TWI363251B - Sublayer coating-forming composition for lithography containing compound having protected carboxy group - Google Patents

Sublayer coating-forming composition for lithography containing compound having protected carboxy group Download PDF

Info

Publication number
TWI363251B
TWI363251B TW093122593A TW93122593A TWI363251B TW I363251 B TWI363251 B TW I363251B TW 093122593 A TW093122593 A TW 093122593A TW 93122593 A TW93122593 A TW 93122593A TW I363251 B TWI363251 B TW I363251B
Authority
TW
Taiwan
Prior art keywords
group
formula
compound
polymer
film
Prior art date
Application number
TW093122593A
Other languages
English (en)
Other versions
TW200506540A (en
Inventor
Satoshi Takei
Takahiro Kishioka
Yasushi Sakaida
Tetsuya Shinjo
Original Assignee
Nissan Chemical Ind Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissan Chemical Ind Ltd filed Critical Nissan Chemical Ind Ltd
Publication of TW200506540A publication Critical patent/TW200506540A/zh
Application granted granted Critical
Publication of TWI363251B publication Critical patent/TWI363251B/zh

Description

1363251 (1) 九、發明說明 【發明所屬之技術領域】 本發明爲有關新穎之微影成像用下層膜形成組成物, 使用該組成物所形成之下層膜,及使用該下層膜之光阻圖 型之形成方法的發明。又,本發明爲有關於製造半導體裝 置之微影成像步驟中,對塗佈於半導體基板上之光阻層進 行曝光照射時,作爲降低基板之反射的下層反射防止膜, 作爲使凹凸之半導體基板平坦化所使用之平坦化膜,及作 爲於加熱燒培時等防止由半導體基板產生之物質污染光阻 層所使用之膜等用途之微影成像用下層膜,及形成該下層 膜所使用之下層膜形成組成物及下層膜之形成方法發明。 又,本發明爲有關嵌埋半導體基板所形成之通孔時所使用 之微影成像用下層膜形成組成物。 【先前技術】 以往於半導體裝置之製造過程中,多使用光阻以微影 成像進行微細加工處理。前述微細加工爲於矽晶圓等半導 體基板上形成作爲光阻之薄膜,並於其上方介由描繪有半 導體裝置圖型之光罩而照射紫外線等活性光線,將顯像所 得之光阻圖型作爲保護膜,而對基板進行蝕刻處理所得之 於基板表面形成對應於前述圖型之微細凹凸的加工方法。 但,近年來,隨半導體裝置之高度集積化,所使用之活性 光線已有由 KrF電漿雷射( 24 8nm)傾向 ArF電漿雷射 (193 nm )之短波長的趨勢。隨著前述趨向,活性光線對 -5- (2) (2)1363251 基板所產生之散射或駐波(Standing Wave )之影響則產 生極大之問題。而爲解決此問題,對於光阻與基板間設置 反射防止膜(Bottom Anti-Reflective Coating,BARC ) 之方法已引起廣泛的硏討。前述反射防止膜,就使用之容 易度等,至吸光性物質與高分子化合物等所得之有機反射 防止膜等已有進行多數之硏討,例如提出使用於同一分子 內具交聯反應基之羥基與吸光基之酚醛淸漆樹脂型反射防 止膜等(例如,專利文獻1、專利文獻2 )。 有機反射膜所被要求之特性,例如對於光或放射線應 具有較大之吸光度、光阻層不會產生內缺陷(不溶於光阻 溶劑)、加熱燒培時反射防止膜不會將低分子物質擴散至 上層之光阻、與光阻相比較時具有較大之乾蝕刻速度等 (例如,非專利文獻 1、非專利文獻 2、非專利文獻 3 ) ° 又,近年來,爲解決隨著半導體裝置圖型線路微細化 所產生之電路延遲等問題,則開始硏究使用銅作爲電路材 料,並同時使用雙嵌刻製程(Dual Damascene Process)形 成通孔,而於具有較大長徑比之基板上形成反射防止膜。 因此,對於此步驟所使用之反射防止膜,常被要求通孔之 嵌埋必須具有無間隙之塡充特性,或基板面必須具有可形 成平坦膜之平坦化特性。 但是一般而言,因將有機系反射防止膜用材料使用於 具有較大長徑比之基板上爲極困難者,所以近年來,已積 極以嵌埋特性或平坦化特性爲重點之材料(例如,專利文 -6 - (3) (3)!363251 獻3、專利文獻4、專利文獻5、專利文獻6 )。 又,於半導體等裝置之製造中,爲降低介電體層對光 阻層所產生之毒害效果,則有提出於介電體層與光阻層之 間設置由含可交聯之聚合物等之組成物所形成之阻隔層的 方法(例如,專利文獻7 )。 如此,於近年來的半導體裝置之製造中,由達到防止 反射之效果開始,至欲達成各種效果時,多於半導體基板 與光阻層之間,即於光阻層之下層,多配置有由含有有機 化合物之組成物所形成之有機系之下層膜。 因下層膜多要求應具有不會產生內部缺陷之特性,故 下層膜之形成多利用交聯反應所得者。又,前述爲形成交 聯性下層膜所使用之組成物,多使用交聯劑與作爲交聯觸 媒之磺酸化合物所形成者(例如,專利文獻1、專利文獻 3、專利文獻4、專利文獻6)。但,因包含磺酸化合物等 強酸,故此組成物於保存安定性上則仍存在有問題。 因此,目前極需一種利用無須強酸觸媒之交聯反應所 形成之下層膜,及所使用之組成物。 其中’目前已知可利用無需強酸觸媒之交聯系統者, 例如反射防止膜用之組成物(例如,專利文獻8、專利文 獻9、專利文獻1 0、專利文獻1 1 )。 〔專利文獻1〕美國專利5 9 1 9 5 9 9號 〔專利文獻2〕美國專利5 6 9 3 6 9 1號 〔專利文獻3〕特開2000-294504號 〔專利文獻4〕特開2002-47430號 (4) (4)1363251 〔專利文獻5〕特開2002-190519號 〔專利文獻6〕國際公開0 2/05 03 5號 〔專利文獻7〕特開2 002-128847號 〔專利文獻8〕美國專利6686124號 〔專利文獻9〕特開2001 - 1 924 1 1號 〔專利文獻10〕特開2000-264921號 〔專利文獻1 1〕特開平7-3 1 6268號 〔專利文獻1〕美國專利第5919599號 〔非專利文獻 1〕Tom Lynch 等 3 名「Properties and Performance of Near U V Reflectivity Control Layers」,(美國),in Advances in Resist Technology and Processing XI > Omkaram Nalamasu 編,Proceedings of SPIE,1 994 年,第 2195 卷(Vol.2195),p.22 5-229 〔非專利文獻 2〕 G Taylor 等 13 名, 「Methacrylate Resist and A n t i r e f 1 e c t i v e Coatings for 193nm Lithography」,(美國),in Microlithography 1 999 : Advances in Resist Technology an d Processing XVI, Will Cnnley 編,Proceedings of SPIE,1 999 年,第 3 678 巻(V〇1.3678),p.174-185 〔非專利文獻 3〕Jim D. Meador 等 6 名,「Recent Progress in 1 93nm Antireflective Coatings j ,(美國),in Micro lithography 1999 : Advances in Resist Technology and Processing XVI,Will Conley 編,Prnceedings of SPIE,I 999 年,第 3 678 巻(Vol.3 678), p.800-809 1363251
【發明內容】
本發明之目的爲提供一種半導体裝置製造用微影成像 用下層膜形成組成物。其不會與上層塗佈、形成之光阻層 產生內部缺陷,且具有較光阻層爲更快之乾蝕刻速度之微 影成像用下層膜與形成該下層膜所使用之微影成像用下層 膜形成組成物。又,本發明復提供一種無需利用強酸觸媒 之交聯反應所形成之下層膜、該下層膜之形成方法及形成 該下層膜所使用之下層膜形成組成物。
又’本發明之另一目的,爲提供一種於製造半導體裝 置之微影成像步驟中,對塗佈於半導體基板上之光阻層進 行曝光照射時,作爲降低基板之反射的下層反射防止膜, 作爲使具有凹凸之半導體基板平坦化之平坦化膜,及作爲 於加熱燒培時等防止由半導體基板產生之物質污染光阻層 所使用之膜等之微影成像用下層膜,及形成該下層膜所使 用之下層膜形成組成物。並提供一種使用下層膜形成組成 物之微影成像用下層膜之形成方法,及光阻圖型之形成方 法發明。 基於前述現狀,本發明者們經過深入硏究結果,得知 使用含有具被保護之羧基的化合物與可與羧基反應之基的 化合物時,或使用含有具被保護之羧基與可與羧基反應之 基的化合物時,即可形成具有前述特徵之下層膜,因而完 成本發明。 本發明之第1觀點,即爲一種微影成像用下層膜形成 -9- (6) (6)1363251 組成物,其特徵爲,含有式(1)所示具被保護之羧基的 化合物、可與羧基反應之基的化合物,及溶劑; —C一〇一έ一〇一R4 (1)
II I Ο Η0—R3 (式中,與r3各自表示氫原子或碳原子數1 至10之烷基,R4爲碳原子數1至10之烷基,又,R3與 R4可相互鍵結形成環)。 第2觀點爲,一種微影成像用下層膜形成組成物,其 特徵爲,含有可與羧基反應之基與式(1)所示具被保護 之羧基的化合物,及溶劑。 第3觀點爲,於第1觀點或第2觀點之下層膜形成組 成物中,可與羧基反應之基爲由環氧基、環氧丙烷基、噁 唑基、環碳酸酯基、烷氧基矽烷基、胺基羥甲基、氮雜環 丙烷基、羥甲基、羥基、異氰酸酯基、烷氧基甲基胺基、 及羥基矽烷基所成群中所選出者。 第4觀點爲,於第1觀點之下層膜形成組成物中,前 述含有式(1)所示具被保護之羧基的化合物爲包含式 (2)所示單位構造之聚合物; (7) 1363251 Μ—C一Ο—0—0—R4 (2)
II I Ο Η0—R3 r2 (式中,L爲構成聚合物主鏈之鍵結基,Μ爲直接鍵 結或連結基)。 第5觀點爲,於第1觀點之下層膜形成組成物中,前 述含有式(1)所示具被保護之羧基的化合物爲,至少含 有2個式(1)所示具被保護之羧基,且分子量爲200至 2000之化合物。 第6觀點爲,於第1觀點之下層膜形成組成物中,前 述含有可與羧基反應之基的化合物,爲至少含有2個式 (3 )所示基之化合物; Ν—C~0—R6 (3) r5H2 [式中,R5爲氫原子、碳原子數1至6之烷基或· CH2OR7 (式中,R7爲氫原子或碳原子數1至]0之烷 基),IU爲氫原子或碳原子數1至10之烷基]。 第7觀點爲,於第1觀點之下層膜形成組成物中,前 述含有可與羧基反應之基的化合物,爲含有由式(4)、 式(5)、式(6)、式(7)、式(8)與式(9)所成群 中所選出之至少1種單位構造之聚合物; -11 - (8) 1363251 2 2 Η Η CIC一 r H CIO /I ) -PIQ(4
I 一 \—/ -PIQ(6
ο ο Λ
Q—N=C=0 q (8) Rii—C—CHo
I I H2〇~0 (9) (式中,P爲構成聚合物主鏈之鍵結基,Q爲直接鍵 結或連結基’ Rs、R9' Rig與Rii各自表示氫原子或碳原 子數1至10之院基,X爲0或1)。 第8觀點爲,於第2觀點之下層膜形成組成物中,前 述含有可與羧基反應之基與式(1)所示具被保護之羧基 的化合物,爲含有由式(2)所示單位構造’與式(4)、 式(5)、式(6)、式(7)、式(8)與式(9)所成群 中所選出之至少1種單位構造之聚合物。 第9觀點爲,於第2觀點之下層膜形成組成物中,前 述含有可與羧基反應之基與式(1)所示具被保護之羧基 的化合物,爲含有式(10)與式(11)所示單位構造之聚 合物; -12- (9) 1363251
R2—C—C—Ri CH2 R3 〇 R14—C-(CH2)y R4 H2C—〇
(10) (11) (式中,r12與r13各自表示氫原子或甲基,r14爲氫 原子、甲基或乙基,y爲〇或1,31與32爲構成聚合物之 各單位構造的莫耳比,s!爲0.05至0.95,s2爲0.05至 0.95 )。
第1 0觀點爲,於第2觀點之下層膜形成組成物中, 前述含有可與羧基反應之基與式(1)所示具被保護之羧 基的化合物,爲含有式(12)、式(13)與式(1〇所示 單位構造之聚合物; -13- 1363251 do) 十s2一 ^15十 S2—c4r c 〇 Η ? 〇 l 1 0 ^—C-C-R-i ?h2 | 9^2 r3〇 Ri4-C~(CH2)y 1 R16 r4 H2C—〇 (14) (12) (13) (式中,R1S爲氫原子或甲基,R|e爲氫原 子數1至6之烷基、苯基、萘基或蒽基,t|、t2 成聚合物之各單位構造的莫耳比,^爲0 05至 爲 0.05 至 0.90,t3 爲 0.05 至 〇.9〇)。 第1 1觀點爲’於第1至1 〇觀點中任—觀點 形成組成物中,尙含有吸光性化合物。 第12觀點爲,一種製造半導體裝置時所使 膜的形成方法,其特徵爲,將第1至11觀點中 之微影成像用下層膜形成組成物,塗佈、燒培於 板上之方法。 第13觀點爲,一種下層膜,其特徵爲,將| 觀點中任一觀點之微影成像用下層膜形成組成物 燒培於半導體基板上所得者。 第14觀點爲,一種製造半導體裝置時所使 圖型的形成方法,其特徵爲,包含將第〗至】1 -14- 子 '碳原 與t3爲構 0.90,t2 之下層膜 用之下層 任一觀點 半導體基 ! 1 至 1 1 ,塗佈、 用之光阻 觀點中任 (11) 1363251 一觀點之微影成像用下層膜形成組成物, 導體基板上以形成下層膜之步驟,於該1 層之步驟,對被覆有下層膜與光阻層之斗 光之步驟,及於曝光後進行顯影之步驟等 第15觀點爲,於第14觀點之光PI 中,則述曝光爲以波長248nm、193nm或 行。 〔發明效果〕 本發明爲有關一種利用無需使用強_ 所形成之下層膜,與形成該下層膜所使用 層膜形成組成物。 本發明之微影成像用下層膜形成組域 酸觸媒成分,故具有優良之保存安定性。 本發明之下層膜形成組成物爲使用晃 應以形成交聯構造之系統,因未含有以Q 聯劑或磺酸化合物等低分子化合物,故於 華物之量,且可避免因昇華物產生之微粒 導體基板或淸淨室。 使用本發明之微影成像用下層膜形成 不產生間隙下在通孔內部達成較高之塡充 有通孔之基板上塡平凹孔而達平坦化,而 於其上之光阻的膜厚均勻性。因此,即使 基板的步驟中,也可以形成具有良好平坦 塗佈、燒培於半 層膜上形成光阻 導體基板進行曝 〇 圖型的形成方法 1 57nm之光線進 觸媒之交聯反應 之微影成像用下 物,因未含有強 合物相互間之反 常用之低分子交 燒培中可減少昇 子或異物污染半 組成物時,可於 性。又,可於具 提昇塗佈、形成 使用具有通孔之 性之光阻圖型。 -15- (12) 1363251 本發明之微影成像用下層膜形成組成物,與 時具有更快之乾蝕刻速度,且與光阻間不會產 陷,故可提供一種具有優良性質之下層膜。 因此,本發明之下層膜,可作爲反射防止膜 膜與光阻層之污染防止膜使用。如此,可使製造 置中之微影成像步驟的光阻圖型之形成,得以更 精確的進行。 〔實施發明之最佳形態〕 本發明之微影成像用下層膜形成組成物爲 (1)所示具被保護之羧基的化合物、含有可與 之基的化合物,及溶劑。又,本發明之微影成像 形成組成物爲,含有可與羧基反應之基與式(1 被保護之羧基的化合物,及溶劑。又,本發明之 成組成物,可含有作爲任意成分之吸光性化合物 性劑等。 本發明之微影成像用下層膜形成組成物中固 比例’只要可使各成分均勻溶解時並未有特別限 0.1至70質量% ’又如0.5至50質量% ,又如 量% ’又如5至25質量% 。前述固體成分,爲 形成組成物之全部成分除以溶劑成分所得者。又 分中之含有式(1)所示具被保護之羧基的化合 可與羧基反應之基的化合物之比例爲70質量% 如80至】00質量% ,又如80至99質量% ,5 光阻比較 生內部缺 、平坦化 半導體裝 容易且更 ,含有式 羧基反應 用下層膜 )所示具 下層膜形 、界面活 體成分之 定,例如 1至30質 由下層膜 ,固體成 物及含有 以上,例 乙如90至 -16- (13) (13)1363251 99質量?6 。又’固體成分中之含有可與羧基反應之基與 式(1)所示具被保護之羧基的化合物之比例爲7〇質量% 以上,例如80至1〇〇質量% ,又如80至99質量% ,又 如90至99質量% 。 本發明之微影成像用下層膜形成組成物爲含有式 (1)所示具被保護之羧基的化合物、含有可與羧基反應 之基的化合物,及溶劑。 式(1)中,R丨、112與R3各自表示氫原子或碳原子 數1至10之烷基,R4爲碳原子數1至10之烷基,又, R3與R4可相互鍵結形成環。碳原子數1至1〇之烷基例 如甲基、乙基、正丁基、正辛基、異丙基、tert-丁基、2-乙基己基、環己基等。又,113與R4可相互鍵結形成環, 依此方式形成之環,例如四氫呋喃環、四氫吡喃環等。 含有式(1)所示具被保護之羧基的化合物,例如可 以使含有羧基之化合物與式(15)所示之乙烯基醚化合物 反應而製得。
含有羧基之化合物與乙烯基醚化合物之反應,例如可 依曰本接著學會誌第34卷(ν〇1·34) ,352-356頁所記載 之內容,使用磷酸作爲觸媒,於室溫下攪拌之方式進行。 式(15)所示之乙烯基醚化合物,例如甲基乙烯基 -17- (14) (14)1363251 醚、乙基乙烯基醚、異丙基乙烯基醚、正丁基乙烯基醚、 2-乙基己基乙烯基醚' tert-丁基乙烯基醚及環己基乙烯基 醚等脂肪族乙烯基醚化合物,或2,3·二氫呋喃、4-甲基-2,3-二氫呋喃、2,3·二氫-4H-呋喃等環狀乙烯基醚化合物 等。 可與式(15)所示之乙烯基醚化合物反應之含有羧基 之化合物,例如苯甲酸、異苯二甲酸、對苯二甲酸、均苯 四甲酸、1,2,4-偏苯三酸、己二酸、馬來酸、丁烷四羧 酸、三(2-羧基乙基)異氰酸酯、萘2-羧酸、萘-2,6·二羧 酸、帕蒙酸(pamoic acid)、宸-1-殘酸、1,6 -二溴-2 -徑 基萘-3-羧酸、1,1’-二萘-2,2’-二羧酸、蒽-9-羧酸、蒽-9,10-二羧酸、丙烯酸、甲基丙烯酸、馬來酸、依康酸' 戊二酸、1,2·環己烷二羧酸及1,2,3,4-環戊烷四羧酸等。 前述化合物所製得之含有式(1)所示具被保護之羧基的 化合物之分子量以200以上爲佳。分子量低於前述範圍 時,於進行燒培以形成下層膜時,極容易產生昇華等問 題。分子量例如200至2000,又如400至2000之範圍爲 佳》又’就含有式(1)所示具被保護之羧基的化合物可 形成堅固之下層膜之觀點而言,式(1)所示具被保護之 羧基以含有2個以上爲佳。 可與式(15)所示之乙烯基醚化合物反應之含有羧基 之化合物,又例如含有羧基之聚合物等。前述聚合物並未 有特別限定,例如含有具丙烯酸、甲基丙烯酸、乙烯基苯 甲酸與馬來酸等之含有羧基之加成聚合性單體作爲單位構 -18- (15) 1363251 造之聚合物等。
本發明中’含有式(1)所示具被保護之羧基的化合 物’又’例如含有式(2 )所示單位構造之聚合物等。式 中,L爲構成聚合物主鏈之鍵結基,μ爲直接鍵結或連結 基。L只要爲可構成聚合物主鏈之鍵結基時並未有特別限 定。Μ則例如含有由伸苯基、-C ( = 0 ) · ' -CH2-、-ΝΗ-及-Ο-中所選出之至少1個連結基之連結基或直接鍵結 等。 式(2 )所示單位構造,例如式(16 )至(20 )之構 造等。 -19- (16)1363251 ch3 η p 十 r H2 C-0-C-0-R4 2 C-0-C-0-R4
II I II I 〇 HC_R3 0 HC—R3 R2 R2 (16) (17)
H
(19)
C 一 0—C—〇一R4 II I 〇 HC—R3 (18)
Η H +十-〒十
0=C C—0_C—〇一R4 I II I Ο 〇 HC—R3 ch3 r2 (20) O HC—R3
II I H2C—C—O—0—O—R4 O R1 含有式(2)所示單位構造之聚合物,例如可以使含 有羧基之聚合物與式(15)所示之乙烯基醚化合物反應而 製得。 -20- (17) (17)1363251 含有式(2)所示單位構造之聚合物,又,例如可以 使含有式(1)所示具被保護之羧基之加成聚合性單體經 聚合反應而製得。含有式(1)所示具被保護之羧基之加 成聚合性單體,例如1-甲氧基乙基甲基丙烯酸酯、1-乙氧 基乙基甲基丙烯酸酯、1-異丙氧基乙基甲基丙烯酸酯、1-正己氧基乙基甲基丙烯酸酯、四氫- 2H -吡喃-2 -基-甲基丙 烯酸酯等甲基丙烯酸半縮醛酯化合物,1_甲氧基乙基丙烯 酸酯、Ι-tert· 丁氧基乙基丙烯酸酯、1-異丙氧基乙基丙烯 酸酯、1-正丁氧基乙基丙烯酸酯、四氫- 2H -吡喃-2-基·丙 烯酸酯等丙烯酸半縮醛酯化合物,1-乙氧基乙基-4·乙烯 基苯甲酸酯、雙(1-乙氧基乙基)馬來酸酯、及甲基(1-乙氧乙基)馬來酸酯等。 含有式(2)所示構造單位之聚合物的製造方法,可 爲僅使用1種上述加成聚合性單體,與將2種以上加成聚 合性單體組合使用等情形。 又,含有式(2)所示構造單位之聚合物的製造方 法,除使用含有式(1)所示具被保護之羧基之上述加成 聚合性單體以外,亦可與其他加成聚合性單體一起使用。 前述其他加成聚合性單體,例如丙烯酸酯化合物、甲基丙 烯酸酯化合物、丙烯醯胺化合物、甲基丙烯醯胺化合物、 乙烯基化合物 '苯乙烯化合物、馬來醯亞胺化合物、馬來 酸酐及丙烯腈等。 丙烯酸酯化合物例如,甲基丙烯酸酯、乙基丙烯酸 酯 '異丙基丙烯酸酯、苄基丙烯酸酯、萘基丙烯酸酯、蒽 -21 - (18) (18)1363251 基丙烯酸酯、蒽基甲基丙烯酸酯、苯基丙烯酸酯、2-羥基 乙基丙烯酸酯、2·羥基丙基丙烯酸酯、2,2,2·三氟乙基丙 烯酸酯、4-羥基丁基丙烯酸酯、異丁基丙烯酸酯、tert-丁 基丙烯酸酯、環己基丙烯酸酯、異甲醯基丙烯酸酯、2-甲 氧基乙基丙烯酸酯、甲氧基三乙二醇丙烯酸酯、2-乙氧基 乙基丙烯酸酯、四氫糠基丙烯酸酯、3-甲氧基丁基丙烯酸 酯、2-甲基·2-金剛烷基丙烯酸酯、2-乙基-2-金剛烷基丙 烯酸酯、2-丙基-2-金剛烷基丙烯酸酯、2-甲氧基丁基-2-金剛烷基丙烯酸酯、8 -甲基-8·三環癸基丙烯酸酯、8 -乙 基-8-三環癸基丙烯酸酯、及5-丙烯醯氧基-6-羥基原菠烯· 2-羧酸-6-內酯等。 甲基丙烯酸酯化合物例如,乙基甲基丙烯酸酯、正丙 基甲基丙烯酸酯、正戊基甲基丙烯酸酯、環己基甲基丙烯 酸酯、苄基甲基丙烯酸酯、萘基甲基丙烯酸酯、蒽基甲基 丙烯酸酯、蒽基甲基甲基丙烯酸酯' 苯基甲基丙烯酸酯、 2-苯基乙基甲基丙烯酸酯、2-羥基乙基甲基丙烯酸酯、2-羥基丙基甲基丙烯酸酯、2,2,2 -三氟乙基甲基丙烯酸酯' 2,2,2-三氯乙基甲基丙烯酸酯、甲基丙烯酸酯、異丁基甲 基丙烯酸酯、2 -乙基己基甲基丙烯酸酯、異癸基甲基丙烯 酸酯、正月桂基甲基丙烯酸酯、正硬脂基甲基丙烯酸酯、 甲氧基二乙二醇甲基丙烯酸酯、甲氧基聚乙二醇甲基丙烯 酸酯、四氫糠基甲基丙烯酸酯、異甲醯基甲基丙烯酸酯' tert-丁基甲基丙烯酸酯、異硬脂基甲基丙烯酸酯、正丁氧 基乙基甲基丙烯酸酯、3 -氯-2-羥基丙基甲基丙烯酸酯、2- -22- (19) 1363251 甲基-2-金剛烷基甲基丙烯酸酯、2-乙基-2-金剛烷基甲基 丙烯酸酯、2-丙基-2-金剛烷基甲基丙烯酸酯、2-甲氧基丁 基-2-金剛烷基甲基丙烯酸酯、8-甲基-8-三環癸基甲基丙 烯酸酯、8-乙基-8-三環癸基甲基丙烯酸酯、5-甲基丙烯醯 氧基-6-羥基原菠烯-2-羧酸-6-內酯,及2,2,3,3,4,4,4-七氟 丁基甲基丙烯酸酯等。 又,丙烯酸酯化合物、甲基丙烯酸酯化合物例如下式 (21 )至(23 )所示化合物等。 丫 〇=c Η 〇
0一C一C-c_〇一ch2 I h2 Z0H
(21)
°=? H 9 ό一c一c_c—〇_c I h2 OH (22) h2
-23- (23) (20) 1363251 丙烯醯胺化合物例如,丙烯醯胺' 甲基 Ν-乙基丙烯醯胺、Ν-苄基丙烯醯胺、Ν-苯基丙 Ν,Ν-二甲基丙烯醯胺等。 甲基丙烯酸醯胺化合物,例如甲基丙烯醯 甲基丙烯醯胺、Ν·乙基甲基丙烯醯胺、Ν-苄基 胺、Ν-苯基甲基丙烯醯胺,及Ν,Ν-二甲基甲 等。 乙烯基化合物,例如乙烯基醚、甲基乙烯 乙烯基醚、2-羥基乙基乙烯基醚、苯基乙烯基 烯基醚等。 苯乙烯化合物例如,苯乙烯、甲基苯乙烯 烯、溴基苯乙烯與羥基苯乙烯等。 馬來醯亞胺化合物例如,馬來醯亞胺、Ν -亞胺、Ν-苯基馬來醯亞胺與Ν-環己基馬來醯亞 使用上述加成聚合性單體之聚合物製造方 加成聚合性單體與必要時所添加之鏈移轉劑( 爲1 〇 %以下)溶解於有機溶劑後,加入聚合 聚合反應,其後,再以添加聚合停止劑方式製 始劑之添加量’對單體之質量而言爲1至10 合停止劑之添加量爲0.01至0.2質量% 。所 溶劑例如可使用丙二醇單甲基醚、丙二醇單丙 乙酯與二甲基甲醯胺等,鏈移轉劑例如十二院 烷基硫醇等’聚合起始劑例如偶氮雙異丁腈與 烷羰腈等’又聚合停止劑例如可使用4_甲氧 丙烯醯胺、 烯醯胺,及 胺、Ν-甲基 甲基丙烯醯 基丙烯醯胺 基醚、苄基 醚與丙基乙 、氯基苯乙 甲基馬來醯 胺等。 法,例如使 對單體質量 起始劑開始 得。聚合起 質量% ,聚 使用之有機 基醚、乳酸 硫醇與十二 偶氮雙環己 基酚等,反 -24 - (21) (21)1363251 應溫度可由3 0至1 Ο 0 °C,反應時間可由1至2 4小時中選 擇。 使用上述加成聚合物,以製造包含式(2)所示單位 構造之聚合物中,於使用含有式(1)所示具被保護之殘 基的加成聚合性單體與其他加成聚合性單體時,該使用比 例以質量比計算時,含有式(1)所示具被保護之殘基的 加成聚合性單體/其他加成聚合性單體,例如爲20/1至 1 /2 0,又例如爲1 〇/ 1至1 /1 〇,又例如爲5 /1至1 /5,又例 如爲3/1至1/3。又,該使用比例以莫耳比而言,含有式 (1) 所示具被保護之羧基的加成聚合性單體:其他加成 聚合性單體,例如爲〇_95: 0.05〜0.05: 〇_95,又例如爲 0·90: 0.10 〜0.10: 0.90’ 又例如爲 0.80: 〇.2〇 〜0.20: 0.80,又例如爲 0.70: 0.30 〜0.30: 0.70。 使用本發明之微影成像用下層_膜_形成組成物時,含有 式(2)所示單位構造之聚合物的重量平均分子量例如爲 1000至500000,又例如爲1000至20000,又例如爲3000 至150000,又例如爲3000至50000。 本發明之下層膜形成組成物中,使用含有式(2)所 示單位構造之聚合物時,其可僅使用1種聚合物,或將2 種以上之聚合物組合使用亦可。 本發明之下層膜形成組成物中,所使用之含有式 (2) 所不單位構造之聚合物’可爲無規聚合物、嵌段聚 合物或接枝聚合物等任一種。其中,前述聚合物可使用自 由基聚合、陰離子聚合、陽離子聚合等方法製得。又,其 -25- (22) (22)1363251 形態可使用溶液聚合、懸濁聚合、乳化聚合、塊狀聚合等 方法。 本發明之微影成像用下層膜形成組成物中所含之可與 羧基反應之基的化合物,只要含有可與羧基反應形成化學 鍵結之基的化合物時,則無特別限定。 可與羧基反應之基,例如環氧基、環氧丙烷基、噁唑 基、環碳酸酯基、烷氧基矽烷基、烷氧基烷基、氮雜環丙 烷基、羥甲基、羥基、異氰酸酯基、縮醛基、羥基矽烷 基、縮酮基、乙烯基醚基、胺基羥甲基、烷氧基甲基胺 基、及亞胺基等。 前述化合物中,例如三縮水甘油醇-P-胺基酚、四縮 水甘油基間二甲苯二胺、四縮水甘油基二胺基二苯基甲 烷、四縮水甘油基-1,3_雙胺基甲基環己烷、雙酚-A-二縮 水甘油基醚、苯甲酸二縮水甘油酯、新戊二醇二縮水甘油 醚、聚丙二醇二縮水甘油醚、甲酚酚醛聚縮水甘油醚、四 溴雙酚-A-二縮水甘油醚、雙酚六氟丙酮二縮水甘油醚、 丙三醇三縮水甘油醚、季戊四醇二縮水甘油醚、三-(2,3-環氧基丙基)-異氰酸酯、單烯丙基二縮水甘油基異氰酸 酯、及縮水甘油基甲基丙烯酸酯等含有環氧基之化合物 等。 又’含有環碳酸酯基之化合物,例如前述含有環氧基 之化合物與二氧化碳反應所得之含有環碳酸酯基之化合 物’例如1,2_丙烯碳酸酯、苯基二噁烷、乙烯基乙烯碳酸 酯、丁烯碳酸酯、四氯乙烯碳酸酯、氯基乙二醇碳酸酯、 -26- (23) (23)1363251 4-氯基甲基-1,3-二噁烷-2-酮、ι,2-二氯基乙基碳酸酯、4· (1·丙稀基氧甲基)-1,3 -二噪院-2 -酮、丙三醇碳酸醋、 (氯甲基)乙烯碳酸醋、1-节基丙三醇-2,3-碳酸醋、4,4-二甲基-5 -伸甲基-1,3-二嚼烷-2-酮,及3,3,3-三氟基丙烯 碳酸酯等。 含有異氰酸酯基之化合物,例如ρ_伸苯基二異訊酸 酯、聯苯基二異氰酸酯、伸甲基雙(苯基異氰酸醋)、2_ 異氣酸醋乙基甲基丙稀酸醋、1,4 -環己基二異氰酸醋、 1,3,5-三(6-異氰酸酯己基)三哄三酮、丨-異氰酸醋萘、 1,5 -萘二異氰酸酯、1-丁基異氰酸酯、環己基異氰酸酯、 节基異氰酸醋、4_氯基苯基異氰酸醋、異氰酸醋三甲基砂 烷、及己基異氰酸酯等。 含有烷氧基矽烷之化合物,例如三乙氧基辛基砂院、 二[3-(二甲氧基砂院)丙基]異三聚氰酸醋、3-(三甲氧 基矽烷)-Ν-[3-(三甲氧基矽烷)丙基]·〗_丙烷胺、3_ (三甲氧基矽烷)丙基甲基丙烯酸酯、3-異氰酸酯丙基三 乙氧基砂院、1,4 -雙(三甲氧基砂院乙基)苯、苯基三乙 氧基矽烷、甲基三乙氧基矽烷、(3-三甲氧基矽烷丙基) 馬來酯、3- ( 2-胺基乙基胺基)丙基三甲氧基矽烷、甲基 三丙酮醯基矽烷、三甲氧基- 2-(3,4-環氧基環己基)乙基 矽烷、3-三甲氧基矽烷基丙基甲基丙烯酸酯、三甲氧基丙 基矽烷' 4-(氯基甲基)苯基三甲氧基矽烷、2-(3,4-環 氧基環己基)乙基三乙氧基矽烷、三乙氧基-η-十二烷基 矽烷,及2-淸流基乙基三乙氧基矽烷等。 -27- (24) (24)1363251 本發明之下層膜形成組成物中所含之具可與羧基反應 之基的化合物,可使用至少含有式(3)所示基之化合 物。式(3)中,115爲氫原子、碳原子數丨至6之烷基或_ CH2OR7 (式中,R7爲氫原子或碳原子數1至1〇之烷 基),R6爲氫原子或碳原子數1至10之烷基。其中,烷 基例如甲基、乙基、正丁基、正辛基、異丙基、tert-丁 基、2-乙基己基、與環己基等。 前述化合物,例如胺基中氫原子被羥甲基或烷氧基甲 基所取代之三聚氰胺化合物、尿素化合物、甘脲化合物與 苯倂鳥糞胺化合物等。具體之例示如,六甲氧基甲基三聚 氰胺、四甲氧基甲基苯倂鳥糞胺、1,3,4,6-四(丁氧基甲 基)甘脲、1^4,6-四(羥基甲基)甘脲、1,3 -雙(羥甲 基)尿素、1,1,3,3-四(丁氧基甲基)尿素、1,1,3,3·四 (甲基甲基)尿素、1,3-雙(羥甲基)_4,5·二甲氧基-2-咪 唑啉酮等,又例如三井科學公司製甲氧甲基形式三聚氰胺 化合物(商品名:賽美爾 300、賽美爾 301、賽美爾 303、賽美爾350) 、丁氧基甲基形式三聚氨胺化合物 (商品名:麥可得506、麥可得5 0 8 )、甘脲化合物(商 品名:賽美爾1 1 70、保爾達1 1 74 )等化合物,甲基化尿 素樹脂(商品名:UFR65 ) 、丁基化尿素(商品名: UFR300 ' U-VAN10S60、U-VAN10R' U-VAN11HV)、大 曰本油墨化學工業公司製尿素/甲醛系樹脂(高縮合型, 商品名:貝可明J-300S、貝可明P-955、貝可明N)等。 又,胺基之氫原子可被羥甲基或烷氧基甲基取代之三聚氰 -28- (25) (25)【1363251 胺化合物、尿素化合物、甘脲化合物與苯并鳥糞胺化合物 縮合所得之化合物亦可。例如美國專利第6 3 2 3 3 1 0號所記 載之三聚氰胺化合物(商品名:賽美爾3 03 )與苯并鳥糞 胺化合物(商品名:賽美爾Π23)所製得之高分子量化 合物等。 本發明之下層膜形成組成物所含之至少含有2個式 (3 )所示基之化合物,例如可使用 N-羥基甲基丙烯醯 胺' N -甲氧甲基甲基丙烯醯胺、N -乙氧基甲基丙烯醯胺與 N-丁氧甲基甲基丙烯醯胺等羥甲基或烷氧甲基所取代之丙 烯醯胺化合物或甲基丙烯醯胺化合物所製得之聚合物。前 述聚合物可單獨由羥甲基或烷氧甲基所取代之丙烯醯胺化 合物或甲基丙烯醯胺化合物所製得,又,可與前述丙烯酸 酯化合物、甲基丙烯酸酯化合物、丙烯醯胺化合物、甲基 丙烯醯胺化合物、乙烯基化合物、苯乙烯化合物、馬來醯 亞胺化合物 '馬來酸酐 '與丙烯腈等其他加成聚合性單體 組合方式而製得。於聚合物之製造中,使用其他加成聚合 性單體時,其使用比例,以質量比而言,羥甲基或烷氧甲 基所取代之丙烯醯胺化合物或甲基丙烯醯胺化合物/其他 加成聚合性單體之比例,例如爲2 0/ 1至1 /2 0,又例如爲 10/1至1/10’又例如爲5/1至1/5,又例如爲3/1至1/3» 又’其使用比例,以莫耳比而言,羥甲基或烷氧甲基所取 代之丙烯醯胺化合物或甲基丙烯醯胺化合物:其他加成聚 合性單體之比例,例如爲〇·95: 0.05至0.05: 0.95,又例 如爲 0.90: 0·]0 至 〇_1〇: 0.90,又例如爲 〇.8〇: 0.20 至 -29- (26) 1363251 〇·20: 0.80,又例如爲 0.70: 0.30 至 0.30: 0.70< 前述聚合物,例如聚(丁氧甲基丙烯醯胺 氧甲基丙烯醯胺與苯乙烯之共聚物、Ν-羥基甲基 酿胺與甲基甲基丙烯酸酯之共聚物、N-乙氧甲基 醯胺與苄基甲基丙烯酸酯之共聚物,與Ν_ 丁氧 醯胺與苄基甲基丙烯酸酯與2 -羥基丙基甲基丙 共聚物等。前述聚合物之重量平均分子量例如爲 500000’又例如爲1〇〇0至2〇〇〇〇,又如3000至 又如3 000至50000。聚合物可單獨使用1種或; 上聚合物組合使用亦可。 本發明之微影成像用下層膜形成組成物中所 可與羧基反應之基的化合物,例如可使用^ (4) '式(5)、式(6)、式(7)、式(8)劈 所成群中所選出之至少1種結構單位之聚合物》 爲構成聚合物主鏈之鍵結基,Q爲直接鍵結或 R8、R9、Rw與Rii各自表示氫原子或碳原子數1 烷基,X爲0或1。其中,P只要爲構成聚合物 結基時,並未有特別限定》P例如下述式(P-1 4 )所列舉之內容。Q例如含有由伸苯基、-C (= CH2-、-NH·及-0-中所選出之至少1個連結基之 直接鍵結等。Q之具體例’如伸苯基、-c ( = 〇) (=〇 ) -〇-CH2-等。
)、N-丁 甲基丙烯 甲基丙烯 甲基丙烯 烯酸酯之 1 000 至 150000, 捋2種以 含之含有 奪有由式 I 式(9) 式中,P 連結基, 至10之 主鏈之鍵 )〜(Ρ- ξ 〇 ) - 、 - 連結基或 -〇 -及-C -30- (27) (27)1363251 H CH3 C2H5 Cl —C-c— —c_c— ^~~c—c— —c—c—
H2 ί H2 I H2 I H2 I (P-1) (P-2) (P-3) (P-4) 前述聚合物例如可使用含有環氧基、環氧丙烷基、嗎 哗基、環碳酸酯基、烷氧基矽烷基或異氰酸酯基之加成聚 合性單體而製得。又,於聚合物之製造中,可將前述丙烯 酸酯化合物、甲基丙烯酸酯化合物、丙烯醯胺化合物、甲 基丙烯醯胺化合物、乙烯基化合物、苯乙烯化合物、馬來 醯亞胺化合物'馬來酸酐,及丙烯腈等其他加成聚合性單 體組合使用。於聚合物之製造中,使用其他接成聚合性單 體時,其使用比例,以質量比而言,含有環氧基、環氧丙 烷基、噁唑基、環碳酸酯基、烷氧基矽烷基或異氰酸酯基 之加成聚合性單體/其他加成聚合性單體,例如爲20/1至 1/20,又例如爲10/1至1/10,或例如爲5/1至1/5,或例 如爲3/1至1/3。又,於使用比例中,以莫耳比而言,含 有環氧基、環氧丙烷基、噁唑基、環碳酸酯基、烷氧基矽 烷基或異氰酸酯基之加成聚合性單體:其他加成聚合性單 體,例如爲0.95 : 0_05至0.05 : 0.95,又例如爲0.90 : 0.10 至 〇.1〇: 0.90,又例如爲 0.80: 0.20 至 0.20: 0.80, 又例如爲 〇·7〇: 〇·30 至 0_30: 0.70。 含有環氧基之加成聚合性單體,例如縮水甘油基丙烯 酸酯,及縮水甘油基甲基丙烯酸酯等。 -31 - (28) 1363251 含有環氧丙烷基之加成聚合性單體,例如(3_: 3 -環氧丙院基)甲基甲基丙稀酸醋、環氧丙院-3-基 丙烯酸酯、(3 -甲基-3-環氧丙烷基)甲基甲基丙 酯、環氧丙烷·2 -基甲基丙烯酸酯,及環氧丙院_2_基 丙烯酸酯等。 含有噁唑基之加成聚合性單體,例如2-異丙稀 噁唑等。 含有環碳酸酯基酯加成聚合性單體,例如乙烯基 碳酸酯等。 含有院氧基砂院基之加成聚合性單體,例如乙烯 甲氧基矽烷、3-甲基丙烯氧丙基三甲氧基矽烷、3_甲 烯氧丙基三乙氧基矽烷、3·甲基丙烯氧丙基甲基二乙 矽烷,及3-丙烯氧丙烯三甲氧基矽烷等。 含有異氰三酯基之加成聚合性單體,例如2 -異 酯乙基甲基丙烯酸酯,及烯丙基異氰酸酯等。 含有式(4)單位構造之聚合物,例如可使用含 基之聚合物與環氧氯丙烷、縮水甘油基甲苯磺酸酯等 環氧基之化合物反應而製得。例如,使用酚酚醛與環 丙烷所製得之環氧基酚酚醛或,其他環氧基環甲酚酚 及環氧基萘醇酚醛等。 由式(4)、式(5)、式(6)、式(7)、式I 與式(9)所成群中所選出之至少1種單位構造之聚 的重量平均分子量,例如爲1〇〇〇至500000,又例 】000至20000,又例如爲3000至1 50000,又例如爲 己基-甲基 烯酸 甲基 基-2- 乙烯 基三 基丙 氧基 氰酸 有羥 含有 氧氯 醛, :8 ) 合物 如爲 3 000 -32- (29) 1363251 至50000。其可單獨使用1種聚合物,或將2種 合物組合使用亦可。 本發明之下層膜形成組成物中,含有式(1 被保護之羧基的化合物與含有可與羧基反應之基 之含量比例,以質量比計算時,含有式(1 )所 護之羧基的化合物/含有可與羧基反應之化合物 10/1至1/10,較佳爲5/1至1/5,又例如爲3/1! 如 2/1 至 1/2 。 本發明之下層膜形成組成物,爲含有可與殘 基與式(1)所示具被保護之羧基的化合物與含 基反應之基的化合物,及溶劑。 其中,可與羧基反應之基,例如與前所述 等。 前述化合物,例如可由含有烯烴部分與羧基 以製得含有式(1)所示具被保護之羧基與環氧 物等。羧基與式(1 5 )之化合物反應後,經由將 環氧化即可製得含有式(1)所示具被保護之羧 基的化合物。 又’含有可與翔基反應之基與式(1)所示 之羧基的化合物’例如含有式(1 )所示具被保 與式(3)所示基之聚合物。前述聚合物,例如 乙基甲基丙烯酸酯、1-乙氧基乙基甲基丙烯酸醋 氧基乙基甲基丙烯酸酯、1-正己氧基乙基甲基丙 及四氫-2 H-吡喃-2·基-甲基丙烯酸酯等甲基丙烯 以上之聚 )所示具 的化合物 示具被保 ,例如爲 5 W3,又 基反應之 有可與羧 相同之基 之化合物 基的化合 烴基部分 基與環氧 具被保護 護之羧基 1-甲氧基 、1 -異丙 烯酸酯, 酸半縮醛 -33- (30) (30)1363251 酯化合物,1-甲氧基乙基丙烯酸酯、l-tert-丁氧基乙基丙 烯酸酯、1-異丙氧基乙基丙烯酸酯、1-正丁氧基乙基丙烯 酸酯、四氫-2H-吡喃-2-基-丙烯酸酯等丙烯酸半縮醛酯化 合物,1-乙氧基乙基-4-乙烯基苯甲酸酯、雙(1-乙氧基乙 基)馬來酸酯、及甲基(1-乙氧乙基)馬來酸酯等式 (1)所示具被保護之羧基的加成聚合性單體,與N-羥基 甲基丙烯醯胺、N-甲氧甲基甲基丙烯醯胺、N_乙氧基甲基 丙烯醯胺與N-丁氧甲基甲基丙烯醯胺等羥甲基或烷氧甲 基所取代之丙烯醯胺化合物或甲基丙烯醯胺化合物腈聚合 反應所製得。聚合物之製造中,必要時,如前所述般,可 使用其他加成聚合性單體。製造聚合物所使用之前述含有 式(1)所示具被保護之羧基的加成聚合性單體,與羥甲 基或烷氧甲基所取代之丙烯醯胺化合物或甲基丙烯醯胺化 合物之比例’依質量比而言’含有式(1)所示具被保護 之羧基的加成聚合性單體/被羥甲基或烷氧甲基所取代之 丙烯醯胺化合物或甲基丙烯醯胺化合物,例如爲20/1至 1/20 ’又例如爲1〇/1至1/10,又例如爲5/1至1/5,又例 如爲3/1至1/3。又,其使用比例以莫耳比而言,含有式 (I)所不具被保護之殘基的加成聚合性單體:被經甲基 或烷氧甲基所取代之丙烯醯胺化合物或甲基丙烯醯胺化合 物,例如爲0.95 :〇.〇5至0.05: 0.95,又例如爲0.90: 0.10 至 0.10: 〇‘90,又例如爲 0.80: 〇.2〇 至 0.20: 0.80, 又例如爲 0.70: 0.30 至 0.30: 0.70。 使用前述加成聚合性單體時,其比例爲,於製造聚合 -34- (31) (31)1363251 物所使用之全單體中,例如爲0.5至80質量% ,又例如 爲1至70質量% ,又例如爲5至50質量% 。前述聚合 物,例如可依使用聚合起始劑之前述方法而製得。前述聚 合物之重量平均分子量例如爲1000至500000,又例如爲 1000 至 20000,又如 3000 至 150000,又如 3000 至 5 0000。聚合物可單獨使用1種或將2種以上聚合物組合 使用亦可。 含有可與羧基反應之基與式(1)所示具被保護之羧 基的化合物,例如可使用式(2)所示單位構造,與由式 (4)、式(5)、式(6)、式(7)、式(8)與式(9) 所成群中所選出之至少1種結構單位之聚合物。前述聚合 物’例如可將含有式(1)所示具被保護之羧基的加成聚 合性單體,與前述含有環氧基、環氧丙烷基、噁唑基、環 碳酸酯基、烷氧基矽烷基或異氰酸酯基之加成聚合性單體 經聚合反應而製得。於聚合物之製造中,必要時,可同時 使用前述其他加成聚合性單體,或前述之羥基甲基或烷氧 基甲基所取代之丙烯醯胺化合物或甲基丙烯醯胺化合物。 於製造聚合物中所使用之前述含有式(1)所示具被 保護之羧基的加成聚合性單體,與環氧基、環氧丙烷基、 噁唑基、環碳酸酯基、烷氧基矽烷基或異氰酸酯基之加成 聚合性單體之比例,依質量比而言,含有式(1 )所示具 被保護之羧基的加成聚合性單體/含有環氧基、環氧丙烷 基' 噁唑基、環碳酸酯基、烷氧基矽烷基或異氰酸酯基之 加成聚合性單體,例如爲2 0/1至1 /2 0,又例如爲1 0/1至 -35- (32)1363251 1/10 使用 基的 基、 性單 0.90 0.80 基甲 時, 中, 又例 用聚 基的 造之 ,又例如爲5/1至1/5,又例如爲3/1至1/3。又,其 比例以莫耳比而言,含有式(1)所示具被保護之羧 加成聚合性單體:含有環氧基、環氧丙烷基、噁唑 環碳酸酯基、烷氧基矽烷基或異氰酸酯基之加成聚合 體,例如爲0.95: 0.05至0.05: 0.95,又例如爲 :0.10 至 0_10: 0.90,又例如爲 0.80: 0.20 至 0.20: ,又例如爲 0.70: 0.30 至 0.30: 0.70。 又’使用前述加成聚合性聚合物或被羥基甲基或烷氧 基所取代之丙烯醯胺化合物或甲基丙烯醯胺化合物 其使用比例,以對製造聚合物時所使用之全部單體 例如爲0.5至80質量% ,又例如爲1至70質量% , 如爲5至50質量% 。前述聚合物,例如可依前述使 合起始劑之方法而製得。 含有可與羧基反應之基與式(1)所示具被保護之羧 化合物’例如爲含有式(1 〇 )與式(1丨)所示單位構 聚合物 ^12 ^13 十?太1十5一味 H2 C=0 H2 C=〇 r2 H ? 〇 | CH2 R30 r4 Ri4~C~(CH2)y H2C一0 (10) (11) -36- (33) (33)1363251 式中’ |^2與R,3各自表示氫原子或甲基,Ri4爲氫原 子、甲基或乙基,y爲0或1,51與52爲構成聚合物之各 單位構造的莫耳比,s,爲〇.〇5至0.95,或〇.1〇至0.90, 或 0.20 至 0·80 ,或 〇.3〇 至 0.70 ; s2 爲 〇.〇5 至 0.95 ,或 0.10 至 0.90,或 0.20 至 〇.80,或 0.30 至 0.70。 又’於製造含有式(10)與式(11)所示單位構造之 聚合物中’可同時使用前述丙烯酸酯化合物、甲基丙烯酸 酯化合物、丙烯醯胺化合物、甲基丙烯醯胺化合物、乙烯 基化合物、苯乙烯化合物、馬來醯亞胺化合物、馬來酸 酐、及丙烯腈等其他加成聚合性單體。使用其他加成聚合 性單體時’於含有式(10)與式(11)所示單位構造之聚 合物中之比例’以滿足前述S,與S2之範圍下予以使用。 本發明之微影成像用下層膜形成組成物中所含之含有 式(10)與式(11)所示單位構造之聚合物中,亦包含僅 由式(10)與式(11)所示單位構造所形成之聚合物。 本發明之微影成像用下層膜形成組成物中所含之含有 式(10)與式(11)所示單位構造之聚合物中,除式 (10)與式(11)所示單位構造以外,式(1〇)與式 (]1 )所示單位構造之聚合物中的比例(莫耳比),於滿 足前述Si與SZ之範圍內,可再含有由其他加成聚合性單 體所產生之含有其他單位構造之聚合物。 例如,於聚合物中,式(1 0 )之單位構造之比例(莫 耳比)爲0 · 1 〇 ’式(1 1 )之單位構造之比例(莫耳比)爲 -37- (34) 1363251 所得之聚 構造之比 例(莫耳 0.10 所 保護之羧 式(14 ) 0.60,其他單位構造之比例(莫耳比)爲0.30 合物。又,例如,於聚合物中,式(10)之單位 例(莫耳比)爲0.50,式(11)之單位構造之比 比)爲〇·40,其他單位構造之比例(莫耳比)怎 得之聚合物等。 含有可與羧基反應之基與式(〗)所示具被 基的化合物,例如爲含有式(12 )、式(1 3 )與 所示單位構造之聚合物; ^12 ^13 ^15 卜S〒士1 H2 c=0 1 H2 C=0 I \:9\ 丨2 c=0 1 Η ? I 〇 I 1 0 r2 -C-C-R1 I I CH〇 I “ 1 ch2 r30 Ri4—9~(?H2)y ^16 r4 H2C—〇 (14) (12) (13) 式中,Rl5爲 氫原子或甲基 5 R 1 6 爲氫原子 數1 至6之烷基、 苯基、萘基或 蒽基 ,t 1 ' t2 與 聚合 物之各單位構 造的莫耳比, tl爲 0.05 至 0 如爲 0· 1 5 至 0.80 ,又例如爲〇. 25至 0.60,t2 ί 0.90 ,又例如爲〇. .1 5至0.8 〇,又例如 爲〇·25至 爲 0.05 至.0.90, 又例如爲0 . 〇 5 至〇 .7 0,又例 、碳原子 t3爲構成 .9 0,又例 輸0.05至 0.6 0,t3 如爲·〇. 1 5 -38- (35) (35)1363251 至0.50。碳原子數1至6之烷基的具體例如,甲基、乙 基、異丙基、正己基、與環戊基等。 含有式(12)、式(13)與式(1〇所示單位構造之 聚合物,例如可由前述甲基丙烯酸半縮醛酯化合物或丙烯 酸半酸醛酯化合物與,前述含有環氧基之加成聚合性單體 或含有環氧丙烷基之加成聚合性單體,與式(14)之單位 構造所產生之單體所製得。式(14)之單位構造所產生之 單體,例如甲基丙烯酸酯、甲基甲基丙烯酸酯、乙基甲基 丙烯酸酯、異丙基甲基丙烯酸酯、環己基丙烯酸酯、正己 基甲基丙烯酸酯、苄基丙烯酸酯、苄基甲基丙烯酸酯、萘 基甲基甲基丙烯酸酯、蒽基甲基丙烯酸酯及蒽基甲基甲基 丙烯酸酯等。 又,於製造含有式(12)、式(13)與式(14)所示 單位構造之聚合物中,可同時使用前述丙烯酸酯化合物、 甲基丙烯酸酯化合物、丙烯醯胺化合物、甲基丙烯醯胺化 合物、乙烯基化合物、苯乙烯化合物、馬來醯亞胺化合 物、馬來酸酐及丙烯腈其他皆成聚合性單體等。使用其他 加成聚合性單體時,式(12)、式(13)與式(Μ)所示 單位構造於聚合物中之比例(莫耳比),爲滿足前述η、 t2與t3之範圍。 本發明之微影成像用下層膜形成組成物中所含之含有 式(12) '式(13)與式(14)所示單位構造之聚合物 中,可爲僅含有式(12)、式(13)與式(14)所示單位 構造所得之聚合物。又’本發明之微影成像用下層膜形成 -39- (36) 1363251 組成物中除所含之含有式(12)、式(13)與式 示單位構造以外,除式(12)、式(13)與式( 單位構造所得聚合物中之比例,於滿足前述h、 範圍內,可再含有由其他加成聚合性單體所產生 他單位構造之聚合物。例如,於聚合物中,式( 位構造之比例(莫耳比)爲0.2 5,式(1 3 )之單 比例(莫耳比)爲〇 3 5,式(1 4 )之單位構造之 耳比)爲〇.〇5,其他單位構造之比例(莫耳比 所得之聚合物。又,例如,式(12 )之單位構 (莫耳比)爲0.35,式(13)之單位構造之比 比)爲〇·45,式(14 )之單位構造之比例(莫 0.15,其他單位構造之比例(莫耳比)爲〇.〇5 合物。 前述聚合物之重量平均分子量例如爲 500000,又例如爲1〇〇〇至20000,又如3000至 又如3000至5 0000。聚合物可單獨使用1種或 上聚合物組合使用亦可。 本發明之微影成像用下層膜形成組成物中除 有可與羧基反應之基與式(1)所示具被保護之 合物,例如式(24)至式(52)所示之聚合物 Ρ 1、Ρ 2、p 3、ρ 4爲聚合物中各單位構造之比例) (1 4 )所 1 4 )所示 t2與t3之 之含有其 12 )之單 位構造之 比例(莫 )爲 〇_35 造之比例 例(莫耳 耳比)爲 所得之聚 1 000 至 150000, 將2種以 所含之含 羧基的化 (式中, -40- (37) 1363251 一 2 CH十 ΓΡ200-Η2丁 -I - CIC—C—O -2 H3 2C CH -0CO HCH c丨c·丨c—o \υλ (24 v° 12 CH+ 12 CH+
rp2〇了 II CICIC 12 c H+
5 (2 ΓΡ30了 II CICIC
〇 H3C-CH I〇 Ih2c- o(ch2)3ch3
£^,=0 CICIC— 12 CH HICIC— 12 CH十
HIC P20
\—y 6 (2 〇h3c-ch ο Ih2c-
o(ch2)3ch3 -41 - (27) (38)1363251
I H 〇一c-och2ch3 ch3 ch3 hn-ch2och3
I ά ά H3C-CH ?H2 CH2CH3 CH3 ?H2 NC〇
ch3 (29) -42- (39) 1363251 CH ------- CICICIO I 2 〇
I 2 〇CH I =-CICICIO -2 c H /V \1—/ (30 v°
CH3 一?+P2H2 c=0 〇 I h2c-
V (31) 0-C-OCH2CH3
ch3 ch3十S—令+pi H2 c=0 I 〇 H3C-CH CH3?十P2 H2 C=0 (32) 〇(ch2)3ch3 〇 H2c-c-c—Si(OC2H5)3 H2 h2 -43- (40) 1363251 ch3 ch3 CH3 +S「?+P3(33) h2 c=0 H2 c=0 H2 C=0 I I l λ o o ? I I h3c-ch ch3 h2c~\7 h2c O—C—CH3 a ch3
Η
〇 h3c—chh Ο—C—CH3 ch3
I 〇
HoC—CH2CF3 ch3 ch3 CH3十S—今十pi 十+S「〒+P3(35) H2 C=〇 H2 C=0 H2 C=〇 I ^ 〇 H3c—CH H 0_C—CH3 ch3 h2c o h2c-ch2oh -44 - (36) (41) 1363251
ch3十D H2I H
H 〇-C-〇CH2CH3 ch3
,3 )3ch h2 HHICIC—o—clo( _ I HICICIO c II IΓΙ3 o c H 3 H
I 2 CH H2
£1=0 CICICIOIC \)7 (37 cIc—c-°—c—° I 2 I CH c + H3 H丨C-丨c:丨o丨C-12Η2 CH Η 十ρ1ο IP20
\1 J/ 8 (3 3
OH -45- (42) 1363251
Hi-C-H2 c丨c·丨c:丨ο 12 Η3 2C Η H3+^1H-?-CH ?-c-2ci CH+
Xu/ 9 (3 -2 CH+
H3C H3H^"=0;T c丨c·丨c:—o—c丨o
-2 CH H2
HICICIOIC p2o CH+ _3 )3ch H2 (c Γο 2 H CICICIOIC* 2 ο ό \)/ 40 CICICIOIC -2H2 卜h3I H3-^=o!e(c CICICIOICIO I 2 I CH c 十H3 CH十 p2o (41Ton CICICIO-2 CH十 (43)1363251
ch3 η H 牡1 ^η7^2 Η2 c=0 Η2 C=0 〇 〇 1 H3C-CH H2C-^ OCH2CH3 CH3 H I ?+pi H2 C-0 H2 C=0 1 1 〇 1 0 1 h2c- ch3 “3 (42)
H2 C=0 NH CH2OCH2CH3
-P3 (43) h3c-ch OCH2CH3
I 2 CH
H3C _3 2CH H He —c彳c—o丨c—o P10
-2 CH = Η HοIo—c:—οINIo o P20
P3 \—/ 44 H 20
N ό -47- (44) 1363251 12 CH 十 Η丨c·—c:丨°· -2 CHH3 2ch H c -°co H1H o丨c·—c:—o p2o CH2 45 ο I 2 CH+
H3C CICICIOIC -2 CH+
2 HH3 )3ch £^=0h(ch CICICIOICIO 2 H CICICIOIC 12 c H+ \1/ 46 Hi o
—o HI
\m/ 47 -48- (45) 1363251 c H2
H3C
H3 1D2CH po H H c CICICIOICIO
12 CH H2
CICICIOIC p2o 12 CH+
b P302CC Η CICICIOIC \1/ 48 :〇 I 2 CH+ H3^
H3C H2 H(c o丨c—o—o丨c—o 〇
i 2 CH ,3 )3ch :o H4=o CICICIOIC 一丨·H2
\/ * 2 CH+
H3C
H3 2CH H He CICICIOICIO - 2 CH 十 P20 20 Η H c丨c丨cIοI—c
50) -49- (46) 1363251
Η 1ο2C Ha^pff hch C丨C-丨c=—ο丨C丨ο -2 I CH c + H3 H4=oc--c—2??h2c CH 卜 十
ίΆ?H2 CIO丨c:丨o丨c—^ ^ CH2 CICICIOIC H3C-H2 2C 2 (5 本發明之下層膜形成組成物中,可再添加吸光性化合 物、界面活性劑、流變調整劑及黏著輔助劑等。 吸光性化合物,只要對於設置於下層膜上之光阻層中 的感光成分之感光特性波長領域中之光線具有較高吸收 -50- (47) 1363251 能,且可防止由基板反射產生之駐波或因基板表面之凹凸 所造成之亂反射之化合物時,並未有特別限定。
前述吸光性化合物,例如二苯甲酮化合物、苯并三唑 化合物、偶氮化合物、萘化合物、蒽化合物、蒽醌化合 物、三畊化合物、三畊三酮化合物等。又,吸光性化合物 又以可與前述具有環氧基之成分進行反應者爲佳,因此, 以使用具有羧基或酚性羥基之化合物爲更佳。具體而言, 例如1-萘羧酸、2-萘羧酸、1-萘醇、2-萘醇、萘基乙酸、 1-羥基-2-萘羧酸、3-羥基-2-萘羧酸、3,7-二羥基-2-萘羧 酸、6-溴基-2-羥基萘、2,6-萘二羧酸、9-蒽羧酸、10-溴 基-9-蒽羧酸、蒽-9,10-二羧酸、1-蒽羧酸、1-羥基蒽、 1,2,3-蒽三醇、2,7,9_蒽三醇、苯甲酸、4-羥基苯甲酸、4-溴基苯甲酸' 3-碘基苯甲酸、2,4,6-三溴基酚、2,4,6-三溴 基間苯二酚、3,4,5-三碘基苯甲酸、2,4,6-三碘基-3-胺基 苯甲酸、2,4,6-三碘基-3-羥基苯甲酸、2,4,6-三溴基-3-羥 基苯甲酸等。又,吸光性化合物,例如具有下述式 (53) 、 (54)或(55)所示單位構造之聚合物,或式 (56)所示化合物等。式(56)中,Ar爲可被碳原子數1 至5之烷基、碳原子數1至5之烷氧基、氟原子、氯原 子、溴原子、碘原子、硝基、氰基、羥基、硫醇基、碳原 子數1至5之硫烷基、羧基、苯氧基、乙醯基、碳原子數 1至5之烷氧羰基或乙烯基所取代之苯環、萘環或蒽環 等。 -51 - 1363251
η 〇 Η IIo-c-c-c-o-c
II
(55) ο ΟΗ
Ar—C-O-C-C Η2 Η _/C—C—C—Ο—C—Ar Ν Λ η2Ν" Η Η2
Ν w、0 Ο I Η II H2C—C 一C 一Ο—C—Αγ I (56) ΟΗΗ2 前述吸光性化合物可單獨使用]種或將2種以上組合 使用亦可。本發明之下層膜形成組成物中含有吸光性化合 物時,其添加量爲,於固體成分中爲3 0質量%以下,例 如爲1至20質量% ,又如1至10質量% 。 -52- (49) (49)1363251 本發明之微影成像用下層膜形成組成物可再含有界面 活性劑。界面活性劑,例如聚氧乙烯月桂基醚、聚氧乙烯 硬脂基醚、聚氧乙烯十六烷基醚、聚氧乙烯油基醚等聚氧 乙烯烷基醚類;聚氧乙烯辛基酚醚、聚氧乙烯壬基酚醚等 聚氧乙烯烷基烯丙基醚;聚氧乙烯·聚氧丙烯嵌段共聚物 類;山梨糖醇單月桂酸酯、山梨糖醇單棕櫚酸酯、山梨糖 醇單硬脂酸酯、山梨糖醇單油酸酯、山梨糖醇三油酸酯、 山梨糖醇三硬脂酸酯等山梨糖醇脂肪酸酯類;聚氧乙烯山 梨糖醇單月桂酯、聚氧乙烯山梨糖醇單棕櫚酸酯、聚氧乙 烯山梨糖醇單硬脂酸酯、聚氧乙烯山梨糖醇三油酸酯、聚 氧乙烯山梨糖醇三硬脂酸酯等聚氧乙烯山梨糖醇脂肪酸酯 類等非離子系界面活性劑;愛普脫EF301、EF3 03、EF352 (杜凱公司製)、美隔福F171、F173(大日本油墨化學 公司製)、普樂拉FC430、FC431(住友3M公司製)、 亞沙喜八0710、沙福隆3-382、5(:101、8(:102、8(:103、 SCI 04、SC105' SC106(旭硝子公司製)等氟系界面活性 劑,及有機矽氧烷聚合物KP34 1 (信越化學公司製)等。 前述界面活性劑之添加量,於本發明之下層膜形成組成物 之全成分中,一般爲〇·2質量%以下,較佳爲0.1質量% 以下。前述界面活性劑可單獨添加,或將2種以上組合添 加亦可。 本發明之微影成像用下層膜形成組成物,於微影成像 步驟上爲使上層所被覆之光阻與下層膜具有一致之酸度, 可添加光酸產生劑,光酸產生劑例如鎰鹽化合物、磺醯亞 -53- (50) 1363251 胺化合物,及二磺醯二偶氮甲烷化合物等。 鎗鹽化合物例如,如二苯基碘鑰六氟磺酸鹽 碘鑰三氟甲烷磺酸鹽、二苯基碘鎗九氟-η-丁烷 二苯基碘鎰全氟-η-辛烷磺酸鹽、二苯基碘鎰 鹽、雙 (4-t-丁基苯基)碘鏺莰烷磺酸鹽與雙( 基苯基)碘鑰三氟甲烷磺酸鹽等碘鎗鹽系酸產生 苯基銃六氟銻酸鹽、三苯基銃九氟-η-丁烷磺酸 基銃莰烷磺酸鹽及三苯基锍三氟甲烷磺酸酯等锍 生劑等。 磺醯亞胺化合物例如Ν -(三氟甲烷磺醯氧 醯銑亞胺、Ν-(九氟·η· 丁烷磺醯氧基)琥珀醯 Ν_ (莰烷磺醯氧基)琥珀醯銑亞胺與Ν-(三氟 氧基)萘醯亞胺等。 二磺醯二偶氮甲烷化合物,例如雙(三氟 基)二偶氮甲烷、雙(環己基磺醯基)二偶氮 (苯基磺醯基)二偶氮甲烷、雙(ρ -甲苯磺醯基 甲烷、雙(2,4-二甲基苯磺醯基)二偶氮甲院、 醯基-Ρ-甲苯磺醯基二偶氮甲烷等。 又’光酸產生劑,例如苯偶因甲苯磺酸醋、 烷磺酸三酯及硝基苄基-9,10-二乙氧基蒽_2_磺酸 酯化合物,及苯基-雙(三氯甲基)-s-三畊等鹵 系光酸產生劑等。 前述光酸產生劑可僅使用1種,或將2種以 用亦可。使用光酸產生劑時,其含量於下層膜形 '二苯基 磺酸鹽、 茨烷磺酸 4-tert-丁 劑,及三 鹽、三苯 鹽系酸產 基)號拍 銑亞胺、 甲烷磺醯 甲基磺醯 甲烷、雙 )二偶氮 及甲基磺 焦培酚甲 酯等磺酸 素化合物 上組合使 成組成物 -54- (51) (51)1363251 之固體成分中’例如爲20質量96以下,可爲0.01至10 質量% ,或爲〇.1至5質量% ,或爲0.5至3質量% 。 本發明之下層膜形成組成物,必要時可再含有流變調 整劑、黏著輔助劑等。 流變調整劑,例如二甲基苯甲酸酯、二乙基苯甲酸 酯、二異丁基苯甲酸酯、二己基苯甲酸酯、丁基異癸基苯 甲酸酯、二正丁基己二酸酯、二異丁基己二酸酯、二異辛 基己二酸酯、辛基癸基己二酸酯、二正丁基馬來酸酯、二 乙基馬來酸酯、二壬基馬來酸酯、甲基油酸酯、丁基油酸 酯、四氫呋喃基油酸酯、正丁基硬脂酸酯、及縮水甘油基 硬脂酸酯等。前述流變調整劑,於下層膜形成組成物之固 體成分中,一般添加量爲10質量%以下。 黏著輔助劑,例如三甲基氯矽烷、二甲基乙烯基氯矽 烷、甲基二苯基氯矽烷、氯甲基二甲基氯矽烷、三甲基甲 氧基矽烷、二甲基二乙氧基矽烷、甲基二甲氧基矽烷、二 甲基乙烯基乙氧基矽烷、r·甲基丙烯醯基丙基三甲氧基 矽烷' 二苯基二甲氧基矽烷、苯基三乙氧基矽烷、六甲基 二矽氨烷、n,n’-雙(三甲基甲矽烷基)脲、二甲基三甲 基甲矽烷基胺、三甲基甲矽烷基咪唑、乙烯基三氯矽烷、 r-氯基丙基三甲氧基矽烷' r-胺基丙基三乙氧基矽烷、 r-環氧丙氧基丙基三甲氧基矽烷、r-甲基丙烯醯基丙基 三甲氧基矽烷、苯并三唑、苯并咪唑、吲唑、咪唑、2-氫 硫基苯并咪唑、2 -氫硫基苯并噻唑、2 -氫硫基苯并噁唑、 尿唑、硫尿嘧啶、氫硫基咪唑、邱硫基吡啶、1 -二甲基 -55- (52) 1363251 脲、153·二甲基脲及硫尿素等。前述黏著輔助劑,於 膜形成組成物之固體成分中,一般添加量爲2質量 下。 本發明之微影成像用下層膜形成組成物中,爲溶 述固體成分所使用之溶劑,可使用各種溶劑皆可,前 劑,例如乙二醇單甲基醚、乙二醇單乙基醚、甲基乙 乙醚乙酸酯、乙基乙二醇乙醚乙酸酯、二乙二醇單 醚、二乙二醇單乙基醚、丙二醇、丙二醇單甲基醚、 醇單甲基醚乙酸酯、丙二醇丙基醚乙酸酯、甲苯、 苯、甲基乙基酮、環戊酮、環己嗣、2-羥基丙酸乙酯 羥基-2 -甲基丙酸乙酯、乙氧基乙酸乙酯、羥基乙 酯、2-羥基-3-甲基丁酸甲酯、3-甲氧基丙酸甲酯、3-基丙酸乙酯、3 -乙氧基丙酸乙酯、3 -乙氧基丙酸甲酯 酮酸甲酯、丙酮酸乙酯、乙酸乙酯、乙酸丁酯、乳 酯、乳酸丁酯、Ν,Ν -二甲基甲醯胺、ν,Ν·二甲基乙醯 Ν-甲基吡咯烷酮等。前述溶劑可單獨或將2種以上組 用皆可。又’可再混合丙二醇單丁基醚、丙二醇單丁 乙酸酯等高沸點溶劑後使用亦可。 以下,將說明本發明之微影成像用下層膜形成組 之使用方法。於半導體基板(例如矽/二氧化矽包 板、氮化矽(SiNx)基板、玻璃基板、及ΙΤΟ基板等) 使用旋轉塗佈器、條狀塗佈器以適當的塗佈方法塗佈 明之微影成像用下層膜形成組成物,其後,經由燒培 成下層膜。燒培之條件,例如可由燒培溫度8 0至 下層 %以 解前 述溶 二醇 甲基 丙二 二甲 、2- 酸乙 甲氧 、丙 酸乙 胺、 合使 基醚 成物 覆基 上, 本發 而形 -56- 250 (53) 1363251 °C、燒培時間0.3至60分鐘之間作適當的選擇。較 燒培溫度130至250〇C、燒培時間0.5至5分鐘。其 下層膜之膜厚度,例如爲0.01至3.0#m,又例如爲 至 1.0/zm,又例如爲 〇.〇5 至 0.50/zm。 本發明之微影成像用下層膜形成組成物,如前 般’爲含有式(1)所示具被保護之羧基的化合物、 可與羧基反應之基的化合物,又,亦爲含有可與羧基 之基與式(1)所示具被保護之羧基的化合物。 將此組成物塗佈於基板上,並經由燒培以形成下 之際’式(1)所示具被保護之羧基將因熱產生分解 供羧基(式(EQ1))。經由此方式生成之羧基,於 中,可與環氧基、環氧丙烷基、烷氧基矽烷基、胺基 基、烷氧基甲基胺基及異氰酸酯基等前述可與羧基反 基產生反應。經由此反應,可使下層膜形成組成物中 之化合物間產生鍵結。例如環氧基可產生式(EQ2) 應式。 佳爲 中, 0.03 所述 含有 反應 層膜 而提 燒培 羥甲 應之 所含 之反 -57- (54) 1363251 〇=C I 〇 Η
OJVVP R-
0=C R-j—C—C_R2 〇 r3 r4 〇H R4 一〇 R3 (EQ1) l—CIOor--〇 + Η jh2p ;-HC丨 c—?c—一
OH H2 〇
2 Q (E 又,環氧丙烷基、異氰酸酯基、烷氧基矽烷基、烷氧 基甲基胺基、噁唑啉基及環碳酸酯基,則推測其分別產生 (EQ3 )至(EQ8 )等反應式。 -58- (55)1363251 R11 H2 CIO I I CIC 厂H2 R1 + H CIO II 〇
A 一 —GIG—olo—< H 〇 H2-CH2
3 Q (E 〇 TCIOH -Ι ο + >——Nncno tn—-cn
H o 〇 I c=〇
\J/ Q4 (E 一—CIO --〇 + R9〇-Sh〇Ri〇 〇r8
RgO~Si~ORi〇 〇 〇=9 (EQ5)
T TC-OH -- o +
N丨cIo丨R
5 R H2 6 π-τνχτ*N-R5C-〇-CH2 〇 -59- (56) (56)1363251
特別是,使用2個以上式(1)所示具被保護之羧基 與2個以上含有可與羧基反應之基的化合物時,經由羧基 與可與羧基產生反應之基的反應結果,可使化合物間形成 連續鍵結。而經由於前述連續化合物間形成鍵結,而可使 所形成之下層膜更爲強固化。其結果,可降低下層膜對塗 佈於其上層之光阻組成物所常使用之有機溶劑,例如乙二 醇單甲基醚、乙基乙二醇乙醚乙酸酯、二乙二醇單乙基 酸、丙二醇、丙二醇單甲基醚、丙二醇單甲基醚乙酸酯、 丙二醇丙基醚乙酸酯、甲苯、甲基乙基酮、環戊酮、2-經 基丙酸乙酯、2-羥基-2_甲基丙酸乙酯、乙氧基乙酸乙 醋、丙酮酸甲酯、乙酸乙酯與乳酸乙酯等之溶解性。因 -60- (57) (57)1363251 此,使用本發明之下層膜形成組成物所形成之下層膜,不 容易引起與光阻間之內部缺陷。又,推測使用具有多數反 應部位之化合物時,可加強所形成之下層膜的強固性。特 別是使用含有式(1)所示具被保護之羧基或含有可與羧 基反應之基的聚合物時,因可於燒培反應中形成交聯構 造,故可使下層膜更佳強固化。因此,本發明之下層膜形 成組成物,以含有式(1)所示具被保護之羧基的聚合 物、含有可與羧基反應之基的聚合物,或含有可與羧基反 應之基與式(1)所示具被保護之羧基的聚合物爲佳。 又,式(1)所示具被保護之羧基經熱分解所產生之 羧基,及經由此方式生成之羧基極容易與環氧基、環氧丙 烷基、噁唑啉基、烷氧基矽烷基、胺基羥甲基及異氰酸酯 基等於燒培條件下進行反應,故並無需使用觸媒。因此, 本發明之下層膜形成組成物,無須如以往般,於形成交聯 性下層膜時所使用之組成物中添加作爲觸媒之磺酸化合物 等強酸。又,本發明之下層膜形成組成物爲可使聚合物於 相互反應間形成交聯構造之系統,且並未含有以往所常用 之低分子交聯劑或磺酸化合物等低分子化合物,故可降低 燒培中所產生之昇華物量,並迴避因昇華物所產生之微細 粒子或異物對半導體基板或淸靜室所造成之污染。 其次,於下層膜上方形成光阻層。光阻層之形成,如 眾所皆知之方法,即將光阻組成物溶液塗佈於下層膜上後 進行燒培而製得者。 於本發明之下層膜上塗佈、形成之光阻,只要可對曝 -61 - (58) (58)1363251 光光線感光時並無特別限定,又,負型光阻與正型光阻皆 可使用。例如酚醛樹脂與1,2·萘醌二疊氮磺酸酯所得之正 型光阻、含有可因酸分解而提高鹼溶解速度之基的膠黏劑 與光酸產生劑所得之增強化學型光阻、含有可因酸分解使 光阻之鹼溶解速度提高之低分子化合物與鹸可溶解性膠黏 劑與光酸產生劑所得之增強化學型光阻、含有可因酸分解 而提高鹼溶解速度之基的膠黏劑與可因酸分解而提高光阻 之鹼溶鹼速度之低分子化合物與光酸產生劑所得之增強化 學型光阻等,例如西普來公司製商品APEX-E、住友化學 工業公司製商品PAR710、信越化學工業公司製商品名 SEPR430 等。 隨後’通過特定之光罩以進行曝光。一般曝光爲使用 KrF電漿雷射(波長248nm ) 、ArF電漿雷射(波長 193nm)與F2電漿雷射(波長I57nm)等。曝光後,可再 視需要進ί了曝光後加熱(PEB ; Post Exposure Bake)。曝 光後加熱’例如可於加熱溫度7 0至1 5 0 °C、加熱時間〇 · 3 至1〇分鐘之範圍內適當的進行。 其次’使用光阻用顯像液進行顯像。經此處理,例如 使用正型光阻時’可去除曝光部份之光阻,而形成光阻之 圖型。 光阻用顯像液,例如可使用氫氧化鉀、氫氧化鈉等鹼 金屬氫氧化物之水溶液,氫氧化四甲基胺、氫氧化四乙基 銨、膽鹼等氫氧化四級銨之水溶液,乙醇胺' 丙基胺、乙 烯二胺等胺水溶液等之鹼性水溶物等。又,前述顯像液中 -62- (59) (59)1363251 可加入界面活性劑等。顯像條件,例如於溫度5至50 °C ’ 1 〇至3 00秒之範圍間作適當的選擇。 又,依此方式形成之光阻的保護膜,隨後將進行去除 下層膜與半導體基板之加工。下層膜之去除方式,例如可 使用四氟甲烷、全氟環丁烷(C4F8 )、全氟丙烷 (c3F8)、三氟甲烷、一氧化碳、氬氣、氧氣、氮氣、六 氟化硫、二氟甲烷、三氟化氮及三氟化氯等氣體。 於半導體基板上形成本發明之下層膜之前或後時,可 塗佈 '形成有機系反射防止膜。其中,所使用之反射防止 膜組成物並未有特別限定,其可由目前爲止於微影成像步 驟中所常用之組成物中適當的選擇使用,又,常用之方 法,例如使用旋轉塗佈器、條狀塗佈器等進行塗佈與燒培 以形成反射防止膜。反射防止膜組成物,例如吸光性組成 物、以聚合物與溶劑爲主成分之組成物、具有以化學鍵結 連結吸光基之組成物、以交聯劑與溶劑爲主成分之組成 物、以吸光性化合物、交聯劑與溶劑爲主成分之組成物、 與以具有吸光性高分子交聯劑與溶劑爲主成物之組成物 寺。目1_|述反射防止膜組成物’必要時,可再含有酸成分、 酸產生劑成分 '流變調整劑等。吸光性化合物,例如只要 對於設置於反射防止膜上之光阻中的感光成分之感光特性 波長區域中之光具有較闻吸收能之化合物時,並未有特別 限定。例如二苯甲酮化合物、苯并三唑化合物、偶氮化合 物、萘化合物、蒽化合物、三哄化合物等。聚合物,例如 聚酯、聚醯亞胺 '聚苯乙烯、酚醛樹脂、聚縮醛樹脂 '丙 -63- (60) (60)1363251 烯酸聚合物等》具有以化學鍵結連結吸光性基之聚合物, 例如蒽環、萘環、苯環、咱琳環、喹喔啉環、噻唑環等具 有吸光性芳香環構造之聚合物。 又,塗佈有本發明之下層膜形成組成物的半導體基 板’其表面可具有以CVD法等所形成之無機系之反射防 止膜,且於其上方可形成本發明之下層膜。 使用本發明之下層膜形成組成物所形成之下層膜,由 微影成像步驟中所使用之曝光光線波長得知,其對於該光 線具有吸收,故於前述情形中,可將其作爲具有可防止基 板產生反射光之層,即作爲反射防止膜使用。 將下層膜於使用KrF電漿雷射(波長248nm)之微影 成像步驟中作爲反射防止膜使用時,於下層膜形成組成物 之固體成分中,以含有具蒽環或萘環成分者爲佳。又,將 下層膜於使用ArF電漿雷射(波長193nm)之微影成像步 驟中作爲反射防止膜使用時,於下層膜形成組成物之固體 成分中,以含有具苯環成分者爲佳。又,將下層膜於使用 F2電漿雷射(波長157nm)之微影成像步驟中作爲反射防 止膜使用時,於下層膜形成組成物之固體成分中,以含有 具溴原子或碘原子之化合物者爲佳。 又,本發明之下層膜,可作爲防止基板與光阻產生相 互作用之層、具有防止作爲光阻之材料或對光阻曝光時所 生成之物質對基板產生不良作用的機能之層、具有防止加 熱燒培時版所生成之物質擴散至上層光阻或對上層光阻產 生不良作用的機能之層、及作爲可減少半導體基板介電體 -64- (61) 1363251 層對光阻層產生毒害效果之阻隔層使用。 又,微影成像用下層膜形成組成物所形成之下層膜, 適用於雙炭刻製程(Dual Damascene Process)中形成有 通孔之基板中,作爲可無間隙塡滿通孔內部之嵌埋材料使 用’又,可作爲使基板表面平坦化之平坦化材料使用。 以下,本發明將以實施例作更具體之說明,但本發明 並不受前述實施例所限定。 【實施方式】 〔實施例〕 合成例1 h2c
ch3 Η (57) C—0~C—〇—CH2CH3 o ch3 於76g丙二醇單甲基醚乙酸酯中,溶解l〇g式(57) 所示之1-乙氧基乙基甲基丙烯酸酯(本州化學工業公司 製)與9g縮水甘油基甲基丙烯酸酯後,於溶液中使氮氣 流通3 0分鐘後,再昇溫至7 0 °C。反應溶液於保持7 〇 °C 下,添加〇.38g之偶氮異丁腈與〇.38g之1-十二烷硫醇。 於氮氣環境下,在70°C下攪拌8小時後,添加O.lg之4-甲氧基酚後,得含有1-乙氧基乙基甲基丙烯酸酯與縮水 甘油基甲基丙烯酸酯之共聚聚合物的溶液。對所得聚合物 -65- (62) 1363251 進行GPC分析結果,得知其數平均分子量Μη爲7 600, 重量平均分子量(以標準聚苯乙稀換算)Mw爲23000。 合成例2
於126.6g丙二醇單甲基醚乙酸酯中,溶解10g式 (57)所示之1-乙氧基乙基甲基丙烯酸酯(本州化學工 業公司製)、9g縮水甘油基甲基丙烯酸酯、及12.7g之甲 基甲基丙烯酸酯後,於溶液中使氮氣流通30分鐘後,再 昇溫至7〇°C。反應溶液於保持70°C下,添加0.63g之偶 氮異丁腈與〇.63g之卜十二烷硫醇。於氮氣環境下,在 7 0 °C下攪拌8小時後,添加0 . 1 g之4 -甲氧基酚後,得含 有1-乙氧基乙基甲基丙烯酸酯與縮水甘油基甲基丙烯酸 酯之共聚聚合物的溶液。對所得聚合物進行GPC分析結 果,得知其數平均分子量Μη爲5500,重量平均分子量 (以標準聚苯乙烯換算)Mw爲12000。
合成例 H2CV/CH3 T Η c-o-c-o 0 ch3
(58) 於38.0g乙酸丁酯中’溶解15g式(58)所示之卜環 己基氧乙基甲基丙烯酸酯(本州化學工業公司製)與l〇g -66 - 1363251 縮水甘油基甲基丙烯酸酯後,於溶液中使氮氣流通30分 鐘後,再昇溫至7(TC。反應溶液於保持70°C下,添加 〇.25g之偶氮異丁腈與〇.25g之1-十二烷硫醇。於氮氣環 境下,在70°C下攪拌8小時後,添加0.1 g之4-甲氧基酚 後,得含有1-環己氧基乙基甲基丙烯酸酯與縮水甘油基 甲基丙烯酸酯之共聚聚合物的溶液。對所得聚合物進行 GPC分析結果,得知其數平均分子量Μη爲9000,重量平 均分子量(以標準聚苯乙烯換算)Mw爲50000。 合成例4
C-O-C-O-CH2CH2CH2CH3 (59) 0 ch3
^CH3 ο
I
C-O—^ (60) II 0 於128g乳酸乙酯中,溶解10.5g式(59)所示之1-丁氧基乙基甲基丙烯酸酯' 8.0g縮水甘油基甲基丙烯酸 酯、及3.2g式(60)之丁內酯甲基丙烯酸酯後,於溶液 中使氮氣流通30分鐘後,再昇溫至70 °C。反應溶液於保 持70°C下,添加0.25g之偶氮異丁腈與0.25g之1·十二烷 硫醇。於氮氣環境下,在70 °C下攪拌8小時後,添加 1363251 O.lg之4-甲氧基酚後,得含有1-丁氧基乙基甲基丙烯酸 酯與縮水甘油基甲基丙烯酸酯與苄基甲基丙烯酸酯與丁內 酯甲基丙烯酸酯之共聚聚合物的溶液。對所得聚合物進行 GPC分析結果,得知其數平均分子量Μη爲7000,重量平 均分子量(以標準聚苯乙烯換算)Mw爲21000。 合成例5
?r°~c
(61) 於36.77g丙二醇單甲基醚乙酸酯中,溶解7.0g式 (5 7 )所示之1 -乙氧乙基甲基丙烯酸酯(本州化學工業 公司製)與8.15g式(61)所示之(3 -乙基-3-環氧丙烷 基)甲基甲基丙烯酸酯(大阪有機化學工業公司製)後, 於溶液中使氮氣流通30分鐘後,再昇溫至70°C。反應溶 液於保持7〇°C下,添加0.303g之偶氮異丁腈與0.303g之 1-十二烷硫醇。於氮氣環境下,在70 °C下攪拌8小時 後,添加O.lg之4·甲氧基酣後,得含有1-乙氧基乙基甲 基丙烯酸酯與環氧丙烷甲基丙烯酸酯之共聚聚合物的溶 液。對所得聚合物進行GPC分析結果,得知其數平均分 子量Μη爲4300,重量平均分子量(以標準聚苯乙烯換 算)Mw 爲 7900。 -68- (65) (65)1363251 合成例6 於78.88g丙二醇單甲基醚乙酸酯中,溶解8.0g式 (57)所示之1-乙氧乙基甲基丙烯酸酯(本州化學工業 公司製)、9.32g式(61)所示之(3 -乙基-3-環氧丙烷 基)甲基甲基丙烯酸酯(大阪有機化學工業公司製),及 15.19g甲基甲基丙烯酸酯後,於溶液中使氮氣流通30分 鐘後,再昇溫至7〇 °C。反應溶液於保持 70°C下,添加 0.650g之偶氮異丁腈與0.650g之1-十二烷硫醇。於氮氣 環境下,在7〇°C下攪拌8小時後,添加〇」g之4·甲氧基 酚後,得含有1-乙氧基乙基甲基丙烯酸酯與環氧丙烷甲 基丙烯酸酯與甲基甲基丙烯酸酯之共聚聚合物的溶液。對 所得聚合物進行GPC分析結果,得知其數平均分子量Μη 爲5000,重量平均分子量(以標準聚苯乙稀換算)Mw爲 9200 » 合成例7 於44.64 g丙二醇單甲基醚乙酸酯中,溶解3.43g式 (57)所示之1·乙氧乙基甲基丙烯酸酯(本州化學工業 公司製)、3.43 g式(61)所示之(3 -乙基-3·環氧丙烷 基)甲基甲基丙烯酸酯(大阪有機化學工業公司製),及 3.28g苄基甲基丙烯酸酯後,於溶液中使氮氣流通30分鐘 後,再昇溫至70°C »反應溶液於保持70°C下,添加〇.22g 之偶氮異丁腈與〇.22g之1-十二烷硫醇。於氮氣環境下, -69- (66) 1363251 在70 °C下攪拌8小時後,添加O.lg之4 -甲氧基酚後,得 含有1-乙氧基乙基甲基丙烯酸酯與環氧丙烷甲基丙烯酸 酯與苄基甲基丙烯酸酯之共聚聚合物的溶液。對所得聚合 物進行GPC分析結果,得知其數平均分子量Μη爲 22000’重量平均分子量(以標準聚苯乙烯換算)Mw爲 37000 〇 合成例
Γ'η2 Μ (62) 於46.4g丙二醇單甲基醚乙酸酯中,溶解5.0g式 (59)所示之1·丁氧乙基甲基丙烯酸酯、3.81g縮水甘油 基甲基丙烯酸酯、2.97g式(62)所示之9 -蒽基甲基甲基 丙烯酸酯,及6.99g甲基甲基丙烯酸酯後,於溶液中使氮 氣流通30分鐘後,再昇溫至80°C。反應溶液於保持80°C 下,添加〇.936g之偶氮異丁腈與〇.l87g之1-十二烷硫 醇。於氮氣環境下,在80 °C下攪拌8小時後,添加O.lg 之4-甲氧基酚後,得含有1-丁氧基乙基甲基丙烯酸酯與 縮水甘油基甲基丙烯酸酯與9-蒽甲基甲基丙烯酸酯與甲 基甲基丙烯酸酯之共聚聚合物的溶液。對所得聚合物進行 -70- (67)1363251 GPC分析結果,得知其數平均分子量Μη 均分子量(以標準聚苯乙烯換算)Mw爲 實施例1 於含有合成例1所得聚合物之溶液 20.6質量% ) 10g中,加入丙二醇骂 1.35g,及乳酸乙酯3.97g以形成13.5質 用孔徑0.05 /zm之聚乙烯製微過濾器過據 形成組成物之溶液。 爲3 1 00,重量平 8400 » (固體成分濃度 :甲基醚乙酸酯 量%溶液後,使 ,以調製下層膜 實施例2 於含有合成例2所得聚合物之溶液 20.6質量% ) l〇g中,加入丙二醇骂 1.35g,及乳酸乙酯3.97g以形成13.5質 用孔徑〇.〇5//m之聚乙烯製微過濾器過鴻 形成組成物之溶液。 (固體成分濃度 甲基醚乙酸酯 量%溶液後,使 ,以調製下層膜 實施例3 於含有合成例3所得聚合物之溶液 40.0質量% ) 10g中,加入乙酸丁酯12 7.72g以形成13.5質量%溶液後,使用孔 乙烯製微過濾器過濾,以調製下層膜形成 (固體成分濃度 .〇 g,及乳酸乙酯 徑0.05 μ m之聚 組成物之溶液。 實施例4 -71 - (68) 1363251 於含有合成例4所得聚合物之溶液(固體成 20.6質量% ) l〇g中,加入乳酸乙酯1.35g,及丙 甲基醚乙酸酯3.97g以形成13.5質量%溶液後, 徑0.05 // m之聚乙烯製微過濾器過濾,以調製下層 組成物之溶液。 實施例5 於含有合成例5所得聚合物之溶液(固體成 30質量% ) 10g中,加入乳酸乙酯6.52g,及丙二 基醚乙酸酯5.8〇g以形成13.5質量%溶液後,使 〇.〇5 之聚乙烯製微過濾器過濾,以調製下層膜 成物之溶液。 實施例6 於含有合成例6所得聚合物之溶液(固體成 30質量% ) 10g中,加入乳酸乙酯6.52g,及丙二 基醚乙酸酯5.80g以形成13.5質量?6溶液後,使 〇.〇5 /zm之聚乙烯製微過濾器過濾,以調製下層膜 成物之溶液。 實施例7 於含有合成例7所得聚合物之溶液(固體成 20質量% ) 10g中,加入乳酸乙酯l.Olg,及丙二 基醚乙酸酯3.86g以形成13.5質量%溶液後,使 分濃度 二醇單 使用孔 膜形成 分濃度 醇單甲 用孔徑 形成組 分濃度 醇單甲 用孔徑 形成組 分濃度 醇單甲 用孔徑 -72- (69) (69)1363251 0-05 之聚乙烯製微過濾器過濾,以調製下層膜形成組 成物之溶液。 實施例8 於含有合成例8所得聚合物之溶液(固體成分濃度 30質量% ) 50g中,加入乳酸乙酯30.4g,及丙二醇單甲 基醚乙酸酯36.0g以形成13.5質量%溶液後,使用孔徑 0.05 /zm之聚乙烯製微過濾器過濾,以調製下層膜形成組 成物之溶液。 光阻溶劑之溶離試驗 將實施例1至8 .所得之下層膜形成組成物溶液使用旋 轉塗佈器,塗佈於半導體基板(矽晶圓)上。於熱壓板上 以20 5 °C燒培1分鐘後形成下層膜(膜厚0.22 a m)。將 此下層膜浸漬於光阻所使用之溶劑,例如乳酸乙酯、丙二 醇單甲基醚乙酸酯及丙二醇單甲基醚中,確認其不溶於該 溶劑中。 光阻與內部缺陷試驗 將實施例1至8所得之下層膜形成組成物溶液使用旋 轉塗佈器,塗佈於矽晶圓上。於熱壓板上以205 °C燒培1 分鐘後形成下層膜(膜厚0.50/zm)。於此下層膜之上 層,使用旋轉塗佈器將市售之光阻溶液(使用富士寫真薄 膜公司製,商品名GARS8105G1與信越化學工業公司製, -73- (70) (70)1363251 商品名SEP R4 30)塗佈於其上。於熱壓板上以90 °C或110 t加熱5分鐘。將光阻曝光後’於90°C下進行1.5分鐘之 曝光後加熱。將光阻顯像後,測定下層膜之膜厚度’確認 出於下層膜與光阻間並未產生有內部缺陷等情形。 平坦化率、塡充性之試驗 將實施例1至8所得之下層膜形成組成物溶液使用旋 轉塗佈器,塗佈於具有孔洞(直徑〇.18/zm,深度1.0 ν m )之Si 02晶圓基板上。所使用之基板爲具有如圖1所示 孔洞之Iso (粗)與Dense (細密)圖型之 Si 02晶圓基 板。Iso圖型係指由某一孔洞中心至相鄰之另一孔洞中心 之間隔,爲該孔洞之直徑的5倍之圖型。又,Dense圖型 係指由某一孔洞中心至相鄰之另一孔洞中心之間隔,爲該 孔洞之直徑的1倍之圖型。孔洞之深度爲孔洞 之直徑爲0.]8//m。 塗佈後,於熱壓板上以2 0 5 °C燒培1分鐘後形成下層 膜’膜厚係測定非孔洞圖型附近之空曠地區,得知爲〇. 5 0 /zm。使用掃描型電子顯微鏡(SEM)觀察塗佈有實施例 1至8所得下層膜形成組成物之具有孔洞之Si02晶圓基板 的截面形狀,以評估下層膜之平坦化率。平坦化率爲依下 述平衡式計算。其中,將基板上之孔洞完全平坦化時之平 坦化率設定爲100% 。 -74- (71)1363251 平: 坦化率 ={1 ·(孔洞中心部之光 阻用塡充材 料 的 凹 陷深度 a ) / (孔洞之深度b) }x 100 其中,孔 洞內部並未 觀察出間隙, 同時觀察出 孔 洞 內 部塡充有下層 膜等結果。 [表 π 膜厚(nm ) 平坦化率(°/« |) Iso Dense Bias Iso Dense Bias 實施例1 500 400 100 100 100 0 實施例2 5 10 430 80 100 100 0 實施例3 500 380 120 100 100 0 實施例4 530 440 90 100 100 0 實施例5 490 430 60 100 100 0 實施例6 520 420 100 100 1 00 0 實施例7 500 4 10 90 100 100 0 實施例8 500 400 100 100 100 0 於實施例 1至8中, Iso ( 粗)與I: > e n s e (細密 ) 圖 型 上之下層膜之 膜厚度差( Bias) 可降至 極小。此點 推 測 爲 基板上: 之單位 面積中之孔洞數 (孔洞密度),即 使 於 較 I s 〇部爲大之 D e n s e部中 ,下層膜形成 組成物之溶 液 可 順 暢的流入大部 份之孔洞中 ,而得到一定 厚度之膜厚 > 其 結 果可降低Iso i 部與Dense 部之膜厚度差 ,進而增大 平 坦 化 率。又 ,使用1 實施例1至 8之下層膜形 成組成物結 果 Μ -75- (72) (72)1363251 論Iso部或Dense部,皆可達到平坦化結果。 光學參數之測定 將實施例4所得之下層膜形成組成物溶液使用旋轉塗 佈器塗佈於矽晶圓上。於熱壓板上以205 °C燒培1分鐘後 形成下層膜(膜厚0.20// m)。將此下層膜使用分光橢圓 測厚儀(Ellipsometer)測定波長193nm下之折射率(η値) 與衰減係數(k値)結果,得知折射率(η値)爲1·83, 孩減係數(k値)爲0.40。 將實施例7所得之下層膜形成組成物溶液使用旋轉塗 佈器塗佈於矽晶圓上。於熱壓板上以205 °C燒培1分鐘後 形成下層膜(膜厚0.20/zm)。將此下層膜使用分光橢圓 測厚儀測定波長1 93 nm下之折射率(η値)與衰減係數 (k値)結果,得知折射率(η値)爲1 · 8 1,衰減係數(k 値)爲0.3 8。 將實施例8所得之下層膜形成組成物溶液使用旋轉塗 佈器塗佈於矽晶圓上。於熱壓板上以2 0 5 °C燒培1分鐘後 形成下層膜(膜厚0.5 0 # m)。將此下層膜使用分光橢圓 測厚儀測定波長1 93 nm下之折射率(η値)與衰減係數 (k値)結果,得知折射率(π値)爲1 · 6 6 ’哀減係數(k 値)爲0.01又,測定波長24 8nm下之折射率(η値)與 衰減係數(k値)結果,得知折射率(η値)爲1 .5 0,衰 減係數(k値)爲0.26。 -76- (73) (73)1363251 乾蝕刻速度之試驗 將實施例1至8所得之下層膜形成組成物使用旋轉塗 佈器塗佈於矽晶圓上。於熱壓板上以2 05t燒培1分鐘後 形成下層膜(膜厚〇.22/zm)。將此下層膜使用日本科學 公司製RIE系列ES401,於乾蝕刻氣體使用CF4之條件下 測定乾蝕刻速度。其結果如表2所示。乾蝕刻之選擇性 爲,相對於將KrF雷射微影成像用光阻(信越化學工業公 司製,商品名SEPR430 )之乾蝕刻速度設定爲1.00時, 下層膜所顯示之乾蝕刻速度。 [表2] 乾蝕刻選擇性 實施例1 1.53 實施例2 1.53 實施例3 1.53 實施例4 1.45 實施例5 1.5 1 實施例6 1.50 實施例7 1.42 實施例8 1.25 確認出實施例1至8之下層膜形成組成物所得之下層 膜的蝕刻速度,與光阻相比較時爲較大。下層膜之乾蝕刻 速度必須較光阻之乾蝕刻速度爲快之理由爲,於下層膜上 -77- (74) (74)1363251 所形成之光阻經顯像後,經乾蝕刻使其露出基板底層之步 驟中,若下層膜之乾蝕刻速度快於光阻之乾蝕刻速度時, 可於光阻被切削之前去除下層膜,而使顯像之光阻的圖型 正確的轉印於基板上。 【圖式簡單說明】 圖1爲於具有孔洞之基板上形成下層膜之狀態的截面 圖。 【主要元件符號說明】 a :孔洞中心部之光阻用塡充材料的凹陷深度 b :所使用基板最初之孔洞深度 c :下層膜 d :基板 -78-

Claims (1)

1363251 |<)沒彳月/:^日修正本 第093122593號專利申請案中文申請專利範圍修正本 民國100年9月13日修正 申請專利範圍 物物 成合 組化 成的 形基 膜羧J; 層之劑 下護溶 用保及 像被, 成具物 影示合 微所化 種彡的 I 1基 C 之 1 式應 有反 含基 其特徵爲, 具有可與殘 一C-〇-C-〇-R4 (1) O HC—R3 r2 (式中,1^、尺2與r3各自表示氫原子或碳原子數1 至ίο之烷基,r4爲碳原子數1至ίο之烷基,又,r3與 b可相互鍵結形成環) 又,前述具被保護之羧基的化合物爲包含式(2)所示單 位構造之聚合物; ㈣ M-( _C一〇一C一〇一R4 (2) Ο HC—R3 (式中,L爲構成聚合物主鏈之鍵結基,Μ爲直接鍵 結或連結基) 具有可與前述羧基反應之基的化合物,爲至少含有2 1363251 個式(3)所示基之化合物,或含有由式(4)、式 (5)、式(6)、式(7)、式(8)與式(9)所成群中 所選出之至少1種單位構造之聚合物; —N—C—0—尺6 ⑶ 0 [式中,R5爲氫原子、碳原子數1至6之烷基或 • CH2OR7(式中,R7爲氫原子或碳原子數1至10之烷 基),R6爲氫原子或碳原子數1至10之烷基] •P Η Q—C 一 CH2 (4) 〇_(CH2)x
-P I Q ⑹
Ο >=〇 0—N=C=0 (8) Q I RgO^Si—ORi〇 0R8 (7) Q H2C—Ο (9) (式中,P爲構成聚合物主鏈之鍵結基,Q爲直接鍵結或 連結基,Rs、R9 ' R1G與Rn各自表示氫原子或碳原子數 1至1〇之院基,X爲0或1)。 2. —種微影成像用下層膜形成組成物,其特徵爲, 含有可與羧基反應之基與式(1)所示具被保護之羧基的 -2- 1363251 化合物,及溶劑, —C—0_C—0_R4 (1) II I 〇 hc-r3 r2 (式中,r,、r2與r3各自表示氫原子或碳原子數1 至10之烷基,R4爲碳原子數1至10之烷基,又,R3與 R4可相互鍵結形成環); 其中,前述化合物爲包含由式(2)所示單位構造,
i- R1 一C一Ο—C—Ο—R4 (2) Ο HC—R3 R2 (式中,L爲構成聚合物主鏈之鍵結基,μ爲直接鍵 結或連結基) 與,由式(4)、式(5)、式(6)、式(7) '式 (8)與式(9)所成群中所選出之至少1種單位構造之聚 合物; 1363251
I Q- ⑹ 〇 >=〇 Rg〇—Si-OR-|〇 or8(7) (8) QRi厂?-〒H2 H2〇—〇(9) (式中,p爲構成聚合物主鏈之鍵結基,Q爲直接鍵結或 連結基,R8、R9、R1C與Rm各自表示氫原子或碳原子數 1至10之烷基,X爲0或1) 或, 含有式(10)與式(11)所示單位構造之聚合物; ^12 十 ^13 十S—?卡2 H2 c=0 I H2 C=0 | Η ? I 〇 I R2—C—0—Ri ch2 I R3〇 R14—cp-(CH2)y r4 h2c-〇 (10) (11) (式中,R12與R 13各自表不氣原子 -4- Rl4爲氫 1363251 原子、甲基或乙基,y爲〇或1’ 31與S2爲構成聚合物之 各單位構造的莫耳比,S,爲0.05至〇.95,S2爲〇·〇5至 0.95 ) 或, 含有式(12)、式(13)與式(14)所示單位構造之聚合 物; C-H2 HC-R3 li「II _ 4 ) VCICIOICIOIR 2 -XMO R1 F<15+C_(^2 十 S-?卡3h2 6=0 H2 C=〇 I I o ^13 0 1ch2 R14—c_(〇H2)y H2C—〇 (13) ch2 Rl6 (14) (式中,Rl 5爲氫原子或甲基,Rl6爲氫原子、碳原 子數1至6之烷基、苯基、萘基或惠基’ h、〖2與t3爲構 成聚合物之各單位構造的莫耳比’ u爲〇.05至0·90’ t2 爲 0.05 至 0.90,t3 爲 0.05 至 Ο.90) ° 3.如申請專利範圍第1項之微影成像用下層膜形成 組成物,其中,含有式(1)所不具被保護之竣基的化合 物爲,至少含有2個式(1)所示具被保護之羧基,且分 子量爲200至2000之化合物。 -5- 1363251 4. 如申請專利範圍第1至3項中任一項之微影成像 用下層膜形成組成物,其尙含有吸光性化合物。 5. —種製造半導體裝置時所使用之下層膜的形成方 法,其特徵爲,將申請專利範圍第1至4項中任一項之微 影成像用下層膜形成組成物,塗佈、燒培於半導體基板上 之方法。 * 6. —種微影成像用下層膜,其特徵爲,將申請專利 ••範圍第1至4項中任一項之微影成像用下層膜形成組成 物,塗佈、燒培於半導體基板上所得者。 7. —種製造半導體裝置時所使用之光阻圖型的形成 . 方法,其特徵爲,包含將申請專利範圍第1至4項中任一 , 項之微影成像用下層膜形成組成物,塗佈、燒培於半導體 基板上,以形成下層膜之步驟,於該下層膜上形成光阻層 之步驟,對被覆有下層膜與光阻層之半導體基板進行曝光 之步驟,及於曝光後進行顯影之步驟等。 8.如申請專利範圍第7項之光阻圖型的形成方法, 其中,曝光爲以波長248nm、193nm或157nm之光線進
TW093122593A 2003-07-30 2004-07-28 Sublayer coating-forming composition for lithography containing compound having protected carboxy group TWI363251B (en)