TWI772399B - 聚氨酯凝膠組合物及其用途 - Google Patents
聚氨酯凝膠組合物及其用途 Download PDFInfo
- Publication number
- TWI772399B TWI772399B TW107111164A TW107111164A TWI772399B TW I772399 B TWI772399 B TW I772399B TW 107111164 A TW107111164 A TW 107111164A TW 107111164 A TW107111164 A TW 107111164A TW I772399 B TWI772399 B TW I772399B
- Authority
- TW
- Taiwan
- Prior art keywords
- polyurethane
- oil
- mass
- gel
- composition
- Prior art date
Abstract
本發明提供一種聚氨酯凝膠組合物,包含A與B,其中A是以(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3
-OH(式中,R3
表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,或A是以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3
-OH(式中,R3
表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,B是油劑。 藉由該聚氨酯凝膠組合物獲得的油溶性凝膠膜,即使在透明性、光澤亮度、彈力性及復原力的任一點都極為優越,所以本發明的聚氨酯凝膠組合物做為化妝材料的原料特別有用。
Description
本發明關於一種擁有強度與柔軟性,具有高彈性的新聚氨酯凝膠組合物及其用途、特別是用於化妝材料。
以往,聚氨酯做為熱可塑性樹脂、接著劑、水溶性膠化劑等來使用(參照下述專利文獻)。做為熱可塑性樹脂,提出例如使用具有氫化聚丁二烯骨架的聚氨酯丙烯酸酯或具有聚丁二烯骨架的聚氨酯丙烯酸酯來製造的樹脂片做為印刷用強光澤片(專利文獻1)。又,提出一種用來製造熱可塑性聚氨酯的組合物,具有良好的物理性質及優越的耐氣候性,包含:具有每一分子1.6~2個末端羥基及數均分子量500~20,000的聚二烯二醇、具有每一分子2個異氰酸基的異氰酸、以及對應需要,具有每一分子2個羥基的低分子量的鏈伸長劑(專利文獻2)。
做為接著劑,提出一種化妝板,其特徵在於例如在基材上,設有接著劑層或接著劑層及底塗層、以及轉移層,前述接著劑層是由含羥基的聚丁二烯類聚合物及有機多異氰酸酯構成的接著劑所獲得者,並教導該接著劑依需要可包含上述含羥基的聚丁二烯類聚合物以外的含羥基樹脂(例如以乙二醇為出發原料的樹脂)(專利文獻3)。
做為水溶性膠化劑,提出一種用於沖水馬桶的自動芳香洗滌劑基材,例如是由水溶性聚氧化烯多元醇(A)、數均分子量為500~2000的非水溶性多元醇(B)以及有機聚異氰酸酯(C)所衍生,由(A):(B)的重量比是
(99.9~85.0):(0.1~15.0)的水溶性固體聚氨酯樹脂(D)所構成(專利文獻4)。
到目前為止,聚氨酯已被用在化妝品領域的各種用途。例如,提出一種化妝材料組合物(專利文獻5),包含由具有氨基甲酸酯鍵的親水性化合物構成的締合性增稠劑(以親水基部做為骨架,末端具有疏水部分的共聚物)。又,提出一種睫毛膏產品(專利文獻6),具備:水性介質與分散在該水性介質中的固體顆粒形態的成膜聚氨酯,包含:儲藏器,包含在25℃的溫度,及200s-1的截斷速度下,具有在5Pa.s至18Pa.s的範圍內的黏度,不包含蠟的組合物;以及具備塗抹器的密封手段。再者,也提出了一種乳液型組合物(專利文獻7),是包含以締合性聚氨酯增稠的生理上可接受的介質的組合物,上述介質包含乳液中的水相和液體的脂肪相,具有用於人臉及如身體的皮膚、睫毛、眉毛、頭髮的角蛋白織維,甚至唇部的保養、治療或化妝的有黏性的黏稠度,提出了一種化妝用貼片(專利文獻8),其特徵在於具有親水性環氧乙烷的片段與疏水性環氧乙烷的片段,大部分或全部片段在常溫下為液體的黏著性聚氨酯凝膠組成的凝膠層中含有維生素,提出了一種彈性凝膠狀油性化妝材料(專利文獻9),其特徵在於包含:部分交聯型的有機聚矽氧聚合物、固體油及粉末(例如聚氨酯粉末),提出了一種化妝材料(專利文獻10),其特徵在於在包含含有功能性成分及/或設計性成分的聚氨酯凝膠粒子的化妝品中,至少一該凝膠粒子是三個官能基以上的,聚異氰酸酯、分子內具有活性氫基的化合物、以及分子內具有活性氫基的聚矽氧烷及/或聚矽氧烷與內酯的反應產物共聚而成的三維交聯的聚氨酯凝膠粒子(粒子A),粒子A的表面是以從聚脲膠體非水溶劑的溶液析出的聚脲膠體粒子(粒子B)所被覆的聚氨酯凝膠粒子(粒子C)。
先前技術文獻
專利文獻
[專利文獻1]特開平9-228294號公報
[專利文獻2]特表平11-507975號公報
[專利文獻3]特開2001-287309號公報
[專利文獻4]特開平8-218097號公報
[專利文獻5]特開2000-239120號公報
[專利文獻6]特開2000-178137號公報
[專利文獻7]特開2000-63235號公報
[專利文獻8]特開2005-15457號公報
[專利文獻9]特開2008-88099號公報
[專利文獻10]特許第4802136號公報
本案發明人們對先前技術進行反覆研究,以解決肌膚或眼瞼皺紋、下垂、黑眼圈、暗沉等煩惱。做為對皺紋、下垂、黑眼圈、暗沉等的先前技術的處理,舉出以粉末固體、油性固體劑型等各種劑型進行的處理。但是,在包含珠光劑的粉末固體,具有不自然的強光,強調了凹凸,反而使皺紋顯眼,珠光的附著力差的缺點。另一方面,在油性固體劑型中結晶成分多,所以具有光澤度不足,隨著時間經過產生凹凸(雙重溝)的誤導的缺點。因此,在製造用來改善皺紋、下垂、黑眼圈、暗沉的化妝材料時,需要立體地處理活動激烈的臉和眼瞼。從這種觀點出發,本案發明人們的目標在於開發具有下述特徵的化妝膜。
(1)柔軟運動,具有自癒性。即使產生凹凸也能自然修復,並化妝膜表面總是平滑。也就是說,膜不扭曲。
(2)膜本身具有光澤和厚度。也就是說,因潮濕光澤而有亮度。
(3)化妝膜的持續效果優越。
本案發明人們使用矽橡膠、多醣類、水性聚氨酯做為復原性材料並反覆研究。但是,這些素材伴隨著優點,有需要解決的缺點。也就是說,雖然矽橡膠是柔軟的凝膠,但缺點是缺乏光澤、缺乏復原力。多醣類凝膠透明度和凝膠強度強,但具有彈性與復原力差的缺點。儘管水性聚氨酯凝膠透明且,彈性、復原力強,但由於需要水而有色域的限制,具有光澤與化妝膜的持續效果不足的重大缺點。
通常,已知聚氨酯是使使二異氰酸酯和多元醇反應而獲得的,並由氫化聚丁烯和多元醇組成的聚氨酯是屬於公知技術的範疇。但是,沒有使用聚氨酯做為油溶性膠凝劑的例子。
因此,本案發明人們為了獲得透明,高光澤,有彈性,恢復力,優異的化妝持續效果的化妝膜,認真反覆進行研究開發。
其結果是,本案發明人們發現將油劑與以(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,或以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯混合,獲得有彈性、復原性的聚氨酯凝膠組合物。將本聚氨酯凝膠組合物用於化妝材料,獲得光澤優越的化妝膜,發現可提高因肌膚或眼瞼等的運動導致經時脫妝等的抑制效果(化妝持續效果)。本發明是根據此之事而完成者。
也就是說,本發明如以下所述。
(1)一種聚氨酯凝膠組合物,包含A與B,其中A是以(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或
分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,或A是以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,B是油劑。
(2)如(1)所述的組合物,其中A的(a)是(c)以(c)末端具有羥基的氫化聚丁二烯與(d)二異氰酸酯化合物反應所獲得的異氰酸酯化合物。
(3)如(1)或(2)所述的組合物,其中A的(d)是以OCN-R2-NCO(式中R2為C2~C6亞烷基)所表示的二異氰酸酯化合物。
(4)如(1)~(3)中任一所述的組合物,其中A的(a)是以式(1)表示的異氰酸酯化合物。
(5)如(1)~(4)中任一所述的組合物,其中A的(a)是以式(2)表示的異氰酸酯化合物。
(6)如(2)所述的組合物,其中在(c)末端具有羥基的氫化聚丁二烯是式(3)(式中,n表示10~100的整數)。
(b)以HO-R3-OH表示的二元醇是式(5)。
式(5)HO-CH 2 -CH 2 -OH (5)
(7)如(1)所述的組合物,其中A的聚氨酯是油溶性聚氨酯。
(8)如(1)所述的組合物,其中A的聚氨酯的平均分子量(Mw)是10000~100000。
(9)如(1)所述的組合物,其中B的油劑是在25℃下的液狀油劑。
(10)如(1)所述的組合物,其中B的油劑是從烴油、羥基數為0或1的酯油及矽油中任選一種以上。
(11)如(1)所述的組合物,其中A的聚氨酯的含有量為1~35質量%。
(12)如(1)所述的組合物,其中B的油劑的含有量為65~99質量%。
(13)如(1)~(12)中任一所述的組合物,其中將如(1)~(12)中任一所述的聚氨酯凝膠組合物30份與液體石蠟70份在85℃加熱溶解,冷卻得到的凝膠,以2cm/min使2cmφ球形適配器穿透10mm時的負重值為0.20~10.00N。
(14)如(1)~(13)中任一所述的組合物,具有凝膠復原性。
(15)如(1)~(14)中任一所述的組合物,700nm的波長的透射率為90%以上。
(16)一種化妝材料,包含如(1)~(15)中任一所述的組合物。
(17)一種聚氨酯凝膠組合物的製造方法,該聚氨酯凝膠組合物包含A與B(在此,A是聚氨酯,B是油劑),其步驟包含:在B的油劑中,添加以A的(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇,進行加成聚合反應。
(18)如(17)所述的製造方法,其中A的(a)是(c)以(c)末端具有羥基的氫化聚丁二烯與(d)二異氰酸酯化合物反應所獲得的異氰酸酯化合物。
(19)如(17)所述的製造方法,其中A的聚氨酯是以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH所表示的二元醇反應所獲得的聚氨酯(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)。
(20)如(18)或(19)所述的製造方法,其中A的(d)是以OCN-R2-NCO所表示的二異氰酸酯化合物(式中R2為C2~C6亞烷基)。
(21)如(17)、(18)或(20)所述的製造方法,其中A的(a)是以式(1)表示的異氰酸酯化合物。
(22)如(17)、(18)、(20)或(21)項所述的製造方法,其中A的(a)是以式(2)表示的異氰酸酯化合物。
(b)以HO-R3-OH表示的二元醇是式(5)。
式(5)HO-CH 2 -CH 2 -OH (5)
(24)如(17)或(19)所述的製造方法,其中A的聚氨酯是油溶性聚氨酯。
(25)如(17)或(19)所述的製造方法,其中A的聚氨酯的平均分子量(Mw)是10000~100000。
(26)如(17)所述的製造方法,其中B的油劑是在25℃下的液狀油劑。
(27)如(26)所述的製造方法,其中B的油劑是從烴油、羥基數為0或1的酯油及矽油中任選一種以上。
(28)如(17)或(19)所述的製造方法,其中A的聚氨酯的含有量為1~35質量%。
(29)如(17)所述的製造方法,其中B的油劑的含有量為65~99質量%。
(30)如(17)~(29)中任一所述的製造方法,其中將如(1)~(12)中任一所述的聚氨酯凝膠組合物30份與液體石蠟70份在85℃加熱溶解,冷卻得
到的凝膠,以2cm/min使2cm φ球形適配器穿透10mm時的負重值為0.20~10.00N。
(31)如(17)~(30)中任一所述的製造方法,具有凝膠復原性。
(32)如(17)~(31)中任一所述的製造方法,700nm的波長的透射率為90%以上。
本發明的聚氨酯凝膠組合物,在透明性、光澤亮度、彈力性及復原力的任一點都極為優越,所以本發明的聚氨酯凝膠組合物用來做為塗布在肌膚多動部分的身體保養油、化妝基底、防曬材料、眼彩等化妝材料的基材。
第1圖表示測量以製造實施例2獲得的本發明的聚氨酯凝膠組合物與以製造比較例2所獲得的糊精脂肪酸酯凝膠的自我復原力的方法的概略圖。
第2圖表示分別進行關於以製造實施例2獲得的本發明的聚氨酯凝膠組合物及以製造比較例2所獲得的糊精脂肪酸酯凝膠的自我復原力的測量結果的圖。
本發明的包含A與B的聚氨酯凝膠組合物,包含下列組合物。
組合物包含:A,以(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯;以及B,油劑。
組合物包含:A,以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯;以及B,油劑。
在本發明中,「末端」是指「兩末端」。
在組合物1所使用的A的(a),若為末端具有異氰酸基的氫化聚丁二烯則沒有特別限定。例如表示為下述式(1)所示的化合物。
R1、R2分別獨立,即相同或不同地表示C1~C6亞烷基,亞烷基可以是直鍊,也可以是支鏈。做為C1~C6亞烷基,舉出例如亞甲基、亞乙基、正亞丙基、正亞丁基、正亞己基等。
n表示10~100的整數,n的較佳範圍為15~55。
n1、n2分別獨立,即相同或不同地表示0或1。
在本發明使用的末端具有異氰酸基的氫化聚丁二烯的氫化聚丁二烯部分,也可以是由在上例示的重複單位中的一種構成者,或,也可以是規則或隨機地包含兩種以上的重複單位者。構成氫化聚丁二烯部分的重複單位「C4H8」的立體結構可以相同也可以不同,氫化聚丁二烯部分以式(6)所表示的結構,全部包含在本發明中。
做為以式(1)表示的末端具有異氰酸基的氫化聚丁二烯,例如例示為以下式(2)表示的化合物。
式(2)的化合物相當於在以式(1)表示的末端具有異氰酸基的氫化聚丁二烯中,R1是亞乙基,R2是六亞甲基,n1=n2=1的情況。
做為在組合物1及2中使用的A的(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的乙二醇的例,舉出例如乙二醇(HOCH2CH2OH)、丙二醇(HOCH2CH(OH)CH3)、1,3-丁二醇(HOCH2CH2CH(OH)CH3)、二甘醇(HOCH2CH2OCH2CH2OH)等。
在組合物2所使用的A的(c)末端具有羥基的氫化聚丁二烯沒有特別限制。例如,表示有以下式(3)所示的化合物。
在式(3)中,氫化聚丁二烯部分(式(6))具有與上述相同的意思。
又,做為在組合物2所使用的(d)二異氰酸酯化合物,可舉出例如六亞甲基二異氰酸酯、1,3-雙(異氰酸根合甲基)苯、1,3-雙(異氰酸根合甲基)環己烷、2,4-甲苯二異氰酸酯、2,6-甲苯二異氰酸酯等。這些之中,以下式(4)所示的六亞甲基二異氰酸酯為較佳。
在上述組合物1中,將以A的(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇,進行加成聚合反應來製造聚氨酯的情況下,以莫耳比(a):(b)=2:3~3:2來進行為更佳。當聚氨酯聚合物分子中的疏水部的氫化聚丁烯部分多時,在油劑中的溶解度提高,且透明性提升。另一方面,當以構成聚氨酯聚合物分子中的親水部的HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇量多時,聚氨酯凝膠的自締合性提高,彈性增加,但若量多,則溶解性降低。也就是說,疏水部與親水部之間的平衡變得重要,較佳的莫耳比為2:3~3:2。包含在此範圍的莫耳比(a):(b)例示為2:3~3:2、3:4~4:3、4:5~5:4、4:5~4:3以及9:10~10:9。在此情況下,(a)的平均分子量(Mw)較佳為1000~3000。做為包含在該範圍內的分子量,除了1000~3000以外,例示有1200~2800、1200~2600、1200~2400、1200~2000、1200~1800、1300~2700、1300~2500、1300~2100、1300~1800、1500~2500、1500~2100、1800~2800、1800~2600、1800~2400以及1800~2100等。
在上述組合物2中,以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇,進行加成聚合反應來製造聚氨酯的情況下,以莫耳比(c):(b)=2:3~3:2來進行為更佳。當聚氨酯聚合物分子中的疏水部的氫化聚丁烯部分多時,在油劑中的溶解度提高,且透明性提升。另一方面,當以構成聚氨酯聚合物分子中的親水部的HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇量多時,聚氨酯凝膠的自締合性提高,彈性增加,但若量多,則溶解性降低。也就是說,疏水部與親水部之間的平衡變得重要,較佳的莫耳比為2:3~3:2。包含在此範圍的
莫耳比(c):(b)例示為2:3~3:2、3:4~4:3、4:5~5:4、4:5~4:3以及9:10~10:9。在此情況下,(c)的平均分子量(Mw)較佳為1000~3000。做為包含在該範圍內的分子量,除了1000~3000以外,例示有1200~2800、1200~2600、1200~2400、1200~2000、1200~1800、1300~2700、1300~2500、1300~2100、1300~1800、1500~2500、1500~2100、1800~2800、1800~2600、1800~2400以及1800~2100等。
以加成聚合所獲得的聚氨酯的平均分子量(Mw)較佳為10000~100000。做為包含在此範圍的分子量,例示有10000~100000、10000~90000、10000~80000、10000~70000、10000~60000、10000~50000、20000~90000、20000~80000、20000~70000、20000~60000、20000~50000、30000~90000、30000~80000、30000~70000、30000~60000、30000~50000、40000~90000、40000~80000、40000~70000,40000~60000、50000~90000、50000~80000以及50000~70000。
在本發明所使用的A的聚氨酯較佳為油溶性。在本發明中,「油溶性」是指「能在30℃溶解至少1質量%於2-乙基己酸鯨蠟醇酯」。
組合物1中的A的聚氨酯的含量較佳為1~35質量%。如果聚氨酯聚合物的濃度小於此範圍,則雖然透明性高,但彈力感(負重值)差,賦予化妝材料的彈力感差。做為包含在此範圍的聚氨酯的含量,例示有1~35質量%、1~30質量%、1~25質量%、1~20質量%、1~15質量%、1~10質量%、1~5質量%、5~30質量%、5~25質量%、5~20質量%、5~15質量%、5~10質量%、10~30質量%、10~25質量%、10~20質量%以及10~15質量%。又,組合物1中的B的油劑的含量較佳為65至99質量%。做為包含在此範圍的油劑的含量,例示有65~99質量%、70~99質量%、80~99質量%、85~99質量%、90-99質量%、95~99質量%、70~95質量%、75~95質量%、80-95質量%、85~95質量%、
90~95質量%、70~90質量%、75~90質量%、80~90質量%以及85~90質量%。
組合物2中的A的聚氨酯的含量更佳為1~35質量%。若聚氨酯聚合物的濃度小於此範圍,則雖然透明性高,但彈力感(負重值)差,賦予化妝材料的彈力感差。做為包含在此範圍的聚氨酯的含量,例示有1~35質量%、1~30質量%、1~25質量%、1~20質量%、1~15質量%、1~10質量%、1~5質量%、5~30質量%、5~25質量%、5~20質量%、5~15質量%、5~10質量%、10~30質量%、10~25質量%、10~20質量%以及10~15質量%。又,組合物2中B的油劑的含量較佳為65~99質量%。做為包含在此範圍的油劑的含量為65~99質量%、70~99質量%、80~99質量%、85~99質量%、90~99質量%、95~99質量%、70~95質量%、75~95質量%、80~95質量%、85~95質量%、90~95質量%、70~90質量%、75~90質量%、80~90質量%以及85~90質量%。
在聚氨酯凝膠組合物中的B的油劑,若為用於一般化妝材料者,則可以沒有特別限定地使用。做為其性質沒有特別限定,但在10℃~30℃,特別是在25℃為液態的油劑為較佳。
做為在聚氨酯凝膠組合物所使用的B的油劑,不管動物油、植物油、合成油等的起源,舉出烴油、酯油、油脂類、矽油、氟油類等。在這些之中,因為極性低者有傾向聚氨酯凝膠組合物的強度變高,所以例示有從烴油、羥基數為0或1的酯油、以及含有苯基的矽油選出一種以上來使用者。具體來說,舉出液體石蠟、角鯊烷、聚丁烯、聚異丁烯等烴類,橄欖油、蓖麻油、貂油、澳洲胡桃油、荷荷芭油等油脂類,、異辛酸鯨蠟酯(2-乙基己酸鯨蠟醇酯)、肉荳蔻酸異丙酯、棕櫚酸異丙酯、辛基十二烷基肉荳蔻酸酯、三辛酸甘油酯、聚甘油二異硬脂酸酯、二甘油異硬脂酸酯、二異硬脂醇蘋果酸酯、三山嵛酸甘油酯、松香酸季戊
四醇酯、新戊二醇二辛酸酯等酯類,甲基苯基聚矽氧烷、二苯基聚矽氧烷等矽氧烷類,可使用這些中的一種或兩種以上。
本發明的聚氨酯凝膠組合物,較佳為不僅具有透明性與光澤,還具有極高的彈性、復原性的特徵。穿透負重值測量的結果是將此聚氨酯凝膠組合物30份與液體石蠟(以ASTM D445測量方法在40℃的動黏度為8mm2/s)70份,在85℃加熱溶解,在30℃冷卻獲得的凝膠,表示以2cm/min使2cmφ球形適配器穿透10mm時的負重值為0.20~10.00N的優越特性。這表示本發明的聚氨酯凝膠組合物具有彈性、復原力。又,關於透明性,本發明的聚氨酯凝膠組合物在700nm的波長下具有90%以上的透射率。即,本發明的聚氨酯凝膠組合物具有極高的透明性。
本發明的聚氨酯凝膠組合物1可以使用公知的聚氨酯製造方法來製造。也就是說,本發明的聚氨酯凝膠組合物1是在B的油劑中,添加以A的(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇,進行加成聚合反應所獲得。
本發明的聚氨酯凝膠組合物2可以使用公知的聚氨酯製造方法來製造。也就是說,本發明的聚氨酯凝膠組合物2是可藉由加入以(c)末端具有羥基的氫化聚丁二烯、(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇、B的油劑均勻混合,投入(d)二異氰酸酯化合物反應來製造。
做為在本發明的聚氨酯凝膠組合物1和聚氨酯凝膠組合物2中的聚氨酯的一例,舉出在INCI(International Nomenclature of Cosmetic Ingredient(化妝品原料的國際命名法))中,賦予有「氫化聚丁二烯/乙二醇/HDI共聚物」的名稱的聚氨酯。
在本發明的聚氨酯凝膠組合物中,可根據需要適當使用可含有的各種成分。做為這些成分,例示有揮發性成分、界面活性劑、油劑、粉末、水性成分、醇類、水溶性聚合物、紫外線吸收劑、保濕劑、膠凝化劑與增稠劑、防褪色劑、抗氧化劑、消泡劑、美容成分(美白劑、細胞活化劑、消炎劑、血液循環促進劑、皮膚收斂劑、抗脂漏劑等)、防腐劑、抗菌劑、香料、維他命類、胺基酸類、核酸、激素等。
做為水性成分並沒有特別限制,在室溫下為液體成分,若為通常用於化妝材料者,則可以使用任何成分。舉出例如水、乙醇、丙二醇、1,3-丁二醇、二丙二醇等多元醇類,甘油、雙甘油、聚甘油等甘油類,蘆薈、金縷梅、黃瓜、檸檬、薰衣草、玫瑰等植物萃取液等,這些水性成分根據需要可使用一種或兩種以上。用於本發明的水性成分的含量,因使用性、使用感及劑型而不同,並沒有特別限制,但組合物中,較佳為10質量%以下,更佳為5質量%以下,特別是0.1質量%在化妝效果、使用性、使用感方面較佳。
做為界面活性劑若為通常使用於化妝材料者,則沒有特別限制,可使用任何物。雖然界面活性劑例示有陰離子界面活性劑、陽離子界面活性劑、非離子界面活性劑、兩性界面活性劑等,但可根據需要組合一種或兩種以上來使用。
做為陰離子表面活性劑,具體來說,舉出硬脂酸鈉與三乙醇胺棕櫚酸酯等脂肪酸皂、烷基醚羧酸及其鹽、氨基酸與脂肪酸縮合等的羧酸鹽、烷基磺酸、烯烴磺酸鹽、脂肪酸酯的磺酸鹽、脂肪酸醯胺的磺酸鹽、烷基磺酸鹽與其福馬林縮合物的磺酸鹽、烷基硫酸酯鹽、高級仲醇硫酸酯鹽、烷基及烯丙基醚硫酸酯鹽、脂肪酸酯硫酸酯鹽、脂肪酸烷醇醯胺的硫酸鹽、聚氧乙烯烷基硫酸酯鹽、磺化蓖麻油等硫酸酯鹽類、磷酸酯鹽、磷酸醚鹽、烷基烯丙基醚磷酸酯鹽、醯胺磷酸酯鹽、N-醯基氨基酸類活性劑等。
做為陽離子界面活性劑,舉出以長鏈烷基三甲基銨鹽、二長鏈烷基二甲基銨鹽、長鏈烷基二甲基芐基銨鹽、二聚氧乙烯烷基甲基銨鹽、二聚氧乙烯烷基醚二甲基銨鹽、聚氧丙烯甲基二乙基銨鹽等烷基季銨鹽與芳香族季銨鹽為代表,還有烷基吡啶鎓鹽等吡啶鎓鹽、烷基二羥基乙基咪唑啉鹽斗咪唑啉鹽、N-醯基鹼性胺基酸低級烷基酯鹽以及烷基胺鹽、聚胺、氨基醇脂肪酸衍生物等胺鹽等。
做為非離子界面活性劑,舉出山梨醇酐脂肪酸酯、甘油脂肪酸酯、聚甘油脂肪酸酯、丙二醇脂肪酸酯、聚乙二醇脂肪酸酯、蔗醣脂肪酸酯、聚氧乙烯烷基醚、聚氧丙烯烷基醚、聚氧乙烯烷基苯基醚、聚氧乙烯脂肪酸酯、聚氧乙烯山梨醇脂肪酸酯、聚氧乙烯山梨糖醇脂肪酸酯、聚氧乙烯甘油脂肪酸酯、聚氧乙烯丙二醇脂肪酸酯、聚氧乙烯蓖麻油、聚氧乙烯氫化蓖麻油、聚氧乙烯氫化蓖麻油脂肪酸酯、聚氧乙烯植物甾烷醇醚、聚氧乙烯植物甾烷醇醚、聚氧乙烯膽固醇醚、聚氧乙烯膽固醇醚、聚氧化烯改性的有機聚矽氧烷、聚氧化烯烷基共改性的有機聚矽氧烷、烷醇醯胺、糖醚、糖醯胺等。
做為兩性界面活性劑,舉出烷基二甲基胺基乙酸甜菜鹼、脂肪酸醯胺基丙基二甲基胺基乙酸甜菜鹼、烷基二羥基乙基胺基乙酸甜菜鹼等碳酸甜菜鹼型兩性界面活性劑、烷基磺酸甜菜鹼等磺酸甜菜鹼型兩性界面活性劑、N-脂肪酸醯基-N-羧甲基-N-羥乙基乙二胺鹽、N-脂肪酸醯基-N-羧甲氧基乙基-N-羧甲基乙二胺二鈉鹽等醯胺胺型(咪唑啉型)兩性界面活性劑、N-[3-烷氧基-2-羥丙基]精胺酸鹽等胺基酸型兩性界面活性劑、烷基亞胺基二羧酸酯鹽型兩性界面活性劑等。
做為保濕劑,舉出尿素、玻尿酸、硫酸軟骨素、吡咯烷酮羧酸鹽等。
在膠凝化劑中,作為水性膠凝化劑,舉出阿拉伯膠、黃蓍膠、半乳聚醣、角豆樹膠、瓜爾膠、刺梧桐樹膠、角叉菜膠、果膠、瓊脂、榅桲籽(marmelo)、澱粉(大米、玉米、馬鈴薯、小麥)、海藻膠體、特拉普膠、刺槐豆膠等植物類聚合物、黃原膠、葡聚糖、琥珀醯基葡聚糖、普魯蘭多糖等微生物聚合物、膠原蛋白、酪蛋白、白蛋白、明膠等動物類聚合物、羧甲基澱粉、甲基羥丙基澱粉等澱粉類聚合物、甲基纖維素、羥丙基甲基纖維素、羧甲基纖維素、羥甲基纖維素、羥丙基纖維素、硫酸纖維素鈉、羧甲基纖維素鈉等纖維素類聚合物、海藻酸鈉、海藻酸丙二醇酯等海藻酸鹽聚合物、聚丙烯酸鈉、羧基乙烯基聚合物、烷基改性羧基乙烯基聚合物、聚丙烯醯胺、聚乙烯醇、聚乙烯基吡咯烷酮等乙烯類聚合物、聚乙二醇、環氧乙烷-環氧丙烷共聚物、丙烯酸酯-聚丙烯醯基二甲基牛磺酸鈉共聚物、聚丙烯酸鈉、聚丙烯酸乙酯、聚丙烯醯胺等丙烯酸類聚合物、膨土、矽酸鋁鎂、合成鋰皂石、鋰膨潤石、無水矽酸等無機膠凝化劑及增稠劑,聚乙烯亞胺、陽離子聚合物等。
做為皮膜形成劑,使用天然橡膠、天然纖維素、陽離子化纖維素、各種丙烯酸樹脂(包含共聚物)、各種醇酸樹脂、聚乙烯醇、聚乙烯吡咯烷酮、硝基纖維素、各種有機矽樹脂(包含共聚物)、尿素樹脂、改性玉米澱粉等。做為具體的皮膜形成劑,舉出丙烯酸醯胺.丙烯酸烷基酯/甲氧基聚乙二醇甲基丙烯酸酯共聚物、甲氧基聚乙二醇甲基丙烯酸酯、二十碳烯/乙烯基吡咯烷酮聚合物、1,1'-亞甲基雙(4-異氰酸根合環己烷)-聚丙二醇共聚物、全氟聚醚、(丙烯酸酯/聚三甲基甲矽烷氧基甲基丙烯酸酯)共聚物、聚丙基倍半矽氧烷、(二十碳烯/乙烯基吡咯烷酮)共聚物、(乙烯基吡咯烷酮/十六碳烯)共聚物、羥乙基纖維素、矽酮改性降莰烯等。
若著色劑是通常使用於化妝材料的著色劑,則對於球形、板狀、紡錘狀、針狀等形狀或煙霧狀、微粒子、顏料級等的粒徑,或者是多孔、無孔
等的粒子結構等並沒有特別限定,可使用無機顏料、有機顏料、光亮性顏料、金屬類等。做為具體的粉末,可例示氧化鈦、氧化鋅、氧化鈰、硫酸鋇等白色無機顏料、氧化鐵、炭黑、氧化鉻、氫氧化鉻、普魯士藍、群青藍、紅丹等有色無機顏料、雲母鈦、氯氧化鉍、有機顏料處理雲母鈦、被覆二氧化鈦的雲母、被覆二氧化鈦的合成金雲母、被覆二氧化鈦的氯氧化鉍、氧化鐵雲母鈦、普魯士藍處理的雲母鈦、胭脂紅處理的雲母鈦、魚鱗箔、被覆二氧化鈦的玻璃粉末、聚對苯二甲酸-鋁-環氧樹脂層壓粉末、聚對苯二甲酸乙酯-聚烯烴層壓薄膜粉末、聚乙烯對苯二甲酸酯-聚甲基丙烯酸甲酯層壓薄膜粉末等樹脂層壓粉末等的光輝性顏料、紅色201號、紅色202號、紅色205號、紅色226號、紅色228號、橙色203號、橙色204號、藍色404號、黃色401號等有機顏料粉末、紅色3號、紅色104號、紅色106號、橙色205號、黃色4號、黃色5號、綠色3號、藍色1號等鋯、鋇或鋁色淀等有機顏料粉末,或是鋁粉末、金粉末、銀粉末等金屬粉末、被覆氧化鈦微粒的雲母鈦、被覆氧化鋅微粒的雲母鈦、被覆硫酸鋇的雲母鈦、含有氧化鈦的二氧化矽、含有氧化鋅的二氧化矽等複合粉末等,做為天然色素,舉出胭脂紅、紫膠酸、紅花素、巴西蘇木素、番紅花等,根據需要可以使用一種或兩種以上。這些也可以使用氟類化合物、矽氧類化合物、金屬皂、卵磷脂、氫化卵磷脂、膠原、烴、高級脂肪酸、高級醇、酯、蠟、界面活性劑等一種或兩種以上來施加表面處理。
除了著色劑外,若可做為一般化妝材料原料來使用,則不特別受限於板狀、紡錘狀、針狀等形狀、微粒子級等的粒子徑、多孔質、無孔質等粒子結構等,舉出無機粉末類、氧化鋁、氧化鈰、氧化鎂、氧化鋯、碳酸鎂、碳酸鈣、矽酸鋁、矽酸鎂、矽酸鋁鎂、雲母、合成雲母、合成絹雲母、絹雲母、滑石、高嶺土、二氧化矽、碳化矽、氮化硼等無機粉末類、硬脂酸鎂、硬脂酸鋅、N-醯基離胺酸、尼龍等有機粉末類,可以使用這些之中的一種或兩種以上。
又,這些粉末也可以用一種或兩種以上的複合化物,其表面處理也可以施加油劑處理、有機矽化合物處理、水溶性聚合物處理等。
做為油劑,舉出固體油、半固體油、液體油等,例示有天然動植物及半合成油、烴油、酯油、甘油酯油、矽油、高級醇、高級脂肪酸,有機溶劑等。
做為固體油,可例示巴西棕櫚蠟、小燭樹蠟、棉蠟、蟲膠蠟、硬化油等天然蠟類、地石蠟、純地蠟、固體石蠟、微晶蠟等礦物類蠟、聚乙烯蠟、費托蠟、乙烯-丙烯共聚物等合成蠟、二十二醇、鯨蠟醇、硬脂醇、膽固醇、植物甾醇等高級醇、硬脂酸、山嵛酸等高級脂肪酸等。
在液體油中,做為天然動植物油及半合成油,具體舉出酪梨油、亞麻子油、巴丹杏油(almond oil)、蟲蠟、紫蘇油、橄欖油、香茅油、肝油、杏仁油(apricot kernel oil)、小麥胚芽油、芝麻油、米胚芽油、米糠油、山茶花油、紅花油、九重桐油、肉桂油、龜油、大豆油、茶籽油、山茶油、月見草油、玉米油、菜籽油、日本桐油、核果蠟、胚芽油、桃仁油、棕櫚油、棕櫚仁油、蓖麻油、向日葵油、葡萄油、荷荷巴油、澳洲堅果油、棉籽油、椰子油、三椰子油脂肪酸甘油酯、花生油、羊毛脂、液體羊毛脂、還原羊毛脂、羊毛脂醇、羊毛脂乙酸酯、羊毛脂脂肪酸異丙酯、POE羊毛脂醇醚、POE羊毛脂乙酸酯、羊毛脂脂肪酸聚乙二醇、POE氫化羊毛脂醇醚、蛋黃油等。
做為烴油,舉出角鯊烷、角鯊烯、液體石蠟、姥鮫烷、聚異丁烯等。
做為酯油,舉出己二酸二異丁酯、己二酸2-己基癸酯、己二酸二-2-庚基十一烷基酯、N-烷基甘油單異硬脂酸酯、異硬脂酸異鯨蠟酯、三羥甲基丙烷三異硬脂酸酯、2-乙基己酸鯨蠟酯、二-2-乙基己酸乙二醇、二-2-乙基己酸新戊二醇、三-2-乙基己酸三羥甲基丙烷、四-2-乙基己酸季戊四醇、辛酸鯨蠟酯、辛基十二烷基膠酯、油酸油醇酯、油酸辛基十二烷基酯、油酸癸酯、新戊二醇二癸酸酯、
檸檬酸三乙酯、琥珀酸2-乙基己酯、乙酸戊酯、乙酸乙酯、乙酸丁酯、異鯨蠟醇硬脂酸酯、硬脂酸丁酯、癸二酸二異丙酯、癸二酸二-2-乙基己酯、乳酸鯨蠟酯、乳酸肉荳蔻酯、棕櫚酸異丙酯、棕櫚酸2-乙基己酯、棕櫚酸2-己基癸酯、棕櫚酸2-庚基十一烷基酯、膽固醇12-羥基硬脂酸酯、二季戊四醇脂肪酸酯、肉荳蔻酸異丙酯、肉荳蔻酸2-辛基十二烷基酯、肉荳蔻酸2-己基癸酯、肉荳蔻酸肉荳蔻酯、二甲基辛酸己基癸酯、月桂酸乙酯、月桂酸己酯、N-月桂醯-L-麩胺酸-2-辛基十二烷基酯、蘋果酸二異硬脂酯等。
做為甘油酯油,舉出醋酸甘油酯、三異辛酸甘油酯、三異硬脂酸甘油酯、三異棕櫚酸甘油酯、三-2-乙基己酸甘油酯、單硬脂酸甘油酯、二-2-庚基十一烷酸甘油酯、三肉荳蔻酸甘油酯等。
做為矽油,舉出二甲基聚矽氧烷、甲基苯基聚矽氧烷、甲基氫聚矽氧烷、八甲基環四矽氧烷、十甲基環戊矽氧烷、十二甲基環六矽氧烷、四甲基四氫環四矽氧烷、烷基改性聚矽氧烷等。
做為高級醇,舉出油醇、月桂醇、硬脂醇、異硬脂醇、2-辛基十二烷醇等。
做為高級脂肪酸,舉出油酸、棕櫚酸、肉荳蔻酸、硬脂酸、異硬脂酸等。
做為有機溶劑,舉出正己烷、環己烷等烴、苯、甲苯、二甲苯等芳香族化合物、乙酸乙酯、乙酸丁酯等非芳香族化合物、氯仿、二氯甲烷、二氯乙烷等氯類化合物、二噁烷、四氫呋喃等醚類化合物、2-丙醇、苯甲醇、苯氧乙醇、卡必醇、賽珞蘇、錠子油等。
做為醇類,具體例示有乙醇、異丙醇等低級醇、甘油、雙甘油、聚甘油、二甘醇、聚乙二醇、丙二醇、二丙烯甘醇、聚丙烯甘醇、1,3-丁二醇、赤蘚糖醇等多元醇、山梨糖醇,麥芽糖,木糖醇、麥芽糖醇等糖醇、苯甲醇等。
做為美容成分,舉出熊果苷、穀胱甘肽、虎耳草提取物等美白劑、蜂王漿、光敏劑、膽固醇衍生物、幼牛血提取物等細胞活化劑、皮膚粗糙改善
劑、天竺葵酸香蘭基醯胺、菸酸芐酯、菸酸β-丁氧基乙酯、辣椒素、薑油酮、斑蝥酊(Cantharides tincture)、魚石脂、咖啡因、單寧酸、α-冰片、生育酚菸酸酯、肌醇六菸酸酯、環扁桃酯、桂利嗪、妥拉蘇林、乙醯膽鹼、維拉帕米、千金藤素、γ-榖維素等血液循環促進劑、氧化鋅、鞣酸等皮膚收斂劑、硫磺、THIATROL®等抗皮脂漏劑等。
做為防腐劑、抗菌劑,舉出對羥基苯甲酸酯、苯甲酸、苯甲酸鈉、山梨酸、山梨酸鉀、苯氧乙醇、水楊酸、碳酸、4-氯-3-甲基苯酚、六氯酚、氯化苯二甲羥銨、氯己定氯化物、三氯碳醯苯胺、光敏劑、異丙基甲基苯酚等。
做為香料,有天然香料(動物性香料、植物性香料)、合成香料、以及調合香料(天然香料與合成香料的混合物),對於目前的美容產品,最常使用天然香料與合成香料混合的調合香料。做為香料,舉出例如茉莉、孔雀草、迷迭香、香草、薑油、玫瑰油、茉莉花油、薰衣草油、依蘭油、薄荷油、老鸛草油、檸檬油、橙油、八角茴香油、葡萄柚油、按樹油、檀香油、黑胡椒油、羅勒油、廣藿香油、香豆素、麝香酮、向日花香醛、1-辛烯-3-醇以及這些的混合物等。
做為抗氧化劑,舉出生育酚、丁基羥基茴香醚、二丁基羥基甲苯等,做為pH調節劑,舉出乳酸、乳酸鹽、檸檬酸、檸檬酸鹽、乙醇酸、琥珀酸、酒石酸、蘋果酸、碳酸鉀、碳酸氫鈉、碳酸氫銨等,做為螯合劑,舉出丙氨酸、依地酸鈉鹽、聚磷酸鈉、偏磷酸鈉、磷酸鹽、羥基乙二胺三磷酸酯等,做為清涼劑,舉出L-薄荷醇、樟腦、薄荷油、胡椒薄荷油、尤加利樹油等,做為抗炎劑,舉出尿囊素、甘草次酸鹽、甘草次酸衍生物、傳明酸、甘菊藍等。
做為維生素類,舉出維生素A油、視黃醇、視黃醇乙酸酯、視黃醇棕櫚酸酯等維生素A類、核黃素、核黃素四丁酸酯、黃素腺嘌呤核苷酸等維生素B2類、鹽酸吡哆醇、二辛酸吡哆醇酯等維生素B6類、L-抗壞血酸、L-抗壞血酸二棕櫚酸酯、L-抗壞血酸-2-硫酸鈉、dl-α-生育酚-L-抗壞血酸磷酸二酯二鉀等
維生素C類、泛酸鈣、D-泛醇、泛醯基乙醚、乙醯基泛基乙基醚等泛酸類、麥角鈣化醇、膽鈣化醇等維生素D類、菸酸、菸酸芐酯、菸酸醯胺等菸酸類、dl-α-生育酚、dl-α-生育酚乙酸酯、dl-α-生育酚菸酸酯、dl-α-生育酚琥珀酸酯等維生素E類、維生素P、生物素等。
做為胺基酸,舉出精胺酸,天門冬胺酸、胱胺酸、半胱胺酸、蛋胺酸、絲胺酸、亮胺酸、異亮胺酸、色胺酸、丙胺酸、甘胺酸、脯胺酸等,做為核酸,舉出去氧核糖核酸等,做為激素,舉出雌二醇、乙炔雌二醇等。
本發明的聚氨酯凝膠組合物也可以藉由被覆於粉末表面來做為表面處理劑來製造表面處理粉末(以下稱為「聚氨酯凝膠處理粉末」)。做為以本發明的聚氨酯凝膠組合物被覆處理的粉末,若為一般用於化妝材料的粉體,則可以是球狀、板狀、針狀等形狀或煙霧狀、微粒狀、顏料級等的粒子徑或多孔質、無孔質等粒子結構等,沒有特別限定,可使用一種或兩種以上的無機粉末類、光澤粉末類、有機粉末類、色素粉末類、複合粉末類等。
做為前述無機粉末類,可從氧化鈦、黑色氧化鈦、氧化鋅、普魯士藍、群青藍、紅丹、黃色氧化鐵、黑色氧化鐵、氧化鋅、氧化鋁、氧化矽、氧化鎂、氧化鋯、碳酸鎂、碳酸鈣、氧化鉻、氫氧化鉻、炭黑、矽酸鋁、矽酸鎂、矽酸鎂鋁、雲母、合成雲母、絹雲母、滑石、高嶺土、碳化矽、硫酸鋇、膨土、膨潤石,氮化硼等選出一種或兩種以上來使用。此外,也可以使用製備成約10~100nm的微粒子。
做為光澤粉末類,可從氯氧化鉍、氧化鈦被覆的雲母、氧化鐵被覆的雲母、氧化鐵被覆的雲母鈦、有機顏料被覆的雲母鈦、氧化鈦被覆的玻璃粉末以及鋁粉等選擇一種或兩種以上來使用。
做為前述有機粉末類,可從尼龍粉末、聚甲基丙烯酸甲酯粉末、丙烯腈-甲基丙烯酸共聚物粉末、二氯亞乙烯-甲基丙烯酸共聚物粉末、PET樹脂
粉末、聚乙烯粉末、聚苯乙烯粉末、有機聚矽氧烷彈性體粉末、聚甲基倍半矽氧烷粉末、聚氨酯粉末、羊毛粉末、絲粉末、結晶纖維素粉末及N-醯基離胺酸粉末等選出一種或兩種以上來使用。
做為前述色素粉末,可從有機焦油類顏料、有機色素的色澱顏料等選出一種或兩種以上來使用。
做為前述複合粉末,可從微粒子氧化鈦被覆的雲母鈦、微粒子氧化鋅被覆的雲母鈦、硫酸鋇被覆的雲母鈦、含氧化鈦的二氧化矽、含氧化鋅的二氧化矽等選擇一種或兩種以上來使用。
在這些之中,特別是做為被覆處理的粉末,較佳者為無機質粉末的氧化鈦、紅丹、滑石、絹雲母及雲母。由於這些粉末廣泛用於化妝材料,並大量含有,所以藉由被覆處理這些粉末,可在使用於化妝材料時發揮顯著的效果。
做為將上述聚氨酯凝膠被覆處理在這些粉末的方法,沒有特別限定,通常以已知方法來製造。例如舉出將聚氨酯凝膠與粉末直接混合的方法(乾式處理法)、使用溶劑的方法(濕式法)等。在這些之中,從獲得均勻且使用感優越的聚氨酯凝膠粉末來看,使聚氨酯凝膠分散於溶劑的分散液與粉末混煉後,蒸發除去溶劑使其完全乾燥的濕式法為較佳,再者藉由粉碎此,可製造更均勻且使用感優越的聚氨酯凝膠處理粉末。粉碎方法也沒有特別限定。做為前述溶劑來使用的化合物,若可分散聚氨酯凝膠則沒有特別限制,但可例示水、乙醇、正丙基醇、異丙醇、正己烷、異鏈烷烴、苯、甲苯等,可使用一種或兩種以上。從獲得更均勻且使用感優越的聚氨酯凝膠處理粉末來看,較佳為使用一種或兩種以上的異丙醇和正己烷。
又,前述聚氨酯凝膠處理粉末,在化妝材料基材的分散性改良、觸感改良等目的,也可以進一步被覆處理,矽酮化合物、氟化合物、油劑、油脂、高級醇、蠟、聚合物、樹脂等通常已知表面處理劑來使用。
前述聚氨酯凝膠處理粉末是以聚氨酯凝膠處理粉末處理粉末表面者,並在粉末表面存在有聚氨酯凝膠。雖然其被覆量沒有特別限定,但從更顯著地發揮本發明的效果的觀點來看,以被覆處理粉末的總質量為基準,較佳為0.1至10質量%。做為在此範圍所包含的被覆量,例示有0.1~10質量%、0.1~7.5質量%、0.1~5質量%、0.5~10質量%、0.5~7.5質量%、0.5~5質量%、1~10質量%、1~7.5質量%、1~5質量%、2~10質量%、2~7.5質量%、2~5質量%、3~10質量%、3~7.5質量%以及3~5質量%。
根據一般方法,可以藉由將一種或兩種以上的前述聚氨酯凝膠處理粉末與已知的化妝材料成分組合使用,來製造化妝材料。雖然在前述化妝材料中的該處理粉末的含量沒有特別限制,依化妝材料的劑型而不同,但為1~99質量%,較佳為5~95質量%。又,使用前述聚氨酯凝膠處理粉末的化妝材料可以在以粉末為主要成分的粉末化妝材料中發揮顯著的效果,在此情況下為1~70質量%,較佳為5~50質量%,特佳為10~30質量%。
在包含前述聚氨酯凝膠處理粉末的化妝材料中,可以根據需要適當使用可含有的成分。
例如,可以適當使用上述揮發性組分、界面活性劑、油劑、粉末、水性成分、醇類、水溶性聚合物、紫外線吸收劑、保濕劑、膠凝劑及增稠劑、防褪色劑、抗氧化劑、消泡劑、美容成分(美白劑、細胞活化劑、抗炎劑、血液循環促進劑、皮膚收斂劑、抗皮脂劑等)、防腐劑、抗菌劑、香料、維生素類、胺基酸類、核酸、激素等為了賦予各種效果而用於一般化妝品的其他成分。
根據一般方法,可以藉由將本發明的聚氨酯凝膠組合物與已知的化妝材料成分組合使用,來製造化妝材料。前述化妝材料中的該聚氨酯凝膠組合物的含量沒有特別限定,依化妝材料的劑型而不同,但為0.1~99質量%,較佳為1~95質量%。
在包含前述聚氨酯凝膠組合物的化妝材料中,可以根據需要適當使用可含有的成分。
例如,做為如此成分,例示有前述揮發性成分、界面活性劑、油劑、粉末、水性成分、醇類、水溶性聚合物、紫外線吸收劑、保濕劑、膠凝劑及增稠劑、防褪色劑、抗氧化劑、消泡劑、美容成分(美白劑、細胞活化劑、抗炎劑、血液循環促進劑、皮膚收斂劑、抗皮脂劑等)、防腐劑、抗菌劑、香料、維生素類、胺基酸類、核酸、激素等。
本發明的聚氨酯凝膠組合物可以使用於製造各種劑型,例如液狀、乳液狀、乳膏狀、固體狀、糊狀、凝膠狀、粉末狀、壓製狀、多層狀、慕絲狀、噴霧狀或棒狀等劑型的化妝材料。又,本發明的聚氨酯凝膠組合物可使用於製造以各種適用部位為對象的化妝材料、例如臉部化妝材料、皮膚保養化妝材料、頭髮化妝材料、止汗劑、或紫外線防護用化妝材料等的化妝材料等。
做為含有本發明的聚氨酯凝膠組合物的化妝材料用品,例示有化妝水、乳液、精華液、泥敷劑、全效凝膠、乳霜、身體乳液、卸粧油、卸粧乳、防曬乳等基礎化妝材料、定型液、髮蠟等頭髮用化妝材料、睫毛膏、唇彩、唇膏、眼影、眼線、粉底、腮紅、遮瑕膏、化妝底霜等。
以下舉出實施例更詳細地說明本發明。再者,這些完全不限定本發明。
雖然以下的製造實施例1~5皆關於組合物2,但藉由以末端羥基氫化聚丁二烯取代末端具有異氰酸基的氫化聚丁二烯,也相同於使用組合物1的情況來製造聚氨酯凝膠。
具體如下所述。即,在組合物2的聚氨酯,是以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯。對此,在組合物1的聚氨酯,是將組合物2的(c)末端具有羥基的氫化聚丁二烯取代成(a)末端具有異氰酸基的氫化聚丁二烯,以(a)氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯。在此情況下,在這種情況下,可使(a)與(b)的莫耳比相同於(c)與(b)的莫耳比來製造相同的聚氨酯。
實施例
[製造實施例1]
將末端羥基化氫化聚丁二烯899份(分子量2200)、2-乙基己酸十六烷酯2450份、六亞甲基二異氰酸酯128份裝入3L的三口燒瓶中,均勻混合。
控制在60℃並投入二月桂酸二丁基錫0.9份,攪拌3小時後,投入聚乙二醇24份。
投入結束後,在將80℃攪拌5小時後,加入乙醇18份使反應完成。
所得聚氨酯凝膠中聚氨酯的重量平均分子量,以GPC測量(按聚苯乙烯計)為10000。此外,將獲得的凝膠30份與液體石蠟70份在85℃加熱溶解,冷卻至30℃的凝膠的負重值,以負重測量機(FUDOH製造)進行以2cm/min使2cmφ球形適配器穿透10mm的條件時下為2.50N。
[製造實施例2]
將末端羥基化氫化聚丁二烯899份(分子量2200)、2-乙基己酸十六烷酯2450份、六亞甲基二異氰酸酯128份裝入3L的三口燒瓶中,均勻混合。
控制在60℃並投入二月桂酸二丁基錫0.9份,攪拌3小時後,投入聚乙二醇24份。
投入結束後,在將80℃攪拌10小時後,加入乙醇18份使反應完成。
所得聚氨酯凝膠中聚氨酯的重量平均分子量,以GPC測量(按聚苯乙烯計)為50000。此外,將獲得的凝膠30份與液體石蠟70份在85℃加熱溶解,冷卻至30℃的凝膠的負重值,以負重測量機(FUDOH製造)進行以2cm/min使2cmφ球形適配器穿透10mm的條件時下為5.00N。
[製造實施例3]
將末端羥基化氫化聚丁二烯899份(分子量2200)、2-乙基己酸十六烷酯2450份、六亞甲基二異氰酸酯128份裝入3L的三口燒瓶中,均勻混合。
控制在60℃並投入二月桂酸二丁基錫0.9份,攪拌3小時後,用2-乙基己酸十六烷基酯稀釋,並投入聚乙二醇24份。
投入結束後,在將80℃攪拌15小時後,加入乙醇18份使反應完成。
所得聚氨酯凝膠中聚氨酯的重量平均分子量,以GPC測量(按聚苯乙烯計)為100000。此外,將獲得的凝膠30份與液體石蠟70份在85℃加熱溶解,冷卻至30℃的凝膠的負重值,以負重測量機(FUDOH製造)進行以2cm/min使2cmφ球形適配器穿透10mm的條件時下為7.50N。
[製造實施例4]
在3L的三口燒瓶中加入末端羥基氫化聚丁二烯899份(分子量2200)、乙二醇24份、二月桂酸二丁基錫0.9份、2-乙基己酸十六烷基酯2450份,均勻混合。
控制在60℃並投入六亞甲基二異氰酸酯128份,投入結束後以80℃攪拌10小時,之後加入乙醇18份使反應完成。
所得聚氨酯凝膠中聚氨酯的重量平均分子量,以GPC測量(按聚苯乙烯計)為50000。此外,將獲得的凝膠30份與液體石蠟70份在85℃加熱溶解,冷卻至30℃的凝膠的負重值,以負重測量機(FUDOH製造)進行以2cm/min使2cmφ球形適配器穿透10mm的條件時下為3.00N。
[製造實施例5]
在3L的三口燒瓶中加入末端羥基氫化聚丁二烯899份(分子量2200)、乙二醇24份、二月桂酸二丁基錫0.9份、2-乙基己酸十六烷基酯2450份,均勻混合。
控制在60℃並投入六亞甲基二異氰酸酯128份,投入結束後以80℃攪拌15小時,之後加入乙醇18份使反應完成。
所得聚氨酯凝膠中聚氨酯的重量平均分子量,以GPC測量(按聚苯乙烯計)為100000。此外,將獲得的凝膠30份與液體石蠟70份在85℃加熱溶解,冷卻至30℃的凝膠的負重值,以負重測量機(FUDOH製造)進行以2cm/min使2cmφ球形適配器穿透10mm的條件時下為4.50N。
[製造比較例1]
使用100份交聯矽酮凝膠(KSG-43,信越化學工業公司製造)。
[製造比較例2]
將糊精脂肪酸酯(Leopard ISK,千葉製粉公司製造)35份與2-乙基己酸十六烷基酯65份,在90℃下加熱、冷卻,製備多醣類凝膠。
[製造比較例3]
將結晶聚乙烯蠟(PERFORMALENE 655,New Phase Technology Co.,Ltd製造)35份與2-乙基己酸十六烷基酯65份,在90℃下加熱、冷卻,製備蠟油凝膠。
[測試例1]
[凝膠的評估]
從以前述製法獲得的聚氨酯凝膠中,對於製造實施例2的聚氨酯凝膠,評估對於通常用於化妝品的各種油劑的負重值、以及關於凝膠的透明性。結果如表1所示。又,各種評估方法如下。
[負重值的測量和評估]
將製造實施例2的聚氨酯凝膠與表1所記載的各種油劑在85℃下加熱溶解,冷卻至30℃,製成彈性凝膠。關於凝膠的負重值,使用負重測量機(由FUDOH公司製造),以2cm/min使2cmφ球形適配器穿透10mm的條件來測量。實施例1
~4的結果可以確認,分子中的羥基數越少的油劑,有負重值越高的傾向。這是因為油劑中的羥基影響聚氨酯凝膠的親水基團締合增稠機制中的親水基團部分,導致黏度降低。
[透明性的測量和評估]
對於表1所記載的各種凝膠的透明性,是使用透射率測定儀(由島津製作所公司製造)測量在700nm的透射率。結果,在實施例1~6的所有凝膠中表示出90%以上的良好透明性(A)。
[自恢復力的測量和評估]
使用製造實施例2的聚氨酯凝膠及製造比較例2的糊精脂肪酸酯凝膠,評價自我復原力。測量樣本的各純度為10.5質量%,以2-乙基己酸十六烷基酯稀釋,在85℃下加熱後,流入廣口容器,藉由冷卻至30℃製備彈性凝膠。對於製備完的樣本,使用質構分析儀(英榮精機公司製造),以2cmφ球形適配器從施加5g負重時,在1mm/min的速度,穿透5mm的條件下,重複相同的操作7次,確認負重不會破壞凝膠結構,且具有復原力。測量示意圖如第1圖所示。其結果(第2圖)可知,製造比較例2的糊精脂肪酸酯凝膠在重複的負重下凝膠結構破壞,不是相同的曲線,製造實施例2的聚氨酯凝膠是在重複的負重下凝膠不崩壞,達到相同的曲線,所以知道凝膠的復原性高。此外,由於負重值本身的值,高於製造比較例2的糊精脂肪酸酯凝膠,所以知道彈性優越。
根據上述研究可知,本發明的聚氨酯凝膠組合物是透明性、高彈性優越,且自恢復力優越的高新穎性凝膠。
[測試例2]
[凝膠的評估]
如表2所示,除了末端羥基氫化聚丁二烯、六亞甲基二異氰酸酯、2-乙基己酸十六烷基酯以及乙二醇的各成分的配合比例變化以外,與製造實施例2同樣地
操作,製造實施例6~16的聚氨酯凝膠。評估關於這些聚氨酯凝膠的負重值及透明度。結果顯示在表2中。為了參考,製造實施例2的聚氨酯凝膠的資料也示於表2。評估方法如下所述。
[負重值的測量和評估]
將表2所記載的各製造實施例的聚氨酯凝膠30份與液體石蠟70份,在85℃下加熱溶解,冷卻至30℃的凝膠負重值,使用負荷測量裝置(FUDOH公司製造),使用2cmφ球形適配器、2cm/min、10mm穿透的條件測量。評估是根據以下標準進行。
A:4.50N以上
B:2.50N以上,未滿4.50N
C:0.50N以上,未滿2.50N
D:小於0.50N
[透明性的測量和評估]
表2所記載的聚氨酯凝膠的透明性是使用透射率測量儀器(島津製作所公司製造),測量在700nm的透射率。評估是根據以下基準進行。
A:90%以上
B:85%以上,未滿90%
C:80%以上,未滿85%
D:少於80%
關於製造實施例2、6~16所得到的聚氨酯凝膠,從表2可以說明以下內容。
(c):(b)的莫耳比((c)/(b)的莫耳比率)較佳為2:3~3:2(0.66~1.5)。
A(聚氨酯)的含量(質量%),較佳為1~35質量%,B(2-乙基己酸十六烷基酯(油劑))的含量(質量%),較佳為65~99質量%。
[油性身體保養油的實施例1~7及比較例1~5]
表3所示的組成的油性身體保養油,藉由以下製造方法製備,以下述評估方法來評估各樣本為關於「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」,其結果也顯示在表3。
[製造方法]
(1)將成分1~16在分散液均勻混合。
(2)將成分17添加到(1),經除氣並填充到容器,獲得油型身體保養油。
[評估]
對於實施例1~7,及比較例1~5的油性型身體保養油,化妝品專業評估小組20人,各自根據以下的評估基準進行七階段評估關於「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」的各項目,進一步使用全組評估平均分數,根據以下判斷基準來判斷。
[評估基準]
(評估結果):(評分)
非常好:6分
好:5分
略好:4分
正常:3分
稍差:2分
缺陷:1分
非常糟:0分
[判斷基準]
(評分的平均分數):(判斷)
5.0以上:A
3.5以上未滿5.0:B
1.5以上未滿3.5:C
未滿1.5:D
實施例1~7的油性型身體保養油是伸展度優異性、彈力感、光澤感、無黏性、化妝持續效果優越的油性型身體保養油。與實施例1~7的油性型身體保養油相比,已確認比較例1~5的油性型身體保養油分別在以下幾點較差。比較例1的油性型身體保養油,其交聯型有機矽凝膠的彈性與透明性低,特別是彈力感、光澤感差,又,比較例2的油性型身體保養油,其糊精脂肪酸酯的多醣類凝膠的透明性相對較高,但有醣類特有的黏感,且彈性低,伸展性差、在彈力感、無黏性方面差。再者,比較例3的油性型身體保養油,其蠟油凝膠的透明性感、彈力感差且硬,所以伸展度差,光澤感也差。使用聚氨酯粉末與多醣凝膠的比較例4的油性型身體保養油來取代本發明的聚氨酯凝膠,伸展度與黏性不足,彈力感、光澤感及化妝持續效果差。此外,使用聚氨酯粉末代替本發明的聚氨酯凝膠的比較例5,聚氨酯粉末會沉澱,難以進行評估。
實施例8:乳液型化妝水
(製法)
(1)將成分1~6加熱至75℃,均勻混合溶解。
(2)將成分7、8加熱至75℃,均勻混合溶解。
(3)將(2)加入(1)並乳化。
(4)將(3)冷卻,加入成分9,獲得乳液型化妝水。
實施例8的乳液型化妝水是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的乳液型化妝水。
實施例9 乳液
(製法)
(1)將成分1~7加熱至80℃,均勻混合。
(2)將成分8~14加熱至80℃,均勻混合。
(3)將(2)加入(1)並乳化。
(4)將(3)攪拌並冷卻,獲得乳液。
實施例9的乳液是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的乳液。
實施例10 O/W型乳膏
(製法)
(1)將成分1~6加熱至80℃,均勻混合。
(2)將成分7~12加熱至80℃,均勻混合。
(3)將(2)加入(1)並乳化。
(4)將(3)攪拌並冷卻,獲得乳膏。
實施例10的O/W型乳膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的O/W型乳膏。
實施例11 W/O型乳膏
(製法)
(1)將成分1~7加熱至75℃,均勻混合溶解。
(2)將成分8、11加熱至75℃,均勻混合溶解。
(3)將(2)加入(1)並乳化。
(4)將(3)冷卻,添加成分9、10,獲得W/O型乳膏。
實施例11的W/O型乳膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的W/O型乳膏。
實施例12 卸粧油
(製法)
(1)將成分1~7在室溫下均勻混合,獲得卸粧油。
實施例12的卸粧油是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的卸粧油。
實施例13 卸粧乳
(製法)
(1)將成分1~7加熱至80℃,均勻混合。
(2)將成分8~13加熱至80℃,均勻混合。
(3)將(2)加入(1)並乳化。
(4)將(3)攪拌並冷卻,獲得卸粧乳。
實施例13的卸粧乳是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的卸粧乳。
實施例14 定型液
(製法)
(1)將成分1~9在室溫下均勻混合,獲得定型液。
實施例14的定型液是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的定型液。
實施例15 髮蠟
(製法)
(1)將成分1~3在80℃下均勻混合。
(2)將成分4~8在80℃下均勻混合。
(3)將(2)加入(1)並乳化。
(4)在(3)中添加成分9~15後,攪拌並冷卻,得到髮蠟。
實施例15的髮蠟是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的髮蠟。
實施例16 O/W型睫毛膏
(製造方法)
(1)將成分1~3在80℃下均勻混合。
(2)用滾筒處理成分4~8。
(3)將成分9~14在80℃下均勻混合。
(4)混合(1)、(2)後,加入(3)並乳化。
(5)將(4)冷卻,獲得O/W型睫毛膏。
實施例16的O/W型睫毛膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的O/W型睫毛膏。
實施例17 糊狀唇彩
(註11)ANTARON V-220(ISP公司製造)
(註12)AEROSIL 200(日本Aerosil公司製造)
(製法)
(1)在100℃下熔融混合成分1~9。
(2)在(1)中添加成分10~18,均勻混合分散。
(3)將(2)倒入管中並冷卻,獲得糊狀唇彩。
實施例17的糊狀唇彩是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的糊狀唇彩。
實施例18 棒狀唇膏
(製法)
(1)將成分1~7在100℃均勻溶解混合。
(2)將成分8~13加入(1)並均勻混合。
(3)將(2)倒入容器並冷卻,獲得棒狀唇膏。
實施例18的棒狀唇膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的棒狀唇膏。
實施例19 油性眼影
(製法)
(1)在100℃下溶解混合成分1~9。
(2)在(1)中添加成分10~18,均勻混合分散。
(3)將(2)倒入容器,冷卻固化來獲得油性眼影。
實施例19的油性眼影是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的油性眼影。
實施例20 固體粉末狀粉底
(製法)
(1)在亨舍爾混合機(三井三池公司製造)75℃下將成分1~9均勻分散。
(2)將成分10~13均勻混合溶解。
(3)以亨舍爾混合機攪拌(1),並加入(2)與成分14,均勻分散。
(4)以粉碎機粉碎(3)。
(5)將(4)填充在金屬皿,壓縮成型,獲得固體粉末狀粉底。
實施例20的固體粉末狀粉底是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的固體粉末狀粉底。
實施例21 固體粉末狀眼影
(製法)
(1)在亨舍爾混合機(三井三池公司製造)75℃下將成分1~9均勻分散。
(2)將成分10~13均勻混合溶解。
(3)以亨舍爾混合機攪拌(1),並加入(2)及成分14,均勻分散。
(4)以粉碎機粉碎(3)。
(5)將(4)填充在金屬皿,壓縮成型,獲得固體粉末狀眼影。
實施例21的固體粉末狀眼影是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的固體粉末狀眼影。
實施例22 固體粉末狀腮紅
(製法)
(1)在亨舍爾混合機(三井三池公司製造)75℃下將成分1~7均勻分散。
(2)將成分8~11加熱到65℃,均勻混合溶解。
(3)以亨舍爾混合機攪拌(1),並加入(2)及成分12,均勻分散。
(4)以粉碎機粉碎(3)。
(5)將(4)填充在金屬皿,壓縮成型,獲得固體粉末狀腮紅。
實施例22的固體粉末狀腮紅是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的固體粉末狀腮紅。
實施例23 棒狀遮瑕膏
(製法)
(1)在100℃下混合溶解成分1~8。
(2)在(1)中將成分9~14於90℃下均勻混合。
(3)以3個滾筒處理(2)。
(4)將(3)除氣,在85℃下溶解填充至膠囊後,冷卻至4℃,得到棒狀遮瑕膏。
實施例23的棒狀遮瑕膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的棒狀遮瑕膏。
實施例24 W/O型防曬材料
(製法)
(1)將成分3、4加熱溶解後,添加成分1、2,以滾筒均勻分散。
(2)在70℃下使成分5~10溶解後,在60℃添加(1),均勻混合溶解。
(3)使成分11~13混合溶解後,在60℃下添加到(2)並乳化。
(4)將成分14、15加入(3)並均勻混合,獲得W/O型防曬材料。
實施例24的W/O型防曬材料是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的W/O型防曬材料。
實施例25 W/O型粉底
(註16)KF-6026(信越化學工業公司製造)
(註17)KF-6015(信越化學工業公司製造)
(製法)
(1)將成分1~3均勻混合。
(2)以滾筒將成分4~11均勻分散。
(3)將(2)加入(1),均勻混合。
(4)在(3)中添加成分12~16並乳化,得到W/O型粉底。
實施例25的W/O型粉底是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的W/O型粉底。
實施例26 O/W型粉底
(製法)
(1)以滾筒將成分1~8均勻分散。
(2)將成分9~12均勻混合。
(3)將(1)加入(2)並均勻混合。
(4)在80℃下混合溶解成分13~20。
(5)在80℃下將(4)加入(3)並乳化。
(6)將(5)冷卻,添加成分21,得到O/W型粉底。
實施例26的O/W型粉底是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的O/W型粉底。
實施例27 油性固體粉底
(製法)
(1)將成分7~14在90℃下加熱溶解。
(2)將成分1~6添加到(1),以滾筒均勻分散。
(3)將成分15添加到(2),在80℃下溶解後,填充於金屬皿,獲得油性固體粉底。
實施例27的油性固體粉底是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的油性固體粉底。
實施例28 化妝底霜
(製法)
(1)在80℃下均勻溶解成分1~4。
(2)在80℃下均勻溶解成分5~13。
(3)將(1)加入(2)並乳化。
(4)將成分14加入(3)並冷卻,獲得化妝底霜。
實施例28的化妝底霜是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的化妝底霜。
實施例29 身體乳液
(製法)
(1)在80℃均勻溶解成分1~7。
(2)在80℃均勻溶解成分8~16。
(3)將(1)加入(2)並乳化。
(4)將(3)攪拌、冷卻,獲得身體乳液。
實施例29的身體乳液是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的身體乳液。
實施例30 卸妝劑
(製法)
(1)將成分1~4均勻混合。
(2)在60℃下將成分5~8添加到(1)並乳化。
(3)攪拌(2)並冷卻,獲得卸妝劑。
實施例30的卸妝劑是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的卸妝劑。
實施例31 非水性睫毛膏
(製法)
(1)加熱成分1~5至110℃。
(2)將成分6~10加入(1)並混合。
(3)將成分11~13加入(2)並混合。
(4)以滾筒處理(3),獲得非水性睫毛膏。
實施例31的非水性睫毛膏是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的非水性睫毛膏。
實施例32 油性眼線筆
(製法)
(1)將成分1~5加熱至100℃,均勻混合。
(2)將成分6~9加熱至80℃,均勻混合。
(3)將(2)加入(1)並均勻混合。
(4)以滾筒處理(3),獲得油性眼線筆。
實施例32的油性眼線筆是「伸展度優異性」、「彈力感」、「光澤感」、「無黏性」、「化妝持續效果」優異的油性眼線筆。
產業利用性
因為本發明的聚氨酯凝膠組合物,提供在透明性、光澤亮度、彈力性及復原力的任一點都極為優越的油溶性凝膠膜,所以是特別在化妝材料的技術領域極為有用的發明。
Claims (10)
- 一種聚氨酯凝膠組合物,包含A與B,其中A是以(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,或A是以(c)末端具有羥基的氫化聚丁二烯、(d)二異氰酸酯化合物與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇反應所獲得的聚氨酯,B是油劑,且A的聚氨酯的含有量為1~35質量%,B的油劑的含有量為65~99質量%。
- 如申請專利範圍第1項所述的組合物,其中A的聚氨酯的平均分子量(Mw)是10000~100000。
- 如申請專利範圍第1項所述的組合物,其中B的油劑是從烴油、羥基數為0或1的酯油及矽油中任選一種以上。
- 如申請專利範圍第1項所述的組合物,其中將如申請專利範圍第1項所述的聚氨酯凝膠組合物30質量份與液體石蠟70質量份在85℃加熱溶解,冷卻得到的凝膠,以2cm/min使2cm φ球形適配器穿透10mm時的負重值為0.20~10.00N。
- 如申請專利範圍第1項所述的組合物,具有凝膠復原性。
- 一種化妝材料,包含如申請專利範圍第1項至第6項中任一項所述的組合物。
- 一種聚氨酯凝膠組合物的製造方法,該聚氨酯凝膠組合物包含A與B(在此,A是聚氨酯,B是油劑),其步驟包含:在B的油劑中,添加以A的(a)末端具有異氰酸基的氫化聚丁二烯與(b)HO-R3-OH(式中,R3表示可具有醚鍵的直鏈或分歧的C2~C6亞烷基)所表示的二元醇,進行加成聚合反應,且A的聚氨酯的含有量為1~35質量%,B的油劑的含有量為65~99質量%。
- 如申請專利範圍第8項所述的製造方法,其中A的聚氨酯的平均分子量(Mw)是10000~100000。
- 如申請專利範圍第7項所述之化妝材料,其中前述化妝材料是選自眼影、粉底、底霜、防曬乳、唇膏以及睫毛膏所成群組。