US20110223486A1 - Biaxially oriented porous membranes, composites, and methods of manufacture and use - Google Patents

Biaxially oriented porous membranes, composites, and methods of manufacture and use Download PDF

Info

Publication number
US20110223486A1
US20110223486A1 US13/044,708 US201113044708A US2011223486A1 US 20110223486 A1 US20110223486 A1 US 20110223486A1 US 201113044708 A US201113044708 A US 201113044708A US 2011223486 A1 US2011223486 A1 US 2011223486A1
Authority
US
United States
Prior art keywords
membrane
stretching
machine direction
nonwoven
transverse direction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/044,708
Other languages
English (en)
Inventor
Xiaomin Zhang
Gerald P. Rumierz
Karl F. Humiston
Charles E. Haire
Tyrone S. Fields
Michael A. Braswell
Ronald A. Proctor
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Celgard LLC
Original Assignee
Celgard LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=44560305&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20110223486(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Celgard LLC filed Critical Celgard LLC
Priority to US13/044,708 priority Critical patent/US20110223486A1/en
Priority to KR1020217001682A priority patent/KR102373866B1/ko
Priority to KR1020127023376A priority patent/KR20130039713A/ko
Priority to PCT/US2011/028019 priority patent/WO2011112885A1/en
Priority to KR1020187026494A priority patent/KR102206794B1/ko
Priority to KR1020177025941A priority patent/KR101900241B1/ko
Priority to CN201710665948.2A priority patent/CN107362693A/zh
Priority to TW106139335A priority patent/TWI635644B/zh
Priority to JP2012557266A priority patent/JP2013527260A/ja
Priority to KR1020227007744A priority patent/KR102629227B1/ko
Priority to KR1020247002330A priority patent/KR20240014616A/ko
Priority to EP11754128.4A priority patent/EP2544841B2/en
Priority to CN2011800231871A priority patent/CN102892534A/zh
Assigned to CELGARD, LLC reassignment CELGARD, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: RUMIERZ, GERALD P., BRASWELL, MICHAEL A., FIELDS, TYRONE S., ZHANG, XIAOMIN, HAIRE, CHARLES E., HUMISTON, KARL F., PROCTOR, RONALD A.
Assigned to CELGARD, LLC reassignment CELGARD, LLC CORRECTIVE ASSIGNMENT TO CORRECT THE APPLICATION NUMBER PREVIOUSLY RECORDED ON REEL 025948 FRAME 0316. ASSIGNOR(S) HEREBY CONFIRMS THE TO RE-RECORD ASSIGNMENT PREVIOUSLY RECORDED UNDER REEL/FRAME 025948/0316 TO CORRECT THE APPLICATION # FROM 13944697 TO 13044708.. Assignors: RUMIERZ, GERALD P., BRASWELL, MICHAEL A., FIELDS, TYRONE S., ZHANG, XIAOMIN, HAIRE, CHARLES E., HUMISTON, KARL F., PROCTOR, RONALD A.
Publication of US20110223486A1 publication Critical patent/US20110223486A1/en
Assigned to BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT reassignment BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT PATENT SECURITY AGREEMENT Assignors: CELGARD, LLC (F/K/A CELGARD, INC.)
Assigned to CELGARD, LLC (F/K/A/ CELGARD, INC.) reassignment CELGARD, LLC (F/K/A/ CELGARD, INC.) TERMINATION AND RELEASE OF SECURITY INTEREST IN UNITED STATES PATENTS Assignors: BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT
Priority to JP2016022936A priority patent/JP2016166334A/ja
Priority to US15/582,866 priority patent/US20170266865A1/en
Priority to JP2017225491A priority patent/JP6773630B2/ja
Priority to JP2020166927A priority patent/JP2021021072A/ja
Priority to JP2022191517A priority patent/JP2023021167A/ja
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C55/00—Shaping by stretching, e.g. drawing through a die; Apparatus therefor
    • B29C55/02—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets
    • B29C55/10—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial
    • B29C55/12—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial biaxial
    • B29C55/14—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial biaxial successively
    • B29C55/143—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial biaxial successively firstly parallel to the direction of feed and then transversely thereto
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D67/00—Processes specially adapted for manufacturing semi-permeable membranes for separation processes or apparatus
    • B01D67/0002—Organic membrane manufacture
    • B01D67/0023—Organic membrane manufacture by inducing porosity into non porous precursor membranes
    • B01D67/0025—Organic membrane manufacture by inducing porosity into non porous precursor membranes by mechanical treatment, e.g. pore-stretching
    • B01D67/0027—Organic membrane manufacture by inducing porosity into non porous precursor membranes by mechanical treatment, e.g. pore-stretching by stretching
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C55/00—Shaping by stretching, e.g. drawing through a die; Apparatus therefor
    • B29C55/02—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets
    • B29C55/10—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial
    • B29C55/12—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial biaxial
    • B29C55/16—Shaping by stretching, e.g. drawing through a die; Apparatus therefor of plates or sheets multiaxial biaxial simultaneously
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G69/00—Macromolecular compounds obtained by reactions forming a carboxylic amide link in the main chain of the macromolecule
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/18—Manufacture of films or sheets
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/20—Manufacture of shaped structures of ion-exchange resins
    • C08J5/22—Films, membranes or diaphragms
    • C08J5/2206—Films, membranes or diaphragms based on organic and/or inorganic macromolecular compounds
    • C08J5/2275—Heterogeneous membranes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
    • H01M10/0564—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of organic materials only
    • H01M10/0565—Polymeric materials, e.g. gel-type or solid-type
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H01M50/406—Moulding; Embossing; Cutting
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H01M50/417—Polyolefins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
    • H01M50/454—Separators, membranes or diaphragms characterised by the material having a layered structure comprising a non-fibrous layer and a fibrous layer superimposed on one another
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H01M50/491—Porosity
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H01M50/494—Tensile strength
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/50—Current conducting connections for cells or batteries
    • H01M50/572—Means for preventing undesired use or discharge
    • H01M50/574—Devices or arrangements for the interruption of current
    • H01M50/581—Devices or arrangements for the interruption of current in response to temperature
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2325/00—Details relating to properties of membranes
    • B01D2325/02—Details relating to pores or porosity of the membranes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2325/00—Details relating to properties of membranes
    • B01D2325/02—Details relating to pores or porosity of the membranes
    • B01D2325/021—Pore shapes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2325/00—Details relating to properties of membranes
    • B01D2325/02—Details relating to pores or porosity of the membranes
    • B01D2325/0283—Pore size
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2031/00—Other particular articles
    • B29L2031/755—Membranes, diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
    • Y10T428/249978—Voids specified as micro
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/30—Woven fabric [i.e., woven strand or strip material]
    • Y10T442/3854—Woven fabric with a preformed polymeric film or sheet
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/40—Knit fabric [i.e., knit strand or strip material]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/674—Nonwoven fabric with a preformed polymeric film or sheet

Definitions

  • the invention is directed to biaxially oriented porous membranes, composites including biaxially oriented porous membranes, biaxially oriented microporous membranes, biaxially oriented macroporous membranes, battery separators, filtration media, humidity control media, flat sheet membranes, liquid retention media, and the like, related methods, methods of manufacture, methods of use, and the like.
  • Microporous polymer membranes are known, can be made by various processes, and the process by which the membrane is made may have a material impact upon the membrane's physical attributes. See, for example, Kesting, Robert E., Synthetic Polymeric Membranes, A Structural Perspective, Second Edition, John Wiley & Sons, New York, N.Y., (1985).
  • Three different known processes for making microporous polymer membranes include: the dry-stretch process (also known as the CELGARD process), the wet process, and the particle stretch process.
  • the dry-stretch process refers to a process where pore formation results from stretching a nonporous, semicrystalline, extruded polymer precursor in the machine direction (MD stretch). See, for example, Kesting, Ibid. pages 290-297, incorporated herein by reference. Such a dry-stretch process is different from the wet process and the particle stretch process.
  • the wet process also known as the phase inversion process, the extraction process, or the TIPS process
  • the polymeric raw material is mixed with a processing oil (sometimes referred to as a plasticizer), this mixture is extruded, and pores are then formed when the processing oil is removed (these films may be stretched before or after the removal of the oil). See, for example, Kesting, Ibid. pages 237-286, incorporated herein by reference.
  • the polymeric raw material is mixed with particulate, this mixture is extruded, and pores are formed during stretching when the interfaces between the polymer and the particulate fracture due to the stretching forces. See, for example, U.S. Pat. Nos. 6,057,061 and 6,080,507, incorporated herein by reference.
  • each membrane arising from these different formation processes are usually physically different and the process by which each is made typically distinguishes one membrane from the other.
  • dry-stretch process membranes may have slit shaped pores due to the stretching of the precursor in the machine direction (the MD)(for example, see FIGS. 1-3 ).
  • Wet process membranes tend to have rounder pores and a lacelike appearance due to the oil or plasticizer and the stretching of the precursor in the machine direction (MD) and in the transverse machine direction or transverse direction (the TD)(for example, see FIG. 4 ).
  • Particle stretch process membranes on the other hand, may have oval shaped pores as the particulate and machine direction stretching (MD stretch) tend to form the pores (for example, see FIG. 5A ). Accordingly, each membrane may be distinguished from the other by its method of manufacture.
  • membranes made by the dry-stretch process have met with excellent commercial success, such as a variety of CELGARD® dry-stretch porous membranes sold by Celgard, LLC of Charlotte, N.C., including flat sheet membranes, battery separators, hollow fibers, and the like, there is a need to improve, modify or enhance at least selected physical attributes thereof, so that they may be used in a wider spectrum of applications, may perform better for particular purposes, or the like.
  • air-filters to remove or reduce airborne contaminants such as dust, dust mites, molds, bacteria, dog dander, odors, and gases.
  • air-filters include a filter medium formed from a bat, mat or sheet of porous material that is pleated and placed in a rectangular frame or support or folded into a corrugated oval or cylinder to provide a large filtration area in a relatively small volume.
  • LIQUI-CEL® hollow fiber membrane contactors sold by Membrana-Charlotte a division of Celgard, LLC of Charlotte, N.C., are used for degassing or debubbling liquids. More particularly, LIQUI-CEL® membrane contactors are used extensively for deaeration of liquids in the microelectronics, pharmaceutical, power, food, beverage, industrial, photographic, ink, and analytical markets around the world.
  • porous materials for filtration or separation processes.
  • various flat sheet membranes marketed or sold by Membrana GmbH of Wuppertal, Germany, or by Celgard, LLC and Daramic, LLC both of Charlotte, N.C., are used for filtration or separation processes. More particularly, such flat sheet membranes have been used to separate solid particles and liquids, gases from liquids, particles from gases, and the like.
  • porous materials for filtration or separation processes have met with commercial success, there is a need for improved porous materials so that they may be used in a wider spectrum of applications, may perform better for particular purposes, or the like.
  • porous materials for the selective passage of humidity (moisture vapor) and blockage of liquid water, liquid desiccant, or other aqueous solutions may be known.
  • temperature and humidity may be controlled by a salt solution (or desiccant) which absorbs or emits water vapor.
  • porous materials for the selective passage of water vapor (heat and moisture) and the blockage of gasses (exhaust and intake gases) may be known in connection with energy recovery ventilation (ERV) wherein heat and humidity are exchanged between make-up and exhaust air in a ventilation system.
  • ERP energy recovery ventilation
  • porous materials for the selective passage of pure or fresh water and blockage of salt or salt water is also known in connection with reverse osmosis desalination wherein a porous material, such as a reverse osmosis filter (RO filter) which allows pure water (fresh water) to pass there through but which restrains salt.
  • RO filter reverse osmosis filter
  • porous materials for the selective passage of water vapor or humidity (moisture vapor) and blockage of liquid salt water may also be known in connection with steam desalination wherein a porous material, such as a high charge density membrane may hold back salt water but pass salt-free water vapor to separate salt water and fresh water. With the salt water at a high temperature, fresh water vapor emits from the salt water, may migrate through the porous material, and condense to form a fresh water stream.
  • a porous material such as a high charge density membrane may hold back salt water but pass salt-free water vapor to separate salt water and fresh water.
  • porous materials for the selective passage of gases or humidity (moisture vapor) and blockage of liquids such as water may be known in connection with fuel cells such as hydrogen fuel cells having a proton exchange membrane (PEM) that must stay continually humidified. Waste water in the form of humid vapor may pass through a porous material and may be collected in a waste water holding compartment or discharged.
  • PEM proton exchange membrane
  • porous materials for the selective passage of gases or humidity (moisture vapor) and blockage of liquid water or salt water may have met with commercial success, such as RO membranes sold by Dow Chemical, or expanded polytetrafluoroethylene (ePTFE) membranes sold by W. L. Gore, BHA, and others, there is a need for improved porous materials so that they may be used in a wider spectrum of applications, may perform better for particular purposes, or the like.
  • RO membranes sold by Dow Chemical
  • ePTFE expanded polytetrafluoroethylene
  • some areas of improvement may include pore shapes other than slits, round shaped pores, increased transverse direction tensile strength, a balance of MD and TD physical properties, high performance related to, for example, moisture transport and hydrohead pressure, reduced Gurley, high porosity with balanced physical properties, uniformity of pore structure including pore size and pore size distribution, enhanced durability, composites of such membranes with other porous materials, composites or laminates of such membranes, films or layers with porous nonwovens, coated membranes, coextruded membranes, laminated membranes, membranes having desired moisture transport (or moisture vapor transport), hydrohead performance, and physical strength properties, usefulness in more physically abusive environments without loss of desirable membrane features, combination of membrane moisture transport performance combined with the macro physical properties, being hydrophobic, highly permeable, chemically and mechanically stable, having high tensile strength, combinations thereof, and/or the like.
  • some areas of improvement may include pore shapes other than slits, round shaped pores, increased transverse direction tensile strength, a balance of MD and TD physical properties, uniformity of pore structure including pore size and pore size distribution, high performance related to, for example, moisture transport (or moisture vapor transport) and hydrohead pressure, reduced Gurley, high porosity with balanced physical properties, enhanced durability, composites of such membranes with other porous materials, composites or laminates of such membranes with porous nonwovens, coated membranes, coextruded membranes, laminated membranes, membranes having desired moisture transport, hydrohead performance, and physical strength properties, useful in more physically abusive environments without loss of desirable membrane features, combination of the membrane moisture transport performance combined with the macro physical properties, combinations thereof, and/or the like.
  • the porous membrane of the present invention is possibly preferably a dry-stretch process, porous membrane, film, layer, or composite that is hydrophobic, highly permeable, chemically and mechanically stable, has high tensile strength, and combinations thereof.
  • At least a selected porous mono-layer polypropylene (monolayer PP) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected monolayer PP membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PP membrane or film can be produced in union with or laminated to a porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (monolayer PP/nonwoven PP) or (nonwoven PP/monolayer PP/nonwoven PP) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PP/nonwoven PP) or (nonwoven PP/monolayer PP/nonwoven PP) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • these selected monolayer PP membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polypropylene (multilayer PP) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected multilayer PP membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PP membrane or film can be produced in union with or laminated to a porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • the resultant composite, membrane or product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • multilayer PP membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous mono-layer polyethylene (monolayer PE) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected monolayer PE membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PE membrane or film can be produced in union with or laminated to a porous polyethylene (PE) nonwoven material (nonwoven PE) or porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (monolayer PE/nonwoven PE) or (nonwoven PE/monolayer PE/nonwoven PE) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PE/nonwoven PE) or (nonwoven PE/monolayer PE/nonwoven PE) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • these selected monolayer PE membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polyethylene (multilayer PE) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected multilayer PE membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PE membrane or film can be produced in union with or laminated to a porous polyethylene (PE) nonwoven material (nonwoven PE) or porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (multilayer PE/nonwoven PE) or (nonwoven PE/multilayer PE/nonwoven PE) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (multilayer PE/nonwoven PE) or (nonwoven PE/multilayer PE/nonwoven PE) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • multilayer PE membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous monolayer polymer membrane for example, a monolayer (may have one or more plies) polyolefin (PO) membrane, such as a polypropylene (PP) and/or polyethylene (PE) (including PE, PP, or PE+PP blends) monolayer membrane, has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport (or moisture vapor transport) and hydrohead performance.
  • This selected monolayer PO membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PO membrane or film can be produced in union with or laminated to a porous nonwoven material, such as a nonwoven polymer material, for example, a PO nonwoven material (such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP) (including PE, PP, or PE+PP blends)) on one or both sides thereof.
  • a PO nonwoven material such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP) (including PE, PP, or PE+PP blends)
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product (monolayer PO/nonwoven PO) or (nonwoven PO/monolayer PO/nonwoven PO) may preferably retain the excellent moisture transport (or moisture vapor transport) and even more improved hydrohead performance.
  • this resultant composite product may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PO/nonwoven PO) or (nonwoven PO/monolayer PO/nonwoven PO) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features. It is believed that these selected monolayer PO membrane and composite products (monolayer PO; monolayer PO/nonwoven PO; or, nonwoven PO/monolayer PO/nonwoven PO) are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, moisture vapor transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polymer membrane for example, a multi-layer (two or more layer) polyolefin (PO) membrane, such as a polypropylene (PP) and/or polyethylene (PE) (including PE, PP, or PE+PP blends) multilayer membrane, has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport (or moisture vapor transport) and hydrohead performance.
  • This selected multilayer PO membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PO membrane or film can be produced in union with or laminated to a porous PO nonwoven material (such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP)) on one or both sides thereof.
  • a porous PO nonwoven material such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP)
  • the resultant composite, membrane or product (multilayer PO/nonwoven PO) or (nonwoven PO/multilayer PO/nonwoven PO) may preferably retain the excellent moisture transport and even more improved hydrohead performance.
  • this resultant composite product (multilayer PO/nonwoven PO) or (nonwoven PO/multilayer PO/nonwoven PO) may have physical strength properties that far exceed comparative membranes.
  • this new resultant composite product may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features. It is believed that these selected multilayer PO membrane and composite products (multilayer PO; multilayer PO/nonwoven PO; or, nonwoven PO/multilayer PO/nonwoven PO) are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • the pores (openings) have the following pore aspect ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), and transverse machine direction (TD)(width) by measuring, for example, one or more of the pores (preferably several of the pores to ascertain an average) in SEMs of the surface, top or front (A side) of selected membranes or composites, for example, mono-layer, bi-layer or tri-layer membranes:
  • a three-dimensional or 3D pore sphericity factor or ratio (MD/TD/ND) range could be: 1.0 to 8.0 or more; possibly preferred 1.0 to 2.5; and, most possibly preferred 1.0 to 2.0 or less (based on physical dimensions of the pore openings in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness); for example, measuring the MD and TD of one or more pores (preferably several pores to ascertain an average) in SEMs of the surface, top or front (A side), or the surface, bottom or back (B side), and measuring the ND of one or more pores (preferably several pores to ascertain an average) in SEMs of the cross-section, depth, or height (C side)(either length or width cross-section or both)(the ND dimension may be of a different pore than the MD and
  • the pores (openings) have the following pore aspect ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), and transverse machine direction (TD)(width) based on measuring the pores in SEMs of the top or front (A side) of selected mono-layer and tri-layer membranes: Typical numbers for aspect ratio range of Machine direction MD (length) and Transverse direction TD (width): MD/TD aspect ratio in range of 0.75 to 1.50
  • the pores (openings) have the following three dimensional or 3D pore sphericity factors or ratios (based on physical dimensions of the pore openings in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness); for example, measuring one or more pores (preferably several pores to ascertain an average) in SEMs of the surface, top or front (A side), the surface, bottom or back (B side), and the cross-section, depth, or height (C side)(either length or width cross-section or both)(the ND dimension may be of a different pore than the MD and TD dimension as it may be difficult to measure the ND, MD and TD dimension of the same pore) of selected membranes, layers or composites, for example, of selected mono-layer and tri-layer membranes:
  • the pores (openings) have the following pore sphericity factors or ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness) based on measuring the pores in SEMs of the top or front (A side) and the length and with cross-sections (C side) of selected mono-layer and tri-layer membranes:
  • a microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, preferably 0.5 to 5.0.
  • the method of making the foregoing microporous membrane includes the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction stretching including a simultaneous controlled machine direction relax.
  • a porous membrane is made by a modified dry-stretch process and has substantially round shaped pores, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, and has low Gurley as compared to prior dry-stretch membranes, has larger and more uniform mean flow pore diameters as compared to prior dry-stretch membranes, or both low Gurley and larger and more uniform mean flow pore diameters.
  • porous materials for the selective passage of gases or humidity (moisture vapor) and blockage of liquid water or salt water may have met with commercial success, such as RO membranes sold by Dow Chemical, ePTFE membranes sold by W. L. Gore, BHA, and others, in accordance with at least selected embodiments of the present invention, there is provided improved, modified or enhanced porous materials so that they may be used in a wider spectrum of applications, may perform better for particular purposes, and/or the like.
  • an air-filter cartridge includes at least one pleated porous membrane such as a microporous membrane.
  • FIG. 1 is a photograph (SEM surface photomicrograph) of a CELGARD® monolayer, conventional dry-stretch, polypropylene, battery separator.
  • FIG. 2 is a photograph of a prior art dry-stretched membrane (single ply membrane).
  • FIG. 3 is a photograph of a prior art dry-stretched membrane (multi-ply membrane, plies laminated then stretched).
  • FIG. 4 is a photograph (SEM surface photomicrograph) of a CELGARD® monolayer, wet process, polyethylene battery separator.
  • FIG. 5A is a photograph (SEM surface photomicrograph) of a particle stretch membrane.
  • FIG. 5B is a photograph (SEM cross-section photomicrograph) of a particle stretch membrane.
  • FIG. 6 is a photograph (SEM surface photomicrograph) of a membrane in accordance with one embodiment of the present invention (single ply membrane, biaxially oriented process).
  • FIG. 7 is a photograph (SEM surface photomicrograph) of a membrane in accordance with another embodiment of the present invention (multi-ply membrane, plies laminated together then stretched, biaxially oriented process).
  • FIG. 8 is a photograph (SEM surface photomicrograph) of a membrane in accordance with yet another embodiment of the instant invention (multi-ply membrane, plies coextruded then stretched, biaxially oriented process).
  • FIG. 9 is a schematic representation of exemplary TD stretch processes in accordance with at least one embodiment of the biaxially oriented membrane manufacturing method of the present invention.
  • FIG. 10 is a photograph (SEM surface photomicrograph) of a conventional CELGARD® 2500 membrane (PP monolayer, dry-stretch process) at 20,000 ⁇ magnification.
  • FIG. 11 is a photograph (SEM surface photomicrograph) of the membrane of FIG. 10 at 5,000 ⁇ magnification.
  • FIG. 12 is a photograph (SEM cross section photomicrograph) of the membrane of FIGS. 10 and 11 at 20,000 ⁇ magnification.
  • FIGS. 13 and 14 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of a membrane Sample B in accordance with another membrane embodiment of the instant invention (PP monolayer, collapsed bubble, biaxially oriented process).
  • FIGS. 15 and 16 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample B of FIGS. 13 and 14 .
  • FIGS. 17 and 18 are respective photographs (SEM cross section photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample B of FIGS. 13 to 16 .
  • FIGS. 19 , 20 and 21 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ , 5,000 ⁇ and 1,000 ⁇ magnification) of a membrane Sample C in accordance with still another membrane or composite embodiment of the instant invention (PP monolayer [of Sample B]/nonwoven PP, laminated [heat+pressure]).
  • FIGS. 22 , 23 and 24 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ , 5,000 ⁇ and 1,000 ⁇ magnification) of the membrane Sample C of FIGS. 19 to 21 .
  • FIGS. 25 and 26 are respective photographs (SEM cross section photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample C of FIGS. 19 to 24 .
  • FIG. 27 is a photograph (SEM cross section photomicrograph at 615 ⁇ magnification) of the membrane Sample C of FIGS. 19 to 26 with the nonwoven PP layer on top (inverted).
  • FIG. 27A is a photograph (SEM cross section photomicrograph at 3,420 ⁇ magnification) of a portion of the monolayer PP layer of the membrane Sample C of FIG. 27 (note the rectangle in FIG. 27 ).
  • FIGS. 28 and 29 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of a membrane Sample A in accordance with yet another membrane embodiment of the instant invention (monolayer PP, non-collapse bubble, biaxially oriented process).
  • FIGS. 30 and 31 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample A of FIGS. 28 and 29 .
  • FIGS. 32 , 33 and 34 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ , 5,000 ⁇ and 1,000 ⁇ magnification) of a membrane or composite Sample G in accordance with another embodiment of the instant invention (PP monolayer, non-collapse bubble, biaxially oriented process [of Sample A]/nonwoven PP, laminated [heat+pressure]).
  • FIGS. 35 , 36 and 37 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ , 5,000 ⁇ and 1,000 ⁇ magnification) of the membrane Sample G of FIGS. 32 to 34 .
  • FIGS. 38 and 39 are respective photographs (SEM cross section photomicrographs at 20,000 ⁇ and 3,420 ⁇ magnification) of the membrane Sample G of FIGS. 32 to 37 .
  • FIG. 40 is a photograph (SEM cross section photomicrograph at 615 ⁇ magnification) of the membrane Sample G of FIGS. 32 to 39 with the nonwoven PP layer on top (inverted).
  • FIG. 40A is a photograph (SEM cross section photomicrograph at 3,420 ⁇ magnification) of a portion of the monolayer PP layer of the membrane Sample G of FIG. 40 (note the rectangle in FIG. 40 ).
  • FIGS. 41 and 42 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of a membrane Sample E in accordance with still another membrane embodiment of the instant invention (PP monolayer, collapsed bubble, biaxially oriented process).
  • FIGS. 43 and 44 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample E of FIGS. 41 and 42 .
  • FIGS. 45 and 46 are respective photographs (SEM cross section photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample E of FIGS. 41 to 44 .
  • FIGS. 47 and 48 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of a membrane Sample F in accordance with yet another membrane embodiment of the instant invention (monolayer PP, non-collapse bubble, biaxially oriented process).
  • FIGS. 49 and 50 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample F of FIGS. 47 and 48 .
  • FIGS. 51 and 52 are respective photographs (SEM surface A (top) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of a membrane Sample D in accordance with still yet another membrane embodiment of the instant invention (coextruded PP/PE/PP tri-layer, collapsed bubble, biaxially oriented process).
  • FIGS. 53 and 54 are respective photographs (SEM surface B (bottom) photomicrographs at 20,000 ⁇ and 5,000 ⁇ magnification) of the membrane Sample D of FIGS. 51 and 52 .
  • a microporous membrane is made by a preferred modified dry-stretch process (biaxially oriented process) and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, preferably 0.5 to 5.0, most preferably 0.5 to 4.0.
  • a porous membrane such as a microporous membrane is a thin, pliable, polymeric sheet, foil, or film having a plurality of pores therethrough.
  • Such membranes may be single or multiple plies, single or multiple layers, composites, laminates, or the like and may be used in a wide variety of applications, including, but not limited to, mass transfer membranes, pressure regulators, filtration membranes, medical devices, separators for electrochemical storage devices, membranes for use in fuel cells, and/or the like.
  • At least selected embodiments of the membrane of the present invention are made by a modified version of the dry-stretch process (also known as the CELGARD process).
  • the dry-stretch process refers to a process where pore formation results from stretching the nonporous precursor. See, Kesting, R., Synthetic Polymeric Membranes, A structural perspective, Second Edition, John Wiley & Sons, New York, N.Y., (1985), pages 290-297, incorporated herein by reference.
  • the dry-stretch process is distinguished from the wet process and particle stretch process, as discussed above.
  • At least selected membrane embodiments of the present invention may be distinguished from prior dry-stretched membranes in at least two ways: 1) substantially round shape pores, and 2) a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, preferably 0.5 to 5.0, most preferably 0.5 to 4.0.
  • At least selected membrane embodiments of the present invention may be distinguished from prior dry-stretched membranes in at least five ways: 1) substantially round shape pores, 2) a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, 3) mean flow pore diameters in the range of 0.025 to 0.150 um, 4) high gas or moisture permeability, with JIS Gurley in the range of 0.5 to 200 seconds, and (5) hydrohead pressure higher than 140 psi.
  • the pores are preferably characterized as substantially round shaped. See, for example, FIGS. 6-8 , 13 - 16 , 19 , 20 , 22 , 23 , 28 - 31 , 32 , 33 , 35 , 36 , 41 - 44 , 47 - 50 , and 51 - 54 .
  • This pore shape is contrasted with the slit shaped pores of the prior conventional dry-stretched membranes. See FIGS. 1-3 and Kesting, Ibid.
  • the pore shape of the instant membrane may be characterized by an aspect ratio, the ratio of the length (MD) to the width (TD) of the pore. In one embodiment of the instant membrane, the aspect ratio ranges from 0.75 to 1.25. This is contrasted with the aspect ratio of the prior dry-stretched membranes which are greater than 5.0. See Table I below.
  • this ratio is between 0.5 to 6.0, preferably 0.5 to 5.0. This ratio is contrasted with the corresponding ratio of the prior art membranes which is greater than 10.0. See Table I below.
  • U.S. Pat. No. 6,602,593 is directed to a microporous membrane, made by a dry-stretch process, where the resulting membrane has a ratio of transverse direction tensile strength to machine direction tensile strength of 0.12 to 1.2. Therein, the TD/MD tensile ratio is obtained by a blow-up ratio of at least 1.5 as the precursor is extruded.
  • At least selected embodiments of the instant membrane may be further characterized as follows: an average pore size in the range of 0.03 to 0.30 microns ( ⁇ m); a porosity in the range of 20-80%; and/or a transverse direction tensile strength of greater than 250 Kg/cm 2 .
  • the foregoing values are exemplary values and are not intended to be limiting, and accordingly should be viewed as merely representative of at least selected embodiments of the instant membrane.
  • At least selected embodiments of the instant membrane may be further characterized as follows: a pore size in the range of 0.30 to 1.0 microns ( ⁇ m); and an average aspect ratio in the range of about 1.0 to 1.10.
  • a pore size in the range of 0.30 to 1.0 microns ( ⁇ m); and an average aspect ratio in the range of about 1.0 to 1.10.
  • At least selected possibly preferred embodiments of the instant membrane may be further characterized as follows: an average aquapore size in the range of 0.05 to 0.50 microns ( ⁇ m); a porosity in the range of 40-90%; and/or a transverse direction tensile strength of greater than 250 Kg/cm 2 .
  • the foregoing values are exemplary values and are not intended to be limiting, and accordingly should be viewed as merely representative of at least selected possibly preferred embodiments of the instant membrane.
  • the preferred polymers used in the instant membrane may be characterized as thermoplastic polymers. These polymers may be further characterized as semi-crystalline polymers.
  • semi-crystalline polymer may be a polymer having a crystallinity in the range of 20% to 80%.
  • Such polymers may be selected from the following group: polyolefins, fluorocarbons, polyamides, polyesters, polyacetals (or polyoxymethylenes), polysulfides, polyvinyl alcohols, co-polymers thereof, and combinations thereof.
  • Polyolefins may be preferred and may include polyethylenes (LDPE, LLDPE, HDPE, UHMWPE), polypropylene, polybutene, polymethylpentene, co-polymers thereof, and blends thereof.
  • Fluorocarbons may include polytetrafluoroethylene (PTFE), polychlorotrifluoroethylene (PCTFE), fluorinated ethylene propylene (FEP), ethylene chlortrifluoroethylene (ECTFE), ethylene tetrafluoroethylene (ETFE), polyvinylidene fluoride (PVDF), polyvinylfluoride (PVF), prefluoroalkoxy (PFA) resin, co-polymers thereof, and blends thereof.
  • Polyamides may include, but are not limited to: polyamide 6, polyamide 6/6, Nylon 10/10, polyphthalamide (PPA), co-polymers thereof, and blends thereof.
  • Polyesters may include polyester terephthalate (PET), polybutylene terephthalate (PBT), poly-1-4-cyclohexylenedimethylene terephthalate (PCT), and liquid crystal polymers (LOP).
  • PET polyester terephthalate
  • PBT polybutylene terephthalate
  • PCT poly-1-4-cyclohexylenedimethylene terephthalate
  • LOP liquid crystal polymers
  • Polysulfides include, but are not limited to, polyphenylsulfide, co-polymers thereof, and blends thereof.
  • Polyvinyl alcohols include, but are not limited to, ethylene-vinyl alcohol, co-polymers thereof, and blends thereof.
  • At least certain embodiments of the instant membrane may include other ingredients, as is well known.
  • those ingredients may include: fillers (inert particulates typically used to reduce the cost of the membrane, but otherwise having no significant impact on the manufacture of the membrane), anti-static agents, anti-blocking agents, anti-oxidants, lubricants (to facilitate manufacture), colorants, and/or the like.
  • Various materials may be added to the polymers to modify or enhance the properties of the membrane.
  • Such materials include, but are not limited to: (1) polyolefins or polyolefin oligomers with a melting temperature less than 130° C.;
  • mineral fillers include, but are not limited to: calcium carbonate, zinc oxide, diatomaceous earth, talc, kaolin, synthetic silica, mica, clay, boron nitride, silicon dioxide, titanium dioxide, barium sulfate, aluminum hydroxide, magnesium hydroxide, and/or the like, and blends thereof;
  • (3) elastomers include, but are not limited to: ethylene-propylene (EPR), ethylene-propylene-diene (EPDM), styrene-butadiene (SBR), styrene isoprene (SIR), ethylidene norbornene (ENS), epoxy, and polyurethane, and blends thereof;
  • wetting agents include, but are not
  • beta-nucleated polypropylene (At least the preferred instant membrane, however, specifically excludes any beta-nucleated polypropylene (BNPP) as disclosed in U.S. Pat. No. 6,368,742, incorporated herein by reference.
  • a beta-nucleating agent for polypropylene is a substance that causes the creation of beta crystals in polypropylene.
  • the instant membrane may be a single ply or multi-ply membrane.
  • the instant biaxially oriented membrane may be one ply or layer of the multi-ply membrane or the instant membrane may be all of the plies of the multi-ply membrane. If the instant membrane is less than all of the plies of the multi-ply membrane, the multi-ply membrane may be made via a coating, lamination or bonding process. If the instant membrane is all plies of the multi-ply membrane, the multi-ply membrane may be made via a lamination or extrusion process (such as coextrusion). Further, multi-ply membranes may be made of plies of the same materials or of differing materials.
  • the instant membrane is preferably made by a modified dry-stretch process where the precursor membrane is biaxially stretched (i.e., not only stretched in the machine direction, but also in the transverse machine direction). This process will be discussed in greater detail below.
  • the process for making the foregoing membrane includes the steps of extruding a nonporous (single or multi-layer) precursor, and then biaxially stretching the nonporous precursor.
  • the nonporous precursor may be annealed prior to stretching.
  • the biaxial stretching includes a machine direction stretch and a transverse direction stretch with a simultaneous controlled machine direction relax.
  • the machine direction stretch and the transverse direction stretch may be simultaneous or sequential.
  • the machine direction stretch is followed by the transverse direction stretch with the simultaneous machine direction relax. This process is discussed in greater detail below.
  • Extrusion is generally conventional (conventional refers to conventional for a dry-stretch process).
  • the extruder may have a slot die (for flat precursor) or an annular die (for parison or bubble precursor).
  • an inflated parison technique may be employed (e.g., a blow up ratio (BUR) of less than 1.5 as the precursor is extruded).
  • BUR blow up ratio
  • the birefringence of the nonporous precursor does not have to be as high as in the conventional dry-stretch process.
  • the birefringence of the precursor would be >0.0130; while with the instant process, the birefringence of the PP precursor could be as low as 0.0100.
  • a membrane with a >35% porosity from a polyethylene resin the birefringence of the precursor would be >0.0280; while with the instant process, the birefringence of the PE precursor could be as low as 0.0240.
  • Annealing may be carried out, in one embodiment, at temperatures between T m -80° C. and T m -10° C. (where T m is the melt temperature of the polymer); and in another embodiment, at temperatures between T m -50° C. and T m -15° C.
  • T m is the melt temperature of the polymer
  • T m -50° C. and T m -15° C Some materials, e.g., those with high crystallinity after extrusion, such as polybutene, may require no annealing. Additional optional steps may be carried out, for example but not limited to heat set, extraction, removal, winding, slitting, and/or the like.
  • Machine direction stretch may be conducted as a cold stretch or a hot stretch or both, and as a single step or multiple steps.
  • cold stretching may be carried out at ⁇ T m -50° C., and in another embodiment, at ⁇ T m -80° C.
  • hot stretching may be carried out at ⁇ T m -10° C.
  • total machine direction stretching may be in the range of 50-500%, and in another embodiment, in the range of 100-300%.
  • the precursor may shrink in the transverse direction (conventional).
  • Transverse direction stretching includes a simultaneous controlled machine direction relax. This means that as the precursor is stretched in the transverse direction (TD stretch) the precursor is simultaneously allowed to contract (i.e., relax), in a controlled manner, in the machine direction (MD relax).
  • the transverse direction stretching may be conducted as a cold step, or a hot step, or a combination of both.
  • total transverse direction stretching may be in the range of 100-1200%, and in another embodiment, in the range of 200-900%.
  • the controlled machine direction relax may range from 5-80%, and in another embodiment, in the range of 15-65%.
  • transverse stretching may be carried out in multiple steps.
  • the precursor may or may not be allowed to shrink in the machine direction.
  • the first transverse direction step may include a transverse stretch with the controlled machine direction relax, followed by simultaneous transverse and machine direction stretching, and followed by transverse direction relax and no machine direction stretch or relax.
  • the precursor, after machine direction and transverse direction stretching may be subjected to a heat setting, as is well known.
  • test values reported herein, thickness, porosity, tensile strength, and aspect ratio were determined as follows: thickness-ASTM-D374 using the Emveco Microgage 210-A micrometer; porosity-ASTM D-2873; tensile strength-ASTM D-882 using an Instron Model 4201; and aspect ratio-measurements taken from the SEM micrographs.
  • Polypropylene (PP) resin is extruded using a 2.5 inch extruder.
  • the extruder melt temperature is 221° C.
  • Polymer melt is fed to a circular die.
  • the die temperature is set at 220° C., polymer melt is cooled by blowing air.
  • Extruded precursor has a thickness of 27 micrometers ( ⁇ m) and a birefringence of 0.0120.
  • the extruded film was then annealed at 150° C. for 2 minutes.
  • the annealed film is then cold stretched to 20% at room temperature, and then hot stretched to 228% and relaxed to 32% at 140° C.
  • the machine direction (MD) stretched film has a thickness of 16.4 ⁇ m, and porosity of 25%.
  • the MD stretched film is then transverse direction (TD) stretched 300% at 140° C. with MD relax of 50%.
  • the finished film has a thickness of 14.1 ⁇ m, and porosity of 37%.
  • TD tensile strength of finished film is 550 Kg/cm 2 . See FIG. 6 .
  • Polypropylene (PP) resin is extruded using a 2.5 inch extruder.
  • the extruder melt temperature is 220° C.
  • Polymer melt is fed to a circular die.
  • the die temperature is set at 200° C., polymer melt is cooled by blowing air.
  • Extruded precursor has a thickness of 9.5 ⁇ m and a birefringence of 0.0160.
  • HDPE resin is extruded using a 2.5 inch extruder.
  • the extruder melt temperature is 210° C.
  • Polymer melt is fed to a circular die. Die temperature is set at 205° C., polymer melt is cooled by air.
  • Extruded precursor has a thickness of 9.5 ⁇ m and a birefringence of 0.0330.
  • Lamination roll temperature is 150° C.
  • Laminated tri-layer film is then annealed at 125° C. for 2 minutes.
  • the annealed film is then cold stretched to 20% at room temperature, and then hot stretched to 160% and relaxed to 35% at 113° C.
  • the MD stretched film has a thickness of 25.4 ⁇ m, and porosity of 39%.
  • the MD stretched film is then TD stretched 400% at 115° C. with MD relax of 30%.
  • the finished film has a thickness of 19.4 ⁇ m and porosity of 63%.
  • TD tensile strength of finished film is 350 Kg/cm 2 . See FIG. 7 .
  • PP resin and HDPE resin are extruded using a co-extrusion die to form a PP/PE/PP tri-layer film.
  • Extruder melt temperature for PP is 243° C.
  • extruder melt temperature for PE is 214° C.
  • Polymer melt is then fed to a co-extrusion die which is set at 198° C. Polymer melt is cooled by blowing air.
  • the extruded film has a thickness of 35.6 ⁇ m.
  • the extruded precursor is then annealed at 125° C. for 2 minutes. The annealed film is then cold stretched to 45% at room temperature and hot stretched to 247% and relaxed to 42% at 113° C.
  • the MD stretched film has a thickness of 21.5 ⁇ m and porosity of 29%.
  • the MD stretched film is then TD stretched 450% at 115° C. with 50% MD relax.
  • the finished film has a thickness of 16.3 ⁇ m and porosity of 59%.
  • TD tensile strength of finished film is 570 Kg/cm 2 .
  • PP resin and HDPE resin are co-extruded and MD stretched the same way as in Example 3.
  • the MD stretched film is then TD stretched 800% at 115° C. with 65% MD relax.
  • the finished film has a thickness of 17.2 ⁇ m and porosity of 49%.
  • TD tensile strength of finished film is 730 Kg/cm 2 . See FIG. 8 .
  • PP resin and PB resin are extruded using a co-extrusion die.
  • Extruder melt temperature for PP is 230° C.
  • extruder melt for PB is 206° C.
  • Polymer melt is then fed to a co-extrusion die which is set at 210° C. Polymer melt is then cooled by blowing air.
  • the extruded film has a thickness of 36.0 ⁇ m.
  • the extruded precursor is then annealed at 105° C. for 2 minutes.
  • the annealed film is then cold stretched to 20%, and then hot stretched at 105° C. to 155% and then relaxed to 35%.
  • the MD stretched film is then TD stretched 140% at 110° C. with 20% MD relax.
  • the finished film has a thickness of 14.8 ⁇ m and porosity of 42%.
  • TD tensile strength of finished film is 286 Kg/cm 2 .
  • PP resin and PE resin are extruded using a co-extrusion die to form a PP/PE/PP trilayer film.
  • Extruder melt temperature for PP is 245° C.
  • extruder melt temperature for PE is 230° C.
  • Polymer melt is then fed to a co-extrusion die which is set at 225° C. Polymer melt is cooled by blowing air.
  • the extruded film has a thickness of 27 ⁇ m and a birefringence of 0.0120.
  • the extruded precursor is then annealed at 115° C. for 2 minutes.
  • the MD stretched film has a thickness of 15 ⁇ m and porosity of 16%.
  • the MD stretched film is then TD stretched 260% at 130° C. with 50% MD relax, followed by a simultaneous MD and TD stretch of 50% and 216% in each direction at 130° C., and finally the film is held fast in the MD (100%) and allowed to relax 57.6% in the TD at a temperature of 130° C.
  • the finished film has a thickness of 7.6 ⁇ m and porosity of 52%.
  • TD tensile strength of finished film is 513 Kg/cm 2 .
  • Polypropylene and polyethylene resin(s) are extruded using a co-extrusion die to form a PP/PE/PP tri-layer film.
  • Extruder melt temperature for PP is 222° C.
  • extruder melt temperature for PE is 225° C.
  • Polymer melt is then fed to a co-extrusion die which is set at 215° C.
  • Polymer melt is cooled by blowing air.
  • the extruded film has a thickness of 40 ⁇ m and birefringence of 0.0110.
  • the extruded precursor is then annealed at 105° C. for 2 minutes.
  • the annealed film is then cold stretched to 36% at room temperature and hot stretched to 264% and relaxed to 29% at 109° C.
  • total machine direction stretch 271%.
  • the MD stretched film has a thickness of 23.8 ⁇ m and porosity of 29.6%.
  • the MD stretched film is then TD stretched 1034% at 110° C. with 75% MD relax.
  • the finished film has a thickness of 16.8 ⁇ m and porosity of 46%.
  • TD tensile strength of finished film is 1037 Kg/cm 2 .
  • the preferred membranes have or are:
  • High porosity 40%-90%.
  • Hydro-head pressure >140 psi
  • water intrusion pressure >80 psi.
  • Porometry/Aquapore Test/SEM mean flow pore diameter measured by capillary flow of at least about 0.04 micron; Uniform, round or non-slit type of pore structure, with narrow range of pore diameter. Aquapore size of at least about 0.07 micron
  • TD strength (>300 kg/cm2).
  • puncture energy Puncture strength
  • Tensile properties are tested using ASTM-882 standard using an Instron Model 4201. Shrinkage is measured at 90 C. for 60 minutes using a modified ASTM-2732-96 procedure. Mean flow pore diameter, bubble point pore diameter were measured with Capillary Flow analysis based on ASTM F316-86 standard. Hydrohead pressure was measured based on ASTM D3393-91. Water Intrusion was tested per ASTM F316-93 (Wetting fluid-water, 68.8 dynes/cm. Gas: air.)
  • a filled, microporous ultra-high molecular weight polyethylene membrane could be used as a precursor in the stretching process of the present invention.
  • the membrane of the present invention may be laminated on one or both sides to a non-woven substrate for additional durability, or it can be coated with a surfactant to make it hydrophilic.
  • the present invention may be directed to:
  • the present invention may be directed to membranes having the following properties:
  • the membrane is a hydrophobic, highly permeable, chemically and mechanically stable, high tensile strength membrane.
  • the unique pore structure may have some specific benefits.
  • the preferred laminated products may have the combination of the desired membrane moisture transport performance combined with the desired macro physical properties.
  • the preferred monolayer PP products may have excellent balance of MD and TD physical properties while also being high performance membranes as measured by the moisture transport (moisture vapor transport) and hydrohead performance.
  • the membrane may also have uncharacteristically high porosity (>60%) but still maintains the balanced physical properties when compared to more traditional membranes.
  • the membrane can be produced in union with a laminated PP nonwoven.
  • the resultant laminated product may still retain the excellent moisture vapor transport and even more improved hydrohead performance.
  • the resultant product may have physical strength properties that far exceed comparative membranes. Therefore, the product may have the added advantage of being used in more physical abusive environments without a loss of the highly desirable membrane features.
  • the membrane may have a unique pore structure and distribution or properties that may appear to make it an ideal film for the following applications:
  • some areas of improvement may include pore shapes other than slits, round shaped pores, increased transverse direction tensile strength, a balance of MD and TD physical properties, high performance related to, for example, moisture transport (or moisture vapor transport) and hydrohead pressure, reduced Gurley, high porosity with balanced physical properties, uniformity of pore structure including pore size and pore size distribution, enhanced durability, composites of such membranes with other porous materials, composites or laminates of such membranes, films or layers with porous nonwovens, coated membranes, coextruded membranes, laminated membranes, membranes having desired moisture transport, hydrohead performance, and physical strength properties, usefulness in more physically abusive environments without loss of desirable membrane features, combination of membrane moisture transport (or moisture vapor transport) performance combined with the macro physical properties, being hydrophobic, highly permeable, chemically and mechanically stable, having high tensile strength, combinations thereof
  • some areas of improvement may include pore shapes other than slits, round shaped pores, increased transverse direction tensile strength, a balance of MD and TD physical properties, uniformity of pore structure including pore size and pore size distribution, high performance related to, for example, moisture transport (moisture vapor transport) and hydrohead pressure, reduced Gurley, high porosity with balanced physical properties, enhanced durability, composites of such membranes with other porous materials, composites or laminates of such membranes with porous nonwovens, coated membranes, coextruded membranes, laminated membranes, membranes having desired moisture transport (or moisture vapor transport), hydrohead performance, and physical strength properties, useful in more physically abusive environments without loss of desirable membrane features, combination of the membrane moisture transport (moisture vapor transport) performance combined with the macro physical properties, combinations thereof, and/or the like.
  • the porous membrane of the present invention is possibly preferably a dry-stretch process, porous membrane, film, layer, or composite that is hydrophobic, highly permeable, chemically and mechanically stable, has high tensile strength, and combinations thereof.
  • the unique pore structure of at least selected embodiments of the present invention may have certain specific benefits, such as the benefits of durability, high efficiency, narrow pore size distribution, and uniform flow rate.
  • At least a selected porous mono-layer polypropylene (monolayer PP) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected monolayer PP membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PP membrane or film can be produced in union with or laminated to a porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (monolayer PP/nonwoven PP) or (nonwoven PP/monolayer PP/nonwoven PP) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PP/nonwoven PP) or (nonwoven PP/monolayer PP/nonwoven PP) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • these selected monolayer PP membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like.
  • at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polypropylene (multilayer PP) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected multilayer PP membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PP membrane or film can be produced in union with or laminated to a porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • the resultant composite, membrane or product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (multilayer PP/nonwoven PP) or (nonwoven PP/multilayer PP/nonwoven PP) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • multilayer PP membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like.
  • at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous mono-layer polyethylene (monolayer PE) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected monolayer PE membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PE membrane or film can be produced in union with or laminated to a porous polyethylene (PE) nonwoven material (nonwoven PE) or porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (monolayer PE/nonwoven PE) or (nonwoven PE/monolayer PE/nonwoven PE) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PE/nonwoven PE) or (nonwoven PE/monolayer PE/nonwoven PE) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • these selected monolayer PE membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like.
  • at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polyethylene (multilayer PE) membrane has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport and hydrohead performance.
  • This selected multilayer PE membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PE membrane or film can be produced in union with or laminated to a porous polyethylene (PE) nonwoven material (nonwoven PE) or porous polypropylene (PP) nonwoven material (nonwoven PP) on one or both sides thereof.
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product may preferably retain the excellent moisture transport and even more improved hydrohead performance. Also, this resultant composite product (multilayer PE/nonwoven PE) or (nonwoven PE/multilayer PE/nonwoven PE) may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (multilayer PE/nonwoven PE) or (nonwoven PE/multilayer PE/nonwoven PE) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features.
  • multilayer PE membrane and composite products are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like.
  • at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • At least a selected porous monolayer polymer membrane for example, a monolayer (may have one or more plies) polyolefin (PO) membrane, such as a polypropylene (PP) and/or polyethylene (PE) (including PE, PP, or PE+PP blends) monolayer membrane, has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport (or moisture vapor transport) and hydrohead performance.
  • This selected monolayer PO membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected monolayer PO membrane or film can be produced in union with or laminated to a porous nonwoven material, such as a nonwoven polymer material, for example, a PO nonwoven material (such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP) (including PE, PP, or PE +PP blends)) on one or both sides thereof.
  • a PO nonwoven material such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP) (including PE, PP, or PE +PP blends)
  • PE polyethylene
  • PP porous polypropylene
  • the resultant composite, membrane or product (monolayer PO/nonwoven PO) or (nonwoven PO/monolayer PO/nonwoven PO) may preferably retain the excellent moisture transport (or moisture vapor transport) and even more improved hydrohead performance.
  • this resultant composite product may have physical strength properties that far exceed comparative membranes. Therefore, this new resultant composite product (monolayer PO/nonwoven PO) or (nonwoven PO/monolayer PO/nonwoven PO) may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features. It is believed that these selected monolayer PO membrane and composite products (monolayer PO; monolayer PO/nonwoven PO; or, nonwoven PO/monolayer PO/nonwoven PO) are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, moisture vapor transport, hydrohead pressure, strength, and the like.
  • At least a selected porous multi-layer polymer membrane for example, a multi-layer (two or more layer) polyolefin (PO) membrane, such as a polypropylene (PP) and/or polyethylene (PE) (including PE, PP, or PE+PP blends) multilayer membrane, has excellent balance of MD and TD physical properties while also being a high performance membrane as measured by the moisture transport (or moisture vapor transport) and hydrohead performance.
  • This selected multilayer PO membrane may also have high porosity (>60%) but still maintain the balanced physical properties when compared to more traditional membranes.
  • this selected multilayer PO membrane or film can be produced in union with or laminated to a porous PO nonwoven material (such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP)) on one or both sides thereof.
  • a porous PO nonwoven material such as a porous polyethylene (PE) nonwoven material (nonwoven PE) and/or porous polypropylene (PP) nonwoven material (nonwoven PP)
  • the resultant composite, membrane or product (multilayer PO/nonwoven PO) or (nonwoven PO/multilayer PO/nonwoven PO) may preferably retain the excellent moisture transport and even more improved hydrohead performance.
  • this resultant composite product (multilayer PO/nonwoven PO) or (nonwoven PO/multilayer PO/nonwoven PO) may have physical strength properties that far exceed comparative membranes.
  • this new resultant composite product may have the added advantage of being useful in more physically abusive environments without a loss of the highly desirable membrane features. It is believed that these selected multilayer PO membrane and composite products (multilayer PO; multilayer PO/nonwoven PO; or, nonwoven PO/multilayer PO/nonwoven PO) are unique in their combination of membrane moisture transport performance combined with their macro physical properties.
  • prior membranes may have had porosity but not sufficient hydrohead pressure or performance, other membranes were too fragile, other membranes were strong but lacked other properties, or the like, while at least selected embodiments of the present invention may have, for example, desired porosity, moisture transport, hydrohead pressure, strength, and the like.
  • the pores (openings) have the following pore aspect ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), and transverse machine direction (TD)(width) by measuring, for example, one or more of the pores (preferably several of the pores to ascertain an average) in SEMs of the surface, top or front (A side) of selected membranes or composites, for example, mono-layer, bi-layer or tri-layer membranes:
  • a three-dimensional or 3D pore sphericity factor or ratio (MD/TD/ND) range could be: 1.0 to 8.0 or more; possibly preferred 1.0 to 2.5; and, most possibly preferred 1.0 to 2.0 or less (based on physical dimensions of the pore openings in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness); for example, measuring the MD and TD of one or more pores (preferably several pores to ascertain an average) in SEMs of the surface, top or front (A side), or the surface, bottom or back (B side), and measuring the ND of one or more pores (preferably several pores to ascertain an average) in SEMs of the cross-section, depth, or height (C side)(either length or width cross-section or both)(the ND dimension may be of a different pore than the MD and
  • the three-dimensional or 3D MD/TD/ND pore sphericity factor or ratio range could be: 0.25 to 8.0 or more ; possibly preferred 0.50 to 4.0 ; and, most possibly preferred 1.0 to 2.0 or less.
  • the pores (openings) have the following pore aspect ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), and transverse machine direction (TD)(width) based on measuring the pores in SEMs of the top or front (A side) of selected mono-layer and tri-layer membranes:
  • MD machine direction
  • TD transverse machine direction
  • MD/TD aspect ratio in range of 0.75 to 1.50
  • the pores (openings) have the following three dimensional or 3D pore sphericity factors or ratios (based on physical dimensions of the pore openings in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness); for example, measuring one or more pores (preferably several pores to ascertain an average) in SEMs of the surface, top or front (A side), the surface, bottom or back (B side), and the cross-section, depth, or height (C side)(either length or width cross-section or both)(the ND dimension may be of a different pore than the MD and TD dimension as it may be difficult to measure the ND, MD and TD dimension of the same pore) of selected membranes, layers or composites, for example, of selected mono-layer and tri-layer membranes:
  • the pores (openings) have the following pore sphericity factors or ratios (based on physical dimensions of the pore opening in the machine direction (MD)(length), transverse machine direction (TD)(width) and thickness direction or cross section (ND)(thickness) based on measuring the pores in SEMs of the top or front (A side) and the length and with cross-sections (C side) of selected mono-layer and tri-layer membranes:
  • a microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, preferably 0.5 to 5.0.
  • the method of making the foregoing microporous membrane includes the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction stretching including a simultaneous controlled machine direction relax.
  • a porous membrane is made by a modified dry-stretch process and has substantially round shaped pores, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, and has low Gurley as compared to prior dry-stretch membranes, has larger and more uniform mean flow pore diameters as compared to prior dry-stretch membranes, or both low Gurley and larger and more uniform mean flow pore diameters.
  • membranes made by the conventional dry-stretch process have met with excellent commercial success, in accordance with at least selected embodiments of the present invention, there is provided improved, modified or enhanced at least selected physical attributes thereof, so that they may be used in a wider spectrum of applications, may perform better for particular purposes, and/or the like.
  • porous materials for the selective passage of gases or humidity (moisture vapor) and blockage of liquid water or salt water may have met with commercial success, such as RO membranes sold by Dow Chemical, ePTFE membranes sold by W. L. Gore, BHA, and others, in accordance with at least selected embodiments of the present invention, there is provided improved, modified or enhanced porous materials so that they may be used in a wider spectrum of applications, may perform better for particular purposes, and/or the like.
  • an air-filter includes at least one porous membrane such as a microporous membrane.
  • a microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 5.0.
  • the method of making the foregoing microporous membrane includes the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction stretching including a simultaneous controlled machine direction relax.
  • a porous membrane is made by a modified dry-stretch process and has substantially round shaped pores, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0, and has low Gurley as compared to prior dry-stretch membranes, has larger and more uniform mean flow pore diameters as compared to prior dry-stretch membranes, or both low Gurley and larger and more uniform mean flow pore diameters.
  • An air-filter cartridge according to the instant invention may include at least one pleated microporous membrane, a plurality of microporous membranes, and it may further include end-plates, spacers, or the like.
  • An air-filter cartridge refers to a cartridge that may either be used in an air-filter or an air-purifier.
  • the instant application describes the instant invention in terms of an air-filter cartridge; however, the instant invention is not limited so, and it may include air-purifier cartridges as well.
  • the membrane may be pleated to provide a large filtration area in a relatively small volume. In the alternative, the membrane may have a sinusoidal pattern to provide a large filtration area in a relatively small volume.
  • the membrane may have any configuration; for example, it may have a configuration selected from the group consisting of pleated cylinder configuration, pleated flat sheet configuration, and spiral wound configuration.
  • At least one flat sheet microporous membrane is constructed and then, the membrane is folded into a pleated or an accordion folded shape thereby increasing the filtration area. Subsequently, the pleated membrane may be wound into a cylinder, and sealed via end-plates thereby forming an air-filter cartridge.
  • the air-filter cartridge may be inserted into a housing, and sealed via end caps.
  • the possibly preferred membrane is preferably made of one or more polyolefins and may be further characterized by one or more of the following parameters: thickness, porosity, average pore size, puncture strength, JIS Gurley Number, and shutdown temperature.
  • the thickness of the membrane may be less than 6.0 mils (150 microns). In another embodiment, the thickness may range from 10 microns to 150 microns. In yet another embodiment, the thickness may range from 10 microns to 50 microns.
  • the porosity of the membrane may be between 40 and 90%. In one embodiment, porosity ranges from 60-90%. In yet another embodiment, porosity ranges from 65-80%.
  • the average Aquapore size of the membrane may be between 0.04-0.20 microns. In one embodiment, the average pore size ranges from 0.04-0.120 microns. In yet another embodiment, the average pore size ranges from 0.07-0.12 microns.
  • the puncture strength may be greater than or equal to 300 gr-force/mil. Puncture strength is determined by averaging 10 measurements across the width of the final product using a Midtech Stevens LFRA texture analyzer and a needle with a 1.65 mm diameter and a 0.5 mm radius recording data at a rate of 2 mm/sec with a maximum amount of deflection of 6 mm.
  • the JIS Gurley Number (normalized to one mil thickness) may be less than 100 sec/100 cc/mil thickness. In one embodiment, the JIS Gurley number ranges from 12 to 80 sec/10 cc/mil.
  • the intrinsic viscosity (IV) of the membrane may be greater than or equal to 1.0 dl/g. In another embodiment, the IV may be greater than or equal to 5.0 dl/g. In another embodiment, the IV may preferably be greater than or equal to 3.0 dl/g.
  • the IV of the film is not the weighted average of the pre-extruded resins composing the membrane because during extrusion the polymers undergo chain scission and the molecular weight is thereby lowered.
  • Intrinsic viscosity refers to the measure of the capability of a polymer in solution to enhance the viscosity of the solution.
  • the intrinsic viscosity number is defined as the limiting value of the specific viscosity/concentration ratio at zero concentration. Thus, it becomes necessary to find the viscosity at different concentrations, and then extrapolate to zero concentration. The variation of the viscosity number with concentration depends on the type of molecule as well as the solvent. In general, the intrinsic viscosity of linear macromolecular substances is related to the weight average molecular weight or degree of polymerization. With linear macromolecules, viscosity number measurements can provide a method for the rapid determination of molecular weight when the relationship between viscosity and molecular weight has been established. IV is measured by first dissolving 0.02 g of the membrane in 100 ml of decalin at 150° C. for one hour, and then, determining its intrinsic viscosity at 135° C. via an Ubbelohd viscometer. This is according to ASTM D4020 (RSV values reported herein).
  • the shutdown temperature may be less than 260° C. (260 degrees Centigrade or Celsius). In one embodiment, the shutdown temperature may be less than 190° C. In yet another embodiment, the shutdown temperature may be less than 140° C. In still another embodiment, the shutdown temperature may be less than 130° C. In yet still another embodiment, the shutdown temperature may be less than 120° C.
  • the membrane of the present invention may be made of a single polymer or a blend of polymers or of layers of the same or different polymers or of layers of different materials bonded, laminated or coextruded together.
  • the possibly preferred polymers are polyolefins, such as polypropylene (PP) and/or polyethylene (PE).
  • PP polypropylene
  • PE polyethylene
  • the membrane may be made of one or more layers of PP and/or PE.
  • the membrane is a porous PP film or sheet.
  • the membrane is a porous PE film or sheet.
  • the membrane is a tri-layer membrane made of two exterior PP layers and an intermediate or center PE layer.
  • the membrane is a bi-layer membrane made of two PP layers, two PE layers, or one PP and one PE layer bonded together, laminated together, or coextruded together.
  • the membrane is a composite of a porous PP film or sheet and a porous material such as nonwoven glass or PP material.
  • the membrane is a porous film or sheet made of a blend of polyolefins having differing molecular weights.
  • a gas filtration media comprises a microporous membrane.
  • a gas filtration media refers to a filtration media for removal of particulates from a gas, e.g., air.
  • the gas filter media of the present invention may include an ultrahigh molecular weight polyethylene and an inorganic material.
  • the gas filter media may further include a processing oil (i.e., oil remains in the media after extraction).
  • the gas filter media may further include a thermoplastic polyolefin, conventional additives, such as stabilizers and antioxidants, and the like as is well known in the art.
  • the gas filter media may be used as a filter media for any end-use applications.
  • the gas filter media may be used as a filter media for an end-use application selected from the group consisting of particulate removal from gases, air-filtration application, elevated temperature application, baghouse application, particulate filtration in food and pharmaceuticals, particulate filtration in combustion process, particulate filtration in metals, and particulate filtration in cements.
  • Particulate removal from gases includes industries such as HVAC, HEPA and ULPA clean rooms, vacuum cleaning, respirators, cement, metals, food, pharmaceuticals, processed fluids, and combustion processes.
  • the gas filter media may stand alone as a filter media; or in the alternative, it may be joined with (e.g., laminated to or bonded to) a support material, for example, a non-woven material or a fabric.
  • a support material for example, a non-woven material or a fabric.
  • Exemplary lamination or bonding techniques include such conventional methods as, but not limited to, adhesives, welding (heat/ultrasonics) and the like.
  • the gas filter media may be flat or formed into pleats or shapes.
  • a battery separator is made from a nonwoven flat sheet material having high temperature melt integrity, a microporous membrane having low temperature shutdown properties, and an optional adhesive bonding the nonwoven flat sheet to the microporous membrane and being adapted for swelling when contacted by an electrolyte.
  • the high temperature melt integrity separator may comprise a microporous membrane and a nonwoven flat sheet that are bonded together with or without an adhesive or polymer therebetween.
  • Nonwoven flat sheet may refer to a plurality of fibers held together by various methods, e.g., thermal fusion, resin, solvent bonding, or mechanical interlocking of fibers, sometimes concurrently with their extrusion.
  • Nonwoven flat sheet includes fibrous structures made by such processes as dry, wet, or air laying, needlepunching, spunbonding, or melt blowing processes, and hydroentanglement.
  • the fibers may be directionally or randomly oriented. While nonwoven typically does not include paper, for this application, papers are included.
  • the fibers may be made of thermoplastic polymers, cellulosic, and/or ceramics.
  • Thermoplastic polymers include, but are not limited to, polystyrenes, polyvinyl chlorides, polyacrylics, polyacetals, polyamides, polycarbonates, polyesters, polyetherimides, polyimides, polyketones, polyphenylene ethers, polyphenylene sulfides, polysulfones.
  • Cellulosics include, but are not limited to, cellulose (e.g., cotton or other naturally occurring sources), regenerated cellulose (e.g., rayon), and cellulose acetate (e.g., cellulose acetate and cellulose triacetate).
  • Ceramics include, but are not limited to, glass of all types and alumina, silica, and zirconia compounds (e.g., aluminum silicate).
  • the nonwoven or the fibers of the nonwoven may be coated or surface treated to improve the functionality of the nonwoven.
  • the coating or surface treatment may be to improve the adhesiveness of the nonwoven or its fibers, to improve the high temperature melt integrity of the nonwoven, and/or to improve the wettability of the nonwoven.
  • the nonwoven and/or its fibers may be coated or surface treated with a ceramic material.
  • ceramic materials include, but are not limited to, alumina, silica, and zirconia compounds, and combinations thereof.
  • bonding of the microporous membrane to the nonwoven flat sheet should maintain a high discharge rate which may require that there will be free mobility of the ionic species of the electrolyte between the anode and the cathode.
  • the mobility of the ionic species is typically measured as electrical resistance (ER) or MacMullen number (the ratio of electrical resistance of an electrolyte-saturated porous medium to the electrical resistance of an equivalent volume of electrolyte [See: U.S. Pat. No. 4,464,238, incorporated herein by reference]).
  • ER electrical resistance
  • MacMullen number the ratio of electrical resistance of an electrolyte-saturated porous medium to the electrical resistance of an equivalent volume of electrolyte
  • the adhesive may be selected from, but is not limited to, polyvinylidene fluoride (PVDF); polyurethane; polyethylene oxide (PEO); polyacrylonitrile (PAN); polymethylacrylate (PMA); poly(methylmethacrylate) (PMMA); polyacrylamide; polyvinyl acetate; polyvinylpyrrolidone; polytetraethylene glycol diacrylate; copolymers of any the foregoing and combinations thereof.
  • PVDF polyvinylidene fluoride
  • PEO polyethylene oxide
  • PAN polyacrylonitrile
  • PMA polymethylacrylate
  • PMMA poly(methylmethacrylate)
  • polyacrylamide polyvinyl acetate
  • polyvinylpyrrolidone polytetraethylene glycol diacrylate
  • copolymers of any the foregoing and combinations thereof copolymers of any the foregoing and combinations thereof.
  • One criterion for comonomer selection is the comonomer's ability to modify the surface
  • Suitable comonomers include, but are not limited to, hexafluoropropylene, octofluoro-1-butene, octofluoroisobutene, and tetrafluoroethylene.
  • the comonomer content preferably ranges from 3 to 20% by weight, and most preferably, 7 to 15%.
  • the adhesive or swellable polymer is a copolymer of polyvinylidene fluoride.
  • the PVDF copolymer is a copolymer of polyvinylidene fluoride and hexafluoropropylene (PVDF:HFP), and, most preferably, the PVDF:HFP ratio is 91:9.
  • PVDF copolymers are commercially available from Elf Atochem, Philadelphia, Pa., USA; Solvay SA, Brussels, Belgium; and Kureha Chemical Industries, LTD, Ibaraki, Japan.
  • a preferred PVDF:HFP copolymer is KYNAR 2800 from Elf Atochem.
  • the wetting agent may be selected from materials that are compatible with (i.e., miscible with or will not phase separate from) the swellable polymer, that, in trace amounts (e.g., 10 20% of the swellable polymer), will not have a detrimental effect upon the battery chemistry (such as wetting agents that contain sulfones, sulphates, and nitrogen), and that are fluid at room temperature or have a Tg (glass transition temperature) ⁇ 50° C.
  • the wetting agent may be selected from, but is not limited to, phthalate-based esters, cyclic carbonates, polymeric carbonates, and mixtures thereof. Phthalate-based esters are selected from, but are not limited to, dibutyl phthalate (DBP).
  • Cyclic carbonates are selected from ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), and mixtures thereof.
  • Polymeric carbonates are selected from, but are not limited to; polyvinylene carbonate, and linear propylene carbonates.
  • At least selected embodiments of the present invention may provide a microporous battery separator having two portions bonded together. Each portion may consist of a co-extruded or non-coextruded layer and may be made of the same or different materials. To obtain greater puncture strength, certain embodiments may bond together two portions that are sized, when combined, to have the desired total thickness of the separator. Selected embodiments may, preferably, be made by a collapsed bubble technique; i.e.
  • the bubble which issues from the die has a first portion and a second portion (each portion representing roughly one-half of the circumference of the bubble), and then the bubble is collapsed onto itself and bonded prior to micropore formation (preferably by annealing and stretching).
  • the bubble issues from the die it is substantially oriented in the machine direction.
  • the first portion and the second portion may be oriented in substantially the same direction (angular bias between oriented portions being less than)15°.
  • the first portion and the second portion which when bonded provide the precursor for the micropore formation process (e.g. an anneal and stretch operation), may be made of materials such as polyolefins, preferably polyethylene or polypropylene, copolymers thereof, and mixtures thereof, and most preferably polyethylene and polypropylene.
  • a trilayer, shutdown battery separator may refer to a porous film for use in electrochemical cells, e.g., batteries, particularly secondary (or rechargeable) batteries, such as lithium batteries.
  • This trilayer separator may have a polypropylene-polyethylene-polypropylene construction.
  • the separator may have a thickness of less than 3 mils (about 75 microns).
  • the separator's thickness preferably ranges between 0.5 mils (about 12 microns) and 1.5 mils (about 38 microns). Most preferably, the separator's thickness is about 1 mil (about 25 microns).
  • the separator has a permeability, as measured by JIS Gurley, of less than 300 sec.
  • the separator has a puncture strength of at least 300 grams.
  • the separator has porosity in the range of 40% to 70%.
  • One method of making the trilayer, shutdown battery separator generally comprises the steps of: extruding non-porous polypropylene precursors; extruding a non-porous polyethylene precursor; forming a non-porous trilayer precursor where the polyethylene precursor is sandwiched between the polypropylene precursors; bonding the trilayer precursor; annealing the trilayer precursor; and stretching the bonded and annealed, non-porous trilayer precursor to form the porous battery separator.
  • the membrane may be a microporous sheet made from a blend of at least two ultra high molecular weight polyolefins having differing molecular weights. In one embodiment, these ultra high molecular weight polyolefins may be ultra high molecular weight polyethylene (UHMWPE). In another embodiment, the membrane is a blend of a first ultra high molecular weight polyethylene having a first molecular weight and a second ultra high molecular weight polyethylene having a second molecular weight, the first molecular weight and the second molecular weight being greater than 1 million and being different from one another.
  • UHMWPE ultra high molecular weight polyethylene
  • the membrane is a blend of a first ultra high molecular weight polyethylene having a first molecular weight, a second ultra high molecular weight polyethylene having a second molecular weight, the first molecular weight and the second molecular weight being greater than 1 million and being different from one another, and a third polyolefin having a third molecular weight, the third molecular weight being less than 1 million.
  • the membrane may have an IV greater than or equal to 6.3 dl/g. In another embodiment, the membrane may have an IV greater than or equal to 7.7 dl/g.
  • the invention is directed to biaxially oriented porous membranes, composites including biaxially oriented porous membranes, biaxially oriented microporous membranes, biaxially oriented macroporous membranes, battery separators, filtration media, humidity control media, flat sheet membranes, liquid retention media, and the like, related methods, methods of manufacture, methods of use, and the like.
  • a laminated material or fabric may incorporate a composite membrane made according to the present invention and that is wind and liquid penetration resistant, moisture vapor transmissive and air permeable.
  • the laminated fabric may also include one or more layers of textile base or shell fabric material that are laminated to the membrane by any suitable process.
  • the shell fabric may be made from any suitable material that meets performance and other criteria established for a given application.
  • “Moisture vapor transmissive” is used to describe an article that permits the passage of water vapor through the article, such as the laminated fabric or composite membrane.
  • the term “resistant to liquid penetration” is used to describe an article that is not “wet” or “wet out” by a challenge liquid, such as water, and prevents the penetration of liquid through the membrane under ambient conditions of relatively low pressure.
  • the term “resistant to wind penetration” describes the ability of an article to prevent air penetration above more than about three (3) CFM per square foot at a pressure differential across the article of 0.5′′ of water.
  • jackets, coats, or other garments or finished products incorporating the laminated fabric may permit moisture vapor transmission through the garment.
  • Moisture vapor may result from perspiration of the user, and the garment or finished product preferably permits moisture vapor transmission at a rate sufficient for the user to remain dry and comfortable during use in typical conditions.
  • the laminated fabric is also preferably resistant to liquid and wind penetration, while being air permeable.
  • an air-filter cartridge includes at least one pleated microporous membrane.
  • At least a selected microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0.
  • the method of making the foregoing microporous membrane may include the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction including a simultaneous controlled machine direction relax.
  • At least selected embodiments of the invention may be directed to biaxially oriented porous membranes, composites including biaxially oriented porous membranes, biaxially oriented microporous membranes, biaxially oriented macroporous membranes, battery separators, filtration media, humidity control media, flat sheet membranes, liquid retention media, and the like, related methods, methods of manufacture, methods of use, and the like.
  • a membrane comprising:
  • a porosity of about 40% to 90%, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of about 0.5 to 5.0, a Gurley of less than about 100, a mean flow pore diameter of at least about 0.04 microns, an Aquapore size of at least about 0.07 microns, and a hydro-head pressure greater than about 140 psi.
  • said biaxially stretching of said nonporous precursor includes the machine direction stretching, an additional transverse direction stretching with simultaneous machine direction stretching, and a transverse direction relax.
  • the above membrane with said porous polymer film further having a thickness of at least about 8 microns, a transverse direction tensile strength of at least about 300 kgf/cm2, a standard deviation of mean flow pore diameter of less than about 0.025, a water intrusion pressure of at least about 80 psi, and a WVTR of at least about 8,000 g/m 2 -day.
  • said nonporous precursor is one of a blown film and a slot die film.
  • nonporous precursor is a single layer precursor formed by at least one of single layer extrusion and multilayer extrusion.
  • nonporous precursor is a multilayer precursor formed by at least one of coextrusion and lamination.
  • porous polymer film comprises one of polypropylene, polyethylene, blends thereof, and combinations thereof.
  • porous polymer film uses polyolefin resins which have a melt flow index (MFI) of about 0.01 to 10.0 and a polymer crystallinity of at least about 45%.
  • MFI melt flow index
  • said membrane further includes at least one nonwoven, woven, or knit layer bonded to at least one side of said porous polymer film.
  • the above membrane wherein said membrane has substantially round shaped pores, a porosity of about 40% to 90%, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of about 0.5 to 5.0, a Gurley of less than about 100, a mean flow pore diameter of at least about 0.04 microns, an Aquapore size of at least about 0.07 microns, and a hydro-head pressure greater than about 140 psi.
  • polymer being selected from the group consisting of polyolefins, fluorocarbons, polyamides, polyesters, polyacetals (or polyoxymethylenes), polysulfides, polyphenyl sulfide, polyvinyl alcohols, co-polymers thereof, blends thereof, and combinations thereof.
  • the above membrane with said porous polymer film further having a porosity of about 65% to 90%, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of about 1.0 to 5.0, a Gurley of less than about 20, a mean flow pore diameter of at least about 0.05 microns, an Aquapore size of at least about 0.08 microns, and a hydro-head pressure greater than about 145 psi.
  • substantially round shaped pores have at least one of an aspect ratio in the range of about 0.75 to 1.25 and a sphericity factor in the range of about 0.25 to 8.0.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of a plurality of separate, superimposed, layers or plies of nonporous precursor, wherein none of the plies are bonded together during the stretching process.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of at least three separate, superimposed, layers of nonporous precursor.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of at least eight separate, superimposed, layers of nonporous precursor.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of at least sixteen separate, superimposed, layers of nonporous precursor.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of a plurality of bonded, superimposed, layers or plies of nonporous precursor, wherein all of the plies are bonded together during the stretching process.
  • said biaxially stretching step of said dry-stretch process includes the simultaneous biaxial stretching of a plurality of separate, superimposed, layers or plies of nonporous precursor, and a plurality of bonded, superimposed, layers or plies of nonporous precursor, wherein some of the plies are bonded together during the stretching process.
  • said extruding step is a dry extrusion process, using an extruder having at least one of a slot die and an annular die.
  • a battery separator comprising:
  • a porosity of about 40% to 70%, a ratio of machine direction tensile strength to transverse direction tensile strength in the range of about 0.5 to 5.0, a Gurley of less than about 300, a mean flow pore diameter of at least about 0.01 microns, and an Aquapore size of at least about 0.04 microns.
  • said at least one layer of porous polymer film further having a thickness of at least about 8 microns, a transverse direction tensile strength of at least about 300 kgf/cm2, a standard deviation of mean flow pore diameter of less than about 0.025.
  • nonporous precursor is formed by at least one of single layer extrusion and multilayer extrusion.
  • nonporous precursor is a multilayer precursor formed by at least one of coextrusion and lamination.
  • polymer being selected from the group consisting of polyolefins, fluorocarbons, polyamides, polyesters, polyacetals (or polyoxymethylenes), polysulfides, polyphenyl sulfide, polyvinyl alcohols, co-polymers thereof, blends thereof, and combinations thereof.
  • substantially round shaped pores have at least one of an aspect ratio in the range of about 0.75 to 1.25 and a sphericity factor in the range of about 0.25 to 8.0.
  • a porous membrane comprising:
  • a porosity of at least about 40% a ratio of machine direction tensile strength to transverse direction tensile strength in the range of about 0.5 to 5.0, a Gurley of less than about 300, a mean flow pore diameter of at least about 0.01 microns, and an Aquapore size of at least about 0.04 microns.
  • the improvement comprising the above membrane.
  • the improvement comprising the above membrane.
  • the improvement comprising the above membrane.
  • a method of making a microporous membrane comprising the steps of:
  • the polymer being selected from the group consisting of polyolefins, fluorocarbons, polyamides, polyesters, polyacetals (or polyoxymethylenes), polysulfides, polyvinyl alcohols, co-polymers thereof, and combinations thereof.
  • a membrane comprising:
  • microporous polymer film having a porosity in the range of 20-80%.
  • a battery separator comprising the above membrane.
  • a multi-layered membrane structure comprising the above membrane.
  • An air-filter cartridge comprising the above membrane.
  • a gas filtration media comprising the above membrane.
  • a battery separator comprising: a nonwoven flat sheet having a high temperature melt integrity; and the above membrane.
  • a battery made with the above separator A battery made with the above separator.
  • a porous membrane comprising at least one of: pore shapes other than slits, round shaped pores, pores like those shown in one of FIGS. 6-8 and 13 - 54 , pores like those shown in one of FIGS. 13-50 , pores like those shown in one of FIGS.
  • At least a selected microporous membrane is made by a dry-stretch process and has substantially round shaped pores and a ratio of machine direction tensile strength to transverse direction tensile strength in the range of 0.5 to 6.0.
  • the method of making the foregoing microporous membrane may include the steps of: extruding a polymer into a nonporous precursor, and biaxially stretching the nonporous precursor, the biaxial stretching including a machine direction stretching and a transverse direction stretching, the transverse direction including a simultaneous controlled machine direction relax.
  • At least selected embodiments of the invention may be directed to biaxially oriented porous membranes, composites including biaxially oriented porous membranes, biaxially oriented microporous membranes, biaxially oriented macroporous membranes, battery separators, filtration media, humidity control media, flat sheet membranes, liquid retention media, and the like, related methods, methods of manufacture, methods of use, and the like.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Polymers & Plastics (AREA)
  • Medicinal Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Dispersion Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Materials Engineering (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Separation Using Semi-Permeable Membranes (AREA)
  • Laminated Bodies (AREA)
  • Cell Separators (AREA)
  • Shaping By String And By Release Of Stress In Plastics And The Like (AREA)
  • Molding Of Porous Articles (AREA)
US13/044,708 2010-03-12 2011-03-10 Biaxially oriented porous membranes, composites, and methods of manufacture and use Abandoned US20110223486A1 (en)

Priority Applications (18)

Application Number Priority Date Filing Date Title
US13/044,708 US20110223486A1 (en) 2010-03-12 2011-03-10 Biaxially oriented porous membranes, composites, and methods of manufacture and use
CN2011800231871A CN102892534A (zh) 2010-03-12 2011-03-11 双轴取向的多孔膜、复合材料以及制造和使用方法
KR1020247002330A KR20240014616A (ko) 2010-03-12 2011-03-11 이축배향 다공막, 복합체, 및 제조방법 및 용도
JP2012557266A JP2013527260A (ja) 2010-03-12 2011-03-11 二軸配向細孔性膜、合成物、ならびに製造および使用の方法
PCT/US2011/028019 WO2011112885A1 (en) 2010-03-12 2011-03-11 Biaxially oriented porous membranes, composites, and methods of manufacture and use
KR1020187026494A KR102206794B1 (ko) 2010-03-12 2011-03-11 이축배향 다공막, 복합체, 및 제조방법 및 용도
KR1020177025941A KR101900241B1 (ko) 2010-03-12 2011-03-11 이축배향 다공막, 복합체, 및 제조방법 및 용도
CN201710665948.2A CN107362693A (zh) 2010-03-12 2011-03-11 双轴取向的多孔膜、复合材料以及制造和使用方法
TW106139335A TWI635644B (zh) 2010-03-12 2011-03-11 多孔膜以及包含其之物件及電池隔板
KR1020127023376A KR20130039713A (ko) 2010-03-12 2011-03-11 이축배향 다공막, 복합체, 및 제조방법 및 용도
KR1020227007744A KR102629227B1 (ko) 2010-03-12 2011-03-11 이축배향 다공막
KR1020217001682A KR102373866B1 (ko) 2010-03-12 2011-03-11 이축배향 다공막, 복합체, 및 제조방법 및 용도
EP11754128.4A EP2544841B2 (en) 2010-03-12 2011-03-11 Biaxially oriented porous membranes, composites, and methods of manufacture and use
JP2016022936A JP2016166334A (ja) 2010-03-12 2016-02-09 二軸配向細孔性膜、合成物、ならびに製造および使用の方法
US15/582,866 US20170266865A1 (en) 2010-03-12 2017-05-01 Biaxially oriented porous membranes, composites, and methods of manufacture and use
JP2017225491A JP6773630B2 (ja) 2010-03-12 2017-11-24 二軸配向細孔性膜、合成物、ならびに製造および使用の方法
JP2020166927A JP2021021072A (ja) 2010-03-12 2020-10-01 二軸配向細孔性膜、合成物、ならびに製造および使用の方法
JP2022191517A JP2023021167A (ja) 2010-03-12 2022-11-30 二軸配向細孔性膜、合成物、ならびに製造および使用の方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US31315210P 2010-03-12 2010-03-12
US13/044,708 US20110223486A1 (en) 2010-03-12 2011-03-10 Biaxially oriented porous membranes, composites, and methods of manufacture and use

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/582,866 Division US20170266865A1 (en) 2010-03-12 2017-05-01 Biaxially oriented porous membranes, composites, and methods of manufacture and use

Publications (1)

Publication Number Publication Date
US20110223486A1 true US20110223486A1 (en) 2011-09-15

Family

ID=44560305

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/044,708 Abandoned US20110223486A1 (en) 2010-03-12 2011-03-10 Biaxially oriented porous membranes, composites, and methods of manufacture and use
US15/582,866 Pending US20170266865A1 (en) 2010-03-12 2017-05-01 Biaxially oriented porous membranes, composites, and methods of manufacture and use

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/582,866 Pending US20170266865A1 (en) 2010-03-12 2017-05-01 Biaxially oriented porous membranes, composites, and methods of manufacture and use

Country Status (7)

Country Link
US (2) US20110223486A1 (ko)
EP (1) EP2544841B2 (ko)
JP (5) JP2013527260A (ko)
KR (6) KR102629227B1 (ko)
CN (2) CN107362693A (ko)
TW (1) TWI635644B (ko)
WO (1) WO2011112885A1 (ko)

Cited By (68)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100313753A1 (en) * 2008-02-22 2010-12-16 Lydall Solutech B.V. Polyethylene membrane and method of its production
CN102751460A (zh) * 2012-05-23 2012-10-24 杭州福膜新材料科技有限公司 耐高温复合隔离膜及其制备方法
US20130112621A1 (en) * 2011-11-03 2013-05-09 Lei Zheng Water filtration article and related methods
US20130299060A1 (en) * 2012-05-11 2013-11-14 Entire Technology Co., Ltd. Manufacturing method of porous composite film
US20140068927A1 (en) * 2012-09-12 2014-03-13 GM Global Technology Operations LLC Reverse Osmosis Membranes Made with PFSA Ionomer and ePTFE
US20140127492A1 (en) * 2012-11-06 2014-05-08 Celgard, Llc Copolymer membranes, fibers, products and methods
WO2014077499A1 (ko) * 2012-11-14 2014-05-22 제일모직주식회사 분리막의 제조 방법과 그 분리막 및 이를 이용한 전지
WO2014091159A1 (fr) 2012-12-13 2014-06-19 Arkema France Formulation d'une membrane fluoree poreuse mise en œuvre par un procede d'etirage
US20140217992A1 (en) * 2013-02-05 2014-08-07 Hrl Laboratories, Llc Separators for lithium-sulfur batteries
US20150010798A1 (en) * 2012-02-28 2015-01-08 Sei Corporation Electrolyte holder for lithium secondary battery and lithium secondary battery
US20150050545A1 (en) * 2012-03-28 2015-02-19 Asahi Kasei E-Materials Corporation Porous membrane and multilayer porous membrane
WO2015057929A1 (en) * 2013-10-18 2015-04-23 Celgard, Llc Porous membrane wipes and methods of manufacture and use
CN104835930A (zh) * 2015-03-24 2015-08-12 中国科学技术大学 一种聚烯烃微孔隔膜的制备方法
WO2015143106A1 (en) * 2014-03-19 2015-09-24 Celgard, Llc Embossed microporous membrane wipes and methods of manufacture and use thereof
WO2015143425A1 (en) * 2014-03-21 2015-09-24 Celgard, Llc Seam tape and methods of manufacture and use thereof
US20150364764A1 (en) * 2013-02-28 2015-12-17 Sanyo Electric Co., Ltd Nonaqueous electrolyte secondary battery
WO2016008648A1 (de) * 2014-07-15 2016-01-21 Robert Bosch Gmbh Separator mit kraftschlüssig eingespannten partikeln
WO2016085970A1 (en) 2014-11-26 2016-06-02 Celgard, Llc Improved multilayer microporous separators for lithium ion secondary batteries and related methods
US20160185519A1 (en) * 2013-08-14 2016-06-30 Merck Patent Gmbh High pressure extraction capsule
CN105922605A (zh) * 2016-05-12 2016-09-07 武汉纺织大学 一种双向拉伸的聚丙烯纤维多孔膜的制备方法
CN105926168A (zh) * 2016-05-12 2016-09-07 武汉纺织大学 一种双向拉伸的聚苯硫醚纤维多孔膜的制备方法
CN106003747A (zh) * 2016-05-12 2016-10-12 武汉纺织大学 一种双向拉伸的聚酯纤维多孔膜的制备方法
US20160329541A1 (en) * 2015-05-08 2016-11-10 Celgard, Llc Coated or treated microporous battery separators, rechargeable lithium batteries, systems, and related methods of manufacture and/or use
WO2016196870A1 (en) * 2015-06-03 2016-12-08 Celgard, Llc Improved low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
WO2017083633A1 (en) * 2015-11-11 2017-05-18 Celgard, Llc Microlayer membranes, improved battery separators, and methods of manufacture and use
WO2017132439A1 (en) 2016-01-29 2017-08-03 Celgard, Llc Improved separators, battereies systems, vehicles, and related methods
CN107079207A (zh) * 2014-10-16 2017-08-18 日东电工株式会社 透声膜和具备该透声膜的透声膜构件、以及传声器及电子设备
CN107078257A (zh) * 2014-10-17 2017-08-18 丰田自动车株式会社 用于电池的分隔器、层压分隔器、锂离子二次电池和电池组
US9810439B2 (en) 2011-09-02 2017-11-07 Nortek Air Solutions Canada, Inc. Energy exchange system for conditioning air in an enclosed structure
US9816760B2 (en) 2012-08-24 2017-11-14 Nortek Air Solutions Canada, Inc. Liquid panel assembly
WO2018033921A1 (en) * 2016-08-18 2018-02-22 Advanced Mem-Tech Ltd. Improved filtration membrane
US9909768B2 (en) 2013-03-13 2018-03-06 Nortek Air Solutions Canada, Inc. Variable desiccant control energy exchange system and method
US9920960B2 (en) 2011-01-19 2018-03-20 Nortek Air Solutions Canada, Inc. Heat pump system having a pre-processing module
US10030157B2 (en) 2014-04-15 2018-07-24 Celgard, Llc Electrically conductive, transparent, translucent, and/or reflective materials
US10069126B2 (en) 2011-07-18 2018-09-04 Celgard, Llc Surface modified polymeric materials, modified functionalized polymers, functional polymers, and methods
US20180254453A1 (en) * 2017-03-03 2018-09-06 Sumitomo Chemical Company, Limited Nonaqueous electrolyte secondary battery separator
US10139116B2 (en) 2014-06-16 2018-11-27 Core Energy Recovery Solutions Inc. Blended membranes for water vapor transport and methods for preparing same
US10184674B2 (en) * 2015-09-16 2019-01-22 Kabushiki Kaisha Toshiba Vapor separator and dehumidifier using the same
US10196495B2 (en) 2014-05-13 2019-02-05 Celgard, Llc Functionalized porous membranes and methods of manufacture and use
US10302317B2 (en) 2010-06-24 2019-05-28 Nortek Air Solutions Canada, Inc. Liquid-to-air membrane energy exchanger
US10352628B2 (en) 2013-03-14 2019-07-16 Nortek Air Solutions Canada, Inc. Membrane-integrated energy exchange assembly
WO2019169210A1 (en) * 2018-03-02 2019-09-06 Celgard, Llc Microporous membranes, battery separator, and methods for making and using the same
US10569230B2 (en) 2015-05-30 2020-02-25 Core Energy Recovery Solutions Inc. Supported water vapor transport membrane comprising polyethylene oxide copolymer
US10584884B2 (en) 2013-03-15 2020-03-10 Nortek Air Solutions Canada, Inc. Control system and method for a liquid desiccant air delivery system
WO2019126602A3 (en) * 2017-12-22 2020-03-19 Braskem America, Inc. Method of 3d printing, and resulting article having porous structure
US10634392B2 (en) 2013-03-13 2020-04-28 Nortek Air Solutions Canada, Inc. Heat pump defrosting system and method
WO2020142708A1 (en) * 2019-01-04 2020-07-09 Celgard, Llc Polyimide coated separator for lithium batteries or capacitor
US10712024B2 (en) 2014-08-19 2020-07-14 Nortek Air Solutions Canada, Inc. Liquid to air membrane energy exchangers
US10782045B2 (en) 2015-05-15 2020-09-22 Nortek Air Solutions Canada, Inc. Systems and methods for managing conditions in enclosed space
CN111697189A (zh) * 2020-06-28 2020-09-22 佛山市金辉高科光电材料股份有限公司 聚烯烃微孔基膜及其制备方法、隔膜和电池
US20200303704A1 (en) * 2017-11-03 2020-09-24 Celgard, Llc Improved microporous membranes, battery separators, batteries, and devices having the same
US10804516B2 (en) 2014-03-19 2020-10-13 Celgard, Llc Embossed microporous membrane battery separator materials and methods of manufacture and use thereof
US10808951B2 (en) 2015-05-15 2020-10-20 Nortek Air Solutions Canada, Inc. Systems and methods for providing cooling to a heat load
EP3539174A4 (en) * 2016-11-11 2020-10-28 Celgard LLC IMPROVED MICROLAYER MEMBRANES, IMPROVED BATTERY SEPARATORS AND RELATED PROCESSES
EP3646399A4 (en) * 2017-05-26 2021-01-27 Celgard LLC NEW OR IMPROVED MICROPOROUS MEMBRANES, BATTERY SEPARATORS, COATED SEPARATORS, BATTERIES AND RELATED PROCESSES
CN112275145A (zh) * 2020-09-16 2021-01-29 浙江赛迅环保科技有限公司 一种口罩用聚四氟乙烯覆膜的制备方法
CN112470331A (zh) * 2018-05-10 2021-03-09 赛尔格有限责任公司 电池隔板、带涂层的电池隔板、电池及相关方法
US10962252B2 (en) 2015-06-26 2021-03-30 Nortek Air Solutions Canada, Inc. Three-fluid liquid to air membrane energy exchanger
EP3674354A4 (en) * 2017-08-25 2021-07-28 Beijing Normal University COMPOSITE POROUS MEMBRANE AND PROCESSES FOR PREPARATION AND USE
US11092349B2 (en) 2015-05-15 2021-08-17 Nortek Air Solutions Canada, Inc. Systems and methods for providing cooling to a heat load
US20210291451A1 (en) * 2016-01-13 2021-09-23 Fujian Institute Of Research On The Structure Of Matter, Chinese Academy Of Science Semi-permeable element, use thereof and preparation method therefor and 3d printing device
US11325074B2 (en) * 2018-05-04 2022-05-10 Shanghai Energy New Materials Technology Co., Ltd. Porous membrane for water treatment and method for preparing the same
CN114474905A (zh) * 2020-11-13 2022-05-13 贝里国际公司 透气阻隔层合体
US20220192415A1 (en) * 2018-04-23 2022-06-23 2266170 Ontario Inc. Capsules And Other Containers With Optimized Recycling Attributes And Methods For Making Same
US11389772B2 (en) 2017-12-18 2022-07-19 The Hong Kong University Of Science And Technology Method for synthesis of flexible multifunctional high-voidage ultrathin PE membranes
US11408681B2 (en) 2013-03-15 2022-08-09 Nortek Air Solations Canada, Iac. Evaporative cooling system with liquid-to-air membrane energy exchanger
US11420162B2 (en) 2017-11-28 2022-08-23 Lg Chem, Ltd. Method for preparing porous membrane of fluorine-based resin
US11892193B2 (en) 2017-04-18 2024-02-06 Nortek Air Solutions Canada, Inc. Desiccant enhanced evaporative cooling systems and methods

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110223486A1 (en) * 2010-03-12 2011-09-15 Xiaomin Zhang Biaxially oriented porous membranes, composites, and methods of manufacture and use
CN103964074A (zh) * 2013-02-01 2014-08-06 成都与康科技有限公司 具有呼吸功能的食品包装容器
JP2014169405A (ja) * 2013-03-04 2014-09-18 Sekisui Chem Co Ltd プロピレン系樹脂微孔フィルムの製造方法及びプロピレン系樹脂微孔フィルム
CN107210406B (zh) * 2014-11-26 2020-11-10 赛尔格有限责任公司 用于锂离子可充电电池的改进的微孔膜隔板及相关方法
ES2730017T3 (es) * 2015-02-24 2019-11-07 Gore W L & Ass Gmbh Proceso para la formación de un conjunto de película porosa
EP3350854B1 (en) * 2015-09-18 2022-10-19 Celgard, LLC Improved membranes, calendered microporous membranes, battery separators and related methods
CN106953054B (zh) * 2016-01-06 2020-02-07 中国科学院化学研究所 一种长碳链聚酰胺多孔膜及其制备方法与用途
KR102576219B1 (ko) * 2016-09-12 2023-09-07 에스케이이노베이션 주식회사 역삼투막 및 이의 제조방법
KR102553022B1 (ko) * 2016-11-07 2023-07-07 셀가드 엘엘씨 개선된 전지 성능을 위한 첨가제, 개선된 첨가제 함유 멤브레인, 개선된 전지 분리기, 개선된 전지, 및 관련 방법
CN106584878A (zh) * 2016-11-23 2017-04-26 广东工业大学 一种含有片晶结构的聚苯硫醚微孔膜及其制备方法
WO2018109747A1 (en) * 2016-12-17 2018-06-21 Reliance Industries Limited A barrier film and process of preparation thereof
KR102119477B1 (ko) * 2017-07-21 2020-06-05 주식회사 아모그린텍 필터여재, 이의 제조방법 및 이를 포함하는 필터유닛
KR102109454B1 (ko) * 2017-07-21 2020-05-12 주식회사 아모그린텍 필터여재, 이의 제조방법 및 이를 포함하는 필터유닛
WO2019107746A1 (ko) * 2017-11-28 2019-06-06 주식회사 엘지화학 불소계 수지 다공성 막의 제조방법
JP6805371B2 (ja) * 2018-07-25 2020-12-23 帝人株式会社 液体フィルター用基材
CN109280321B (zh) * 2018-08-07 2020-01-21 唐山开滦化工科技有限公司 一种聚甲醛薄膜及其制备方法
CN109316974B (zh) * 2018-11-23 2021-04-30 浙江福斯特新材料研究院有限公司 一种半透膜支撑材料
KR102382246B1 (ko) * 2018-12-07 2022-04-08 시바우라 기카이 가부시키가이샤 세퍼레이터 필름 제조 장치 및 세퍼레이터 필름의 제조 방법
JP6974413B2 (ja) * 2018-12-07 2021-12-01 芝浦機械株式会社 セパレータフィルム製造装置及びセパレータフィルムの製造方法
CN111029661B (zh) * 2019-12-26 2021-01-01 成都新柯力化工科技有限公司 一种锂电池超薄柔性无机固态电解质及制备方法和应用
CN111634021B (zh) * 2020-06-22 2022-05-13 中国科学技术大学 一种医用一次性防护服
CN112549475B (zh) * 2020-11-24 2022-04-19 中国科学技术大学 一种制备液晶高分子薄膜的方法及制备装置
CN112531288B (zh) * 2020-12-07 2022-11-08 安徽南都华拓新能源科技有限公司 阻燃型纳米纤维锂电池隔膜及其制备方法
CN113276384A (zh) * 2021-04-28 2021-08-20 河北金力新能源科技股份有限公司 一种新风交换膜及其制备方法和应用
KR20240054308A (ko) * 2021-08-30 2024-04-25 더블유. 엘. 고어 앤드 어소시에이트스, 인코포레이티드 폴리에틸렌 멤브레인 음향 조립체
CN114130221B (zh) * 2021-12-01 2022-11-18 山东融星膜材料科技有限公司 耐高压聚丙烯中空纤维脱氧膜及其制备方法和应用
CN114437647B (zh) * 2021-12-15 2023-01-31 清华大学 柔性耐磨超疏水材料及其制备方法和应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4464238A (en) * 1983-05-09 1984-08-07 The Dow Chemical Company Porous separators for electrolytic processes
US6057061A (en) * 1997-11-13 2000-05-02 Celgard Inc. Ethylene-vinyl alcohol copolymer battery separator
US6080507A (en) * 1998-04-13 2000-06-27 Celgard Inc. Trilayer battery separator
US6602593B1 (en) * 1999-08-30 2003-08-05 Celgard Inc. Battery separators with reduced splitting propensity
US6811643B2 (en) * 2002-02-22 2004-11-02 Clopay Plastic Products Company, Inc. Film, laminated sheet and methods of making same
US20070196638A1 (en) * 2006-02-21 2007-08-23 Xiangyun Wei Biaxially oriented microporous membrane
US20080118827A1 (en) * 2006-11-17 2008-05-22 Call Ronald W Co-extruded, multi-layered battery separator

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4138459A (en) 1975-09-08 1979-02-06 Celanese Corporation Process for preparing a microporous polymer film
DE2853398C3 (de) 1978-12-11 1981-09-17 Unilever N.V., Rotterdam Verfahren und Vorrichtung zum simultanen biaxialen Recken einer Folienbahn aus Kunststoff
US4257997A (en) 1979-06-01 1981-03-24 Celanese Corporation Solvent stretch process for preparing a microporous film
US4298666A (en) 1980-02-27 1981-11-03 Celanese Corporation Coated open-celled microporous membranes
US5013439A (en) 1988-05-12 1991-05-07 Hoechst Celanese Corporation Microporous membranes having increased pore densities and process for making the same
US5051225A (en) 1988-06-22 1991-09-24 E. I. Du Pont De Nemours And Company Method of drawing plastic film in a tenter frame
CA2007160C (en) 1989-01-09 1997-08-19 Gunilla E. Gillberg-Laforce Microporus membrane from cold-rolled precursor films
US5565281A (en) 1994-12-02 1996-10-15 Hoechst Celanese Corporation Shutdown, bilayer battery separator
US6368742B2 (en) 1998-06-26 2002-04-09 Celgard, Inc. Polypropylene microporous membrane for battery separator
JP4158004B2 (ja) 2000-06-02 2008-10-01 新日本理化株式会社 多孔性ポリプロピレンフィルム、その製造方法及び該フィルムを用いた吸収性物品
US20020119300A1 (en) 2000-12-22 2002-08-29 Taylor Jack D. Breathable and elastic polyurethane films and laminates containing same
JP2006028495A (ja) * 2004-06-18 2006-02-02 Toray Ind Inc 微多孔ポリプロピレンフィルムおよびそれを用いてなる透湿防水布。
US7604687B2 (en) * 2005-06-03 2009-10-20 Daramic Llc Gas filtration media
CN1887581A (zh) * 2005-06-30 2007-01-03 佛山塑料集团股份有限公司 聚烯烃微多孔膜的制作方法
KR20060001849A (ko) * 2005-11-15 2006-01-06 (주)인터포어 신선 식품 또는 발효 식품 포장용 필름 및 포장용기
US20070238017A1 (en) * 2006-04-07 2007-10-11 Celgard Llc Multilayer separator exhibiting improved strength and stability
CN101724168B (zh) * 2009-11-16 2011-09-21 深圳市星源材质科技股份有限公司 一种聚烯烃微孔膜制备方法
US20110223486A1 (en) * 2010-03-12 2011-09-15 Xiaomin Zhang Biaxially oriented porous membranes, composites, and methods of manufacture and use

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4464238A (en) * 1983-05-09 1984-08-07 The Dow Chemical Company Porous separators for electrolytic processes
US6057061A (en) * 1997-11-13 2000-05-02 Celgard Inc. Ethylene-vinyl alcohol copolymer battery separator
US6080507A (en) * 1998-04-13 2000-06-27 Celgard Inc. Trilayer battery separator
US6602593B1 (en) * 1999-08-30 2003-08-05 Celgard Inc. Battery separators with reduced splitting propensity
US6811643B2 (en) * 2002-02-22 2004-11-02 Clopay Plastic Products Company, Inc. Film, laminated sheet and methods of making same
US20070196638A1 (en) * 2006-02-21 2007-08-23 Xiangyun Wei Biaxially oriented microporous membrane
US20080118827A1 (en) * 2006-11-17 2008-05-22 Call Ronald W Co-extruded, multi-layered battery separator

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Equistar. "Factors Affecting the Permeability of PE Blown Films" by Equistar p.6 "Conclusions". 1997. *

Cited By (135)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8465565B2 (en) * 2008-02-22 2013-06-18 Lydall Solutech B.V. Polyethylene membrane and method of its production
US20100313753A1 (en) * 2008-02-22 2010-12-16 Lydall Solutech B.V. Polyethylene membrane and method of its production
US10302317B2 (en) 2010-06-24 2019-05-28 Nortek Air Solutions Canada, Inc. Liquid-to-air membrane energy exchanger
US9920960B2 (en) 2011-01-19 2018-03-20 Nortek Air Solutions Canada, Inc. Heat pump system having a pre-processing module
US10665839B2 (en) 2011-07-18 2020-05-26 Celgard, Llc Surface modified polymeric materials, modified functionalized polymers, functional polymers, and methods
US10069126B2 (en) 2011-07-18 2018-09-04 Celgard, Llc Surface modified polymeric materials, modified functionalized polymers, functional polymers, and methods
US11761645B2 (en) 2011-09-02 2023-09-19 Nortek Air Solutions Canada, Inc. Energy exchange system for conditioning air in an enclosed structure
US9810439B2 (en) 2011-09-02 2017-11-07 Nortek Air Solutions Canada, Inc. Energy exchange system for conditioning air in an enclosed structure
US10928082B2 (en) 2011-09-02 2021-02-23 Nortek Air Solutions Canada, Inc. Energy exchange system for conditioning air in an enclosed structure
US20130112621A1 (en) * 2011-11-03 2013-05-09 Lei Zheng Water filtration article and related methods
US10230089B2 (en) * 2012-02-28 2019-03-12 Sei Corporation Electrolyte holder for lithium secondary battery and lithium secondary battery
EP2822086B1 (en) * 2012-02-28 2018-09-05 Sei Corporation Liquid holding body for lithium secondary batteries, and lithium secondary battery
US20150010798A1 (en) * 2012-02-28 2015-01-08 Sei Corporation Electrolyte holder for lithium secondary battery and lithium secondary battery
US9911959B2 (en) 2012-03-28 2018-03-06 Asahi Kasei E-Materials Corporation Porous membrane and multilayer porous membrane
US9911960B2 (en) 2012-03-28 2018-03-06 Asahi Kasei E-Materials Corporation Porous membrane and multilayer porous membrane
US20150050545A1 (en) * 2012-03-28 2015-02-19 Asahi Kasei E-Materials Corporation Porous membrane and multilayer porous membrane
US9627672B2 (en) * 2012-03-28 2017-04-18 Asahi Kasei E-Materials Corporation Separator for nonaqueous electrolyte batteries containing a porous membrane
US8834656B2 (en) * 2012-05-11 2014-09-16 Entire Technology Co., Ltd. Manufacturing method of porous composite film
US20130299060A1 (en) * 2012-05-11 2013-11-14 Entire Technology Co., Ltd. Manufacturing method of porous composite film
CN102751460A (zh) * 2012-05-23 2012-10-24 杭州福膜新材料科技有限公司 耐高温复合隔离膜及其制备方法
US11035618B2 (en) 2012-08-24 2021-06-15 Nortek Air Solutions Canada, Inc. Liquid panel assembly
US9816760B2 (en) 2012-08-24 2017-11-14 Nortek Air Solutions Canada, Inc. Liquid panel assembly
US11732972B2 (en) 2012-08-24 2023-08-22 Nortek Air Solutions Canada, Inc. Liquid panel assembly
US20140068927A1 (en) * 2012-09-12 2014-03-13 GM Global Technology Operations LLC Reverse Osmosis Membranes Made with PFSA Ionomer and ePTFE
US10020526B2 (en) * 2012-09-12 2018-07-10 GM Global Technology Operations LLC Reverse osmosis membranes made with PFSA ionomer and ePTFE
US10544521B2 (en) 2012-11-06 2020-01-28 Celgard, Llc Copolymer membranes, fibers, products and methods
US20140127492A1 (en) * 2012-11-06 2014-05-08 Celgard, Llc Copolymer membranes, fibers, products and methods
CN104884693A (zh) * 2012-11-06 2015-09-02 赛尔格有限责任公司 共聚物膜、纤维、产品和方法
US9783914B2 (en) * 2012-11-06 2017-10-10 Celgard, Llc Copolymer membranes, fibers, products and methods
US20200157707A1 (en) * 2012-11-06 2020-05-21 Celgard, Llc Copolymer membranes, fibers, products and methods
CN107385536A (zh) * 2012-11-06 2017-11-24 赛尔格有限责任公司 共聚物膜、纤维、产品和方法
WO2014077499A1 (ko) * 2012-11-14 2014-05-22 제일모직주식회사 분리막의 제조 방법과 그 분리막 및 이를 이용한 전지
CN104871342A (zh) * 2012-11-14 2015-08-26 三星Sdi株式会社 生产隔离膜的方法、所述隔离膜及使用其的电池
WO2014091159A1 (fr) 2012-12-13 2014-06-19 Arkema France Formulation d'une membrane fluoree poreuse mise en œuvre par un procede d'etirage
US20140217992A1 (en) * 2013-02-05 2014-08-07 Hrl Laboratories, Llc Separators for lithium-sulfur batteries
US10164231B2 (en) * 2013-02-05 2018-12-25 Hrl Laboratories, Llc Separators for lithium-sulfur batteries
US9947928B2 (en) * 2013-02-28 2018-04-17 Sanyo Electric Co., Ltd. Nonaqueous electrolyte secondary battery
US20150364764A1 (en) * 2013-02-28 2015-12-17 Sanyo Electric Co., Ltd Nonaqueous electrolyte secondary battery
US9909768B2 (en) 2013-03-13 2018-03-06 Nortek Air Solutions Canada, Inc. Variable desiccant control energy exchange system and method
US10480801B2 (en) 2013-03-13 2019-11-19 Nortek Air Solutions Canada, Inc. Variable desiccant control energy exchange system and method
US10634392B2 (en) 2013-03-13 2020-04-28 Nortek Air Solutions Canada, Inc. Heat pump defrosting system and method
US11300364B2 (en) 2013-03-14 2022-04-12 Nortek Air Solutions Canada, Ine. Membrane-integrated energy exchange assembly
US10352628B2 (en) 2013-03-14 2019-07-16 Nortek Air Solutions Canada, Inc. Membrane-integrated energy exchange assembly
US11598534B2 (en) 2013-03-15 2023-03-07 Nortek Air Solutions Canada, Inc. Control system and method for a liquid desiccant air delivery system
US11408681B2 (en) 2013-03-15 2022-08-09 Nortek Air Solations Canada, Iac. Evaporative cooling system with liquid-to-air membrane energy exchanger
US10584884B2 (en) 2013-03-15 2020-03-10 Nortek Air Solutions Canada, Inc. Control system and method for a liquid desiccant air delivery system
US20160185519A1 (en) * 2013-08-14 2016-06-30 Merck Patent Gmbh High pressure extraction capsule
US11607856B2 (en) 2013-10-18 2023-03-21 Celgard, Llc Porous membrane wipes and methods of manufacture and use
JP2017500070A (ja) * 2013-10-18 2017-01-05 セルガード エルエルシー 多孔膜ワイパー並びに製造および使用の方法
CN111466810A (zh) * 2013-10-18 2020-07-31 赛尔格有限责任公司 多孔膜擦拭件及其制造与使用方法
WO2015057929A1 (en) * 2013-10-18 2015-04-23 Celgard, Llc Porous membrane wipes and methods of manufacture and use
US20150266064A1 (en) * 2014-03-19 2015-09-24 Celgard, Llc Embossed microporous membrane wipes and methods of manufacture and use thereof
US10953591B2 (en) * 2014-03-19 2021-03-23 Celgard, Llc Embossed microporous membrane wipes and methods of manufacture and use thereof
WO2015143106A1 (en) * 2014-03-19 2015-09-24 Celgard, Llc Embossed microporous membrane wipes and methods of manufacture and use thereof
US10804516B2 (en) 2014-03-19 2020-10-13 Celgard, Llc Embossed microporous membrane battery separator materials and methods of manufacture and use thereof
US20210155767A1 (en) * 2014-03-21 2021-05-27 Celgard, Llc Seam tape and methods of manufacture and use thereof
US9790337B2 (en) 2014-03-21 2017-10-17 Celgard, Llc Seam tape and methods of manufacture and use thereof
US11708467B2 (en) * 2014-03-21 2023-07-25 Celgard, Llc Seam tape and methods of manufacture and use thereof
US10899898B2 (en) 2014-03-21 2021-01-26 Celgard, Llc Seam tape and methods of manufacture and use thereof
WO2015143425A1 (en) * 2014-03-21 2015-09-24 Celgard, Llc Seam tape and methods of manufacture and use thereof
CN113290949A (zh) * 2014-03-21 2021-08-24 赛尔格有限责任公司 接缝带及其制造和使用方法
US10030157B2 (en) 2014-04-15 2018-07-24 Celgard, Llc Electrically conductive, transparent, translucent, and/or reflective materials
US10934440B2 (en) 2014-04-15 2021-03-02 Celgard, Llc Electrically conductive, transparent, translucent, and/or reflective materials
US10196495B2 (en) 2014-05-13 2019-02-05 Celgard, Llc Functionalized porous membranes and methods of manufacture and use
US11124622B2 (en) 2014-05-13 2021-09-21 Celgard, Llc Functionalized porous membranes and methods of manufacture and use
US10139116B2 (en) 2014-06-16 2018-11-27 Core Energy Recovery Solutions Inc. Blended membranes for water vapor transport and methods for preparing same
US10866001B2 (en) 2014-06-16 2020-12-15 Core Energy Recovery Solutions Inc. Blended membranes for water vapor transport and methods for preparing same
WO2016008648A1 (de) * 2014-07-15 2016-01-21 Robert Bosch Gmbh Separator mit kraftschlüssig eingespannten partikeln
US10559857B2 (en) * 2014-07-15 2020-02-11 Robert Bosch Gmbh Separator comprising force-locked particles
US20170222279A1 (en) * 2014-07-15 2017-08-03 Robert Bosch Gmbh Separator comprising force-locked particles
US10712024B2 (en) 2014-08-19 2020-07-14 Nortek Air Solutions Canada, Inc. Liquid to air membrane energy exchangers
CN107079207A (zh) * 2014-10-16 2017-08-18 日东电工株式会社 透声膜和具备该透声膜的透声膜构件、以及传声器及电子设备
US10944086B2 (en) * 2014-10-17 2021-03-09 Toyota Jidosha Kabushiki Kaisha Separator for battery, laminated separator, lithium ion secondary battery, and battery pack
CN107078257A (zh) * 2014-10-17 2017-08-18 丰田自动车株式会社 用于电池的分隔器、层压分隔器、锂离子二次电池和电池组
US10938011B2 (en) 2014-11-26 2021-03-02 Celgard, Llc Multilayer microporous separators for lithium ion secondary batteries and related methods
WO2016085970A1 (en) 2014-11-26 2016-06-02 Celgard, Llc Improved multilayer microporous separators for lithium ion secondary batteries and related methods
US11799169B2 (en) 2014-11-26 2023-10-24 Celgard, Llc Multilayer microporous separators for lithium ion secondary batteries and related methods
EP3224880A4 (en) * 2014-11-26 2018-04-11 Celgard LLC Improved multilayer microporous separators for lithium ion secondary batteries and related methods
US10333125B2 (en) 2014-11-26 2019-06-25 Celgard, Llc Multilayer microporous separators for lithium ion secondary batteries and related methods
EP4246702A3 (en) * 2014-11-26 2023-11-22 Celgard, LLC Improved multilayer microporous separators for lithium ion secondary batteries and related methods
CN104835930A (zh) * 2015-03-24 2015-08-12 中国科学技术大学 一种聚烯烃微孔隔膜的制备方法
RU2721330C2 (ru) * 2015-05-08 2020-05-19 СЕЛГАРД, ЭлЭлСи Усовершенствованные, покрытые или обработанные микропористые аккумуляторные сепараторы, перезаряжаемые литиевые батареи, системы и соответствующие способы изготовления и/или применения
US11658333B2 (en) 2015-05-08 2023-05-23 Celgard, Llc Microporous battery separators including polyolefin layer and non-woven layer with alkylbenzene sulfonic acid lithium salt surfactant, lithium batteries utilizing the same, and methods of manufacture of the same
US10741814B2 (en) * 2015-05-08 2020-08-11 Celgard, Llc Microporous battery separators including polyolefin layer and non-woven layer with alkylbenzene sulfonic acid lithium salt surfactant, lithium batteries utilizing the same, and methods of manufacture of the same
WO2016182827A1 (en) * 2015-05-08 2016-11-17 Celgard, Llc Improved, coated or treated microporous battery separators, rechargeable lithium batteries, systems, and related methods of manufacture and/or use
US20160329541A1 (en) * 2015-05-08 2016-11-10 Celgard, Llc Coated or treated microporous battery separators, rechargeable lithium batteries, systems, and related methods of manufacture and/or use
US10782045B2 (en) 2015-05-15 2020-09-22 Nortek Air Solutions Canada, Inc. Systems and methods for managing conditions in enclosed space
US11092349B2 (en) 2015-05-15 2021-08-17 Nortek Air Solutions Canada, Inc. Systems and methods for providing cooling to a heat load
US11815283B2 (en) 2015-05-15 2023-11-14 Nortek Air Solutions Canada, Inc. Using liquid to air membrane energy exchanger for liquid cooling
US11143430B2 (en) 2015-05-15 2021-10-12 Nortek Air Solutions Canada, Inc. Using liquid to air membrane energy exchanger for liquid cooling
US10808951B2 (en) 2015-05-15 2020-10-20 Nortek Air Solutions Canada, Inc. Systems and methods for providing cooling to a heat load
US10569230B2 (en) 2015-05-30 2020-02-25 Core Energy Recovery Solutions Inc. Supported water vapor transport membrane comprising polyethylene oxide copolymer
WO2016196870A1 (en) * 2015-06-03 2016-12-08 Celgard, Llc Improved low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
US10720623B2 (en) 2015-06-03 2020-07-21 Celgard, Llc Low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
US11731407B2 (en) 2015-06-03 2023-08-22 Celgard, Llc Low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
US11075429B2 (en) 2015-06-03 2021-07-27 Celgard, Llc Low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
US10256447B2 (en) 2015-06-03 2019-04-09 Celgard, Llc Low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
US10962252B2 (en) 2015-06-26 2021-03-30 Nortek Air Solutions Canada, Inc. Three-fluid liquid to air membrane energy exchanger
US10184674B2 (en) * 2015-09-16 2019-01-22 Kabushiki Kaisha Toshiba Vapor separator and dehumidifier using the same
US11784344B2 (en) 2015-11-11 2023-10-10 Celgard, Llc Microlayer membranes, improved battery separators, and methods of manufacture and use
EP4099493A1 (en) * 2015-11-11 2022-12-07 Celgard, LLC Microlayer membranes, improved battery separators, and methods of manufacture and use
EP3375026A4 (en) * 2015-11-11 2019-07-03 Celgard, LLC MICROSOUND MEMBRANES, IMPROVED BATTERY PACKAGES, AND METHOD FOR THE PREPARATION AND USE THEREOF
US11056750B2 (en) 2015-11-11 2021-07-06 Celgard, Llc Microlayer membranes, improved battery separators, and methods of manufacture and use
WO2017083633A1 (en) * 2015-11-11 2017-05-18 Celgard, Llc Microlayer membranes, improved battery separators, and methods of manufacture and use
US20210291451A1 (en) * 2016-01-13 2021-09-23 Fujian Institute Of Research On The Structure Of Matter, Chinese Academy Of Science Semi-permeable element, use thereof and preparation method therefor and 3d printing device
WO2017132439A1 (en) 2016-01-29 2017-08-03 Celgard, Llc Improved separators, battereies systems, vehicles, and related methods
EP4234206A2 (en) 2016-01-29 2023-08-30 Celgard, LLC Improved separators, batteries systems, vehicles, and related methods
US11833763B2 (en) * 2016-01-29 2023-12-05 Celgard, Llc Separators, batteries, systems, vehicles, and related methods
US10944087B2 (en) 2016-01-29 2021-03-09 Celgard, Llc Separators, batteries, systems, vehicles, and related methods
CN106003747A (zh) * 2016-05-12 2016-10-12 武汉纺织大学 一种双向拉伸的聚酯纤维多孔膜的制备方法
CN105926168A (zh) * 2016-05-12 2016-09-07 武汉纺织大学 一种双向拉伸的聚苯硫醚纤维多孔膜的制备方法
CN105922605A (zh) * 2016-05-12 2016-09-07 武汉纺织大学 一种双向拉伸的聚丙烯纤维多孔膜的制备方法
WO2018033921A1 (en) * 2016-08-18 2018-02-22 Advanced Mem-Tech Ltd. Improved filtration membrane
US11495865B2 (en) * 2016-11-11 2022-11-08 Celgard, Llc Microlayer membranes, improved battery separators, and related methods
EP3539174A4 (en) * 2016-11-11 2020-10-28 Celgard LLC IMPROVED MICROLAYER MEMBRANES, IMPROVED BATTERY SEPARATORS AND RELATED PROCESSES
EP3539173A4 (en) * 2016-11-11 2020-10-28 Celgard LLC IMPROVED MICROLAYER MEMBRANES, IMPROVED BATTERY SEPARATORS, AND RELATED PROCEDURES
US20180254453A1 (en) * 2017-03-03 2018-09-06 Sumitomo Chemical Company, Limited Nonaqueous electrolyte secondary battery separator
US11892193B2 (en) 2017-04-18 2024-02-06 Nortek Air Solutions Canada, Inc. Desiccant enhanced evaporative cooling systems and methods
EP3646399A4 (en) * 2017-05-26 2021-01-27 Celgard LLC NEW OR IMPROVED MICROPOROUS MEMBRANES, BATTERY SEPARATORS, COATED SEPARATORS, BATTERIES AND RELATED PROCESSES
EP3674354A4 (en) * 2017-08-25 2021-07-28 Beijing Normal University COMPOSITE POROUS MEMBRANE AND PROCESSES FOR PREPARATION AND USE
US20200303704A1 (en) * 2017-11-03 2020-09-24 Celgard, Llc Improved microporous membranes, battery separators, batteries, and devices having the same
US11420162B2 (en) 2017-11-28 2022-08-23 Lg Chem, Ltd. Method for preparing porous membrane of fluorine-based resin
US11389772B2 (en) 2017-12-18 2022-07-19 The Hong Kong University Of Science And Technology Method for synthesis of flexible multifunctional high-voidage ultrathin PE membranes
US11718735B2 (en) 2017-12-22 2023-08-08 Braskem America, Inc. Method of 3D printing, and resulting article having porous structure
WO2019126602A3 (en) * 2017-12-22 2020-03-19 Braskem America, Inc. Method of 3d printing, and resulting article having porous structure
WO2019169210A1 (en) * 2018-03-02 2019-09-06 Celgard, Llc Microporous membranes, battery separator, and methods for making and using the same
US20220192415A1 (en) * 2018-04-23 2022-06-23 2266170 Ontario Inc. Capsules And Other Containers With Optimized Recycling Attributes And Methods For Making Same
US11325074B2 (en) * 2018-05-04 2022-05-10 Shanghai Energy New Materials Technology Co., Ltd. Porous membrane for water treatment and method for preparing the same
EP3811439A4 (en) * 2018-05-10 2022-02-09 Celgard, LLC BATTERY SEPARATORS, COATED BATTERY SEPARATORS, BATTERIES AND RELATED PROCESSES
CN112470331A (zh) * 2018-05-10 2021-03-09 赛尔格有限责任公司 电池隔板、带涂层的电池隔板、电池及相关方法
WO2020142708A1 (en) * 2019-01-04 2020-07-09 Celgard, Llc Polyimide coated separator for lithium batteries or capacitor
CN111697189A (zh) * 2020-06-28 2020-09-22 佛山市金辉高科光电材料股份有限公司 聚烯烃微孔基膜及其制备方法、隔膜和电池
CN112275145A (zh) * 2020-09-16 2021-01-29 浙江赛迅环保科技有限公司 一种口罩用聚四氟乙烯覆膜的制备方法
US20220153002A1 (en) * 2020-11-13 2022-05-19 Berry Global, Inc. Breathable Barrier Laminate
CN114474905A (zh) * 2020-11-13 2022-05-13 贝里国际公司 透气阻隔层合体

Also Published As

Publication number Publication date
JP2018035374A (ja) 2018-03-08
US20170266865A1 (en) 2017-09-21
KR20130039713A (ko) 2013-04-22
TWI635644B (zh) 2018-09-11
KR20220034938A (ko) 2022-03-18
EP2544841B1 (en) 2018-01-17
CN102892534A (zh) 2013-01-23
CN107362693A (zh) 2017-11-21
KR20240014616A (ko) 2024-02-01
KR102206794B1 (ko) 2021-01-22
EP2544841A4 (en) 2015-09-02
JP2021021072A (ja) 2021-02-18
KR20180105262A (ko) 2018-09-27
JP2016166334A (ja) 2016-09-15
TW201824613A (zh) 2018-07-01
EP2544841A1 (en) 2013-01-16
JP6773630B2 (ja) 2020-10-21
KR102629227B1 (ko) 2024-03-13
KR102373866B1 (ko) 2022-03-11
WO2011112885A1 (en) 2011-09-15
JP2023021167A (ja) 2023-02-09
KR101900241B1 (ko) 2018-09-19
KR20210008954A (ko) 2021-01-25
JP2013527260A (ja) 2013-06-27
KR20170106523A (ko) 2017-09-20
EP2544841B2 (en) 2021-07-07

Similar Documents

Publication Publication Date Title
US20170266865A1 (en) Biaxially oriented porous membranes, composites, and methods of manufacture and use
US20200219796A1 (en) Multilayer hybrid battery separators for lithium ion secondary batteries and methods of making same
KR101651298B1 (ko) 폴리에틸렌 멤브레인 및 이의 생산 방법
CA2650680C (en) Gas separation membrane
RU2434754C2 (ru) Многослойная, микропористая полиэтиленовая мембрана, разделитель аккумулятора, изготовленный из нее, и аккумулятор
CA2615495C (en) Multi-layer, microporous polyolefin membrane and battery separator
KR100637972B1 (ko) 리튬이온 전지용 고온 용융 무결성 전지 격리판
EP2206546A1 (en) Gas separation membrane
KR20180067723A (ko) 마이크로층 막, 개선된 전지 분리기, 및 제조 및 사용 방법
US20140094076A1 (en) Microporous Materials With Fibrillar Mesh Structure and Methods of Making and Using the Same
CN107078259B (zh) 微孔片材产品及制备和使用其的方法
US20200047473A1 (en) Polyolefin microporous membrane
JP7227507B2 (ja) エアフィルタ濾材、フィルタパック、エアフィルタユニット、およびこれらの製造方法
US7662518B1 (en) Shutdown separators with improved properties
TW201137000A (en) Biaxially oriented porous membranes, composites, and methods of manufacture and use
JP2018143993A (ja) 積層不織布及びベントフィルター
JP2024049359A (ja) ポリオレフィン微多孔膜、電池用セパレータおよび二次電池

Legal Events

Date Code Title Description
AS Assignment

Owner name: CELGARD, LLC, NORTH CAROLINA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ZHANG, XIAOMIN;RUMIERZ, GERALD P.;HUMISTON, KARL F.;AND OTHERS;SIGNING DATES FROM 20110308 TO 20110310;REEL/FRAME:025948/0316

AS Assignment

Owner name: CELGARD, LLC, NORTH CAROLINA

Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE APPLICATION NUMBER PREVIOUSLY RECORDED ON REEL 025948 FRAME 0316. ASSIGNOR(S) HEREBY CONFIRMS THE TO RE-RECORD ASSIGNMENT PREVIOUSLY RECORDED UNDER REEL/FRAME 025948/0316 TO CORRECT THE APPLICATION # FROM 13944697 TO 13044708.;ASSIGNORS:ZHANG, XIAOMIN;RUMIERZ, GERALD P.;HUMISTON, KARL F.;AND OTHERS;SIGNING DATES FROM 20110308 TO 20110310;REEL/FRAME:026014/0552

AS Assignment

Owner name: BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT, NORTH CAROLINA

Free format text: PATENT SECURITY AGREEMENT;ASSIGNOR:CELGARD, LLC (F/K/A CELGARD, INC.);REEL/FRAME:032631/0655

Effective date: 20140408

Owner name: BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT, NO

Free format text: PATENT SECURITY AGREEMENT;ASSIGNOR:CELGARD, LLC (F/K/A CELGARD, INC.);REEL/FRAME:032631/0655

Effective date: 20140408

AS Assignment

Owner name: CELGARD, LLC (F/K/A/ CELGARD, INC.), NORTH CAROLINA

Free format text: TERMINATION AND RELEASE OF SECURITY INTEREST IN UNITED STATES PATENTS;ASSIGNOR:BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:036485/0267

Effective date: 20150826

Owner name: CELGARD, LLC (F/K/A/ CELGARD, INC.), NORTH CAROLIN

Free format text: TERMINATION AND RELEASE OF SECURITY INTEREST IN UNITED STATES PATENTS;ASSIGNOR:BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT;REEL/FRAME:036485/0267

Effective date: 20150826

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION