DE947729C - Verfahren zur Herstellung verdickter Schmieroele und Schmierfette - Google Patents
Verfahren zur Herstellung verdickter Schmieroele und SchmierfetteInfo
- Publication number
- DE947729C DE947729C DES37897A DES0037897A DE947729C DE 947729 C DE947729 C DE 947729C DE S37897 A DES37897 A DE S37897A DE S0037897 A DES0037897 A DE S0037897A DE 947729 C DE947729 C DE 947729C
- Authority
- DE
- Germany
- Prior art keywords
- hydrogel
- water
- lubricating oil
- oil
- multiple solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
AUSGEGEBEN AM 23. AUGUST 1956
S 37897 IVc/23c
(Gr oßbritanni en)
ist in Anspruch genommen
Die Erfindung betrifft ein Verfahren zur Herstellung von mit anorganischen Kolloiden verdicken
Schmierölen und Schmierfetten.
Die üblicherweise verwendeten Verdickungs-
oder Geliermittel sind Seifen; es wurde jedoch vor kurzem eine neue Art von besonders temperaturbeständigem
Schmierfett entwickelt, bei welchem das Geliermittel ein anorganisches Kolloid ist. Es
wurden bereits einige Verfahren zur Herstellung dieser anorganischen Gelfette beschrieben, von
denen das sogenannte »Alcogel-Verfahren« und das »d'rekte Überführungsverfahren« sich bisher am
besten erwiesen haben. Beim Alcogel-Verfahren
wird das im anorganischen Hydrogel zunächst enthaltene Wasser mittels eines organischen Lösungsmittels,
wie z. B. eines Alkohols, verdrängt. Das so erhaltene Organogel wird mit einem Schmieröl
gemischt, das organische Lösungsmittel durch Destillation entfernt und das Produkt, falls erforderlich,
gemahlen, um eine Schmierfettstruktur zu erhalten. Im allgemeinen wird in einem beliebigen
Stadium des Verfahrens ein wasserabweisendes Mittel zugesetzt. Beim Direktverfahren
wird einem Schmieröl in Gegenwart eines oberflächenaktiven Mittels ein anorganisches Hydrogel
direkt einverleibt und das Wasser, z. B. durch Verdampfen, aus der erhaltenen Mischung entfernt.
Auch in diesem Fall kann es erforderlich sein, das
Produkt zu mahlen, um eine Schmierfettstruktur zu erhalten.
Vom verfahrenstechnischen Standpunkt aus ist
das Direktverfahren dem Alcogel-Verfahren vorzuziehen,
da es beträchtlich einfacher und billiger ist. Es hat aber den Nachteil, daß die Produkte
bei längerer Anwendung bei hohen Temperaturen ihre mechanische Stabilität verlieren, beispielsweise
nach etwa 48stündiger Verwendung bei 1500.
Mittels des Alcogel-Verfahrens hergestellte Fette bleiben dagegen, bei dieser Temperatur 120 Stunden
und langer stabil.
Man hat auch bereits vorgeschlagen, Schmieröle mittels Aerogelen zu verdicken, doch ist dieses Verfahren
noch teurer und umständlicher als das Alcogel-Verfahren. Eine weitere Möglichkeit besteht
in der Erzeugung eines Kolloids, in alkoholischer
Lösung, wobei jedoch keine Hydrogele mit ihren besonderen Eigenschaften erhalten werden.
Das wesentliche technische Problem bei der Einarbeitung eines Hydrogels in ein Schmieröl
besteht in der Entfernung des Hydrogel wassers auf solche Weise, daß eine Schrumpfung der Gelstruktur
λ-ermieden wird. Eine einfache Trocknung des Hydrogels gelingt nur im Sonderfall -eines
Montmorillonit-Amin-Komplexes.
Es wurde nun ein neues Verfahren gefunden,
welches die Vorteile des Alcogel-Verfahrens und des Direktverfahrens vereint, ohne ihre Nachteile
aufzuweisen, d. h. welches mit einer einzigen Arbeitsstufe arbeitet und doch die Herstellung verdickter
Schmieröle und Schmierfette mit einer vorzüglichen mechanischen Stabilität bei hohen
Temperaturen ermöglicht.
Erfindungsgemäß werden verdickte Schmieröle und Schmierfette dadurch hergestellt, daß man ein
Uydrogel eines anorganischen Kolloids mit einem Schmieröl und einer solchen Menge eines Mehrfach
lösungsmittel*; für das Schmieröl und Wasser
mischt, daß beim Erhitzen der Mischung, gegebenenfalls unter Druck, eine homogene, flüssige
Phase erhalten wird, sodann die Mischung solchen
Temperatur- und Druckbedingungen aussetzt, daß eine homogene, flüssige Phase erhalten wird, und
das Wasser und gegebenenfalls das Mehrfachlösungsmittel abdestilliert, wobei die genannte
flüssige Phase homogen bleibt.
Von besonderer Bedeutung ist hierbei, daß die drei in der Mischung vorhandenen Flüssigkeiten in
Form einer einzigen flüssigen Phase vorliegen, während dasAVasser entfernt wird. Überraschenderweise
ist dieser Umstand ausschlaggebend dafür, daß Produkte mit der erwünschten hohen mechanischen
Stabilität bei hohen Temperaturen erhalten werden. Es ist z. B. auch schon vorgeschlagen
worden, anorganische Gelfette herzustellen, indem man ein Hydrogel und Alkohol mit einem Schmieröl
mischt, das Wasser durch azeotrope Destillation entfernt und schließlich den restlichen Alkohol
abdestilliert. Hierbei wurde jedoch nicht erkannt, daß die verwendeten Flüssigkeiten während der
Destillation des Wassers in einer einzigen flüssigen Phase vorliegen müssen, damit die erhaltenen
Produkte bei hohen Temperaturen eine bessere mechanische Stabilität als die durch das Direktverfahren
hergestellten Schmierfette aufweisen. Diese bekannte Arbeitsweise bedeutet also gegenüber
dem Direktverfahren eine Komplizierung, ohne die diesem anhaftenden Nachteile zu beheben.
Das als Ausgangsmaterial für das erfmdungsgemäße Verfahren dienende anorganische Material
ist ein Hydrogel. Ein Hydrogel ist eine gelatinöse Masse, welche im allgemeinen durch Altern oder
Erhitzen eines Hydrosols erhalten wird und von einem einfachen Suspensionskolloid unterschieden
werden muß, welches nicht die charakteristische Gelstruktur aufweist.
Man hat auch schon vorgeschlagen, wäßrige Suspensionen oder Pasten eines feinverteilten
festen Materials unter Zusatz einer solchen Hilfsflüssigkeit
in ein öliges Medium einzuarbeiten, welche sowohl mit der wäßrigen Phase wie mit
dem Öl mischbar ist. Hieraus könnte man aber nicht auf das Verhalten der strukturell ganz anders
gebauten Hydrogele schließen, und es ist als außerordentlich überraschend anzusehen, daß es mittels
der erfindungsgemäßen Arbeitsweise gelingt, Schmierfette mit günstigen mechanischen Eigenschaften
bei hohen Temperaturen herzustellen.
Das erfindungsgemäße Verfahren läßt sich mit einer großen Anzahl verschiedener Komponenten
durchführen. Die verwendeten synthetischen .und/ oder natürlichen Schmieröle sind praktisch mit
Wasser nicht mischbar. Vorzugsweise ist das Schmieröl ein Mineralöl mit einer Viskosität von
mindestens der eines SAE-io-Schmieröls. Für die
Verwendung bei hohen Temperaturen sind jedoch schwerere öle zweckmäßiger, insbesondere das als
»bright stock« bekannte Öl. Als synthetische Schmieröle sind die Ester von Phosphorsäuren, wie
z. B. Trioctylphosphat. Di-(2-äthylhexyl)-hexanphosphonat und Bis-i, 3-(dioctylphosphon)-butan
sehr geeignet. Andere für diesen Zweck verwendbare Stoffe sind die Ester aliphatischer Dicarbonsäuren,
in welchen der Alkohol rest eine aliphatische Kohlenwasserstoffkette von 4 bis 12 C-Atomen enthält
und der Dicarbonsäurerest 6 bis 12 C-Atome enthält, z.B. Bis-(2-äthylhexyl)-sebazat und Bis-(isooctyl)-adipat.
Auß-rdem eignen sich auch polymere Oxya'kylenverbindungen. wie z. B. Poly- uo
propylenoxyd und seine Mischpolymerisate mit Äthylenoxyd, sowie Polymere von Glykolen, wie
z. B. Polymere von Trimethylenglykol, ferner hochsiedende,
flüssige organische Polymere, die Silicium enthalten, wie z, B. die flüssigen Polymethylphenyl- ng
siloxane und Polymethyisiloxane.
Die erfindungsgemäß verwendbaren anorganischen kristallinen oder amorphen Kolloide müssen
zur Hydrogelbildung befähigt sein. Als kristalline Kolloide kommen hauptsächlich synthetische oder
natürliche Tonsorten in Frage, vorzugsweise die sogenannten »quellenden« Tonsorten und insbesondere
die Montmorillonite. Zwei besonders geeignete Tonsorten sind Wyoming-Betonit und
Hectorit. Von den amorphen anorganischen Kolloiden sind verschiedene Metalloxyde, Hydroxyde,
Sulfide, Silikate, Sulfate und Chloride oder Mischungen solcher Substanzen zu nennen. Kieselsäure
eignet sich besonders gut, da sie billig und leicht zu beschaffen ist. Erdalkalihydroxyde sind
ebenfalls gut verwendbar, besonders in Mischung mit Kieselsäure.
Vorzugsweise enthält das bei den erfindungsgemäßen Verfahren als Ausgangsstoff dienende
Hydrogel etwa 0,5 bis 10 Gewichtsprozent des anorganischen Kolloids. Die besten Ergebnisse
werden erzielt, wenn der Gehalt an anorganischem Kolloid etwa 1 bis 5 Gewichtsprozent beträgt.
Als Mehrfachlösungsmittel für das Schmieröl und Wasser kann jede Flüssigkeit dienen, die bei
geeigneten Mengenverhältnissen, Temperatur- und Druckbedingungen mit dem Schmieröl und Wasser
ein flüssiges Einphasensystem bildet. Die speziellen Bedingungen schwanken mit den jeweils verwendeten Bestandteilen, für die in der vorliegenden
Beschreibung lediglich Beispiele gegeben werden. Jedoch können die erforderlichen Mengenverhältnisse,
Temperatur- und Druckbedingungen für eine bestimmte Kombination von Stoffen in einfacher
Weise jeweils durch Vorversuche oder durch Prüfung der Mischbarkeitskurven festgestellt
werden.
Die Mischbarkeit des Mehrfachlösungsmittels mit dem Schmieröl und mit Wasser soll vorzugsweise
so groß sein, daß die Verwendung einer großen Menge desselben zur Erreichung des gewünschten
Einphasensystems vermieden werden kann. Wenn das Mehrfachlösungsmittel mit dem
Wasser kein azeotropes Gemisch bildet, so soll es vorzugsweise einen höheren Siedepunkt als Wasser
haben. Ein Mehrfachlösungsmittel, dessen Siedepunkt nicht höher als der des Wassers liegt und das
mit dem Wasser kein azeotropes Gemisch bildet, kann zwar manchmal verwendet werden, jedoch
sind dann- große Mengen erforderlich, um im wesentlichen alles Wasser zu entfernen. Soll das
Mehrfachlösungsmittel nicht in dem fertigen Schmierfett oder eingedickten Schmieröl verbleiben,
so muß sein Siedepunkt wesentlich niedriger als der des verwendeten Schmieröls sein. Bisweilen ist
es zweckmäßig, ein bei niedrigen Temperaturen nur wenig mit Wasser mischbares Mehrfachlösungsmittel
zu verwenden, da dann das Destillat in zwei Phasen anfällt und dadurch die Rückgewinnung
des Lösungsmittels erleichtert wird.
Beispiele geeigneter Mehrfachlösungsmittel sind Alkohole, wie z. B. Äthylalkohol, Propylalkohole
und Cyclohexanol; Ketone, wie Diäthylketon; Äther, wie die Diisopropyl- und Diphenyläther und
Dioxan; Ester; Diole, Diglykole; Glykolmonoalkyläther;
Glycerinmono- oder -dialkyläther; Phenol
und Kresole, Amine und heterocyclische Basen, wie Alkanolamine, Pyridin und Morpholin. Es können
auch Mischungen solcher Lösungsmittel zur Anwendung kommen.
Schmierfette, die nur aus einem Schmieröl und einem anorganischen Kolloid bestehen, neigen in
Gegenwart von Wasser zum Zerfall. Daher ist es auch bei dem erfindungsgemäßen Verfahren zweckmäßig,
beim Mischen von Hydrogel, Schmieröl und Mehrfachlösungsmittel vor der Destillation ein
öllösliches, oberflächenaktives Mittel zuzusetzen. Dieses kann dem Hydrogel oder dem Schmieröl
oder auch dem Mehrfachlösungsmittel vor dem Mischen zugesetzt oder dem Gemisch getrennt einverleibt
werden. In vielen Fällen ist es erforderlich, 70-ein oberflächenaktives Mittel, insbesondere ein
kationaktives Mittel, zu verwenden, um das anorganische Kolloid in Form eines Hydrogels zu
erhalten, z. B. bei der Herstellung eines Tonhydrogels. Das für diesen Zweck verwendete oberflächenaktive
Mittel dient dann außerdem zur Stabilisierung des fertigen Schmierfettes gegen den zerstörenden
Einfluß von Wasser.
Die erfindungsgemäß verwendeten oberflächenaktiven Mittel können sowohl kationaktiv, anionaktiv
als auch nicht ionogen sein. Vorzugsweise sind es kationaktive Stoffe. Um in öl genügend
löslich zu sein, soll das oberflächenaktive Mittel im allgemeinen mindestens 12 Kohlenstoffatome pro
Molekül und vorzugsweise mindestens einen Kohlen- 8g
wasserstoff rest mit mindestens 12 Kohlenstoffatomen enthalten. Geeignete kationaktive Stoffe
sind z.B. »Oniumverbindungen«, wie Ammonium-, Phosphonium-, Sulfonium- und Arsoniumverbindungen.
Andere geeignete kation&ktive Stoffe sind die aliphatischen Amine mit langer Kette mit 12 oder
mehr Kohlenstoffatomen, wie Octadecylamin, und die Polyamine mit langer Kette. Komplexe Stoffe,
wie z. B. die partiellen Amide aus höheren Fettsäuren oder Harzsäuren mit aliphatischen PoIyamino-Hydroxyverbindungen
können ebenfalls verwendet werden.
Geeignete anionaktive Stoffe sind z. B-. Fettsäuren und hydroxysubstituierte Fettsäuren mit 10Q
mindestens 12, vorzugsweise mindestens 16 Kohlenstoffatomen
pro Molekül. Die Säuren können als solche oder in Form ihrer Seifen, vorzugsweise von
Seifen mehrwertiger und insbesondere amphoterer Metalle, verwendet werden. log
Um das fertige Schmierfett genügend wasserabweisend zu machen, soll das oberflächenaktive
Mittel in einer Menge von mindestens 25 Gewichtsprozent des anorganischen Kolloids vorliegen.
Wird das oberflächenaktive Mittel dem Hydrogel no
zugesetzt, ehe dieses mit dem Schmieröl und dem Mehrfachlösungsmittel gemischt wird, so ist es
zweckmäßig, Hydrogel und oberflächenaktives Mittel mindestens 30 Minuten lang miteinander auf
eine Temperatur über 6o° zu erhitzen. Dadurch wird das oberflächenaktive Mittel gleichmäßig auf
der Oberfläche der Gelpartikel verteilt, was zu einer Ausflockung der Gelpartikel führt und das Absetzen
erleichtert. Das sich abscheidende Wasser wird aus dem Hydrogel entfernt, ehe dieses mit dem
Schmieröl und dem Mehrfachlösungsmittel gemischt wird; dadurch wird die zur Abdestillation
des Wassers erforderliche Zeit verkürzt.
Das erfindungsgemäße Verfahren eignet sich außer zur Herstellung von Schmierfetten auch zur
Gewinnung von Schmierölkompositionen, die mit
anorganischen Kolloiden verdickt, aber"nicht geliert
sind. Beispiele solcher Kompositionen sind Bohrschlämme auf ölbasis, die anorganische Gele enthalten.
Das erfindungsgemäße Verfahren besteht aus folgenden Stufen:
A. Herstellung des Hydrogels des anorganischen Kolloids und dessen Zerkleinern bis 'zu einem Grad,
der ein Handhaben und Waschen erlaubt, um die
ίο während der Herstellung gebildeten Salze zu entfernen;
hierauf gegebenenfalls teilweise Entfernung des Wassers. Diese Arbeitsstufe, fällt nicht in den
Rahmen der vorliegenden Erfindung und kann nach einer der bekannten Methoden ausgeführt
werden.
B. Mischen des Hydrogels mit dem Mehrfachlösungsmittel und dem Schmieröl und gegebenenfalls
mit einem oberflächenaktiven Mittel.
C. Abdestillieren des Wassers und gegebenenfalls des Mehrfachlösungsmittels, wobei die flüssigen
Bestandteile in einer einzigen homogenen Phase vorliegen müssen.
D. Im allgemeinen mahlen oder scherende Behandlung des erhaltenen Produktes zwecks Eras
zielung einer fettartigen Struktur.
Bei der Stufe B ist es zweckmäßig, das Hydrogel mit dem Mehrfachlösungsmittel und gegebenenfalls
dem oberflächenaktiven Mittel vor Zugabe des Schmieröls zu mischen. Die Menge des Mehrfachlösungsmitteln
kann innerhalb weiter Grenzen schwanken, je nach dem Wassergehalt des Hydrogels,
der Menge des in dem fertigen Fett gewünschten anorganischen Kolloids und der Lösefähigkeit
des Mehrfachlösungsmittels für Schmieröl und Wasser. Falls die letztere nicht aus den. entsprechenden
Mischbarkeitskurven bekannt ist, kann sie leicht im Laboratorium durch Prüfung von entsprechenden
Mischungen festgestellt werden. Falls z. B. ein Schmierfett mit Isopropylalkohol als
Mehrfachlösungsmittel und Di-(2-äthylhexyl)-sebazat als Schmieröl hergestellt werden soll, kann
man eine Reihe von Wasserlösungen in Isopropylalkohol herstellen und diese mit dem Sebazat in
einem Gewichtsverhältnis von etwa 1 Teil Alkohollösung auf 2 Teile Sebazat mischen. Jede der
Mischungen kann sodann unter ständigem Rühren bis zum Sieden erhitzt und die Veränderungen in
den Phasensystemen beobachtet werden. Wird beim Sieden ein klares Einphasensystem erhalten, so
eignet sich die betreffende Mischung für das erfindungsgemäße Verfahren. Es wurde z. B. gefunden,
daß mit den obengenannten Bestandteilen beim Sieden Einphasenlösungen erhalten werden
können, vorausgesetzt, daß der Wassergehalt der Wasser-Isopropylalkohol-Lösung nicht mehr als
20 Gewichtsprozent beträgt. Bei Durchführung der Prüfung kann es erforderlich sein, den Druck anzupassen,
um die besten Bedingungen für die gegenseitige Lösefähigkeit beim Siedepunkt festzustellen;
in solchen Fällen wird dann natürlich, der gefundene optimale Druck bei der Verwendung der Mischung
in der eigentlichen Schmierfettherstellung angewandt.
Vorzugsweise wird das Mehrfachlösungsmittel mit dem Hydrogel chargenweise gemischt, wobei
nach jeder Zugabe kräftig gerührt wird, um ein Diffusionsgleichgewicht zu erreichen. Falls erforderlich,
kann nach jeder Zugabe etwa überstehende Flüssigkeit dekantiert werden, um die
Gesamtmenge der für das weitere Verfahren vorhandenen Flüssigkeit zu verringern. Wenn die erforderliche
Menge des Mehrfachlösungsmittels dem Hydrogel zugegeben ist, wird das Schmieröl,
gegebenenfalls zusammen mit dem oberflächenaktiven Mittel, eingerührt. An dieser Stelle können
auch etwaige weitere Bestandteile des Schmierfettes, wie Antioxydationsmittel, zugegeben werden.
Das Vermischen mit dem Schmieröl erfolgt zweckmäßig in dem gleichen Gefäß, in dem die Destillation
durchgeführt werden soll.
Die Arbeitsstufe C kann in jedem geeigneten Destillierapparat durchgeführt werden, der die
Anwendung von Hitze, die Beibehaltung eines gewünschten Druckes, die Einführung mehrerer Komponenten
und die Entfernung und Kondensation von Wasser und den Dämpfen des Mehrfachlösungsmittels
erlaubt. Die Destillation kann fortgesetzt werden bis zur völligen Entfernung des
Wassers und des Mehrfachlösungsmittels, oder sie kann unterbrochen werden, wenn der Wassergehalt
der Mischung einen genügend niedrigen Grad erreicht hat. Es kann z. B. bis zu 1 Gewichtsprozent
Wasser in den erfindungsgemäß erhaltenen Schmierfetten belassen werden.
Nach der Destillation ist es im allgemeinen erforderlich, die entwässerte Mischung zu mahlen
oder einer scherenden Einwirkung zu unterwerfen, um die Struktur eines Schmierfettes zu erhalten,
indem man sie z. B. unter Anwendung von hohem Druck durch kleine Öffnungen treibt. Diese öffnungen
haben zweckmäßig einen Durchmesser von 0,25 bis 0,62 mm und sind 7,5 bis 30 cm lang,
während der Druck im allgemeinen 350 bis 840 kg/cm2 beträgt. Es kann jedoch auch eine im
Handel erhältliche Homogenisiervorrichtung oder eine Farbenmühle verwendet werden. Vorzugsweise
wird die Mischung bei einer Temperatur von 20 bis 55° gemahlen oder der Scherung unterworfen.
Die folgenden Beispiele sollen das erfindungsgemäße Verfahren näher erläutern. Die angegebenen
Teile sind, wenn nicht anders erwähnt, Gewichtsteile, diese beziehen sich zu Volumteilen wie
das Kilogramm zum Liter.
6000 Volumteile einer wäßrigen Natriumsilikatlösung,
die 750 Teile SiO2 enthielt, wurden zu 10 200 Volumteilen 0,86 η-Schwefelsäure unter
Rühren gegeben. Nach etwa 2 Minuten hatte sich ein weiches Gel mit einem pH-Wert von 6 und
einem SiO2-Gehalt von 5 Gewichtsprozent gebildet.
Das Gel wurde durch, wiederholtes Aufschlämmen mit Wasser und Filtrieren von Salzen befreit. Zu
dem salzfreien Gel wurde chargenweise Isopropylalkohol zugesetzt und nach jeder Zugabe gerührt,
so daß vor der Dekantierung der überschüssigen
Flüssigkeit ein Diffusionsgleichgewicht hergestellt wurde. Dies wurde fortgesetzt, bis 89,2 Gewichtsprozent
des ursprünglich in dem Gel vorhandenen Wassers durch Isopropylalkohol ersetzt waren.
Als Schmieröl wurde Di-(2-äthylhexyl)-sebazat verwendet. In diesem wurden 2 Gewichtsprozent
eines öllöslichen oberflächenaktiven Mittels gelöst. Dieses wurde hergestellt, indem man Epichlorhydrin
mit wäßrigem Ammoniak kondensierte und das Produkt durch Umsetzung mit einer einem
Drittel seiner Baisizität entsprechenden Menge handelsüblicher Stearinsäure in ein partielles Amid
überführte. Ferner wurden in dem Schmieröl 0,1% Phenyl-/?-naph.thylamin als Antioxydationsmittel
gelöst. Dieses Schmieröl wurde mit der Mischung aus Kieselsäuregel und Isopropylalkohol in solcher
Menge gemischt, daß 95,3 Teile Öl auf 4,6 Teile Kieselsäure in demKieselsäuregel-Isopropylalkohol-Gemisch
kaftnen. Es war vorher festgestellt worden, daß das Wasser, der Isopropylalkohol und das öl
in der Mischung bei Zimmertemperatur ein Einphasensystem bilden, das auch beim Sieden erhalten
bleibt.
Die so hergestellte Mischung von Hydrogel, Isopropylalkohol und Schmieröl wurde sodann
destilliert, bis der Isopropylalkohol entfernt und der Wassergehalt gerade unter ο, ι Gewichtsprozent
gesunken war. Die erhaltene Mischung wurde der scherenden Einwirkung unterworfen, indem man
sie dreimal bei einem Druck von etwa 700 kg/cm2 durch ein 15 cm langes Röhrchen mit einem Durchmesser
von 0,5 mm preßte.
Das erhaltene Produkt war ein ausgezeichnetes Schmierfett mit einem Kieselsäuregehalt von
4,6 Gewichtsprozent und einem Wassergeihalt von 0,07 Gewichtsprozent. Es war außerordentlich
stabil bei hohen Temperaturen und behielt seine Konsistenz bei, nachdem es 120 Stunden lang einer
Temperatur von 1500 ausgesetzt worden war.
Wie in Beispiel I wurde ein Kieselsäurehydrogel hergestellt und gewaschen. 94,4 Gewichtsprozent
des in dem Gel vorhandenen Wassers wurden durch Isopropylalkohol auf die in Beispiel I beschriebene
Weise ersetzt.
Ais Schmieröl wurde medizinisches (chemisch reines) Paraffinöl verwendet, das die gleichen Zusätze
wie in Beispiel I in den gleichen Mengen enthielt. Dieses öl wurde mit der Kieselsäuregel-Isopropylalkohol-Mischung
in solcher Menge gemischt, daß 95,8 Teile öl auf 4,2 Teile der in der Mischung
vorhandenen Kieselsäure entfielen. Es war vorher festgestellt worden, daß das Wasser, der Isopropylalkohol
und das öl in der Mischung bei ungefähr 900 ein Einphasensystem bilden, das auch beim
Sieden erhalten bleibt.
Die Mischung von Hydrogel, Isopropylalkohol
Die Mischung von Hydrogel, Isopropylalkohol
60· und Schmieröl wurde sodann destilliert, bis die gesamte Menge Wasser und Isopropylalkohol entfernt
war, und die restliche Mischung wurde wie in Beispiel I der scherenden Behandlung unterworfen.
Das Produkt stellte ein ausgezeichnetes Schmierfett dar, das einen Kieselsäuregehalt von 4,2 Gewichtsprozent
hatte und kein Wasser mehr enthielt. Es war bei hohen Temperaturen äußerst stabil und
behielt seine Konsistenz auch nach 120 Stunden bei 1500 bei.
Beispiel III 7&
1000 Volumteile wäßriges Ammoniumhydroxyd mit einem Ammoniakgehalt von 17 Gewichtsprozent
wurden unter ständigem Rühren zu 1000 Volumteilen einer o,5molaren wäßrigen Aluminiumsulfatlösung
gegeben. Das erhaltene Hydrogel wurde mit Wasser auf 15000 Volumteile verdünnt und
15 Minuten gerührt. Nach dem Absetzen wurde das Wasser dekantiert und das Hydrogel wiederholt
gewaschen, bis es im wesentlichen salzfrei war. Hierauf wurde dem Gel chargenweise Isopropylalkohol
zugesetzt, wobei nach jeder Zugabe gerührt wurde, um vor der Dekantierung der überstehenden
Flüssigkeit ein Diffusionsgleichgewicht zu erhalten. Dies wurde fortgesetzt, bis 90 Gewichtsprozent des
ursprünglich im Gel vorhandenen Wassers durch Isopropylalkohol ersetzt waren.
Di-(2-äthylhexyl)-sebazat wurde mit der Mischung aus Aluminiumoxydgel und Isopropylalkohol
in solcher Menge gemischt, daß 93,35 Teile öl go:
auf je 6,65 Teile des in der Mischung vorhandenen Aluminiumoxyds kamen. Es war vorher festgestellt
worden, daß das Wasser, der Isopropylalkohol und das öl in der Mischung bei Zimmertemperatur ein
Einphasensystem bilden, das auch beim Sieden erhalten bleibt. Sodann wurden 40 Gewichtsprozent,
bezogen auf das vorhandene Aliuminiumoxyd, des öllöslichen oberflächenaktiven Mittels des
Beispiels I zugegeben und die Mischung so lange destilliert, bis die gesamte Menge an Wasser und
Isopropylalkohol entfernt war. Das Produkt wurde in einer 3-Walzen-Farbmühle gemahlen und ergab
ein Schmierfett mit einem Aluminiumoxydgehalt von 6,65 Gewichtsprozent und einer Mikropenetration
von 137.
Wenn man genau das gleiche Schmierfett, jedoch
mit dem Unterschied herstellte, daß nur 78 Gewichtsprozent des ursprünglich in dem Hydrogel
vorhandenen Wassers durch' Isopropylalkohol ersetzt wurden, wobei man ein Gemisch aus Hydnygel,
Isopropylalkohol und öl erhielt, dessen flüssige Bestandteile beim Sieden kein Einphasensystem
ergaben, so betrug die Mikropenetration des Fettes 252. Daraus geht hervor, daß sich mit dem erfindungsgemäßen
Verfahren höhere Ausbeuten, d. h. Schmierfette mit höherer Konsistenz bei gleicher
Geliermittelmenge erhalten lassen.
19 Teile Magnesiumsulfat und 132 Teile verdünnte
Schwefelsäure (45 Gewichtsprozent H2 S O4)
wurden in 1350 Volumteilen Wasser gelöst. Eine verdünnte Natriumsilikatlösung wurde unter Rühren
zugegeben, bis die Lösung einen pH-Wert von 6 hatte. Nach 2 Minuten setzte die Gelbildung ein, 125.
und das erhaltene Gel ließ man 15 Minuten altern,
ehe es mit 15000 Volumteilen Wasser verdünnt
wurde. Das Gel wurde sodann zerkleinert und mit Wasser gewaschen, bis es salzfrei war.
Hierauf wurde das erhaltene Gel ipit Isopropylalkohol
behandelt und wie in Beispiel III in ein Seihmierfett übergeführt, jedoch mit der Änderung,
daß das Di-(2-äthylhexyl)-sebazat in solcher Menge angewandt wurde, daß 95,8 Teile öl auf je 4,2 Teile
der vorhandenen Menge von Kieselsäure und Magmesia
kamen.
Nach dem Verfahren des Beispiels IV wurde ein
Schmierfett hergestellt, wobei jedoch an Stelle des Di-(2-äthylhexyl)-sebazats medizinisches Paraffinöl
in einer Gesamtmenge von 95 Teilen auf je 5 Teile der vorhandenen Gesamtmenge Kieselsäure und
Magnesia verwendet wurde.
Claims (9)
1. Verfahren zur Herstellung verdickter Schmieröle und Schmierfette durch Erhitzen
einer Dispersion eines anorganischen Hydrogels in einem Schmieröl und Abtrennen des Hydrogelwassers,
dadurch gekennzeichnet, daß das Erhitzen, gegebenenfalls unter Druck, unter Zusatz eines Mehrfachlösungsmittels für das
Schmieröl und das Hy drogel wasser erfolgt und aus der erhaltenen flüssigen homogenen Phase
das Hydrogelwasser sowie gegebenenfalls' das Mehrfachlösungsmittel abdestilliert werden.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet,
daß das Hy drogel etwa 0,5 bis ίο Gewichtsprozent an anorganischem Kolloid
enthält.
3. Verfahrennach Anspruch 1 oder 2, dadurch
gekennzeichnet, daß dem Hydrogel und/oder dem Schmieröl und/oder dem Mehrfachlösungsmittel
vor der Destillation ein öllösliches oberflächenaktives Mittel einverleibt wird.
4. Verfahren nach Anspruch 1 bis 3, dadurch gekennzeichnet, daß das Hydrogel mit dem
Mehrfachlösungsmittel vor Zugabe des Schmieröles gemischt wird.
5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, daß dais Mehrfachlösungsmittel
. mit dem Hydrogel chargenweise gemischt und nach jeder Zugabe gerührt wird.
6. Verfahren nach Anspruch 1 bis 5, dadurch gekennzeichnet, daß die Destillation so lange
durchgeführt wird, bis das Schmierfett einen Wassergehalt bis zu 1 Gewichtsprozent besitzt.
7. Verfahren nach Anspruch 1 bis 6, dadurch gekennzeichnet, daß das Produkt nach der
Destillation gemahlen oder einer scherenden Einwirkung unterworfen wird.
8. Verfahren nach Anspruch 1 bis 7, dadurch
gekennzeichnet, daß das Mehrfachlösungsmittel ein Alkohol, Keton oder Äther ist.
9. Verfahren nach Ansprüche, dadurch gekennzeichnet,
daß das Mehrfachlösungsmittel Isopropylalkohol ist.
In Betracht gezogene Druckschriften:
Deutsche Patentschriften Nr. 864 722, 864 723, 198, 865 P40.
Deutsche Patentschriften Nr. 864 722, 864 723, 198, 865 P40.
S 509 660/465 2.56 (609 589 8.56)