PL168341B1 - Barwiona kompozycja szklana PL - Google Patents
Barwiona kompozycja szklana PLInfo
- Publication number
- PL168341B1 PL168341B1 PL91289844A PL28984491A PL168341B1 PL 168341 B1 PL168341 B1 PL 168341B1 PL 91289844 A PL91289844 A PL 91289844A PL 28984491 A PL28984491 A PL 28984491A PL 168341 B1 PL168341 B1 PL 168341B1
- Authority
- PL
- Poland
- Prior art keywords
- coo
- glasses
- composition
- coloring agents
- glass
- Prior art date
Abstract
1. Barwiona kompozycja szklana zawierajaca nastepujace tlenki w podanych zakre- sach wagowych S i0 2 64 do 75%, A120 3 0 do 5%, B20 3 do 5%, CaO 5 do 15%, MgO 0 do 5%, Na2 0 10 do 18%, K2 0 0 do 5%, przy czym suma tlenków metali ziem alkalicznych zawarta jest w zakresie 6 i 16%, a tlenków metali alkalicznych zawarta jest w zakresie 1 0 i 2 0 %, znam ienna tym, ze zawiera jako czynniki barwiace w podanych zakresach wago- wych Fe20 3 (calkowite zelazo) 1,4 do 4,8%, CoO 0 do 0,05% z CoOniz okolo 0,02%, je - zeli Fe2O 3niz okolo 2%, jak równiez ewentualnie selen i tlenek chromu, przy czym suma CoO + Se + Cr20 3 wynosi najwyzej 0,24%. PL
Description
Przedmiotem wynalazku jest barwiona kompozycja szklana do wytwarzania przeszkleń, zwłaszcza osadzonych w pojazdach mechanicznych lub samochodach. Wynalazek dotyczy szczególnie kompozycji szklanej umożliwiającej przeszklenie słoneczne dachu samochodu.
Projektanci samochodów proponują swoim klientom przeszklenia z barwionego szkła spełniającego cel funkcjonalny, które muszą mieć atrakcyjny wygląd. Tendencję tę potwierdza zwiększające się wciąż powlekanie powierzchni w nowych modelach pojazdów mechanicznych w porównaniu ze starszymi typami.
W wyniku rozwijania przeszkleń występuje efekt cieplarniany będący ważnym czynnikiem, który należy uwzględniać w klimatyzowanych samochodach. Jest to szczególnie istotne w przypadku przeszkleń używanych jako dach słoneczny samochodu.
Zgodnie z wynalazkiem proponuje się szkła wysoce barwione w masie, a szczególnie szkła szaro-niebieskie lub zielone, które są odpowiednie do zastosowania i które, dla danej grubości, mają bardzo niskie całkowite przenoszenie światła i całkowite przenoszenie energii.
Przedmiotem wynalazku jest barwiona kompozycja szklana zawierająca następujące tlenki w podanych zakresach wagowych:
SiOo : 6-4 do 75%o
A12O3 : o do 5%
B2O3 : 0 do 5%
CaO : 5 do 15%o
MgO : 0 do 5%
Na20 : 10 do 18%
K2O : 0 do 5% przy czym suma tlenków metali ziem alkalicznych zawarta jest w zakresie 6 i 16%, a tlenków metali alkalicznych zawarta jest w zakresie 10 i 20%, która zgodnie z wynalazkiem zawiera jako czynniki barwiące w podanych zakresach wagowych:
Fe203 (całkowite żelazo) : k4do4%
CoO : 0 do 0,05%)
168 341 z CoO>niż około 0,02%, jeżeli Fe203<niż około 2%, jak również ewentualnie selen i tlenek chromu, przy czym suma CoO + Se + CiAT wynosi najwyżej 0,24%. Takie szkło ma współczynnik przepuszczania całkowitego światła oświetlacza A /Tla/ równy lub niższy od około 20%, a współczynnik przepuszczania całkowitej energii /Te/ równy lub niższy od około 12%» dla grubości 3,85 mm.
Szkła według wynalazku wytwarza się w takich warunkach, że ich potencjał redoks, czyli stosunek tlenku żelazawego do całkowitej ilości żelaza wyrażonej w postaci tlenku żelazowego, pozostaje pomiędzy około 0,16 i około 0,40. Większość szkieł według wynalazku, a co najmniej te mające zawartość żelaza równą lub wyższą od około 2%, wytwarza się w piecach elektrycznych, a pozostałe są zgodne ze znanymi piecami rewerberacyjnymi.
Dla danej grubości, barwione szkła według wynalazku mają korzystnie przepuszczanie całkowitego światła poniżej około 15% lub nawet poniżej 12%. Przepuszczanie całkowitej energii tych szkieł jest zwykle poniżej około 8%.
W celu otrzymania potrzebnych charakterystyk optycznych, a szczególnie wspomnianych wyżej wartości przepuszczania, dokładne udziały procentowe czynników barwiących w szkle będą regulowane z uwzględnieniem wybranej grubości.
Tak więc dla grubości 3,85 milimetrów barwione szkła według wynalazku mogą mieć włączone jako jedyne czynniki barwiące tlenki żelaza, jeżeli ich całkowita zawartość, wyrażona w Fe203, przewyższa około 3%. Dla tych szkieł warunki produkcji są kontrolowane w taki sposób, żeby ich potencjał redoks pozostawał korzystnie równy lub niższy od 0,30. Przeważająca długość fali otrzymanych w ten sposób szkieł i oświetlanych oświetlaczem C jest pomiędzy około 500 i 570 nonametrów.
Dla pewnych grubości, barwione szkła według wynalazku, których całkowita zawartość tlenku żelaza, wyrażona jako Fe203, jest równa lub niższa od około 3%, mogą również zawierać jako czynnik barwiący tlenek kobaltu.
Tak więc według jednego z aspektów wynalazku barwione szkła zawierają pomiędzy około 2 i 3% Feo03 i około 140 do 400 ppm CoO i ewentualnie do 50 ppm selenu.
Na ogół szkła te mają przeważającą długość fali przy oświetlaczu C pomiędzy około 485 i 505 nm. Ich współczynnik przenoszenia całkowitej energii jest równy lub niższy od około 10%o, a zwykle jest około 4 i 6,5%. Czystość wzbudzenia tych szkieł przy oświetlaczu C jest zwykle poniżej około 30%o. Szkła według wynalazku mające szczególnie niski współczynnik przenoszenia całkowitego światła mogą mieć względnie wysoką czystość wzbudzenia, nie mając stosunkowo wysokiej czystości wzbudzania bez nadmiernie szkodliwego wpływu na neutralność barwy.
Szkła według wynalazku mogą mieć niższą zawartość związaną z tlenkiem kobaltu i selenem, zgodnie z następującymi proporcjami wagowymi.
Fe203 : 1,4 do 2,5%
CoO : 150 do 330 ppm
Selen : 10 do 35 ppm
Szkła te oświetlane oświetlaczem C mają dominującą długość fali pomiędzy około 485 i 570 nm, a ich czystość wzbudzenia jest zwykle poniżej 20%. Ich współczynnik przepuszczania całkowitej energii jest niższy od 10%, a zwykle jest pomiędzy 5 i 8%o. Szkła o dominującej długości fali pomiędzy około 485 i 500 nm są korzystne ze względów estetycznych.
Dla grubości 3,85 mm, barwione szkła według wynalazku, których zawartość całkowitego tlenku żelaza, wyrażona jako Fe203, jest równa lub niższa od około 2,5%, mogą zawierać tlenek kobaltu i tlenek chromu.
Tak więc według jednego z aspektów wynalazku barwione szkła zawierają między około 1,5 i 2,5%o Feo03, między około 150 i 300 ppm tlenku kobaltu i między 700 i 2000 ppm tlenku chromu. Podczas oświetlania oświetlaczem C szkła te mają dominującą długość fali między około 490 i 510 nm i czystość wzbudzania około 10 do 25%. Ich współczynnik przenoszenia całkowitej energii jest poniżej 10%o, a zwykle jest pomiędzy około 5 i 8%o.
W celu otrzymania szkieł według wynalazku przedstawiony skład używany do znanych kompozycji stosowanych w przemyśle wytwarzającym szkło okienne uzupełnia się czynnika4
168 341 mi barwiącymi według takich proporcji, które dla danej grubości umożliwiają otrzymanie przewidywanej charakterystyki optycznej i wyglądu. Podstawowe szkło ma następujący skład wagowy:
SiO2 : 72,1%
AlzOs : 0,74%
CaO : 8,90%
MgO : 3,79%
Na20 : 14,16%
K2O : 0,11%
SO3 : 0,20%
Czynniki barwiące dodaje się do takiego szkła zmniejszając udział krzemionki. Różne przykłady podane w następującej tabeli ilustrują różne kombinacje czynników barwiących. Wartości charakterystyki optycznej podane w tabeli mieszano przy grubości szkła 3,85 mm.
Szkła te stapiano w takich warunkach, żeby miały one potencjał redoks korzystnie równy lub niższy od 0,35.
Dla szkieł barwionych przez związanie tlenków żelaza i kobaltu i dla procentowej zawartości żelaza między około 2 i 3% zaleca się wprowadzenie co najmniej około 140 ppm CoO dla szkła o grubości 3,85 mm. Poniżej tej zawartości przepuszczanie światła przez szkło ma tendencję wzrostową i może przekroczyć 15%.
Dla szkieł barwionych przez związanie selenu i tlenków żelaza i kobaltu zaleca się wprowadzenie co najmniej 1,4% tlenku żelaza dla grubości przeszklenia 3,85 mm. Poniżej tego udziału procentowego przenoszenia światła i energii szkła odpowiednio przekraczają 15 i 12%.
Kompozycje szklane podane w tabeli i powyższe uwagi dotyczące pewnych kombinacji czynników barwiących sąjedynie ilustracją wielu możliwych kompozycji, które mogą być wytwarzane bez wykraczania poza zakres wynalazku.
Szkła według wynalazku wytwarza się zgodnie z normalnymi sposobami postępowania stosowanymi do wytwarzania szkła okiennego, pod warunkiem, że w przypadku pewnych szkieł wytwarza się je w piecach wyposażonych w elektrody. Grubość wstęgi otrzymanego szkła, np. przez odkładanie stopionego szkła do łaźni cynowej, może zmieniać się między 2 i 10 mm, a korzystnie między 3 i 6 mm, kiedy szkło to ma być wykorzystane do wytwarzania przeszkleń dachów słonecznych.
Przeszklenia otrzymane przez cięcie wstęgi barwionego szkła według wynalazku, ewentualnie po wygięciu, mają tę zaletę, że są używane bezpośrednio do wytwarzania dachów słonecznych do samochodów w taki sposób, żeby pogodzić wymagania estetyczne i wymagania związane z wygodą pasażerów.
Tak jak w przypadku innych przeszkleń, można je uprzednio obróbce powierzchniowej albo można je połączyć, np. z płytą niebarwionego szkła lub z powłoką organiczną, taką jak błona na podstawie poliuretanu o właściwościach uniemożliwiających zranienie odłamkami albo błoną zapewniającą szczelność w przypadku rozbicia. Można takie przeszklenie powlekać miejscowo, np. emalią.
Przeszklenie według wynalazku może być pokryte co najmniej jedną warstwą tlenku metalu otrzymaną przez wysokotemperaturowe osadzanie chemiczne, takie jak piroliza lub chemiczne osadzanie par (CVD) albo przez osadzanie próżniowe.
Tak więc przeszklenia według wynalazku mogą być pokrywane powłoką na podstawie tlenku cyny. W przypadku dachu słonecznego w samochodzie z takiego przeszklenia pozwala to na dalszą poprawę właściwości. Powłoki takie otrzymuje się znanymi środkami, np. według sposobu znanego z opisu patentowego EP-B-121 459, który polega na termicznym rozkładzie organicznego związku cyny.
168 341
Tabela
| Numer kompozycji szklanej | Fe2O3 | Czynniki barwiące (% wagowy) | Fe/II/ całkowity Fe | ||
| CoO | Se | Cr2O3 | |||
| 1. | 3,72 | - | - | - | 0,26 |
| 2. | 1,45 | 0,0280 | 0,0024 | - | 0,35 |
| 3. | 1,54 | 0,0234 | 0,0026 | - | 0,34 |
| 4. | 1,59 | 0,0245 | 0,0031 | - | 0,35 |
| 5. | 1,58 | 0,0234 | 0,0023 | - | 0,39 |
| 6. | 1,76 | 0,0300 | 0,0023 | - | 0,33 |
| 7. | 1,74 | 0,0290 | 0,0019 | - | 0,34 |
| 8. | 2,27 | 0,0310 | 0,0015 | - | 0,34 |
| 9. | 2,85 | 0,0272 | - | - | 0,31 |
| 10. | 2,81 | 0,0160 | - | - | 0,26 |
| 11. | 2,80 | 0,0203 | - | - | 0,35 |
| 12. | 2,91 | 0,0270 | - | - | 0,27 |
| 13. | 2,36 | 0,0250 | - | 0,15 | 0,30 |
Charakterystyka optyczna
Numer kompozycji szklanej
TLa (%)
TE (%) (nm)
Po (%)
1.
11,3
4,5
566
43,7
2.
11,7
8,4
485
14,7
3.
9,8
6,5
551
7,2
4.
10,1
7,1
565
11,6
5.
11,7
7,2
493
8,3
6.
9,3
6,4
489
12,3
7.
11,1
7,5
485
19,3
8.
7,8
4,5
488
20,3
9.
8,2
4,2
489
25,7
10.
13,5
6,3
501
10,8
11.
9,7
4,5
494
17,3
12.
10,2
5,4
490
22,4
13.
11,1
7,0
500
18,2
168 341
Departament Wydawnictw UP RP. Nakład 90 egz Cena 1,50 zł
Claims (6)
- Zastrzeżenia patentowe1. Barwiona kompozycja szklana zawierająca następujące tlenki w podanych zakresach wagowych S1O2 64 do 75%, Al2C>3 0 do 5%, B203 do 5%, CaO 5 do 15%, MgO 0 do 5%, Na20 10 do 18%o, K2O 0 do 5%, przy czym suma tlenków metali ziem alkalicznych zawarta jest w zakresie 6 i 16%o, a tlenków metali alkalicznych zawarta jest w zakresie 10 i 20%, znamienna tym, że zawiera jako czynniki barwiące w podanych zakresach wagowych Fe203 (całkowite żelazo) 1,4 do 4,8%, CoO 0 do 0,05% z CoO>niż około 0,02%, jeżeli Fe203>niż około 2%, jak również ewentualnie selen i tlenek chromu, przy czym suma CoO + Se + Cd03 wynosi najwyżej 0,24%.
- 2. Kompozycja według zastrz. 1, znamienna tym, że zawiera miedzy 16 i 40% FeO całkowitego żelaza wyrażonego w postaci Fe203.
- 3. Kompozycja według zastrz. 1 albo 2, znamienna tym, że zawiera jako czynniki barwiące 3 do 4% tlenków żelaza wyrażonych w postaci Fe203.
- 4. Kompozycja według zastrz. 1 albo 2, znamienna tym, że zawiera jako czynniki barwiące Fe203 (całkowite żelazo) 2 do 3%, CoO 0,014 do 0,04%, Se 0 do 0,005%.
- 5. Kompozycja według zastrz. 1 albo 2, znamienna tym, że zawiera jako czynniki barwiące Fe203 (całkowite żelazo) 1,4 do 2,5%, CoO 0,015 do 0,033%, Se 0,0010 do 0,0035%o.
- 6. Kompozycja według zastrz. 1 albo 2, znamienna tym, że zawiera jako czynniki barwiące Fe203 (całkowite żelazo) 1,4 do 2,5%, CoO 0,015 do 0,030%), Cr203 0,07 do 0,2%.* * *