JPH05330847A - 着色ガラス組成物及びこのガラスを用いた窓ガラス - Google Patents
着色ガラス組成物及びこのガラスを用いた窓ガラスInfo
- Publication number
- JPH05330847A JPH05330847A JP3080021A JP8002191A JPH05330847A JP H05330847 A JPH05330847 A JP H05330847A JP 3080021 A JP3080021 A JP 3080021A JP 8002191 A JP8002191 A JP 8002191A JP H05330847 A JPH05330847 A JP H05330847A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- glass
- total
- weight
- colored glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【目的】 ガラス板又は窓ガラスを製造するための着色
ガラス組成物を提供することを目的とする。 【構成】 本着色ガラスは、Fe2O3 で表した酸化鉄を1.
4〜4wt%及び酸化コバルトを0〜0.05wt%含み、Fe2O
3 が約2wt%未満の場合には酸化コバルトが約0.02wt%
より多く、そして必要に応じて更にセレン及び酸化クロ
ムを含み、 Co O+Se+Cr2O3 の合計を0.24wt%とする
ことができる着色剤を含んでなるソーダ−石灰−シリカ
ガラスである。このガラスは、厚さ3.85mmに対して、A
光源の全光透過率が約20%以下であり且つ全エネルギー
透過率が約12%以下である。このガラスは特に自動車用
サンルーフに適する。
ガラス組成物を提供することを目的とする。 【構成】 本着色ガラスは、Fe2O3 で表した酸化鉄を1.
4〜4wt%及び酸化コバルトを0〜0.05wt%含み、Fe2O
3 が約2wt%未満の場合には酸化コバルトが約0.02wt%
より多く、そして必要に応じて更にセレン及び酸化クロ
ムを含み、 Co O+Se+Cr2O3 の合計を0.24wt%とする
ことができる着色剤を含んでなるソーダ−石灰−シリカ
ガラスである。このガラスは、厚さ3.85mmに対して、A
光源の全光透過率が約20%以下であり且つ全エネルギー
透過率が約12%以下である。このガラスは特に自動車用
サンルーフに適する。
Description
【0001】
【産業上の利用分野】本発明は窓ガラス、特に自動車用
窓ガラスの製造に適合できる着色ガラス組成物に関す
る。更に詳しくは、車のサンルーフを形成することがで
きる窓ガラスの製造を可能にするガラス組成物に関す
る。
窓ガラスの製造に適合できる着色ガラス組成物に関す
る。更に詳しくは、車のサンルーフを形成することがで
きる窓ガラスの製造を可能にするガラス組成物に関す
る。
【0002】機能的な目的をもち且つ人目を引く外觀と
なる着色した自動車用窓ガラスが注目されている。ニュ
ーモデルでガラスをはめた外面が増々増加することから
この傾向は明らかである。
なる着色した自動車用窓ガラスが注目されている。ニュ
ーモデルでガラスをはめた外面が増々増加することから
この傾向は明らかである。
【0003】上記開発の結果として、車内空調において
考慮すべき温室効果が重要な要素となる。サンルーフと
して用いる窓ガラスの場合には特にそうである。
考慮すべき温室効果が重要な要素となる。サンルーフと
して用いる窓ガラスの場合には特にそうである。
【0004】
【発明が解決しようとする課題】本発明は、均一に高度
に着色した、特に灰青色又は緑色に着色したガラスであ
って、しかも任意の厚さにおいて非常に低い全光透過率
及び全エネルギー透過率を有するガラスを提供すること
を目的とする。
に着色した、特に灰青色又は緑色に着色したガラスであ
って、しかも任意の厚さにおいて非常に低い全光透過率
及び全エネルギー透過率を有するガラスを提供すること
を目的とする。
【0005】
【課題を解決するための手段】本発明に従って、以下に
示す成分を含む組成物からなる着色ガラスによって上記
目的を達成することができる。すなわち主成分が、 SiO2:64〜75重量パーセント Al2O3 :0〜5 B2O3:0〜5 CaO :5〜15 MgO :0〜5 Na2O:10〜18 K2O :0〜5 で表される組成及び含有率の酸化物からなり、アルカリ
土類酸化物の合計は6〜16重量パーセントであり、アル
カリ金属酸化物の合計が10〜20重量パーセントであり、
且つ着色剤として以下に示す成分を含み、 Fe2O3(全鉄分):1.4〜4重量パーセント C o O :0〜0.05 Fe2O3 含有率が約2重量パーセント未満の場合には Co
O 含有率が約0.02重量パーセントより大きく、そして必
要に応じて更にセレン及び酸化クロムを含み、 C o O +
Se +Cr2O3 の合計が0.24重量パーセント以下である着
色ガラス組成物である。この着色ガラス組成物から作る
ガラスは、厚さ3.85mmに対して、A光源の全光透過率
(TLA ) が約20%以下であり且つ全エネルギー透過率
(TE ) が約12%以下である。
示す成分を含む組成物からなる着色ガラスによって上記
目的を達成することができる。すなわち主成分が、 SiO2:64〜75重量パーセント Al2O3 :0〜5 B2O3:0〜5 CaO :5〜15 MgO :0〜5 Na2O:10〜18 K2O :0〜5 で表される組成及び含有率の酸化物からなり、アルカリ
土類酸化物の合計は6〜16重量パーセントであり、アル
カリ金属酸化物の合計が10〜20重量パーセントであり、
且つ着色剤として以下に示す成分を含み、 Fe2O3(全鉄分):1.4〜4重量パーセント C o O :0〜0.05 Fe2O3 含有率が約2重量パーセント未満の場合には Co
O 含有率が約0.02重量パーセントより大きく、そして必
要に応じて更にセレン及び酸化クロムを含み、 C o O +
Se +Cr2O3 の合計が0.24重量パーセント以下である着
色ガラス組成物である。この着色ガラス組成物から作る
ガラスは、厚さ3.85mmに対して、A光源の全光透過率
(TLA ) が約20%以下であり且つ全エネルギー透過率
(TE ) が約12%以下である。
【0006】ガラスの酸化還元電位、すなわち酸化第二
鉄の形で表した全鉄分に対する酸化第一鉄の比率が約0.
16〜約0.40である条件下で本発明に従うガラスを製造す
る。本発明に従うガラスの大部分そして鉄含有率が約2
重量パーセント以上を有するガラスは少なくとも電気炉
で製造され、他のガラスは普通の反射炉に適合する。
鉄の形で表した全鉄分に対する酸化第一鉄の比率が約0.
16〜約0.40である条件下で本発明に従うガラスを製造す
る。本発明に従うガラスの大部分そして鉄含有率が約2
重量パーセント以上を有するガラスは少なくとも電気炉
で製造され、他のガラスは普通の反射炉に適合する。
【0007】任意の厚さに対して、本発明に従う着色ガ
ラスは約15%より低く又は12%以下である全光透過率を
有するものが好ましい。一般にこれらガラスの全エネル
ギー透過率は約8%よりも低い。
ラスは約15%より低く又は12%以下である全光透過率を
有するものが好ましい。一般にこれらガラスの全エネル
ギー透過率は約8%よりも低い。
【0008】所望の光学的特性、特に上述した透過率を
得るために、選んだ厚みを考慮してガラス中の着色剤の
正確な百分比を調整することができる。
得るために、選んだ厚みを考慮してガラス中の着色剤の
正確な百分比を調整することができる。
【0009】従って、厚さ3.85mmに対して、Fe2O3 で表
した全酸化鉄含有率が約3重量パーセントを越える場合
には、単一着色剤として酸化鉄を本発明に従う着色ガラ
スに混ぜることができる。これらのガラスに対して、酸
化還元電位を好ましくは0.30以下に保つように製造条件
をコントロールする。このようにして得たガラスのC光
源で照らした主波長は約500 〜570 ナノノートル(nm)で
ある。
した全酸化鉄含有率が約3重量パーセントを越える場合
には、単一着色剤として酸化鉄を本発明に従う着色ガラ
スに混ぜることができる。これらのガラスに対して、酸
化還元電位を好ましくは0.30以下に保つように製造条件
をコントロールする。このようにして得たガラスのC光
源で照らした主波長は約500 〜570 ナノノートル(nm)で
ある。
【0010】更に同じ厚みに対して、Fe2O3 で表した全
酸化鉄含有率が約3重量パーセント以下である本発明に
従う着色ガラスに、着色剤として酸化コバルトを混ぜる
ことができる。
酸化鉄含有率が約3重量パーセント以下である本発明に
従う着色ガラスに、着色剤として酸化コバルトを混ぜる
ことができる。
【0011】それ故本発明の態様の1つに従って、着色
ガラスは約2〜3重量パーセントのFe2O3 及び約140 〜
400ppmの Co O 、そして任意付加的に50ppm までのセレ
ンを有する。
ガラスは約2〜3重量パーセントのFe2O3 及び約140 〜
400ppmの Co O 、そして任意付加的に50ppm までのセレ
ンを有する。
【0012】一般に、これらのガラスはC光源で約485
〜505nm の主波長をもつ。全エネルギー透過率は約10%
以下であり、そして一般に4〜6.5%である。一般に、
これらガラスのC光源での刺激純度は約30%より小さ
い。著しく低い全光透過率を有する本発明に従うガラス
は、カラーニュートラリティにはなはだしく有害な作用
を及ぼすことなしに比較的高い刺激純度を有することが
できる。
〜505nm の主波長をもつ。全エネルギー透過率は約10%
以下であり、そして一般に4〜6.5%である。一般に、
これらガラスのC光源での刺激純度は約30%より小さ
い。著しく低い全光透過率を有する本発明に従うガラス
は、カラーニュートラリティにはなはだしく有害な作用
を及ぼすことなしに比較的高い刺激純度を有することが
できる。
【0013】本発明に従うガラスは以下の重量比率であ
る低い含有率の酸化コバルト及びセレンを含むことがで
きる。 Fe2O3 :1.4〜2.5重量パーセント C o O :150 〜330ppm Se :10〜35ppm
る低い含有率の酸化コバルト及びセレンを含むことがで
きる。 Fe2O3 :1.4〜2.5重量パーセント C o O :150 〜330ppm Se :10〜35ppm
【0014】これらのガラスは、C光源で照らして約48
5 〜570nm の主波長を有し、そして一般に刺激純度は20
%より低い。全エネルギー透過率は10%より低く、そし
て通常5〜8%である。主波長が485 〜500nm であるガ
ラスは美感上の理由で好ましい。
5 〜570nm の主波長を有し、そして一般に刺激純度は20
%より低い。全エネルギー透過率は10%より低く、そし
て通常5〜8%である。主波長が485 〜500nm であるガ
ラスは美感上の理由で好ましい。
【0015】厚さ3.85mmに対して、Fe2O3 で表した全酸
化鉄含有率が約2.5重量パーセント以下である本発明に
従う着色ガラスに酸化コバルト及び酸化クロムを組込む
ことができる。
化鉄含有率が約2.5重量パーセント以下である本発明に
従う着色ガラスに酸化コバルト及び酸化クロムを組込む
ことができる。
【0016】それ故、本発明の態様の1つに従って、着
色ガラスは、約1.5〜2.5重量パーセントのFe2O3 、約
150 〜300ppmの酸化コバルト、そして700 〜2000ppm の
酸化クロムを含む。C光源で照らす場合、これらのガラ
スは約490 〜510nm の主波長、そして約10〜25%の刺激
純度を有する。全エネルギー透過率は10%より低く、そ
して一般に約5〜8%である。
色ガラスは、約1.5〜2.5重量パーセントのFe2O3 、約
150 〜300ppmの酸化コバルト、そして700 〜2000ppm の
酸化クロムを含む。C光源で照らす場合、これらのガラ
スは約490 〜510nm の主波長、そして約10〜25%の刺激
純度を有する。全エネルギー透過率は10%より低く、そ
して一般に約5〜8%である。
【0017】本発明に従ってガラスを製造するために、
用いる基本組成物は平板ガラス業界で用いる普通のガラ
ス組成物であり、任意の厚さに対して所望の光学的特性
及び外觀を得ることができる比率に従って着色剤をガラ
ス組成物に加える。選んだ基本ガラスは以下の重量組成
をもつ。 SiO2:72.1重量パーセント Al2O3 :0.74 CaO :8.90 MgO :3.79 Na2O:14.16 K2O :0.11 SO3 :0.20 シリカ分を減らしてこのガラスに着色剤を加える。
用いる基本組成物は平板ガラス業界で用いる普通のガラ
ス組成物であり、任意の厚さに対して所望の光学的特性
及び外觀を得ることができる比率に従って着色剤をガラ
ス組成物に加える。選んだ基本ガラスは以下の重量組成
をもつ。 SiO2:72.1重量パーセント Al2O3 :0.74 CaO :8.90 MgO :3.79 Na2O:14.16 K2O :0.11 SO3 :0.20 シリカ分を減らしてこのガラスに着色剤を加える。
【0018】着色剤の異なる組合せの例を表1に示す。
厚さ3.85mmの窓ガラスで光学的特性を測定した。
厚さ3.85mmの窓ガラスで光学的特性を測定した。
【0019】これらガラスの酸化還元電位が好ましくは
0.35以下となる条件でガラスを溶融する。
0.35以下となる条件でガラスを溶融する。
【0020】酸化鉄と酸化コバルトを組合わせ、そして
鉄含有率が約2〜3重量パーセントにて着色したガラス
に対して、厚さ3.85mmの窓ガラスの場合少なくとも約14
0ppmの Co O を入れることが望ましい。この含有率より
低いと、ガラスの光透過率は増加する傾向にあり、15%
を越えることもありうる。
鉄含有率が約2〜3重量パーセントにて着色したガラス
に対して、厚さ3.85mmの窓ガラスの場合少なくとも約14
0ppmの Co O を入れることが望ましい。この含有率より
低いと、ガラスの光透過率は増加する傾向にあり、15%
を越えることもありうる。
【0021】セレン、酸化鉄及び酸化コバルトを組合わ
せて着色したガラスに対して、厚さ3.85mmの窓ガラスの
場合少なくとも1.4重量パーセントの酸化鉄を入れるこ
とが望ましい。この含有率より低いと、ガラスの光透過
率及びエネルギー透過率はそれぞれ15及び12%を越えて
しまう。
せて着色したガラスに対して、厚さ3.85mmの窓ガラスの
場合少なくとも1.4重量パーセントの酸化鉄を入れるこ
とが望ましい。この含有率より低いと、ガラスの光透過
率及びエネルギー透過率はそれぞれ15及び12%を越えて
しまう。
【0022】表1に示すガラス組成物及び着色剤の組合
わせに関して上述した値は単なる例示であって、本発明
はこれらに限定されるものではない。
わせに関して上述した値は単なる例示であって、本発明
はこれらに限定されるものではない。
【0023】電極棒を備えた炉でガラスを製造する場合
には、本発明に従うガラスは平板ガラスを製造する普通
の方法に適合する。サンルーフ用の窓ガラスを作りたい
場合、例えば溶融ガラスを錫浴上で層にして作るガラス
のリボンの厚さを2〜10mmに、そして好ましくは3〜6
mmに変えることができる。
には、本発明に従うガラスは平板ガラスを製造する普通
の方法に適合する。サンルーフ用の窓ガラスを作りたい
場合、例えば溶融ガラスを錫浴上で層にして作るガラス
のリボンの厚さを2〜10mmに、そして好ましくは3〜6
mmに変えることができる。
【0024】本発明に従って着色ガラスのリボンを切断
し、必要に応じて更にベンディングして作った窓ガラス
は、美觀上の要求及び乗客の快適さに関する要求を満足
させるような自動車用サンルーフを製造するために直接
使用できるという利点を有する。
し、必要に応じて更にベンディングして作った窓ガラス
は、美觀上の要求及び乗客の快適さに関する要求を満足
させるような自動車用サンルーフを製造するために直接
使用できるという利点を有する。
【0025】別の窓ガラスの場合、本発明に従って作っ
た窓ガラスを前もって表面処理することができ、あるい
は例えば未着色ガラスのシート、耐損傷特性を有するポ
リウレタン系フィルム、あるいは破損の場合の密封性を
確保するフィルムのような有機コーティングと組合わせ
ることができる。更に、例えばエナメルコーティングで
部分的にコーティングすることもできる。
た窓ガラスを前もって表面処理することができ、あるい
は例えば未着色ガラスのシート、耐損傷特性を有するポ
リウレタン系フィルム、あるいは破損の場合の密封性を
確保するフィルムのような有機コーティングと組合わせ
ることができる。更に、例えばエナメルコーティングで
部分的にコーティングすることもできる。
【0026】熱分解又は化学気相蒸着(CVD) のような高
温化学蒸着、あるいは真空蒸着によって得る少なくとも
1つの金属酸化物被膜でもって、本発明に従う窓ガラス
をコーティングすることができる。
温化学蒸着、あるいは真空蒸着によって得る少なくとも
1つの金属酸化物被膜でもって、本発明に従う窓ガラス
をコーティングすることができる。
【0027】それ故、本発明に従う窓ガラスを酸化錫系
塗料でコーティングすることができる。自動車用サンル
ーフを形成する窓ガラスの場合、このコーティングによ
って温度の快適さを更に改善することができる。このよ
うなコーティングは周知の方法、例えば、有機錫化合物
を熱分解することからなるヨーロッパ特許第121,459号
に記述されている方法に従っておこなうことができる。
塗料でコーティングすることができる。自動車用サンル
ーフを形成する窓ガラスの場合、このコーティングによ
って温度の快適さを更に改善することができる。このよ
うなコーティングは周知の方法、例えば、有機錫化合物
を熱分解することからなるヨーロッパ特許第121,459号
に記述されている方法に従っておこなうことができる。
【表1】
───────────────────────────────────────────────────── フロントページの続き (72)発明者 ペドロ カサリエゴ アルバレツ スペイン国,エー−33400 サリナス,ア ベニュ ルイ オーゾール,18
Claims (12)
- 【請求項1】 主成分が、 SiO2:64〜75重量パーセント Al2O3 :0〜5 B2O3:0〜5 CaO :5〜15 MgO :0〜5 Na2O:10〜18 K2O :0〜5 で表される組成及び含有率の酸化物からなり、アルカリ
土類酸化物の合計が6〜16重量パーセントであり、アル
カリ金属酸化物の合計が10〜20重量パーセントであり;
そして着色剤として、 Fe2O3(全鉄分):1.4〜4重量パーセント C o O :0〜0.05 を含み、Fe2O3 含有率が約2重量パーセント未満の場合
に Co O 含有率が約0.02重量パーセントより大きく、そ
して必要に応じて更にセレン及び酸化クロムを含み、 C
o O +Se +Cr2O3 の合計が0.24重量パーセント以下で
ある着色ガラス組成物であって、該着色ガラス組成物か
ら作るガラスは、厚さ3.85mmに対してA光源の全光透過
率(TLA ) が約20%以下であり且つ全エネルギー透過率
(TE ) が約12%以下である前記着色ガラス組成物。 - 【請求項2】 該組成物の FeO含有率が、Fe2O3 の形で
表した全鉄分の16〜40重量パーセントであることを特徴
とする請求項1記載の組成物。 - 【請求項3】 該組成物が、着色剤としてFe2O3 の形で
表した3〜4重量パーセントの酸化鉄を含んでなること
を特徴とする請求項1又は請求項2記載の組成物。 - 【請求項4】 該組成物が着色剤として、 Fe2O3(全鉄分):2〜3重量パーセント C o O :0.014 〜0.04 Se :0〜0.005 を含んでなることを特徴とする請求項1又は請求項2記
載の組成物。 - 【請求項5】 該組成物が着色剤として、 Fe2O3(全鉄分):1.4〜2.5重量パーセント C o O :0.015 〜0.033 Se :0.0010〜0.0035 を含んでなることを特徴とする請求項1又は請求項2記
載の組成物。 - 【請求項6】 該組成物が着色剤として、 Fe2O3(全鉄分):1.4〜2.5重量パーセント C o O :0.015 〜0.030 Cr2O3 :0.07〜0.2 を含んでなることを特徴とする請求項1又は請求項2記
載の組成物。 - 【請求項7】 請求項3記載のガラス組成物であること
を特徴とする着色ガラス板を組込む窓ガラス。 - 【請求項8】 請求項4記載のガラス組成物であること
を特徴とする着色ガラス板を組込む窓ガラス。 - 【請求項9】 請求項5記載のガラス組成物であること
を特徴とする着色ガラス板を組込む窓ガラス。 - 【請求項10】 請求項6記載のガラス組成物であること
を特徴とする着色ガラス板を組込む窓ガラス。 - 【請求項11】 厚さが2〜10ミリメートル、そして好ま
しくは3〜6ミリメートルである着色ガラス板で作るこ
とを特徴とする請求項7〜10のいずれか1項に記載の窓
ガラス。 - 【請求項12】 酸化錫被膜のような少なくとも1つの金
属酸化物被覆でコーティングすることを特徴とする請求
項11記載の窓ガラス。