JP5171040B2 - 構造物の中にガラスを接着するシステム - Google Patents
構造物の中にガラスを接着するシステム Download PDFInfo
- Publication number
- JP5171040B2 JP5171040B2 JP2006543999A JP2006543999A JP5171040B2 JP 5171040 B2 JP5171040 B2 JP 5171040B2 JP 2006543999 A JP2006543999 A JP 2006543999A JP 2006543999 A JP2006543999 A JP 2006543999A JP 5171040 B2 JP5171040 B2 JP 5171040B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- composition
- glass
- weight
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
A)本発明に従った透明プライマーを、ガラス又は耐摩耗性被覆プラスチックの表面に、構造物の中に接着させるべきガラス又は被覆プラスチックの部分に沿って適用する工程、
B)ポリイソシアネート官能性接着組成物を、ガラス又は被覆プラスチックの表面に、透明プライマーが予め適用された、構造物の中に接着させるべきガラス又は被覆プラスチックの部分に沿って適用する工程並びに
C)ガラス又は被覆プラスチックを構造物と、ガラス又は被覆プラスチックと構造物との間に配置された接着剤と共に接触させる工程
を含んでなる方法である。
に対応する。好ましくは、R1は、それぞれ存在する場合には独立に、アルキルカルボキシル、アルケニルカルボキシル、アリール若しくはアラルキルスルホニル、アルキルアミノ、ポリアルキルアミノ、ホスファトアルキル、ピロホスファトアルキルであり又はR1の2個若しくはそれ以上は組合さって、アルキレン若しくはカルボニルアルキレン含有環を形成することができる。一つの好ましい態様に於いて、R1は、式:
に対応するアルキルカルボキシル又はアルケニルカルボキシル部分を含む。
に対応する。
に対応する。更に、「a」は、それぞれ存在する場合に独立に、約0と3との間の有理数である。
に対応する。
に対応する。c及びdの合計は3である。
に対応する。好ましいポリアミノシランの中には、N−2−アミノエチル−3−アミノプロピルトリメトキシシラン及びN−アミノエチル−3−アミノプロピルメチルジメトキシシランがある。ポリアミノシランは、イソシアネート官能性接着剤の基体表面に対する接着の耐久性を増強するために十分な量で存在している。好ましくは、ポリアミノシランは、溶媒を含有する透明プライマー組成物中に、約0重量%又はそれ以上、更に好ましくは約0.1重量%又はそれ以上、最も好ましくは約0.3重量%又はそれ以上の量で存在している。好ましくは、ポリアミノシランは、透明プライマー組成物中に、約16重量%又はそれ以下、更に好ましくは約11重量%又はそれ以下、最も好ましくは約5重量%又はそれ以下の量で存在している。好ましくは、ポリアミノシランは、溶媒を除く固体のみの透明プライマー組成物中に、約0重量%又はそれ以上、更に好ましくは約1重量%又はそれ以上、最も好ましくは約3重量%又はそれ以上の量で存在している。好ましくは、ポリアミノシランは、固体のみベースの透明プライマー組成物中に、組成物の重量基準で、約22重量%又はそれ以下、更に好ましくは約15重量%又はそれ以下、最も好ましくは約7重量%又はそれ以下の量で存在している。
に対応する。好ましくは、R8は、C2〜C8アルキル、最も好ましくはC1〜C3アルキルである。別の態様に於いて、第二級アミノシランは、アミノアルキルアルキルポリシロキサン、例えば、ダイナシラン(Dynasylan)1146アミノアルキルアルキルポリシロキサンである。好ましい第二級アミノシランの中には、ビス−(3−トリメトキシシリルプロピルアミン)、3−エチルアミノ−2−メチル−プロピルトリメトキシシラン、3−エチルアミノ−2−メチルプロピルジメトキシ(メチル)シラン、N−メチルアミノプロピルトリメトキシシラン及びダイナシラン1146アミノアルキルアルキルポリシロキサンがある。第二級アミノシランは、イソシアネート接着剤の基体に対する耐久性を増強するために十分な量で存在している。好ましくは、第二級アミノシランは、溶媒を含有する透明プライマー組成物中に、約0重量%又はそれ以上、更に好ましくは約0.01重量%又はそれ以上、最も好ましくは約0.02重量%又はそれ以上の量で存在している。好ましくは、第二級アミノシランは、透明プライマー組成物中に、約16重量%又はそれ以下、更に好ましくは約9重量%又はそれ以下、最も好ましくは約3重量%又はそれ以下の量で存在している。好ましくは、第二級アミノシランは、溶媒を除く固体のみの透明プライマー組成物中に、約0重量%又はそれ以上、更に好ましくは約1重量%又はそれ以上、尚更に好ましくは約2重量%又はそれ以上、最も好ましくは約3重量%又はそれ以上の量で存在している。好ましくは、第二級アミノシランは、固体のみの透明プライマー中に、組成物の重量基準で、約22重量%又はそれ以下、更に好ましくは約13重量%又はそれ以下、最も好ましくは約4重量%又はそれ以下の量で存在している。
P−(OR10)3 又は(R10O)2−P−OR11O−P−(OR10)2
に対応する。好ましくは、R10は、それぞれの存在に於いて独立に、C6〜C18アルキル、C7〜C30アルカリール又はC6〜C20アリール、更に好ましくはC6〜C12アルキル、最も好ましくはC9〜C12アルキルである。好ましくは、R11は、それぞれの存在に於いて独立に、C6〜C18アルキレン、C7〜C30アルカリーレン又はC6〜C20アリーレン、更に好ましくはC7〜C30アルカリーレン又はC6〜C20アリーレン、尚更に好ましくはC7〜C30アルカリーレン、最も好ましくは二価のビスフェノール構造、例えば1,3−プロピレンジフェニル又はメチレンジフェニルである。好ましくは、二価のビスフェノールは、ビスフェノールA又はビスフェノールFをベースにする。本明細書で使用するアルキルは、飽和直鎖又は分岐鎖炭素鎖を意味する。
下記の実施例は、例示目的のためにのみ含められ、本発明の範囲を限定することを意図しない。他の方法で記載しない限り、全ての部及びパーセントは重量基準である。
配合物は、溶液の部として又は固体を基準にする%として列挙し、そして、適当な量の所望の材料を単純に混合することによって製造する。プライマーは、溶媒を予備乾燥したガラスボトルに添加することによって製造する。それぞれのシランを、このガラスボトルに添加し、そしてボトルを振盪機上で2分間振盪する。最後に、チタネートを添加し、そして混合物全体を3分間振盪する。
チゾール(Tyzor)(登録商標)OGTチタネート−オクチレングリコールチタネート=テトラキス(2−エチル−ヘキサン’−1,3,ジオラト)チタネート;
チゾール(登録商標)TOTチタネート−2−エチルヘキシルチタネート;
KR−TTS(登録商標)チタネート−イソプロピルトリイソステアロイルチタネート;
KR(登録商標)95チタネート−イソプロピルトリ(ドデシル)ベンゼンスルホニルチタネート;
KR(登録商標)44チタネート−イソプロピルトリ(N−エチレンジアミノ)エチルチタネート;
チゾール(登録商標)NBZジルコネート−N−ブチルジルコネート;
チゾール(登録商標)NBZジルコネート−トリエタノールアミンジルコネート;
メルカプトシランは、メルカプトプロピルトリメトキシシランである。
ポリアミノシランは、N−2−アミノエチル−3−アミノプロピルトリメトキシシランである。
第二級アミノシランは、ビス(トリメチルオキシシリルプロピル)アミンである。
エチルトリアセトキシシラン
例23のプライマーを、フリット1エナメルで被覆したガラス試片に適用した。この試片を、35℃で90%相対湿度中に記載した時間貯蔵した。接着剤A及びBを、前記のQKA試験に従って試片に適用した。表面に適用した接着剤を有する試片を、次いで、23℃及び50%相対湿度で7日間硬化させた。それぞれの開放時間について、1個の試片を、初期硬化時間の後、QKAに従って試験した。第二試片を、100℃及び100%相対湿度で更に14日間付し、貯蔵した。接着剤Aは、イソシアネート及びシラン官能性プレポリマーをベースにする接着剤である。接着剤Bは、イソシアネート官能性プレポリマーをベースにする接着剤である。
態様1.a)4個の配位子を有する1種又はそれ以上の有機チタネート(但し、これらの配位子は、任意的に、酸素、窒素、リン及び硫黄からなる群から選択された1種又はそれ以上のヘテロ原子を有する1個又はそれ以上の官能基を含むヒドロカルビルであり、これらの配位子の2個又はそれ以上は環状構造を形成していてもよい)、b)1種又はそれ以上のメルカプトシラン、c)1種又はそれ以上のポリアミノシラン、d)1種又はそれ以上の第二級アミノシラン並びにe)1種又はそれ以上の、この組成物の前記成分を溶解する溶媒を含んでなる組成物。
態様2.前記チタネートの配位子がヒドロカルビル、ヒドロカルビルカルボキシル、ヒドロカルビルスルホニル、ヒドロカルビルアミノ、ホスファトヒドロカルビル、ピロホスファトヒドロカルビルであり、2個又はそれ以上の配位子がヒドロカルビレン部分を形成し、2個又はそれ以上の配位子がカルボキシル含有ヒドロカルビレン部分若しくはこれらの混合物を形成する態様1に記載の組成物。
態様3.有機チタネートが、式Ti(−OR 1 ) 4 (式中、R 1 は、それぞれ存在する場合に独立に、ヒドロカルビル、ヒドロカルビルカルボキシル、ヒドロカルビルスルホニル、ヒドロカルビルアミノ、ホスファトヒドロカルビル、ピロホスファトヒドロカルビルであるが、R 1 の2個又はそれ以上が、組合さって、環状環構造を形成していてもよい)に対応する態様1又は2に記載の組成物。
態様4.a)0.08〜45重量%の1種又はそれ以上の有機チタネート、b)0.03〜59重量%の1種又はそれ以上のメルカプトシラン、c)0.005〜16重量%の1種又はそれ以上のポリアミノシラン、d)0.01〜16重量%の1種又はそれ以上の第二級アミノシラン並びにe)30〜99.5重量%の1種又はそれ以上の溶媒(但し、記載した重量%は、全組成物の重量基準である)を含む、態様1〜3の何れか1項に記載の組成物。
態様5.i)態様1〜4の何れか1項に記載の組成物並びにii)イソシアネート官能性プレポリマー及びイソシアネート官能性プレポリマーの硬化用触媒を含む添加物からなるガラスを基体に接着するシステム。
態様6.組成物(i)、接着組成物(ii)又は両方が、更に、紫外線安定剤を含む態様5に記載のシステム。
態様7.組成物(i)、接着組成物(ii)又は両方が、更に、ヒンダードアミン光安定剤からなる、態様6に記載のシステム。
態様8.A)態様1〜4の何れか1項に記載の組成物を、ガラス又は耐摩耗性で被覆したプラスチック基体の表面に、構造物の中に接着すべきガラス又は被覆プラスチック基体の部分に沿って適用する工程、
B)ポリイソシアネート官能性接着組成物を、ガラス又は被覆プラスチック基体の表面に、態様1〜4の何れか1項に記載の組成物が予め適用された、構造物の中に接着すべき部分に沿って適用する工程並びに
C)被覆プラスチック基体を構造物と、ガラス又は被覆プラスチック基体と構造物との間に配置された接着剤と共に接触させる工程
を含んでなる方法。
態様9.窓の一つを自動車の中に保持する接着システムが、態様5〜7の何れか1項に記載のシステムである自動車。
態様10.A)態様1に記載の組成物を、自動車の中への窓の部分と接触させる工程、
B)5〜90日後に、ポリイソシアネート官能性接着組成物を、態様1に記載の組成物を予め適用した、構造物に接着すべきガラス又はプラスチック窓の部分に沿ってガラス又はプラスチック窓の表面に適用する工程及び
C)この窓を構造物と、窓と構造物との間に配置された接着剤と共に接触させる工程を含んでなる、窓を自動車の中に接着する方法。
Claims (10)
- a)4個の配位子を有する1種又はそれ以上の有機チタネート(但し、これらの配位子は、酸素、窒素、リン及び硫黄からなる群から選択された1種又はそれ以上のヘテロ原子を有する1個又はそれ以上の官能基を、任意的に、含むヒドロカルビルであり、これらの配位子の2個又はそれ以上は環状構造を形成していてもよい)、
b)1種又はそれ以上のメルカプトシラン、
c)式:
(R7)c
|
(R 8 ) f −NH 2-f −(R 6 −NH) e −R 6 −Si−(X) d
(式中、R 6 はヒドロカルビレン基であり、R 7 は、それぞれ独立に、炭素数1〜20のアルキル基、炭素数6〜20のアリール基、炭素数7〜20のアラルキル基又は(R’) 3 SiO−(式中、同じか又は異なっていてよい3個のR’基のそれぞれは、炭素数1〜20の一価の炭化水素基を表す)によって表されるトリオルガノシロキシ基であり、Xは、それぞれ独立に、ヒドロキシル基又は加水分解性基であり、dは、それぞれ独立に、1、2又は3であり、そしてcは、それぞれ独立に、0、1又は2であり、c及びdの合計は3であり、R 8 はアルキル基であり、fは0又は1であり、そしてeは1〜3の有理数である)で表わされる1種又はそれ以上のポリアミノシラン、
d)式:
(R7)c
|
(R 8 ) f −NH−(R 6 −Si−(X) d ) g
(式中、R 6 、R 7 、R 8 、X、c、d及びfは前記定義の通りであり、そしてgは1又は2であり、f及びgの合計は2である)で表わされる1種又はそれ以上の第二級アミノシラン並びに
e)1種又はそれ以上の、この組成物の前記成分を溶解する溶媒
を含んでなる、接着剤用プライマー組成物。 - 前記チタネートの配位子がヒドロカルビル、ヒドロカルビルカルボキシル、ヒドロカルビルスルホニル、ヒドロカルビルアミノ、ホスファトヒドロカルビル、ピロホスファトヒドロカルビルであり、2個又はそれ以上の配位子が、ヒドロカルビレン部分、カルボキシル含有ヒドロカルビレン部分又はこれらの混合物を形成する請求項1に記載の組成物。
- 有機チタネートが、式Ti(−OR1)4(式中、R1は、それぞれ存在する場合に独立に、ヒドロカルビル、ヒドロカルビルカルボキシル、ヒドロカルビルスルホニル、ヒドロカルビルアミノ、ホスファトヒドロカルビル、ピロホスファトヒドロカルビルであるが、R1の2個又はそれ以上が、組合さって、環状環構造を形成していてもよい)に対応する請求項1又は2に記載の組成物。
- a)0.08〜45重量%の1種又はそれ以上の有機チタネート、
b)0.03〜59重量%の1種又はそれ以上のメルカプトシラン、
c)0.005〜16重量%の1種又はそれ以上のポリアミノシラン、
d)0.01〜16重量%の1種又はそれ以上の第二級アミノシラン並びに
e)30〜99.5重量%の1種又はそれ以上の溶媒
(但し、記載した重量%は、全組成物の重量基準である)
を含む、請求項1〜3の何れか1項に記載の組成物。 - (i)請求項1〜4の何れか1項に記載の組成物並びに(ii)イソシアネート官能性プレポリマー及びイソシアネート官能性プレポリマーの硬化用触媒を含む接着剤からなるガラスを基体に接着するシステム。
- 組成物(i)及び/又は接着剤(ii)が、更に、紫外線安定剤を含む請求項5に記載のシステム。
- 組成物(i)及び/又は接着剤(ii)が、更に、ヒンダードアミン光安定剤を含む、請求項6に記載のシステム。
- A)請求項1〜4の何れか1項に記載の組成物を、ガラス又は耐摩耗性の皮膜で被覆したプラスチック基体の表面に、構造物の中に接着すべきガラス又は被覆プラスチック基体の部分に沿って適用する工程、
B)ポリイソシアネート官能性接着組成物を、ガラス又は被覆プラスチック基体の表面に、請求項1〜4の何れか1項に記載の組成物が予め適用された、構造物の中に接着すべき部分に沿って適用する工程並びに
C)被覆プラスチック基体を構造物と、ガラス又は被覆プラスチック基体と構造物との間に配置された接着剤と共に接触させる工程
を含んでなる方法。 - 窓の一つを自動車の中に保持する接着システムが、請求項5〜7の何れか1項に記載のシステムである自動車。
- A)請求項1に記載の組成物を、自動車の中の窓の部分と接触させる工程、
B)5〜90日後に、ポリイソシアネート官能性接着組成物を、請求項1に記載の組成物を予め適用した、構造物に接着すべきガラス又はプラスチック窓の部分に沿ってガラス又はプラスチック窓の表面に適用する工程及び
C)この窓を構造物と、窓と構造物との間に配置された接着剤と共に接触させる工程を含んでなる、窓を自動車の中に接着する方法。