RU2012127880A - Формовочные смеси, содержащие карбонатные соли, и их применение - Google Patents
Формовочные смеси, содержащие карбонатные соли, и их применение Download PDFInfo
- Publication number
- RU2012127880A RU2012127880A RU2012127880/02A RU2012127880A RU2012127880A RU 2012127880 A RU2012127880 A RU 2012127880A RU 2012127880/02 A RU2012127880/02 A RU 2012127880/02A RU 2012127880 A RU2012127880 A RU 2012127880A RU 2012127880 A RU2012127880 A RU 2012127880A
- Authority
- RU
- Russia
- Prior art keywords
- mold
- molding
- mixture according
- iron oxide
- molding sand
- Prior art date
Abstract
1. Формовочная смесь, содержащая:(а) заполнитель формовочной смеси; и(б) карбонатную соль в количестве, эффективном для снижения образования просечек в металлической отливке, изготовленной с использованием формовочной смеси.2. Формовочная смесь по п.1, отличающаяся тем, что она дополнительно содержит оксид железа, выбранный из группы, состоящей из красного оксида железа, черного оксида железа и их смесей.3. Формовочная смесь по п.2, отличающаяся тем, что оксидом железа является красный оксид железа.4. Формовочная смесь по п.3, отличающаяся тем, что заполнитель для формовочной смеси содержит кварцевый песок.5. Формовочная смесь по п.4, отличающаяся тем, что карбонатная соль выбрана из группы, состоящей из карбоната кальция, карбоната магния и их смесей.6. Формовочная смесь по п.5, отличающаяся тем, что в качестве источника карбоната кальция и/или карбоната магния она содержит доломит.7. Формовочная смесь по п.4, отличающаяся тем, что она дополнительно содержит гипс.8. Формовочная смесь по пп.5, 6 или 7, отличающаяся тем, что массовое соотношение карбонатной соли и красного оксида железа лежит в диапазоне от 1:1 до 4:1.9. Формовочная смесь по п.8, отличающаяся тем, что массовое соотношение карбонатной соли и красного оксида железа лежит в диапазоне от 1:1 до 2:1.10. Формовочная смесь по п.9, отличающаяся тем, что она содержит органическое связующее.11. Формовочная смесь по п.10, отличающаяся тем, что связующим является фенолуретановое связующее или эпоксиакрилатное связующее.12. Формовочная смесь по п.11, отличающаяся тем, что она содержит катализатор.13. Формовочная смесь по п.11, отличающаяся тем, что количество соли в формовочной смеси лежит в �
Claims (23)
1. Формовочная смесь, содержащая:
(а) заполнитель формовочной смеси; и
(б) карбонатную соль в количестве, эффективном для снижения образования просечек в металлической отливке, изготовленной с использованием формовочной смеси.
2. Формовочная смесь по п.1, отличающаяся тем, что она дополнительно содержит оксид железа, выбранный из группы, состоящей из красного оксида железа, черного оксида железа и их смесей.
3. Формовочная смесь по п.2, отличающаяся тем, что оксидом железа является красный оксид железа.
4. Формовочная смесь по п.3, отличающаяся тем, что заполнитель для формовочной смеси содержит кварцевый песок.
5. Формовочная смесь по п.4, отличающаяся тем, что карбонатная соль выбрана из группы, состоящей из карбоната кальция, карбоната магния и их смесей.
6. Формовочная смесь по п.5, отличающаяся тем, что в качестве источника карбоната кальция и/или карбоната магния она содержит доломит.
7. Формовочная смесь по п.4, отличающаяся тем, что она дополнительно содержит гипс.
8. Формовочная смесь по пп.5, 6 или 7, отличающаяся тем, что массовое соотношение карбонатной соли и красного оксида железа лежит в диапазоне от 1:1 до 4:1.
9. Формовочная смесь по п.8, отличающаяся тем, что массовое соотношение карбонатной соли и красного оксида железа лежит в диапазоне от 1:1 до 2:1.
10. Формовочная смесь по п.9, отличающаяся тем, что она содержит органическое связующее.
11. Формовочная смесь по п.10, отличающаяся тем, что связующим является фенолуретановое связующее или эпоксиакрилатное связующее.
12. Формовочная смесь по п.11, отличающаяся тем, что она содержит катализатор.
13. Формовочная смесь по п.11, отличающаяся тем, что количество соли в формовочной смеси лежит в диапазоне от 0,5 до 4,0% от массы заполнителя для формовочной смеси.
14. Формовочная смесь по п.12, отличающаяся тем, что количество соли в формовочной смеси лежит в диапазоне от 0,5 до 4,0% от массы заполнителя для формовочной смеси.
15. Формовочная смесь по п.11, отличающаяся тем, что количество соли в формовочной смеси лежит в диапазоне от 0,5 до 2,5% от массы заполнителя для формовочной смеси.
16. Формовочная смесь по п.12, отличающаяся тем, что количество соли в формовочной смеси лежит в диапазоне от 0,5 до 2,5% от массы заполнителя для формовочной смеси.
17. Способ изготовления литейной формы методом cold-box, включающий:
(а) помещение формовочной смеси по п.15 в модель для получения литейной формы;
(б) обеспечение контакта литейной формы, полученной на стадии (а), с парообразным катализатором отверждения, способным отвердить форму;
(в) отверждение литейной формы, полученной на стадии (б), до тех пор, пока эта форма не станет пригодной для обращения; и
(г) извлечение литейной формы из модели.
18. Способ литья металлических деталей, включающий:
(а) введение литейной формы, изготовленной способом по п.15, в литейную форму в сборке;
(б) заливку металла, находящегося в жидком состоянии, в форму в сборке;
(в) охлаждение и отверждение металла; и
(г) отделение отлитой металлической детали от формы в сборке.
19. Металлическая деталь, изготовленная способом по п.18.
20. Способ изготовления литейной формы методом no-bake, включающий:
(а) помещение формовочной смеси по п.12 в модель для получения литейной формы;
(б) отверждение литейной формы, полученной на стадии (а), до тех пор, пока эта форма не станет пригодной для обращения; и
(в) извлечение литейной формы из модели.
21. Способ литья металлической детали, включающий:
(а) введение литейной формы, изготовленной способом по п.20, в литейную форму в сборке;
(б) заливку металла, находящегося в жидком состоянии, в форму в сборке;
(в) охлаждение и отверждение металла; и
(г) отделение отлитой металлической детали от формы в сборке.
22. Способ изготовления литейной формы методом warm-box, включающий:
(а) помещение формовочной смеси по п.12 в модель для получения литейной формы;
(б) нагревание литейной формы до температуры в диапазоне от 150°C до 260°C;
(в) отверждение литейной формы до тех пор, пока эта форма не станет пригодной для обращения; и
(г) извлечение литейной формы из модели.
23. Способ литья металлической детали, включающий:
(а) введение литейной формы, изготовленной способом по п.17 или 20, в литейную форму в сборке;
(б) заливку металла, находящегося в жидком состоянии, в форму в сборке;
(в) охлаждение и отверждение металла; и
(г) отделение отлитой металлической детали от формы в сборке.