JP6773893B2 - 熱可塑性エラストマー組成物及びその用途 - Google Patents
熱可塑性エラストマー組成物及びその用途 Download PDFInfo
- Publication number
- JP6773893B2 JP6773893B2 JP2019509152A JP2019509152A JP6773893B2 JP 6773893 B2 JP6773893 B2 JP 6773893B2 JP 2019509152 A JP2019509152 A JP 2019509152A JP 2019509152 A JP2019509152 A JP 2019509152A JP 6773893 B2 JP6773893 B2 JP 6773893B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- olefin
- mass
- thermoplastic elastomer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)エチレン・α−オレフィン・非共役ポリエン共重合体(A)5〜30質量部と、密度が0.90g/cm3以上、0.92g/cm3以下である結晶性オレフィン系樹脂(B)20〜40質量部と、密度が0.94g/cm3以上、0.97g/cm3以下である高密度ポリエチレン(C)20〜40質量部と、エチレンと炭素数が3から12のα−オレフィンからなるエチレン・α−オレフィン共重合体(D)5〜12質量部と、シリコーン化合物(E)5〜9質量部とを含む熱可塑性エラストマー組成物(但し、(A)、(B)、(C)、(D)及び(E)の合計を100質量部とする)。
(2)シリコーン化合物(E)がシリコーンオイル及び高分子量シリコーンを含む前記(1)に記載の熱可塑性エラストマー組成物。
(3)エチレン・α−オレフィン共重合体(D)がエチレン・オクテンゴム及びエチレン・ブテンゴムから選ばれる1種類以上を含む前記(1)又は(2)に記載の熱可塑性エラストマー組成物。
(4)前記(1)〜(3)のいずれかに記載の熱可塑性エラストマー組成物で形成されている自動車用グラスランチャネル。
高密度ポリエチレン、及びエチレン・オクテンゴム、エチレン・ブテンゴム等のエチレン・α−オレフィン共重合体等のエチレン系樹脂を配合しても摺動性を維持できることは当業者にとっても予測できないことである。
本発明に用いるエチレン・α−オレフィン・非共役ポリエン共重合体(A)は、エチレンと、エチレン以外のα−オレフィン、好ましくは炭素数3〜20のα−オレフィンと、非共役ポリエン、好ましくは非共役ジエンとからなる共重合体である。
バナジウム(V)、ジルコニウム(Zr)、チタニウム(Ti)等の遷移金属化合物と、有機アルミニウム化合物(有機アルミニウムオキシ化合物)とからなる公知のチーグラー触媒;
元素の周期律表第4族から選ばれる遷移金属のメタロセン化合物と、有機アルミニウムオキシ化合物又はイオン化イオン性化合物とからなる公知のメタロセン触媒、例えば特開平9−40586号公報に記載されているメタロセン触媒;
特定の遷移金属化合物と、ホウ素化合物等の共触媒とからなる公知のメタロセン触媒、例えばWO2009/072553号パンフレットに記載されているメタロセン触媒;
特定の遷移金属化合物と、有機金属化合物、有機アルミニウムオキシ化合物又は該遷移金属化合物と反応してイオン対を形成する化合物とからなる遷移金属化合物触媒、例えば特開2011−52231号公報に記載されている遷移金属化合物触媒;
が挙げられる。特にメタロセン触媒を用いると、ジエンの分布が均一となってジエンの導入が少なくても高い架橋効率を得ることができ、また触媒活性が高いため触媒由来の塩素含量を低減できるため特に好ましい。
本発明に用いる結晶性オレフィン系樹脂(B)としては、好ましくはペルオキシド分解型オレフィン系プラスチックが挙げられる。
(1)プロピレン単独重合体
(2)プロピレンと10モル%以下の他のα−オレフィンとのランダム共重合体
(3)プロピレンと30モル%以下の他のα−オレフィンとのブロック共重合体
(4)1−ブテン単独重合体
(5)1−ブテンと10モル%以下の他のα−オレフィンとのランダム共重合体
(6)4−メチル−1−ペンテン単独重合体
(7)4−メチル−1−ペンテンと20モル%以下の他のα−オレフィンとのランダム共重合体
(1)(a)ペルオキシド架橋型オレフィン系共重合体ゴムと、(b)ペルオキシド分解型オレフィン系プラスチック(結晶性オレフィン系樹脂(B))とからなる混合物、又は(a)ペルオキシド架橋型オレフィン系共重合体ゴムと、(b)ペルオキシド分解型オレフィン系プラスチック(結晶性オレフィン系樹脂(B))と、(c)ペルオキシド非架橋型ゴム状物質及び/又は(d)鉱物油系軟化剤とからなる混合物を、有機ペルオキシドの存在下に動的に熱処理して得られた、部分的に架橋された熱可塑性エラストマー、
(2)(a)ペルオキシド架橋型オレフィン系共重合体ゴムと、(b)ペルオキシド分解型オレフィン系プラスチック(結晶性オレフィン系樹脂(B))と、(c)ペルオキシド非架橋型ゴム状物質及び/又は(d)鉱物油系軟化剤とからなる混合物を、有機ペルオキシドの存在下に動的に熱処理して得られた架橋されたゴム組成物に、(e)結晶性オレフィン系樹脂(B)を均一に配合せしめた、部分的に架橋された熱可塑性エラストマー等が挙げられる。
本発明に用いる高密度ポリエチレン(C)は、接着性と摺動性を両立させるための成分であり、密度は、通常0.940〜0.970g/cm3、好ましくは0.945〜0.965g/cm3である。ここで、密度はピクノメーター法(JIS K7112 B法)により測定した密度である。
本発明に用いるエチレン・α−オレフィン共重合体(D)は、得られる成形体の低温衝撃強度を高めるための成分であり、非晶性であり、かつ、メルトフローレート(MFR)は、摺動性改良の観点から、好ましくは0.05〜15g/10分、より好ましくは0.05〜10である。ここで、MFRはASTM D1238に準拠して測定される値であり、その測定条件は230℃、2.16kg荷重である。
本発明に用いるシリコーン化合物(E)は、主として、摺動抵抗低減のために添加するものである。
機器 :東ソー株式会社製HLC−8120
カラム :Polymer Laboratories製PL 10u Mixed B(7.5mm I.D×30cm×2)
検出器 :示差屈折率検出器(RI/内蔵)
溶媒 :トルエン(特級)
温度 :40℃
流速 :1.0mL/分
注入量 :110μL
濃度 :0.1質量%
較正試料:単分散ポリスチレン
較正法 :ポリスチレン換算
はじめに、試料(マスターバッチ)を0.05g秤量し、0.1g/L BHT(ジブチルヒドロキシトルエン)添加キシレン10mLを加えた後、125℃で60分攪拌してマスターバッチを溶解させる。マスターバッチが全溶したことを目視で確認した後、溶液を室温で3時間程度静置して、液中に結晶性ポリプロピレンを析出させる。この結晶が析出した溶液を住友電工製Fluoropore FP−100(1μm)を用いて吸引ろ過し、キシレン3mLで洗浄して、CXS(キシレン可溶部、高分子量シリコーン(シリコーンガム))とCXIS(キシレン不可溶部、ポリプロピレン)とに分離する。CXSを室温の窒素ブローにより予備乾固した後、60℃で真空乾燥する。真空乾燥は重量減少が認められなくなるまで行う。真空乾燥後のCXS分を用いてGPC測定を行う。
本発明の熱可塑性エラストマー組成物は、エチレン・α−オレフィン・非共役ポリエン共重合体(A)5〜30質量部と、結晶性オレフィン系樹脂(B)20〜40質量部と、高密度ポリエチレン(C)20〜40質量部と、エチレン・α−オレフィン共重合体(D)5〜12質量部と、シリコーン化合物(E)5〜9質量部とを含む(但し、(A)、(B)、(C)、(D)及び(E)の合計を100質量部とする)。前記の割合で成分(A)、(B)、(C)、(D)及び(E)を配合することにより、得られる成形体のコーナー部の接着性と摺動性を両立させ、かつ、低温衝撃強度に優れたグラスランチャネル等の成形体を製造することができる。
本発明の熱可塑性エラストマー組成物は、種々公知の成形方法、具体的には、例えば、押出成形、プレス成形、射出成形、カレンダー成形、中空成形棟の各種の成形方法により、熱可塑性エラストマー成形体とすることができる。更に、前記成形方法で得られたシートなど成形体を熱成形などで二次加工することができる。
実施例で作成した熱可塑性エラストマー組成物(摺動材料)からなるペレットで2層成形を行った。押出機は50mmの単軸押出機(株式会社日本製鋼社製)を用いて基材にミラストマーA800B(三井化学株式会社製)を用いて温度条件C1/C2/C3/C4/C5=160/170/180/190/200℃で押出成形を実施した。また摺動層には30mmの単軸押出機(株式会社プラスチック工学研究所)でC1/C2/C3=200/210/230℃の条件で摺動層の2層成形を行い、基材/摺動材=1.8mmt/0.2mmtの押出シートを作成した。
JIS K6253に準拠して、厚さ2mmのプレスシートを2枚重ねにし、ショアーA硬度計により測定した。
50tプレス機を用いて、熱可塑性エラストマー組成物から調製した(調製条件:予熱230℃、8分間、加圧、6分間)シートサンプル(2mm厚)を被験試料とし、測定温度25℃、引張速度500mm/分及び200mm/分の条件で引張試験を行い、引張破断強度(TB)及び引張破断伸び(EB)を測定した。
ASTM D1238に準拠して230℃、10kg荷重にて測定されるメルトフローレート(MFR)を求めた。
ASTM D746に準拠して測定した。
サンプルフィルムの表面に200gの荷重のあるガラス板をのせ、これを0.3m/分でフィルム表面と平行方向に引張った。その際に要した力(g)を測定し、この力をガラス板の重さで除したものを動摩擦係数で表した(ASTM D 1894−63に準じる)。
実施例及び比較例で得られた熱可塑性エラストマー組成物(摺動材料)からなるペレットを用いて、以下の方法で融着試験を行った。まず、厚み2mm(摺動面厚み0.2mm)の押出シートからJIS3号ダンベル試験片を打ち抜いて試験片を作成した。その後、このダンベル試験片を2分割し、150ton射出成形機(日本精工製 NEX140)の50℃の試験片金型にインサートした。この後、ミラストマーG800BS(オレフィン系熱可塑性エラストマー、三井化学株式会社製)を射出し、ダンベル試験片を作成した。(シリンダー温度はノズル前部/中間部/後部=250℃/230℃/210℃)その後、引張速度500mm/分で引張試験を行い、接着力(接着力、接着伸び)の評価を行った。
ガラスラン摺動摩耗試験機(日計電測株式会社)を用いて前記で2層成形した押出シートを用いて摺動層の評価を行った。摩耗子にガラスを使用して摩耗試験を行った。ガラスへの荷重を3kgfとしサイクルスピードを1サイクル/秒として1万回摺動試験を行い、ガラス接触部の削れ面の残存率から摺動性評価を行った。
(1)エチレン・α−オレフィン・非共役ポリエン共重合体(A)を含有する熱可塑性エラストマー(α)の製造
エチレン・α−オレフィン・非共役ポリエン共重合体(A)として三井EPT(商標)3072EPM(三井化学社製エチレン・プロピレン・ENB共重合体)(カタログ値:エチレン含量64質量%、ENB含量5.4質量%;モル換算値(エチレンとプロピレンの合計を100モル%とする):エチレン含量75.8モル%、プロピレン含量24.2モル%;油展量40質量部;ヨウ素価11.5)を140質量部、結晶性オレフィン系樹脂(B)としてポリプロピレン系樹脂(商品名:プライムポリプロE−200GP、(株)プライムポリマー製、ホモタイプ、MFR(230℃、21.2N)2.0g/10分、密度0.90g/cm3)を40質量部、架橋剤として有機ペルオキシド(1,3−ビス(tert−ブチルペルオキシイソプロピル)ベンゼン)0.3質量部と、架橋助剤としてジビニルベンゼン0.3質量部と、酸化防止剤としてフェノール系酸化防止剤(商品名:イルガノックス1010、BASFジャパン(株)製)0.20質量部と、ベンゾトリアゾール系紫外線吸収剤(商品名:Tinuvin 326FL、BASFジャパン(株)社製)0.20質量部、ヒンダードアミン(HALS)系耐候安定剤(商品名:サノールLS−770、三共ライフテック社製)0.10質量部、カーボンブラックマスターバッチ(PE4993、Cabot社製)4.0質量部と、軟化剤(ダイアナプロセスPW−100、パラフィンオイル)60質量部とをヘンシェルミキサーで充分に混合し、下記条件下で押出混練して、部分的又は完全に架橋された熱可塑性エラストマー(α)を得た。
押出機:品番 KTX−46、神戸製鋼(株)製
シリンダー温度:C1〜C2 120℃、C3〜C4 140℃、C5〜C14 200℃
ダイス温度:200℃
スクリュー回転数:400rpm
押出量:80kg/h
前記工程により得られた、部分的又は完全に架橋された熱可塑性エラストマー(α)25質量部に対し、結晶性オレフィン系樹脂(B)として、プロピレン/エチレンランダム共重合体(結晶性樹脂)(商品名:プライムポリプロB241、(株)プライムポリマー社製、密度:0.91g/cm3、MFR(温度:230℃、荷重:21.2N):0.5g/10分、密度0.91g/cm3)20質量部及び超高分子量ポリエチレン(商品名:ミペロンXM−220、三井化学社製、重量平均分子量200万、融点136℃、平均粒子径30μm)10質量部、高密度ポリエチレン(C)として(株)プライムポリマー社製高密度ポリエチレン(商品名:ハイゼックス8200B、密度=0.95g/cm3、ASTM D1238によるMFR(190℃、2.16kg荷重)0.03g/10分)40質量部、エチレン・α−オレフィン共重合体(D)としてダウ・ケミカル社製エチレン・オクテンゴム(商品名:エンゲージEG8003、MFR(230℃、2.16kg荷重)2g/10分、密度0.885g/cm3)10質量部、シリコーン化合物(E)として、シリコーンマスターバッチ(商品名:BY27−001、東レ・ダウコーニング(株)製、ポリプロピレン中にシリコーンガムを分散させたペレット、シリコーンガム含量:50質量%)10質量部及びシリコーンオイル(商品名:SH200−3000CS、東レ・ダウコーニング社製)4質量部をヘンシェルミキサーで充分に混合した後、押出機を用いて下記条件下で混練した。
押出機:品番 KTX−46、神戸製鋼(株)製
シリンダー温度:C1〜C2 120℃、C3〜C4 140℃、C5〜C14 200℃
ダイス温度:200℃
スクリュー回転数:400rpm
押出量:80kg/h
実施例1(2)において、各成分の配合比率を表1に記載のように変えた以外は、実施例1と同様にして熱可塑性エラストマー組成物のペレットを製造した。
Claims (4)
- エチレン・α−オレフィン・非共役ポリエン共重合体(A)5〜30質量部と、密度が0.90g/cm3以上、0.92g/cm3以下である結晶性オレフィン系樹脂(B)20〜40質量部と、密度が0.945g/cm3以上、0.97g/cm3以下である高密度ポリエチレン(C)20〜40質量部と、エチレンと炭素数が3から12のα−オレフィンからなるエチレン・α−オレフィン共重合体(D)5〜12質量部と、シリコーン化合物(E)5〜9質量部とを含む熱可塑性エラストマー組成物(但し、(A)、(B)、(C)、(D)及び(E)の合計を100質量部とする)であって、未架橋のエチレン・α−オレフィン・非共役ポリエン共重合体(A)と、結晶性オレフィン系樹脂(B)と、有機ペルオキシドと、必要に応じて、その他の成分を含有する混合物を動的に熱処理して、部分的又は完全に架橋されたエチレン・α−オレフィン・非共役ポリエン共重合体(A)を含む熱可塑性エラストマーを作成した後、残りの結晶性オレフィン系樹脂(B)と、高密度ポリエチレン(C)、エチレン・α−オレフィン共重合体(D)及びシリコーン化合物(E)と、必要に応じて、その他の成分を溶融混練後、造粒あるいは粉砕する方法により製造される熱可塑性エラストマー組成物。
- シリコーン化合物(E)がシリコーンオイル及び高分子量シリコーンを含む請求項1記載の熱可塑性エラストマー組成物。
- エチレン・α−オレフィン共重合体(D)がエチレン・オクテンゴム及びエチレン・ブテンゴムから選ばれる1種類以上を含む請求項1又は2記載の熱可塑性エラストマー組成物。
- 請求項1〜3のいずれか1項に記載の熱可塑性エラストマー組成物で形成されている自動車用グラスランチャネル。