DE69106830T2 - Verfahren zum Vermindern des Schrumpfens beim Brennen keramischer Körper. - Google Patents

Verfahren zum Vermindern des Schrumpfens beim Brennen keramischer Körper.

Info

Publication number
DE69106830T2
DE69106830T2 DE1991606830 DE69106830T DE69106830T2 DE 69106830 T2 DE69106830 T2 DE 69106830T2 DE 1991606830 DE1991606830 DE 1991606830 DE 69106830 T DE69106830 T DE 69106830T DE 69106830 T2 DE69106830 T2 DE 69106830T2
Authority
DE
Germany
Prior art keywords
ceramic bodies
firing ceramic
reducing shrinkage
shrinkage
reducing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE1991606830
Other languages
English (en)
Other versions
DE69106830D1 (de
Inventor
Kurt Richard Mikeska
Daniel T Schaefer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Application granted granted Critical
Publication of DE69106830D1 publication Critical patent/DE69106830D1/de
Publication of DE69106830T2 publication Critical patent/DE69106830T2/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
    • C04B35/632—Organic additives
    • C04B35/634—Polymers
    • C04B35/63404—Polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B18/00—Layered products essentially comprising ceramics, e.g. refractory products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
    • C04B35/632—Organic additives
    • C04B35/634—Polymers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
    • C04B35/632—Organic additives
    • C04B35/634—Polymers
    • C04B35/63404—Polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • C04B35/63424—Polyacrylates; Polymethacrylates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having potential barriers, e.g. a PN junction, depletion layer or carrier concentration layer
    • H01L21/48—Manufacture or treatment of parts, e.g. containers, prior to assembly of the devices, using processes not provided for in a single one of the subgroups H01L21/06 - H01L21/326
    • H01L21/4803—Insulating or insulated parts, e.g. mountings, containers, diamond heatsinks
    • H01L21/4807—Ceramic parts
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6562—Heating rate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6567—Treatment time
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/341—Silica or silicates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/343—Alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/56—Using constraining layers before or during sintering
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/56—Using constraining layers before or during sintering
    • C04B2237/562—Using constraining layers before or during sintering made of alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/66—Forming laminates or joined articles showing high dimensional accuracy, e.g. indicated by the warpage
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/68—Forming laminates or joining articles wherein at least one substrate contains at least two different parts of macro-size, e.g. one ceramic substrate layer containing an embedded conductor or electrode
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T156/00—Adhesive bonding and miscellaneous chemical manufacture
    • Y10T156/11—Methods of delaminating, per se; i.e., separating at bonding face
    • Y10T156/1142—Changing dimension during delaminating [e.g., crushing, expanding, warping, etc.]
    • Y10T156/1147—Using shrinking or swelling agent during delaminating
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24802—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
    • Y10T428/24893—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.] including particulate material
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24802—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
    • Y10T428/24917—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.] including metal layer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24802—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
    • Y10T428/24926—Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.] including ceramic, glass, porcelain or quartz layer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/25—Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
    • Y10T428/252—Glass or ceramic [i.e., fired or glazed clay, cement, etc.] [porcelain, quartz, etc.]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Inorganic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Computer Hardware Design (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Power Engineering (AREA)
  • Production Of Multi-Layered Print Wiring Board (AREA)
  • Devices For Post-Treatments, Processing, Supply, Discharge, And Other Processes (AREA)
  • Compositions Of Oxide Ceramics (AREA)
DE1991606830 1990-10-04 1991-10-01 Verfahren zum Vermindern des Schrumpfens beim Brennen keramischer Körper. Expired - Lifetime DE69106830T2 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/591,192 US5254191A (en) 1990-10-04 1990-10-04 Method for reducing shrinkage during firing of ceramic bodies

Publications (2)

Publication Number Publication Date
DE69106830D1 DE69106830D1 (de) 1995-03-02
DE69106830T2 true DE69106830T2 (de) 1995-08-31

Family

ID=24365456

Family Applications (1)

Application Number Title Priority Date Filing Date
DE1991606830 Expired - Lifetime DE69106830T2 (de) 1990-10-04 1991-10-01 Verfahren zum Vermindern des Schrumpfens beim Brennen keramischer Körper.

Country Status (8)

Country Link
US (3) US5254191A (de)
EP (1) EP0479219B1 (de)
JP (1) JP2554415B2 (de)
KR (1) KR940001653B1 (de)
CN (3) CN1035609C (de)
CA (1) CA2052210A1 (de)
DE (1) DE69106830T2 (de)
MY (1) MY107198A (de)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10145362A1 (de) * 2001-09-14 2003-04-17 Epcos Ag Verfahren zur Herstellung eines keramischen Substrats

Families Citing this family (144)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5254191A (en) * 1990-10-04 1993-10-19 E. I. Du Pont De Nemours And Company Method for reducing shrinkage during firing of ceramic bodies
EP0535711A3 (en) * 1991-10-04 1993-12-01 Matsushita Electric Ind Co Ltd Method for producing multilayered ceramic substrate
DE69328390T2 (de) * 1992-05-20 2000-12-07 Matsushita Electric Ind Co Ltd Verfahren zur Herstellung eines mehrlagigen Substrats
US5470412A (en) * 1992-07-30 1995-11-28 Sumitomo Metal Ceramics Inc. Process for producing a circuit substrate
US5456778A (en) * 1992-08-21 1995-10-10 Sumitomo Metal Ceramics Inc. Method of fabricating ceramic circuit substrate
JP3003413B2 (ja) * 1992-09-21 2000-01-31 松下電器産業株式会社 多層セラミック基板の製造方法
US5798469A (en) * 1992-12-29 1998-08-25 International Business Machines Corporation Non-sintering controlled pattern formation
US5662755A (en) * 1993-10-15 1997-09-02 Matsushita Electric Industrial Co., Ltd. Method of making multi-layered ceramic substrates
DE69515584T2 (de) * 1994-09-27 2000-09-07 Nippon Shokubai Osaka Kk Keramische Schicht und Verfahren zur Herstellung derselben
US6001761A (en) * 1994-09-27 1999-12-14 Nippon Shokubai Co., Ltd. Ceramics sheet and production method for same
JP3570447B2 (ja) * 1994-12-21 2004-09-29 セイコーエプソン株式会社 積層型インクジェット式記録ヘッド、及びその製造方法、及び記録装置
US5655209A (en) * 1995-03-28 1997-08-05 International Business Machines Corporation Multilayer ceramic substrates having internal capacitor, and process for producing same
US6709749B1 (en) 1995-06-06 2004-03-23 Lamina Ceramics, Inc. Method for the reduction of lateral shrinkage in multilayer circuit boards on a substrate
WO1996039298A1 (en) * 1995-06-06 1996-12-12 Sarnoff Corporation Method for the reduction of lateral shrinkage in multilayer circuit boards on a support
US5708570A (en) * 1995-10-11 1998-01-13 Hughes Aircraft Company Shrinkage-matched circuit package utilizing low temperature co-fired ceramic structures
US5759669A (en) * 1995-12-22 1998-06-02 International Business Machines Corporation Apparatus and method for screening green sheet with via hole using porous backing material
US6042667A (en) * 1996-03-13 2000-03-28 Sumotomo Metal Electronics Devices, Inc. Method of fabricating ceramic multilayer substrate
JP3780386B2 (ja) * 1996-03-28 2006-05-31 株式会社村田製作所 セラミック回路基板及びその製造方法
US5676788A (en) * 1996-06-21 1997-10-14 International Business Machines Corporation Method for forming cavity structures using thermally decomposable surface layer
US5785800A (en) * 1996-06-21 1998-07-28 International Business Machines Corporation Apparatus for forming cavity structures using thermally decomposable surface layer
US5800761A (en) * 1996-10-08 1998-09-01 International Business Machines Corporation Method of making an interface layer for stacked lamination sizing and sintering
US5874162A (en) * 1996-10-10 1999-02-23 International Business Machines Corporation Weighted sintering process and conformable load tile
US5858145A (en) * 1996-10-15 1999-01-12 Sarnoff Corporation Method to control cavity dimensions of fired multilayer circuit boards on a support
US5948193A (en) * 1997-06-30 1999-09-07 International Business Machines Corporation Process for fabricating a multilayer ceramic substrate from thin greensheet
JPH11116279A (ja) * 1997-10-14 1999-04-27 Mitsuboshi Belting Ltd ガラス着色剤組成物
US6016005A (en) * 1998-02-09 2000-01-18 Cellarosi; Mario J. Multilayer, high density micro circuit module and method of manufacturing same
JP3601671B2 (ja) * 1998-04-28 2004-12-15 株式会社村田製作所 複合積層体の製造方法
US6228196B1 (en) * 1998-06-05 2001-05-08 Murata Manufacturing Co., Ltd. Method of producing a multi-layer ceramic substrate
US6258191B1 (en) 1998-09-16 2001-07-10 International Business Machines Corporation Method and materials for increasing the strength of crystalline ceramic
US6592696B1 (en) 1998-10-09 2003-07-15 Motorola, Inc. Method for fabricating a multilayered structure and the structures formed by the method
US6572830B1 (en) 1998-10-09 2003-06-03 Motorola, Inc. Integrated multilayered microfludic devices and methods for making the same
US6245171B1 (en) 1998-11-23 2001-06-12 International Business Machines Corporation Multi-thickness, multi-layer green sheet lamination and method thereof
US6447712B1 (en) * 1998-12-28 2002-09-10 University Of Washington Method for sintering ceramic tapes
US7216348B1 (en) 1999-01-05 2007-05-08 Net2Phone, Inc. Method and apparatus for dynamically balancing call flow workloads in a telecommunications system
JP3771099B2 (ja) * 1999-01-27 2006-04-26 松下電器産業株式会社 グリーンシート及びその製造方法、多層配線基板の製造方法、両面配線基板の製造方法
US6258192B1 (en) 1999-02-10 2001-07-10 International Business Machines Corporation Multi-thickness, multi-layer green sheet processing
JP3656484B2 (ja) 1999-03-03 2005-06-08 株式会社村田製作所 セラミック多層基板の製造方法
US6139666A (en) * 1999-05-26 2000-10-31 International Business Machines Corporation Method for producing ceramic surfaces with easily removable contact sheets
JP3687484B2 (ja) 1999-06-16 2005-08-24 株式会社村田製作所 セラミック基板の製造方法および未焼成セラミック基板
JP3601679B2 (ja) * 1999-07-27 2004-12-15 株式会社村田製作所 複合積層体の製造方法
DE19935677B4 (de) * 1999-07-29 2005-07-07 Robert Bosch Gmbh Paste für den Siebdruck von elektrischen Strukturen auf Trägersubstraten
US6395337B1 (en) * 1999-07-30 2002-05-28 International Business Machines Corporation Substrate with ceramic coating for camber modification and method for making
JP3554962B2 (ja) * 1999-10-28 2004-08-18 株式会社村田製作所 複合積層体およびその製造方法
DE10063265A1 (de) * 1999-12-20 2001-07-05 Murata Manufacturing Co Äußeres Überzugsubstrat für ein elektronisches Bauteil und ein piezoelektrisches Resonanzbauteil
TW507484B (en) * 2000-03-15 2002-10-21 Matsushita Electric Ind Co Ltd Method of manufacturing multi-layer ceramic circuit board and conductive paste used for the same
JP3633435B2 (ja) * 2000-04-10 2005-03-30 株式会社村田製作所 多層セラミック基板、その製造方法および設計方法、ならびに電子装置
JP4576670B2 (ja) * 2000-06-07 2010-11-10 パナソニック株式会社 セラミック基板の製造方法
JP3511982B2 (ja) * 2000-06-14 2004-03-29 株式会社村田製作所 多層配線基板の製造方法
JP3528045B2 (ja) * 2000-07-31 2004-05-17 株式会社村田製作所 積層セラミック電子部品の製造装置
JP3396465B2 (ja) * 2000-08-25 2003-04-14 三井金属鉱業株式会社 銅張積層板
JP3591437B2 (ja) * 2000-09-07 2004-11-17 株式会社村田製作所 多層セラミック基板およびその製造方法ならびに電子装置
JP2002084065A (ja) * 2000-09-07 2002-03-22 Murata Mfg Co Ltd 多層セラミック基板およびその製造方法ならびに電子装置
JP3593964B2 (ja) * 2000-09-07 2004-11-24 株式会社村田製作所 多層セラミック基板およびその製造方法
TW562737B (en) * 2000-11-27 2003-11-21 Murata Manufacturing Co Method of manufacturing ceramic multi-layer substrate, and unbaked composite laminated body
JP4557417B2 (ja) * 2000-12-26 2010-10-06 京セラ株式会社 低温焼成セラミック配線基板の製造方法
JP2002368422A (ja) * 2001-04-04 2002-12-20 Murata Mfg Co Ltd 多層セラミック基板及びその製造方法
JP2002368420A (ja) 2001-06-05 2002-12-20 Murata Mfg Co Ltd ガラスセラミック多層基板の製造方法およびガラスセラミック多層基板
JP3807257B2 (ja) * 2001-06-25 2006-08-09 松下電器産業株式会社 セラミック部品の製造方法
JP2003110238A (ja) * 2001-09-28 2003-04-11 Murata Mfg Co Ltd ガラスセラミック多層基板の製造方法
DE60220687T2 (de) 2001-10-01 2007-12-27 Heraeus, Inc. Ungesintertes niedertemperaturglaskeramikband für elektronische mikrobauteile, verfahren zur herstellung und verwendung
JP3716783B2 (ja) * 2001-11-22 2005-11-16 株式会社村田製作所 セラミック多層基板の製造方法及び半導体装置
US6615931B2 (en) * 2002-01-07 2003-09-09 Boart Longyear Co. Continuous feed drilling system
JP2003246680A (ja) * 2002-02-26 2003-09-02 Murata Mfg Co Ltd 多層セラミック基板の製造方法
JP4029207B2 (ja) * 2002-03-06 2008-01-09 株式会社村田製作所 セラミック多層基板の製造方法
US7381283B2 (en) * 2002-03-07 2008-06-03 Yageo Corporation Method for reducing shrinkage during sintering low-temperature-cofired ceramics
TW587067B (en) * 2002-03-07 2004-05-11 Yageo Corp Method for reducing shrinkage during sintering low-temperature ceramic and constrain layer
DE10221483C1 (de) * 2002-05-15 2003-12-04 Saint Gobain Winter Diamantwer Verfahren zur Herstellung frei gesinterter ringförmiger Schleifbeläge für Schleifscheiben
US6827800B2 (en) * 2003-01-30 2004-12-07 E. I. Du Pont De Nemours And Company Process for the constrained sintering of asymmetrically configured dielectric layers
US6960741B2 (en) * 2002-08-26 2005-11-01 Lexmark International, Inc. Large area alumina ceramic heater
TW540285B (en) * 2002-09-11 2003-07-01 Universal Scient Ind Co Ltd Parallel stack process of multi-layer circuit board
JP4517566B2 (ja) * 2002-09-11 2010-08-04 パナソニック株式会社 無収縮セラミック多層基板の製造方法
US6835260B2 (en) * 2002-10-04 2004-12-28 International Business Machines Corporation Method to produce pedestal features in constrained sintered substrates
AU2003257659A1 (en) 2002-10-10 2004-05-04 Murata Manufacturing Co., Ltd. Process for producing ceramic multilayer board
JP4426805B2 (ja) * 2002-11-11 2010-03-03 日本特殊陶業株式会社 配線基板およびその製造方法
EP1435651B1 (de) * 2003-01-02 2012-11-07 E.I. Du Pont De Nemours And Company Prozess zur eingeengten Sinterung von assymetrisch angeordneten Dielektrikalagen
DE10309689B4 (de) * 2003-02-27 2005-04-07 Bundesanstalt für Materialforschung und -Prüfung (BAM) Keramische Platte mit monolithischem Schichtaufbau und Verfahren zu seiner Herstellung
DE102004043273A1 (de) * 2003-09-09 2005-05-04 Ngk Spark Plug Co Verfahren zur Herstellung eines Keramiksubstrats und Keramiksubstrat
EP1675446A4 (de) 2003-10-17 2009-12-02 Hitachi Metals Ltd Keramisches mehrschichtsubstrat, herstellungsverfahren dafür und elektronisches bauelement damit
US7303698B2 (en) * 2003-11-19 2007-12-04 E.I. Du Pont De Nemours And Company Thick film conductor case compositions for LTCC tape
US7130522B2 (en) 2004-01-13 2006-10-31 International Business Machines Corporation Method and structure for two-dimensional optical fiber ferrule
US20050194085A1 (en) * 2004-03-02 2005-09-08 Matsushita Electric Industrial Co., Ltd. Method for producing ceramic multilayer substrate
JP2005268692A (ja) * 2004-03-22 2005-09-29 Mitsubishi Electric Corp 多層基板の製造方法
KR100670595B1 (ko) * 2004-03-24 2007-01-17 삼성광주전자 주식회사 업라이트 청소기
JP4496529B2 (ja) * 2004-06-07 2010-07-07 日立金属株式会社 多層セラミック基板の製造方法及び多層セラミック基板
JP2008501612A (ja) * 2004-06-08 2008-01-24 トライアンフ，オペレーティング アズ ア ジョイント ヴェンチャー バイ ザ ガバナーズ オブ ザ ユニバーシティ オブ アルバータ，ザ ユニバーシティ オブ ブリティッシュ コロンビア，カールトン 複合セラミック対象物の形成方法
US20060009036A1 (en) * 2004-07-12 2006-01-12 Bacher Rudolph J High thermal cycle conductor system
US7731812B2 (en) * 2004-10-19 2010-06-08 E.I. Du Pont De Nemours And Company Thick film conductor case compositions for LTCC tape
US7068492B2 (en) * 2004-11-22 2006-06-27 E. I. Du Pont De Nemours And Company Process for the constrained sintering of a pseudo-symmetrically configured low temperature cofired ceramic structure
US7067026B2 (en) * 2004-11-22 2006-06-27 E. I. Du Pont De Nemours And Company Process for the constrained sintering of a pseudo-symmetrically configured low temperature cofired ceramic structure
US7175724B2 (en) 2004-11-22 2007-02-13 E. I. Du Pont De Nemours And Company Process for the constrained sintering of a pseudo-symmetrically configured low temperature cofired ceramic structure
US20060163768A1 (en) 2005-01-26 2006-07-27 Needes Christopher R Multi-component LTCC substrate with a core of high dielectric constant ceramic material and processes for the development thereof
US20060162844A1 (en) * 2005-01-26 2006-07-27 Needes Christopher R Multi-component LTCC substrate with a core of high dielectric constant ceramic material and processes for the development thereof
KR100703406B1 (ko) * 2005-02-04 2007-04-03 삼성전자주식회사 Ｄｍａ 제어 장치 및 방법
US7687137B2 (en) 2005-02-28 2010-03-30 Kyocera Corporation Insulating substrate and manufacturing method therefor, and multilayer wiring board and manufacturing method therefor
JP3956148B2 (ja) * 2005-03-25 2007-08-08 株式会社村田製作所 セラミック多層基板の製造方法及び半導体装置
US7611645B2 (en) * 2005-04-25 2009-11-03 E. I. Du Pont De Nemours And Company Thick film conductor compositions and the use thereof in LTCC circuits and devices
US7326367B2 (en) * 2005-04-25 2008-02-05 E.I. Du Pont De Nemours And Company Thick film conductor paste compositions for LTCC tape in microwave applications
JP4557003B2 (ja) * 2005-07-01 2010-10-06 株式会社村田製作所 多層セラミック基板およびその製造方法ならびに多層セラミック基板作製用複合グリーンシート
WO2007004414A1 (ja) * 2005-07-01 2007-01-11 Murata Manufacturing Co., Ltd. 多層セラミック基板およびその製造方法ならびに多層セラミック基板作製用複合グリーンシート
US20070023388A1 (en) * 2005-07-28 2007-02-01 Nair Kumaran M Conductor composition for use in LTCC photosensitive tape on substrate applications
DE102005037456B4 (de) * 2005-08-01 2007-10-25 Technische Universität Ilmenau Verfahren zur Herstellung eines mehrlagigen Keramikverbundes
JP2007048844A (ja) * 2005-08-08 2007-02-22 Murata Mfg Co Ltd セラミック電子部品の製造方法およびセラミック電子部品
US7550319B2 (en) * 2005-09-01 2009-06-23 E. I. Du Pont De Nemours And Company Low temperature co-fired ceramic (LTCC) tape compositions, light emitting diode (LED) modules, lighting devices and method of forming thereof
CN101129103B (zh) * 2005-11-25 2011-04-06 株式会社村田制作所 多层陶瓷基板的制造方法
WO2007083811A1 (ja) 2006-01-23 2007-07-26 Hitachi Metals, Ltd. 導体ペースト、多層セラミック基板及び多層セラミック基板の製造方法
US7740725B2 (en) * 2006-04-05 2010-06-22 E.I. Du Pont De Nemours And Company Thick film conductor paste composition for LTCC tape in microwave applications
WO2007149298A2 (en) 2006-06-16 2007-12-27 E. I. Du Pont De Nemours And Company Improved process for pressureless constrained sintering of low temperature co-fired ceramic with surface circuit patterns
US20080018995A1 (en) * 2006-07-21 2008-01-24 Baun Kenneth W User-directed automated telescope alignment
EP2053030B1 (de) * 2006-08-18 2011-10-12 Murata Manufacturing Co. Ltd. Verfahren zur herstellung von keramikformkörpern
ATE556040T1 (de) * 2006-10-24 2012-05-15 Murata Manufacturing Co Schlickerzusammensetzung für eine keramik- grünfolie und verfahren zu deren herstellung sowie mehrschichtiges keramik-elektronik-bauteil und verfahren zu dessen herstellung
WO2009031348A1 (ja) * 2007-09-06 2009-03-12 Jtekt Corporation 切削刃具、切削刃具の成形方法および製造方法
KR100930165B1 (ko) * 2007-11-29 2009-12-07 삼성전기주식회사 구속용 그린시트 및 이를 이용한 다층 세라믹 기판의 제조방법
US20090162674A1 (en) * 2007-12-20 2009-06-25 Brett Allen Boutwell Tapes comprising barrier coating compositions and components comprising the same
EP2120522A4 (de) * 2008-02-19 2011-01-26 Murata Manufacturing Co Verfahren zur herstellung von laminierten keramischen elektronischen teilen
WO2009119198A1 (ja) * 2008-03-25 2009-10-01 株式会社村田製作所 セラミック基板の製造方法
EP2131637B1 (de) * 2008-03-28 2012-10-31 Murata Manufacturing Co. Ltd. Produktionsmethode für keramiksubstrat und verbundblech
KR100973059B1 (ko) * 2008-05-28 2010-07-29 한국세라믹기술원 저온동시소성세라믹스 모듈의 제조방법
DE112009001448T5 (de) 2008-06-13 2011-06-16 Murata Manufacturing Co., Ltd., Nagaokakyo-shi Verfahren zum Herstellen eines Keramikformkörpers
US20090311124A1 (en) * 2008-06-13 2009-12-17 Baker Hughes Incorporated Methods for sintering bodies of earth-boring tools and structures formed during the same
WO2010122822A1 (ja) 2009-04-21 2010-10-28 株式会社村田製作所 多層セラミック基板の製造方法
KR101079381B1 (ko) * 2009-09-11 2011-11-02 삼성전기주식회사 세라믹 기판의 제조 방법 및 이를 이용하여 제작한 세라믹 기판
US8704105B2 (en) 2009-12-31 2014-04-22 E I Du Pont De Nemours And Company Mixed-metal system conductors for LTCC (low-temperature co-fired ceramic)
WO2011108227A1 (ja) 2010-03-01 2011-09-09 パナソニック株式会社 発光素子用基板及びその製造方法ならびに発光装置
US8552311B2 (en) 2010-07-15 2013-10-08 Advanced Bionics Electrical feedthrough assembly
US8386047B2 (en) 2010-07-15 2013-02-26 Advanced Bionics Implantable hermetic feedthrough
KR101179330B1 (ko) 2010-07-30 2012-09-03 삼성전기주식회사 저온 동시 소성 세라믹 조성물, 이를 포함하는 저온 동시 소성 세라믹 기판 및 이의 제조방법
JP2012044133A (ja) * 2010-08-18 2012-03-01 Samsung Electro-Mechanics Co Ltd 熱電モジュール及びその製造方法
CN102219480A (zh) * 2011-04-22 2011-10-19 辽宁中大超导材料有限公司 一种利用温度梯度控制氧化镁烧结体靶材物理尺寸的方法
US20130052433A1 (en) 2011-08-29 2013-02-28 E I Du Pont De Nemours And Company Compositions for low k, low temperature co-fired composite (ltcc) tapes and low shrinkage, multi-layer ltcc structures formed therefrom
US20150084080A1 (en) 2012-02-15 2015-03-26 Panasonic Corporation Light emitting apparatus and method for manufacturing same
US20140015405A1 (en) * 2012-07-12 2014-01-16 Elementech International Co., Ltd. Light emitting diode module
CN105451950B (zh) 2013-08-15 2019-03-12 哈利伯顿能源服务公司 支撑剂的加成制造
CN105522137B (zh) 2014-10-24 2018-09-11 比亚迪股份有限公司 一种金属陶瓷复合体及其制备方法
US10000011B1 (en) 2016-12-02 2018-06-19 Markforged, Inc. Supports for sintering additively manufactured parts
US10800108B2 (en) 2016-12-02 2020-10-13 Markforged, Inc. Sinterable separation material in additive manufacturing
WO2018106733A1 (en) 2016-12-06 2018-06-14 Markforged, Inc. Additive manufacturing with heat-flexed material feeding
CN114989733A (zh) 2016-12-21 2022-09-02 康宁股份有限公司 烧结系统和烧结制品
CN106851871A (zh) * 2017-01-13 2017-06-13 杭州格拉思康科技有限公司 层状陶瓷电热元件
CN107759226A (zh) * 2017-10-29 2018-03-06 贵州喜文化艺术有限责任公司 一种陶瓷粉体制备方法
KR102072287B1 (ko) * 2018-02-21 2020-01-31 한국산업기술대학교산학협력단 Ltcc(저온 동시 소성 세라믹)를 이용한 유해가스 감지센서의 제조방법
KR102013896B1 (ko) * 2018-03-29 2019-08-23 조인셋 주식회사 세퍼레이터 및 이를 적용한 다수의 그린시트 유닛의 소성방법
CN108652088A (zh) * 2018-08-06 2018-10-16 云南中烟工业有限责任公司 一种新型卷烟加热元件及其制备方法
CN109678530B (zh) * 2019-01-24 2021-07-23 中国电子科技集团公司第四十三研究所 一种隔离粉及其制作方法
CN112225458B (zh) * 2020-08-13 2022-09-23 航天特种材料及工艺技术研究所 一种陶瓷基复合材料用耐高温低膨胀系数粘接浆料及其制备方法

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3655496A (en) * 1969-09-25 1972-04-11 Vitta Corp Tape transfer of sinterable conductive, semiconductive or insulating patterns to electronic component substrates
US3879509A (en) * 1971-09-07 1975-04-22 Gilbert James Elderbaum Method of producing thin ceramic sheets with minimal distortion
US4259061A (en) * 1979-12-07 1981-03-31 International Business Machines Corporation Method of achieving uniform sintering shrinkage in a laminated planar green ceramic substrate and apparatus therefor
JPS57181356A (en) * 1981-04-30 1982-11-08 Hitachi Ltd Sintered aluminum nitride body with high heat conductivity
US4521449A (en) * 1984-05-21 1985-06-04 International Business Machines Corporation Process for forming a high density metallurgy system on a substrate and structure thereof
US4654095A (en) * 1985-03-25 1987-03-31 E. I. Du Pont De Nemours And Company Dielectric composition
JPS62128973A (ja) * 1985-11-25 1987-06-11 松下電工株式会社 セラミツクス基板の焼成法
US5130067A (en) * 1986-05-02 1992-07-14 International Business Machines Corporation Method and means for co-sintering ceramic/metal mlc substrates
US5102749A (en) * 1988-01-27 1992-04-07 W. R. Grace & Co.-Conn. Electronic package comprising aluminum nitride and aluminum nitride-borosilicate glass composite
US4806188A (en) * 1988-03-04 1989-02-21 E. I. Du Pont De Nemours And Company Method for fabricating multilayer circuits
US4880684A (en) * 1988-03-11 1989-11-14 International Business Machines Corporation Sealing and stress relief layers and use thereof
US5035961A (en) * 1989-07-05 1991-07-30 Combustion Engineering, Inc. Internal cross-anchoring and reinforcing of multi-layer conductive oxides
US5102720A (en) * 1989-09-22 1992-04-07 Cornell Research Foundation, Inc. Co-fired multilayer ceramic tapes that exhibit constrained sintering
US5006182A (en) * 1989-11-17 1991-04-09 E. I. Du Pont De Nemours And Company Method for fabricating multilayer circuits
US5085720A (en) * 1990-01-18 1992-02-04 E. I. Du Pont De Nemours And Company Method for reducing shrinkage during firing of green ceramic bodies
US5254191A (en) * 1990-10-04 1993-10-19 E. I. Du Pont De Nemours And Company Method for reducing shrinkage during firing of ceramic bodies

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10145362A1 (de) * 2001-09-14 2003-04-17 Epcos Ag Verfahren zur Herstellung eines keramischen Substrats
DE10145362C2 (de) * 2001-09-14 2003-10-16 Epcos Ag Verfahren zur Herstellung eines keramischen Substrats

Also Published As

Publication number Publication date
CN1048969C (zh) 2000-02-02
US5254191A (en) 1993-10-19
CN1130606A (zh) 1996-09-11
CA2052210A1 (en) 1992-04-05
US5387474A (en) 1995-02-07
JPH04243978A (ja) 1992-09-01
KR940001653B1 (ko) 1994-02-28
MY107198A (en) 1995-09-30
CN1035609C (zh) 1997-08-13
EP0479219A1 (de) 1992-04-08
KR920007950A (ko) 1992-05-27
JP2554415B2 (ja) 1996-11-13
CN1125002C (zh) 2003-10-22
CN1061585A (zh) 1992-06-03
EP0479219B1 (de) 1995-01-18
CN1145350A (zh) 1997-03-19
DE69106830D1 (de) 1995-03-02
US5474741A (en) 1995-12-12

Similar Documents

Publication Publication Date Title
DE69106830T2 (de) Verfahren zum Vermindern des Schrumpfens beim Brennen keramischer Körper.
DE68914773D1 (de) Verfahren zum Herstellen von teilchengefüllten mikroporösen Gegenständen.
HU9200301D0 (en) Process for decreasing trqnsmitted pollution in amplification processes
DE69025746D1 (de) Verfahren zum Auftragen keramischer Schichten
DE59106370D1 (de) Verfahren zum Herstellen von Zementklinker.
DK0458150T3 (da) Fremgangsmåde til fremstilling af formede genstande
DE68907105D1 (de) Verfahren zum brennen von keramischen formkoerpern und tunnelofen dafuer.
DE69710398D1 (de) Verfahren zum Gravieren vorgesinterter keramischer Körper
DE69322753T2 (de) Verfahren zum Brennen von Kalkstein
DE68913348T2 (de) Verfahren zum Verkürzen der Formgebungstaktzeit.
DE68906311D1 (de) Verfahren zum vakuumentgasen und vakuumentkohlen bei temperaturausgleich.
DE69106345D1 (de) Verfahren zur verminderung des schrumpfens beim brennen von keramischen grünkörpern.
DE69007391T2 (de) Verfahren zum Spritzgiessen von keramischen Werkstoffen.
DE69209266T2 (de) Verfahren zum Entwässern
EP0464895A3 (en) Process for selectively acylating immunomycin
DE59005179D1 (de) Verfahren zum Verringern der Schwefelemission bei Sinterprozessen.
DE59005443D1 (de) Verfahren zum Trocknen und Brennen von Keramikteilen, zum Beispiel Sintern von Ferriten und dergleichen sowie Brennofen zur Verfahrensdurchführung.
DE68908095T2 (de) Verfahren zum Entfetten von keramischen Formkörpern.
DE59103312D1 (de) Verfahren zum Herstellen von multifunktionalen Verkleidungsteilen.
DE59105170D1 (de) Verfahren zum Schleifen der Standflächen keramischer Artikel.
DE59300470D1 (de) Vorrichtung zum Bilden von Zigarettenblöcken.
DE68911967D1 (de) Verfahren zum Brennen von Keramik und dafür verwendetes Brennhilfsmittel.
DE69410703D1 (de) Verfahren zum Vakuumdruckgiessen
DE69102740D1 (de) Werkzeug zum Setzen von einsteckbaren Klammern.
DE3778138D1 (de) Verfahren zum entfernen der zusaetze beim pulverformverfahren.

Legal Events

Date Code Title Description
8364 No opposition during term of opposition