-04-30 2023-11-17 다우 글로벌 테크놀로지스 엘엘씨 폴리올레핀의 실란 가교결합을 위한 경화 조절 첨가제로서 하이드록실-말단화된 pdms
US10563022B2 (en) 2015-04-30 2020-02-18 Dow Global Technologies Llc Hydroxyl-terminated PDMS as cure control additive for the silane crosslinking of polyolefins
KR20200037274A (ko) * 2017-07-31 2020-04-08 다우 글로벌 테크놀로지스 엘엘씨 와이어 및 케이블 절연 층 및 재킷 층을 위한 수분 경화성 조성물
US20200199397A1 (en) * 2017-07-31 2020-06-25 Dow Global Technologies Llc Moisture Curable Composition for Wire and Cable Insulation and Jacket Layers
US10954410B2 (en) 2017-07-31 2021-03-23 Dow Global Technologies Llc Moisture curable composition for wire and cable insulation and jacket layers
RU2769510C2 (ru) * 2017-07-31 2022-04-01 Дау Глоубл Текнолоджиз Ллк Влагоотверждаемая композиция для изоляции провода и кабеля и слоёв оболочки
US11361879B2 (en) 2017-07-31 2022-06-14 Dow Global Technologies Llc Moisture curable composition for wire and cable insulation and jacket layers
KR102540458B1 (ko) 2017-07-31 2023-06-12 다우 글로벌 테크놀로지스 엘엘씨 와이어 및 케이블 절연 층 및 재킷 층을 위한 수분 경화성 조성물
WO2019027955A1 (en) * 2017-07-31 2019-02-07 Dow Global Technologies Llc HUMIDITY-CURABLE COMPOSITION FOR ISOLATION AND SHEATH LAYERS OF WIRES AND CABLE
US11460654B2 (en) * 2017-09-13 2022-10-04 Hexatronic Cables & Interconnect Systems Ab Cable sheath material
US11884821B2 (en) 2018-02-01 2024-01-30 Dow Silicones Corporation Composition, polymer composite article formed therewith, and method of preparing same

Also Published As

Publication number Publication date
KR101768730B1 (ko) 2017-08-16
MX342552B (es) 2016-10-04
US20150028518A1 (en) 2015-01-29
WO2011034838A1 (en) 2011-03-24
US9272469B2 (en) 2016-03-01
CA2774284C (en) 2017-11-28
CN102630236B (zh) 2015-08-12
EP2478042A1 (en) 2012-07-25
JP5647688B2 (ja) 2015-01-07
KR20120090065A (ko) 2012-08-16
MX2012003320A (es) 2012-07-23
BR112012006019A2 (pt) 2020-08-25
MX2012003330A (es) 2012-07-23
JP2013505331A (ja) 2013-02-14
KR20120089482A (ko) 2012-08-10
JP2013505332A (ja) 2013-02-14
BR112012006019B1 (pt) 2021-05-11
US9387625B2 (en) 2016-07-12
CA2774280C (en) 2016-11-08
US20140193628A1 (en) 2014-07-10
US20120178867A1 (en) 2012-07-12
EP2478042B1 (en) 2019-02-20
JP5723372B2 (ja) 2015-05-27
BR112012006018A2 (pt) 2020-10-13
WO2011034838A8 (en) 2011-06-30
WO2011034836A8 (en) 2011-04-28
TW201116561A (en) 2011-05-16
TW201125902A (en) 2011-08-01
WO2011034836A1 (en) 2011-03-24
CN102630237B (zh) 2015-06-24
CN102630236A (zh) 2012-08-08
EP2478041A1 (en) 2012-07-25
CN102630237A (zh) 2012-08-08
KR101740080B1 (ko) 2017-05-25
CA2774284A1 (en) 2011-03-24
BR112012006018B1 (pt) 2021-03-02
US8835548B2 (en) 2014-09-16
CA2774280A1 (en) 2011-03-24
EP2478041B1 (en) 2014-04-23

Similar Documents

Publication Publication Date Title
US9272469B2 (en) Crosslinked, melt-shaped articles and compositions for producing same
US9595365B2 (en) Thermoplastic, semiconductive compositions
JP5331900B2 (ja) エチレン−ビニルシランコポリマーの湿分硬化用触媒系
EP3784721A1 (en) Non-foam polyolefin compositions for wire and cable coating
WO2010074925A1 (en) In-situ catalyst and moisture generation for crosslinking of silane-functionalized polyolefins

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION