JP2016505502A - トータルピッチ安定性が改善されているガラス - Google Patents
トータルピッチ安定性が改善されているガラス Download PDFInfo
- Publication number
- JP2016505502A JP2016505502A JP2015549720A JP2015549720A JP2016505502A JP 2016505502 A JP2016505502 A JP 2016505502A JP 2015549720 A JP2015549720 A JP 2015549720A JP 2015549720 A JP2015549720 A JP 2015549720A JP 2016505502 A JP2016505502 A JP 2016505502A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- temperature
- consolidation
- less
- viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)40ppmより小さい高温試験サイクル(HTTC)における圧密、
(2)5.5ppmより小さい低温試験サイクル(LTTC)における圧密、及び
(3)応力緩和試験サイクルにおける50%未満の緩和に調和する応力緩和率、
で測定されるような、トータルピッチ変動(TPV)が特に優れたガラス基板である。単一のガラス製品で3つの規準の全てを満たすことにより、最高解像度THTサイクルに対して基板が受け入れられることが保証される。ガラス緩和の基礎的物理の最近の理解により、出願人等が3つの規準の全てを満たすガラスを開示することが可能になった。
SiO2 50〜85
Al2O3 0〜20
B2O3 0〜10
MgO 0〜20
CaO 0〜20
SrO 0〜20
BaO 0〜20
を含み、
0.9≦(MgO+CaO+SrO+BaO)/Al2O3≦3
である。ここで、Al2O3,MgO,CaO,SrO,BaOはそれぞれの酸化物成分のモル%を表す。
SiO2 68〜74
Al2O3 10〜13
B2O3 0〜5
MgO 0〜6
CaO 4〜9
SrO 1〜8
BaO 0〜5
を含み、
1.05≦(MgO+CaO+SrO+BaO)/Al2O3≦1.2
である。ここで、Al2O3,はMgO,CaO,SrO,BaOはそれぞれの酸化物成分のモル%を表す。
最小T35k−Tliq=0.25T35k−225
と表すことができる。ここで温度は全て℃単位である。したがって、開示されるガラスの別の態様はT35k−Tliq>0.25T35k−225℃であることである。
SO4 2―→SO2+O2+2e−
のような半反応を用いて書くことができる。ここで、e−は電子を表す。この半反応についての「平衡定数」は:
Keq=[SO2][O2][e−]2/[SO4 2―]
である。ここで、括弧は化学活量を表す。理想的には、SO2,O2及び2e−から硫酸塩を生成するように反応を進めさせたいであろう。硝酸塩、過酸化物またはその他の酸素に富む原材料の添加が役立ち得るが、溶融の早期段階においては硫酸塩低減に不利にはたらき得るし、これがまず第一にこれらの添加の効力を妨害し得る。SO2はほとんどのガラスにおいて溶解度が非常に低く、よってガラス溶融プロセスへの添加は実用的ではない。電子は還元された多価イオンによって「添加」することができる。例えば、第1鉄イオン(Fe2+)についての適切な電子供与半反応は:
2Fe2+→2Fe3++2e−
と表される。
(1)40ppmより小さい高温試験サイクル(HTTC)における圧密、
(2)5.5ppmより小さい低温試験サイクル(LTTC)における圧密、及び
(3)応力緩和試験サイクル(SRTC)における50%より小さい緩和と調和する応力緩和率、
で測定されるような、トータルピッチ変動(TPV)が特に優れたガラス基板である。3つの規準の全てを満たすことにより、基板は高解像度TFTサイクルに受容され得ることが保証される。これらの試験サイクルの簡単な説明は以下の通りである。
試料を箱形炉内で図1に示される温度プロファイルにしたがって熱処理した。初めに、炉を590℃よりやや高い温度に予備加熱した。次いで、重ねた5つの試料を炉の前面の小さなスリットを通して入炉させた。30分後、試料を出炉させて大気中で急冷した。試料が590℃のピーク温度にあった総時間は約18分であった。本開示の目的に対して、この試験の規準は高温試験サイクルまたはHTTCと定義されることになる。一実施形態において、HTTC圧密は40ppm以下である。別の実施形態において、HTTC圧密は38ppm以下である。別の実施形態において、HTTC圧密は36ppm以下である。別の実施形態において、HTTC圧密は30ppm以下である。別の実施形態において、HTTC圧密は25ppm以下である。別の実施形態において、HTTC圧密は20ppm以下である。
一般的なTFTアレイまたはCF基板温度サイクルで生じる熱圧密の大きさは、信頼できる品質保証測定を行うには不十分である。性能の実変化の識別を可能にする、より大きな圧密信号を達成するため、450℃/1時間の温度サイクルが用いられる。重ねた5つの試料(4つが実験試料で、1つは対照試料)を入炉させる前に、炉は450℃の直上の温度に保持される。炉が目標保持温度まで回復するにはほぼ7分が必要である。試料は450℃で1時間保持され、次いで出炉されて室温におかれる。一例の温度トレースが図2に示される。本開示の目的に対し、この試験の規準は低温試験サイクルまたはLTTCと定義されることになる。一実施形態において、LTTC圧密は5.5ppm以下である。別の実施形態において、LTTC圧密は5ppm以下である。別の実施形態において、LTTC圧密は4.6ppm以下である。
ガラス板を切断して10.00mm幅の角材にした。ガラスの厚さは成形されたままの厚さ(0.5mmと0.7mmの間)に維持した。抵抗加熱電気炉内部におかれた2つの支持剛体上にガラス試料を載せ、角材の中心のごく近くにSタイプ熱電対を配置し、プッシュロッド位置を調節することで、応力緩和実験を開始した。2つの支持剛体の支間は88.90mmであった。室温においてプッシュロッドの下端をガラスの表面の上方約5mmにおいた。炉の温度を650℃の最終実験温度まで急速に上げ、炉の内部におかれた全てのパーツの熱平衡を達成するために約5分間そのままにしておいた。プッシュロッドを2.54mm/分の速度で下降させ、ロードセル(LC)の信号をモニタすることで実験を続けた。これはガラス角材とのプッシュロッドの接触を見いだすために行った。LC信号が0.1ポンド(45.4g)に達すると、LC信号は荷重速度を10.16mm/分に増速をさせた。角柱の中心撓みが最終目標値(例えば、2.54mm)に達したときに荷重印加を停止し、プログラムを応力制御モードから歪制御モードに切り換えた。実験の残りの間、歪を一定に保ち、応力は可変とした。プッシュロッドのガラスへの最初の接触から2.54mmの最大歪に達する時点までの総時間は約12秒であった。数時間のデータが集まった後に実験を終了した。炉コントローラの比例−積分−微分パラメータの慎重な最適化により、等温保持の開始時に有意な温度オーバーシュートは見られなかったことは注目すべきである。
上記の3つの測定は、高温及び低温における構造緩和(すなわち圧密)並びに応力緩和の、熱プロセス下におけるトータルピッチ変動に対する主駆動機構を取り込んでいるから、ガラス基板のトータルピッチ変動性能を表すことができる。歴史的に、トータルピッチ変動への圧密の寄与は、顧客のTFTプロセスにおいて目合わせマークは後からおかれるから、高温挙動によって支配され、これらのプロセスにおける早期の低温プロセスの多くは無関係とされていた。高温圧密はHTTC圧密によって表され、製造中のガラスリボンの冷却速度を低める、ガラスシートをオフラインでアニールする、及び/または(T(ann)によって捕捉されるような)ガラスの粘度を高めることで低減される。図3はT(ann)が高くなるにともなう圧密の全体的な減少を示し、主な例外はガラスが(フュージョンドロープロセスの代わりにフロートプロセスによるような)かなり異なる熱履歴をもってつくられていることである。これはガラス製造業者が以前はトータルピッチをどのように扱っていたかを示す。ガラス製造業者は問題の温度領域(すなわち、高温領域)における圧密を抑えるため、冷却速度を低め、及び/またはアニール点を高めていた。
Claims (6)
- ガラスにおいて、以下の性能規準、
A:LTTCにおける圧密が5.5ppm以下、
B:HTTCにおける圧密が40ppm以下、
C:SRTCにおける誘起応力の緩和が50%より小さい、
を示すことを特徴とするガラス。 - 酸化物基準のモル%で、SiO2 50〜85,Al2O3 0〜20,B2O3 0〜10,MgO 0〜20,CaO 0〜20,SrO 0〜20,BaO 0〜20を含むことを特徴とする請求項1に記載のガラス。
- 酸化物基準のモル%で、SiO2 68〜74,Al2O3 10〜13,B2O3 0〜5,MgO 0〜6,CaO 4〜9,SrO 1〜8,BaO 0〜5を含むことを特徴とする請求項1に記載のガラス。
- As2O3及びSb2O3の含有量が約0.005モル%より少ないことを特徴とする請求項1に記載のガラス。
- 前記ガラスの内、Li2O,Na2O,K2Oまたはこれらの組合せの含有量が約0.1モル%より少ないことを特徴とする請求項1に記載のガラス。
- 1.05≦(MgO+CaO+SrO+BaO)/Al2O3≦1.2である(ここでAl2O3,MgO,CaO,SrO及びBaOは酸化物成分のモル%を表す)ことを特徴とするガラス。