CN113416293B - 一种高拉伸性能医用水凝胶及其制备方法和应用 - Google Patents
一种高拉伸性能医用水凝胶及其制备方法和应用 Download PDFInfo
- Publication number
- CN113416293B CN113416293B CN202110583440.4A CN202110583440A CN113416293B CN 113416293 B CN113416293 B CN 113416293B CN 202110583440 A CN202110583440 A CN 202110583440A CN 113416293 B CN113416293 B CN 113416293B
- Authority
- CN
- China
- Prior art keywords
- polyurethane
- hydrogel
- reaction
- sdpu
- double bonds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种高拉伸性能医用水凝胶及其制备方法和应用，属于高分子材料制备技术领域。本发明首先制备出侧链含双键的聚氨酯(SDPU)，再利用巯基与双键的点击化学反应制备高拉伸性能聚氨酯水凝胶。该水凝胶通过侧链的双键形成三维网络的交联位点，交联密度高，能够提供良好的力学性能。此外，该水凝胶的力学性能可以通过调节软硬段之间的比例来进行调控。同时，该聚氨酯水凝胶的软段和交联剂基于聚乙二醇分子链段，硬段可以降解为赖氨酸，具有较高的生物相容性，从而可作为医用软体组织的填充材料，因此具有良好的实际应用之价值。
Description
技术领域
本发明属于高分子材料制备技术领域，具体涉及一种高拉伸性能医用水凝胶及其制备方法和应用。
背景技术
公开该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不必然被视为承认或以任何形式暗示该信息构成已经成为本领域一般技术人员所公知的现有技术。
水凝胶是一类由亲水性高分子或聚合物形成的高含水量软材料,能够模拟细胞外基质的三维微环境,对细胞行为、组织功能进行调控,在生物医学工程领域有广泛的应用前景。
现有技术中，采用两步自由基聚合的方法合成了化学交联DN水凝胶。该DN水凝胶已被证明具有一定的力学强度和较高的断裂伸长率(典型的断裂拉伸强度高于1MPa，断裂伸长率在1000％～2000％范围内)，与软骨或橡胶的性能相当。
现有技术中也公开了一种高强度海藻酸钠水凝胶，该水凝胶是利用海藻酸盐分子和共聚物链上丰富的羧基与多价金属离子的高配位能力，采用“一步法”离子双交联制备而成，同时该离子双交联高强度水凝胶还具有高的含水量(76％)。
聚甲基丙烯酸-2-羟基乙酯(英文简称PHEMA)凝胶材料是由甲基丙烯酸-2-羟基乙酯单体为主组成的共聚物水凝胶，但由于其具有较差的力学强度、渗透性不足以及吸水能较弱等劣势，使其应用受到了一定的限制。而发明人发现，目前常用的增强凝胶材料的方法为化学交联，但制备过程复杂，工艺要求较高，不易工业化生产。
发明内容
针对上述现有技术的不足，本发明提供一种高拉伸性能医用水凝胶及其制备方法和应用。本发明首先制备出侧链含双键的聚氨酯(SDPU)，再利用巯基与双键的点击化学反应制备高拉伸性能聚氨酯水凝胶。该水凝胶通过侧链的双键形成三维网络的交联位点，交联密度高，能够提供良好的力学性能。此外，该水凝胶的力学性能可以通过调节软硬段之间的比例来进行调控。同时，该聚氨酯水凝胶的软段和交联剂基于聚乙二醇分子链段，硬段降解产物为赖氨酸，具有较高的生物相容性，从而可作为医用软体组织的填充材料，因此具有良好的实际应用之价值。
具体的，本发明采用如下技术方案：
本发明的第一方面，提供一种侧链含双键的聚氨酯，其分子结构式如下所示：
其中，m，n均取自不为0的自然数；
进一步的，m＝69～206；n＝8～21。
本发明的第二方面，提供上述侧链含双键的聚氨酯的制备方法，所述制备方法包括：
将二异氰酸酯、聚乙二醇、1,5-己二烯-3,4-二醇溶于有机溶剂进行催化升温反应后即得侧链含双键的聚氨酯(SDPU)。
本发明的第三方面，提供上述侧链含双键的聚氨酯在制备高拉伸性能聚氨酯医用水凝胶中的应用。
本发明的第四方面，提供一种高拉伸性能聚氨酯医用水凝胶，所述高拉伸性能聚氨酯医用水凝胶，其制备方法包括：将上述SDPU和巯基封端的多臂聚乙二醇溶于水中，在催化剂作用下通过点击化学反应经交联获得。
本发明制得的水凝胶交联密度高，形成的分子网络大小统一，受力时能够均匀受力，有优异的拉伸性能，同时也具有良好韧性；经试验验证，上述水凝胶的拉伸性能的断裂强度大于15MPa，断裂伸长率大于180％；因此，本发明的第五方面，提供上述水凝胶在生物医学工程领域中的应用。
上述一个或多个技术方案的有益技术效果：
(1)上述技术方案制备水凝胶的反应条件温和，制备简单，产率高。
(2)上述技术方案提供的聚氨酯水凝胶主要由聚氨酯链段和聚乙二醇链段组成，均具有良好的生物相容性，其最终的降解产物可被人体吸收或代谢出体外，具有良好的生理可接受性。
(3)上述技术方案提供的水凝胶为全合成产物，无生物源性。
(4)上述技术方案提供的水凝胶交联密度高，形成的分子网络大小统一，受力时能够均匀受力，有优异的拉伸性能，同时也具有良好韧性，因此具有良好的实际应用之价值。
附图说明
构成本发明的一部分的说明书附图用来提供对本发明的进一步理解，本发明的示意性实施例及其说明用于解释本发明，并不构成对本发明的不当限定。
图1为本发明实施例中聚乙二醇、1,5-己二烯-3,4-二醇比例对水凝胶SDPU-W1、SDPU-W4和SDPU-W5拉伸性能的影响。
图2为本发明实施例中不同臂数巯基封端聚乙二醇交联剂对水凝胶SDPU-W1、SDPU-W6、SDPU-W7拉伸性能的影响。
图3为本发明实施例中水凝胶SDPU-W1、SDPU-W4、SDPU-W5的提取物中细胞存活率情况。
具体实施方式
应该指出，以下详细说明都是例示性的，旨在对本申请提供进一步的说明。除非另有指明，本文使用的所有技术和科学术语具有与本申请所属技术领域的普通技术人员通常理解的相同含义。
需要注意的是，这里所使用的术语仅是为了描述具体实施方式，而非意图限制根据本申请的示例性实施方式。如在这里所使用的，除非上下文另外明确指出，否则单数形式也意图包括复数形式，此外，还应当理解的是，当在本说明书中使用术语“包含”和/或“包括”时，其指明存在特征、步骤、操作、器件、组件和/或它们的组合。
如前所述，目前常用的增强凝胶材料的方法为化学交联，但制备过程复杂，工艺要求较高，不易工业化生产。
有鉴于此，本发明的一个典型具体实施方式中，提供一种侧链含双键的聚氨酯，其分子结构式如下所示：
其中，m，n均取自不为0的自然数；
优选的，m＝69～206；n＝8～21。
本发明的又一具体实施方式中，提供上述侧链含双键的聚氨酯的制备方法，所述制备方法包括：
将二异氰酸酯、聚乙二醇、1,5-己二烯-3,4-二醇溶于有机溶剂进行催化升温反应后即得侧链含双键的聚氨酯(SDPU)。
本发明的又一具体实施方式中，所述二异氰酸酯为脂肪族二异氰酸酯；进一步优选为赖氨酸二异氰酸酯。
本发明的又一具体实施方式中，上述反应中的聚乙二醇的分子量控制为3000～9000g/mol。
本发明的又一具体实施方式中，上述反应中催化剂可以为锡类催化剂，包括但不限于二丁基锡二月桂酸酯、辛酸亚锡、二醋酸二丁基锡；
为了进一步提高反应速率，并降低反应成本，控制催化剂的用量为单体总质量的0.1-0.5％。
本发明的又一具体实施方式中，上述反应中的有机溶剂可以是N,N-二甲基甲酰胺(DMF)；所述有机溶剂的用量控制为每1mL有机溶剂溶解0.5-1g总反应物。
经试验证明，当1,5-己二烯-3,4-二醇的含量越高时，所制备的水凝胶强度越大，最大可达18MPa。这是因为1,5-己二烯-3,4-二醇的含量增加时，双键的含量也随之增加，极大的增加了其交联作用位点，从而使之形成交联网络更加稳定的聚合物。故可以通过调节聚乙二醇与1,5-己二烯-3,4-二醇之间的摩尔比来控制水凝胶的强度。在本发明的又一具体实施方式中，上述反应中的1,5-己二烯-3,4-二醇与聚乙二醇的摩尔比为1:0.5-1:1。
本发明的又一具体实施方式中，上述反应中加入二异氰酸酯的用量为-NCO与-OH的摩尔比为1:1。
本发明的又一具体实施方式中，上述反应的反应温度为65-80℃，进一步优选为70-75℃。
本发明的又一具体实施方式中，上述反应的反应时间约2-4h；具体的，反应终点红外光谱检测-NCO的特征吸收峰消失为止。
本发明的又一具体实施方式中，反应结束后经提纯后获得SDPU，所述提纯具体方法为：使用DMF将含SDPU溶液稀释至0.1～0.2g/mL，然后冰乙醚进行沉降，抽滤，常温真空干燥至恒重。
本发明的又一具体实施方式中，提供上述侧链含双键的聚氨酯在制备高拉伸性能聚氨酯医用水凝胶中的应用。
本发明的又一具体实施方式中，提供一种高拉伸性能聚氨酯医用水凝胶，所述高拉伸性能聚氨酯医用水凝胶，其制备方法包括：将上述SDPU和巯基封端的多臂聚乙二醇溶于水中，在催化剂作用下通过点击化学反应经交联获得。
本发明的又一具体实施方式中，上述反应中的巯基封端多臂聚乙二醇包括4arm-PEG-SH、6arm-PEG-SH、8arm-PEG-SH，其分子量分别为2000-5000、2000-10000、2000-20000g/mol；需要说明的是，相同分子量的八臂巯基聚乙二醇相比较于六臂和四臂巯基聚乙二醇提供的交联点更多，聚乙二醇的分子链更短，经过双键与巯基的交联作用，增加了水凝胶网络交联密度，从而增强了分子链之间的链缠结作用，从而可以使水凝胶能承受更大的压力。
本发明的又一具体实施方式中，上述反应中选用的催化剂为有机碱催化剂，所述有机碱催化剂包括N,N-二异丙基丙胺，所述有机碱催化剂用量为反应物总质量的0.05-0.5％，优选为0.1％。
本发明的又一具体实施方式中，上述反应中加入巯基封端多臂聚乙二醇中的巯基与SDPU的双键的摩尔比为1:1。
本发明的又一具体实施方式中，上述反应中SDPU和巯基封端多臂聚乙二醇在去离子水中的总浓度控制为15wt％-35wt％。
本发明的又一具体实施方式中，上述点击反应的反应温度可以为常温，具体的，反应温度为20-30℃。
本发明的又一具体实施方式中，上述反应中反应时间控制为约2-3h，具体的，反应终点为红外光谱检测双键的特征吸收峰消失为止(～1630cm-1)。
本发明制得的水凝胶交联密度高，形成的分子网络大小统一，受力时能够均匀受力，有优异的拉伸性能，同时也具有良好韧性；经试验验证，上述水凝胶的拉伸性能的断裂强度大于15MPa，断裂伸长率大于180％；同时水凝胶具有良好的生物相容性和生物可降解性，降解产物无毒可吸收或代谢；因此，本发明的又一具体实施方式中，提供上述水凝胶在生物医学工程领域中的应用。
具体的，所述应用包括水凝胶作为体内植入材料(如医用软体填充材料)中的应用。
以下通过实施例对本发明做进一步解释说明，但不构成对本发明的限制。应理解这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，45g聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.059g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.1g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU1)。
水凝胶的制备：将20g SDPU1和10.24g 4arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.03g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W1)
实施例2
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，75g聚乙二醇(5000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.089g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.15g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU2)。
水凝胶的制备：将20g SDPU2和6.77g 4arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.027g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W2)
实施例3
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，105g聚乙二醇(7000g/mol)，3.42g1,5-己二烯-3,4-二醇和0.119g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.1g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU3)。
水凝胶的制备：将20g SDPU3和5.06g 4arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.027g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W3)
实施例4
聚氨酯的制备：将11.31g赖氨酸二异氰酸酯，60聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.075g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.15g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU4)。
水凝胶的制备：将20g SDPU4和8.03g 4arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.028g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W4)
实施例5
聚氨酯的制备：将13.57g赖氨酸二异氰酸酯，90g聚乙二醇(5000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.11g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.1g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU5)。
水凝胶的制备：将20g SDPU5和5.61g 4arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.027g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W5)
实施例6
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，45g聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.089g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.15g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU6)。
水凝胶的制备：将20g SDPU6和6.83g 6arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.027g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W6)
实施例7
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，45g聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.089g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至80℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3h；再加入DMF稀释至0.1g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU7)。
水凝胶的制备：将20g SDPU7和5.12g 8arm-PEG-SH(2000g/mol)溶于400mL去离子水后，在0.025g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W7)
实施例8
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，45g聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.059g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至80℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3h；再加入DMF稀释至0.1g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU8)。
水凝胶的制备：将20g SDPU8和20.48g 4arm-PEG-SH(4000g/mol)溶于400mL去离子水后，在0.04g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W8)
实施例9
聚氨酯的制备：将10.18g赖氨酸二异氰酸酯，45g聚乙二醇(3000g/mol)，3.42g 1,5-己二烯-3,4-二醇和0.059g辛酸亚锡溶于200mL N,N-二甲基甲酰胺(DMF)中，油浴加热至75℃恒温反应至用为红外光谱检测-NCO的特征吸收峰消失为止，约3.5h；再加入DMF稀释至0.15g/mL,然后用十倍体积的冰乙醚(-6-1℃)进行沉降，抽滤，常温真空干燥至恒重，得到侧链含双键的聚氨酯(SDPU9)。
水凝胶的制备：将20g SDPU9和30.72g 4arm-PEG-SH(6000g/mol)溶于400mL去离子水后，在0.05g N,N-二异丙基丙胺的催化下常温反应至检测红外光谱中双键的特征吸收峰消失，约24h，交联得到聚氨酯水凝胶(SDPU-W9)。
效果验证
拉伸性能测试：采用万能力学实验机对水凝胶试样进行拉伸强度测试。试样规格：宽6.0mm、厚1.2mm、长度30mm，测试标距为15mm；测试条件：室温，拉伸速率为50mm/min。韧性是由应力应变曲线所围成的面积。
细胞毒性测试：将水凝胶用紫外光灭菌2h，然后浸于提取完全的DMEM培养基中两天。以DMEM和L929小鼠成纤维细胞分别作为空白对照和模型细胞。将含提取物的DMEM与成纤维细胞在37℃下孵育3d，孵育期结束后用MTT法检测细胞活力。用酶联免疫检测仪检测在570nm波长处的光吸收值，可间接反映活细胞数量。
细胞存活率＝(A1/A2)×100％
A1为提取物处理细胞的吸光度值；A2为对照细胞的吸光度值
为了探究聚乙二醇、1,5-己二烯-3,4-二醇之间的比例对水凝胶强度的影响，对SDPU-W1、SDPU-W4、SDPU-W5分别进行拉伸性能测试。结果如图1所示，由此可知，当1,5-己二烯-3,4-二醇的含量越高时，所制备的水凝胶强度越大，最大可达18MPa。这是因为1,5-己二烯-3,4-二醇的含量增加时，双键的含量也随之增加，极大的增加了其交联作用位点，从而使之形成交联网络更加稳定的聚合物。因此，可以通过调节聚乙二醇与1,5-己二烯-3,4-二醇之间的摩尔比来控制水凝胶的强度。
为了探究多巯基化合物对水凝胶强度的影响，对SDPU-W1、SDPU-W6和SDPU-W7进行拉伸性能测试。其测试结果如图2所示，可以发现，所制备的水凝胶最大拉伸强度很高，均大于15MPa，相比较之前文献报道的水凝胶强度更高，此外，水凝胶SDPU-W1、SDPU-W6、SDPU-W7的拉伸强度从16.4MPa增加至20MPa，断裂伸长率依次从350％降低至180％。这是因为在相同分子量的情况下，八臂巯基聚乙二醇相比较于六臂和四臂巯基聚乙二醇提供的交联点更多，聚乙二醇的分子链更短，经过双键与巯基的交联作用，增加了水凝胶网络交联密度，从而增强了分子链之间的链缠结作用，使水凝胶能承受更大的压力。
分别对水凝胶SDPU-W1、SDPU-W4、SDPU-W5进行细胞毒性测试，其测试结果如图3所示，可以发现，水凝胶对细胞无明显毒性，其细胞存活率均能达到90％以上，其细胞存活率都很高，按照国标GB/T16886.20-2015规定，细胞毒性为一级，适用于体内植入材料。此外，尽管不同水凝胶之间己二烯二醇的含量不同，但其细胞存活率在相同浓度下均无明显差异，表明己二烯二醇的含量对细胞存活率影响甚低。
以上所述仅为本申请的优选实施例而已，并不用于限制本申请，对于本领域的技术人员来说，本申请可以有各种更改和变化。凡在本申请的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本申请的保护范围之内。
Claims (18)
1.一种侧链含双键的聚氨酯在制备高拉伸性能聚氨酯医用水凝胶中的应用，其特征在于，所述侧链含双键的聚氨酯的分子结构式为：
其中，m，n均取自不为0的自然数。
2.如权利要求1所述的应用，其特征在于，m=69~206；n=8~21。
3.如权利要求1或2所述的应用，其特征在于，所述侧链含双键的聚氨酯的制备方法包括：
将二异氰酸酯、聚乙二醇、1,5-己二烯-3,4-二醇溶于有机溶剂进行催化升温反应后即得侧链含双键的聚氨酯SDPU。
4.如权利要求3所述的应用，其特征在于，所述聚乙二醇的分子量控制为3000~9000 g/mol；或，
反应中催化剂为锡类催化剂，包括二丁基锡二月桂酸酯、辛酸亚锡和二醋酸二丁基锡；
或，所述有机溶剂为N,N-二甲基甲酰胺。
5.如权利要求3所述的应用，其特征在于，所述二异氰酸酯为赖氨酸二异氰酸酯。
6.如权利要求4所述的应用，其特征在于，所述锡类催化剂的用量为单体总质量的0.1-0.5％。
7.如权利要求3所述的应用，其特征在于，所述有机溶剂的用量控制为每1mL有机溶剂溶解0.5-1g总反应物。
8.如权利要求3所述的应用，其特征在于，所述1,5-己二烯-3,4-二醇与聚乙二醇的摩尔比为1:0.5-1:1；或，
上述反应中加入二异氰酸酯的用量为-NCO与-OH的摩尔比为1:1，或，
反应温度为65-80℃；或，反应时间控制为2-4h。
9.如权利要求3所述的应用，其特征在于，制备侧链含双键的聚氨酯的反应温度为70-75℃。
10.如权利要求3所述的应用，其特征在于，制备侧链含双键的聚氨酯的反应终点为红外光谱检测-NCO的特征吸收峰消失为止。
11.如权利要求3所述的应用，其特征在于，反应结束后经提纯后获得SDPU。
12.如权利要求11所述的应用，其特征在于，所述提纯具体方法为：使用DMF将含SDPU溶液稀释至0.1~0.2g/mL，然后冰乙醚进行沉降，抽滤，常温真空干燥至恒重。
13.一种高拉伸性能聚氨酯医用水凝胶，其特征在于，所述高拉伸性能聚氨酯医用水凝胶，其制备方法包括：将SDPU和巯基封端的多臂聚乙二醇溶于水中，在催化剂作用下通过点击化学反应经交联获得。
14.如权利要求13所述的高拉伸性能聚氨酯医用水凝胶，其特征在于，所述巯基封端的多臂聚乙二醇包括4arm-PEG-SH、6arm-PEG-SH、8arm-PEG-SH，其分子量分别为2000-5000、2000-10000、2000-20000 g/mol；或，
选用的催化剂为有机碱催化剂，所述有机碱催化剂包括N,N-二异丙基丙胺，所述有机碱催化剂用量为反应物总质量的0.05-0.5%；或，
加入巯基封端多臂聚乙二醇中的巯基与SDPU的双键的摩尔比为1:1；或，
上述反应中SDPU和巯基封端多臂聚乙二醇在去离子水中的总浓度控制为15-35wt%；或，上述反应的反应温度为常温；或，上述反应中反应时间控制为2-3h。
15.如权利要求14所述的高拉伸性能聚氨酯医用水凝胶，其特征在于，所述有机碱催化剂用量为反应物总质量的0.1%。
16.如权利要求13所述的高拉伸性能聚氨酯医用水凝胶，其特征在于，所述高拉伸性能聚氨酯医用水凝胶制备的反应温度为20-30℃。
17.如权利要求13所述的高拉伸性能聚氨酯医用水凝胶，其特征在于，所述高拉伸性能聚氨酯医用水凝胶制备的反应终点为红外光谱检测双键的特征吸收峰~1630 cm-1消失为止。
18.权利要求13-17任一项所述的高拉伸性能聚氨酯医用水凝胶在制备体内植入材料中的应用。